Evidence from EXAFS for Different Ta/Ti Site Occupancy in High Critical Current Density Nb3Sn Superconductor Wires


To meet critical current density, J c , targets for the Future Circular Collider (FCC), the planned replacement for the Large Hadron Collider (LHC), the high field performance of Nb3Sn must be improved, but champion J c values have remained static for the last 10 years. Making the A15 phase stoichiometric and enhancing the upper critical field H c2 by Ti or Ta dopants are the standard strategies for enhancing high field performance but detailed recent studies show that even the best modern wires have broad composition ranges. To assess whether further improvement might be possible, we employed Extended X-ray Absorption Fine Structure (EXAFS) to determine the lattice site location of dopants in modern high-performance Nb3Sn strands with J c values amongst the best so far achieved. Although Ti and Ta primarily occupy the Nb sites in the A15 structure, we also find significant Ta occupancy on the Sn site. These findings indicate that the best performing Ti-doped stand is strongly sub-stoichiometric in Sn and that antisite disorder likely explains its high average H c2 behavior. These new results suggest an important role for dopant and antisite disorder in minimizing superconducting property distributions and maximizing high field J c properties.


Nb3Sn superconducting wires are the first choice for magnet applications at fields above 10–11 T, such as NMR spectroscopy, compact cyclotrons, magnetically confined fusion reactors and the next generation of particle accelerators because of their relatively low cost compared to HTS superconductors. In particular, Nb3Sn wires are being used to wind magnets for the Hi-Lumi upgrade of the Large Hadron Collider1,2,3 and they are the most technologically ready candidates for the LHC replacement, the envisioned Future Circular Collider (FCC)4. However, the performance of these wires must be improved to meet the FCC requirements5, so there is an important need to understand the limitations of the best currently produced wires. One area of uncertainty is how close we are to full optimization of the wires because Nb3Sn is in fact a compound with a range of Sn composition and the critical temperature, Tc, upper critical field, Hc2, and critical current density, J c , are all sensitive to the composition, which is never without variation within real wires. In binary Nb3Sn, Tc and Hc2 increase as the ratio of Nb:Sn approaches the stoichiometric value of 36. However, dopants (typically Ti and/or Ta) are required for high field operation. In fact these dopants can raise the Hc2(0) by ~3 T7 (conventionally attributed to additional electron scattering increasing the normal state resistivity and thus Hc2(0))8. For the strand design closest to meeting the FCC critical current target (which uses the “internal-Sn” process), we have previously shown that doping with Ti rather than Ta produces a more homogeneous A15 composition and a tighter distribution of Tc. Furthermore, Ti appears to accelerate the diffusion reaction that creates the A15 phase from its Sn and Nb constituents9. An early EXAFS (Extended X-ray Absorption Fine Structure) study of Ta doped samples10 and an ALCHEMI (Atom Location by Channeling Enhanced Microanalysis) study of both Ti-doped and Ta-doped samples11 using older generation strands indicated that both dopants substitute on the Nb sites. However, more recent studies hypothesized that Ti might substitute on the Sn site12,13. This hypothesis seemed to better fit the normal and superconducting properties of Ti-doped rather than Ta-doped Nb3Sn and their average Sn chemical compositions. In ref.9 we found that the Ti-doped wire had very high J c values (3035 A/mm2 at 12 T and 4.2 K) and a relatively narrow specific heat T c -distribution at 15 T despite measuring only 23.1 at%Sn in the A15 layer. Ti doping on the Nb site would lead to a strongly off-stoichiometric A15, whereas the Flukiger et al.12,13 suggestion of Ti being on the Sn site would lead to a composition much closer to stoichiometry. This apparent inconsistency between studies persuaded us to revisit the early EXAFS study with our modern high-Jc wires with Ta, Ti and Ta + Ti-doping.

The extended x-ray absorption fine structure (EXAFS) is sensitive to the local environment of the dopant atoms. It occurs at x-ray energies above the absorption edge energy of the element under study. Thus, by tuning the x-ray energy to different absorption edges, the local structure of individual elements in a complex material can be determined. In general terms, considering only the dominant single scattering paths, the EXAFS function, χ(k), can be expressed as:

$$\chi (k)=\frac{\mu (k)-{\mu }_{0}(k)}{{\mu }_{0}(k)}=\sum _{j}\frac{{N}_{j}}{k{R}_{j}^{2}}{A}_{j}(k)\sin [2k{R}_{j}+{\psi }_{j}(k)],\quad \quad \quad k=\frac{\sqrt{2{m}_{e}(E-{E}_{0})}}{\hslash }$$

where μ is the x-ray absorption coefficient, μ0 is the smoothly varying absorption of an isolated atom, E0 is the absorption edge energy of the element under study, and k is the wave vector of the photoelectron that is ejected when the absorption edge energy is crossed. The sum is over the local coordination shells of atoms, where N is the number of atoms in the shell, R is the distance from the absorbing atom, ψ(k) is a phase shift term, and A(k) is an overall amplitude factor that includes a Debye-Waller like factor, \({e}^{-2{k}^{2}{\sigma }^{2}}\), where σ2 is a measure of the disorder over the distance R. The disorder can be structural due to a rearrangement of the atoms around the dopant or vibrational due to the natural vibrations of the atoms about their lattice sites. Because each shell of atoms give rise to a distinct frequency, 2kR + ψ, a Fourier transform of the spectrum can be used to separate the contributions of the different shells.

For the Nb3Sn structure there is a distinct difference in the local environment of the two sites. The Nb atoms have three closely spaced nearby coordination shells, while the Sn site has a single nearest neighbor shell (Fig. 1). For a reference sample, we characterized a bulk binary Nb3Sn sample fabricated from just Nb and Sn powders. Table 1 summarizes the parameters for the two sites. Because of the difference in the coordination shells, the EXAFS from the Nb and Sn sites is distinctly different. Figure 1 shows the Fourier transformed spectra from Nb and Sn in pure Nb3Sn. The three closely spaced nearest neighbor shells for the Nb site gives rise to a distinct 3-peak structure in the Fourier transform. These can be well fit using the parameters given in Table 1. In this fitting the number of neighbors N was fixed, and theoretical amplitudes and phase shifts were calculated using FEFF 714. The fitted distances agree well with the crystallographic values15, and the Debye-Waller factors are reasonable. Also, note that the data from the two edges were fit independently. The R and σ2 values for the Nb-Sn and Sn-Nb paths should be the same. Although unconstrained, the close agreement between these two results supports the accuracy of the fitting model.

Figure 1

Fourier transformed k2 weighted EXAFS spectra from the Sn and Nb sites in pure Nb3Sn and sketch of the Nb3Sn structure with the main scattering paths. The blue points and line in the spectra are the data, whereas the green line is a fit to the nearest neighbors using the Nb3Sn structure (the data are not phase corrected). The fitting window was between 1.7 and 3.3 Å for the Nb spectrum and from 1.9 to 3 Å for the Sn spectrum. We also show the Nb3Sn structure schematic showing the three nearby coordination shells for Nb (blue) and a single nearby shell of neighbors for Sn (orange).

Table 1 Parameters for the nearest neighbors in Nb3Sn for the Nb and Sn sites. N and R are from crystallography. The other parameters are a result of fitting the data in Fig. 1 \({{S}}_{0}^{2}\) and E0 are an overall amplitude and energy shift to match the theory to the data14.


Samples and initial characterizations

A binary Nb3Sn bulk sample to serve as a standard was prepared with a nominal 25 at% Sn (see Methods) and the composition was verified by EDS (Energy Dispersive Spectroscopy) to be between 24.3 and 25.3 at.% Sn. The descriptions and basic properties of the wires under investigation are summarized in Table 2. To compare Ti, Ti + Ta and Ta doping, we chose a first series of samples with nominally identical designs but with doping changes only, as detailed by Field Emission Scanning Electron Microscope (FESEM) in Fig. 2(a–d). These strands were of the internal-Sn design (Nb3Sn is formed by diffusion of Sn from central Sn cores to surrounding Nb filaments through a Cu matrix) manufactured by the Restacked Rod Process (RRP®) by Oxford Superconducting Technologies (now Bruker-OST). The 54 internal-Sn sub-elements were hexagonally stacked around 7 Cu blanks inside an outer Cu tube to create the “54/61” multifilamentary composites. In the Ti-doped strand (OST billet #9415-BE), ~2 at% Ti was introduced by inserting 30 Nb-47wt.%Ti rods into the filament packs within each sub-element. This sample is referred to here as Ti#1. For the Ta-doped strand (OST #8781) the filaments and the diffusion barriers were 4 at% Ta instead of pure Nb. The Ta + Ti composite (OST #9362-5) used a combination of the 4 at.% Ta alloy filaments and barrier with 16 Nb-Ti filaments produced a composition of ~1 at.% Ti + 4 at.% Ta. The samples were part of an extensive strain study16 using a common reaction heat treatment (HT) of 40 h at 640 °C. They were slightly underreacted to avoid any Sn diffusion into the stabilizer Cu. In addition, a second similarly made RRP® “108/127” wire series was included: a Ti-doped (Ti#2) and a Ta-doped (Ta#2) wire from our earlier Tc-distribution comparison study9 (OST #14895 and #12879). These samples were heat treated by Arup Ghosh at Brookhaven National Laboratory at 662–665 °C for 48 h and reacted close to their maximum J c as is reflected in the ≈3000 A/mm2 (12 T, 4.2 K) performance. Because of the different heat treatments, the two series show differences in both J c and the extrapolated Kramer field: J c ~ 2620–2870 A/mm2, µ0Hk ~ 22.7–24.6 T for the 54/61 series and J c ~3130–3210 /mm2, µ0Hk ~ 23.8–25.5 T for the 108/127 series (µ0Hk was estimated by the linear extrapolation of the Kramer function f k  = J c 1/2H1/4)17. Noticeable is also the larger Hk of the Ta + Ti strand, despite its inferior J c (12 T) performance when compared with both Ti#1 and Ta#1. For completeness the “54/61” series was analyzed by specific heat to determine the 0–15 T T c -distributions, in the same way that we previously characterized the “108/127” wires9. This characterization is shown in Fig. 3. Besides confirming the results found for the “108/127” series wires (better homogeneity of the Ti-doped sample with respect to the Ta-doped one), reveals that the Ta + Ti strand has a tighter in-field Tc-distribution than both Ta- or Ti-doped samples, despite a quite broad zero-field Tc-distribution. The WHH extrapolations18 of H c2 (0) obtained for all the samples from the Tc-distributions are reported in Table 2 as well. Similarly to Hk, also for H c2 (0) we found a higher value in the double-doped Ta + Ti wire than with Ta#1 and Ti#1.

Table 2 Description and Properties of Wire Samples. The chemical composition was estimated by EDS in the central part of the A15 layer. J c and Hk values are self-field corrected.
Figure 2

FESEM-BSE images and x-ray fluorescence maps of internal-Sn A15 wires. FESEM-BSE image of a 54 sub-element strand overview (a) and individual sub-elements of the Ta#1 (b), Ti#1 (c) and Ti + Ta (d) doped strands. X-ray fluorescence maps from a similar region in sample Ti#2 for Ti (e) and Sn (f) (the apparent high Ti (Sn) composition on the right side of the sub-element is an artifact due to the experiment geometry).

Figure 3

T c -distributions at 0 and 15 T of the A15 phase in differently doped internal-Sn A15 wires. The T c -distributions were obtained analyzing specific heat characterizations of Ti#1, Ti + Ta and Ta#1 doped strands.

EXAFS characterization

Most of the EXAFS measurements were made using the 20-ID-B microprobe station at the Advanced Photon Source19. This provided a 3 µm beam that could be focused onto the narrow Nb3Sn regions in the strands. Figure 2(e,f) shows some examples of fluorescence maps from one of the samples. These were used to select the proper area for the EXAFS measurements (since the core is not fully dense and the incident/emission beams to obtain the maps are at +/− 45° from the surface normal, the apparent high Ti (Sn) composition on the right side of the sub-element is an artifact due to the experiment geometry). The EXAFS set-up is described in the Methods. Supplementary Figures S1 and S2 show the raw χ(k) data measured on the Ta and Ti edges for all samples. The corresponding Fourier transformed data are plotted in Figs 4 and 5. Also shown in these figures are fits to the data limited to the main structure region using the Artemis software20, which allows the dopants to enter either site. Because the fitting range is limited, it was not possible to vary all of the parameters corresponding to the 4 separate scattering paths of the two sites (see Fig. 1). To minimize the variable parameters, there were two main assumptions. First the coordination numbers were assumed to remain the same. The second is the assumption that the distance and Debye Waller factors for the second shell of the Nb site are the same as for the first shell of the Sn site. While strictly correct for the binary sample, it is, however, a reasonable assumption also for the doped compounds. The overall amplitude factor was allowed to vary. It ended up in the range of 0.65 to 0.72 for the three samples containing Ti and about 1.1–1.3 for the Ta samples.

Figure 4

Fourier transforms of the k2 weighted χ(k) data for the Ta L3 edge using the k range 2–11.5. The blue points and line are the data, the green curve is a two-site fit as described in the text, and the red dashed curve is a fit to the Nb site only (fitting window from 1.9 to 3.5 Å; the data are not phase corrected).

Figure 5

Fourier transforms of the k2 weighted χ(k) data for the Ti K edge using the k range 2–12.9. The blue points and line are the data, and the green curve is the fit result for the Nb site (fitting window from 1.8 to 3.3 Å; the data are not phase corrected).

The fitting results for the Ta data are shown in Fig. 4 and the parameters summarized in Table 3. From the transforms, it is obvious that most of the Ta is in the Nb sites (3-peak structure). However, the best fits were obtained with significant Ta occupation of Sn sites (solid green lines): about 30% for Ta#1, 32% for the Ta + Ti and 21% for Ta#2. For comparison these data were also fit with Ta on the Nb site only. These fits are also shown in Fig. 4 (dashed red lines) where it is clear that the single-site fits are inferior.

Table 3 Fitting results for the Ta L3 edge data.

For the Ti samples, the fits are shown in Fig. 5 and summarized in Table 4. Again, the transforms indicate that the Nb site is preferred but, in this case, the Ti occupancy of the Sn site in the two-site fit always refined to 0. Thus, for the Ti doped samples, the EXAFS indicates that Ti sits only on the Nb sites.

Table 4 Fitting results for the Ti K edge data.

Analysis of disorder and correlation to H c2

At the root of our concern for the site occupancy is consideration of whether there might be an effect on H c2 , especially if site disorder could add to the electron scattering that drives up H c2 . Indeed the EXAFS results provide us information useful to correlate the disorder introduced into the A15 phase with the H c2 trend, taking into account the WHH formula \({H}_{c2}(0)=0.69{T}_{c}{d{H}_{c2}/dT|}_{{T}_{c}}\) with \({d{H}_{c2}/dT|}_{{T}_{c}}\propto \gamma {\rho }_{0}\) (where γ and ρ0 are the Sommerfeld constant and the normal state resistivity)18. Since γ is proportional to the density of states N F and ρ0 is proportional to 1/N F τ (with τ being the scattering rate), H c2 can be written as \({H}_{c2}(0)\propto {T}_{c}/\tau \). Moreover, the scattering rate is related to the long-range order (LRO) parameter η by the relation \(1/\tau \propto (1-{\eta }^{2})\)21, so H c2 should follow the relation \({H}_{c2}(0)\propto {T}_{c}(1-{\eta }^{2})\). Before estimating the LRO parameter, we need to clarify what type of disorder is present in the A15 phase. In fact, Table 5 shows that the Nb/Sn ratio estimated by EDS in the A15 layer is off-stoichiometric in all samples. If the dopant occupancy x on the Sn site obtained by EXAFS is taken into account, the resulting ratio (Nb + Ti + (1−x)Ta)/(Sn + xTa) is in most cases even more strongly off-stoichiometry: this is particularly evident in the Ti-doped samples where it exceeds 3.4. This off-stoichiometry implies that the dopants are not the only source of disorder in the A15 structure but either vacancy (i.e. empty site) or antisite (i.e. atom occupying the “wrong” site) disorder has to be considered. By ab initio calculations, Besson et al.22 estimated the defect structure in Nb3Sn finding that it is of antisite nature: in fact, their results indicate that the fraction of defects by vacancies is at least 7 orders of magnitude smaller than by antisite disorder at 1000 K (more than 20 orders of magnitude at 300 K). This means that vacancies are extremely rare in Nb3Sn and that off-stoichiometry occurs by antisite disorder.

Table 5 Composition ratios as obtained by EDS and EDS + EXAFS, site occupancies in the A3B structure taking into account antisite disorder (and exchange antisite for Ta + Ti) and long range order parameters.

For an alloy with two sublattices (as in the case of the A15 structure, A3B) two distinct LRO parameters have to be defined as: \({\eta }_{A}={c}_{A}(A)-{c}_{A}(B)\) and \({\eta }_{B}={c}_{B}(B)-{c}_{B}(A)\) where c k (α) is the fraction of the α sites occupied by the κ element23. The LRO parameter is then defined by the fractional difference between elements siting on the “right” sites and those sitting on the “wrong” sites and in general it varies between 1 (perfectly ordered system) and 0 (a completely disordered system with random site occupancy). With ternary additions (X), as in our case, the LRO is always less than 1, requiring use of the parameters c X (A) and c X (B). To calculate the LRO parameters η Nb and η Sn for our samples we can take into account the global composition determined by EDS (Table 2), the occupancy resulting from the EXAFS (Tables 3 and 4) and we can impose the 3:1 ratio of the A3B structure as being fulfilled by antisite substitutions (following the conclusions of the ref.21 calculations). It is important to notice that this evaluation will underestimate the disorder because disorder induced by antisite exchange (i.e. Nb and Sn atoms exchanging sites) is unknown. Although this contribution might be limited for single doping, it is likely important for the Ta + Ti sample (because Ta and Ti favor opposite antisite disorder in the 54/61 series). In this case, we include a small amount of exchange antisites proportional to the amount of antisites that Ti generates in the Ti-doped samples reduced by the amount of Ta on the Sn sites (Ta on Sn already acts like an exchange antisite). The resulting values are reported in Table 5 (the values in parentheses for the Ta + Ti sample do not include any exchange antisites and they are shown for comparison: clearly, they are incompatible with the high Hc2 of Ta + Ti). In both series, Ta-doped samples are the more ordered (highest η Nb and η Sn values) whereas Ti-doped samples are more disordered than Ta-doped ones. We also found that Ta + Ti sample from the 54/61 series is more disordered than either Ta#1 or the Ti#1.

Due to the complexity of the system (ternary/quaternary phase in a structure with 2 sublattices), in order to test the presence of the H c2 -disorder relationship given by \({H}_{c2}(0)\propto {T}_{c}(1-{\eta }^{2})\), we used an effective η value calculated as the weighted average of η Nb and η Sn . This trend is shown in Fig. 6. Despite the approximations of the disorder estimate, four of the samples follow a linear trend and only the least disordered sample (Ta#1) appears slightly out of trend: this could mean that this sample is not completely in the dirty limit or that its level of disorder has been underestimated.

Figure 6

Comparison between H c2 (0) and disorder-related parameter. H c2 (0) estimated by WHH extrapolation versus Tc(1-η2) where Tc is the critical temperature and η is a weighted average of the long-range order parameters.

Discussion and Conclusions

The drive to higher magnetic field superconducting Nb3Sn magnets for important applications in physics, chemistry and medical devices means that a better understanding of the high-field limitations of doped wires is highly desirable. Our recent studies showed that even the highest J c Nb3Sn strands still suffer from composition gradients that lead to property gradients9. For the HiLumi LHC upgrade, Nb3Sn wires were optimized for 12 T use by not pushing the heat treatment to maximum extent so as to prevent Sn leakage out of the sub-bundles into the surrounding high purity Cu. This involves some compromise to the irreversibility field and H c2 but also has the benefit of maintaining a high grain boundary density essential for strong vortex pinning. However, higher field applications such as the proposed FCC require optimization of J c for fields closer to Hc2 (for the FCC the Nb3Sn target is 16 T) thus shifting the balance towards increasing H c2 24 and making the A15 layer more uniform. Until now it has been thought that the route to this goal requires maximum Sn stoichiometry. However, a full understanding of how Ta and/or Ti dopants act to enhance H c2 was not clear and several contradictory hypotheses remained in play. To clarify the dopant site occupancy, we performed EXAFS characterizations of the highest performance Nb3Sn strands available that surprisingly revealed that Ta atoms not only substitute on the Nb sites but also occupy a significant fraction (~21–32%) of Sn sites in the Nb3Sn, whereas Ti sits only on the Nb site. These findings raise the question whether or not the ability of Ta to occupy either site makes it compete with Sn for the Sn sites, slowing down the Sn diffusion that drives A15 phase conversion and producing Sn gradients at both layer and filament levels as observed in ref.25. On the other hand, the strong preference of Ti for the Nb sites might favorably contribute to the Sn diffusion on its own sites, helping produce a more homogeneous phase with tighter distribution of properties9. The reasons for these site occupancies of the two dopants do not appear to be straightforward, for instance, the atomic radii are similar for all 4 elements and the oxidation states are 5 for Nb and Ta and 4 for Sn and Ti. Ab-initio density functional theory calculations will probably be necessary to provide a better understanding of this behavior and could prove useful in predicting the behavior of other potential dopants. These new insights suggest further studies to understand if and to what extent the choice of heat treatment temperature influences not only the distribution of the Sn but also the dopants distribution. Because of the evident off-stoichiometry of these strands, doping cannot be the only source of disorder in the A15 phase and antisite disorder seems to contribute significantly in increasing H c2 . In particular, the antisite disorder induced by Ti appears more effective than Ta in driving up H c2 . Interestingly, despite the lower 12 T performance, the double-doped (Ta + Ti) sample showed higher Kramer field (Hk) and upper critical field (H c2 ) extrapolations with respect to similar single doped strands. This suggests that double-doped strands should be re-explored for 16–20 T applications, like FCC, re-investigating both the absolute dopant level and the optimal heat treatment.

These considerations and the markedly sub-stoichiometric Sn composition of the best performing Ti-doped internal-Sn strands (layer J c ~5.2 kA/mm2, 4.2 K, 12 T) indicate that further investigation of global and local properties are needed in what will probably always be compositionally inhomogeneous wires. The striking possibility suggested by this site occupancy study, coupled to the compositional and high field specific heat study, is that antisite disorder in Ti-doped wires mitigates degradation of H c2 in the Sn-deficient regions of the wires. We conclude that improvements of J c properties in the >16 T range at 4.2 K are still possible, also perhaps by using longer and higher HT temperatures to make the layers more compositionally uniform (recognizing of course that more effective diffusion barriers must be provided to protect the outer stabilizing Cu too). Although high field J c can also be enhanced by increasing the density and effectiveness of flux pinning sites by decreasing the grain size, adding pinning centers26,27 or introducing point pinning by irradiation28,29, these techniques do not raise H c2 . Thus, consideration of these surprising site disorder results should also be incorporated into any enhanced pinning center approach in order to raise the high field J c .


Nb3Sn bulk sample synthesis

Constituent powders were first densified using a cold isostatic press (CIP) at 40 kpsi and then subjected to two separate heat treatments (HT) in a hot isostatic press (HIP) at 29 kpsi. The first was a two-step HT (650 °C for 16 h +1200 °C for 72 h). The second HT occurred at 1800 °C for 24 h. The composition was verified by EDS (Energy Dispersive Spectroscopy) and confirmed to be between 24.3 and 25.3 at.% Sn.

EXAFS set-up

The EXAFS measurements of the wires using the 20-ID-B microprobe station were done using a Si (111) monochromator with energy resolution ΔE/E of 1.4 × 10−4 in fluorescence mode using a 4-element vortex detector for the Ti K edge, and a bent Laue analyzer for the Ta L3 edge. Since the filaments are surrounded by Cu, the bent Laue analyzer30 was necessary to distinguish the Ta Lα1 line at 8146 eV from the Cu Kα lines near 8040 eV. The Nb3Sn standard was measured at beamline 20-BM also using a Si(111) monochromator. A focused beam of 0.5 mm2 was provided by a toroidal mirror. The measurements were made in fluorescence using a 13-element Ge detector. Since the sample was thick, the results were corrected for self-absorption using the FLUO algorithm31 in the Athena analysis software20. Because of this correction, the \({S}_{0}^{2}\) values in Table 1 may be different from those needed to fit data for pure Nb3Sn measured in transmission mode.


  1. 1.

    Bottura, L., de Rijk, G., Rossi, L. & Todesco, E. Advanced Accelerator Magnets for Upgrading the LHC. IEEE Transactions on Applied Superconductivity 22, 4002008–4002008 (2012).

  2. 2.

    Todesco, E. et al. A First Baseline for the Magnets in the High Luminosity LHC Insertion Regions. IEEE Transactions on Applied Superconductivity 24, 1–5 (2014).

  3. 3.

    Chlachidze, G. et al. Performance of the First Short Model 150-mm-Aperture Nb3Sn Quadrupole MQXFS for the High-Luminosity LHC Upgrade. IEEE Transactions on Applied Superconductivity 27, 1–5 (2017).

  4. 4.

    Van Nugteren, J. et al. Layout Study for the Dipole Magnets of the Future Circular Collider Using Nb-Ti and Nb3Sn. IEEE Transactions on Applied Superconductivity 26, 1–6 (2016).

  5. 5.

    Tommasini, D. et al. The 16 T Dipole Development Program for FCC. IEEE Transactions on Applied Superconductivity 27, 1–5 (2017).

  6. 6.

    Devantay, H., Jorda, J. L., Decroux, M., Muller, J. & Flükiger, R. The physical and structural properties of superconducting A15-type Nb-Sn alloys. Journal of Materials Science 16, 2145–2153 (1981).

  7. 7.

    Suenaga, M., Welch, D. O., Sabatini, R. L., Kammerer, O. F. & Okuda, S. Superconducting critical temperatures, critical magnetic fields, lattice parameters, and chemical compositions of “bulk” pure and alloyed Nb3Sn produced by the bronze process. Journal of Applied Physics 59, 840 (1986).

  8. 8.

    Orlando, T. et al. The role of disorder in maximizing the upper critical field in the Nb-Sn system. IEEE Transactions on Magnetics 17, 368–369 (1981).

  9. 9.

    Tarantini, C., Sung, Z.-H., Lee, P. J., Ghosh, A. K. & Larbalestier, D. C. Significant enhancement of compositional and superconducting homogeneity in Ti rather than Ta-doped Nb3Sn. Applied Physics Letters 108, 042603 (2016).

  10. 10.

    Heald, S. M. & Tranquada, J. M. The Characterization of Cryogenic Materials by X-Ray Absorption Methods. Advances in Cryogenic Engineering Materials 32, 471–478 (1986).

  11. 11.

    Tafto, J., Suenaga, M. & Welch, D. O. Crystal site determination of dilute alloying elements in polycrystalline Nb3Sn superconductors using a transmission electron microscope. Journal of Applied Physics 55, 4330 (1984).

  12. 12.

    Flükiger, R. et al. Optimization of Nb3Sn and MgB2 wires. Superconductor Science and Technology 21, 054015 (2008).

  13. 13.

    Flükiger, R., Uglietti, D., Senatore, C. & Buta, F. Microstructure, composition and critical current density of superconducting Nb3Sn wires. Cryogenics 48, 293–307 (2008).

  14. 14.

    Ankudinov, A. L. & Rehr, J. J. Relativistic calculations of spin-dependent x-ray-absorption spectra. Physical Review B 56, R1712 (1997).

  15. 15.

    Baier, M., Wordel, R., Wagner, F. E., Antonova, T. E. & Antonov, V. E. Mössbauer study of the hydrides of Nb3Me with A15 structure. J. Less-Common Met. 172, 358 (1991).

  16. 16.

    Cheggour, N. et al. Influence of Ti and Ta doping on the irreversible strain limit of ternary Nb3Sn superconducting wires made by the restacked-rod process. Superconductor Science and Technology 23, 052002 (2010).

  17. 17.

    Kramer, E. J. Scaling laws for flux pinning in hard superconductors. J. Appl. Phys. 44, 1360 (1973).

  18. 18.

    Werthamer, N. R., Helfand, E. & Hohenberg, P. C. Temperature and Purity Dependence of the Superconducting Critical Field, H c2 . III. Electron Spin and Spin-Orbital Effects. Physical Review 147, 295 (1966).

  19. 19.

    Heald, S. M., Cross, J. O., Brewe, D. L. & Gordon, R. A. The PNC/XOR X-ray microprobe station at APS sector 20. Nuclear Instruments and Methods in Physics Research Section A: Accelerators, Spectrometers, Detectors and Associated Equipment 582, 215–217 (2007).

  20. 20.

    Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. Journal of Synchrotron Radiation 12, 537–541 (2005).

  21. 21.

    Rossiter, P. L. Long-range order and the electrical resistivity. J. Phys. F: Metal Phys. 10, 1459 (1980).

  22. 22.

    Besson, R., Guyot, S. & Legris, A. Atomic-scale study of diffusion in A15 Nb3Sn. Physical Review B 75, 054105 (2007).

  23. 23.

    Ruban, A. V. & Skriver, H. L. Calculated site substitution in ternary γ′-Ni3Al: temperature and composition effects. Physical Review B 55, 856 (1997).

  24. 24.

    Ochiai, S. & Osamura, K. Influence of grain size and upper critical magnetic field on global pinning force of bronze-processed Nb3Sn compound. Acta metall. 34, 2425 (1986).

  25. 25.

    Tarantini, C., Lee, P. J., Craig, N., Ghosh, A. & Larbalestier, D. C. Examination of the trade-off between intrinsic and extrinsic properties in the optimization of a modern internal tin Nb3Sn conductor. Supercond. Sci. Technol. 27, 065013 (2014).

  26. 26.

    Xu, X., Sumption, M. D. & Peng, X. Internally Oxidized Nb3Sn Strands with Fine Grain Size and High Critical Current Density. Advanced Materials 27, 1346–1350 (2015).

  27. 27.

    Motowidlo, L. R. et al. An intermetallic powder-in-tube approach to increased flux-pinning in Nb3Sn by internal oxidation of Zr. Supercond. Sci. Technol. 31, 014002 (2018).

  28. 28.

    Spina, T. et al. Correlation Between the Number of Displacements Per Atom and After High-Energy Irradiations of Nb3Sn Wires for the HL-LHC. IEEE Transactions on Applied Superconductivity 26, 1–5 (2016).

  29. 29.

    Baumgartner, T. et al. Performance Boost in Industrial Multifilamentary Nb3Sn Wires due to Radiation Induced Pinning Centers. Scientific Reports 5 (2015).

  30. 30.

    Karanfil, C. et al. A bent Laue analyzer detection system for dilute fluorescence XAFS. AIP Conference Proceedings. 521, 178 (2000).

  31. 31.

    Haskel, D. FLUO: Correcting XANES for Self-absorption in Fluorescence Measurements. http://www.aps.anl.gov/haskel/fluo.html (UWXAFS Project, University of Washington, Seattle, 1999).

Download references


RRP® strands were developed under the DOE Conductor Development Program managed by Dan Dietderich of the Lawrence Berkeley National Laboratory and they were provided by the LARP (LHC-Accelerator Research Program) and by Najib Cheggour (NIST- National Institute of Standards and Technology). Sector 20 facilities at the Advanced Photon Source, and research at these facilities, are supported by the US Department of Energy - Basic Energy Sciences, the Canadian Light Source and its funding partners, and the Advanced Photon Source. Use of the Advanced Photon Source, an Office of Science User Facility operated for the U.S. Department of Energy (DOE) Office of Science by Argonne National Laboratory, was supported by the U.S. DOE under Contract No. DE-AC02-06CH11357. This material is based upon work partially supported by the U.S. Department of Energy, Office of Science, Office of High Energy Physics under Award Number DE-SC0012083. A portion of this work was performed at the National High Magnetic Field Laboratory, which is supported by National Science Foundation Cooperative Agreement No. DMR-1157490 and DMR-1644779 and the State of Florida. The authors would like to thank J. Murray Gibson, FAMU/FSU College of Engineering, for fruitful discussions.

Author information

S.M.H. performed EXAFS measurements and analysis. C.T. performed specific heat characterizations and disorder analysis. P.J.L. performed FESEM characterizations. Z.-H.S. performed the EDS chemical analysis. M.D.B. synthetized and performed EDS analysis on the binary sample. A.K.G. reacted the sample and measured the transport properties. C.T., P.J.L. and D.C.L. designed the study. C.T., S.M.H., P.J.L. and D.C.L. prepared the manuscript. All authors discussed the results and implications and commented on the manuscript.

Correspondence to Chiara Tarantini.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Heald, S.M., Tarantini, C., Lee, P.J. et al. Evidence from EXAFS for Different Ta/Ti Site Occupancy in High Critical Current Density Nb3Sn Superconductor Wires. Sci Rep 8, 4798 (2018) doi:10.1038/s41598-018-22924-3

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.