Article | Open | Published:

# Stress-induced long-range ordering in spider silk

## Abstract

The emergence of order from disorder is a topic of vital interest. We here propose that long-range order can arise from a randomly arranged two-phase material under mechanical load. Using Small-Angle Neutron Scattering (SANS) experiments and Molecular Dynamics based finite element (FE) models we show evidence for stress-induced ordering in spider dragline silk. Both methods show striking quantitative agreement of the position, shift and intensity increase of the long period upon stretching. We demonstrate that mesoscopic ordering does not originate from silk-specific processes such as strain-induced crystallization on the atomistic scale or the alignment of tilted crystallites. It instead is a general phenomenon arising from a non-affine deformation that enhances density fluctuations of the stiff and soft phases along the direction of stress. Our results suggest long-range ordering, analogously to the coalescence of defects in materials, as a wide-spread phenomenon to be exploited for tuning the mechanical properties of many hybrid stiff and soft materials.

## Introduction

A material’s mechanical behavior is ultimately defined by the underlying structure. Enormous progress has been made in the last decades in the knowledge and design of the molecular to macroscopic structure for even high-complexity materials, in order to tailor their mechanics and mechanical properties. However, our understanding of how the application of mechanical stress effects the material’s structure on the relevant length scales, even though at least similarly critical for mechanical performance, needs expanding.

Many composite materials of mechanical interest feature a coexistence of stiff and soft phases, in which the stiff phase reinforces and thereby strengthens the soft phase. Analogously, semi-crystalline polymers, including synthetic and biological materials, consist of a highly structured stiff phase alternating with an amorphous and comparably soft phase. It is well established that stretching semi-crystalline materials can lead to order on a short length scale, namely by stress-induced crystallization1,2,3,4. Amorphous chains straighten and align, and thereby self-assemble into more ordered structures under force. This also leads to a reduction in the average tilt angle of the backbones within crystallites relative to the fiber axis1,2,5,6. Thus, such materials feature different facets of stress-induced ordering on the scale of the individual chains and crystals. A completely unaddressed question, however, is if applied stress can also increase long-range order on the mescoscopic scale of a few nanometers in the distribution of stiff components within the amorphous matrix of composite or semi-crystalline materials, or of defects, respectively.

Interestingly, in a material with randomly distributed voids or defects, stress application causes these voids to nucleate. The coalescence and gradual volumetric growth of voids leads to the formation of larger defect-free regions and lowers the total internal energy of the system7,8,9. Similarly, stress can increase structural order in metals with irradiation-induced defects10,11,12. Each defect in a periodic arrangement of atoms or molecules gives rise to a local stress concentration. This stress can cause these defects to be ‘dragged’ towards each other, which lowers the total internal energy of the system. This results in larger defect-free regions separated by clusters of defects along the direction of stress application.

Protein crystals show a similar behavior: Zemlin et al. could show that upon irradiation beyond a critical threshold, defects vanish in finite sized protein crystals, resulting in stress-induced order due to the build-up of internal stresses13. They observed the same effect in regular 2D-lattices of macroscopic bubbles, corroborating their conclusion that mechanical stress and not thermal energy induced the order. These seminal experiments nearly two decades ago have not yet been attempted with other systems. Stress-induced order as a general principle has yet to be uncovered.

Given that defects can be considered as a second phase in a two-phase system with inherently different mechanical properties, an obvious question is if stress-induced long-range order is a phenomenon similarly at play in composite or semi-crystalline materials (Fig. 1). An intriguing consequence of such ordering would be an attenuation of stress concentrations and an enhancement in toughness.

We here addressed this question for the nanoscale arrangement of crystallites within silk fibers. Silk is a protein-based high-performance semi-crystalline material. In contrast to synthetic semi-crystalline materials, crystalline regions are imprinted into the sequence, namely poly-alanine repeat units of a length of 6–10 monomers14,15,16. They alternate with glycine-rich disordered regions of roughly three times the length, which form the amorphous phase. The nanometer-sized crystalline units show a preferred orientation of the crystallites c-axis (chain direction) along the fiber direction1,6,17,18, but are otherwise thought to be randomly positioned1. Both, Small-angle neutron (SANS) and X-ray scattering (SAXS) experiments show a mesoscopic long period in fiber direction at a length scale similar to the length scale of individual crystallites, which currently lacks a structural interpretation19,20,21,22,23,24. Interestingly, we could previously show in a highly simplified finite element model that an ordered arrangement of crystallites, with regions of high and low crystallinity alternating along the fiber axis, would increase the fiber’s toughness25.

We here present results from a purely atomistically-informed (bottom-up) finite element model of a silk fiber under stress and small-angle neutron scattering (SANS) experiments of Nephila edulis dragline fibers. Both simulations and experiments unequivocally show an increase in long-range order of crystals along the fiber axis beyond the purely geometric effect of fiber elongation. Fluctuations of crystal density along the fiber axis increase upon stretching, thereby lowering mechanical energy. Our data suggests long-range order arising from mechanical work performed on the material to be vitally important to our understanding of silk fiber structure and mechanics, and potentially many other semi-crystalline or composite materials.

## Results and Discussion

### Crystals distribute periodically in strained silk fibers

To analyze potential stress-induced ordering in silk, we here resorted to a simplified two-phase finite element (FE) model of silk fiber comprising of the stiffer crystalline and the softer amorphous phase. We have developed this bottom-up FE model on the basis of atomistic MD simulations of Araneus diadematus silk protein26,27. We here present a novel refined FE model, which describes the amorphous phase as a viscoelastic and the crystalline phase as a plastoelastic material, of which the viscosity and yield stress again obtained from MD simulations28,29,30. Crystals were randomly distributed into the amorphous phase with the experimentally known FWHM for the tilt angle of 15° for native dragline silk of A. trifasciata 18 and N. clavipes 1 at crystallinities varying between 9 and 14% (Fig. 2a)1. We note that silk also features a phase of intermediate order, primarily composed of the glycine-alanine rich sequences flanking the poly-alanine repeats1, which extend the crystallites apparent dimensions and might also be the cause of the measured higher total crystallinity1,18. We therefore considered additional models with larger crystals and up to 17% crystallinity (Supplement Fig. 4). We applied constant strain rates to the fibers, and observed typical stress-strain curves with yield stress and strain, rupture stress and strain, and toughness values in agreement with experimental observations (see Supplementary Information, Suppl. Table 1), validating our simplified model.

Changes in structural order were also analyzed within the fiber under load. Figure 2 shows the crystallinity along the fiber axis for different strain values. The initial random packing transforms into a crystal distribution with pronounced peaks of higher crystallinity upon stretching (Fig. 2a). The increase in crystallinity fluctuations was quantified by summing up the deviations from the mean crystallinity along the fiber axis (Fig. 2b,c). We always observed a significant increase in these fluctuations upon straining. These fluctuations roughly lie in the 4–8 nm range, i.e. beyond the length of single crystals along the fiber axis, which here was chosen to fall in line with the poly-alanine repeat lengths of 2.7 nm27. This advocates a stress-induced ordering. The significantly larger increase in MAD for a crystalinity of 13% might originate from the packing routine for this specific volume and size. ratio of crystal and fibers, or is simply a consequence of insufficient sampling. We observe the same increase in MAD upon straining the fiber for models with larger crystal sizes and overall crystallinity (Suppl. Fig. 4) or with zero tilt angle (Suppl. Fig. 5), suggesting our finding to be robust with regard to these structural parameters.

### SANS confirms stress-induced order in silk

Small-angle neutron scattering (SANS) was undertaken to test our computational prediction of stress-induced ordering in silk fibers. Deuterated fiber bundles using H/D exchange of Nephila edulis spider silk23,31 were subjected to increasing values of constant strains, for each of which a SANS pattern was recorded. An increase in scattering peak intensity on the nanometer length scale upon fiber stretch would reflect a long-range order of crystalline units within the flexible and thus more strongly deuterated amorphous phase, which also includes a partially ordered phase around the non-deuterated crystallites32. The two-dimensional SANS patterns (inset in Fig. 3a) show the distinct meridional peaks as an indication of the mesoscopic long period in fiber direction previously reported19,20,21,22,23,24,33 as well as a strong equatorial streak. The latter would yield additional information on the lateral (perpendicular to the fiber axis) arrangement of the nanocrystals in the spider silk fiber; however, in the context of the ordering effect in fiber direction, the respective analysis is not relevant and will be discussed elsewhere. Upon tensile load, the 2D SANS pattern exhibits two obvious changes: the position of the meridional peaks moves towards smaller scattering angles and the peaks become more pronounced. The integration of the two meridional peaks (symmetrically above and below the equator) over a 45° azimuthal angle each result in radial intensity distributions I(q) where q is the modulus of the wave vector transfer defined as $$q=\frac{4\pi }{\lambda }\,\sin \,\theta$$ with the scattering angle 2θ. I(q) measures correlations of distances $$d=\frac{2\pi }{q}$$ along the fiber axis between less deuterated regions, which here are the highly ordered β-sheet rich crystal units. The respective I(q) curves are shown in Fig. 3a for different values of the macroscopic strain ε. The second order peak (at 2q) is extremely weak, which is consistent with SAXS experiments on wet silk fibers20. As already seen in the 2D pattern, the long-period peak intensity increases and shifts to smaller q upon stretch.

The increase in I(q) of the long period observed in the SANS experiment is in line with the observations from the FE silk fiber model (Fig. 2). For a more direct comparison, we calculated the SANS observable, I(q), from the fiber model. More precisely, I(q) was obtained from the ensemble averaged correlations of distances $$d=\frac{2\pi }{q}$$ between the mesh nodes within and between the crystals (Fig. 3b, see Suppl. Information for details). As expected, the finite size of the model causes high intensities below 1 nm−1, and correlations within the crystalline units result in high intensities in the q = 10–13 nm−1 range (Fig. 3b, inset). We can also recover the long period, i.e. the correlations of inter-crystal distances along the fiber axis, as observed in the SANS experiments, with high I(q) in the range of 1 nm−1. We note that quantitative comparisons of absolute I(q) values between SANS experiments and FE simulations are not possible, because the number of scatterers in the experiment are unknown. As in the SANS experiments, the maximum of I(q) increases with strain and moves towards smaller q upon stretching.

For both, the SANS and FE long period, the q-position of the peak maximum was then used to calculate the corresponding d-spacing. Taking the value at no strain as reference $${d}_{0}=d(\varepsilon =\mathrm{0)}$$, we can define the microscopic small-angle strain as $${\varepsilon }_{d}(\varepsilon )=\frac{d(\varepsilon )-{d}_{0}}{{d}_{0}}$$. The strain dependence of ε d is plotted in Fig. 3c and is clearly linear with a ratio of 0.86 (SANS) or 0.85–0.91 (FE) between ε d and ε at maximal experimental ε. A value < 1 is associated with deformation by fibril slip34, which is consistent with our simulation results assuming lateral friction within the amorphous phase of spider silk29. The lateral friction within the amorphous phase is connected to the increased unraveling of the random polymer chains upon strain, which is be a process associated with friction and thus reflected in the spectroscopic response29,31,35.

Figure 3d shows the stress-induced change in the intensity maximum. In both the SANS experiments and FE calculations, independent from the initial arrangement and crystallinity of the model, we obtained a significant stress-induced increase in I(q) of the long period. This finding indicates increased order of the periodic arrangement of the long period structure. To distinguish such stress-induced ordering from a purely geometric effect, we calculated the strain-dependent long periods also for a fictitious reference system, namely a homogeneous fiber with identical viscoelastic properties throughout (Fig. 3d). In this case, the intensity of the long-period also steadily increases upon loading, but to a significantly smaller extent than in the SANS experiment or in the actual FE silk fiber models. Remarkably, the extent of ordering we observe in our silk fiber models is as high as the stress-induced ordering expected for a toy model of an already completely pre-ordered fiber. In this simple model, patches of high crystallinity move away from one another under tensile stress in an affine deformation. The toy model qualitatively confirms the strain-dependence of the position and height of the long-range peak observed in FE calculations and SANS experiments (Fig. 3c,d and Supplementary Methods):

$${q}_{{\rm{\max }}}\sim 2\pi /\mathrm{(1}+\varepsilon ),\quad S({q}_{{\rm{\max }}})\sim 1+N\mathrm{[1}-{\mathrm{(2}\pi \sigma )}^{2}\mathrm{/(1}+\varepsilon {)}^{2}]\quad \quad \mathrm{(0 < }\varepsilon \ll \mathrm{1)}$$
(1)

Taken together, the combined results from experiments and simulations strongly support the notion of stress-induced ordering of the crystalline phase along spider silk fibers, which relies on the fact that one component is significantly stiffer than the other, resulting in a phase separation. Regions rich in amorphous phase can more readily expand separating crystal-reinforced regions from one another and minimizing mechanical energy. While experiments have been performed with supercontracted silk, our more general computational and analytical models suggests that ordering can be at play in both supercontracted and native silks. The independence of our results with respect to crystal tilting, which is more pronounced for supercontracted silk, corroborates this notion. The striking quantitative agreement between the SANS experiments and the FE simulations, which have been performed independently and on different spider silks, hint towards that long-range ordering is a general phenomenon not depending on intricate details of specific silks such as exact tilting of crystals, sequence of the amorphous phase, chain connectivity, or crystal size and distribution. Yet, we only have started to assess how much these factors influence the extent of ordering, by varying some of the model parameters (tilt angles, crystal sizes, crystallinity). The simplicity and versatility of our model, however, opens new roads towards deciphering the determinants of mesoscopic order in silk, being supercontracted or dry, dragline or not, from spiders or bombyx mori.

## Conclusions

By combining simulations and experiments, we here show that tensile forces acting on systems with two mechanically distinct phases can lead to an increase in long-range order. The ordering goes significantly beyond a purely geometric effect, which solely arises from the lengthening and thinning of the specimen. Remarkably, we obtained a striking quantitative agreement between the finite element simulations, the SANS experiments and a simple analytical model. Together, this strongly advocates stretch-induced ordering in silk, and possibly as a general principle of any two-phase system, being it semi-crystalline or a composite, and at varying length scales of the two phases, from the nanometer to micrometer scale or even beyond. Whenever one of the two phases is much softer than the other (or actually a defect13), the softer phase will more readily extend in regions less stiffened by the other phase, resulting in a mechanically induced phase segregation. We also show that stress-induced long-range ordering is largely independent from the extent of crystallinity fluctuations at zero stress. It does rely, however, on some pre-existing fluctuations in the distribution of crystals, such that order should not arise from a fiber with a perfectly homogenous crystal distribution. The observed ordering effect is in line with the very recent observation by quasi-elastic neutron scattering experiments of spider silk that the diffusive mobility of the amorphous phase increases with tensile strain31. We propose that tensile forces present during the spinning process of silk or other synthetic fibers enhance long-range pre-order, which in turn boosts further ordering during tensile loading. The parameter range of volume ratios, pre-order, and mechanical properties of the two phases within which stress-induced ordering is at play remains to be systematically quantified. Given that the toughness of a fiber is maximal for a highly ordered arrangement26, lowering the friction between the soft and stiff components of a hybrid material might improve ordering and thereby toughness, another important point of future studies. We envision a wide range of materials, from nano-composites to block-copolymers, for which stress-induced long-range order can be exploited as a mean to tune mechanical properties.

## Materials and Methods

The reported SANS experiments were performed for a fiber bundle of Nephila edulis spider dragline silk at different strains. The fibers were humidified with D2 O, and the scattering contrast arose from the H/D-contrast between the D2 O-accessible disordered (amorphous) regions and the crystallites. The latter are much less accessible for D2 O and therefore do not undergo an H/D-exchange. A novel bottom-up finite element (FE) fiber model for Araneus diadematus spider dragline silk based on previous atomistic Molecular Dynamics simulations25,26,29 was subjected to constant strain rates using LS-DYNA. All computational and experimental details are given in the Supplementary Methods.

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## References

1. 1.

Grubb, D. T. & Jelinski, L. W. Fiber morphology of spider silk: the effects of tensile deformation. Macromolecules 30, 2860–2867 (1997).

2. 2.

Grubb, D. T. & Ji, G. Molecular chain orientation in supercontracted and re-extended spider silk. Int. J. Biol. Macromol. 24, 203–210 (1999).

3. 3.

Hill, M. J. & Keller, A. Direct evidence for distinctive, stress-induced nucleus crystals in the crystallization of oriented polymer melts. J. Macromol. Sci., Part B: Phys. 3, 153–169 (2006).

4. 4.

Toki, S., Fujimaki, T. & Okuyama, M. Strain-induced crystallization of natural rubber as detected real-time by wide-angle x-ray diffraction technique. Polymer 41, 5423–5429 (2000).

5. 5.

Riekel, C. et al. Aspects of x-ray diffraction on single spider fibers. Int. J. Biol. Macromol. 24, 179–186 (1999).

6. 6.

Glišović, A., Vehoff, T., Davies, R. J. & Salditt, T. Strain dependent structural changes of spider dragline silk. Macromolecules 41, 390–398 (2008).

7. 7.

McClintock, F. A. A criterion for ductile fracture by the growth of holes. J. Appl. Mech. 35, 363–371 (1968).

8. 8.

Thomason, P. A theory for ductile fracture by internal necking of cavities. J. Inst. Metals 96, 360–365 (1968).

9. 9.

Rice, J. R. & Tracey, D. M. On the ductile enlargement of voids in triaxial stress fields. J. Mech. Phys. Solids 17, 201–217 (1969).

10. 10.

Simpson, H. M., Sosin, A., Edwards, G. R. & Seiffert, S. L. New mechanism for internal friction. Phys. Rev. Lett. 26, 897–900 (1971).

11. 11.

Townsend, J. R., Schildcrout, M. & Reft, C. Mechanical studies of irradiation-induced defects in cu and w. Phys. Rev. B 14, 500–516 (1976).

12. 12.

Nowick, A. S., Berry, B. S. & Katz, J. L. Anelastic relaxation in crystalline solids. J. Appl. Mech. 42, 750–751 (1975).

13. 13.

Zemlin, F. et al. Stress-induced recrystallization of a protein crystal by electron irradiation. Nature 399, 51–54 (1999).

14. 14.

Xu, M. & Lewis, R. V. Structure of a protein superfiber: spider dragline silk. Proc. Natl. Acad. Sci. USA 87, 7120–7124 (1990).

15. 15.

Gosline, J., Guerette, P., Ortlepp, C. & Savage, K. The mechanical design of spider silks: from fibroin sequence to mechanical function. J. Exp. Biol. 202, 3295–3303 (1999).

16. 16.

Gatesy, J., Hayashi, C., Motriuk, D., Woods, J. & Lewis, R. Extreme diversity, conservation, and convergence of spider silk fibroin sequences. Science 291, 2603–2605 (2001).

17. 17.

Parkhe, A. D., Seeley, S. K., Gardner, K., Thompson, L. & Lewis, R. V. Structural studies of spider silk proteins in the fiber. J. Mol. Recogn. 10, 1–6 (1997).

18. 18.

Plaza, G. R. et al. Relationship between microstructure and mechanical properties in spider silk fibers: identification of two regimes in the microstructural changes. Soft Matter 8, 6015–12 (2012).

19. 19.

Mahoney, D., Vezie, D., Eby, R., Adams, W. W. & Kaplan, D. Aspects of the morphology of dragline silk of nephila clavipes. ACS Symp. Ser. 544, 196–210 (1994).

20. 20.

Yang, Z., Grubb, D. T. & Jelinsk, L. W. Small-angle x-ray scattering of spider dragline silk. Macromolecules 30, 8254–8261 (1997).

21. 21.

Riekel, C. & Vollrath, F. Spider silk fibre extrusion: combined wide-and small-angle x-ray microdiffraction experiments. Int. J. Biol. Macromol. 29, 203–210 (2001).

22. 22.

Valluzzi, R. & Jin, H.-J. X-ray evidence for a super-secondary structure in silk fibers. Biomacromolecules 5, 696–703 (2004).

23. 23.

Sapede, D. et al. Nanofibrillar structure and molecular mobility in spider dragline silk. Macromolecules 38, 8447–8453 (2005).

24. 24.

Du, N. et al. Design of superior spider silk: From nanostructure to mechanical properties. Biophys. J. 91, 4528–4535 (2006).

25. 25.

Cetinkaya, M., Xiao, S. & Gräter, F. Effects of crystalline subunit size on silk fiber mechanics. Soft Matter 7, 8142–8148 (2011).

26. 26.

Cetinkaya, M., Xiao, S., Markert, B., Stacklies, W. & Gräter, F. Silk fiber mechanics from multiscale force distribution analysis. Biophys. J. 100, 1298–1305 (2011).

27. 27.

Xiao, S., Stacklies, W., Cetinkaya, M., Markert, B. & Gräter, F. Mechanical response of silk crystalline units from force-distribution analysis. Biophys. J. 96, 3997–4005 (2009).

28. 28.

Patil, S. P., Gräter, F. & Markert, B. Refining a bottom-up computational approach for spider silk fibre mechanics. Proc. 3rd GAMM Seminar Continuum Biomech. II–21, 75–87 (2012).

29. 29.

Patil, S. P., Markert, B. & Gräter, F. Rate-dependent behavior of the amorphous phase of spider dragline silk. Biophys. J. 106, 2511–2518 (2014).

30. 30.

Patil, S. P., Xiao, S., Gkagkas, K., Markert, B. & Gräter, F. Viscous friction between crystalline and amorphous phase of dragline silk. PLoS ONE 9, e104832 (2014).

31. 31.

Krasnov, I. et al. Strain-dependent fractional molecular diffusion in humid spider silk fibres. J. R. Soc., Interface 13, 20160506 (2016).

32. 32.

Paquet-Mercier, F., Lefèvre, T., Auger, M. & Pézolet, M. Evidence by infrared spectroscopy of the presence of two types of β-sheets in major ampullate spider silk and silkworm silk. Soft Matter 9, 208–215 (2013).

33. 33.

Seydel, T. et al. Increased molecular mobility in humid silk fibers under tensile stress. Phy. Rev. E Stat. Nonlin. Soft Matter Phys. 83, 016104 (2011).

34. 34.

Ginzburg, B. M. & Tuichiev, S. Microdeformational behavior of oriented semicrystalline polymers. J. Macromol. Sci., Part B: Phys. 31, 291–317, https://doi.org/10.1080/00222349208215518 (1992).

35. 35.

Perea, B. G. et al. Unexpected behavior of irradiated spider silk links conformational freedom to mechanical performance. Soft matter 11, 4868–4878 (2015).

## Acknowledgements

We thank the members of the Molecular Biomechanics Group at the Heidelberg Institute for Theoretical Studies for helpful discussions, and Fritz Vollrath for generously providing the spider silk sample for SANS experiments. Ralf Schweins (ILL) is acknowledged for work at the D11 beamline. F. G. is supported by the Klaus Tschira Foundation and Toyota Europe. F. G. and B. M. acknowledge support by the DFG grant GR 3494/7–1.

## Author information

### Affiliations

1. #### Heidelberg Institute for Theoretical Studies (HITS), Heidelberg, 69118, Germany

• Johannes A. Wagner
•  & Frauke Gräter
2. #### Heidelberg University, Institute for Theoretical Physics, Heidelberg, 69120, Germany

• Johannes A. Wagner
3. #### RWTH Aachen University, Institute of General Mechanics, Aachen, 52062, Germany

• Sandeep P. Patil
•  & Bernd Markert
4. #### Helmholtz-Zentrum Geesthacht (HZG), Institute of Materials Research, Geesthacht, 21502, Germany

• Imke Greving
•  & Martin Müller
5. #### University of Leipzig, Institute for Theoretical Physics, Leipzig, 04103, Germany

• Marc Lämmel
6. #### Toyota Motor Europe NV/SA, Advanced Technology Division, Zaventem, 1930, Belgium

• Konstantinos Gkagkas
7. #### Institut Max von Laue-Paul Langevin (ILL), Grenoble, 38042, France

• Tilo Seydel
8. #### University of Kiel, Institute for Experimental and Applied Physics, Kiel, 24098, Germany

• Martin Müller
9. #### Heidelberg University, Interdisciplinary Center for Scientific Computing (IWR), Heidelberg, 69120, Germany

• Frauke Gräter

### Contributions

Experimental design, Finite element simulations, Analyses: J.A.W., S.P.P., B.M., K.G., M.M., F.G.; SANS experiments: I.G., T.S., M.M.; Analytical toy model: M.L.; Manuscript writing: J.A.W., F.G., I.G., M.M., T.S., S.P.P.

### Competing Interests

The authors declare that they have no competing interests.

### Corresponding author

Correspondence to Frauke Gräter.