Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Gunn-Hilsum Effect in Mechanically Strained Silicon Nanowires: Tunable Negative Differential Resistance


Gunn (or Gunn-Hilsum) Effect and its associated negative differential resistivity (NDR) emanates from transfer of electrons between two different energy subbands. This effect was observed in semiconductors like GaAs which has a direct bandgap of very low effective mass and an indirect subband of high effective mass which lies ~300 meV above the former. In contrast to GaAs, bulk silicon has a very high energy spacing (~1 eV) which renders the initiation of transfer-induced NDR unobservable. Using Density Functional Theory (DFT), semi-empirical 10 orbital (sp3d5s*) Tight Binding and Ensemble Monte Carlo (EMC) methods we show for the first time that (a) Gunn Effect can be induced in silicon nanowires (SiNW) with diameters of 3.1 nm under +3% strain and an electric field of 5000 V/cm, (b) the onset of NDR in the I-V characteristics is reversibly adjustable by strain and (c) strain modulates the resistivity by a factor 2.3 for SiNWs of normal I-V characteristics i.e. those without NDR. These observations are promising for applications of SiNWs in electromechanical sensors and adjustable microwave oscillators. It is noteworthy that the observed NDC is different in principle from Esaki-Diode and Resonant Tunneling Diodes (RTD) in which NDR originates from tunneling effect.


Silicon is predicted to remain as the fundamental material for the micro- and nano-electronics industry and ultra large scale integrated (ULSI) circuits1 despite the ever growing research devoted to other materials and their nano structured variants. Silicon Nanowires (SiNW) are one of the members of silicon nanostructure family, which have so far shown promising applications in areas ranging from biological sensors2, thermoelectric converters3, opto-mechanical devices4, piezoelectric sensors5, and solar cells6 among others. Ease of bandgap conversion from indirect to direct one with crystallography7, mechanical strain8,9,10,11, and alloying bring SiNWs into realm of optical applications e.g. photodetectors12,13,14,15 and light emitters16. In addition, breaking the centro-symmetricity in strained nanowires was shown to enhance the second order nonlinear optical susceptibility suitable for second harmonic or frequency difference (THz) generation applications17,18,19,20. With the advent of new top-down CMOS compatible fabrication methods for silicon nanowires21,22 it is now feasible to build spin-based quantum gates23, spintronic devices24,25,26, MOSFETs with critical dimensions approaching 5 nm or less27,28,29, logic circuits30, memory31 and memristive devices32,33. Readers are referred to refs34,35 for an extensive review of the field. To add more to the list of SiNW applications and functionalities, looking back at differences of bulk silicon and their III-V counterparts is instructive. We have to ask what are the other properties which bulk silicon could not possess and yet they might be achievable in silicon nanowire due to its peculiar band structure and its adjustability?

Our answer to this question was “Gunn (or Gunn-Hilsum) Effect” and in this article we show for the first time that this effect and its associated negative differential resistivity (NDR) is observable in silicon nanowires. The negative differential resistivity which is reduction of current density (j) with an increase in the electric field (E), arises when the scattering rate of electrons by lattice vibrations (phonons) or impurities is enhanced by electric field. Recall that J and E are related as j = σ.E wherein σ is the conductivity tensor. Among these scattering processes the electron transfer mechanism is the one which involves migration of electrons from a low effective mass sub band to another sub band of higher effective mass which is mediated by the momentum of phonons as the field increases. The difference between the energies of these sub bands (ΔE) must be reasonably high e.g. a few k B T to ensure that this upper valley or sub band is yet unpopulated at room temperature for low electric field values. Here K B and T, are Boltzmann constant and the absolute temperature in Kelvin, respectively. On the other hand, ΔE has to be small enough to avoid dielectric breakdown under an intense electric field. Figure 1a shows the band structure of bulk GaAs in which the valley splitting or offset between the energies of Γ and L valleys is about 300 meV. The Γ valley has a very low effective mass (0.0632m0) where m0 is the free mass of electron. For low to moderate electric fields, most electrons are within this sub band (valley) and contribute to large electron mobility (μH ~ 8000 cm2/V.s)36. As populating the L valley with high effective mass (0.55m0) occurs for higher electric fields (>3000 V/cm) along the 111 crystallographic direction, the mobility, and as a result the current, reduces (μL ~ 2500 cm2/V.s) [See Fig. 1b]. This leads to an I-V characteristics or velocity versus electric field as shown in Fig. 1b which has a NDR section. This mechanism of obtaining NDR in general was proposed by Ridley37 and Hlisum38 and later as Ehrenreich experimentally obtained the band structure of GaAs, the search for materials of suitable band structure for this type of NDR has begun39. As the negative differential resistivity of the GaAs (or as it was later called Gunn diode) can compensate the Ohmic loss in electric circuits, it was proposed to be applied in electric oscillators of microwave frequencies (Fig. 1c).

Figure 1

Comparing the band structure of bulk GaAs and Si and NDR-induced oscillation in a Gunn diode. Band structures of (a) Gallium Arsenide with direct bandgap. Direct and indirect sub bands are called Γ and L valley, respectively. The energy offset is 300 meV. (b) Negative Differential Resistance (NDR) for GaAs as a result of velocity drop for electrons which migrated to high effective mass (L) band. The NDR emanated from a large ratio of effective mass of indirect to direct conduction sub band which is about 100 for GaAs. (c) The electric network shows how compensating the loss of an electric LC resonator using a Gunn diode with NDR results in a perpetual oscillation in microwave frequencies. (d) Band structure of bulk silicon with more than 1 eV offset between Γ and Χ valleys which explains why there is no NDR in bulk silicon. (e) The second type of Gunn oscillation (intrinsic) is a result of self-repeating formation of accumulation/depletion sandwich inside the bulk material which moves with saturated drift velocity from cathode to anode.

However, the aforementioned electron transfer mechanism is lacking in bulk silicon, the reason of which is evident by looking at its band structure in Fig. 1d. As it can be seen, the offset between X and Γ sub bands is about 1 eV which mandates a very high voltage to induce NDR. Uniaxial straining of p-type doped silicon was suggested to reduce this energy offset and initiate NDR37. Unaware of the theoretical and experimental investigations of high electric field effect on charge transport in GaAs, J. B. Gunn observed instabilities in the current flowing through a piece of GaAs under high voltage40, the source of which was the same I-V characteristics of Fig. 1b. He observed that when the electric field reaches to a threshold value of 2000–4000 V/cm, the current (drift velocity) of electron drops and an accumulation layer is built up after which there is a depleted region (positively charged) since the electrons left that section with their high speed [See Fig. 1e].

The internal dipolar field of such accumulation/depletion sandwich reduces the total external field and reverts the current back to its original value. After the dipolar region reaches to one end of the device, i.e. moves from cathode and arrives at anode, the voltage across the device increases again, hence the current increases to the point at which the same NDR drop occurs and the procedure repeats itself. This results in an oscillating current around an average DC value [Fig. 1e]. This self-repeating increase and decrease of current can reach up to 12 GHz in frequency depending on the length and doping density. Length and drift velocity of electrons determine the transit time through the sample or the frequency of current oscillation. Oscillations of the same origin were observed in materials like CdTe, GaAs1−xPx, InP and GaSb39. In addition to exploiting this effect as an intrinsic source of microwave oscillations, the resulting NDR in I-V characteristics, can also be used to compensate the Ohmic loss of an electrical resonator (Fig. 1c). The oscillator of this type is called Gunn diode oscillator and is used in microwave applications with frequencies of up to 100 GHz depending on the required output power41.

Motivated by previous theoretical and experimental observations of indirect to direct bandgap conversion in SiNWs due to mechanical strain8,42,43 and the advent of novel nanofabrication methods to put these devices into work5,21,44 we investigated the possibility of observing Gunn-type NDR in SiNWs. In contrast to bulk silicon in which no Gunn Effect was observed under high electric field (below breakdown field), in this article for the first time we show that; (a) Gunn Effect or NDR emerges in narrow [110] SiNWs under tensile strain, (b) The threshold voltage (field) for this NDR emergence is tunable by the strain, i.e., NDR can be inhibited or initiated reversibly, and (c) the conductivity of the SiNWs before NDR occurrence is also tunable by mechanical strain as a result of direct to indirect bandgap conversion and corresponding effective mass change. This leads to a factor of 2.3 change in the resistivity as the SiNW is strained between 0% and −3%. The NDR observed here is different in essence from the NDR which arises in Esaki45,46 as well as Resonant Tunneling Diodes (RTDs)47,48. The abovementioned observations, i.e., (a), (b) and (c), promise application of SiNWs in tunable microwave oscillators and mechanical (force, pressure) sensors. The rest of this article is organized by explaining the computational methods including energy minimization, band structure, and electron-phonon scattering rate calculations, followed by Ensemble Monte Carlo (EMC) simulations. Thereafter, we will discuss the observed results and prospects of an experimental proof-of-concept device.


Energy Minimization and Band structure

Relaxation of the structural energy of SiNWs as well as mechanical strain application are performed using Density Functional Theory (DFT) method as implemented in SIESTA®49. The hydrogen terminated nanowires have [110] crystallographic direction due to their proven relative stability compared to [100] direction50. To avoid the inherent bandgap underestimation in DFT and diameter sensitive many–body GW corrections, the band structure and eigenstates were calculated with 10 orbital (sp3d5s*) Tight Binding (TB) method using the parameters given in ref.51. The TB method has shown success in reproducing the experimental data of the effect of radial strain on the photoluminescence spectra in narrow SiNWs52,53. The resulting unit cell after each minimization step is fed to the next minimization round by increasing or decreasing the unit cell length (a) according to the desired strain amount (ε), i.e., ± as shown in Fig. 2a. During these steps the volume of the unit cell is kept fixed in order to let the desired strain take effect. A detailed EMC simulator was developed that incorporated the four lowest conduction sub bands of the calculated band structure of SiNWs (strained & unstrained), to study the effect of electron-phonon scattering under high electric fields.

Figure 2

Atomic structure of an unstrained 3.1 nm [110] SiNW and corresponding electronic (band) structure. (a) Front view and side view of a 3.1 nm [110] SiNW under no strain. Five unit cells of SiNW are shown in the side view highlighting the canted SiH2 (silicon dihydride) units. (b) Graphical representation of finding secondary states for an electron in sub band 1 (B1) which scatters to sub band 3 (B3) assisted by LA phonons. Ideally the secondary states in B3 (shadowed strip) form a quasi-continuum. In simulation, this is limited by the resolution of discretizing the BZ along kz. (c) The same graphical example for scattering from B1 to all sub bands (B1, B2, B3 and B4) assisted by LO phonons. Here there is a limited number of secondary states with corresponding rates arranged in a table. (d) Band structure of the unstrained nanowire showing a direct bandgap value of Eg = 1.554 eV and an energy offset of ΔE = 131 meV. The first four conduction sub bands (numbered as S1, S2, S3 and S4) are selected to calculate all electron-phonon scattering events required by EMC simulation.

Scattering Rates and Ensemble Monte Carlo (EMC) simulations

The electron-phonon scattering rates were calculated with first order perturbation theory using Fermi’s Golden rule54,55. The total scattering rate for a given state within a Brillouin Zone (BZ) with a wave vector of kz, is written as a sum over all individual scattering rates from this state to available states k′z:

$${W}_{{k}_{z}}=\sum _{{k^{\prime} }_{z}}W({k}_{z},{k^{\prime} }_{z})$$

here, W(kz, k′z) is the scattering rate of an electron from its initial state at kz to a possible final (secondary) state (at k′z). W(kz, k′z) includes both inter- and intra-sub band electron-phonon scattering events. The secondary (final) states corresponding to each initial state are determined by the phonon type. For Longitudinal Acoustic (LA) phonons, all final states lie inside a window of Ez ± EDebye (starting from initial state energy, Ez), and constitute all possible k′z. This is graphically shown in Fig. 2b for an initial state in sub band 1 (B1), with all possible secondary states in sub band 3 (B3) marked by circles. EDebye = 63 meV is the Debye energy or the maximum energy of LA phonons, and within the Debye energy window (shaded strip on Fig. 2b), the secondary states form a quasi-continuum. In practice however, the number of secondary states is limited by the resolution with which the BZ is discretized along kz. For each individual term of equation (1) due to electron-LA phonon scattering, the corresponding rate, i.e., W (kz, k′z), is written as follows:

$$W({k}_{z},{k^{\prime} }_{z})=\frac{{D}_{e}^{2}\,}{8{\pi }^{2}\rho {\hslash }^{3}{v}_{s}^{4}}{\rm{\Delta }}{{E}_{kk^{\prime} }}^{2}{B}_{\pm }(|\pm \frac{{\rm{\Delta }}{E}_{kk^{\prime} }}{\hslash {v}_{s}}|){\rm{\Phi }}({q}_{t},{q}_{z}).$$

here De, ρ and vs are electron deformation potential (De = 9.5 eV), mass density (ρ = 2329 Kg/m3) and velocity of sound in silicon (vs = 9.01 × 105 cm/s), respectively. \({B}_{\pm }(|\tilde{{\boldsymbol{q}}}|)\) is the Bose-Einstein factor of phonons and it is \(1/({e}^{\frac{\hslash {\omega }_{q}}{{K}_{B}T}}-1)\) for absorption and \(1+\frac{1}{({e}^{\frac{\hslash {\omega }_{q}}{{K}_{B}T}}-1)}\) for emission of a phonon, where \(\hslash {\omega }_{{\boldsymbol{q}}}\) is the energy of a phonon with a wave vector of q. Ф is a structural factor involving inter-atomic and intra-atomic matrix elements of terms like \({e}^{-i\tilde{{\boldsymbol{q}}}.({{\boldsymbol{r}}}_{m^{\prime} }-{{\boldsymbol{r}}}_{m})}\), where r is the coordinate of an atom. The indices m and m′ are indices of different atoms within a unit cell. Details of deriving Ф or structure factors is explained in the Supplementary Information and refs56,57. ΔEkk′ is the energy difference between initial and final states, and qt and qz are transversal and longitudinal wave vectors of phonons, respectively. When electron scattering emanates from a Longitudinal Optical (LO) phonon, the secondary states are those which lie exactly above or below the energy of the initial state (at kz) by ELO. Figure 2c depicts an example of finding available secondary states for an electron in B1 which is scattered to all other sub bands including itself (intra-band scattering) assisted by LO phonons. As the optical phonon branch is almost flat and independent of wave vector, then it is possible to assume a dispersion less or flat (i.e., kz independent) line on which all LO phonons have the same energy of ELO = 54 meV. The individual rate in equation (1), W(kz, k′z), for LO phonons is then found by:

$$W({k}_{z},{k^{\prime} }_{z})=\frac{{|{D}_{op}|}^{2}}{8{\pi }^{2}\rho {\omega }_{0}}{\int }_{0}^{{q}_{c}}{\rm{\Phi }}({q}_{t},{q}_{z})d{q}_{t}{B}_{\pm }({E}_{LO}=\hslash {\omega }_{0})\frac{1}{{|\frac{\partial E({k^{\prime} }_{z})}{\partial {q}_{z}}|}_{{k^{\prime} }_{z}={k}_{p}}},$$

here D op is deformation potential of LO phonons for electrons (D op  = 11 × 108 eV/cm), ωo is the maximum phonon frequency of LO phonons or E LO , where ħ is Planck’s constant (ħ = 6.582 × 10−16 eV.s), and q c is the maximum allowable value of phonon transversal component (q t ) within the BZ of bulk silicon which is q c  = 1.9π/a58. The last term in equation (3) is density of states evaluated at each available final state (k p ) into which an electron can scatter. The wave vectors of phonons and electrons are represented by q z and k z , respectively. These quantities satisfy momentum conservation (See Supplementary Information and ref.58). The scattering rates as well as the corresponding final states available after scattering are tabulated according to the index of the secondary sub band as well as the type of scattering, i.e., phonon absorption (ABS) or phonon emission (EM) to be used by EMC code. Figure 2c shows a simple example of such a table.

Within EMC simulation, a uniform electric field along the nanowire axis is applied, and temperature is assumed to be uniform. Initially, electrons are assumed to be distributed uniformly with an equilibrium thermal distribution. As time increase, the evolution of each electron under drift process with multi-phonon scattering is recorded to calculate the electric current in response to the applied voltage (field). At each step of EMC simulation54, electron transport is confined to the first BZ, which is divided into many k z grid points (e.g. 8001 points). Corresponding to each point, electron energy, scattering rates and the available final states after scattering, are all recorded and fed into the EMC code from which (a) the time dependent evolution of electron population at each state within the BZ as well as (b) the velocity-electric field plots of the biased SiNWs, are obtained. Details of EMC can be found in ref.59.

The methodology in this work was once used to predict population inversion in strained silicon nanowires and modulation of electron-hole radiative recombination as a result of bandgap and wave function symmetry change42. Modulation of recombination rates was later confirmed by experimental works in ref.43. Later theoretical works on SiGe nanowires also showed the radiative life times of the same order of magnitude as our method60, which supports the reliability of our approach in predicting the carrier dynamics under the influence of electric field and multi-phonon scattering events.

Results and Discussions

Figure 2a illustrates the front view and side view of a 3.1 nm [110] unstrained silicon nanowire terminated by hydrogen atoms. The top and bottom surfaces of the nanowire show canted silicon dihydride (SiH2) units as a result of energy minimization in SIESTA®. The diameter is defined as the average of long and short diameters. The band structure of the unstrained SiNW is shown in Fig. 2d wherein the energy of electrons is plotted against the quasi momentum or wave vector along the periodic length of the nanowire which is k z . The SiNW in this case shows a direct bandgap, i.e., both conduction band minimum and valence band maximum are at the same value of wave vector on BZ center or Γ point. Four lowest conduction sub bands numbered from 1 to 4 [Fig. 2d] are those which are used in calculation of electron-phonon scattering under high electric field. This is because the rest of the sub bands are more than 5k B T ≈ 125 meV above the first sub band minimum and under moderate electric fields they do not play any significant role in our study. The unstrained nanowire has a direct bandgap of 1.554 eV at BZ center, and there are two indirect sub bands which lie symmetrically at k z  = ±2.67/π and their energy is 131 meV above the direct sub band minimum. We label this energy difference between minima of direct and indirect conduction sub bands as energy offset ΔE as indicated in Fig. 2d.

It was previously observed that applying compressive strain lowers the indirect sub band energy and shifts the direct conduction sub band as these bands are made of bonding and anti-bonding p orbitals, respectively42,9,10. Therefore, by continuing the application of compressive strain, there is a state at which the direct and indirect sub bands change roles and the bandgap becomes indirect. Hence the conduction sub band minimum and the valence sub band maximum are no longer at the same value of wave vector. Here this transition or sub band flip point occurs at −2% strain wherein the direct and indirect conduction sub bands are at the same energy level and ΔE ≈ 0. After this point, e.g., at −3% strain (see Fig. 3a), the bandgap is of indirect type and ΔE = −19 meV. Figure 3b,c depict sub bands 1–4 for unstrained and tensile strained (+3%) SiNWs, respectively. In case of tensile strain, the sub bands respond opposite to the compressive case. Here indirect sub bands experience an upshift in the energy value and direct sub band (at BZ center) experiences a down shift. This results in a higher offset (ΔE = 280 meV) than that of unstrained with ΔE = 131 meV. For narrower silicon nanowire with diameters of 1.7 nm, 2.3 nm, this indirect-to-direct conversion occurs at −5% and −4%, respectively. From the experimental point of view, larger diameters are preferred as they require less amount of compressive strain, i.e., they are less prone to undergo a buckling instability. Hence, we decided to work with a computationally-possible largest diameter and at the same time the experimentally-feasible smallest diameter i.e. 3.1 nm in which direct to indirect bandgap conversion occurs at −3%.

Figure 3

Conduction sub bands and drift velocity of electrons in response to longitudinally applied electric field under three strain values. (a) Four conduction sub bands of a −3% strained 3.1 nm [110] SiNW. The energy offset in this case is ΔE = −19 meV, i.e., the bandgap is of indirect type. Panels (b) and (c) show the same sub bands and their new energy values in response to 0% and + 3% (tensile) strain, respectively. In these cases the offset is ΔE = +131 meV and ΔE = +283 meV, respectively. (d) The drift velocity versus applied longitudinal electric field is a plot proportional to current-voltage characteristics of the device (I-V). Application of tensile strain initiates the current reduction or NDR at Ethreshold = 5 × 105 V/m or 5000 V/cm. The horizontal axis starts at 1 × 10V/m.

The effect of compressive strain in lowering the energy offset (ΔE) may suggest that compressive strain eases the electron transfer from BZ center to the bottom of indirect sub bands with higher effective mass. Hence the onset of negative I-V slope, i.e., a kink in the I-V characteristic could occur at lower values of the electric field. Looking at Fig. 3d suggests otherwise. The plot of velocity (current) versus longitudinal electric field (voltage) shows no sign of kink or negative slope for the SiNWs with small offset, i.e., those at 0% and −3%. This is not unexpected by recalling that at room temperature the heavy indirect (high effective mass) sub band must be empty in order to observe NDR. For 0% and −3% strained nanowires the ratios of indirect to direct populations are \({{\rm{e}}}^{-{\rm{\Delta }}E/{{\rm{k}}}_{{\rm{B}}}{\rm{T}}}={{\rm{e}}}^{+19\text{meV}/25{\rm{meV}}}=2.07\), and \({{\rm{e}}}^{-{\rm{\Delta }}E/{{\rm{k}}}_{{\rm{B}}}{\rm{T}}}={{\rm{e}}}^{-131{\rm{meV}}/25{\rm{meV}}}=0.007\), respectively. Hence indirect sub bands at these strain values are already thermally filled and mask the occurrence of NDR effect.

On the other hand, Fig. 3d shows that as the nanowires become of more direct bandgap type, it is at +3% tensile strain that the sought-for NDR emerges. As the effect of applying tensile strain on the band structure is increasing the energy offset (see Fig. 3c with ΔE = 280 meV), this suggests that the indirect sub band is significantly less populated than those at 0% and −3% (\({{\rm{e}}}^{-{\rm{\Delta }}E/{{\rm{k}}}_{{\rm{B}}}{\rm{T}}}=4.6\times {10}^{-5}\)). After seeing this, now the detailed examination of carrier populations and electron-phonon scattering rates for sub bands is called for.

By examining the carrier populations of each individual sub band (S1, S2, S3 and S4 Fig. 4) we deduced:

Figure 4

Evolution of charge carrier (electron) population with electric field. Sub bands S1, S2, S3 and S4 are shown by blue, red, green and black, respectively. Both in −3% strained nanowire (a) and unstrained one (b), sub band S2 is being emptied into indirect sub band S1, as the small offset value increases the chance of electron scattering between S1 and S2. Hence there is no significant increase of population in sub bands S3 and S4 which are very high above S1 and S2. For a +3% strained SiNW (c), both sub bands S1 and S2 are being emptied and high effective mass S4 is populated significantly.

For a −3% strained nanowire (Fig. 4a), there is no pronounced increase of population in indirect sub bands S3 and S4 (bottom panel) and the populations in sub bands S1 and S2 are changing in unison but with different signs, i.e., as one of them is being filled (S1) the other one (S2) is being depleted. Hence there is carrier transfer from sub band S1 to S2 via all inter-band events for which the scattering rate is around 1–10 psec. In other words, both S1 and S2 are within the Debye energy window, facilitating scattering between them rather than scattering (phonon absorption) to S3 and S4, which are at least 200 meV outside the Debye window.

Observing the same behavior as that of Fig. 4a for carrier populations of unstrained nanowire (Fig. 4b), confirms this interpretation. For unstrained SiNW, the indirect sub band S1 and S2 are again being emptied in favor of filling up direct sub band S1 as the distance from indirect (S1 & S2) minima to indirect (S3 & S4) minima is about 200 meV which makes the phonon absorption events to S3 and S4 less probable.

Consequently for −3% and 0% strained SiNWs no NDR is observed. However recalling Fig. 3d, and comparing I-V plots for the two cases (blue and red) suggests that indirect bandgap nanowires (i.e. −3% strained) have higher resistivity than unstrained SiNW by a factor of 2.3. This is because the indirect sub bands of −3% SiNW are responsible for charge transport and as their effective mass is four times larger than the direct sub band, less mobility or conductivity is expected. Biasing a nanowire with a fixed bias voltage and switching the nanowire between unstrained and compressively strained states will result in a strain sensitive resistor or mechanical force sensor.

Further examination of Fig. 3d reveals that the peak in the velocity-field plot, is shifting to lower electric field values as strain is relaxed from −3% to 0%. Finally, at +3% strain where the offset is maximal, (ΔE = 280 meV), NDR emerges. This is because after the carriers scatter into indirect sub bands (direct S1 & S2 → indirect S1 & S2), they now have a higher probability to scatter into indirect sub bands S3 and S4 which are now closer as opposed to the rest of sub bands i.e. direct S1 & S2, and direct S3 & S4 (See Fig. 4c). The significant increase of population in indirect S3 and S4 (bottom of panel of Fig. 4c) confirms that both S1 and S2 are being emptied (top panel) in favor of transferring carriers to high effective mass indirect S3 and S4 which results in current drop and NDR (see Fig. 3d). Seeing this suggests that increasing the energy offset between direct and indirect sub band leads to reduced backscattering probability for those electrons which travelled to indirect sub bands S1 and S2.

Hence they will have a higher probability to absorb phonons and end up being in indirect S3 and S4 which are of higher effective mass. Figure 5 shows the evolution of electron population within the BZ of +3% strained SiNW. It reveals how the population decays from direct sub bands (around BZ center) by increasing the electric field and migrates to indirect ones with higher effective mass which leads to lower velocity.

Figure 5

Evolution of electron population inside the BZ of a +3% strained SiNW. Increasing the field results in reduction of the population from BZ center and favors the increase of the same quantity in indirect sub bands and further migration to indirect S3 and S4 with higher effective mass. The overall effect is the current (velocity) reduction leading to NDR.

Referring back to the band structures with small energy offset (e.g. ΔE = 131 meV for 0% strain), it is expected that decreasing the temperature helps to increase the population difference and initiating NDR. For example at T = 70 K, \({e}^{-(\Delta {\rm{E}}=131{\rm{meV}})/{{\rm{k}}}_{{\rm{B}}}{\rm{T}}}=1.5\times {10}^{-8}\) . This implies that small energy offset (ΔE) does not preclude the Gunn-Effect provided that the working temperature of the device is lowered. Similar effects were observed for low energy offset InSb and GaSb at T = 77 K39,61. We already observed that decreasing the temperature from 300 K to 70 K drops the direct to indirect electron-phonon scattering rates involving phonon absorption by three orders of magnitude42. This unilaterally fills the low energy sub band and enhances the population difference which is useful for emergence of NDR under high electric fields.

In conclusion there are two main ingredients in order to observe NDR and resulting Gunn Effect in silicon nanowire; (a) A strain dependent band structure in which the sub band energy difference can be controlled by mechanical strain, and (b) Asymmetric electron-phonon scattering channels which work to the benefit of filling up a higher effective mass sub band as the electric field increases. Moreover, mechanical strain gives freedom to tune or change the onset of NDR initiation or the position of the kink in I-V characteristics with respect to the field. For example embedding silicon nanowires on a deformable substrate, deflecting the substrate can change the band structure. Thus the onset of the NDR or Gunn oscillations will be modulated by strain.

Figure 6 sketches such a proposed experiment in which an array of nanowires is mounted on a deformable substrate (e.g. a piezo electrically actuated diaphragm) and biased with a voltage source. In the unstrained state there is no NDR. By deforming the substrate into tensile strain state the onset of oscillations or I-V kink approaches to the desired bias voltage (V threshold ) and Gunn oscillations will ensue. Reversibly this oscillation can be inhibited by returning to zero or compressive strain regime. The sources of mechanical strain are abundant. Also as we have seen before, even in cases where there is no NDR, the resistivity is modulated by more than 100% using strain. Another useful experiment could be bending and unbending a long nanowire similar to those fabricated by43,62, and recording the voltage across the bent sections which are under tensile strain.

Figure 6

A proposed experiment where using mechanical strain initiates or inhibits Gunn oscillations in SiNWs. (a) While the platform is unstrained (Vpiezo = 0 V) there is no NDR for the applied bias voltage VB. (b) When Vpiezo≠ 0 V, the platform is deflected which strains the wires and VB finds itself within the range of NDR, hence Gunn oscillations are initiated. The oscillation frequency is adjustable by either strain (Vpiezo), DC bias voltage or electric field (VB) and values of L and C.

Adding spin degree of freedom to this effect will also lead to a rich playground for physical effects and promising spintronic devices63,64. We speculate that in nanowires with large Spin Orbit Interaction (SOI) e.g. InSb, the combination of electric field65 and mechanical strain will lead to interesting spin-resolved Gunn Effect or oscillations of spin up or spin down currents as they can be initiated under different voltages and strain values (spin resolved Gunn Effect). Alloying SiNWs with germanium is another way of tailoring the band structure and threshold voltage for NDR initiation. The recent techniques of growing SiGe nanowires e.g. in core-shell form are promising44. In addition, it was experimentally observed66 that applying perpendicular magnetic field on bulk InSb samples reduces the Gunn Effect threshold voltage due to Hall Effect. Adding this degree of freedom to the presented theoretical models uncovers new phenomena worth of understanding and consummating to device applications.

In summary using DFT, TB and ensemble Monte Carlo simulations we observed that; firstly, in contrast to bulk silicon, Gunn Effect is observable in [110] SiNWs under tensile strain of 3%. This is the result of a tunable direct bandgap with high energy offset (ΔE) which creates the same mechanism occurring in GaAs, i.e., migration of electrons from low effective mass sub band to indirect high effective mass one as a result of which NDR emerges. Secondly, the value of threshold field to induce Gunn Effect is reversibly adjustable by mechanical strain. Thirdly, direct to indirect bandgap conversion in response to the applied strain causes more than 100% change of resistivity. All the above mentioned observations are promising for more applications of silicon nanowires in the realm of electronic and nano-mechanical devices.


  1. 1.

    Allan, A. et al. More Moore: White Paper, International Roadmap for Devices and Systems (IRDS) 2016, ( (2016).

  2. 2.

    Shen, F. et al. Rapid Flu Diagnosis Using Silicon Nanowire Sensor. Nano Lett. 12, 3722 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  3. 3.

    Hashimoto, S. et al. Anomalous Seebeck coefficient observed in silicon nanowire microthermoelectric generator. Appl. Phys. Lett. 111, 023105 (2017).

    ADS  Article  Google Scholar 

  4. 4.

    Ramos, D. et al. Silicon nanowires: where mechanics and optics meet at the nanoscale. Sci. Rep. 3, 3445 (2013).

    Article  PubMed  PubMed Central  Google Scholar 

  5. 5.

    Lugstein, A., Steinmair, M., Steiger, A., Kosina, H. & Bertagnolli, E. Anomalous Piezoresistance Effect in Ultrastrained Silicon Nanowiresm. Nano Lett. 10, 3204 (2010).

    ADS  CAS  Article  PubMed  Google Scholar 

  6. 6.

    Liu, R. et al. Silicon Nanowire/Polymer Hybrid Solar Cell-Supercapacitor: A Self-Charging Power Unit with a Total Efficiency of 10.5%. Nano Lett. 17, 4240 (2017).

    ADS  CAS  Article  PubMed  Google Scholar 

  7. 7.

    Zianni, X. & Nassiopoulou, A. G. Photoluminescence lifetimes of Si quantum wires. Phys. Rev. B 66, 205323 (2002).

    ADS  Article  Google Scholar 

  8. 8.

    Shiri, D., Kong, Y., Buin, A. K. & Anantram, M. P. Strain induced change of bandgap and effective mass in silicon nanowires. Appl. Phys. Lett. 93, 073114 (2008).

    ADS  Article  Google Scholar 

  9. 9.

    Hong, K.-H., Kim, J., Lee, S.-H. & Shin, J. K. Strain-driven electronic band structure modulation of Si nanowires. Nano Lett. 8, 1335 (2008).

    ADS  CAS  Article  PubMed  Google Scholar 

  10. 10.

    Leu, P. W., Svizhenko, A. & Cho, K. Ab initio calculations of the mechanical and electronic properties of strained Si nanowires. Phys. Rev. B 77, 235305 (2008).

    ADS  Article  Google Scholar 

  11. 11.

    Wu, Z., Neaton, J. B. & Grossman, C. Charge separation via strain in silicon nanowires. Nano Lett. 9, 2418 (2009).

    ADS  CAS  Article  PubMed  Google Scholar 

  12. 12.

    Ahn, Y., Dunning, J. & Park, J. Scanning photocurrent imaging and electronic band studies in silicon nanowire field effect transistors. Nano Lett. 5, 1367 (2005).

    ADS  CAS  Article  PubMed  Google Scholar 

  13. 13.

    Yang, C., Barrelet, C. J., Capasso, F. & Lieber, C. M. Single p-type/Intrinsic/n-type silicon nanowires as nanoscale avalanche photo detectors. Nano Lett. 6, 2929 (2006).

    ADS  CAS  Article  PubMed  Google Scholar 

  14. 14.

    Hayden, O., Agarwal, R. & Lieber, C. M. Nanoscale avalanche photodiodes for highly sensitive and spatially resolved photon detection. Nat. Mater. 5, 352 (2006).

    ADS  CAS  Article  PubMed  Google Scholar 

  15. 15.

    Zhang, A., You, S., Soci, C., Wang, D. & Lo, Y.-H. Planar and Vertical Si Nanowire Photo Detectors, 2008 Conference on Lasers and Electro-Optics and 2008 Conference on Quantum Electronics and Laser Science, San Jose, CA, pp. 1–2 (2008).

  16. 16.

    Fazio, B. et al. Strongly enhanced light trapping in a two-dimensional silicon nanowire random fractal array. Light: Science & Applications volume 5, page e16062 (2016).

  17. 17.

    Jacobsen, R. S. et al. Strained silicon as a new electro-optic material. Nature 441, 199 (2006).

    ADS  CAS  Article  PubMed  Google Scholar 

  18. 18.

    Chmielak, B. et al. Pockels effect based fully integrated, strained silicon electro-optic modulator. Optics Express 19, 17212 (2011).

    ADS  CAS  Article  PubMed  Google Scholar 

  19. 19.

    Cazzanelli, M. et al. Second-harmonic generation in silicon waveguides strained by silicon nitride. Nat. Mater. 11, 148 (2011).

    ADS  CAS  Article  PubMed  Google Scholar 

  20. 20.

    Shiri, D. Ab initio Study of Nonlinear Optical Susceptibilities in Silicon Nanowires ( (2017).

  21. 21.

    Moselund, K. E. et al. Bended Gate-All-Around Nanowire MOSFET: a device with enhanced carrier mobility due to oxidation-induced tensile stress. 2007 IEEE International Electron Devices Meeting, Washington, DC, pp. 191–194, (2007).

  22. 22.

    Pott, V. et al. Fabrication and characterization of gate-all-around silicon nanowires on bulk silicon. IEEE Trans. Nanotechnol. 7, 733 (2008).

    ADS  Article  Google Scholar 

  23. 23.

    De Franceschi, S. et al. SOI platform for spin qubits. 2016 Joint International EUROSOI Workshop and International Conference on Ultimate Integration on Silicon (EUROSOI-ULIS), Vienna, pp. 124–126, (2016).

  24. 24.

    Hu, Y., Kuemmeth, F., Lieber, C. M. & Marcus, C. M. Hole spin relaxation in Ge-Si core-shell nanowire qubits. Nat. Nanotechnol. 7, 47 (2012).

    ADS  CAS  Article  Google Scholar 

  25. 25.

    Higginbotham, A. P. et al. Hole Spin Coherence in a Ge/Si Heterostructure Nanowire. Nano Lett. 14, 3582 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  26. 26.

    Voisin, B. et al. Electrical control of g-factors in a few-hole silicon nanowire MOSFET. Nano Lett. 16, 88 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  27. 27.

    Trivedi, K. et al. Quantum Confinement Induced Performance Enhancement in Sub-5-nm Lithographic Si Nanowire Transistors. Nano Lett. 11, 1412 (2011).

    ADS  CAS  Article  PubMed  Google Scholar 

  28. 28.

    Heinzig, A., Slesazeck, S., Kreup, F., Mikolajick, T. & Weber, W. M. Reconfigurable Silicon Nanowire Transistors. Nano Lett. 12, 119 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  29. 29.

    Mirza, M. M. et al. One dimensional transport in silicon nanowire junction-less field effect transistors. Sci. Rep. 7, 3004 (2017).

    ADS  Article  PubMed  PubMed Central  Google Scholar 

  30. 30.

    Shim, W., Yao, J. & Lieber, C. M. Programmable Resistive-Switch Nanowire Transistor Logic Circuits. Nano Lett. 14, 5430 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  31. 31.

    Li, Q. et al. Silicon nanowire on oxide/nitride/oxide for memory application. Nanotechnol. 18, 235204 (2007).

    ADS  Article  Google Scholar 

  32. 32.

    Sacchetto, D., Ben-Jamaa, M. H., Carrara, S., De Micheli, G. & Leblebici, Y. Memristive devices fabricated with silicon nanowire schottky barrier transistors. Proceedings of 2010 IEEE International Symposium on Circuits and Systems, Paris, pp. 9–12, (2010).

  33. 33.

    Yang, J., Strukov, D. B. & Stewart, D. R. Memristive devices for computing. Nat. Nanotechnol. 8, 13 (2013).

    ADS  CAS  Article  PubMed  Google Scholar 

  34. 34.

    Rurali, R. Colloquium: Structural, electronic, and transport properties of silicon nanowires. Rev. Mod. Phys. 82, 427 (2010).

    ADS  CAS  Article  Google Scholar 

  35. 35.

    Ramanujam, J., Shiri, D. & Verma, A. Silicon Nanowire Growth and Properties: A Review. Mater. Express 1(2), 105 (2011).

    CAS  Article  Google Scholar 

  36. 36.

    Blakemore, J. S. Semiconducting and other major properties of gallium arsenide. J. Appl. Phys. 53, R123 (1982).

    ADS  CAS  Article  Google Scholar 

  37. 37.

    Ridley, B. K. & Watkins, T. B. The Possibility of Negative Resistance Effects in Semiconductors. Proc. Phys. Soc. 78, 293 (1961).

    ADS  Article  Google Scholar 

  38. 38.

    Hilsum, C. Transferred Electron Amplifiers and Oscillators. Proc. IRE 50, 185 (1962).

    Article  Google Scholar 

  39. 39.

    Conwell, E. M. High Field Transport in Semiconductors. Solid State Physics, Supplement 9, (Academic Press, New York 1967).

  40. 40.

    Gunn, J. B. Microwave oscillations of current in III–V semiconductors. Solid State Commun. 1, 88 (1963).

    ADS  Article  Google Scholar 

  41. 41.

    Collin, R. E. Foundations of Microwave Engineering, (McGraw-Hill, New York 1991).

  42. 42.

    Shiri, D., Verma, A., Selvakumar, C. R. & Anantram, M. P. Reversible Modulation of Spontaneous Emission by Strain in Silicon Nanowires. Sci. Rep. 2, 461 (2012).

    ADS  Article  PubMed  PubMed Central  Google Scholar 

  43. 43.

    Grumstrup, E. M. et al. Reversible strain-induced electron–hole recombination in silicon nanowires observed with femto second pump–probe microscopy. Nano Lett. 14, 6287 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  44. 44.

    Dillen, D. C., Wen, F., Kim, K. & Tutuc, E. Coherently Strained Si–SixGe1−x Core–Shell Nanowire Heterostructures. Nano Lett. 16, 392 (2016).

  45. 45.

    Esaki, L. New Phenomenon in Narrow Germanium p–n Junctions. Phys. Rev. 109, 603 (1958).

    ADS  CAS  Article  Google Scholar 

  46. 46.

    Schmid, H., Bessire, C., Björk, M. T., Schenk, A. & Riel, H. Silicon Nanowire Esaki Diodes. Nano Lett. 12, 699 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  47. 47.

    Sollner, T. C. L. G., Goodhue, W. D., Tannenwald, P. E., Parker, C. D. & Peck, D. D. Resonant tunneling through quantum well at frequencies up to 2.5 THz. Appl. Phys. Lett. 43, 588 (1983).

    ADS  CAS  Article  Google Scholar 

  48. 48.

    Kluksdahl, N. C., Kriman, A. M., Ferry, D. K. & Ringhofer, C. Transient switching behavior of the resonant-tunneling diode. IEEE Elect. Dev. Lett. 9, 457 (1988).

  49. 49.

    Soler, J. M. et al. The SIESTA method for ab initio order-N materials simulation. J. Phys.: Condens. Matter. 14, 2745 (2002).

    ADS  CAS  Google Scholar 

  50. 50.

    Ma, D. D. D., Lee, C. S., Au, F. C. K., Tong, S. Y. & Lee, S. T. Small-diameter silicon nanowire surfaces. Science 299, 1874 (2003).

    ADS  CAS  Article  PubMed  Google Scholar 

  51. 51.

    Jancu, J. –M., Scholz, R., Beltram, F. & Bassani, F. Empirical sp3d5s tight-binding calculation for cubic semiconductors: General method and material parameters. Phys. Rev. B 57, 6493 (1998).

    ADS  CAS  Article  Google Scholar 

  52. 52.

    Walavalkar, S. S. et al. Tunable visible and near-IR emission from sub-10 nm etched single-crystal Si nanopillars. Nano Lett. 10, 4423 (2010).

    ADS  CAS  Article  PubMed  Google Scholar 

  53. 53.

    Demichel, O. et al. Quantum confinement effects and strain-induced band-gap energy shifts in core-shell Si-SiO2 nanowires. Phys. Rev. B. 83, 245443 (2011).

    ADS  Article  Google Scholar 

  54. 54.

    Tomizawa, K. Numerical Simulation of Submicron Semiconductor Devices (Artech House, Boston, London, 1993).

  55. 55.

    Leburton, J.-P. Size effects on polar optical phonon scattering of 1‐D and 2‐D electron gas in synthetic semiconductors. J. Appl. Phys. 56, 2850 (1984).

    ADS  CAS  Article  Google Scholar 

  56. 56.

    Shiri, D. Electronic and Optical Properties of Silicon Nanowires: Theory and Modeling, ( (2012).

  57. 57.

    Neophytou, N. & Kosina, H. Atomistic simulations of low-field mobility in Si nanowires: Influence of confinement and orientation. Phys. Rev. B 84, 085313 (2011).

    ADS  Article  Google Scholar 

  58. 58.

    Buin, A. K., Verma, A. & Anantram, M. P. Carrier-phonon interaction in small cross-sectional silicon nanowires. J. Appl. Phys. 104, 053716 (2008).

    ADS  Article  Google Scholar 

  59. 59.

    Verma, A., Buin, A. K. & Anantram, M. P. High-field hole transport in silicon nanowires. J. Appl. Phys. 106, 113713 (2009).

    ADS  Article  Google Scholar 

  60. 60.

    Cartoixà, X. et al. Optical Emission in Hexagonal SiGe Nanowires. Nano Lett. 17, 4753 (2017).

    ADS  Article  PubMed  Google Scholar 

  61. 61.

    Smith, J. E. Jr., Nathan, M. I., McGroddy, J. C., Porowski, S. A. & Paul, W. GUNN EFFECT in n‐TYPE InSb. Appl. Phys. Lett. 15, 242 (1969).

    ADS  CAS  Article  Google Scholar 

  62. 62.

    Ryu, S. Y. et al. Lateral buckling mechanics in silicon nanowires on elastomeric substrates. Nano Lett. 9, 3214 (2009).

    ADS  CAS  Article  PubMed  Google Scholar 

  63. 63.

    Qi, Y., Yu, Z.-G. & Flatte, M. E. Spin Gunn Effect. Phys. Rev. Lett. 96, 026602 (2006).

    ADS  Article  PubMed  Google Scholar 

  64. 64.

    Okamoto, N. et al. Electric control of the spin Hall effect by intervalley transitions. Nat. Mater. 13, 932 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  65. 65.

    Pramanik, S., Bandyopadhyay, S. & Cahay, M. Spin dephasing in quantum wires. Phys. Rev. B 68, 075313 (2003).

    ADS  Article  Google Scholar 

  66. 66.

    Heinrich, H. & Keeler, W. Gunn effect threshold and domain formation in transverse magnetic fields in indium antimonide. Appl. Phys. Lett. 21, 171 (1972).

    ADS  CAS  Article  Google Scholar 

Download references


D.S acknowledges access to the supercomputing facilities provided by Shared Hierarchical Academic Research Computing Network (SHARCNET®) in Ontario, Canada while he was working at University of Waterloo. A.I and D.S acknowledge financial support from Swedish Research Council (Vetenskapsrådet). M.P.A was supported by the National Science Foundation through the Division of Electrical, Communications and Cyber Systems under Grant ECCS-1231927. A.V and R.N acknowledge the Texas Advanced Computing Center (TACC) at The University of Texas at Austin for providing HPC resources that have contributed to the research results reported within this paper.

Author information




D.S. wrote the electron-phonon scattering codes and performed band-structure calculation and energy minimization using DFT and tight binding methods for strained silicon nanowires. D.S. and C.R.S. helped in defining the problem to look for Gunn Effect. A.V. and R.N. performed Ensemble Monte Carlo simulations and calculate I-V characteristics and carrier populations. A.I. and M.P.A. helped in understanding and explaining the results and putting them together for manuscript. All authors helped equally in writing the manuscript.

Corresponding author

Correspondence to Daryoush Shiri.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Shiri, D., Verma, A., Nekovei, R. et al. Gunn-Hilsum Effect in Mechanically Strained Silicon Nanowires: Tunable Negative Differential Resistance. Sci Rep 8, 6273 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing