Abstract
Magneto-optical Faraday effect is widely applied in optical devices and is indispensable for optical communications and advanced information technology. However, the bismuth garnet Bi-YIG is only the Faraday material since 1972. Here we introduce (Fe, FeCo)-(Al-,Y-fluoride) nanogranular films exhibiting giant Faraday effect, 40 times larger than Bi-YIG. These films have a nanocomposite structure, in which nanometer-sized Fe, FeCo ferromagnetic granules are dispersed in a Al,Y-fluoride matrix.
Similar content being viewed by others
Introduction
Optical isolators utilizing Faraday rotation are of importance in many applications, such as quality assurance of optical amplifiers1, optical ring lasers2, and optical communication systems3,4,5. They are highly reliable and important tools to support advanced information technology. An image of Faraday effect is shown in Fig. 1. However, since the discovery of the bismuth garnet Bi-YIG6,7 in 1972, no material with Faraday effect beyond Bi-YIG has been found. Although thin films with a large Faraday angle have been examined to miniaturize optical devices, their properties are inferior to bulk Bi-YIG8,9. Therefore, optical devices are very limited10,11.
Here we introduce (Fe, FeCo)-(Al-, Y-fluoride) nanogranular films exhibiting Faraday rotation 40 times larger than that of Bi-YIG at the wavelength of optical communication band (1500 nm). These films have a nanocomposite structure, in which nanometer-sized Fe or FeCo ferromagnetic granules are dispersed in an Al-,Y-fluoride matrix. Nanogranular materials consisting of nanometer-sized magnetic metal granules and a ceramic insulating matrix exhibit various functional properties depending on the composition ratio of the two elements, granules and matrix12,13,14,15. In addition, since they are easily fabricated and are thermally stable, they have significant practical advantages. For example, the films have been applied in magnetic sensors16,17. A new transparent ferromagnetic material, FeCo-(Al-fluoride) nanogranular structure with a new magneto-optical effect, was recently proposed18. The material is transparent enough even for short wavelengths of light (less than 400 nm) and exhibits 90% transmittance at a wavelength of 1500 nm. Magnetization exceeds 18 kA/m (0.023 T) at room temperature.
Results
Faraday effect and structure of (Fe,FeCo)-(Al-fluoride) films
Figure 2a presents the magnetization curve and optical transmittance of a Fe26Al28F46 film deposited on a glass substrate heated to 660 °C. Magnetization exceeds 387 kA/m (0.49 T) at room temperature. The film is ferromagnetic and transparent. The Faraday loop of this film is depicted in Fig. 2b. The loop was measured with incident light wavelengths of 405, 650 and 1550 nm. The magnetization and the Faraday loop exhibit the same behavior. The Faraday loop at 1550 nm is opposite from those at 405 and 650 nm. Figure 2c shows the relationship between wavelength and Faraday rotation angle. The angle changes from plus to minus around 1200 nm, and the value is 3.4 deg./μm at 405 nm and −0.53 deg./μm at 1550 nm.
Figure 3a presents the high-resolution transmission electron microscope image obtained from the Fe13Co10Al22F55 film deposited on the substrate at 600 °C. The film consists of FeCo magnetic alloy of nanometer-sized granules dispersed in an Al-fluoride matrix. The micrograph has many dark circles with diameters ranging from 10 to 15 nm. In addition, the bright section covers the whole area. The dark circles correspond to FeCo alloy granules, and the bright section indicates the Al-fluoride matrix. The schematic of the nanogranular structure is illustrated in Fig. 3b. When deposited on a heating substrate, the FeCo alloy granules become larger. FeCo granules with diameters 10–20 nm are single domain19 and exhibit ferromagnetism because the granules are larger than the superparamagnetic critical diameter at room temperature20.
Giant Faraday effect of nanogranular films
Wavelength dependence of the Faraday rotation angle of Fe21Co14Y24F41, Fe25Y23F52 and Fe13Co10Al22F55 are presented in Fig. 4a, along with that of bulk Bi-YIG8 for comparison. All the nanogranular films depicted in Fig. 4a have much larger absolute Faraday rotation angles than Bi-YIG. It is noteworthy that the value of the Faraday rotation angle of Bi-YIG decreases with increasing wavelength. The angle in the wavelength of 1310 to 1550 nm, which corresponds to the bands of optical communication, is small in Bi-YIG. In contrast, the nanogranular films exhibit large values in optical communication bands.
Figure 4b indicates the Faraday rotation angles at wavelengths of 405 and 1550 nm as functions of the Fe + Co content in films deposited on substrates of different temperatures. The Faraday rotation angle increases with the Fe + Co content, indicating that the Faraday effect of the nanogranular films is due to the magnetic state of the FeCo granules. In this study, the substrates were heated to give ferromagnetism to the films by controlling the granular size. Depending on the substrate temperature, granular size may change; however, neither ferromagnetic properties nor Faraday rotation angle are affected.
Table 1 lists the Faraday rotation angles in the visible light region (650 nm) and the optical communication band (1550 nm) of the nanogranular films, as well as that of Bi-YIG for comparison. At both wavelengths, the Faraday rotation angles of the nanogranular films are much larger than that of Bi-YIG; for example, the angle of the Fe21Co14Y24F41 film is about 40 times larger than that of Bi-YIG at 1550 nm. This is a great practical advantage. In addition, the nanogranular materials are thin films (less than 1 μm thick). In contrast, Bi-YIG is a bulk material (1 mm thick). Optical devices can be miniaturized and integrated using the thin-film materials.
Nanogranular Fe,FeCo-(Al-,Y-fluoride) films are new Faraday materials. They exhibit much larger Faraday rotation angles than Bi-YIG. The angle is 8.0 deg./μm in the visible light region (650 nm) and −4.0 deg./μm in the optical communication band (1550 nm) in the Fe21Co14Y24F41 film. This value at 1550 nm is 40 times larger than that of Bi-YIG. The Faraday rotation angle of the nanogranular films depends on the wavelength on incident light, and the sign changes at 1000 to 1200 nm.
Mechanism of giant Faraday effects in nanogranular films
First, we calculated the electronic states at Fe/insulator interfaces in density functional theory to clarify the mechanism of giant Faraday effect. In the density functional theory calculation with the WIEN2K package21, we obtain the occupation number nd of 3d orbitals of Fe atoms, spin moment Sz, and orbital moment Lz in Fe-bcc (body-centered cubic) bulk, Fe(001) surface, Fe-2ML with ML being the monolayer, and Fe/insulator interfaces with the insulators being MgO, AlF3 and YF3.
Generalized gradient approximation (GGA) is used with spin-orbit (SO) coupling in the calculation. For bulk Fe and Fe(001) surface, our GGA + SO results are in good agreement with previous calculations22,23. It is clear that the orbital moment of the Fe atom is enhanced at the Fe(001) surface, Fe-2ML, and Fe/insulator interfaces compared with that of bulk.
Fe (Table 2). The supercells of Fe/AlF3 and Fe/YF3 interfaces used in the calculation are depicted in Fig. 5. Enhancement of the orbital moment obtained on 3d transition metal surfaces is similar to that in previous studies22,23. It has been argued that the enhanced orbital moment comes from the reduced coordination of surface atoms, which causes narrower 3d electron bands and higher density of states at the Fermi level23. We use a similar argument for Fe-2ML and Fe/insulator interfaces: the Fe atoms at the interfaces have low-dimensional nature, which causes localized 3d electrons.
Our results suggest that the orbital moment is enhanced in various interfaces and is almost independent of the interfaces. Since the electronic states including the orbital moment are similar between interfaces, in the following Maxwell-Garnett theory the dielectric tensor \({\hat{{\epsilon }}}_{m}(\lambda )\) of magnetic nanogranules is calculated using the density functional theory in the supercell of Fe-2ML as a function of light wavelength λ.
Next, we calculated Faraday rotation angle using the Maxwell-Garnett theory. The Faraday effect is a magneto-optical phenomenon caused by interaction between light and magnetic moment and gives rise to the rotation of light-polarization when a polarized light is transmitted through a magnetic film. The angle of rotation is the Faraday rotation angle given by24
where ϵxx and ϵxy are the diagonal and off-diagonal components of the dielectric tensor, d is the thickness of the magnetic film and λ is the light wavelength. The film thickness in Eq. (1) is fixed to d = 1 μm. In the Maxwell-Garnett theory25 for magnetic nanogranular films with spherical nanogranules dispersed in an insulator matrix, the effective dielectric tensor is given by26,27,28,29
where \({\hat{{\epsilon }}}_{d}\) and \({\hat{{\epsilon }}}_{m}(\lambda )\) are the dielectric tensors of the insulator matrix and magnetic nanogranules, and p m (0 ≤ p m ≤ 1) is the volume fraction of magnetic nanogranules. The Maxwell-Garnett theory is applicable at small p m , since it is assumed that nanogranules are spatially separated. Here, we consider ferromagnetic nanogranules of Fe in a nanogranular film. The values of \({{\epsilon }}_{d}^{xx}=2\) and \({{\epsilon }}_{d}^{xy}=0\) are used for the insulator matrix. For p m = 1, \(\hat{{\epsilon }}(\lambda )\) is reduced to \({\hat{{\epsilon }}}_{m}(\lambda )\) of pure Fe.
For a nanogranular film, it is difficult to obtain \({\hat{{\epsilon }}}_{m}(\lambda )\) by taking into account the modification of electronic structure of granules near the interface. Thus, we assume that \({\hat{{\epsilon }}}_{m}(\lambda )\) is described by the dielectric tensor of Fe-2ML, where the supercell consists of 2-ML Fe and 2-ML vacuum and interfacial Fe atoms. Using \({\hat{{\epsilon }}}_{m}(\lambda )\) of Fe-2ML, we evaluate \(\hat{{\epsilon }}(\lambda )\) in Eq. (2) and obtain θ f . The result for p m = 0.5 is denoted by the blue line in Fig. 6. We find that the sign of θ f changes at long wavelengths λ of 2500 nm.
We also assume that \({\hat{{\epsilon }}}_{m}(\lambda )\) is described by the dielectric tensor of Fe bcc bulk numerically obtained in density functional theory calculation with the Quantum-Espresso package30. The result for p m = 0.5 is denoted by the red line in Fig. 6. Sign change occurs at a long wavelength of λ of 1500 nm.
In Fig. 6, it is clear that the magnitude of the Faraday rotation angle θ f for Fe-2ML is larger than that for Fe-bcc in the whole wavelength range. This result indicates that the larger orbital moment in Fe-2ML gives rises to a larger magnitude of θ f . This result is in qualitative agreement with experimental results for nanogranular films. We note that the electronic states including orbital moment are similar between interfaces as discussed before.
As a result, we conclude that the enhancement of the Faraday effect in magnetic nanogranular films originates from the contribution of interfacial magnetic atoms.
Discussion
We analyzed the mechanism of the giant Faraday angle in nanogranular films. In each nanogranule, the surface/interface produces a main contribution to physical properties, where the orbital magnetic moments of 3d electrons are enhanced31. Orbital magnetic moments are of crucial importance for the Faraday effect, since the off-diagonal component of the dielectric tensor is given by spin-orbit coupling. Using the Maxwell-Garnett theory25, we examined the Faraday rotation angle as a function of the wavelength of light in nanogranular films with 50% volume fraction of Fe granules with dielectric tensors of bulk-Fe and 2 mono-layer-Fe. Here, in 2 mono-layer-Fe, all Fe atoms correspond to surface ones. We found that in nanogranular films with a dielectric tensor of 2-mono-layer-Fe, the Faraday rotation angle is enhanced in the short wavelength region and exhibits a sign change in the long wavelength region. These results explain the experimental data.
Giant Faraday materials were discovered for the first time in 45 years. These materials will contribute greatly to the miniaturization and integration of optical devices.
Methods
Preparation of thin film samples
Thin films were prepared using tandem deposition32 with a conventional RF-sputtering apparatus. The films were 0.3 to 1.0 μm thick. Sputter deposition was performed on a 50 × 50 mm glass substrate (Corning Eagle 2000) at 500 to 700 °C in an argon atmosphere with 1.3 Pa pressure during deposition, using a 76 mm-diameter Fe or Fe60Co40 alloy disk as the metal target and a 76 mm-diameter AlF3 or YF3 powder compacted disk as the insulator ceramics target.
Composition and structural analysis
The composition ratio of Fe,Fe-Co (granule) and Al-,Y-F (matrix) was controlled by changing the RF power applied to each target. The chemical composition of Fe, Co, Al, Y and F in the thin films was analyzed using wavelength dispersion spectroscopy (WDS). For structural analysis, transmission electron microscopy (TEM) was performed on several selected thin films.
Measurements of magnetic properties, optical transmittance and Faraday angle
The magnetization curves were measured using an alternating gradient force magnetometer (AGM). Optical transmittance was measured using Fourier transform infrared spectroscopy (FTIR) with a measurement waveband of 400 to 2000 nm. The incident light is transmitted through the film samples or absorbed. The Faraday angle was measured using six laser light sources (405, 515, 650, 830, 1310 and 1550 nm). The magnetic field was applied from 0 to ± 800 kA/m perpendicular to the film surface of the samples in measurement of magnetization curves and Faraday angle. All measurements were carried out at room temperature.
References
Yadlowsky, J. M., Deliso, M. E. & Da Silva, L. V. Optical fibers and amplifiers for WDM systems. Proc. IEEE 85, 1765–1779 (1997).
Nabors, D. C. et al. Injection locking of a 13-W cw Nd:YAG ring laser. Opt. Lett. 14, 1189–1191 (1989).
Fischer, G. The Faraday optical isolator. J. Opt. Commun. 8, 18–21 (1987).
Žutić, I. & Paulo, E. Semiconductor lasers: Taken for a spin. Nat. Nanotech. 9, 845–850 (2014).
Paulo, E. et al. Toward high-frequency operation of spin lasers. Phys. Rev. B 92, 075311 (2015).
Wittekoek, S., Robertson, M. J., Popma, A. J. T. & Bongers, F. P. Faraday rotation and optical absorption of epitaxial films of Y3-xBixFe5O12. AIP Conf. proc. 10, 1418–1422 (1972).
Takeuchi, S., Ito, I., Mikami, I. & Taniguchi, S. Faraday rotation and optical absorption of a single crystal of bismuth substituted gadolinium iron garnet. J. Appl. Phys. 44, 4789–4790 (1973).
Dionne, F. G. & Allen, A. G. Spectral origins of giant Faraday rotation and ellipticity in Bi-substituted magnetic garnets. J. Appl. Phys. 73, 6127–6129 (1993).
Higuchi, S., Furukawa, Y., Kamada, O., Kitamura, K. & Uyeda, K. Magnetooptical properties of cerium-substituted yttrium iron garnet single crystals for magnetic-field sensor. Sen. Act. A 105, 293–296 (2003).
Bi, L. et al. Magneto-Optical thin films for on-chip monolithic integration of non-reciprocal photonic devices. Materials 6, 5094–5117 (2013).
Bi, L. et al. On-chip optical isolation in monolithically integrated non-reciprocal optical resonators. Nat. Pho. 13, 270 (2011).
Hirohata, A. et al. Roadmap for emerging materials for spintronic device applications. IEEE Trans. Magn. 51, 0800511 (2015).
Kobayashi, N., Masumoto, H., Takahashi, S. & Maekawa, S. Giant dielectric magnetoelectric responses in insulating nanogranular films at room temperature. Nat. Commun. 5, 5417 (2014).
Fujimori, H., Ohnuma, S., Kobayashi, N. & Masumoto, T. Spintronics in metal-insulator nanogranular magnetic thin films. J. Magn. Magn. Mater. 304, 32–35 (2006).
Ohnuma, S., Kobayashi, N., Fujimori, H. & Masumoto, T. Metal-insulator type nano-granular magnetic thin films. J. Phys. Conf. Ser. 191, 012020 (2009).
Kobayashi, N. et al. Enhancement of low-field magnetoresistive response of tunnel-type magnetoresistance in metal-nonmetal granular thin films. J. Magn. Magn. Mater. 188, 30–34 (1998).
Kobayashi, N., Ohnuma, S., Masumoto, T. & Fujimori, H. (Fe-Co)-(Mg-fluoride) insulating nanogranular system with enhanced tunnel-type magnetoresistance. J. Appl. Phys. 90, 4159–4162 (2001).
Kobayashi, N., Masumoto, H., Takahashi, S. & Maekawa, S. Optically transparent ferromagnetic nanogranular films with tunable transmittance. Sci. Rep. 6, 34227 (2016).
Kittel, C. Theory of the Structure of Ferromagnetic Domains in Films and Small Particles. Phys. Rev. 70, 965–971 (1946).
Bean, C. P. & Libingston, D. J. Superparamagnetism. J. Appl. Phys. 30, S120–S129 (1959).
Blaha, P. et al. WIEN2K, An Augmented Plane Wave Plus Local Orbitals Program for Calculating Crystal Properties. (Vienna University of Technology, Vienna, 2001).
Bruno, P. Tight-binding approach to the orbital magnetic moment and magnetocrystalline anisotropy of transition-metal monolayers. Phys. Rev. B 39, 865–868 (1989).
Eriksson, O. et al. Enhanced orbital contribution to surface magnetism in Fe, Co, and Ni. Solid State Commun. 78, 801–806 (1991).
Sato, K. Light and Magnetism, (Asakura, Tokyo, 2001).
Garnett, J. C. M. Colours in metal glasses and in metallic films and in metallic solutions. Proc. R. Soc. A. 76, 370–373 (1905).
Lissberger, H. P. & Saunders, W. P. Optical and magneto-optical properties of thin film cermets. Thin Solid Films 34, 323–333 (1976).
Abe, M. Derivation of nondiagonal effective dielectric-permeability tensors for magnetized granular composites. Phys. Rev. B 53, 7065–7075 (1996).
Zhigalov, S. V. et al. Faraday effect in nanogranular Co-Sm-O films. Phys. Solid State 47, 1129–1133 (2005).
Ozaki, S., Kura, H., Maki, H. & Sato, T. Size effect in magneto-optical properties of Co nanoparticle dispersed systems. Jpn. J. Appl. Phys. 105, 113913 (2009).
Giannozzi, P. et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys.: Condens. Matter 21, 395502 (2009).
Ogata, Y. et al. Enhanced orbital magnetic moment in FeCo nanogranules observed by Barnett effect. J. Magn. Magn. Mater. 442, 329–331 (2017).
Kobayashi, N., Ohnuma, S., Masumoto, T. & Fujimori, H. Tunnel-type magnetoresistance in metal-nonmetal granular films prepared by tandem deposition method. J. Magn. Soc. Jpn 23, 76–78 (1999).
Acknowledgements
The authors are grateful to T. Masumoto and K. I. Arai for valuable discussions. They are indebted to K. Ishida for the sample preparation and to T. Iwasa for the measurement of optical transmittance. This work was supported by Engineering and Grant-in-Aids for Scientific Research (Grant Nos 17H03385, 17H03420, 17H02927, 25247056 and 26103006) from the JSPS.
Author information
Authors and Affiliations
Contributions
The experiments were carried out by N.K. and K.I. The data was discussed by N.K. and H.M. The theoretical model was developed by S.T. and S.M. Calculation based on the theoretical model was conducted by B.G. All authors contributed to the writing and editing of this paper.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Kobayashi, N., Ikeda, K., Gu, B. et al. Giant Faraday Rotation in Metal-Fluoride Nanogranular Films. Sci Rep 8, 4978 (2018). https://doi.org/10.1038/s41598-018-23128-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-23128-5
This article is cited by
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.