Article | Open

Engineered nonlinear materials using gold nanoantenna array

  • Scientific Reportsvolume 8, Article number: 780 (2018)
  • doi:10.1038/s41598-017-19066-3
  • Download Citation
Published online:


Gold dipole nanoantennas embedded in an organic molecular film provide strong local electromagnetic fields to enhance both the nonlinear refractive index (n2) and two-photon absorption (2PA) of the molecules. An enhancement of 53× for 2PA and 140× for nonlinear refraction is observed for BDPAS (4,4′-bis(diphenylamino)stilbene) at 600 nm with only 3.7% of gold volume fraction. The complex value of the third-order susceptibility enhancement results in a sign change of n2 for the effective composite material relative to the pure BDPAS film. This complex nature of the enhancement and the tunability of the nanoantenna resonance allow for engineering the effective nonlinear response of the composite film.


Nanoantennas have gathered great attention due to their strong, frequency tunable, electromagnetic field enhancement1. These large local fields enable many applications in near-field optics, nonlinear optics2, and fluorescence research3,4. Although plasmonic nanoparticles have been employed to enhance nonlinear absorption5,6, two-photon absorption (2PA) enhancement in those cases was mainly detected using two-photon excited luminescence, which is not the same as obtaining observable nonlinear absorption in transmission for the composite material7,8. This is because transmission measurements include contributions from both the loss due to the metal nanoparticles and the enhanced absorption of the molecules. Furthermore, the field enhancement is a complex quantity, which cross-couples nonlinear absorption and refraction.

Note, that nonlinear response enhancement due to the intrinsic nonlinearity of plasmonic nanoantennas has previously been explored in some detail but still attracts great interest. These include studies on nanoparticle size-dependence of the nonlinear response9,10,11,12,13, from atomic clusters to plasmonic nanocrystals of Ag and Au14,15,16,17, optical Kerr-effect, inverse Faraday effect and nonlinear optical activity for metal nanoparticles and aggregates18,19, enhancing nonlinearity by using metasurfaces and metamaterial structures20, theory on figure-of-merit for nonlinear response21, core-shell for enhanced second-harmonic22, metasurface defined with e-beam lithography of α-Si:H nanorods for ultrafast spectral and polarization switching23.

However, the enhancement of the “external” material nonlinearity caused by nanoantennas is less well studied. This paper considers nanoantentennas as a pair of nanoparticles, which allows tunability of the plasmon resonance by changing the particle geometry and/or gap size. The nanoantenna array quality requires e-beam lithography defined fabrication and the ability to resist laser damage at high powers.

The effective third-order susceptibility of a metal dielectric composite, in the simplest case24,25, is a product of two complex values: the enhancement factor and the third-order susceptibility of the component materials, which are both wavelength dependent. Therefore, one can engineer an effective nonlinear material by matching the nanoantenna resonance and the wavelength dependence of the susceptibility.

In this paper we describe the use of a gold nanoantenna array to enhance both the nonlinear refractive index (n2) and 2PA of the organic dye 4,4′-bis(diphenylamino)stilbene (BDPAS), which is known as a dye with relatively large 2PA26,27,28. Experimental results show a 53× enhancement for the effective nonlinear absorption, α2, of the composite layer at 600 nm, as supported by 3D finite element method (FEM) numerical simulations. The measured effective nonlinear refractive index, n2, is enhanced by a factor of 140 relative to a BDPAS layer of the same thickness. This is achieved with only 3.7% of gold volume fraction. The numerical simulations show that only 60 nm (the nanoantenna’s height) out of 175 nm of the BDPAS layer participates in the enhancement. Thus, the realistic enhancement of both the n2 and α2 is almost 3× larger.

Results and Discussions

BDPAS has a strong one-photon absorption cross-section, 2.0 × 10−16 cm2, at 390 nm27, and negligible linear absorption in the visible. BDPAS has 42 π-conjugated bonds and exhibits strong 2PA from 600 nm to 800 nm, with a peak 2PA cross section of δ = 320 GM (1 GM = 10−50 cm4s/photon) in dichloromethane (DCM) at 670 nm27,28. The dimensions of the gold nanoantennas shown in Fig. 1(a) (66 nm diameter, 60 nm height (including the 5 nm Ti layer), an antenna gap of 14 nm, and with an array periodicity of 250 nm) were designed so that the resonance wavelength (λ r ) is close to the 2PA cross section peak of BDPAS.

Figure 1
Figure 1

(a) A schematic, h D , h N , h C , g, r = 175, 60, 20, 14, 66 nm respectively, and SEM image of the gold nanoantenna structure.

We demonstrate 2PA enhancement using an array of gold nanoantennas on an indium-tin-oxide (ITO) coated glass substrate coated with a layer of BDPAS by the thermal evaporation in a vacuum chamber. Since the localized field enhancement caused by nanoantennas typically has a range on the order of the nanoantenna thickness, a thin BDPAS film is sufficient to take advantage of nanoantenna enhancement. Our simulations show that 60 nm thickness is enough for the geometry used. The gold nanoantennas are fabricated using electron-beam lithography, as described in the Methods section, to produce larger grain sizes and a lower loss factor, resulting in a stronger plasmonic resonance and larger local electromagnetic fields29. A 175 nm BDPAS film with large molecular density of N = 1.4 × 1021 cm−330, is covered using the thermal evaporation method by a 20 nm layer of silica to protect the sample. The linear refractive index of the BDPAS film is approximately n0 = 1.8 at wavelengths longer than λ = 500 nm, as determined by spectroscopic ellipsometry. Figure 1(b) shows transmission spectra for the BDPAS film, and the film on nanoantennas at both the primary resonance polarization (X) with the incident E-field across the gap, and for the secondary polarization (Y). The transmission spectra show that the resonance wavelength, λ r , of these gold nanoantennas coated with a BDPAS film is 665 nm for X polarization and 630 nm for Y polarization.

Open- and closed-aperture Z-scan measurements were used to measure the film’s nonlinear index of refraction (n2) and the nonlinear absorption coefficient (α2) for the primary X polarization (see Methods section). Introduction of the nanoantennas in the BDPAS film results in a noticeable contribution of the nonlinear reflection in the nonlinear transmission. We show below that the effect of reflection can be taken into account using the n2 obtained from the closed-aperture Z-scan in transmission. Relative to the usual method31, we take into account transmission through the interfaces of the nonlinear slab to retrieve α2 from the experimental results shown in Fig. 2a. Note that interface transmission does not change the wave phase, thus n2 is retrieved in the usual way31. The BDPAS film and film on nanoantennas (indicated herein using subscripts F and N respectively) were measured at 600 nm and 650 nm. The strong nanoantenna resonance near 650 nm caused damage at an energy per pulse smaller than ~1 nJ (2 GW/cm2) and did not provide usable data. Increasing the thickness of the top silica layer might be sufficient to increase the damage threshold of the nanoantennas, but further experiments are necessary to verify this.

Figure 2
Figure 2

Z-scan data for 175 nm BDPAS film on nanoantennas sample [linear transmission offset for clarity]. (a) open-aperture with α2N(600) = 300 cm/GW fit, implying no nonlinear reflection, at 1.4, 4.3, and 6 nJ, and (b) Closed-aperture normalized by 1 mm glass, with n2N(600) = (0.7 ± 0.2) × 10−11 cm2/W fits, at 1.4, 4.3, and 6 nJ.

Closed-aperture Z-scans at 600 and 700 nm, normalized by open-aperture scans, were used to measure the n2 of an 11 mM solution of BDPAS in DCM in a 1 mm cuvette at 40 nJ (41GW/cm2), resulting in (n2(BDPAS+DCM) (600) = 4.5 ± 0.6 × 10−16 cm2/W) and (n2(DCM) (600) = 7.0 ± 1.0 × 10−16 cm2/W). By normalizing the closed-aperture data for BDPAS in DCM by the data for pure DCM, we calculate (n2(BDPAS) (600) = − 2.4 ± 0.8 × 10−16 cm2/W) and (n2(BDPAS) (700) = 2.2 ± 0.8 × 10−16 cm2/W) for 11 mM of BDPAS. Note that we assume the n2 of DCM to be dispersionless across this wavelength range. This results in refractive cross-sections (δr = n2ħωk/N) given in units of Göppert-Mayer32 of δr(BDPAS) (600) =  −1.3 ± 0.4 × 102GM and δr(BDPAS) (700) = 1.2 ± 0.4 × 102 GM.

The n2 at 600 nm for a sample including both the BDPAS film on nanoantennas and 1 mm glass substrate is retrieved using peak to valley transmission:

Δ T p v =0.406 ( 1 0.4 ) 0.25 2 π λ 2 I 0 ( n 2 glass h glass + n 2N h N 1 exp ( α N h N ) α N h N )

From Fig. 2b ΔTpv = 0.0375 at 9.5 GW/cm2, an effective nanoantenna length of h N  0.83 and n2(glass) = 3.0 × 10−16 cm2/W33. Thus we obtain an n2 for the 175 nm BDPAS film with nanoantennas layer of n2N = (0.7 ± 0.2) × 10−11       cm2/W, see Fig. 2(b), resulting in δrN(600) = 1.8 × 104GM.

There was no detectable transmission change for the BDPAS film without nanoantennas.

Based on the known molecular density30, and the refractive cross-section for BDPAS, δr (BDPAS) (600), measured above, we give the nonlinear index of refraction of the film as n2F(600) ≈ −5.0 ± 1.4 × 10−14 cm2/W and n2F(700) ≈ 4.5 ± 1.4 × 10−14 cm2/W.

Using open-aperture Z-scans, shown in Fig. 2(a), we retrieve the nonlinear imaginary refractive index and consequently nonlinear absorption coefficient. The effect of reflection is taken into account using n2 obtained from the closed-aperture Z-scan in transmission. Since the interface transmission does not change the wave phase, n2 is retrieved in the usual way31. Relative to the usual method31, the transmission through the interfaces of the nonlinear slab is taken into account to retrieve α2 from the experimental results shown in Fig. 2a.

For intensity dependent transmission we take into account the reduced intensity at the second interface. Namely T = T1(I)A(Ieff)T2(Ieαh), where transmission at the first interface, transmission through the slab, and transmission at the second interface are: T1,2 = 1 − R1,2 = 4n1,3n/[(n1,3 + n)2 + κ2], A = eαh, n +  = n slab , α = 4πκ/λ. The nonlinear change in transmission, taking into account the averaging coefficient 23/2, is given by (see supplementary information for details):

2 3 / 2 Δ T T Δ I = 1 n ( n 2 n 1 2 κ 2 ) ( n 1 + n ) 2 + κ 2 n nl + n ( n 1 / n + 1 ) 2 + κ 2 / n 2 κ ( n 1 + n ) 2 + κ 2 κ nl 4 π h λ κ nl 1 e α h α h 1 n ( n 2 n 3 2 κ 2 ) ( n 3 + n ) 2 + κ 2 n nl e α h + n ( n 3 / n + 1 ) 2 + κ 2 / n 2 κ ( n 3 + n ) 2 + κ 2 κ nl e α h .

Using nnl = n2N = 0.7 × 10−11 cm2/W, n1 = 1.8, n3 = 1.5, from the linear reflection and transmission fitting n = 2.3 + nnlI, k = 0.117 + κnlI at h = 175 nm, and T exp 0.6, ΔT/T = 0.022 at ΔI = 13 GW/cm2, we obtain κ2N = κnl = 0.17 × 10−11cm2/W and α2N = αnl = 360cm/GW.

Note that, taking into account both absorption and reflection in the open-aperture transmission in Fig. 2a, the analysis gives α2N = 360 cm/GW instead of α2N = 300 cm/GW as given by the usual fitting procedure. Figure 3 shows the transmittance change (ΔT) versus irradiance retrieved from the open-aperture Z-scan results. Note that the nonlinear coefficients are calculated for an effective composite layer of BDPAS and nanoantennas. In the obtained results, the thickness of the effective composite layer is taken as the total thickness of BDPAS and nanoantennas. Another reasonable approach is to consider the effective layer thickness equal to the nanoantennas thickness, 60 nm, since the field enhancement is strong near the nanoparticles.

Figure 3
Figure 3

T from Z-scans vs. incident intensity for BDPAS with nanoantennas, BDPAS film, and BDPAS solution with exponential fit.

Our simulations below confirm that this second approach, with an effective thickness of 60 nm, better describes the experimental situation. Indeed, the intensity mapping in Fig. 4 shows that a layer of 60 nm contains the most intense local field. Also, using the simulated intensity-dependent transmission and reflection shown in Fig. 5, we find that nonlinear changes in transmission and reflection do not grow significantly with the thickness after 60 nm, see Fig. 6. Specifically, in this case, nnl = n2N = 2.48 × 10−11 cm2/W, n1 = 1.8, n3 = 1.5, from linear reflection and transmission fitting n = 2.4 + nnlI, k = 0.31 + κnlI at h = 60 nm, and we obtain κ2N = κnl = 0.6 × 10−11 cm2/W and α2N = αnl = 1257 cm/GW.

Figure 4
Figure 4

Unit cell of the FEM simulations (left), a distribution of the intensity in arbitrary units (center) at 600 nm, normalized transmission spectra with and without Au nanoantennas from the experiments and simulations (right). Simulations for BDPAS film use Eq. 3.

Figure 5
Figure 5

Intensity dependence of the reflection (a) and transmission (b) of the BDPAS with nanoantennas at wavelength 590, 600, and 610 nm.

Figure 6
Figure 6

Change in absorption and reflection versus nonlinear layer (BDPAS) thickness with nanoantennas at wavelength 590, 600, and 610 nm.

We obtain α2F(650) = 13 cm/GW for the BDPAS film, and α2N(600) = 360 cm/GW for the BDPAS film with nanoantennas. The smaller 2PA of BDPAS at 600 nm (δ ≈ 130 GM in DCM) did not provide detectable attenuation to measure α2F(600 nm).

From the measured α2F(650), the 2PA cross-section of BDPAS in film form is calculated to be δF(650) = 287 GM with ± 15% experimental error, which is in good agreement with that of BDPAS in DCM solution. Using the wavelength dependence from ref.27 results in an estimated δF(600) = 162 GM, and using δ = (hc/λ) (α2/N) we obtain α2F(600 nm) = 6.8 cm/GW for the 175 nm BDPAS film. Using Re[ χ ( 3 ) ]= n 2 (4/3) n 0 2 ε 0 c and Im χ ( 3 ) = α 2 ( 2 n 0 2 ε 0 c 2 / 3 ω ), we obtain, χ N ( 3 ) (600)= ( 8.1 + i 1.9 ) × 10 18 m 2 / V 2 for BDPAS on the nanoantennas, and χ F ( 3 ) (600)= ( 5.8 + i 3.6 ) × 10 20 m 2 / V 2 and χ F ( 3 ) (700)= ( 5.3 + i 12.7 ) × 10 20 m 2 / V 2 for the BDPAS film.

The analysis of matching FEM electromagnetic simulations of the nanoantenna-dye unit-cell from Fig. 1(a) supports the experiments as described below. The geometric dimensions and Au loss factor were fit to the experimental results using an efficient simplified model described in ref.34. The experimental geometry was simulated with a commercial full wave electromagnetic simulation software (Comsol Multiphysics) built on the finite-element method. The one-quarter unit cell of the sample bounded by the symmetry planes is shown in Fig. 4 (left). The BDPAS layer was composed of two sublayers, nonlinear and linear. The total thickness is always 175 nm, while the nonlinear one was changed as 10, 30, 60, 90, 120, and 175 nm to find an optimal thickness of the nonlinear material coating. The intensity distribution in Fig. 4 (center) shows that the maximum nonlinear change of the refractive index is expected in the gap in correspondence with the local field distribution and the BDPAS nonlinear refractive index. Figure 4 (right) illustrates the very good correspondence of the experimental and simulated spectra of the BDPAS and a relatively good shape correspondence of the BDPAS with Au nanoantennas. The discrepancy may be due to defects in the array fabrication (missing particles in nanoantennas).

The BDPAS linear permittivity was modeled by a Tauc-Lorentz term and two Lorentz oscillators,

ε BDPAS = ε TL + j = 1 2 ε L , j

A complete description of the Lorentz and Tauc-Lorentz terms along with their experimentally fitted coefficients are shown in the Supporting Information.

The refractive index inside a nonlinear host is,

n= n 0 + ( n 2 + i α 2 2 k 0 ) I,

where k0 = 2π/λ is a free-space wave number, and inside a NL medium the intensities and the field magnitudes are linked as,

I= 1 2 ε 0 n 0 c | E | 2 ,E ( t ) =ReEexp ( i ω t ) ,

with n0 being the real part of the linear component of refractive index.

In the FEM model, the nonlinear properties of the bulk film BDPAS have been taken into account by using n2 = −5.0 × 10−18 m2/W and α2 = 6.7 × 10−11 m/W, while the real and imaginary parts of χ(3) were computed as

Re [ χ ( 3 ) ] = 4 3 ε 0 cn 0 2 n 2
Im [ χ ( 3 ) ] = 2 3 ε 0 c n 0 2 α 2 / k 0

with the principal components of the anisotropic dielectric function in the medium defined as,

ε i i = n 0 2 + 3 4 χ i i ( 3 ) | E i | 2 i { x , y , z }

The solution of resulting nonlinear wave equation ××E k 0 εE=0 in the entire domain is obtained self-consistently at each excitation step with the commercial FEM solver (COMSOL Multiphysics, Wave Optics Module) using a high-performance iterative method (double dogleg). We should note that to avoid possible numerical issues and speed up simulations the illumination intensity is taken to be gradually increasing with the previous solution used as a seed for a new step.

From the literature35,36 for “fast” nonlinearity we take χ Au ( 3 ) = ( 1.1 + i 1.0 ) × 10 22 m 2 / V 2 χ BDPAS ( 3 ) . The simulated intensity dependent transmission and reflection coefficients are shown in Fig. 5.

The thickness dependence (Fig. 6) shows that the nonlinear response is almost saturated after 60 nm. The nonlinear transmission and reflection obtained with the full wave simulations were then fitted with the variable complex refractive index N = n + ik mimicking the intensity dependence. This is done with the J. A. Wollam software37,38. All the layers are glass 1 mm (n = 1.52) without backside reflection, ITO 15 nm (n = 1.9586), BDPAS 175 nm, SiO2 20 nm (n = 1.458). The fitted refractive index corresponds to the BDPAS parameters without nanoantennas and to the effective nonlinear refractive index and effective nonlinear absorption of the effective uniform layer in case of the BDPAS with nanoantennas. Thus for 175 nm BDPAS film we get at 600 nm:

n=1.816× 10 4 ( I / I nl ) ,k=0.00537+9.3× 10 4 ( I / I nl ) ,where I nl =3× 10 14 W m 2 .

This retrieval procedure via the fitting gives for the BDPAS n2F(600) = −16 × 10−4/Inl = −5.3 × 10−18 m2/W, κ2 = 9.3 × 10−4/Inl = 3.1 × 10−18, and α2F(600) = 2k0κ2 = 6.5 × 10−11 m/W. This provides a control retrieval result matching the accepted starting parameters of the BDPAS layer.

The BDPAS with Au nanoantennas and effective layer thickness L = 175 nm at 600 nm results in: n = 2.3 + 0.018(I/Inl), k = 0.117 + 0.0033(I/Inl), where Inl = 2.9 × 1013W/m2. Thus at 175 nm for the effective uniform layer n2eff(600) = 0.62 × 10−11 cm2/W, α2eff(600) = 240 cm/GW. Experimental results give n2N = (0.7 ± 0.2) × 10−11 cm2/W, α2N = 360 cm/GW.

Since approximately only the first 60 nm near the nanoantennas contribute to the enhancement (see Fig. 6), it makes sense to retrieve the complex nonlinear refractive index for the composition of 60 nm of the effective nonlinear BDPAS/Au nanoantennas hybrid and keep the remaining 115 nm as a linear layer. The retrieved effective refractive index for the 60 nm uniform effective layer is: n = 2.4 + 0.021(I/I nl ), k = 0.31 + 0.015(I/I nl ),where Inl = 2.9 × 1013W/m2. Correspondingly, this gives for the 60 nm effective layer n2eff(600) = 0.7 × 10−11 cm2/W,α2eff(600) = 1100 cm/GW.

We also evaluate another approach to define an effective third-order susceptibility, χ eff ( 3 ) , widely used in the earlier literature25 and recent developments5. Namely χ eff ( 3 ) is defined as Eq. 9, where f, g(3) are the volume filling fraction and enhancement factor respectively, subscripts {h, in} denote the host (dye) and inclusions (gold).

X eff ( 3 ) = f in g in ( 3 ) χ in ( 3 ) + f h g h ( 3 ) χ h ( 3 )

The E-field extracted from simulations was used to find the complex nonlinear enhancement ( g h ( 3 ) ), fh = 0.964 from the above geometry since X eff ( 3 ) in our system is dominated by the host (BDPAS) term. One should mention that the approximation based on the local field factor is not practical as this follows from our evaluation in the supplementary information. We conclude that local field enhancement is strongly intensity dependent and cannot be used to define the effective nonlinear susceptibilities. Any detectable nonlinearity will make the approximation used in the literature5,25 unacceptable.

Table 1 summarizes the experimental and simulations’ results. The final enhancement of the nonlinear susceptibility of the dye due to the nanoantennas is found by comparing both the experimental results ( χ N ( 3 ) ) and the FEM simulations ( X eff ( 3 ) ) of the composite structure to the BDPAS film ( χ F ( 3 ) ).

Table 1 Summary of experimental and simulation results.

The nonlinear refractive index of the BDPAS layer is enhanced by n2N/n2F = −140x from experiment, and n2Neff/n2F = −125x from simulations at 600 nm. The retrieval using the effective thickness 60 nm, which corresponds to the characteristic thickness of the nonlinear response saturation presented in Fig. 6, gives n2Neff/n2F = −140. While the sign change in n2 is reproduced in both cases, the magnitude deviation is most likely due to the difference in the resonance quality between the experimental sample and simulated unit cell, which is seen for the linear response in Fig. 1b. The 2PA of the dye layer is enhanced by α2N/α2F = 53 times in the experiment, and α2Neff/α2F = 36 times from simulations at 600 nm. Note that the enhancement due to the nanoantennas changes the sign of the nonlinear refractive index. Such a complex enhancement of the local field in a composite medium has been discussed earlier39. The main reason for the imaginary part of the local field enhancement is the phase shift between the local field and applied field. It is also important that the local field varies in both, magnitude and phase with coordinates near the nanoantenna particles. The simulations suggest also that the nonlinear changes in transmission have a contribution from both nonlinear changes in reflection and in absorption. However, the Z-scan data for n2 allows separating the effects of absorption to get α2 as was shown above.


Gold dipole nanoantennas that produce strong local electromagnetic fields were used to enhance both the nonlinear refractive index and 2PA of a nonlinear dye. Bi-periodic gold nanoantenna arrays with nonlinear dyes also have a large wavelength dependent theoretical enhancement as has been shown from simulations. Furthermore, experimental results have shown that the nonlinear refractive index is enhanced by 140× with a sign change from negative to positive and a 53× enhancement in nonlinear (2PA) absorption at λ = 600 nm for BDPAS (4,4′-bis(diphenylamino)stilbene) with only 10% of surface coverage or 3.7% volume fraction of the gold nanoantennas. Since only 60 nm out of 175 nm of the BDPAS layer contributes to the enhancement, the realistic enhancement of both the n2 and α2 is ~3 times larger.

Both real and imaginary parts of the BDPAS χ F ( 3 ) contribute to the effective nonlinear absorption of the BDPAS/Au nanoantenna composite material, due to the complex nature of the enhancement factor resulting in the sign flip for the nonlinear refractive index. This fact, along with the tunable enhancement of the plasmon resonance, makes it possible to control the effective nonlinear response of the composite film. The above results demonstrate that the nonlinear composite can be further optimized through appropriate selection of component materials.


The gold nanoantennas are fabricated using electron-beam lithography on an ITO-coated glass substrate with a 15 nm ITO layer. An electron-beam evaporator is used to produce a 5 nm adhesion layer of titanium followed by a 55 nm gold film with a 1 Å/s deposition rate in a 7 × 10−7 Torr vacuum chamber (Airco). After lift-off the nanoantennas are annealed at 400 °C for 2 minutes by a rapid thermal processing system (RTP, Minipulse RTA), which has been shown to produce larger grain sizes and a lower loss factor, resulting in a stronger plasmonic resonance and larger local electromagnetic fields29. A 175 nm BDPAS film was then deposited using thermal evaporation in a vacuum chamber, followed by a 20 nm layer of silica to protect the sample. The linear refractive index of the BDPAS film is determined by spectroscopic ellipsometry, which is approximately n0 = 1.8 at wavelengths longer than λ = 500 nm. Open- and closed-aperture Z-scan measurements were used to measure the film’s nonlinear index of refraction (n2) and the nonlinear absorption coefficient (α2) for the primary X polarization. The effect of reflection can be taken into account using the n2 obtained from the closed-aperture Z-scan in transmission. Relative to the usual method31, we take into account transmission through the interfaces of the nonlinear slab to retrieve α2 from the experimental results as explained in supplementary information. Note that interface transmission does not change the wave phase, thus n2 is retrieved in the usual way31. A femtosecond optical parametric amplifier, OPA (Light Conversion, TOPAS-800), pumped by a Ti:Sapphire regenerative amplifier laser system (Clark MXR, CPA 2010), with a pulse duration of 140 fs (FHWM), 1 kHz repetition rate, was used. The focused spot size varied for different measurements, so both pulse energy and irradiance are provided.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1.

    Su, K. H. et al. Interparticle Coupling Effects on Plasmon Resonances of Nanogold Particles. Nano Lett. 3(8), 1087–1090 (2003).

  2. 2.

    Kim, S. et al. High-harmonic generation by resonant plasmon field enhancement. Nature 453, 757–760 (2008).

  3. 3.

    Bakker, R. M. et al. Nanoantenna array-induced fluorescence enhancement and reduced lifetimes. New J. Phys. 10, 125022–16 (2008).

  4. 4.

    Glass, A. M. et al. Enhanced two-photon fluorescence of molecules adsorbed on silver particle films. Phys. Rev. B: Condens. Matter 24, 4906 (1981).

  5. 5.

    Kohlgraf-Owens, D. C. & Kik, P. G. Structural control of nonlinear optical absorption and refraction in dense metal nanoparticle arrays. Opt. Express 17, 15032–15042 (2009).

  6. 6.

    Wenseleers, W. et al. Five Orders-of-Magnitude Enhancement of Two-Photon Absorption for Dyes on Silver Nanoparticle Fractal Clusters. J. Phys. Chem. B 106, 6853–6863 (2002).

  7. 7.

    Cohanoschi, I. & Hernandez, F. E. Surface Plasmon Enhancement of Two- and Three-Photon Absorption of Hoechst 33 258 Dye in Activated Gold Colloid Solution. J. Phys. Chem. B 109, 14506–14512 (2005).

  8. 8.

    Cohanoschi, I., Yao, I. S., Belfield, K. D. & Hernández, F. E. Effect of the concentration of organic dyes on their surface plasmon enhanced two-photon absorption cross section using activated Au nanoparticles. J. Appl. Phys. 101, 086112–3 (2007).

  9. 9.

    Hache, F., Ricard, D. & Flytzanis, C. Optical nonlinearities of small metal particles: Surface-mediated resonance and quantum size effects. J. Opt. Soc. Am. B 3, 1647–1655 (1986).

  10. 10.

    Bloemer, M. J., Haus, J. W. & Ashley, P. R. Degenerate four-wave mixing in colloidal gold as a function of particle size. J. Opt. Soc. Am. B 7, 790–795 (1990).

  11. 11.

    Uchida, K. et al. Optical nonlinearities of a high concentration of small metal particles dispersed in glass: copper and silver particles. J. Opt. Soc. Am. B 11, 1236–1243 (1994).

  12. 12.

    Rautian, S. G. Nonlinear spectroscopy of the degenerate electron gas in spherical metallic particles. SoV. Phys. JETP 85, 451–461 (1997).

  13. 13.

    Drachev, V. P., Buin, A. K., Nakotte, H. & Shalaev, V. M. Size Dependent χ(3) for Conduction Electrons in Ag Nanoparticles. Nano Letters 4, 1535–1539 (2004).

  14. 14.

    Mai, H. H. et al. Nonlinear Optical Properties of Ag Nanoclusters and Nanoparticles Dispersed in a Glass Host. J. Phys. Chem. C 118, 15995–16002 (2014).

  15. 15.

    Philip, R., Chantharasupawong, P., Qian, H., Jin, R. & Thomas, J. Evolution of Nonlinear Optical Properties: From Gold Atomic Clusters to Plasmonic Nanocrystals. Nano Letters 12, 4661–4667 (2012).

  16. 16.

    Liberman, V., Sworin, M., Kingsborough, R. P., Geurtsen, G. P. & Rothschild, M. Nonlinear bleaching, absorption, and scattering of 532-nm-irradiated plasmonic nanoparticles. J. Appl. Phys. 113, 053107–10 (2013).

  17. 17.

    Zhang, X., Luo, W., Wang, L.-J. & Jiang, W. Third-order nonlinear optical vitreous material derived from mesoporous silica incorporated with Au nanoparticles. J. Mat Chem. C 2, 6966–6970 (2014).

  18. 18.

    Drachev, V. P., Perminov, S. V., Rautian, S. G., Safonov, V. P. & Khaliullin, E. N. Polarization effects in silver nano-aggregates caused by local and nonlocal nonlinear-optical responses. J. of Experim. and Theor. Physics 95, 901–915 (2002).

  19. 19.

    Drachev, V. P., Perminov, S. V., Rautian, S. G. & Safonov, V. P. Giant nonlinear optical activity in aggregated silver nanocomposites. JETP Letters 68, 651–656 (1998).

  20. 20.

    Shorokhov, A. S. et al. Ultrafast control of third-order optical nonlinearities in fishnet metamaterials. Scientific Reports 6, 28440, (2016).

  21. 21.

    Khurgin, J. B. & Sun, G. Plasmonic enhancement of the third order nonlinear optical phenomena: Figures of merit. Opt. Express 21, 27460–27480 (2013).

  22. 22.

    Hasan, S. B., Lederer, F. & Rockstuhl, C. Nonlinear plasmonic antennas. Materials Today 7, 478–485 (2014).

  23. 23.

    Valle, G. D. et al. Nonlinear anisotropic dielectric metasurfaces for ultrafast nanophotonics. ACS Photonics 4, 2129–2136 (2017).

  24. 24.

    Debrus, S. et al. Z-scan determination of the third-order optical nonlinearity of gold: silica nanocomposites. J. Appl. Phys. 88, 4469–4475 (2000).

  25. 25.

    Stroud, D. & Hui, P. M. Nonlinear susceptibilities of granular matter. Phys. Rev. B: Condens. Matter 37, 8719–8724 (1988).

  26. 26.

    Ehrlich, J. E. et al. Two-photon absorption and broadband optical limiting with bis-donor stilbenes. Opt. Lett. 22, 1843–1845 (1997).

  27. 27.

    Drobizhev, M., Rebane, A., Suo, Z. & Spangler, C. W. One-, two- and three-photon spectroscopy of [pi]-conjugated dendrimers: cooperative enhancement and coherent domains. J. Lumin. 111, 291–305 (2005).

  28. 28.

    Makarov, N. S., Drobizhev, M. & Rebane, A. Two-photon absorption standards in the 550-1600 nmexcitation wavelength range. Opt. Express 16, 4029–4047 (2008).

  29. 29.

    Chen, K.-P., Drachev, V. P., Borneman, J. D., Kildishev, A. V. & Shalaev, V. M. Drude Relaxation Rate in Grained Gold Nanoantennas. Nano Lett. 10, 916–922 (2010).

  30. 30.

    ChemBlink, “Online Database of Chemicals from Around the World: BDPAS” retrieved 4/3/2010, (2010).

  31. 31.

    Sheik-Bahae, M., Said, A. A., Wei, T. H., Hagan, D. J. & Van Stryland, E. W. Sensitive Measurement of Optical Nonlinearities Using a Single Beam. Journal of Quantum Electronics QE 26, 760–769 (1989).

  32. 32.

    Balu, M. et al. Broadband Z-scan characterization using a high-spectral-irradiance, high-quality supercontinuum. J. Opt. Soc. Am. B 25, 159–165 (2008).

  33. 33.

    Boyd, R. W. Nonlinear Optics. 3rd ed. Academic Press, Inc., SanDiego, 2008.

  34. 34.

    Borneman, J. D., Chen, K.-P., Kildishev, A. V. & Shalaev, V. M. Simplified model for periodic nanoantennae: linear model and inverse design. Opt. Express 17, 11607–11617 (2009).

  35. 35.

    Ganeev, R. A., Ryasnyansky, A. I., Kamalov, S. R., Kodirov, M. K. & Usmanov, T. Nonlinear susceptibilities, absorption coefficients and refractive indices of colloidal metals. J. Phys. D: Appl. Phys. 34, 1602–1611 (2001).

  36. 36.

    Mehendale, S. C. et al. Nonlinear refraction in aqueous colloidal gold. Opt. Commun. 133, 273–276 (1997).

  37. 37.

    The simulations for the experimental and the effective, stratified, planar structures were performed with ellipsometry software (W-VASE, J. A. Woollam Co., Inc.) that is based on a 4x4 scattering-matrix method for solving Maxwell’s Equations Ref. [38].

  38. 38.

    Azzam, R. M. A. & Bashara, N. M. Ellipsometry and polarized light. North Holland (1987).

  39. 39.

    Smith, D. D., Fischer, G., Boyd, R. W. & Gregory, D. A. Cancellation of photoinduced absorption in metal nanoparticle composites through a counterintuitive consequence of local field effects. J. Opt. Soc. Am. B: Opt. Phys. 14, 1625–1631 (1997).

Download references


E.V.S. and D.J.H. thank the Air Force Office of Scientific Research MURI grant FA9550-10-1-0558, the National Science Foundation grant DMR-1609895 and Army Research Laboratory (W911NF-15-2-0090). Purdue University acknowledges the Air Force Office of Scientific Research (AFOSR) MURI grant (FA9550-12-1-0389). AVK would like to acknowledge support  from DARPA/DSO Extreme Optics and Imaging (EXTREME) Program.

Author information

Author notes

    • Lazaro A. Padilha

    Present address: Univ Estadual Campinas, UNICAMP, Sao Paulo, Brazil

    • Trenton R. Ensley

    Present address: U.S. Army Research Laboratory, Adelphi, MD, 20783, USA


  1. Department of Physics and Advanced Materials & Manufacturing Institute, University of North Texas, Denton, Texas, 76203, USA

    • Vladimir P. Drachev
  2. Skolkovo Institute of Science and Technology, Moscow, 143026, Russia

    • Vladimir P. Drachev
  3. School of Electrical and Computer Engineering and Birck Nanotechnology Center, Purdue University, West Lafayette, IN, 47907, USA

    • Alexander V. Kildishev
    • , Joshua D. Borneman
    • , Kuo-Ping Chen
    •  & Vladimir M. Shalaev
  4. College of Optical Sciences, University of Arizona, Tucson, AZ, 85721, USA

    • Konstantin Yamnitskiy
    • , Robert A. Norwood
    •  & Nasser Peyghambarian
  5. Georgia Institute of Technology, Atlanta, GA, 30332, USA

    • Seth R. Marder
  6. CREOL, The College of Optics and Photonics, University of Central Florida, Orlando, FL, 32816, USA

    • Lazaro A. Padilha
    • , Scott Webster
    • , Trenton R. Ensley
    • , David J. Hagan
    •  & Eric W. Van Stryland
  7. Department of Physics, University of Central Florida, Orlando, FL, 32816, USA

    • David J. Hagan
    •  & Eric W. Van Stryland


  1. Search for Vladimir P. Drachev in:

  2. Search for Alexander V. Kildishev in:

  3. Search for Joshua D. Borneman in:

  4. Search for Kuo-Ping Chen in:

  5. Search for Vladimir M. Shalaev in:

  6. Search for Konstantin Yamnitskiy in:

  7. Search for Robert A. Norwood in:

  8. Search for Nasser Peyghambarian in:

  9. Search for Seth R. Marder in:

  10. Search for Lazaro A. Padilha in:

  11. Search for Scott Webster in:

  12. Search for Trenton R. Ensley in:

  13. Search for David J. Hagan in:

  14. Search for Eric W. Van Stryland in:


Project planning: V.P.D., V.M.S., R.A.N., N.P., S.R.M., D.J.H., E.W.V.S.; sample preparation and structural characterization: K.-P.C. and J.D.B. under supervision V.P.D.; organic film synthesis and fabrication: S.R.M., K.Y., R.A.N.; numerical simulations and analysis: A.V.K. and V.P.D.; nonlinear measurements and analysis: L.A.P., S.W., T.R.E., D.J.H., E.W.V.S.; All authors contributed to overall data analysis and scientific discussions. V.P.D., A.V.K., J.D.B., L.A.P., D.J.H., E.W.V.S. wrote the manuscript with contributions from all authors.

Competing Interests

The authors declare that they have no competing interests.

Corresponding author

Correspondence to Vladimir P. Drachev.

Electronic supplementary material


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Creative Commons BY

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit