Abstract
We have developed conductive microstructures using micropatternable and conductive hybrid nanocomposite polymer. In this method carbon fibers (CFs) were blended into polydimethylsiloxane (PDMS). Electrical conductivities of different compositions were investigated with various fiber lengths (50–250 μm), and weight percentages (wt%) (10–60 wt%). Sample composites of 2 cm × 1 cm × 500 μm were fabricated for 4-point probe conductivity measurements. The measured percolation thresholds varied with length of the fibers: 50 wt% (307.7 S/m) for 50 µm, 40 wt% (851.1 S/m) for 150 µm, and 30 wt% (769.23 S/m) for 250 μm fibers. The conductive composites showed higher elastic modulus when compared to that of PDMS.
Similar content being viewed by others
Introduction
Carbon materials (CMs) possess a variety of favorable properties which can be exploited for the fabrication of potential novel functional components for microelectromechanical systems (MEMS)1,2,3,4, electronic skins, human-friendly interactive electronics, and wearable health monitors5,6,7,8. For example, these materials have tendency to form densely packed 3D conductive structures with large surface area. This is highly desirable in devices such as solar cells and miniaturized batteries, where the performance of the device critically depends on large surface area with minimum footprint9,10. The range of different spatial formats of CMs can facilitate new MEMS devices with innovative geometries, which are not possible from traditional substrates such as metals, silicon, and glass. Among the CMs, carbon fiber (CF)11,12,13 is a very attractive substrate for electrical signal transduction in miniaturized electrochemical sensors due to the unique advantageous features such as the small dimensions (5–30 μm), low capacitive current, thermal stability, superior mechanical strength, light weight with a specific strength (strength/density) that can be produced from a roll-to-roll process14. All these merits are advantageous when CF serves as the substrate in the fabrication of sensors such as strain15, pressure16, chemical17,18, as well as optical and humidity19, and MEMS for harvesting energy devices and MEMS scanning micromirror arrays20.
In this study, we have used high-performance pitch-based carbon fibers, which have high strength and high modulus of elasticity (940 GPa) and have high thermal conductivity (800 W/m.k)21,22,23,24,25. These features can be exploited in the fabrication of flexible and mechanically robust sensor systems. Moreover, one of the biggest advantage of milled pitch-based carbon fiber is its excellent dispensability in polymers21,25 which cannot be obtained with graphene or carbon nanotubes. On the other hand, 0D/1D/2D nanomaterials26,27,28,29 have high tendency of agglomeration in the PDMS. Such a feature makes the composite fail with the incorporation of cracks. Also, 0D/1D/2D nanomaterials needs surface stabilization which impede the conduction of current. Therefore, we have used pitch-based carbon fibers that are inexpensive and robust for scalable flexible device fabrication.
More recently, conductive polymeric composites have been extensively employed in the fabrication of energy storage devices, batteries, 3D printing materials, electromagnetic shielding, flexible displays and smart sensors30,31,32,33,34. Compact network of conductive fillers in a polymeric matrix is essential for the development of the composites with high conductivity35,36,37. The characteristics of carbon fibers, such as, high aspect ratio, high conductivity and non-spherical shape are advantageous to achieve percolation path at lower concentration. Most widely used carbon-based polymer composites include polyamides, polymethylmethacrylate (PMMA), acrylonitrile butadiene styrene (ABS), and polyvinylalchol (PVOH). However, many of these are either not flexible and/or difficult to fabricate in micro-scaled features. Therefore, exploration of a flexible materials with better mechanical strength are of great interest.
PDMS is a silicone-based elastomer, which has been widely used as the elastomeric substrate for stretchable electronics. It has been easily and extensively employed for micromolding and fast prototyping of microdevices, such as in the fabrication of microfluidic chip and the stamping for pattern transfer via soft lithography38,39,40. Owing to its diverse properties such as transparency, biocompatibility and flexibility, it has been widely used for fabricating micromixers, microchannels, pumps etc. However due to its non-conductive behavior, the incorporation of electrical functionality has lagged. PDMS is very difficult to pattern conductive pattern lines on it, due to its poor adhesion with metal and conductive polymers41,42. Therefore, the integration of the conducting patterns on PDMS is a critical issue, for the fabrication of microsensors, actuators and micropumps, which need electrodes for signal detection. The incorporation of conductive lines is extremely important for signal routing, signal processing electronics and in some cases to supply power. Therefore, in this paper we present a flexible, conductive PDMS composites by incorporating micrometer size pitch-based milled CF. Moreover, we could construct 3D conducting microstructures with excellent mechanical strength incorporated into the PDMS.
Methods
Materials
Polydimethylsiloxane (Slygard 184 Silicone Elastomer Kit), consist of Slygard elastomer base and Slygard elastomer curing agent was purchased from Dow Corning corporation, Midland MI, USA. Milled CFs of length 50 µm, 150 µm and 250 µm were purchased from Nippon Graphite Fiber Co. (Tokyo, Japan).
Fabrication
Conductive hybrid polymer was prepared using PDMS from elastomer kit by mixing base elastomer and curing agent in ratio of 10:1 weight ratio and degassed to get rid of the bubbles formed during the mixing using a vacuum desiccator for 30 min at room temperature (Fig. 1). Carbon fibers with different wt% (10, 15, 25, 30, 40, 50, and 60) were added and stirred manually in the PDMS matrix. Further, sample were made in the rectangular shape of 2 cm × 1 cm size, and heat pressed at 120 °C at 10 Pa for 3 min to achieve a final thickness of 500 μm.
Microfabrication of Carbon Fiber PDMS Nano composites
PDMS-based electrically conductive composite were micropatterened using hybrid fabrication process shown in Fig. 2. A 3D- printed master with negative tone features, was fabricated using an Objet30 Pro 3D printer.
Results and Discussion
CF with different wt% (10, 15, 40 and 50) were added and stirred manually in the PDMS matrix. Samples were made in the rectangular shape of 2 cm × 1 cm size, and heat pressed at 120 °C at 10 Pa for 3 min. Figure 3 shows scanning electron microscopic (SEM) images of the carbon fibers in the PDMS matrix with different wt% of carbon fiber (average length of 50–250 μm).
Hybrid fabrication process involves pouring electrically conductive nanocomposites on the 3D printed mold and using spin coater at 1000 rpm for 4 min settling the composites on the mold evenly. The excess amount of the composite was wiped off the master using IPA wipes. Undoped PDMS was poured on the master to transfer the conductive features. Hybrid composite was cured at 110 °C under heat plate for 30 min and peel off from the master. This gives the electrically conductive features on the nonconductive PDMS as shown in the Fig. 4.
Conductivity Measurements
Sample size of 500 µm thickness was fabricated and tested with the 4-point terminal sensing to eliminate contact resistance. 3D printed jig was used to place the sample to measure resistance. Known current was passed through the sample using the input leads, and sense leads measured the voltage through the sample43. Resistance between the input and sense leads was calculated using the Ohm’s law. Since no current is withdrawn from the sense leads, contact resistance could be eliminated thus giving bulk resistance. The distance between the leads and sample geometry was known resistivity of the sample and was calculated using Equation 1.
Resistivity (ρ) was calculated by bulk resistance multiplies thickness (t) for variant weight percentage of filler. Samples with different length of the fibers were fabricated and resistance was test was performed as shown in the Fig. 5. From Fig. 5 it can be seen that the resistance values decrease with the increase in the wt% of carbon fibers. Further, Table S1 shows the different values of resistivity as a function of the length of the fibers with the wt% remaining constant.
The electrical conductivity of CFs in PDMS matrix as a function of wt% was measured using the setup shown in Fig. 6. From Fig. 7, it is observed that the conductivity increases slowly up to 30 wt% for 250 μm length fiber, 40 wt% for 150 μm and 50 wt% for 50 μm. However, conductivity increases swiftly after these points. This variation can be explained in terms of percolation theory. The percolation path is not set up at lower concentration of carbon fibers, as the concentration of fibers increases conducting percolation paths are setup44,45. Insulator to conductor transition point on fibers weight percentage plot is referred as percolation threshold. The percolation limit for carbon fiber-PDMS composites for 250 μm, 150 μm and 50 μm length fibers were at 30 wt%, 40 wt% and 50 wt%.
Mechanical Characterization
Thermal gravimetric analysis (TGA)
TGA results for PDMS and hybrid polymer shows the mass reduction as the function of temperature under a nitrogen purge. Approximately, 10 mg of sample was heated at a rate of 10 °C/min. TGA results were calculated three times for each sample which shows that PDMS goes into thermal degradation beginning around 488.53 °C with total mass loss of 74.14%. TGA results of PDMS and carbon fibers shows that due to the incorporation of fibers in the PDMS matrix enhance the thermal stability of composite. However, thermal degradation of PDMS and PDMS-Carbon fibers 15 wt% were left with around 25% of the total weight. Whereas 77–80% weight was remaining for PDMS-Carbon fibers 30 wt% and 50 wt% at around 780 °C as shown in Fig. S1. Furthermore, in PDMS-Carbon fibers composites starts degrading at <170 °C and weight loss of 5–7% occurred at 250 °C. The first derivative of thermo-gravimetric (DTG) shows the small shoulder on the TGA. DTG plot confirms the thermal degradation at 480 °C and 780 °C for the composites46.
Differential Thermal Analysis (DTA)
Further, (DTA-Heat flow) results shows the PDMS and PDMS-carbon fiber samples exhibits small endothermic peak at 180 °C showing loss of adsorbed water as shown in Fig. S2. After a gradual weight loss, a sharp weight loss was observed accompanied by the large broad exothermic peak shows in the DTA curve suggesting the decomposition of some organic compounds. After ∼620 °C the weight loss remained approximately half of the initial weight and the DTA analysis proved endothermic reaction. This could be ascribed to the PDMS weight rapidly decreased after 400 °C which accompanied by large shrinkage and even cracks in the composite (Fig. 8). The overall weight loss is higher in the samples with lower CFs content.
Dynamic Mechanical Analysis (DMA)
To investigate the mechanical properties of the hybrid polymer at varying temperature conditions, DMA was carried out from room temperature to 150 °C. DMA results shown in Fig. 9 for pure PDMS and PDMS-carbon fibers composites demonstrates storage modulus (E′) and loss modulus (E′′) against temperature at frequency of 10 Hz. The storage modulus of pure PDMS has been found to be about 45 times lower than that of PDMS 50 wt% CFs composites. Storage modulus for both cases has been found to remain almost constant throughout the whole temperature region suggesting good mechanical performance at elevated temperature on the other hand loss moduli for both cases showed monotonous decrease with increase in temperature signifying decreased elasticity at elevated temperature. For both samples loss moduli are lower than the storage moduli where loss modulus of PDMS 50 wt% CF has been found higher than the pure PDMS. So, it can be said that doping CFs in PDMS matrix the mechanical properties can be improved to a large extent.
Conclusion
In conclusion, we demonstrated the microfabrication of electrically conductive polymer. Further, we investigated the electrical and mechanical properties as well as the carbon fibers dispersion of carbon fibers/PDMS composites for varying carbon fiber weight ratios. SEM analysis shows that the carbon fibers were dispersed with little agglomeration. It was observed that the percolation threshold for carbon fibers with length 250 μm, 150 μm and 50 μm were observed at 30, 40 and 50 wt% respectively. We compared the thermal stability of PDMS and PDMS-carbon fibers with various wt%. TGA results showed the thermal stability improved with the increase in wt% of carbon fibers and DTA analysis showed the better thermal degradation properties of PDMS-carbon fibers. Hybrid PDMS nanocomposites showed enhancement in elastic modulus than that of pure PDMS. Thus, the developed micropatternable composites can be used to develop flexible and stretchable micro-sensors (chemical and physical), conductive lines or traces, elastomeric printed circuits and flexible sensors for Internet of Things (IoT) and for lab-on-chip devices.
References
Liao., M. & Yasuo, K. Carbon-based materials: growth, properties, MEMS/NEMS technologies, and MEM/NEM switches. Crit. Rev. Solid State Mater. Sci. 36, 66–101 (2011).
Khosla, A. & Gray, B. L. Preparation, characterization and micromolding of multi-walled carbon nanotube polydimethylsiloxane conducting nanocomposite polymer. Mater. Lett. 63, 1203–1206 (2009).
Khosla, A., Gray, B. L., Preparation of micro‐patterning and electrical characterization of functionalized carbon nanotube polydimethylsiloxane nanocomposite polymer. Macromolecular Symposia. Vol 297. No. 1. WILEY‐VCH Verlag, (2010).
Khosla, A. & Gray, B. L. Micropatternable multifunctional nanocomposite polymers for flexible soft NEMS and MEMS applications. ECS Transactions 45, 477–494 (2012).
Schwartz, G. Flexible polymer transistors with high pressure sensitivity for application in electronic skin and health monitoring. Nat. commun. 4, 1859 (2013).
Chaoyi, Y. et al. Highly stretchable piezoresistive graphene–nanocellulose nanopaper for strain sensors. Adv. Mater. 26, 2022–2027 (2014).
Qiang, L. et al. High-performance strain sensors with fish-scale-like graphene-sensing layers for full-range detection of human motions. ACS nano 10(8), 7901–7906 (2016).
Shah, S. et al. Microsyst. Technol. https://doi.org/10.1007/s00542-017-3694-0 (2017).
Netchiporouk, L. I. Properties of carbon fibre microelectrodes as a basis for enzyme biosensors. Anal. Chim. Acta 303, 275–283 (1995).
Argon, A. S. & Cohen, R. E. Toughenability of polymers. Polym. 44, 6013–6032 (2003).
Toprakci, H. A. K. et al. Polymer Nanocomposites Containing Carbon Nanofibers as Soft Printable Sensors Exhibiting Strain‐Reversible Piezoresistivity. Adv. Funct. Mater. 23, 5536–5542 (2013).
Choi, M. H. et al. The effect of coupling agent on electrical and mechanical properties of carbon fiber/phenolic resin composites. Polym. 41, 3243–3252 (2000).
Donnet, J. B. et al. Carbon Fibers, 3rd edn. revised and expanded (1998).
Bellingham, A. et al. Rapid prototyping of slot die devices for roll to roll production of EL fibers. Mater. 10, 594 (2017).
Weijing, Y. et al. Investigation of carbon black/silicone elastomer/dimethylsilicone oil composites for flexible strain sensors. Polym. Test. 31, 677–684 (2012).
Meyer, J. et al. Design and modeling of a textile pressure sensor for sitting posture classification. IEEE Sens. J. 10, 1391–1398 (2010).
Shah, S. et al. Microsyst. Technol. https://doi.org/10.1007/s00542-018-3781-x (2018).
Shang, S. et al. Investigation on the electrical response behaviors of multiwalled carbon nanotube/polyurethane composite in organic solvent vapors. Sensors and Actuators B: Chem. 166, 330–337 (2012).
Jiang, X. Microfiber knot dye laser based on the evanescent-wave-coupled gain. Appl. Phys. Lett. 90, 233501 (2007).
Unalan, H. E. Photoelectrochemical cell using dye sensitized zinc oxide nanowires grown on carbon fibers. Appl. Phys. Lett. 93, 133116 (2008).
Naito, K., Tanaka, Y., Yang, J.-M. & Kagawa, Y. Flexural Properties of PAN and Pitch-Based Carbon Fibers, J. Am. Ceram. Soc. 92, 186–192 (2009).
Lim, T. H. & Yeo, A. Y. Investigation of the degradation of pitch-based carbon fibers properties upon insufficient or excess thermal treatment. Sci. Rep. 7, 4733 (2017).
Asano, K. & Zainuddin, M. F. B. Wear Behavior of PAN- and Pitch-Based Carbon Fiber Reinforced Aluminum Alloy Composites under Dry Sliding Condition. Mater. Trans. 58, 898–905 (2017).
Yang, K. S., Kim, B.-H. & Yoon, S.-H. Pitch based carbon fibers for automotive body and electrodes. Carbon Lett. 15, 162–170 (2014).
Hamid, S. et al. Progress in Carbon Fiber and Its Polypropylene- and Polyethylene-BasedComposites. Poly. Plast. Tech. Engg. 53, 1845–1860 (2014).
Mir, S. H. & Ochiai, B. Development of Hierarchical Polymer@Pd Nanowire‐Network: Synthesis and Application as Highly Active Recyclable Catalyst and Printable Conductive Ink. ChemistryOpen 5, 213–218 (2016).
Mir, S. H. & Ochiai, B. One‐Pot Fabrication of Hollow Polymer@Ag Nanospheres for Printable Translucent Conductive Coatings. Adv. Mater. Interfaces 4, 1601198 (2017).
Mir, S. H. et al. Alignment of Ag nanoparticles with graft copolymer bearing thiocarbonyl moieties. Microsyst. Technol. 24, 605–611 (2018).
Mir, S. H. & Ochiai, B. Fabrication of Polymer‐Ag Honeycomb Hybrid Film by Metal Complexation Induced Phase Separation at the Air/Water Interface. Macromol. Mater. Eng. 301, 1026–1031 (2016).
Cao, Z. et al. Fragmented carbon nanotube macrofilms as adhesive conductors for lithium-ion batteries. ACS Nano 8, 3049–3059 (2014).
Jakus, A. E. Three-dimensional printing of high-content graphene scaffolds for electronic and biomedical applications. ACS Nano 9, 4636–4648 (2015).
Liang, J. Electromagnetic interference shielding of graphene/epoxy composites. Carbon 47, 922–925 (2009).
Xu, Y. et al. A hybrid material of graphene and poly (3, 4-ethyldioxythiophene) with high conductivity, flexibility, and transparency. Nano Res. 2, 343–348 (2009).
Deng, H. et al. Towards tunable resistivity–strain behavior through construction of oriented and selectively distributed conductive networks in conductive polymer composites. J. Mater. Chem. A 5, 5815–5824 (2013).
Karger, K. et al. Recent advances in fiber/matrix interphase engineering for polymer composites. Prog. Mater. Sci. 73, 1–43 (2015).
Bekyarova, E. et al. Multiscale carbon nanotube− carbon fiber reinforcement for advanced epoxy composites. Langmuir 23, 3970–3974 (2007).
Qian, H. et al. Multifunctional structural supercapacitor composites based on carbon aerogel modified high performance carbon fiber fabric. ACS Appl. Mater. Interfaces 5, 6113–6122 (2013).
Xia, Y. et al. Soft lithography. Ann. Rev. Mater. Sci. 28, 153–184 (1998).
Lee, C. C. et al. Multistep synthesis of a radiolabeled imaging probe using integrated microfluidics. Sci. 310, 1793–1796 (2005).
Unger, M. A. et al. Monolithic microfabricated valves and pumps by multilayer soft lithography. Science 288, 113–116 (2000).
Shaikh, K. A. et al. A modular microfluidic architecture for integrated biochemical analysis. PNAS 102, 9745–9750 (2005).
Khosla, A. Micropatternable multifunctional nanocomposite polymers for flexible soft MEMS applications. PhD diss. Appl. Sci.: School of Engineering Science, (2011).
Khosla, A. Nanoparticle-doped electrically-conducting polymers for flexible nano-micro Systems. ECS Interface 21, 67–70 (2012).
Motaghi, A., Hrymak, A. & Motlagh, G. H. Electrical conductivity and percolation threshold of hybrid carbon/polymer composites. J. Appl. Polym. Sci. 132, 41744 (2015).
Iqbal, A., Frormann, L., Saleem, A. & Ishaq, M. The effect of filler concentration on the electrical, thermal, and mechanical properties of carbon particle and carbon fiber‐reinforced poly(styrene‐co‐acrylonitrile) composites. Polym. Compos. 28, 186–197 (2007).
Pan, G. et al. Synthesis and characterization of fillers of controlled structure based on polyhedral oligomeric silsesquioxane cages and their use in reinforcing siloxane elastomers. J. Polym. Sci. Part B: Polym. Phys. 41, 3314–3323 (2003).
Acknowledgements
Authors would like to thank Nippon Graphite Fiber Co., Ltd, Japan; for proving milled carbon fiber and technical support for this project. Authors would like to thank Prof. Bungo Ochiai (Yamagata University), for his help and access to SEM, Prof. Tomoya Higashiara (Yamagata University) for his help and access to TGA and TMA. This study was partly supported by the Grant-in-Aid for Scientific Research (Category A, Project No. 17H01224) from the Japan Society for the Promotion of Science (JSPS), the Center Of Innovation (COI) program from the Japan Science and Technology Agency (JST), the Strategic Innovation Creation Project (SIP) from the New Energy and Industrial Technology Development Organization (NEDO) of Japan, and the Program on Open Innovation Platform with Enterprises, Research Institute and Academia (OPERA) from the JST.
Author information
Authors and Affiliations
Contributions
A.K., L.N., T.T., P.S., M.K., and H.F. designed the experiments and analyzed the results. S.S. and M.N.I.S., performed the experiments and analyzed the results. S.S., S.H.M. and A.K. wrote the manuscript. S.H.M., M.N.I.S., L.N., T.T., P.S., M.K., M.K., H.F. and A.K. revised the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Khosla, A., Shah, S., Shiblee, M.N.I. et al. Carbon fiber doped thermosetting elastomer for flexible sensors: physical properties and microfabrication. Sci Rep 8, 12313 (2018). https://doi.org/10.1038/s41598-018-30846-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-30846-3
This article is cited by
-
Advances in lithographic techniques for precision nanostructure fabrication in biomedical applications
Discover Nano (2023)
-
P(VDF-TrFE)/ZnO nanocomposite synthesized by electrospinning: effect of ZnO nanofiller on physical, mechanical, thermal, rheological and piezoelectric properties
Polymer Bulletin (2023)
-
Highly sensitive, stretchable, piezoresistive auxetic sensor based on graphite powders sandwiched between silicon rubber layers
Polymer Bulletin (2023)
-
Pd-induced phase separation in poly(methyl methacrylate) telopolymer: synthesis of nanostructured catalytic Pd nanorods
Colloid and Polymer Science (2020)
-
A thermosensitive electromechanical model for detecting biological particles
Scientific Reports (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.