Article | Open | Published:

Exfoliated WS2-Nafion Composite based Electromechanical Actuators

Scientific Reportsvolume 7, Article number: 14599 (2017) | Download Citation


The ability to convert electrical energy into mechanical motion is of significant interest in many energy conversion technologies. Here, we demonstrate the first liquid phase exfoliated WS2-Nafion nanocomposite based electro-mechanical actuators. Highly exfoliated layers of WS2 mixed with Nafion solution, solution cast and doped with Li+ was studied as electromechanical actuators. Resonant Raman spectroscopy, X-ray photo-electron-spectroscopy, differential scanning calorimetry, dynamic mechanical analysis, and AC impedance spectroscopy were used to study the structure, photoluminescence, water uptake, mechanical and electromechanical actuation properties of the exfoliated nanocomposites. A 114% increase in elastic modulus (dry condition), 160% increase in proton conductivity, 300% increase in water uptake, cyclic strain amplitudes of ~0.15% for 0.1 Hz excitation frequency, tip displacements greater than nanotube-Nafion and graphene-Nafion actuators and continuous operation for more than 5 hours is observed for TMD-Nafion actuators. The mechanism behind the increase in water uptake is a result of oxygen atoms occupying the vacancies in the hydrophilic exfoliated flakes and subsequently bonding with water, not possible in Nafion composites based on carbon nanotube and graphene.


The ability to convert electrical energy into mechanical motion is highly desirable for energy conversion, actuation, robotics and reconfigurable technologies. Today, a wide variety of smart technologies have been developed based on the conversion of electrical to mechanical energy which is used broadly from simple home blenders to complex aerospace technologies. Materials such as piezoelectrics1, ferroelectrics2, shape memory alloys3 and electroactive polymers4,5,6,7 are used as actuators that convert electrical energy into mechanical output. Many applications of such materials have been proposed including atomic force microscopes8, biomimetic robots9, and artificial muscles6. With the advent of nanomaterials such as carbon nanotubes10 and graphene11, they have also been explored in their native form as electrical actuators12 and also by mixing them in different matrices to make nanocomposites13,14,15.

Here, we describe the working of a new type of actuator based on Nafion and Transition Metal Dichalcogenides (TMDs) based nanocomposites. Nafion is a sulfonated tetrafluoroethylene based fluoropolymer-copolymer with high porosity and unique ionic properties and was initially developed as electrolytic separators16. They have found applications in diverse areas such as ion exchange membranes17, proton conductors18, drug delivery19, batteries20 and in fuel cells21 due to their excellent mechanical properties, stability, electro-activity, water nanochannels and low cost. In the past, Nafion was mixed with carbon nanotubes14, graphene15, and metallic nanoparticles22 to improve actuation and bending characteristics of electro-mechanical actuators. Recently, semiconductors such as TMDs have found various applications as transistors23, optoelectronic devices24, photo-thermal actuators25 and solar cells26. However, they have not been evaluated as electro-active materials in Nafion polymer actuators.

Transition Metal Dichalcogenides (TMDs) are the class of 2D layered materials with transition metal layer between two chalcogen layers. The atoms within the layers are bonded through strong covalent bonds27. The weak van der Waals bonding between the layers enables the triple layers to be mechanically/chemically shear exfoliated. The in-plane structure of WS2 is determined by strong covalent bonds resulting from the overlap between the 4d and 3p electron orbitals of W and S respectively28. The elastic modulus and the breaking strength of an ideal defect-free single-layer WS2 are similar to those of MoS2 and is expected to reach the theoretical limits of E2D/9, where E2D is the in-plane stiffness of the 2D layered material29,30. The ultra-high strength originates from the p orbitals of the chalcogen atoms which give rise to the σ bonds31. The large strength, ability to modulate the conduction of electrons through doping and enhanced water uptake in TMDs can result in their application for Nafion based electro-mechanical actuation technologies.

Layered materials represent a diverse and largely untapped source of two-dimensional (2D) systems with exotic electronic properties and high specific surface areas that are important for sensing32, catalysis33, energy storage34, and actuation applications35. Similar to graphene, the bright future of 2D TMDs can only be realized through large-scale exfoliation36. Making single/bi/few layers TMDs has been attempted using mechanical exfoliation37, chemical synthesis38, and liquid phase exfoliation36. However, Nafion-TMD composites as proposed here and smart materials and systems based on them cannot be achieved using scotch tape exfoliation methods. Liquid-phase exfoliation is the strategy that is used for large volume processing for applications such as composites, batteries, and thin films to name a few36. Initial work by Coleman et al. has shown the liquid phase exfoliation of few layers using a wide variety of solvents. Typically, high yield of few layers and low yield of single layers are obtained36.

By utilizing liquid phase exfoliation, the solution casting of nanocomposite fabrication and electromechanical testing, we present the structural properties, interaction mechanisms and actuation properties of WS2-Nafion nanocomposites. The advantages of our fabrication methods are as follows: (1) the liquid phase exfoliation resulting in high quality single to few layers with distinctive direct electron transition peaks and bandgaps; (2) phase desegregated nanocomposites due to excellent dispersion of exfoliated additives and improvement in mechanical properties, (3) access to the unique layer dependent electronic/optical properties of WS2 layers inside the nanocomposite (ex: photoluminescence), (4) the design enables scalable and flexible process for developing stimuli-responsive wearable and energy harvesting devices in water and air, (5) the exfoliated WS2 nanosheets enhanced water retention properties of Nafion by 300% that served to enhance and tune actuation behavior of Nafion composites.

Results and Discussion

Figure 1 presents the High-Resolution Transmission Electron Micrograph (HRTEM) of the 2H-WS2 single layer with Selected Area Diffraction Pattern (SAED). WS2 belongs to the same family of TMDs as MoS2 and can be mechanically exfoliated using scotch tape and liquid phase exfoliation techniques. In the WS2 lattice, each W atom is located at the center of a trigonal prism created by six S atoms. The lattice  parameters of WS2 was reported to be: a = b = 3.153 Å and c = 12.3 Å39. A single layer of WS2 is ~0.7 nm thick40 and can be exfoliated using scotch tape and liquid phase exfoliation techniques36. The HRTEM was conducted to ascertain the structure of the WS2 presented in Fig. 1 with atoms of W and S atoms indicated in the monolayer inset. The Selected Area Electron Diffraction (SAED) pattern is presented as inset in Fig. 1(a) with (100) and (010) diffraction spots marked. The d-spacing of (100)-type planes were measured from both HRTEM and SAED images as d = 2.76 ± 0.04 Å and d = 2.77 ± 0.06 Å respectively. Within experimental errors, this value agree with the d = 2.73 Å value obtained from the lattice parameter a = 3.1532 Å, reported in literature for 2H-WS239. The distances a1, a2 and a3 measured from this image are close to 3.15 Å value of the W–W interatomic distances in WS241. The bulk form of WS2 has an indirect band gap of ~1–1.4 eV27, and the features of the WS2 band structure are similar to those of MoS2 where a direct and indirect gap coexist irrespective of thickness41. A direct gap exists at the K point of the Brillouin zone between the spin–orbit split valence band and the doubly degenerate conduction band41. On the other hand, indirect gap forms between a local conduction band minimum at a midpoint between Γ and Κ and the valence band maximum at the Γ point41. As the number of layers decreases in WS2, the material changes into a direct band gap semiconductor with Eg~1.9–2.0 eV exhibiting photoluminescence. The elastic modulus of chemical vapor deposited WS2 has been reported to be ~170 N/m similar to 2H-MoS2, and about half the value of graphene which is the strongest 2D material42. While materials such as MoS2 have been intensely researched in recent years, there are only a few reports on structure, properties, and especially applications of WS2 and other layered 2D crystals41. The high strength, electronic properties, and excellent water uptake properties call for the development of ionic electro-mechanical actuators based on WS2.

Figure 1
Figure 1

Structure of WS2: (a) High-resolution TEM image of the WS2 single layer; insets are the SAED pattern and atomic structure of monolayer WS2 with atoms indicated in black and yellow; (b) Schematic of the semiconducting phase of WS2 for 2H-WS2; (c) 3R-WS2; (d) 2D structure of WS2 monolayer seen from above in triangular configuration.

The starting point for our electro-mechanical actuators is the liquid phase exfoliation of WS236 powders in a variety of solvents followed by centrifugation and separation of the layers as presented in Fig. 2(a). Eight different solvents were used: deionized water (DIW), ethanol (EtOH), acetone (Ace), methanol (MeOH), isopropyl alcohol (IPA), dimethyl formamide (DMF), N-vinylpyrrolidone (NVP) and N-Methyl Pyrrolidone (NMP). These enabled varying levels of exfoliation of the layers as presented n Fig. 2(a). Solvents such as NMP, NVP, and DMF gave rise to a high degree of exfoliation, and the color of the solutions suggest a high density of exfoliated layers. Figure 2(b) presents the UV-Visible spectroscopy of the exfoliated layers in different solvents. Lambert-Beer’s law as in A/l = αC, where A/l is the absorbance per unit length, α is the extinction coefficient, and C is the concentration was used to calculate extinction coefficients. The A/l scaled linearly with C provided the α values for the different types of solution. Table 1 presents the calculated extinction coefficients for different solvents. The extinction coefficient increase with a decrease in the number of layers in different solvents. Figure S1 (Suppl.) provides the optical absorption without the scattering component. The two peaks marked A (1.9 eV), and B (2.1 eV) correspond to the direct exciton transition at the K point (peaks assigned to excitons involving the conduction band and the two valence bands split due to spin-orbit coupling)43.

Figure 2
Figure 2

Liquid Phase Exfoliation: (a) Photograph of WS2 dispersions after exfoliation and centrifugation in different solvents; (b) UV- Visible spectra of the WS2 dispersions including their scattering components, (c) The correlation between the exfoliated solutions concentration and Hansen parameters for solvents which were employed, (d) Raman spectra (λexc = 532 nm) of WS2 few layers deposited on silicon wafer suggesting bulk, 4 L, 3 L, 2 L and 1 L flake.

Table 1 Absorption cut off and peak wavelength for different solvents.

Detailed analysis, within the framework of Hansen solubility parameter theory, shows successful solvents to be those with dispersive, polar, and H-bonding components of the cohesive energy density within certain well-defined ranges44. The dispersion of nanomaterials in liquids is partially predicted by the theory of Hansen solubility parameters (HSP), which is a semi-empirical correlation developed to explain dissolution behavior. Three HSP parameters are used to describe the character of a solvent or material: δD, δP, and δH, which are the dispersive, polar, and hydrogen bonding solubility parameters, respectively. Each solubility parameter represents the square root of the contribution to the cohesive energy density, and the sum of their squares equals the square of the Hildebrand solubility parameter: δT2 = δD2 + δP2 + δH2. Typical values for graphene analogs are δD (16–19 MPa1/2), δP (4–12 MPa1/2), and δH (2–19 MPa1/2)44. These were plotted for all the solvents suggesting an excellent agreement between theory and experiments. Figure 2(c) shows the dispersed concentration of different solvents versus Hansen solubility parameters. Based on these results, solvents that have H-parameter (δH) around 8, P-parameter (δP) around 13, and D-parameter (δD) around 18 are excellent choices as a solvent for exfoliation of WS2 as seen in our results and others36.

Figure 2(d) presents the Raman spectroscopy of the WS2 layers, and here we compared it to bulk. The spectra include the first order modes at the Brillouin zone center E2g and A1g plus a zone-edge mode activated by the disorder. This is identified as the longitudinal acoustic mode at the M point, LA(M). The longitudinal acoustic phonons LA (M) are the in-plane collective oscillations of the atoms in the lattice, similar to the sound waves. They are periodic compressions and expansions of the lattice that occur along the direction of propagation. For λexc = 532 nm, it is striking to see the LA(M) at 176 cm−1 and the first order modes E12g at 350 cm−1 and A1g mode at 417 cm−1 for the WS2 single layer. It should be noted that for λexc = 532 nm, the 2LA (M) mode is very close to the first-order E12g(Γ) mode at 350 cm−1. There is a red shift in E12g mode and blue shift in the A1g mode with decreasing number of layers that is the signature in the Raman spectra of WS2 few layers. The blue shift of the A1g mode is consistent with the increasing restoring force caused by van der Waals interactions established between the layers, and it is in agreement with previous results reported for MoS245 and WS246. The change in E2g with decreasing number of layers is quantified, and these results are presented in Table 2. The Raman shift is definitively indicative of 1 L, 2 L, 3 L, 4 L, and bulk. These are in excellent agreement with the other published papers on Raman spectroscopy of WS2 and MoS2 which are similar in structure45,46,47.

Table 2 The Raman shift for major picks in Raman spectra of WS2 flakes.

Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM) was conducted on all the exfoliated samples. Figure 3(a) presents the SEM image panel of the flakes exfoliated from all the solvents. The average height and width of the flakes are presented in the image. The average height and width of the flakes were calculated based on the statistical data obtained from 10 different samples, and over 100 flakes for each sample and these results are shown in detail in Figure S2 (Suppl.). NMP and DMF gave the smallest average height of ~7 nm. The height value may represent ten layers in average, but over 60% of these flakes had a height less than 5 nm, indicating 3–6 layers.

Figure 3
Figure 3

SEM and AFM Imaging of Exfoliated  WS2 Flakes. (a) SEM images of exfoliated WS2 flakes in different solvents; (b) AFM images of exfoliated WS2 flakes that were centrifuged at different speeds. Centrifugation time for SEM and AFM images were 90 minutes.

Figure 3(b) presents the AFM height profiles from several flakes. In Fig. 3(b), striking images of the triangular shape of the WS2 few layers are noted in the images. All these samples were exfoliated in DMF for 40 hours and had the same exfoliation condition. Such triangular shape confirms the lattice structure of WS2 as presented in the schematic of Fig. 1. The height image in each AFM micrograph shows the number of layers. It is clear that these are few layer flakes anywhere from 1–10 layers. In Figure S3 (Suppl.), the width of the flakes and the number of layers of the flakes exfoliated in DMF that were centrifuged at different speeds, are presented as histograms from the AFM images. We found that NMP is the best solvent with respect to both width and few number of layers of the flakes followed by NVP, DMF, IPA, MeOH, Ace, EtOH, and H2O. The ideal solvent should produce few number of layers with larger width of the 2D crystal. Slight differences in exfoliation yield are seen among different solvents, but the overall trends remain the same. Summarizing the gathered data using UV-visible spectra (Fig. 2), AFM statistics and SEM (Fig. 3), it can be concluded that as the wavelength of the major peak around 630 nm is decreased, the solution has a better yield regarding having a fewer number of layers. Also as the average width of the flakes inside the solution is increased, the scattering component of the UV-visible spectra is increased, and the slope of that component in logarithmic presentation (Fig. 2b) is larger.

Centrifugation resulted in exfoliated layers being separated from the bulk particles. We studied the effect of centrifugation speed on the shift in the wavelength of the WS2 signature peak obtained using UV-Visible optical absorbance as presented in Figure S4 (Suppl.). Samples that were exfoliated but not centrifuged were studied and compared to samples that were exfoliated and centrifuged at different speeds for 90 minutes. At 500 rpm (230 G), we saw the greatest change in the blue shifting of the optical absorbance to lower wavelengths. This suggests isolation of the exfoliated layers is highest after centrifugation. The absorbance was blue shifted to 640 nm (1.96 eV) suggesting isolation of few layers in solution. Above 500 rpm, the blue shift in the optical absorbance was small. It is observed that the width and height of flakes had a huge difference when the centrifugation speed was over 1500 rpm. However, when the centrifugation speed was increased to 3500 rpm, there was not a significant difference in the height of flakes while the width of flakes was reduced.

Finally, we also studied the effect of temperature on the exfoliation of the sample in DMF presented in Figure S5 (Suppl.). The sonication bath was heated to different temperatures from 30 °C to 60 °C during exfoliation and all of these samples were exfoliated in DMF. At low temperatures between 30–50 °C, there is no increase in UV-Visible optical absorbance suggesting no change in exfoliation yield with temperature. However, when the temperature was increased to 60 °C, it is striking to see an impressive increase in optical absorbance. The increase in optical absorption is a result of increasing number of few layers with temperature in the DMF solution. Past reports on graphene have reported a temperature of 127 °C-2000 °C to get appreciable few layers in thermal exfoliation process48. We see an unambiguous change in exfoliation yield at these low temperatures suggesting temperature dependent exfoliation can be a useful method for nanomanufacturing of TMDs. For 10°C increase in temperature above 50 °C, there is 300% increase in optical absorbance suggesting an increase in exfoliation yield by a similar amount. The mechanism of such thermal exfoliation in DMF and other solvents needs to be further understood in the future and beyond the scope of this paper.

Resonant Raman measurements provide fundamental information on the vibrational modes and internal structure of the 2D layered material. One can investigate fine details of lattice interactions from resonant Raman spectra due to strong electron-phonon interactions and appearance of the second-order Raman peaks. Due to similar energy bandgap and close energy of the A excitonic resonance, the 633 nm laser excitation also leads to resonant Raman signals in WS2. Figure 4(a) shows the unpolarized 633 nm Raman spectra of our pure Nafion, 0.05 wt.% and 0.1 wt. % exfoliated WS2 in Nafion samples. The inset shows the photoluminescence of the 0.1 wt.% WS2-Nafion composites. The intriguing light emission in these nanocomposites suggest access to the electronic states within the nanocomposites and suggest excellent dispersion of few layers. For a low concentration of WS2, Raman lines of Nafion are well visible, whereas, for higher concentration, the luminescence of WS2 dominates the recorded spectrum suggesting these composites themselves are good candidates to study photoluminescence. A pure Nafion spectrum was also measured and used for deconvolution of spectra obtained for 0.05 wt. % exfoliated WS2 sample. 2H-WS2, like most TMDs, has the D46h point group symmetry and 18 vibrational modes in the Γ-point, out of which, E22g, E12g, E1g, and A1g, are active first-order Raman modes28,47. Usually, E12g and A1g are only observed in Raman spectrum, as the E22g has a too low frequency for typical experimental set-ups, and the E22g is forbidden in backscattering geometry. Additionally, under resonant conditions, second-order Raman peaks is also observed. Resonant Raman spectra of our WS2 composite samples contain the second-order 2LA (M) peak at 351 cm−1 in addition to the first-order E12g(Γ), and the out-of-plane A modes at 355, and ~420 cm−1, respectively. For 633 nm excitations, the 2LA(M) mode is significantly enhanced with respect to the E12g while being in resonance with the excitonic absorption peaks. The lines positions are the same for both WS2 samples. Besides, both samples show a broadening and asymmetric line shape of the out-of-plane A mode, indicating a few layer flake morphology of WS246,49,50. In order to estimate the number of layers of WS2 inside the nanocomposite, we analyzed the line shape of the A mode (Fig. 4 (b)). For few layer samples, the symmetry (and the number of vibrational modes) of the WS2 structure is reduced to the D3h and D3d point groups for an odd and even number of layers, respectively. As shown recently, for a few layer WS2, the A mode peak consists of several components, and their number equals to the number of layers49. For an odd number of layers all components represent Raman active modes, i.e., both, in- and out-of-phase vibrations, are Raman active. On the other hand, for samples with an even number of layers, only in-phase vibrations are Raman active, but they are accompanied by weak infrared active modes located in between Raman modes. Peak deconvolution using pure Lorentzian lines of the A mode peak in 0.05 wt. % exfoliated WS2 yields undoubtedly three components. Moreover, we were able to get a very good fit using three components located at 420.5 cm−1, 418.5 cm−1 and 416.2 cm−1, respectively, i.e., at the locations reported previously for three layer WS249. Out of these three component modes, the first and last ones possess the \({A}_{1}^{{\prime} }\) symmetry (in-phase vibration), whereas the middle mode originates from an infrared active \({A}_{2}^{{\prime\prime}}\) mode, characterized by the middle layer fixed and the sulfur atoms (top and bottom layers) vibrating out-of-phase. The performed fitting indicates clearly that our WS2-Nafion composite samples contain mostly 3 L WS2 flakes. These observations are in-line with past reports on determining a number of layers based on Raman spectroscopy49.

Figure 4
Figure 4

Raman Spectroscopy: (a) Resonant Raman spectra of pure Nafion, 0.05 wt.% and 0.1 wt. % exfoliated WS2 in Nafion suggesting photoluminescence in 0.1 wt.% exfoliated WS2-Nafion nanocomposite; the inset shows the deconvoluted spectra of both exfoliated WS2 sample. (b) The fitting of A mode spectral region in exfoliated sample confirmed the 3 L structure of WS2 inside the nanocomposite suggesting a high dispersion of 3 layer flakes in the composite. The excitation wavelength was 633 nm.

Differential scanning calorimetry was used to investigate the water uptake in these nanocomposites. Figure 5(a) presents the thermograph of the pure Nafion, 0.5 wt. % WS2 powder in Nafion, and 0.5 wt. % exfoliated WS2 flakes in Nafion composites for the ambient condition. The large peak around 80 °C indicates the evaporation of water inside the actuators. When the same temperature range was applied for the second time immediately after the first run, the peak does not present itself anymore confirming water uptake and its evaporation (Figure S6(suppl.)). As it is observed in Fig. 5(a), the peak containing 0.5 wt. % exfoliated WS2 flakes is the largest, and it showed the highest water content among the samples. These results show higher porosity of Nafion composites that contain the exfoliated WS2 flakes compared to pure Nafion and Nafion-WS2 powder based nanocomposite. Figure S7(suppl.) compares the thermograph of the same three samples in fully wet condition. The peak amplitude is higher for all of the samples in comparison to their ambient condition suggesting water is the reason for the large dip in the endotherm. What is striking is the peak value of Nafion composite with exfoliated WS2 flakes is 300% larger than the pure and powder samples. We also calculated the first and second sweeps thermographs for ambient condition samples to calculate the water evaporation enthalpies. The enthalpies of evaporation ΔH (pure Nafion) = 11.056 mJ/mg; ΔH (0.5 wt.% powder WS2 in Nafion) = 13.2823 mJ/mg and ΔH (0.5 wt.% exfoliated WS2 in Nafion) = 42.107 mJ/mg. These suggest, greater than three times increase in enthalpy of water evaporation for the nanocomposites of exfoliated WS2/Nafion compared to pure Nafion. The exfoliated WS2-Nafion composite is, therefore, superb in water uptake ideal for proton exchange membranes for fuel cells.

Figure 5
Figure 5

Differential Scanning Calorimetry and Dynamic Mechanical Analysis: (a) Thermograph of fabricated Nafion composites and the valley shows the evaporation of the water from the samples, (b) Results of tensile test on Nafion composites in ambient and dry conditions suggesting softening of the WS2 Nafion actuators in wet condition. In the dry condition, they showed 114% improvement in elastic modulus with the addition of 0.5 wt.% WS2.

Next, mechanical properties of the samples were investigated using Dynamic Mechanical Analysis (DMA). Figure 5(b) compares the results of a tensile test of the pure Nafion, 0.5 wt. % WS2 powder in Nafion, and 0.5 wt. % exfoliated WS2 flakes in Nafion composites at the ambient and dry condition. This plot shows that the sample containing 0.5 wt. % exfoliated WS2 flakes has the least yield strength and elastic modulus at ambient condition. The average measured values were 159.5 MPa for pure Nafion, 165.1 MPa for 0.2 wt.% bulk WS2 powder-Nafion nanocomposite, 157.6 MPa for 0.05 wt.% exfoliated WS2-Nafion nanocomposite, 152.8 MPa for 0.1 wt.% exfoliated WS2-Nafion nanocomposite, 148.4 MPa for 0.2 wt.% exfoliated WS2–Nafion nanocomposite and 140.7 MPa for 0.5 wt.% exfoliated WS2-Nafion nanocomposites. As the amount of exfoliated WS2 increases, the mechanical properties decrease gradually suggesting increased water content in the sample with the addition of exfoliated WS2 in wet condition. However, the tensile test data on dry samples showed the highest strength was achieved for 0.5 wt.% exfoliated WS2-Nafion nanocomposite, which shows good dispersion. The measured values were 228.6 MPa for pure Nafion, 211.7 MPa for WS2 powder Nafion nanocomposite, 217.6 MPa for 0.05 wt.% exfoliated WS2-Nafion nanocomposite, 221.9 MPa for 0.1 wt.% exfoliated WS2-Nafion nanocomposite, 235.0 MPa for 0.2 wt.% exfoliated WS2-Nafion nanocomposite and finally 261.5 MPa for 0.5 wt.% WS2-Nafion nanocomposite. This suggests that water has significant activity in determining the mechanical properties of these nanocomposites even for pure Nafion. An increase in elastic modulus of dry samples by 185% compared to the wet samples for the 0.5 wt.% exfoliated samples suggest strong water adsorption in the exfoliated samples. In Nafion-graphene nanocomposites, addition of 0.1 wt.% and 1 wt.% graphene decreased the water uptake by twice15. In contrast, the water uptake increased when exfoliated WS2 was added to the Nafion. The measured values were 16.6% for pure Nafion, 16.8% for 0.2 wt.% WS2 powder-Nafion Nanocomposite, 17.1% for 0.05 wt.% exfoliated WS2-Nafion nanocomposite, 17.9% for 0.1 wt.% exfoliated WS2-Nafion nanocomposite, 20.5% for 0.2 wt.% exfoliated WS2-Nafion nanocomposite and 22.2% for 0.5 wt.% exfoliated WS2-Nafion nanocomposite. These values were calculated using this equation:

$$Water\,uptake\,( \% )=\frac{{m}_{ambient}-{m}_{dry}}{{m}_{wet}-{m}_{dry}}$$

where mambient and mwet are the mass of Nafion composite that was kept in ambient and in water bath for 48 hours, respectively. mdry is the mass of Nafion composite that was kept at 110 °C for 12 hours.

These results can be another indication of water content inside exfoliated sample in comparison to bulk and pure sample. Recent work has shown that clean non-aged TMDs such as MoS2 and WS2 are hydrophilic atomic layers51. Liquid exfoliated WS2 nanosheets have recently been demonstrated as ultrasensitive and stable chemiresistive humidity sensors52. Even single-layer of WS2 or MoS2 is a composite of a relatively more hydrophilic metal and a relatively less hydrophilic chalcogen atom51. Sonication and processing can enable the replacement of the chalcogens by oxygen from the ambient (during recasting process) which likely occupy the sulfur vacancy sites. Oxygen is a known hydrophilic atom due to its tendency to form hydrogen bonds with water molecules53. We believe this is the most likely mechanism for significantly increased water uptake in exfoliated samples and not seen in bulk WS2 powder based nanocomposites. The bulk powders were not sonicated before mixing, and thus no vacancies were created for oxygen atoms to occupy and bond with other water molecules subsequently. Another indication of higher porosity of the samples is the difference in their thickness while the same amount of Nafion was used. Table 3 compares the thickness of Nafion composites. The thickness of 0.5 wt. % exfoliated WS2 flakes in Nafion was 34% larger than 0.5 wt. % WS2 powder-Nafion composite and pure Nafion. Since the same amount of Nafion solution was used for all of the samples and the WS2 flakes have negligible volume, the higher thickness of the exfoliated WS2-Nafion composite can only be explained by water uptake by the samples (samples becoming fluffy due to increased water uptake) that contain exfoliated WS2 flakes.

Table 3 Properties of Nafion actuator samples.

X-ray photoelectron spectroscopy (XPS) was used to analyze the surface of the sample and is presented in Fig. 6. The survey spectra and the high-resolution regions of C1s, O1s, and S2p lines were measured for each sample. First, the large fluoride signal and the sulfur signal in the wide scan spectrum (Fig. 6a and b) indicates the success of incorporating Nafion chains to TMDs. The analysis shows for instance that the O1s peak consists of two dominant components, one at 533 eV and the other at 535.5 eV which were attributed to the C-O-C and C-SO3 oxygen bonding in the Nafion structure. The fitting of C1s region reveals several lines; each corresponds to the bonding in Nafion polymer structure. The lines at 285.4, 286.7, 287.7, 289.5, 290.5, 292.2, and 294 eV depict: C-C (sp3), C-O-C, C=O, C-SO3, C-F, CF2, and CF3 bonds, respectively. These peak assignments correspond to the Nafion chains. Interestingly, as the WS2 concentration increases so does the C-O-C signal. Also, for the 0.1 wt. % exfoliated WS2 sample; it is possible to observe the S2p line at 164.1 eV corresponding to W-S bonding in line with other reports54. The major line in this region (169.6 eV), visible for all three samples, originates from the C-SO3 bond in the Nafion structure.

Figure 6
Figure 6

X-ray photoelectron spectroscopy of Nafion-TMD Nanocomposites: XPS analysis of pure Nafion, 0.05 wt.% and 0.1 wt. % exfoliated WS2 in Nafion showing a set of survey spectra, and high-resolution regions of C 1s, O 1s and S2p lines. (a) The complete spectra of all the three samples; (b) S 2p spectra showing -SO3 bonding in Nafion, and weak W-S bonding only for 0.1wt.% WS2 dispersed in Nafion; (c,d) C 1s and O 1s spectra for Nafion, 0.05 wt.% and 0.1 wt.% exfoliated WS2 flakes in Nafion. The improved C-SO3, C-O-C and C=O peaks in 0.1 wt.% suggest successful integration of WS2 flakes with the polymer matrix.

To understand the actuation mechanisms, we conducted testing the samples with a known electric field. Figure 7(a) presents the schematic of the electromechanical actuation set-up and testing. WS2-Nafion composites were cut into 13 mm × 5 mm, and their electro-mechanical tip displacements were studied. Figure 7(b) shows the captured signal during the actuation of 0.5 wt. % exfoliated WS2 flakes in Nafion at 2 V and 5 Hz operation. The electric field of 2 V was applied as a square signal while displacement and current were measured simultaneously. An electrochemical workstation was used for the excitation signal and the current feedback through two wires that are connected to the electrodes at both sides of the actuator. The displacement at the tip of the actuator was captured using the laser displacement laser as presented in Fig. 7(b). Figure 7(c) presents the schematic of the actuator cross-section excited by an electric field. Positive charges diffuse toward the negative electrode. Three following regions can be identified: electrode layer, an interface layer, and a diffusion layer. The electrode is the conductive layer on top. The diffusion layer conducts the ions inside the composites toward the electrode and vice versa. The interface layer is between the electrode and diffusion layer and contains a high concentration of positive ions (cations). The accumulation of ions at the surface of the composite causes the elongation of the surface and deformation of the actuator. For large deformations, considering constant curvature, the maximum strain at the surface of the actuator is given by the following equation:

$${\varepsilon }_{max}=\frac{2t\delta }{{L}^{2}+{\delta }^{2}}$$

where t is the thickness, δ the lateral displacement measured using a laser displacement sensor, and L is the free length of the actuator. Figure 7(d) presents the displacements versus electric field from 0.1 V to 5 V. As it can be observed, the displacements increased with the electric field in all the actuators. The 0.5 wt.% exfoliated WS2 actuators showed the largest displacement at all electric fields. These are quite intriguing that small amount of TMDs can produce a robust and enhanced mechanical response at low voltages. The actuation was almost twice as high for the exfoliated actuators compared to pure Nafion, and the tip displacements (~0.15 mm at 2 V for 10 mm actuator free length) are higher than nanotube14 and graphene-based actuators15 suggesting hydrophilic TMDs are excellent choices for Nafion-based actuators. In carbon nanotube-Nafion actuators, the experiments were performed by dipping the bimorph in LiCl solution whereas here we performed the experiments in air under an ambient condition with actuation caused by cation motion inside the actuator. Further, the amount of nanotube used was also high (18 w/w%) compared to the actuator performance14. Here, we have used minute loading of ~0.5 wt.% for significant improvement in actuation. In electro-active graphene actuator, the tip displacement of 0.15 mm at 0.5 Hz for actuator free lengths of 25 mm15 is actually smaller than our actuators. For an actuator length of 13 mm and since 3 mm was used for clamping the wires, the actuation occurs in 10 mm length of our samples. Thus for 10 mm actuator free lengths, the tip displacement of our actuator is 0.15 mm. For the same free length, we expect our actuators to perform 2.5 times better than graphene-based actuators. There are several reasons for this: 1) Addition of graphene and carbon nanotubes reduces the water content inside the actuators, which could potentially be a problem for long-term stability and operation as both nanotubes and graphene are hydrophobic materials and can lead to faster dehydration15; 2) TMDs are hydrophilic materials and thus can provide long term operation without drifts as these actuators by holding more water. Our results are quite consistent from this point from thickness measurements, a large dip in the differential scanning calorimetry and measurements using dynamic mechanical analysis all point to water in the exfoliated TMD actuators. Further, the increase in proton conductivity with increase in exfoliated TMDs definitely point to better working of these actuators and faster actuation as new proton conducting pathways being established with the addition of TMDs. The photoluminescence in our actuators is also a new addition not possible in graphene-Nafion actuators and thus brings added functionality to Nafion-based actuators.

Figure 7
Figure 7

Testing Set-up, Actuation, and Actuator Model: (a) Schematic of the setup employed for characterizing the actuation of Nafion composites; (b) The actuation results of 0.5 wt. % exfoliated WS2 in Nafion composite at 5 Hz; (c) Schematic of different layers inside WS2 – Nafion composites suggesting electrode layer, interface layer and diffusion layer; (d) Displacement versus electric field for the different types of actuators at 1 Hz color coded in red, black and blue.

A supplementary video shows the displacement of the actuator under positive and negative electric field. This video shows the large actuation of 0.5 wt. % exfoliated WS2 in Nafion sample right after doping and deposition of the silver electrode. The voltage was swept between −10 volts to +10 volts while the scanning rate was maintained at 1 V/s for this video. Grid lines behind the actuator were set up to follow the displacement of the tip. Each of the grid line squares behind the actuator is 1 mm wide. As the video shows, large bending displacements can be obtained in the exfoliated sample. The sample is seen to follow the electric field, and the actuation is fully reversible. Due to non-symmetric plating, the actuator is also seen to undergo torsion during the positive half cycle. As the polarity of the electric field changes in the actuator so does the motion suggesting direct evidence for Li+ ion (cation) induced motion in this electro-mechanical actuator. This unexpected and large actuation in the video is a result of complex effects from the electrode symmetry, internal strains due to doping, water uptake, electro-osmotic pressure and recasting process, all of which can have a profound effect on actuation. In the video, one can see the fast bending of the actuator when the field is applied followed by a slow relaxation when the polarity is changed. This bending motion is a result of the movement of the cations due to the electro-osmotic pressure and diffusion of water through the nanochannels15. A reinforcing filler that can block or delay the water migration will be advantageous in improving the overall actuator performance, and thus 2D materials such as graphene and TMDs can provide a highly tortuous path to delay the onset of this water migration15. One could potentially obtain twisting, rolling, torsion and non-symmetric bending deformation in these actuators by changing the symmetry of the metal plating, ion density, water uptake and electric field.

Figure 8 presents the optical images of the six different composites that were investigated in this research. The top image from left to right are pure Nafion actuator, ~0.5 wt. % WS2 powder in Nafion, ~0.05 wt. % exfoliated WS2 flakes in Nafion, ~0.1 wt. % exfoliated WS2 flakes in Nafion, ~0.2 wt. % exfoliated WS2 flakes in Nafion and ~0.5 wt. % exfoliated WS2 flakes in Nafion. One can see the exfoliated samples changing colors as the amount of WS2 increases turning almost dark at 0.5 wt.% WS2. These suggest excellent dispersion of the exfoliated WS2 in Nafion. Figure 8 presents the actuation of all the six samples. The electric field amplitude for all of these experiments was kept at 5 V. It was observed from Fig. 8 that adding the WS2 bulk powder to Nafion did not produce a significant difference in actuation compared to pure Nafion. However, by adding exfoliated WS2 flakes to Nafion, the actuation of the Nafion composite improves with increasing WS2 weight percentage. There is a significant difference between the actuation of 0.1 wt. % and 0.2 wt. % of exfoliated WS2-Nafion nanocomposites. The inset in Fig. 8 shows the increasing strains with small additions of WS2 flakes into the Nafion polymer. The actuation strain increased by ~74% at 1 Hz for 0.5 wt. % exfoliated WS2-Nafion nanocomposites in comparison to pure Nafion samples suggesting adding small amounts of WS2 flakes into Nafion improves its overall electro-mechanical actuation. As the frequency increases, the strains decrease. The strain versus frequency has a linear relationship even at these low concentrations of WS2 suggesting excellent dispersion and actuation. Figure S8 (Suppl.) presents the voltage sweep and strain amplitude developed. The radius of curvature and the strains are presented. The largest strain was calculated to be 0.27%. Table 3 further summarizes the actuation results for WS2-Nafion composites. The strain amplitudes were compared to the pure Nafion when presenting the results. Figure 9 presented the results of long-term continuous actuation tests (5 hours) on the 0.5 wt.% WS2 flakes-Nafion composite when the 2 V square wave was applied at 1 Hz. The results suggest no drift in the actuators over this period, voltage and frequency suggesting excellent stability of the WS2-Nafion composites.

Figure 8
Figure 8

Strain Amplitudes Vs. Excitation Frequency: Actuation strains of fabricated samples at different excitation frequencies. The exfoliated WS2-Nafion nanocomposites resulted in better actuation at all frequencies tested. The samples are color coded in strain versus excitation frequency graph.

Figure 9
Figure 9

Long Term Actuation: Actuation of ~0.5 wt. % exfoliated WS2-Nafion composite shows consistent behavior over 18000 seconds suggesting excellent stability of these systems.

One of the important aspects of any electromechanical actuator is to explain the experimental results based on theory/simulations. Here we have presented an equivalent circuit model based on the different layers of the actuator. Figure 10 presents the equivalent circuit model of the WS2-Nafion composite actuator based on AC impedance spectroscopy. The RN is the resistance of the Nafion as a solid electrolyte for the electrochemical system, and W is the Warburg resistance for the diffusion of the ions toward the negative electrode. Ri and Ci are the resistance and capacitance of the interface layer, respectively. Re and Ce are the resistance and capacitance of the electrode, respectively. The excellent agreement between the experimental values and the simulation results based on the equivalent circuit suggest the circuit model presented explains well the working of this actuator. AC impedance spectroscopy was carried out in the range of 0.01 Hz to1 MHz, and the amplitude of excitation was 0.05 to have a linear response. Figure 10 shows the experimental data and the fitted curve based on the suggested equivalent circuit. This circuit was selected based on the internal structure of the actuator and the experimental data that was captured using AC impedance spectroscopy. According to the schematic structure of the Nafion in Fig. 7(c), Re and Ce for electrode and Ri and Ci for the interface layer have been considered. For the diffusion layer, a Warburg element and RN as the resistance of Nafion are placed in the circuit. If the Re and Ce were removed, the circuit looks like the Randle’s circuit which has been used for many electrochemical systems55. Since the electrode is attached to the actuator in series, Re and Ce as two parallel elements have been added to the Randle’s circuit. Based on the suggested equivalent circuit and experimental data, numerical optimization was employed to calculate the circuit elements value for each sample. The error for all of the simulated curve is less than 10% for all of the samples and considering the complex structure of Nafion; the model is precise, which agrees well with the experimental results. The high-frequency section of the Impedance curve is very similar to Randle’s circuit. As it has been shown, the end point of the curve is the resistance of the Nafion, and this value can be used to calculate the proton conductivity of the composite:

$$\sigma =\frac{t}{{{\rm{R}}}_{N}\times A}$$

where σ represents the proton conductivity, t is the thickness, RN is the Nafion resistance, and A is the area covered by the electrodes. Other elements of the equivalent circuit are also summarized in Table 4. The proton conductivity was 160% higher for the exfoliated nanocomposite compared to pure Nafion samples and in line with literature reports56. As it is observed, the only resistance which is higher for the exfoliated sample in comparison to the pure sample is the interface resistance (Ri). The other resistances including the Nafion resistance which represents the proton conductivity and Warburg element which represents the diffusion resistance of the composites are improved in the exfoliated samples significantly. Figure S9 (Suppl.) presents the cross-sectional view of the Nafion and 0.5 wt.% exfoliated WS2 Nafion nanocomposite sample under SEM. The cross-sectional SEM suggest two different morphologies. The pure Nafion is featureless (a), but the exfoliated WS2-Nafion nanocomposite show increased surface area with many features (b). In the figure, the flakes can be seen covered by the polymer suggesting uniform dispersion of the flakes. A single flake can be seen in the high magnification images in (c). The Nafion chains attached to the TMD flakes are providing proton conducting pathways for rapid proton transport through the sample. There is clear evidence for this as the proton conductivity steeply increases with increase in weight fraction of exfoliated TMDs as presented in Table 3. TMD-Nafion is also interconnecting the proton-conducting domains of the Nafion matrix thereby lengthening the proton-conducting channels of the sulfonic acid groups of the Nafion chain56. The increase in proton conductivity is also directly supported by the actuation results by almost twice.

Figure 10
Figure 10

AC Impedance Spectroscopy: AC impedance spectroscopy based characterization of fabricated Nafion composites and its corresponding equivalent circuit. The excellent agreement between the experiments and simulations presented indicate the description of the actuator is accurate and can serve as a model to explain the electromechanical behavior of Nafion-TMD nanocomposite.

Table 4 Equivalent circuit elements for Nafion actuators.

In summary, the ability to convert electrical energy into mechanical motion is one of the fundamental building blocks for modern day actuators. The efforts in recent years have been towards understanding various nanomaterials such as carbon nanotubes and graphene in polymers. For the first time, we show interesting effects of incorporating TMDs such as WS2 in Nafion and demonstrate the improvement in the electromechanical actuation performance. The most common TMD namely MoS2 share similar structure as WS2 and are hydrophilic. This opens a broader field of applications of different types of TMDs (MoS2, WS2, MoTe2, etc.) for electrochemical or electromechanical actuation. Morphological studies of TMD–Nafion composites by SEM, AFM, XPS, DSC, and DMA show that highly exfoliated TMDs few layers are dispersed homogeneously in the Nafion polymer matrix by solvent recasting method, which is also confirmed through the photoluminescence of these nanocomposites. Improvements in Young’s modulus of 114% was observed with the addition of 0.5 wt.% of TMDs in dry condition. The proton conductivity increased 160% with the addition of 0.5 wt.% TMDs in Nafion suggesting TMDs improve proton conducting pathways in Nafion, whereas a considerable increase in water uptake (300%) was observed for exfoliated TMDs in Nafion. The increased water uptake due to hydrophilic WS2 additives made the actuator softer in wet and ambient conditions as seen in DMA measurements and is ideal for building Nafion-based actuators as these actuators need water for their working. The defective sites created in WS2 due to the knocking of some of the chalcogen atoms during sonication process provided binding sites for oxygen molecules from the ambient that has natural tendency to form bonds with water. Hence the increased water uptake by unexpected measures. Compared to the recast Nafion-based IPMC actuator, large strain amplitudes of ~0.15% were achieved in 0.5 wt.% exfoliated TMD based Nafion composite actuators. These actuators also showed unusually large bending displacements at large electric fields. The tip displacements were larger than graphene and nanotube-based actuators and used minute quantities of exfoliated TMDs. In the future, one can explore the use of thinner and smaller TMD flakes to fabricate actuators. This can improve the surface area to volume ratio and provide a highly tortuous path to delay the onset of the water migration that can improve the overall actuation performance. Other aspects of using thinner and smaller flakes include increase in interfacial resistance, improvement in proton conducting pathways, increase in photoluminescence and improved water uptake. The results thus provide a foundation for this rich area of study for future development of electromechanical actuators based on TMDs and in general for the development of shape changing materials based on polymers with reversibility. Since TMDs also have high optical absorption, such TMD-Nafion composites could also be prime candidates for creating stimuli-responsive composites, solar water splitting, proton exchange membranes and fuel cells.


Liquid Phase Exfoliation, Imaging, and Optical Absorption Spectroscopy

Two kinds of WS2 powder, micro powder with an average particles size of 0.4–1 µm and ultrafine powder with an average particles size of 90 nm were purchased from Graphene Supermarket. Solvents and Nafion® perfluorinated resin solution (5 wt. %) were purchased from Sigma-Aldrich. 5 mg/ml WS2 ultrafine powder obtained from Graphene Supermarket was sonicated in 100 ml glass vials in DMF inside the bath sonicator for 40 hours at maximum power (110 W), and then it was centrifuged at 1500 rpm (700 G) for 90 minutes. The number of layers of the WS2 flakes was characterized using a NaioAFM of Nanosurf in tapping mode configuration with a cantilever resonance frequency of ~148 kHz. HRTEM was conducted using a transmission electron microscope (TM) (model F20 FEI Tecnai) with an accelerating voltage of 200 kV. The sample was prepared by dropping drops of exfoliated WS2 in ethanol solution on lacey-carbon Cu grids (Ted Pella Inc., CA). The Cu grids were then dried in air to make sure there are sufficient isolated flakes to be observed. SEM images of flakes were obtained using a JEOL JSM-7000F instrument at 20 kV of power and under an ultra-high vacuum, 10−5 Pa. A secondary electron detector was utilized at 8 mm working distance to capture high-resolution images of the WS2 flake at magnifications as high as 100,000X.

The optical absorbance of the WS2 solutions and the nanocomposites were measured in a wavelength range of 300 nm-1100 nm using a Hitachi U–5100 ratio beam spectrophotometer. Raman spectroscopy was conducted in Horiba Xplora Raman system with the power of the laser was kept at 0.2 mW, and for calibration, the phonon mode from the silicon substrate at 520 cm−1 was used. The laser beam (λexc = 532 nm) was focused onto the surface using a 100 × objective. The power was much below one mW, not enough to induce heating in the samples.

Sample Preparation

Nafion Actuator Fabrication

For pure Nafion actuator, 8 ml of Nafion was mixed with 4.6 ml DMF. The components were mixed in a 20 ml glass vial and sonicated for 1 hour. They were transferred to a glass petri dish with 48 mm in diameter. The dish was placed inside a vacuum oven, and it was heated at 110 °C for 4 hours followed by heating at 160 °C for 6 hours. After cooling down, the sample was immersed in DI water for 10 minutes; the as-casted film was then separated from petri dish by peeling. For drying the sample, the film was placed into a vacuum oven at 110 °C for 12 hours. After drying, the sample was soaked in 0.1 M lithium hydroxide at room temperature overnight for doping. After doping and drying in the ambient condition, both sides of the film were coated with thin film silver using sputtering (100 nm thickness). The sample was cut into the desired size (13 mm × 5 mm). The samples were then kept in the laboratory in ambient condition for 48 hours for relaxation before the actuation tests. The preparation steps are in line with many reports indicating that high-boiling-temperature polar solvents, N, N′-dimethyl formamide (DMF), ethylene glycol, hexamethyl phosphoramide, and dimethylacetamide, can be added to the Nafion solutions or used alone to prepare Nafion solutions to get good insoluble with desirable physical, and mechanical characteristics similar to those of the as received Nafion membranes57.

Bulk and Exfoliated WS2 actuators

For bulk WS2 actuator, the WS2 powder was mixed in DMF and Nafion solution. WS2 was exfoliated in DMF for these experiments using sonicator for 40 hours, followed by centrifugation at 1500 rpm to isolate the few layers. The concentration of the WS2 in DMF was 380 μg/ml. The weight of Nafion inside its initial solution was 43.7 mg/ml. Based on these numbers, the final solution for casting was prepared. For 0.5 wt. % exfoliated WS2 in Nafion, 4.6 ml of WS2 solution in DMF was added to 8 ml of Nafion solution. For other exfoliated samples the appropriate volume of WS2 solution in DMF was added to Nafion solution. In the end, the extra amount of pure DMF was added to all of the samples, so all of them had the same 4.6 ml of DMF. This is to ensure that the increase in actuation is not due to the amount of DMF. For example for 0.1 wt. % exfoliated WS2 in Nafion, 0.92 ml of WS2 solution in DMF was added to 8 ml of Nafion solution, and then 3.68 ml of DMF was added. The samples were then cast and prepared as mentioned above for pure Nafion actuator.

Resonant Raman Spectroscopy of Nanocomposites

Resonant Raman spectra of 0.05 wt. % and 0.1 wt. % exfoliated WS2 samples were recorded at room temperature in backscattering geometry with an inVia Renishaw micro-Raman spectrometer using a confocal setup with a 50x objective and excitation wavelengths of 633 nm. A silicon wafer was used for a calibration of the system. 1800 lines mm−1 grid was used to ensure a high spectral resolution of ~1 cm−1.

X-ray photoelectron (XPS) Spectroscopy

XPS measurements were carried out in VG Scientific MultiLab 3000 ultra-high vacuum surface analysis system equipped with CLAM4 hemispherical electron energy analyzer and X-ray source in the form of a dual-anode (Mg/Al) operating at 15 kV voltage and an emission current of 10 mA. XPS spectra were measured at the base chamber pressure in the 10−9 Torr range using a non-monochromatic Al Kα (hν = 1486.6 eV) X-ray radiation. To account for any possible sample charging, a C1s peak of the F-C-F bonding in Nafion at 292.2 eV was used for binding energy calibration. The analysis and deconvolution of XPS spectra were performed using the XPSPEAK41 software. The data was fitted using a pure Gaussian profile and a Shirley baseline subtraction.

Actuation Test Experiments

The actuator was clamped at one end, and the electric contacts are attached to the clamp as well. Micro-Trak laser displacement sensor was used to measure the deflection of the actuator. The laser was calibrated according to manufacturer specifications and then measured on the sample. Using CHI 660E electrochemical workstation, chronoamperometry and AC impedance spectroscopy tests were carried out on samples. For chronoamperometry test, a square waves electric field with different frequencies were applied on the electric contacts, and the current and displacement were measured using an electrochemical workstation and laser displacement sensor, respectively. For doing the AC impedance spectroscopy, measurements were carried out from 0.01 Hz to 1 MHz with the amplitude of 0.05 V for having a linear response. All samples were tested in identical conditions. The temperature was 23 °C with relative humidity RH~43%.

Dynamic Mechanical Analysis and Differential Scanning Calorimetry

Tensile test on the dry and hydrated samples at ambient condition was carried out using a Q800 TA Instruments Dynamic Mechanical Analyzer according to ASTM D882 standard. For measuring the water content of hydrated Nafion samples at fully wet and ambient conditions, Q20 TA Instruments Differential Scanning Calorimetry was used. A small piece of each sample was weighted and placed in a Tzero low mass pan, and the sample was heated from 10 °C to 180 °C.

Additional information

Change History: A correction to this article has been published and is linked from the HTML version of this paper. The error has been fixed in the paper.

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

A correction to this article is available online at

A correction to this article is available online at

Change history

  • 06 March 2018

    A correction to this article has been published and is linked from the HTML and PDF versions of this paper. The error has been fixed in the paper.

  • 05 January 2018

    A correction to this article has been published and is linked from the HTML version of this paper. The error has been fixed in the paper.


  1. 1.

    Petersen, A. Piezoelectric Actuators. F M-Feinwerktech Mes 86, 304–308 (1978).

  2. 2.

    Park, S. E. & Shrout, T. R. Ultrahigh strain and piezoelectric behavior in relaxor based ferroelectric single crystals. Journal of Applied Physics 82, 1804–1811, (1997).

  3. 3.

    Hashimoto, M., Takeda, M., Sagawa, H., Chiba, I. & Sato, K. Application of Shape Memory Alloy to Robotic Actuators. J Robotic Syst 2, 3–25 (1985).

  4. 4.

    Hirai, M. et al. Electrically-Induced Reversible Structural-Change of a Highly Swollen Polymer Gel Network. J Chem Soc Faraday T 91, 473–477, (1995).

  5. 5.

    Bar-Cohen, Y., Xue, T., Shahinpoor, M., Simpson, J. O. & Smith, J. Low-mass muscle actuators using electroactive polymers (EAP). Smart Structures and Materials 1998: SmartMaterials Technologies 3324, 218–223, (1998).

  6. 6.

    Shahinpoor, M., Bar-Cohen, Y., Xue, T., Simpson, J. O. & Smith, J. Some experimental results on ionic polymer-metal composites (IPMC) as biomimetic sensors and actuators. Smart Structures and Materials 1998: SmartMaterials Technologies 3324, 251–267, (1998).

  7. 7.

    Pelrine, R., Kornbluh, R., Pei, Q. B. & Joseph, J. High-speed electrically actuated elastomers with strain greater than 100%. Science 287, 836–839, (2000).

  8. 8.

    Binnig, G., Quate, C. F. & Gerber, C. Atomic Force Microscope. Phys Rev Lett 56, 930–933, (1986).

  9. 9.

    Villanueva, A., Smith, C. & Priya, S. A biomimetic robotic jellyfish (Robojelly) actuated by shape memory alloy composite actuators. Bioinspir Biomim 6, Artn 036004 10.1088/1748-3182/6/3/036004 (2011).

  10. 10.

    Iijima, S. & Ichihashi, T. Single-Shell Carbon Nanotubes of 1-Nm Diameter (Vol 363, Pg 603, 1993). Nature 364, 737–737 (1993).

  11. 11.

    Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669, (2004).

  12. 12.

    Baughman, R. H. et al. Carbon nanotube actuators. Science 284, 1340–1344, (1999).

  13. 13.

    Chen, L. Z. et al. High-Performance, Low-Voltage, and Easy-Operable Bending Actuator Based on Aligned Carbon Nanotube/Polymer Composites. Acs Nano 5, 1588–1593, (2011).

  14. 14.

    Landi, B. J. et al. Single wall carbon nanotube-Nafion composite actuators. Nano Lett 2, 1329–1332, (2002).

  15. 15.

    Jung, J. H., Jeon, J. H., Sridhar, V. & Oh, I. K. Electro-active graphene-Nafion actuators. Carbon 49, 1279–1289, (2011).

  16. 16.

    Grot, W. G. F., Mehra, V., Munn, G. E. & Solenberger, J. C. Nafion Electrolytic Separators. J Electrochem Soc 122, C104–C104 (1975).

  17. 17.

    Hora, C. J. & Maloney, D. E. Chemically Modified Nafion Perfluorosulfonic Acid Membranes as Separators in Chlor-Alkali Cells. J Electrochem Soc 124, C319–C319 (1977).

  18. 18.

    Pu, C., Huang, W. H., Ley, K. L. & Smotkin, E. S. A Methanol Impermeable Proton Conducting Composite Electrolyte System. J Electrochem Soc 142, L119–L120, (1995).

  19. 19.

    Bath, B. D., Lee, R. D., White, H. S. & Scott, E. R. Imaging molecular transport in porous membranes. Observation and analysis of electroosmotic flow in individual pores using the scanning electrochemical microscope. Anal Chem 70, 1047–1058, (1998).

  20. 20.

    Honda, K. & Hayashi, H. Prussian Blue Containing Nafion Composite Film as Rechargeable Battery. J Electrochem Soc 134, 1330–1334, (1987).

  21. 21.

    Schmidt-Rohr, K. & Chen, Q. Parallel cylindrical water nanochannels in Nafion fuel-cell membranes. Nat Mater 7, 75–83, (2008).

  22. 22.

    Bian, K., Liu, H. G., Tai, G. A., Zhu, K. J. & Xiong, K. Enhanced Actuation Response of Nafion-Based Ionic Polymer Metal Composites by Doping BaTiO3 Nanoparticles. J Phys Chem C 120, 12377–12384, (2016).

  23. 23.

    Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nat Nanotechnol 6, 147–150, (2011).

  24. 24.

    Lopez-Sanchez, O., Lembke, D., Kayci, M., Radenovic, A. & Kis, A. Ultrasensitive photodetectors based on monolayer MoS2. Nat Nanotechnol 8, 497–501, (2013).

  25. 25.

    Rahneshin, V., Khosravi, F., Ziolkowska, D. A., Jasinski, J. B. & Panchapakesan, B. Chromatic Mechanical Response in 2-D Layered Transition Metal Dichalcogenide (TMDs) based Nanocomposites. Sci Rep-Uk 6, doi:ARTN 34831 10.1038/srep34831 (2016).

  26. 26.

    Tsai, M. L. et al. Monolayer MoS2 Heterojunction Solar Cells. Acs Nano 8, 8317–8322, (2014).

  27. 27.

    Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically Thin MoS2: A New Direct-Gap Semiconductor. Phys Rev Lett 105, doi:ARTN 136805 10.1103/PhysRevLett.105.136805 (2010).

  28. 28.

    Klein, A., Tiefenbacher, S., Eyert, V., Pettenkofer, C. & Jaegermann, W. Electronic band structure of single-crystal and single-layer WS2: Influence of interlayer van der Waals interactions. Phys Rev B 64, doi:ARTN 205416 10.1103/PhysRevB.64.205416 (2001).

  29. 29.

    Bertolazzi, S., Brivio, J. & Kis, A. Stretching and Breaking of Ultrathin MoS2. Acs Nano 5, 9703–9709, (2011).

  30. 30.

    Griffith, A. A. The phenomenon of rupture and flow in solids. Philosophical Transactions of the Royal Society of Lonon, Series A 221, 163–198 (1921).

  31. 31.

    Britnell, L. et al. Strong Light-Matter Interactions in Heterostructures of Atomically Thin Films. Science 340, 1311–1314, (2013).

  32. 32.

    Li, H. et al. Fabrication of Single- and Multilayer MoS2 Film-Based Field-Effect Transistors for Sensing NO at Room Temperature. Small 8, 63–67, (2012).

  33. 33.

    Lukowski, M. A. et al. Enhanced Hydrogen Evolution Catalysis from Chemically Exfoliated Metallic MoS2 Nanosheets. J Am Chem Soc 135, 10274–10277, (2013).

  34. 34.

    Wang, T. Y., Chen, S. Q., Pang, H., Xue, H. G. & Yu, Y. MoS2-Based Nanocomposites for Electrochemical Energy Storage. Adv Sci 4, doi:ARTN 1600289 10.1002/advs.201600289 (2017).

  35. 35.

    Fan, X. M. et al. MoS2 actuators: reversible mechanical responses of MoS2-polymer nanocomposites to photons. Nanotechnology 26, doi:Artn 261001 10.1088/0957-4484/26/26/261001 (2015).

  36. 36.

    Coleman, J. N. et al. Two-Dimensional Nanosheets Produced by Liquid Exfoliation of Layered. Materials. Science 331, 568–571, (2011).

  37. 37.

    Li, H. et al. Mechanical Exfoliation and Characterization of Single- and Few-Layer Nanosheets of WSe2, TaS2, and TaSe2. Small 9, 1974–1981, (2013).

  38. 38.

    Lee, Y. H. et al. Synthesis of Large-Area MoS2 Atomic Layers with Chemical Vapor Deposition. Adv Mater 24, 2320–2325, (2012).

  39. 39.

    Schutte, W. J., Deboer, J. L. & Jellinek, F. Crystal-Structures of Tungsten Disulfide and Diselenide. J Solid State Chem 70, 207–209, (1987).

  40. 40.

    Ovchinnikov, D., Allain, A., Huang, Y. S., Dumcenco, D. & Kis, A. Electrical Transport Properties of Single-Layer WS2. Acs Nano 8, 8174–8181, (2014).

  41. 41.

    Zhao, W. J. et al. Evolution of Electronic Structure in Atomically Thin Sheets of WS2 and WSe2. Acs Nano 7, 791–797, (2013).

  42. 42.

    Liu, K. et al. Elastic Properties of Chemical-Vapor-Deposited Monolayer MoS2, WS2, and Their Bilayer Heterostructures. Nano Lett 14, 5097–5103, (2014).

  43. 43.

    Wilcoxon, J. P., Newcomer, P. P. & Samara, G. A. Synthesis and optical properties of MoS 2 and isomorphous nanoclusters in the quantum confinement regime. Journal of Applied Physics 84, 7934–7944 (1997).

  44. 44.

    Cunningham, G. et al. Solvent Exfoliation of Transition Metal Dichalcogenides: Dispersibility of Exfoliated Nanosheets Varies Only Weakly between Compounds. Acs Nano 6, 3468–3480, (2012).

  45. 45.

    Li, H. et al. From Bulk to Monolayer MoS2: Evolution of Raman Scattering. Adv Funct Mater 22, 1385–1390, (2012).

  46. 46.

    Berkdemir, A. et al. Identification of individual and few layers of WS2 using Raman Spectroscopy. Sci Rep-Uk 3, doi:ARTN 1755 10.1038/srep01755 (2013).

  47. 47.

    Zhao, W. J. et al. Lattice dynamics in mono- and few-layer sheets of WS2 and WSe2. Nanoscale 5, 9677–9683, (2013).

  48. 48.

    Zhang, H. B. et al. Vacuum-assisted synthesis of graphene from thermal exfoliation and reduction of graphite oxide. J Mater Chem 21, 5392–5397, (2011).

  49. 49.

    Staiger, M. et al. Splitting of monolayer out-of-plane A ‘(1) Raman mode in few-layer WS2. Phys Rev B 91, doi:ARTN 195419 10.1103/PhysRevB.91.195419 (2015).

  50. 50.

    Krause, M. et al. Diameter and Morphology Dependent Raman Signatures of WS2 Nanostructures. Chemphyschem 10, 2221–2225, (2009).

  51. 51.

    Chow, P. K. et al. Wetting of Mono and Few-Layered WS2 and MoS2 Films Supported on Si/SiO2 Substrates. Acs Nano 9, 3023–3031, (2015).

  52. 52.

    Jha, R. K. & Guha, P. K. Liquid exfoliated pristine WS2 nanosheets for ultrasensitive and highly stable chemiresistive humidity sensors. Nanotechnology 27, doi:Artn 475503 10.1088/0957-4484/27/47/475503 (2016).

  53. 53.

    Degennes, P. G. Wetting - Statics, and Dynamics. Rev Mod Phys 57, 827–863, (1985).

  54. 54.

    McCreary, K. M., Hanbicki, A. T., Jernigan, G. G., Culbertson, J. C. & Jonker, B. T. Synthesis of Large-Area WS2 monolayers with Exceptional Photoluminescence. Sci Rep-Uk 6, doi:ARTN 19159 10.1038/srep19159 (2016).

  55. 55.

    Randles, J. E. B. A cathode ray polarograph. Part II.—The current-voltage curves. Transactions of the Faraday Society 44, 327–338 (1948).

  56. 56.

    Liu, Y. L. et al. Preparation and applications of Nafion-functionalized multiwalled carbon nanotubes for proton exchange membrane fuel cells. J Mater Chem 20, 4409–4416, (2010).

  57. 57.

    Lin, H. L., Yu, T. L., Huang, C. H. & Lin, T. L. Morphology study of nafion membranes prepared by solutions casting. J Polym Sci Pol Phys 43, 3044–3057, (2005).

Download references


This work was supported partially by the following grants from the US National Science Foundation (CMMI: 1463869, ECCS: 1463987 and DMR: 1410678) for B.P. DAZ and JBJ acknowledge the Conn Center for Renewable Energy Research and funding from the US National Science Foundation EPSCoR Program (sub-award no. 3048111570-15-016). DAZ acknowledges the support from the Mobility Plus Program funded by the Ministry of Science and Higher Education of the Republic of Poland.

Author information


  1. Small Systems Laboratory Department of Mechanical Engineering, Worcester Polytechnic Institute, Worcester, MA, 01609, USA

    • Masoud S. Loeian
    • , Farhad Khosravi
    •  & Balaji Panchapakesan
  2. Conn Center for Renewable Energy Research, University of Louisville, Louisville, KY, 40292, USA

    • Dominika A. Ziolkowska
    •  & Jacek B. Jasinski
  3. Faculty of Physics, University of Warsaw Pasteura 5, 02-093, Warsaw, Poland

    • Dominika A. Ziolkowska


  1. Search for Masoud S. Loeian in:

  2. Search for Dominika A. Ziolkowska in:

  3. Search for Farhad Khosravi in:

  4. Search for Jacek B. Jasinski in:

  5. Search for Balaji Panchapakesan in:


M.S.L. and B.P. designed the experiments and wrote the manuscript. M.S.L. did the experiments and analyzed the data. F.K. assisted with SEM imaging of Nafion samples. D.A.Z. and J.B.J. did the resonant Raman scattering and XPS experiments and helped in the peak analysis of nanocomposites. J.B.J. did the HRTEM imaging.

Competing Interests

The authors declare that they have no competing interests.

Corresponding author

Correspondence to Balaji Panchapakesan.

Electronic supplementary material

About this article

Publication history






By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.