Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Diatom frustules protect DNA from ultraviolet light


The evolutionary causes for generation of nano and microstructured silica by photosynthetic algae are not yet deciphered. Diatoms are single photosynthetic algal cells populating the oceans and waters around the globe. They generate a considerable fraction (20–30%) of all oxygen from photosynthesis, and 45% of total primary production of organic material in the sea. There are more than 100,000 species of diatoms, classified by the shape of the glass cage in which they live, and which they build during algal growth. These glass structures have accumulated for the last 100 million of years, and left rich deposits of nano/microstructured silicon oxide in the form of diatomaceous earth around the globe. Here we show that reflection of ultraviolet light by nanostructured silica can protect the deoxyribonucleic acid (DNA) in the algal cells, and that this may be an evolutionary cause for the formation of glass cages.


Since the time of Ernst Haeckels elegant illustrations of diatoms in his Kunstformen der Natur, the evolutionary causes for the existence of the nanostructured glass cages, frustules, confining diatoms have been discussed1,2,3. Special proteins, the silaffins and cingulins1,4, extract silicates from water and build the frustules along a chitin-based scaffolding network5,6,7 in geometries specific for different species. The open structure allows material transport but with some limitations; therefore, filtering has been suggested as a reason for their existence. It has also been suggested that the frustule gives mechanical protection from predators8; experiments have verified that mechanical strength can be improved9,10.

In more recent times, it was noted that the somewhat periodic 10–100 nm patterns of holes, slits and ribs, are reminiscent of the geometries of photonic bandgap structures. The first simulation to test this hypothesis used the geometry of the centric diatom Coscinodiscus granii to calculate the electromagnetic properties11. Indeed, photonic bandgap effects were found for optical frequencies for propagation in the plane of the frustule. Experimental measurements of the photonic properties of single diatoms are reported12,13,14,15,16,17,18,19,20,21,22 and for collections of diatoms or frustules. The frustules from the genus Coscinodiscus act as lenses focusing light in a small volume at a distance from the frustule, and this volume is constant with changing direction of light illumination20. It has also been noted that the frustules may act as small spectrographs, focusing photons into specific volumes inside the diatom, possibly for absorption in chlorophyll and other chromophores.

Another possibly photonic structure is formed around algae cells in coccolithophores, with microstructures of calcium carbonate forming spherical protective shells, eventually to be used as chalk. Early calculations indicated that reflection of ultraviolet radiation (UVR, 200–400 nm) would be a property in these structures, built from another material and with a related geometry23.

Protection from UVR may be a reason for the evolution of frustules2. Experimental evidence for the harmful effect of UVR on diatom growth is found for many species and conditions24,25,26,27,28, but it is also clear that diatoms can cope with relatively high UVR intensities in natural communities26. The protection against UVR in diatoms include mycosporine-like amino acids absorbing from 280 to 400 nm29, avoidance, antioxidants and repair mechanisms29. A major victim of high UVR exposure is DNA, with absorption in the 200–300 nm range. Repair systems for DNA in the form of photolyases30 driven by blue light, are present in diatoms31,32. The photolyases are found throughout the living world, and have evolved into the circadian sensor for higher organisms.

The periodic and quasi-periodic patterns of the diatom frustules diffract and refract UVR. DNA is damaged by exposure to UVR. We propose that a major function of the silica frustules is to protect DNA in the algal cell from UVR. To prove this hypothesis, we have carried out experimental optical studies of diatom frustules as well as electromagnetic simulations of simplified geometry models. We have used microscopy and spectroscopy in the near and far field, to characterize the interaction of UV light between 250 to 400 nm, with the diatom frustules. Finite element simulations were used to determine the electromagnetic field distribution and Poynting vector after the interaction of UVR with frustules. In our experiments we have used four diatom species; Navicula perminuta Grunow (NP), Nitzschia sp. (N), Coscinodiscus wailesii Gran & Angst (CW) and Coscinodiscus cf. radiatus Ehrenberg (CR). These species develop distinctive frustule geometries. The general classification, based on the frustule geometry, divide diatoms into two groups of pennate or centric diatoms. NP and N are pennate, and CW and CR are centric.

Results and Discussions

Scanning electron microscopy (SEM) images of single frustules from NP, CW and CR (Fig. 1) show a periodic arrangement of pores. The single layer structure of the NP frustules is decorated with asymmetric pores (Fig. 1d) arranged with bilateral symmetry (Fig. 1a). The size of the NP frustules is ≈10 µm apical and ≈5 µm transapical axis, respectively. The frustules of CW and CR show pores distributed with radial symmetry (at large scale) (Fig. 1b,c) with an almost perfect hexagonal arrangement (small scale) (Fig. 1e,f). Both centric diatoms exhibit more complex structures, compared with the pennate species, with a superposition of three layers with different pore sizes. The inner layer (foramen) include pores of diameter ≈1.4 µm placed in a hexagonal pattern. Above the foramen is the cribrum, with pores sizes ≈0.35 µm (CW) and ≈0.15 µm (CR). A third layer can be found on top of the cribrum containing a less well defined pattern of pores (cribellum); in pennate diatoms this is labeled the hymen (0.005–0.010 µm). For further insight into the terminology see1.

Figure 1

SEM images of (a,d)- Navicula perminuta, (b,e) Coscinodiscus wailesii and (c,f) Coscinodiscus cf. radiatus. Inset shows the Fourier transform for each geometry. Dashed rectangles in (ac) correspond to the magnified areas in (df).

The hierarchical structure of multilevel pores in the diatom frustules can be simplified with a structure with one layer, for NP, or two layers (for CW and CR), with different pore sizes, and excluding the extremely thin hymen. The pore size and wavelengths are the most relevant parameter for scattering of incident light. The finite element method was used to solve Maxwell’s equations in the frequency domain to obtain the electromagnetic field distribution and the energy flow in the UVR range (Supplemental Information (SI)).

Experiments with microscopy and spectroscopy give evidence for the UVR photon flux in the near-field region close to frustules. Reflection of UVR from a monolayer of frustules (Fig. 2a) demonstrates that frustules redistribute UVR in the far field. Images of NP monolayers on a glass (SiO2) substrate were recorded under illumination of a UVR source (360 nm) with a UVR camera (removing all visible light) (Fig. 2a); for comparison, the reflectance image was also recorded in the visible range (Fig. 2b). SEM images of the NP monolayer verify a dense pattern (Fig. 2c–f). Measurements of NP and N monolayer transmittance and reflectance are found in SI.

Figure 2

Pictures under (a) UVR and (b) visible illumination of Navicula perminuta monolayer on a glass slide taken in reflection mode. (c,d,e,f) SEM images of a NP monolayer at different magnifications. Scale bars in (a) and (b) correspond to 1 cm.

The optical measurements and simulations indicate that scattering and reflection of UVR by frustules is relevant in air. With water as the internal medium of the diatoms, the difference of refractive index of the two optical media is much smaller, and the scattering and reflection effects must be smaller.

The near field UVR shielding effect of frustules in air was visualized using a positive photoresist (SI). Frustules of the three species, NP, CW and CR, were dispersed on top of the photoresist layer and illuminated by a 405 nm light source for 10 s seconds, followed by development of resist. In this experiment, the amount of material removed will be proportional to the number of photons, and therefore the shielding effect due to frustules is directly visualized by the remaining photoresist. The surface morphology, after washing off the NP frustules, is imaged in SEM (Fig. 3). The strong light scattering from the frustule structures prevented the direct projection of the hole pattern on the photoresist. For frustules from centric diatoms CW (Fig. 3b,e) and CR (Fig. 3c,f), a clear difference compared with the pennate frustules was noticed. Remaining features correlated with the hole pattern, a frustule’s shadow, was observed.

Figure 3

SEM images of a layer of a positive photoresist cured by a 405 nm excitation (fluorescence microscope line). Morphological detail of the area covered by a single frustule of (a), (d)- Navicula perminuta, (b), (e) Coscinodiscus wailesii and (c), (f) Coscinodiscus cf. radiatus.

The shielding effect from the diatom frustules are demonstrated when the frustules are placed between a UVR source and a UVR sensitive material. PEDOT:PSS, a widely used semitransparent organic conducting material, of relevance in organic solar cells was used. In the presence of oxygen, it is prone to UVR degradation due to overoxidation33, causing bleaching of the film and a decrease in conductivity. When exposing a PEDOT:PSS film to UVR through frustules spread onto the film, the frustules suppressed photobleaching of PEDOT (Fig. S4).

Fluorescence microscopy was used together with a luminescent layer to visualize the energy redistribution by light scattering of the frustules. Frustules from NP, CW and CR were placed on top of an optically transparent PDMS layer stained with a phosphorescent Eu complex emitting at 600 nm. The layers were illuminated by monochromatic UVR (300 nm) in a fluorescence microscope with inverted configuration. The UVR was blocked with an integrated band pass filter. As a result, only the visible emission from the illuminated PDMS layer is detected. The emission intensity is proportional to the number of photons absorbed in the phosphorescent complex, and a uniform distribution of Eu emitters and a constant quantum yield in the PDMS layer was assumed. The image of CW frustules in transmission mode, illuminated by white light and with no filters in the optical path (Fig. 4b), is compared with the image generated by UVR in the same area (Fig. 4e), detecting only the emission of the Eu dispersed in the PDMS layer. The frustules on the film have either face-up or face-down position. With frustules in face-up position, the PDMS layer (n = 1.5 at 300 nm) and the SiO2 structure (n = 1.4878 at 300 nm) form close optical contact. This matching of refractive indexes gives strong light coupling, detected as a bright structure; this is because light is extracted from the guided wave in the PDMS slab beneath. This light dominates the emission from the emitter beneath the frustule. For frustules facing down, the contact area is limited to the perimeter of the frustule and light coupling is reduced. In this geometry a darker area beneath the frustule is observed (marked area), indicating that UV photons do not reach the phosphorescent compound. The inset in Fig. 4e shows the intensity profile along the white line, where inside/outside areas show lower/higher intensities, respectively.

Figure 4

(a) Schematic representation of the emissive layer experimental setup, (b) light source spectrum, (c) transmittance spectrum for the short pass filter, (d) Eu complex excitation (black line) and emission (red line) spectra. Microscopic image of the emission of the Eu layer under different frustule geometries (e) and (h) Navicula perminuta (f) and (i), Coscinodiscus wailesii, (g) and (j), Coscinodiscus cf. radiatus. Insets in (i) and (j) correspond to the intensity values in a.u. measured over the white lines. (eg) Images in transmission mode, (hj) images of the emission of the Eu layer under the frustules, after monochromatic conversion and contrast digitally enhanced. Scales bars in (ej) correspond to 200 µm.

Similar images were obtained for CR (Fig. 4g,j), where a similar interpretation can be applied. For the very small Navicula (Fig. 4e), frustules always outcouple light due to their small dimensions and high curvature; we cannot resolve UVR shadowing in this image.


We suggest that the redistribution of UVR due to SiO2 frustules is an important evolutionary cause of the presence and evolution of frustules in diatoms, by decreasing the rate of UVR-induced degradation of DNA inside the cells. This will improve the energy budget for the photosynthesizing cell, as well as reduce mutations. These weak effects may be sufficient to help explain the surprising number of different diatom species with varying geometries generated by convergent evolution.


  1. 1.

    Round, F. E., Crawford, R. M. & Mann, D. G. The Diatoms - Biology & Morphology of the genera. (Cambridge University Press, 1990, 2000).

  2. 2.

    Ellegaard, M. et al. The fascinating diatom frustule—can it play a role for attenuation of UV radiation? Journal of Applied Phycology 28, 3295–3306, (2016).

    Article  Google Scholar 

  3. 3.

    De Tommasi, E., Gielis, J. & Rogato, A. Diatom Frustule Morphogenesis and Function: a Multidisciplinary Survey. Mar Genomics 35, 1–18, (2017).

    Article  PubMed  Google Scholar 

  4. 4.

    Scheffel, A., Poulsen, N., Shian, S. & Kroger, N. Nanopatterned protein microrings from a diatom that direct silica morphogenesis. Proc Natl Acad Sci USA 108, 3175–3180, (2011).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  5. 5.

    Romann, J. et al. Diatom frustules as a biomaterial: effects of chemical treatment on organic material removal and mechanical properties in cleaned frustules from two Coscinodiscus species. Journal of Porous Materials 23, 905–910, (2016).

    CAS  Article  Google Scholar 

  6. 6.

    Brunner, E. et al. Chitin-based organic networks: an integral part of cell wall biosilica in the diatom Thalassiosira pseudonana. Angew Chem Int Ed Engl 48, 9724–9727, (2009).

    CAS  Article  PubMed  Google Scholar 

  7. 7.

    Tesson, B. et al. Contribution of multi-nuclear solid state NMR to the characterization of the Thalassiosira pseudonana diatom cell wall. Anal Bioanal Chem 390, 1889–1898, (2008).

    CAS  Article  PubMed  Google Scholar 

  8. 8.

    Hamm, C. E. et al. Architecture and material properties of diatom shells provide effective mechanical protection. Nature 421, 841–843, (2003).

    ADS  CAS  Article  PubMed  Google Scholar 

  9. 9.

    Lu, J., Sun, C. & Wang, Q. J. Mechanical Simulation of a Diatom Frustule Structure. Journal of Bionic Engineering 12, 98–108, (2015).

    ADS  Article  Google Scholar 

  10. 10.

    Aitken, Z. H., Luo, S., Reynolds, S. N., Thaulow, C. & Greer, J. R. Microstructure provides insights into evolutionary design and resilience of Coscinodiscus sp. frustule. Proc Natl Acad Sci USA 113, 2017–2022, (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  11. 11.

    Fuhrmann, T., Landwehr, S., El Rharbi-Kucki, M. & Sumper, M. Diatoms as living photonic crystals. Applied Physics B-Lasers and Optics 78, 257–260, (2004).

    ADS  CAS  Article  Google Scholar 

  12. 12.

    De Stefano, L., Rea, I., Rendina, I., De Stefano, M. & Moretti, L. Lensless light focusing with the centric marine diatom Coscinodiscus walesii. Opt Express 15, 18082–18088, (2007).

    ADS  Article  PubMed  Google Scholar 

  13. 13.

    De Tommasi, E. et al. In Micro-Optics 2008Vol. 6992 Proceedings ofSPIE (eds H. Thienpont, P. VanDaele, J. Mohr, & M. R. Taghizadeh) (2008).

  14. 14.

    Noyes, J., Sumper, M. & Vukusic, P. Light manipulation in a marine diatom. Journal of Materials Research 23, 3229–3235, (2008).

    ADS  CAS  Article  Google Scholar 

  15. 15.

    Yamanaka, S. et al. Optical properties of diatom silica frustule with special reference to blue light. Journal of Applied Physics 103, (2008).

  16. 16.

    De Tommasi, E. et al. Multi-wavelength study of light transmitted through a single marine centric diatom. Opt Express 18, 12203–12212, (2010).

    ADS  Article  PubMed  Google Scholar 

  17. 17.

    De Tommasi, E. et al. InNature of Light: Light in Nature Iii Vol. 7782 Proceedings ofSPIE (eds K. Creath & J. A. Shaw) (2010).

  18. 18.

    Kieu, K. et al. Structure-based optical filtering by the silica microshell of the centric marine diatom Coscinodiscus wailesii. Opt Express 22, 15992–15999, (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  19. 19.

    Maibohm, C., Friis, S. M., Ellegaard, M. & Rottwitt, K. Interference patterns and extinction ratio of the diatom Coscinodiscus granii. Opt Express 23, 9543–9548, (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  20. 20.

    Romann, J. et al. Wavelength and orientation dependent capture of light by diatom frustule nanostructures. Sci Rep 5, 17403, (2015).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  21. 21.

    Romann, J., Valmalette, J. C., Royset, A. & Einarsrud, M. A. Optical properties of single diatom frustules revealed by confocal microspectroscopy. Opt Lett 40, 740–743, (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  22. 22.

    Yoneda, S., Ito, F., Yamanaka, S. & Usami, H. Optical properties of nanoporous silica frustules of a diatom determined using a 10 mu m microfiber probe. Japanese Journal of Applied Physics 55, (2016).

  23. 23.

    Aragón, J. L., Torres, M., Estrada, M. & Cros, L. Strong far-field coherent scattering of ultraviolet radiation by holococcolithophores. Physical Review E 74, 032901 (2006).

    ADS  Google Scholar 

  24. 24.

    Karentz, D., Cleaver, J. E. & Mitchell, D. L. Cell-Survival Characteristics and Molecular Responses of Antarctic Phytoplankton to Ultraviolet-B Radiation. Journal of Phycology 27, 326–341, (1991).

    CAS  Article  Google Scholar 

  25. 25.

    Wulff, A., Zacher, K., Hanelt, D., Al-Handal, A. & Wiencke, C. UV radiation - a threat to Antarctic benthic marine diatoms? Antarctic Science 20, 13–20, (2008).

    ADS  Article  Google Scholar 

  26. 26.

    Karsten, U. et al. Physiological responses of polar benthic algae to ultraviolet radiation. Botanica Marina 52, 639–654, (2009).

    CAS  Article  Google Scholar 

  27. 27.

    Piiparinen, J. & Kuosa, H. Impact of UVA radiation on algae and bacteria in Baltic Sea ice. Aquatic Microbial Ecology 63, 75–87, (2011).

    Article  Google Scholar 

  28. 28.

    Beardall, J., Stojkovic, S. & Gao, K. S. Interactive effects of nutrient supply and other environmental factors on the sensitivity of marine primary producers to ultraviolet radiation: implications for the impacts of global change. Aquatic Biology 22, 5–23, (2014).

    Article  Google Scholar 

  29. 29.

    Karentz, D. In Marine Chemical Ecology. (eds JB. Mc Clintock & BJ Baker) (CRC Press, Birmingham, 2001).

  30. 30.

    Sancar, A. Mechanisms of DNA Repair by Photolyase and Excision Nuclease (Nobel Lecture). Angew Chem Int Ed Engl 55, 8502–8527, (2016).

    CAS  Article  PubMed  Google Scholar 

  31. 31.

    Coesel, S. et al. Diatom PtCPF1 is a new cryptochrome/photolyase family member with DNA repair and transcription regulation activity. EMBO Rep 10, 655–661, (2009).

    CAS  Article  PubMed  PubMed Central  Google Scholar 

  32. 32.

    Oliveri, P. et al. The Cryptochrome/Photolyase Family in aquatic organisms. Mar Genomics 14, 23–37, (2014).

    Article  PubMed  Google Scholar 

  33. 33.

    Elschner, A. The spectral sensitivity of PEDOT:PSS films. Solar Energy Materials and Solar Cells 95, 1333–1338, (2011).

    CAS  Article  Google Scholar 

Download references


This work was financed by a Wallenberg Scholar grant to O.I. from the Knut and Alice Wallenberg foundation, and from the J Gustaf Richert foundation. We acknowledge discussions with H. Arwin.

Author information




L.E.A. did all optical and optical microscopy measurements, electromagnetic simulations, frustule manipulation and wrote parts of the paper, L.O. did chemical synthesis of phosphorescent emitter, diatom/frustule preparation and SEM, A.E. did photoresist experiments and SEM microscopy, M.H. cultivated diatoms; all authors participated in data interpretation and writing. A.W. and O.I. coordinated and initiated the project.

Corresponding author

Correspondence to Olle Inganäs.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Aguirre, L.E., Ouyang, L., Elfwing, A. et al. Diatom frustules protect DNA from ultraviolet light. Sci Rep 8, 5138 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing