Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Transparent, abrasion-insensitive superhydrophobic coatings for real-world applications


Superhydrophobic surfaces and surface coatings are of high interest for many applications in everyday life including non-wetting and low-friction coatings as well as functional clothing. Manufacturing of these surfaces is intricate since superhydrophobicity requires structuring of surfaces on a nano- to microscale. This delicate surface structuring makes most superhydrophobic surfaces very sensitive to abrasion and renders them impractical for real-life applications. In this paper we present a transparent fluorinated polymer foam that is synthesized by a simple one-step photoinitiated radical polymerization. We term this material “Fluoropor”. It possesses an inherent nano-/microstructure throughout the whole bulk material and is thus insensitive to abrasion as its superhydrophobic properties are not merely due to a thin-layer surface-effect. Due to its foam-like structure with pore sizes below the wavelength of visible light Fluoropor appears optically transparent. We determined contact angles, surface energy, wear resistance and Vickers hardness to highlight Fluoropor’s applicability for real-word applications.


Transparent, superhydrophobic surfaces are of high interest especially for functional coatings. In order to achieve superhydrophobic properties, i.e. contact angles greater than 150° and roll-off angles of less than 10°1,2, the surface must be engineered in terms of chemistry and surface roughness: only appropriately structured surfaces achieve the superhydrophobic state. State-of-the art techniques for generation of transparent, superhydrophobic surfaces rely on a) deposition or growth of functionalized or embedded nanoparticles (mostly spheres or rods) on surfaces3,4,5,6, b) custom-engineered surface structures (pillars) or induced surface roughness by etching7,8, anodization9 or imprinting10 with optional consecutive hydrophobic functionalization and c) phase-separation effects in polymer deposition upon drying, heating or during polymerization11,12. Most of the reported methods yield thin and fragile coatings which have limited practical relevance mostly due to their abrasion-sensitivity. Thick-layer coatings with nano-/microstructuring throughout the bulk material however would circumvent the problem of abrasion-sensitivity: all layers exposed through abrasion effects display superhydrophobicity due to their inherent structure. Bulk porous polymers with superhydrophobic properties have been reported13,14,15,16,17, as well as self-healing materials based on silica powders18,19,20, however none of the materials combine thick-layer coatings with transparency and abrasion-insensitivity and most reported foams possess low stability owing to their aerogel-like structure.

Here we describe an easy-to-fabricate, optically transparent, abrasion-insensitive bulk nano-/microstructured polymer that can be used for coating surfaces (glass, metals and textiles) as well as bulk substrates. We call this material “Fluoropor”. Fluoropor is made via radical polymerization in a one-step procedure with foam-like structuring just below the threshold of light scattering resulting in optical transparency of the material. All components of Fluoropor are readily commercially available. We have characterized Fluoropor for its real-world applicability by standardized methods such as wear resistance and Vickers hardness measurements which are employed for coating characterization on an industrial scale21. Fluoropor is insensitive even to dramatic abrasion such as scratching or sandpaper abrasion making it ideal for long-term use under harsh abrasive conditions. Fluoropor is an easy-to-create, widely-applicable and wear/abrasion-tolerant material for real-world applications.

We achieved the formation of superhydrophobic transparent polymer foam “Fluoropor” through light-induced polymerization of fluorinated perfluoropolyether methacrylates in a non-solvent (cyclohexanol) and an emulsifying agent (fluorinated alcohol). Fluoropor possesses a bulk nano-/microstructure (see Fig. 1a and Supplementary Fig. S1) and can be polymerized in varying thicknesses (see Fig. 1b). Due to the polymerization process Fluoropor samples possess a non-structured layer of polymer on top (“lid” see Supplementary Fig. S2) which can be readily removed by abrasion. The optical transparency of Fluoropor is mainly dependent on the degree of light scattering of the surface exposed by the removal of the lid. Thus there is no linear correlation between layer thickness and optical transparency. All thin-layer glass coatings between 55 µm and 170 µm show high optical transparency within the visible light region (see Fig. 1c). Bulk samples of 800 µm and 3500 µm thickness show decreased light transmission but are still see-through upon background contact (see Fig. 1b,c). The transparency of foams is dependent on light scattering at the pore surfaces via reflection and refraction22. When the pores are small enough, i.e. when their diameter is well below the wavelength of visible light, the material appears transparent. At 400 nm, non-foamed Fluoropor possesses an optical transmission of 99%, foamed Fluoropor with a smooth surface (lid structure intact) possesses an optical transmission of 86% and the lowest transmission is displayed by foamed Fluoropor with a rough surface (lid structure removed) with 66% at 400 nm (100 µm films, see Supplementary Fig. S3). Therefore, as expected, the pore size in the bulk as well as the surface roughness are responsible for the loss in transparency. Still the pores are small enough to make Fluoropor appear transparent. Optical transmissions were measured against a blank of the supporting glass and therefore display the values for the coating only. The transmission of the supporting glass is displayed Supplementary Fig. S4. Functionalization of glass surfaces relies on exposing the surface silanol groups by treatment with methanol/hydrochloric acid (1:1 v/v)23 and consecutive attachment of 3-(dimethylchlorosilyl)propyl methacrylate to the surface. The methacrylate groups are covalently attached to the glass surface and take part in the polymerization reaction of Fluoropor thus covalently attaching the polymer.

Figure 1
figure 1

Transparent, bulk nano-/microstructured polymer foam “Fluoropor”. (a) Thin-layer (105 µm) optically transparent Fluoropor film on glass with superhydrophobic properties. The SEM images show the porous nano-/microstructure of the material on the surface and in the bulk (side view of a 210 µm coating on glass). (b) Fluoropor bulk nano-/microstructured samples of 820 µm and 3500 µm thickness. (c) Optical transmission of Fluoropor samples with varying average thicknesses between 55 µm and 3500 µm. All scale bars: 1 cm. Optical transmissions were measured against a blank of the supporting glass and therefore display the values for the coating only.

Fluoropor possesses a low Vickers hardness of 1.19 HV at 100 mN/20 s – which is in the appropriate range of rigid polymer foams24. For further comparison, polyethylene possesses a Vickers hardness of 5–8 HV24. Due to its softness Fluoropor is very flexible at layer thicknesses below ~1000 µm (see Fig. 2a). Polymers and fluoropolymers in particular are of high interest for low-friction coatings, i. e. coatings with friction coefficients of 0.4 and lower25. Wear resistance measurements of Fluoropor gave a coefficient of friction of µ = 0.2 sliding against a brass sphere (see Fig. 2b) which is comparable to polytetrafluoroethylene (PTFE) sliding against stainless steel (µ = 0.15–0.2)26. The wear tracks of the tribometer were below 1 µm in depth thus the material is sufficiently robust for prolonged wear-abrasion (see Supplementary Fig. S5). Fluoropor was further characterized in terms of its superhydrophobic properties. A droplet of water readily bounces off a Fluoropor surface (see Fig. 2c). The superhydrophobicity is independent on the drop volume when gravitational effects on the drop-shape are minor, i.e. between 1 µL and 15 µL and the average static contact angle of Fluoropor was calculated to be 163.7 ± 6.8° (see Fig. 2d). The static contact angle is a common but not an ideal characterization method for rough surfaces. The maximum (advancing) and minimum (receding) contact angles are better suited for producing reliable results on inhomogeneous surfaces. The advancing and receding contact angles were determined to be 158.0 ± 7.9° and 151.9 ± 1.9°, respectively (see Fig. 2e) with an average contact angle hysteresis of 6.1°. The variations in the advancing contact angle are due to vibrations of the enlarging droplet during the measurement (see Supplementary Fig. S6), which lead to variations in the contact angles determined by the instrument automatically by evaluating the high-speed video data image-by-image. The decrease in receding contact angles over time is caused by decreasing contact radius of the droplet due to evaporation over time27. The surface possesses a very low free energy of 7.2 mN/m. In accordance with the low hysteresis a water roll-off-angle of 6.6 ± 1.7° was determined.

Figure 2
figure 2

Characterization of Fluoropor bulk nano-/microstructured polymer foam. (a) Fluoropor is a soft material and a substrate of 820 µm thickness is very flexible. (b) The wear resistance of Fluoropor was measured using a tribometer (schematic inset). After a break-in phase of ~50 cycles, a coefficient of friction of µ = 0.2 was determined (µ = FR/FN). (c) A 5 µL droplet of water bounces off a Fluoropor surface (time passed between frame 1 and frame 9: approximately 2.6 s). (d) The static contact angle of Fluoropor shows little variation at various droplet volumes and was determined to be an average of 163.7 ± 6.8°. (e) Advancing and receding contact angle measurements of Fluoropor gave 158.0 ± 7.9° and 151.9 ± 1.9°, respectively. The receding contact angle decreases due to evaporation of the droplet over time.

Abrasion is a threat to any functional structured coating. Fluoropor with its high wear-resistance is not easily abraded but if abrasion occurs the inherent bulk nano-/microstructure makes its superhydrophobic properties insensitive to the abrasion (see Fig. 3). Upon treating Fluoropor with sandpaper and abrading a total of 20 µm of the ~80 µm coating the superhydrophobic properties of the surface are fully retained with a minor change in the static contact angle from 165 ± 2° to 161 ± 4°. Scratching the surface leads to slightly decreased transparency (see Fig. 3b), however the transparency of the material can be recovered by polishing the surface with a microfiber cloth which has no influence on the contact angle which was determined to be 161 ± 2° after polishing (see Fig. 3c). SEM images of Fluoropor after abrasion and after abrasion and consecutive polishing (see Supplementary Fig. S7) show the unaltered nano-/microstructure of Fluoropor.

Figure 3
figure 3

The superhydrophobic properties of Fluoropor are insensitive to abrasion. (a) Schematic illustration of Fluoropor abrasion-test: Fluoropor sample of thickness d [µm] is abraded by x [µm] by using sandpaper under a weight (0.74 kg). The superhydrophobic properties of the surface are retained due to its bulk porosity, while the transparency of the polymer suffers lightly (see photographic insets). Transparency is regained by polishing with a microfiber cloth. (b) Optical Transmission of the Fluoropor coating before abrasion, after abrasion of x~20 µm and after polishing. The optical transparency of the coating is fully regained after sandpaper abrasion and consecutive polishing. (c) Static contact angles of water on Fluoropor before abrasion, after abrasion and after polishing remain nearly constant, making the superhydrophobic properties of Fluoropor insensitive even to drastic abrasion of 20 µm layer thickness.

Besides glass, Fluoropor was also coated on other practically relevant surfaces such as metals, polymers and textiles to show its applicability as a superhydrophobic coating (see Fig. 4). Fluoropor films in the range of ~100 µm were polymerized onto gold, copper and epoxy surfaces using a supporting layer of silane. The metal surfaces were functionalized with a protocol adapted from Wu et al.28 where a self-assembled monolayer of 3-(mercaptopropyl) triethoxysilane is formed on the metal surface, followed by hydrolysis and condensation of the triethoxysilane groups by corona discharge to form a siloxane network with exposed silanol groups. In a second step, the silanol groups react with 3-(dimethylchlorosilyl)propyl methacrylate to give surface-bound methacrylate groups that covalently attach Fluoropor during polymerization. Fluoropor can also be used as a coating for textiles (see Fig. 4e) coating the fibers with a layer of polymer (see Supplementary Fig. S8). Under water the coated substrates form an air-retaining Salvinia layer (see Fig. 4f). Fluoropor on copper was further employed to demonstrate the triboelectrical properties of Fluoropor: rubbing a copper sheet against a copper sheet coated with Fluoropor gave a voltage of 3.5 V.

Figure 4
figure 4

Fluoropor coatings on metal, polymer and textile surfaces. Images above: top view of the substrates, images below: side view with 20 µL droplets of water on the superhydrophobic surfaces. (a) Fluoropor on gold (glass slide with chromium and gold layer, partially etched), static contact angle: 153.4 ± 4.6°. (b) Fluoropor on copper (circuit board partially etched), static contact angle: 153.1 ± 1.6°. (c) Fluoropor on copper sheet, static contact angle: 157.9 ± 2.0°, scale bar: 5 mm. (d) Fluoropor on an epoxy polymer (circuit board, partially etched), static contact angle: 154.9 ± 2.5°, scale bar: 5 mm. (e) Fluoropor on microfiber cloth, static contact angle: 148.9 ± 1.1°, scale bar: 5 mm. (f) Fluoropor on copper sheet shown in c forms an air-retaining Salvinia layer under water.

We demonstrated the formation of nano-/microstructured polymer foam “Fluoropor” with adjustable thickness and high optical transparency. The abrasion-insensitivity of the superhydrophobic properties of Fluoropor, as well as its ease of manufacturing and its compatibility with a wide range of substrate materials makes Fluoropor a transparent coating suitable for real-world applications.


Fluorolink MD700 was purchased from Acota (United Kingdom), 3-(methacryloyloxypropyl) dimethylchlorosilane, 3-(mercaptopropyl)triethoxysilane, methanol, ethanol, methacrylic anhydride, toluene, cyclohexanol, acetone and 2-propanol, hydrochloric acid (37%) were purchased from Merck (Germany). 1 H,1 H,2 H,2H-perfluorooctanol was purchased from Apollo Scientific (United Kingdom) and 2,2-dimethoxy-2-phenylacetophenone (DMPAP) was purchased from Sigma-Aldrich (Germany). Nexterion Slide Glass B clean room slides were purchased from Schott (Germany). AZ photoresist and developer were purchased from microchemicals (Germany).

Synthesis of nano-/microstructured transparent fluoropolymer

50 wt% Fluorolink MD700 was mixed with 15 wt% cyclohexanol and 35 wt% 1 H,1 H,2 H,2H-perfluorooctanol. The mixture was blended with 0.5 wt% DMPAP dissolved in acetone (1 mg/µL). Custom-made polymerization chambers were constructed from regular glass slides, glue and spacers of different height (made from cyclic olefin copolymer, COC). The mixture was polymerized under UV light (370 nm, Lumatec Superlite SUV mercury arc lamp, Lumatech, Germany) for 2–5 min depending on the layer thickness. The polymer was placed in 2-propanol overnight and consecutively dried in a vacuum furnace at 100 °C for 1 h at 30 mbar. The top layer of the Fluoropor samples was removed after drying to expose the nanostructure due to the polymerization of a non-structured layer on top of the polymerization chamber (see Supplementary Fig. S2). This layer can be removed by regular laboratory cotton wipes in case of thin-layer coatings or by abrasion with sandpaper for thicker substrates.

Functionalization of glass slides

Cleanroom glass slides were immersed in a mixture of concentrated hydrochloric acid and methanol (50:50) for 30 min. Afterwards the slides were rinsed with 2-propanol and deionized water and dried with compressed air. To functionalize the surface, the slides were incubated in a 100 mM solution of (3-methacryloyloxypropyl)dimethylchlorosilane in toluene for 1 h. The slides were rinsed with 2-propanol and deionized water and dried with compressed air.

Functionalization of copper, gold and epoxy substrates

Gold slides and copper slides were etched to show the KIT logo by etching with iodine solution and ammonium persulfate solution, respectively, using AZ1514H photoresist as a mask. The metal substrates were cleaned with 2-propanol and dried with compressed air. The substrates were placed in 2 vol% solution of 3-(mercaptopropyl)triethoxysilane in ethanol for 8 min. The substrates were rinsed with deionized water and dried with compressed air. After cleaning the metal substrate were activated with a corona discharger (type BD 20, purchased from ETP, USA) for about 1 min. During activation the corona discharger was placed at a distance of approximately 0.5 cm above the sample surface. The substrates were then immersed in a 100 mM solution of 3-(dimethylchlorosilyl)propyl methacrylate in toluene for 1 h. The slides were rinsed with 2-propanol and deionized water and dried with compressed air.

Textile functionalization

The microfiber cloth was used without prior treatment.

Contact angle measurement

Contact angles were measured with a OCA15 Pro (Data Physics, USA). All droplet-shapes were evaluated by using the Young-Laplace fit if not stated otherwise. For advancing and receding contact angle measurements by the ARCA program of the instrument, a 5 µL droplet of deionized water was dispensed onto the surface and held in place by the dispenser needle. Additional 5 µL of deionized water were dispensed to a final droplet volume of 10 µL (advancing contact angle). After 1 min 5 µL of the droplet volume were removed (receding contact angle). After 1 min the droplet was expanded to 10 µL and consecutively after 1 min reduced to 5 µL again. In this way five receding and five advancing contact angles were measured by evaluation of the video data, in this case the contact angles were determined by the tangent-fit to reduce computing time. Left- and right-sided contact angles were determined for each frame and the arithmetic middle of the two angles was plotted. The roll-off angle was characterized by dispensing a 10 µL droplet onto the surface and consecutive tilting of the instrument at a given angle per time. Static contact angles and the surface energy of the material were determined using 5 µL droplets. For the determination of the free surface energy, the static contact angles of 5 µL droplets of deionized water and diiodomethane were determined and the OWRK method was used to calculate the surface energy.

UV/VIS measurements

The optical transmission of the nano-/microstructured Fluoropor samples was determined using a UV/VIS spectrometer (Evolution 201, Thermo Scientific, Germany). Coatings on glass were measured against a glass blank, free polymer substrates were measured against air.

Vickers Hardness

The Vickers hardness was determined using a Vickers hardness tester (Fischerscope HCU, Fischer, Germany) at a load of 100 mN and a loading time of 20 s.

Wear Resistance

The wear resistance was determined using a custom-built tribometer equipped with a brass test body of 8 mm diameter at 50% relative humidity (RH). The test body moves across the sample thereby causing abrasion. Samples were tested with a load of 400 g, a glide path of 10–12 mm, v = 0.5 mm/s and 1000 experimental cycles.

Sandpaper abrasion test

Fluoropor coatings on glass were glued to the table using double-sided adhesive tape. 2500 grain sandpaper was glued onto the bottom of a flat 0.74 kg Teflon block. The block was moved across the sample approximately 100 times to give an even abrasion across the whole sample. The sample was cleaned by careful strokes with a cotton wipe, microfiber cloth and/or usage of a pressurized air gun to ensure the full removal of any fluorinated particles.

Layer thickness measurements

The thicknesses of thin-layer coatings on glass were determined using a Heidenhain MT 60 M length gauge. Thicker unsupported samples were measured using a caliper.

Triboelectric measurement

A ~ 100 µm layer of Fluoropor was coated onto a copper plate. A second copper plate was rubbed against the coated plate. Both plates were connected to a multimeter to determine the voltage produced by rubbing.

Data availability statement

The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.


  1. Butt, H. J. et al. Characterization of super liquid-repellent surfaces. Curr Opin Colloid In 19, 343–354, (2014).

    CAS  Article  Google Scholar 

  2. Drelich, J., Chibowski, E., Meng, D. D. & Terpilowski, K. Hydrophilic and superhydrophilic surfaces and materials. Soft Matter 7, 9804–9828, (2011).

    CAS  Article  ADS  Google Scholar 

  3. Deng, X., Mammen, L., Butt, H. J. & Vollmer, D. Candle Soot as a Template for a Transparent Robust Superamphiphobic Coating. Science 335, 67–70, (2012).

    CAS  Article  PubMed  ADS  Google Scholar 

  4. Zhang, X. et al. A transparent and photo-patternable superhydrophobic film. Chem Commun, 4949–4951, (2007).

  5. Gao, Y. Q. et al. Highly Transparent and UV-Resistant Superhydrophobic SiO2-Coated ZnO Nanorod Arrays. Acs Appl Mater Inter 6, 2219–2223, (2014).

    CAS  Article  Google Scholar 

  6. Jiang, W. T. et al. An effective route for transparent and superhydrophobic coating with high mechanical stability. Thin Solid Films 562, 383–388, (2014).

    CAS  Article  ADS  Google Scholar 

  7. Kong, J. H. et al. Highly flexible, transparent and self-cleanable superhydrophobic films prepared by a facile and scalable nanopyramid formation technique. Nanoscale 6, 1453–1461, (2014).

    CAS  Article  PubMed  ADS  Google Scholar 

  8. Fresnais, J., Chapel, J. P. & Poncin-Epaillard, F. Synthesis of transparent superhydrophobic polyethylene surfaces. Surf Coat Tech 200, 5296–5305, (2006).

    CAS  Article  Google Scholar 

  9. Kemell, M., Farm, E., Leskela, M. & Ritala, M. Transparent superhydrophobic surfaces by self-assembly of hydrophobic monolayers on nanostructured surfaces. Phys Status Solidi A 203, 1453–1458, (2006).

    CAS  Article  ADS  Google Scholar 

  10. Liu, S. H. et al. Facile synthesis of transparent superhydrophobic titania coating by using soot as a nanoimprint template. Rsc Adv 3, 22825–22829, (2013).

    CAS  Article  Google Scholar 

  11. Hwang, H. S. et al. Facile Fabrication of Transparent Superhydrophobic Surfaces by Spray Deposition. Acs Appl Mater Inter 3, 2179–2183, (2011).

    CAS  Article  Google Scholar 

  12. Ouhib, F. et al. Transparent superhydrophobic coatings from amphiphilic-fluorinated block copolymers synthesized by aqueous polymerization-induced self-assembly. Polym Chem-Uk 7, 3998–4003, (2016).

    CAS  Article  Google Scholar 

  13. Levkin, P. A., Svec, F. & Frechet, J. M. J. Porous Polymer Coatings: a Versatile Approach to Superhydrophobic Surfaces. Adv Funct Mater 19, 1993–1998, (2009).

    CAS  Article  PubMed  PubMed Central  Google Scholar 

  14. Liu, J. F., Xiao, X. Y., Shi, Y. L. & Wan, C. X. Fabrication of a superhydrophobic surface from porous polymer using phase separation. Appl Surf Sci 297, 33–39, (2014).

    CAS  Article  ADS  Google Scholar 

  15. Xue, Z. X. et al. Superoleophilic and superhydrophobic biodegradable material with porous structures for oil absorption and oil-water separation. Rsc Adv 3, 23432–23437, (2013).

    CAS  Article  Google Scholar 

  16. Zahner, D., Abagat, J., Svec, F., Frechet, J. M. J. & Levkin, P. A. A Facile Approach to Superhydrophilic-Superhydrophobic Patterns in Porous Polymer Films. Adv Mater 23, 3030, (2011).

    CAS  Article  PubMed  Google Scholar 

  17. Franco, J. A., Kentish, S. E., Perera, J. M. & Stevens, G. W. Fabrication of a superhydrophobic polypropylene membrane by deposition of a porous crystalline polypropylene coating. J Membrane Sci 318, 107–113, (2008).

    CAS  Article  Google Scholar 

  18. Chen, K. L., Zhou, S. X. & Wu, L. M. Facile fabrication of self-repairing superhydrophobic coatings. Chem Commun 50, 11891–11894, (2014).

    CAS  Article  Google Scholar 

  19. Chen, K. L., Zhou, S. X., Yang, S. & Wu, L. M. Fabrication of All-Water-Based Self-Repairing Superhydrophobic Coatings Based on UV-Responsive Microcapsules. Adv Funct Mater 25, 1035–1041, (2015).

    CAS  Article  Google Scholar 

  20. Chen, K. L., Zhou, S. X. & Wu, L. M. Self-Healing Underwater Superoleophobic and Antibiofouling Coatings Based on the Assembly of Hierarchical Microgel Spheres. Acs Nano 10, 1386–1394, (2016).

    CAS  Article  PubMed  Google Scholar 

  21. Tian, X. L., Verho, T. & Ras, R. H. A. Moving superhydrophobic surfaces toward real-world applications. Science 352, 142–143, (2016).

    CAS  Article  PubMed  ADS  Google Scholar 

  22. Clark, N. O. & Blackman, M. The Transmission of Light through Foam. T Faraday Soc 44, 7–13, (1948).

    CAS  Article  Google Scholar 

  23. Cras, J. J., Rowe-Taitt, C. A., Nivens, D. A. & Ligler, F. S. Comparison of chemical cleaning methods of glass in preparation for silanization. Biosens Bioelectron 14, 683–688, (1999).

    CAS  Article  Google Scholar 

  24. Ashby, M. F. & Johnson, K. Materials and design: the art and science of material selection in product design. (Elsevier, 2010).

  25. Hirvonen, J. P., Koskinen, J., Jervis, J. R. & Nastasi, M. Present progress in the development of low friction coatings. Surf Coat Tech 80, 139–150, (1996).

    CAS  Article  Google Scholar 

  26. Sawyer, W. G., Freudenberg, K. D., Bhimaraj, P. & Schadler, L. S. A study on the friction and wear behavior of PTFE filled with alumina nanoparticles. Wear 254, 573–580, (2003).

    CAS  Article  Google Scholar 

  27. Lam, C. N. C., Wu, R., Li, D., Hair, M. L. & Neumann, A. W. Study of the advancing and receding contact angles: liquid sorption as a cause of contact angle hysteresis. Adv Colloid Interfac 96, 169–191, (2002).

    CAS  Article  Google Scholar 

  28. Wu, W., Wu, J., Kim, J. H. & Lee, N. Y. Instantaneous room temperature bonding of a wide range of non-silicon substrates with poly(dimethylsiloxane) (PDMS) elastomer mediated by a mercaptosilane. Lab Chip 15, 2819–2825, (2015).

    CAS  Article  PubMed  Google Scholar 

Download references


Materials and Methods are presented in the Supplementary Materials Section. This work was funded by the German Ministry of Education and Research (BMBF), funding code 03 × 5527 “Fluoropor”.

Author information

Authors and Affiliations



D.H. Abrasion tests, writing of the paper. N.K. preparation of coatings and bulk materials, S.E.M. images. F.K. Contact angle measurements. F.S. Wear resistance tests. C.G. Vickers Hardness testing. T.M.N. UV/VIS measurements. K.S. thickness measurements. B.E.R. supervision and writing of the paper.

Corresponding author

Correspondence to Bastian E. Rapp.

Ethics declarations

Competing Interests

The authors declare that they have no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Helmer, D., Keller, N., Kotz, F. et al. Transparent, abrasion-insensitive superhydrophobic coatings for real-world applications. Sci Rep 7, 15078 (2017).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing