Characterization and Separation Performance of a Novel Polyethersulfone Membrane Blended with Acacia Gum


Novel polyethersulfone (PES) membranes blended with 0.1–3.0 wt. % of Acacia gum (AG) as a pore-former and antifouling agent were fabricated using phase inversion technique. The effect of AG on the pore-size, porosity, surface morphology, surface charge, hydrophilicity, and mechanical properties of PES/AG membranes was studied by scanning electron microscopy (SEM), Raman spectroscopy, contact angle and zeta potential measurements. The antifouling -properties of PES/AG membranes were evaluated using Escherichia coli bacteria and bovine serum albumine (BSA). The use of AG as an additive to PES membranes was found to increase the surface charge, hydrophilicity (by 20%), porosity (by 77%) and permeate flux (by about 130%). Moreover, PES/AG membranes demonstrated higher antifouling and tensile stress (by 31%) when compared to pure PES membranes. It was shown that the prepared PES/AG membranes efficiently removed lead ions from aqueous solutions. Both the sieving mechanism of the membrane and chelation of lead with AG macromolecules incorporated in the membrane matrix contributed to lead removal. The obtained results indicated that AG can be used as a novel pore-former, hydrophilizing and antifouling agent, as well as an enhancer to the mechanical and rejection properties of the PES membranes.


Polyethersulfone (PES) is a low price commercial polymer, which is widely used in phase inversion fabrication of the polymer membranes for microfiltration, ultrafiltration and gas separation due to its high mechanical strength and chemical stability1. However, PES is quite hydrophobic material (water contact angle between 65 and 80 degrees2) and membrane fouling is one of the main drawbacks of PES membranes3,4. As membrane fouling is more severe with hydrophobic membranes due to the hydrophobic interactions between solutes and the membranes5, the increase in the hydrophilicity of PES membranes is considered as one of the key approaches to mitigate this undesirable phenomenon. Whereas some researchers tried to change the surface properties of PES membrane to increase the hydrophilicity6,7, other researchers used some additives to the cast solution for the sake of lowering the membrane hydrophobicity and enhancing the membrane flux. Some of the frequently used hydrophilic non-solvent additives are: polyvinylpyrrolidone (PVP)8,9, alcohols10, polyethylene glycol (PEG)11,12 and cellulose acetate phthalate13. Such hydrophilic additives are known to cause thermodynamic instability and enhance the instantaneous de-mixing in the casting solutions; as a result, more hydrophilic membranes with larger pore size and higher flux are formed9. Moreover, amphiphilic compounds, which contain both hydrophobic and hydrophilic segments were also used as additives during casting of PES membranes14. Loh et al.15 found that hydrophilic segments of the amphiphilic additives segregated to the polymer/water interface, with the hydrophobic segment firmly anchored in the polymer matrix4,15. The addition of amphiphilic soybean phosphatidylcholine to the casting solution was reported to increase the membrane skin layer thickness and makes it more hydrophilic16. Amphiphilic sulfobetaine copolymer was added to a dope solution to increase hydrophilicity of PES membranes17. The flux recovery ratio of the membrane containing 1.57 wt.% of the copolymer in the casting solution was found to increase by more than 40%4. More details on using of amphiphilic additives for casting PES membranes might be found in a recent review4.

Lately, Acacia gum (AG) has received some significant attention by many scientists due to its amphiphilic nature18,19,20,21. AG is a natural gum which is extracted from the dried gummy exudation which can be found in some acacia trees species22. AG is mainly composed of high molecular weight polysaccharides (97%) and a proteionuos fraction (3%)23. The main mono-saccharides in AG are arobinopyranose (Ara), glucuronic acid (Glca), galactose (Gal) and rhamnose (Rha), while the main amino acids are alanine, arginine, glutamic acid, glycine and histidine23. AG is widely used in food industry as a surfactant and emulsifier24. Moreover, AG is extensively used in cosmetics, pharmaceutics and dentistry to combat periodontic bacteria and deposition of plaque due to its anti-bacterial properties25. Interestingly, AG is extensively used in the Middle East as a chewing gum to beat the harmful bacteria in the mouth which cause several gum diseases. Gazi et al.26 have found that chewing gums made with AG are more efficient in reducing plaque after seven days when compared with regular sugar-free gums. These amphiphilic and antibacterial properties of AG as an additive during membrane casting might be promising for improvement of hydrophilic and the antifouling properties of the PES membranes.

However, up to now, application of AG in the fabrication of PES membranes has not been reported in literature. In this study, AG for the first time has been used as an additive during casting of PES membranes. The aim of this work is to investigate the effect of using AG as an additive to casting solution on the properties and performance of PES membranes including its effect on pore size, porosity, flux, hydrophilicity, surface charge, antifouling and mechanical properties. The prepared PES/AG membranes were also used for lead removal from aqueous solutions. Lead is one of the heavy metals which have been strongly related to numerous health problems due to its high toxicity which can cause permanent intellectual disability and cancer27. Since lead was considered as persistent, bioaccumulative and toxic (PBT), it was banned from use in paints (in 1978) and fuels (in 1996) and now is replaced with other material which has less impact on environment28. However, as being persistent, lead is still found at above EPA action level of 15 ppb29 in surface waters and groundwater in many parts of the world28. Therefore, treatment of lead in water is imperative to circumvent human health risks.

Materials and Methods


N-Methyl-2-pyrrolidone (NMP), AG with a molecular weight of approximately 250,000 and bovine serum albumin (BSA) (molecular weight of 69 KDa) were purchased from Sigma-Aldrich (USA). PES (Ultrason-E 3010 in pellet form) was purchased from BASF (Germany). The non-solvent used in the coagulation bath was Millipore deionized water (DW).

Preparation of PES/AG membranes

PES/AG membranes were cast using the phase inversion technique using PHILOS flat sheet membrane casting system (Republic of Korea). PES/AG membrane samples were prepared with different loadings of AG (0.3, 0.5, 1.0, 1.5 and 3.0 wt.%) in the dope 16 wt.% PES/NMP solutions following the procedure described earlier30. For the preparation of the casting solutions; NMP, PES pellets and AG were mixed using digital mechanical stirrer (an IKA Ultra Turrax T25, USA) for 2 h at 60 °C. The dope solution was then degassed for about 6 h and cast on the surface of a clean glass plate using a casting knife with a gap height of 200 µm at casting speed of 2.5 m/min at 25 °C. After casting, the glass plate with a PES film was immersed in DW at room temperature (21 °C) and kept until the membrane was completely peeled off from the plate. The cast membranes were then washed and kept in DW for 24 h at room temperature to remove any traces of the solvent.

The dynamic viscosity of the casting solutions at different loading of AG was measured using an LVDVE115 viscosimeter (Brookfield Inc, USA). At least three measurements have been performed for each casting solution.

Membrane characterization and testing

Surface morphology and porous structure

The top and cross-sectional structures of the fabricated membranes were analyzed using Field Emission Scanning Electron Microscopy (FESEM) (Gemini model SUPRA 55VP-ZEISS) equipped with Energy-dispersive X-ray spectroscopy (EDX) (Oberkochen, Germany). Membrane samples were fractured using liquid nitrogen and all the membrane samples were coated with platinum before scanning. Vacuum condition (at 3 kV) was applied in order to obtain high resolution surface and cross-sectional SEM images of the membrane.

Gravimetric method was used to evaluate the porosity of the membrane31. In this method, the membranes were dried by keeping them inside an oven at a temperature of 50 °C for 24 h before weighing their mass (w d ). After that, the dried membranes were immersed in distilled water at 25 °C for another 24 h. The water droplets on the membranes surface were carefully wiped off using filter paper when the membrane was removed from water in order to be weighed again (w w ). Equation (1) is used to figure out the total porosity of the membrane (ε) using the average values of the wet and dry masses of each membrane sample:

$$\varepsilon =\,\frac{{w}_{w}-{w}_{d}}{A.l.\rho }\times 100$$

where w w , w d are the wet and dry masses of the membranes, respectively, ρ is the density of the distillated water at 25 °C31, A is the membrane surface area (m2) and l is the thickness of the membranes.

The pore sizes of the prepared membranes can be figured out using Guerout–Elford–Ferry equation and the membrane porosity values32:

$${r}_{m}=\sqrt{\frac{(2.9-1.75\varepsilon )8\,\eta lQ}{\varepsilon A{\rm{\Delta }}P}}$$

where Q is the volume of pure water (permeate) expressed in m3/s, η is the viscosity of water at 25 °C which is 8.9 × 10−4 Pa s and ΔP is the operating pressure which is 4 bar.

Membrane hydrophilicity and surface charge

Ramé-hart Model 200 standard contact angle goniometer was used to measure the water contact angle between the water droplet and the membrane surface with a drop size of 2.0 μl. The contact angle of every sample was measured at 3 different points on the membrane surface.

The electrokinetic analyser SurPass 3 (Anton Paar KG, Austria) was used to measure the zeta potentials of the membrane surfaces. Helmholz–Smoluchowsky equation was used to figure out the value of the zeta potential from the slope of the streaming potential versus operating pressure plot (Equation 3)33:

$${\rm{\zeta }}=\frac{{\rm{\Delta }}E\,{\rm{\mu }}\,k}{{\rm{\Delta }}P\,{{\rm{\phi }}}_{0}{{\rm{\phi }}}_{{\rm{r}}}}$$

where k is the conductivity of the electrolyte, μ is the solution viscosity, ΔE is the streaming potential, φ r is the dielectric constant of water (at 25 °C), φ 0 is the vacuum permittivity of a and ΔP is the pressure drop across the membrane. Surpass 3 electrokinetic analyser can be described simply as a measuring cell in which two membrane pieces are positioned facing each other with 100 µm gap in between and an aqueous solution of 1 mM KCl and pH of 5.3 ± 0.2 passes inside the measuring cell. Two silver electrodes were employed to figure out the electrical potential difference. In order to conduct a pH scan of the zeta potential (zeta potential measurement at different pH values), 0.1 M NaOH and 0.1 M HCl solutions were used to change the pH of the KCl solution.

Fourier Transform Infrared (FTIR) and Raman spectrometer

Nicolet 6700 Thermo Scientific-FITR spectrometer (USA) and Thermo Scientific Nicolet Raman spectrometer were used to analyze the FTIR and Raman spectra of the membrane samples.

Membrane filtration tests

A dead-end stirred cell (HP4750X from Sterlitech (USA)) was used to carry out the filtration tests. The used cell has a volume of 0.3 L and the membrane area of 14.6 cm2. Nitrogen gas was used for the pressurization of the cell.

Equation (4) is used to figure out the amount of permeate flux (J) obtained:


where A is the membrane cross-sectional area (m2), T is the time of permeation (hours), and Q is the permeate volume (L).

Equation (5) was used to estimate the lead rejection with the membrane sample:

$$R( \% )=(1-\frac{{C}_{P}}{{C}_{f}})\times 100$$

where C f is the concentration of lead in the feed and C p is the concentration of lead in the permeate solution.

Lead solutions of 500 ppb were prepared from lead nitrate (PbNO3) and used as a feed. Aurora Elite-Bruker Inductively coupled plasma mass spectrometry (Germany) was used to evaluate the lead concentration in the feed and permeate. Bovine serum albumin (BSA) solution at a concentration of 100 mg/L and at pH 6.5 was used to conduct the fouling tests of the membranes. In this test, initial deionized water (DW) flux of the membranes (J0) was calculated first by filtration of DW for 15 min at operating pressure of 4 bar. After that, the 100 mg/L BSA solution was filtered through membranes for two hours at the same pressure. The membranes were then rinsed thoroughly with DW and water flux after BSA filtration (Jf) was measured. The normalized flux (Jn) values were then calculated using equation (6):


Stability tests of PES/AG membranes

The stability of PES/AG membranes was tested using two different methods; the first method involved FTIR analysing of permeate collected during DW filtration for 3 and 30 min. The spectra were then compared with that of pure DW. The second method involved the immersion of the membrane in DW and sonication with an ultrasonic bath (Branson 8510, USA) with 50/60 Hz for 30 min. After the ultra-sonication, FTIR spectra of the immersing water were recorded and compared with that of pure DW. Also, DW was filtered through the ultra-sonicated PES/AG membranes and the FTIR spectra of the collected permeate were compared with that of DI water.

Testing of PES/AG membranes with bacterial suspensions

Escherichia coli (E.coli) were used to test the antibacterial behavior of the fabricated membranes. A stock E.coli suspension was cultured in nutrient broth media. In this work, an E.coli suspension with cell concentration of 20 × 107 CFU/ml was prepared from the stock suspension by appropriate dilution in nutrient broth (the dilution is based on optical density of the suspensions at 600 nm) and used for membrane testing. The fabricated membranes were dipped in the E.coli suspension for about 10 min before being transferred to be placed on top of nutrient agar plates. The agar plates were inserted into an incubator at 35 °C and left for overnight. FE-SEM was used to inspect the presence of CFUs on the surface of the membranes.

Mechanical testing of the membranes

CT3 Texture Analyzer from Brookfield Engineering (USA) was used to analyse the mechanical properties of the membranes. In this test, the uniaxial tensile behaviour of the membranes was analyzed. In order to conduct the test, the fabricated membranes were cut to a rectangular shape with a size of 75 mm and 25 mm before being dried in oven for overnight. The texture analyser is used to determine the peak load at a crosshead speed of 5 mm/min (following ISO 527-3). The analysis was conducted three times for each sample and the average value was reported. As an indication of the mechanical strength of the membranes, the tensile stress values of the membranes were evaluated. Tensile stress values were calculated from the peak load and the cross-section area of the membrane.

Results and Discussions

Membrane morphology and pore size

FE-SEM was used to inspect the top and cross-section area of the fabricated membranes. As seen in Fig. 1, both pure PES and PES/AG membranes have a thin top layer and a sponge-like substructure with macro-voids; however, the macro-voids in the PES/AG membrane samples were obviously larger (Fig. 1b and c). Usually, the formation of such types of porous membrane structures is a result of the instantaneous de-mixing during the phase inversion34. By enhancing the thermodynamic imbalance in the doping solution, AG behaves as a non-solvent agent in the de-mixing step due to high solubility in water. The overall result is an increase in the phase separation and a faster exchange between non-solvent and the solvent during the de-mixing step which in turn results in increasing the porosity of the top skin layer and the lower sub-layer. In this sense the role of AG in the formation of a porous structure of PES membranes during casting is similar to other polymer additives reported in the literature35,36,37,38,39. However as seen in Fig. 1c, high AG loading resulted in decreasing the macro-voids size in the fabricated membrane. This might be explained due to the increase in the viscosity of the casting solutions which slows down the precipitation process and as a result a membrane with lower porosity is formed40,41.

Figure 1

SEM cross-sections of PES membranes at different AG loadings (wt.%) in the dope solutions: (a) 0% AG, (b) 1% AG and (c) 3% AG.

The SEM findings correlate with data on average porosity of the prepared membrane samples and on viscosity of the casting solutions (Fig. 2). As seen in Fig. 2a, the porosity of the membranes was found to increase with increasing AG content reaching the highest value at 1 wt.% AG in the dope solutions then decreasing slightly after that. The porosity of the PES/AG membrane was found to increase by 77% (at 1 wt.% AG) compared to pure PES membranes. The increase in porosity of the cast membranes when hydrophilic additives were added was also described by Liu et al.40 and van de Witte et al.41 who reported that the use of hydrophilic species in the casting solution results in an accelerated solvent and non-solvent exchange which in turn increases the development of a highly porous membrane structure. The additional increase in the AG loading (>1 wt.%) resulted in decreasing the porosity of the fabricated membranes. This might be explained due to the increase in the viscosity of the casting solutions which slows down the precipitation process. The overall effect is a membrane with a thicker top layer with lower porosity and pore interconnectivity40,41.

Figure 2

Total porosity (a), average pore size (b) of PES/AG membranes as well as the dope viscosity (c) at different AG loading (wt.%) in the casting solutions.

Figure 2b shows the average pore sizes of the fabricated membranes which were calculated using Eq. 2. The average pore radius was between 7.2 and 9.3 nanometers which is in the range of nanofiltration membranes. During the phase inversion process, AG behaved as a non-solvent agent by amplifying the thermodynamic instability in the casting solution. This results in the formation of more porous membrane structure in the presence of AG due to the quick exchange between the solvent and non-solvent. On the other hand, when AG loading in the casting solution was increased beyond 0.5 wt.%, the pore size was found to drop slightly down to 7.2 nm. This behavior has been reported to occur due to impact of high loading of the additive on the viscosity of the casting solutions42. At some point the addition of high molecular weight AG increased the viscosity of the casting solutions to such level that the de-mixing ratio between the polymeric and aqueous phases decreased and the membranes with smaller pores were formed.

The measured viscosity data was in good correlation with the above made consumptions. As seen in Fig. 2c, the dynamic viscosity of the casting solutions increases with AG loading from 172 ± 5 cP for the dope solution without AG up to 238 ± 8 cP for the dope solution with 3 wt.% of AG. As the low ratio of hydrophilic AG was added to casting solution, the thermodynamic stability of the casting solution obviously decreased; such phenomena caused an increase in the phase inversion kinetics during the membrane formation. As the mass transfer rate between the solvent (NMP) and nonsolvent (water) increased, we observed formation of membranes with higher porosity and pore size. However, according to Fig. 2c, when 1wt. % or higher of AG was added to the casting solution, the viscosity of the casting solution increased dramatically (204 ± 5 to 238 ± 8 cP). Such increment resulted in lower mass transfer rate between the solvent and non-solvent and membranes with lower porosity and pore size were formed.

Raman spectra of PES/AG membranes

Figure 3a shows the Raman spectra of AG (powder) while Fig. 3b presents the Raman spectra of the pure PES membrane and PES membrane embedded with AG (3 wt.%). The spectra obtained through Raman analysis confirmed the molecular structure of PES43. AG embedded membrane shows a peak at 2852.6 to 2986.4 cm−1 which correspond to methylene groups in AG macromolecules. This peak was the most intense Raman peak of pure AG powder as shown in Fig. 3a. The frequency bands of PES and PES/AG show some slight shifting (between 3–6 cm−1) after embedding with AG.

Figure 3

Raman spectra of (a) AG and (b) pure PES and PES/AG (3 wt.% in the casting solution) membranes.

Contact angle and zeta potential measurements

The hydrophilicity of the fabricated membranes was evaluated by measuring the contact angle between the membrane surfaces and water droplets. Figure 4a shows the water contact angles values of PES/AG membranes with different AG loading. The effect of adding AG was found to increase the hydrophilicity of the fabricated membranes by lowering the contact angle by 20% (the sample cast at 3 wt.% AG) when compared to pure PES membrane. The reason behind the drop in the contact angle of PES membranes when AG was added can be explained by the distribution of the AG macromolecules to hydrophilize the membrane surface and pores. This is similar to how the amphiphilic nature of AG is used for the stabilization of oil-water emulsions by the adsorption of the hydrophobic sites of AG macromolecules onto the oil droplets surface whereas the hydrophilic residues of AG macromolecule inhibits droplet aggregation and coalescence44. While casting PES/AG membranes, the hydrophobic residues of AG macromolecules possess high interaction with the hydrophobic methyl groups in PES whereas polysaccharide fragments in AG hydrophilize the membrane pores and surface.

Figure 4

Contact angle (a) and zeta potential (b) of PES/AG membranes at different AG loading in the casting solutions.

Zeta potential of pure PES and PES/AG membranes (0.5, 1.0 and 3.0 wt.%) at different pH values (3.9–8.5) is depicted in Fig. 4b. As shown, pure PES membranes, which were in direct contact with KCl solution, demonstrated relatively small negative zeta potential values between −0.9 and −19.8 mV with marginal increase in charge between pH 6.1 and 8.6. The reason behind the increase in the surface charge of the membrane along with the increase in the pH is explained by Ariza and Benavente45 who related this behavior to adsorption of chloride ions from the background electrolyte solution on the membrane surface. The use of AG as an additive to the casting solutions was found to increase the value of the negative zeta potential of the fabricated membranes. The reason behind this could be due to the affixation of some AG macromolecules to PES membranes which end up with (i) strong anchoring of some hydrophobic fragments of AG to PES polymer matrix and (ii) functionalization of the membrane surface with carboxylic groups due to the presence of some polysaccharide residues; these carboxylic groups is thought to dissociate at specific pH conditions. Niu et al.46 have reported that at pH above 1.9, AG macromolecules act as a weak polyelectrolyte bearing negative charge due to the dissociation of carboxyl groups. The effect of having high surface charge and hydrophilicity on PES membranes is thought to be very useful in lowering the membrane fouling with hydrophobic and charge foulants while separating proteins, bacteria and other organic compounds.

Water fluxes and lead removal with PES/AG membranes

The water flux values of the fabricated membranes at different AG loading in the dope solutions shown in Fig. 5a. The addition of AG into the casting solutions of PES was observed to increase the permeate flux by up to 130% (PES/1 wt.% AG membrane) when compared with pure PES membrane. The flux increase can be attributed to the increase in the membranes’ porosity and hydrophilicity. It should be noted that the flux increase for PES/AG membranes was significantly higher than what has been reported in literature when other additives such as PVP, lithium salts, montmorillonite and 1-vinylpyrrolidone-co-styrene copolymers were used during casting of PES membranes6,47,48,49.

Figure 5

Water fluxes for PES membranes with different AG loading (a) and lead rejection versus permeate volume during filtration of 500 ppb lead solutions with bare PES and PES/AG (2 & 3 wt.%) membranes (b). pH is 6.5. Operating pressure is 4 bar.

The separation properties of the fabricated membranes were tested by filtration of 500 ppb lead solutions at different feed pH values. As seen in Fig. 5b, lead rejection with PES/2 &3 wt.% AG membranes were much higher than that of pure PES membrane. The rejection capability of PES/AG membranes is thought to occur due to both the sieving (steric) rejection and complexation of lead ions with amino groups of proteionuos fraction of AG. The latter can be justified by conducting energy-dispersive X-Ray spectroscopy (EDS) on the membranes before and after lead filtration. The membrane’s surfaces were analyzed in order to account for the entrapped lead ions within the membrane matrix. Elemental compositions (mas. %) of lead in PES membranes at different AG loading in the dope solutions before and after lead filtrations are shown in Table 1.

Table 1 Elemental composition (mas. %) of lead in PES membranes at different AG loading in the dope solutions before and after lead filtration.

As seen in Table 1, the percentage of lead bound to PES/AG membrane was higher than that for pure PES membrane. Furthermore, the lead content in PES/3 wt.% AG membrane was higher than that of PES/1 wt.% AG membrane due to a large number of chelating sites available for binding lead ions.

Proteionous fraction of AG contains different amino acids which have strong affinity and distinctive kinetics towards chelating of metallic ions. Amino acids are considered as natural ligands and the ability of amino acids to form lead/amino acid complexes has been widely reported in literature50,51,52,53. In fact the strong affinity between the metal and amino acids is responsible for the spread and accumulation of metals inside organs which leads to the development of some histological abnormalities in patients under parental nutrition treatment50,54,55,56,57. Nascimento et al.50 have listed the order of affinity of amino acids towards lead and cadmium based on the stability constants of metal complexes: alanine> aspartic acid> glutamic acid> glycine> histidine> methionine> phenylalanine> seine> threonine50. The presence of these amino acids in significant proportions (as high as 134 residues per 1000 residues of proteinaceous component of commercially-available AG58) could be responsible for lead binding with PES/AG membranes. The schematic presentation of lead complexation with glycine present in AG is depicted as an insert in Fig. 5b.

Antibacterial testing of the fabricated membranes with E. coli bacteria

The antibacterial properties of PES/AG membranes were tested by the incubation of E.coli on the surface of the fabricated membranes for 24 h. As shown in Fig. 6a, PES membrane surface is thoroughly covered with a layer of bacterial cells after incubation of E.coli bacteria. On the other hand, at the identical conditions only few bacterial cells were found on the surface of the PES/3% AG membrane (Fig. 6b). Several research papers have tested and reported the antibacterial properties of AG against different strains of bacteria59,60,61,62; however, the antimicrobial mechanism of AG has not been covered fully in literature. Tyler63 and Kirtikar64 reported that the reason behind the antibacterial properties of AG could be due to the presence of some active enzymes (such as: peroxidases, oxidases and pectinases) which are known to have antimicrobial properties65. In addition to the presence of these antibacterial enzymes, we believe that the antifouling properties of PES/AG membranes could also be due to the increase in hydrophilicity and surface charge which has an effect on lowering the attachment of bacterial cells on the membrane surface.

Figure 6

FESEM images of the membrane surfaces after the incubation of E.coli cells as described in section 2.3.7: (a) Pure PES membrane (b) PES membrane with 3 wt. % AG in the dope solution; (c) PES membrane with 1 wt. % of AG in the dope solution after filtration of DW for 4 h and incubation of E.coli bacteria.

Moreover DW was filtered through the PES/AG membrane for 4 h before incubating E.coli bacteria on the membrane surface. As seen in Fig. 6c, only few bacterial cells were found on the surface of the conditioned membrane sample. Thus, the conditioned PES/AG membranes preserve their antifouling properties and this is indirect confirmation of the steady incorporation of AG into the membrane. The stability of AG compounds in the PES matrix was also assessed by recording of FTIR spectra of the permeate during filtration of DI water. As seen in Fig. 7 the permeate spectra collected after different filtration time were identical to spectra for DI water which indicates the absence of AG in the permeate and prove the stability of AG anchoring in the polymer matrix. Furthermore, the stability of the PS/AG membranes was also tested by ultra-sonication of the membrane samples for 30 min. Both the immersing water and the permeate collected after the filtration of ultrasonicated membranes with DI were analysed. The observed spectra were identical to that of DI, that further indicates the stability of the prepared membranes.

Figure 7

FTIR of ultrapure water (UPW) water and collected permeate after 3 and 30 minutes of filtration using UPW through PES/AG membrane (1 wt.% in the casting solution).

Fouling test of the membranes with BSA

The fouling test of the PES/AG membranes was conducted by filtering the BSA solution using dead end cell. Figure 8 shows the normalized water flux of PES/AG membranes with 0, 0.3, 0.5, 1.0 and 1.5 wt.% AG content in the dope solution after BSA filtration for two hours. Due to the increase in the hydrophilicity and surface charge, the AG-containing membranes showed higher normalized flux values when compared with pure PES membrane. The reduction in hydrophobicity and increase in the surface charge of the membrane has been reported by several researchers to lower the susceptibility of fouling due to the reduction in the interaction between the foulants and the membrane surface66.

Figure 8

Normalized flux of the PES membranes containing 0, 0.3, 0.5, 1.0 and 1.5 wt.% AG in the dope solution after filtration of BSA solution (100 ppm) for two hours at pH 6.5.

Mechanical testing of the membrane samples

The mechanical properties of the fabricated membranes were characterized using tensile strength test with Brookfield CT3 Texture Analyzer (USA). The maximum tensile stress of PES/AG membranes achieved before snapping is shown in Fig. 9. It was seen that AG addition was found to enhance the mechanical properties of the membrane samples. For instance, PES membrane cast at 3 wt.% of AG demonstrated the increase in the tensile stress by about 31% compared to pure PES membranes. The possible explanation behind the significant enhancement in the mechanical properties of PES/AG membranes is that the addition of the amphiphilic high molecular weight AG to the casting solution results in the anchoring of AG macromolecules to the porous polymer PES matrix by means of the multipoint hydrophobic interactions between PES backbone and hydrophobic residues in AG macromolecules; this will in turn strengthen the porous membrane structure and increase its mechanical properties.

Figure 9

Stress values (MPa) of PES/AG membranes cast at different AG loading in the casting solution.


In summary, in this work, AG was used for the first time as a new additive for the casting of PES membranes. The use of AG was found to remarkably enhance the surface charge, hydrophilicity, rejection, flux and antifouling properties of the fabricated membranes. The flux and the porosity of the PES/1wt.% AG membrane were increased by about 130% and 77%, respectively compared to pure PES membrane. The negative surface charge of the PES/3 wt.% AG membrane was increased from −11.1 to −24.6 mV while the contact angle of the same membrane was reduced by about 20% when compared to bare PES membranes. The reason behind the enhancement in the properties of the fabricated membranes can be attributed to the chemical composition of the AG macromolecules which contains a large number of hydrophilic residues, including carboxyl groups which attach themselves into the surface and the pore walls of the fabricated membranes. The overall effect of the increase in the surface charge and hydrophilicity of the membranes is the reduction in the membrane fouling with BSA. The bacterial tests showed that there was no growth of E.coli bacteria on the PES/AG membranes surface which means the fabricated membranes possess antibacterial properties. Moreover, the fabricated PES/AG membranes are capable to chelation with lead ions to enhance the rejection of the heavy metal. This study showed that AG is a promising additive to the casting solutions during fabrication of PES membranes with enhanced performance in water treatment applications.


  1. 1.

    Rastegarpanah, A. & Mortaheb, H. R. Surface treatment of polyethersulfone membranes for applying in desalination by direct contact membrane distillation. Desalination 377, 99–107, (2016).

    CAS  Article  Google Scholar 

  2. 2.

    Rahimpour, A. & Madaeni, S. S. Improvement of performance and surface properties of nano-porous polyethersulfone (PES) membrane using hydrophilic monomers as additives in the casting solution. Journal of Membrane Science 360, 371–379, (2010).

    CAS  Article  Google Scholar 

  3. 3.

    Shi, Q. et al. A facile method for synthesis of pegylated polyethersulfone and its application in fabrication of antifouling ultrafiltration membrane. Journal of Membrane Science 303, 204–212 (2007).

    CAS  Article  Google Scholar 

  4. 4.

    Ahmad, A. L., Abdulkarim, A. A., Ooi, B. S. & Ismail, S. Recent development in additives modifications of polyethersulfone membrane for flux enhancement. Chemical Engineering Journal 223, 246–267, (2013).

    CAS  Article  Google Scholar 

  5. 5.

    Choi, J.-G., Bae, T.-H., Kim, J.-H., Tak, T.-M. & Randall, A. The behavior of membrane fouling initiation on the crossflow membrane bioreactor system. Journal of Membrane Science 203, 103–113 (2002).

    CAS  Article  Google Scholar 

  6. 6.

    Bolong, N., Ismail, A. F., Salim, M. R., Rana, D. & Matsuura, T. Development and characterization of novel charged surface modification macromolecule to polyethersulfone hollow fiber membrane with polyvinylpyrrolidone and water. Journal of membrane science 331, 40–49 (2009).

    CAS  Article  Google Scholar 

  7. 7.

    Rahimpour, A., Madaeni, S. & Mansourpanah, Y. The effect of anionic, non-ionic and cationic surfactants on morphology and performance of polyethersulfone ultrafiltration membranes for milk concentration. Journal of Membrane Science 296, 110–121 (2007).

    CAS  Article  Google Scholar 

  8. 8.

    Wienk, I., Scholtenhuis, F. O. & Van den Boomgaard, T. & Smolders, C. Spinning of hollow fiber ultrafiltration membranes from a polymer blend. Journal of Membrane Science 106, 233–243 (1995).

    CAS  Article  Google Scholar 

  9. 9.

    Su, B.-h et al. Evaluation of polyethersulfone highflux hemodialysis membrane in vitro and in vivo. Journal of Materials Science: Materials in Medicine 19, 745–751 (2008).

    CAS  PubMed  Google Scholar 

  10. 10.

    Xu, Z.-L. & Qusay, F. A. Polyethersulfone (PES) hollow fiber ultrafiltration membranes prepared by PES/non-solvent/NMP solution. Journal of Membrane Science 233, 101–111 (2004).

    CAS  Article  Google Scholar 

  11. 11.

    Liu, Y., Koops, G. & Strathmann, H. Characterization of morphology controlled polyethersulfone hollow fiber membranes by the addition of polyethylene glycol to the dope and bore liquid solution. Journal of membrane science 223, 187–199 (2003).

    CAS  Article  Google Scholar 

  12. 12.

    Xu, Z. L. & Qusay, F. A. Effect of polyethylene glycol molecular weights and concentrations on polyethersulfone hollow fiber ultrafiltration membranes. Journal of applied polymer science 91, 3398–3407 (2004).

    CAS  Article  Google Scholar 

  13. 13.

    Rahimpour, A. & Madaeni, S. Polyethersulfone (PES)/cellulose acetate phthalate (CAP) blend ultrafiltration membranes: preparation, morphology, performance and antifouling properties. Journal of Membrane Science 305, 299–312 (2007).

    CAS  Article  Google Scholar 

  14. 14.

    Wang, Y. et al. Improved permeation performance of Pluronic F127–polyethersulfone blend ultrafiltration membranes. Journal of membrane science 282, 44–51 (2006).

    CAS  Article  Google Scholar 

  15. 15.

    Loh, C. H., Wang, R., Shi, L. & Fane, A. G. Fabrication of high performance polyethersulfone UF hollow fiber membranes using amphiphilic Pluronic block copolymers as pore-forming additives. Journal of membrane science 380, 114–123 (2011).

    CAS  Article  Google Scholar 

  16. 16.

    Wang, Y.-q. et al. Protein-adsorption-resistance and permeation property of polyethersulfone and soybean phosphatidylcholine blend ultrafiltration membranes. Journal of membrane science 270, 108–114 (2006).

    CAS  Article  Google Scholar 

  17. 17.

    Wang, T., Wang, Y.-Q., Su, Y.-L. & Jiang, Z.-Y. Antifouling ultrafiltration membrane composed of polyethersulfone and sulfobetaine copolymer. Journal of membrane science 280, 343–350 (2006).

    CAS  Article  Google Scholar 

  18. 18.

    Shi, Y. et al. Characterization and emulsifying properties of octenyl succinate anhydride modified Acacia seyal gum (gum arabic). Food Hydrocolloids 65, 10–16, (2017).

    CAS  Article  Google Scholar 

  19. 19.

    Sanchez, C. et al. Acacia gum: History of the future. Food Hydrocolloids,

  20. 20.

    Bhushette, P. R. & Annapure, U. S. Comparative study of Acacia nilotica exudate gum and acacia gum. International Journal of Biological Macromolecules 102, 266–271, (2017).

    CAS  Article  PubMed  Google Scholar 

  21. 21.

    Gashua, I. B., Williams, P. A., Yadav, M. P. & Baldwin, T. C. Characterisation and molecular association of Nigerian and Sudanese Acacia gum exudates. Food Hydrocolloids 51, 405–413, (2015).

    CAS  Article  Google Scholar 

  22. 22.

    Ahmed, S. E. Analytical Studies On The Gum Exud From Anoffeissus leiocarpus Degree Of Doctor Of Philosophy In Agriculture. thesis, University of Khartoum, (1999).

  23. 23.

    Islam, A. M., Phillips, G. O., Sljivo, A., Snowden, M. J. & Williams, P. A. A review of recent developments on the regulatory, structural and functional aspects of gum arabic. Food Hydrocolloids 11, 493–505, (1997).

    CAS  Article  Google Scholar 

  24. 24.

    Patel, S. & Goyal, A. Applications of natural polymer gum arabic: a review. International Journal of Food Properties 18, 986–998 (2015).

    CAS  Article  Google Scholar 

  25. 25.

    Grein, A. et al. Structural characterization and emulsifying properties of polysaccharides of Acacia mearnsii de Wild gum. Carbohydrate Polymers 92, 312–320, (2013).

    CAS  Article  PubMed  Google Scholar 

  26. 26.

    Gazi, M. I. The finding of antiplaque features in Acacia Arabica type of chewing gum. Journal of clinical periodontology 18, 75–77 (1991).

    CAS  Article  PubMed  Google Scholar 

  27. 27.

    Registry, A. f. T. S. a. D. Toxicological profile for lead. (Agency for Toxic Substances and Disease Registry, Atlanta, GA, 2007).

  28. 28.

    Brown, M. J. & Margolis, S. Lead in drinking water and human blood lead levels in the United States. (US Department of Health and Human Services, Centers for Disease Control and Prevention, 2012).

  29. 29.

    Lanphear, B. P., Burgoon, D. A., Rust, S. W., Eberly, S. & Galke, W. Environmental exposures to lead and urban children’s blood lead levels. Environmental Research 76, 120–130 (1998).

    ADS  CAS  Article  PubMed  Google Scholar 

  30. 30.

    Manawi, Y., Kochkodan, V., Mohammad, A. W. & Ali Atieh, M. Arabic gum as a novel pore-forming and hydrophilic agent in polysulfone membranes. Journal of Membrane Science 529, 95–104, (2017).

    CAS  Article  Google Scholar 

  31. 31.

    Rezaee, R. et al. Fabrication and characterization of a polysulfone-graphene oxide nanocomposite membrane for arsenate rejection from water. Journal of Environmental Health Science and Engineering 13, 1 (2015).

    CAS  Article  Google Scholar 

  32. 32.

    Chakrabarty, B., Ghoshal, A. & Purkait, M. Effect of molecular weight of PEG on membrane morphology and transport properties. Journal of membrane science 309, 209–221 (2008).

    CAS  Article  Google Scholar 

  33. 33.

    Mahmoudi, E., Ng, L. Y., Ba-Abbad, M. M. & Mohammad, A. W. Novel nanohybrid polysulfone membrane embedded with silver nanoparticles on graphene oxide nanoplates. Chemical Engineering Journal 277, 1–10 (2015).

    CAS  Article  Google Scholar 

  34. 34.

    Strathmann, H., Kock, K., Amar, P. & Baker, R. W. The formation mechanism of asymmetric membranes. Desalination 16, 179–203, (1975).

    CAS  Article  Google Scholar 

  35. 35.

    Mulder, J. Basic principles of membrane technology. (Springer Science & Business Media, 2012).

  36. 36.

    Boom, R., Wienk, I., Van den Boomgaard, T. & Smolders, C. Microstructures in phase inversion membranes. Part 2. The role of a polymeric additive. Journal of Membrane Science 73, 277–292 (1992).

    CAS  Article  Google Scholar 

  37. 37.

    Yeo, H.-T., Lee, S.-T. & Han, M.-J. Role of a polymer additive in casting solution in preparation of phase inversion polysulfone membranes. Journal of chemical engineering of Japan 33, 180–184 (2000).

    CAS  Article  Google Scholar 

  38. 38.

    Jung, B., Yoon, J. K., Kim, B. & Rhee, H.-W. Effect of molecular weight of polymeric additives on formation, permeation properties and hypochlorite treatment of asymmetric polyacrylonitrile membranes. Journal of Membrane Science 243, 45–57 (2004).

    CAS  Article  Google Scholar 

  39. 39.

    Chakrabarty, B., Ghoshal, A. & Purkait, M. Preparation, characterization and performance studies of polysulfone membranes using PVP as an additive. Journal of Membrane Science 315, 36–47 (2008).

    CAS  Article  Google Scholar 

  40. 40.

    Liu, F., Abed, M. M. & Li, K. Preparation and characterization of poly (vinylidene fluoride)(PVDF) based ultrafiltration membranes using nano γ-Al 2 O 3. Journal of membrane science 366, 97–103 (2011).

    CAS  Article  Google Scholar 

  41. 41.

    Van de Witte, P., Dijkstra, P., Van den Berg, J. & Feijen, J. Phase separation processes in polymer solutions in relation to membrane formation. Journal of Membrane Science 117, 1–31 (1996).

    Article  Google Scholar 

  42. 42.

    Wu, H., Tang, B. & Wu, P. Novel ultrafiltration membranes prepared from a multi-walled carbon nanotubes/polymer composite. Journal of Membrane Science 362, 374–383, (2010).

    ADS  CAS  Article  Google Scholar 

  43. 43.

    Wang, L. et al. Fabrication and characterization of polyethersulfone/carbon nanotubes (PES/CNTs) based mixed matrix membranes (MMMs) for nanofiltration application. Applied Surface Science 330, 118–125 (2015).

    ADS  CAS  Article  Google Scholar 

  44. 44.

    Anderson, D. & Dea, I. Light-scattering studies of Acacia gum exudates. Carbohydrate Research 10, 161–164 (1969).

    CAS  Article  Google Scholar 

  45. 45.

    Ariza, M. & Benavente, J. Streaming potential along the surface of polysulfone membranes: a comparative study between two different experimental systems and determination of electrokinetic and adsorption parameters. Journal of membrane science 190, 119–132 (2001).

    CAS  Article  Google Scholar 

  46. 46.

    Niu, F. et al. Ovalbumin–gum arabic interactions: Effect of pH, temperature, salt, biopolymers ratio and total concentration. Colloids and Surfaces B: Biointerfaces 113, 477–482, (2014).

    CAS  Article  PubMed  Google Scholar 

  47. 47.

    Vatanpour, V., Madaeni, S. S., Moradian, R., Zinadini, S. & Astinchap, B. Novel antibifouling nanofiltration polyethersulfone membrane fabricated from embedding TiO2 coated multiwalled carbon nanotubes. Separation and purification technology 90, 69–82 (2012).

    CAS  Article  Google Scholar 

  48. 48.

    Chaturvedi, B. K. et al. Preparation, characterization and performance of polyethersulfone ultrafiltration membranes. Desalination 133, 31–40, (2001).

    CAS  Article  Google Scholar 

  49. 49.

    Kim, J. & Kim, C. Ultrafiltration membranes prepared from blends of polyethersulfone and poly(1-vinylpyrrolidone-co-styrene) copolymers. Journal of membrane science 262, 60–68 (2005).

    CAS  Article  Google Scholar 

  50. 50.

    Do Nascimento, P. C., Da Marques, M. S., Bohrer, D., de Carvalho, L. M. & Carvalho, C. W. Chromatography and Atomic Absorption Spectrometry for the Assessment of Heavy Metal Distribution among Amino Acids Used in Parenteral Nutrition Formulations—Studies with Cadmium and Lead. Biological trace element research 141, 76–85 (2011).

    CAS  Article  PubMed  Google Scholar 

  51. 51.

    Shankar, R., Kolandaivel, P. & Senthilkumar, L. Interaction studies of cysteine with Li+, Na+, K+, Be2+, Mg2+, and Ca2+metal cation complexes. Journal of Physical Organic Chemistry 24, 553–567, (2011).

    CAS  Article  Google Scholar 

  52. 52.

    E, M. A., M, S. R. & J, M. R. (ed National Institute of Standards and Technology NIST) (Gaithersburg, 1998).

  53. 53.

    Parr, J. Some recent coordination chemistry of lead (II). Polyhedron 16, 551–566 (1997).

    CAS  Article  Google Scholar 

  54. 54.

    Pluhator-Murton, M. M. et al. Trace element contamination of total parenteral nutrition. 1. Contribution of component solutions. Journal of Parenteral and Enteral Nutrition 23, 222–227 (1999).

    CAS  Article  PubMed  Google Scholar 

  55. 55.

    Leung, F. Y., Grace, D. M., Alfieri, M. A. & Bradley, C. Abnormal trace elements in a patient on total parenteral nutrition with normal renal function. Clinical biochemistry 28, 297–302 (1995).

    CAS  Article  PubMed  Google Scholar 

  56. 56.

    Alfieri, M., Leung, F. & Grace, D. Selenium and zinc levels in surgical patients receiving total parenteral nutrition. Biological trace element research 61, 33–39 (1998).

    CAS  Article  PubMed  Google Scholar 

  57. 57.

    Mahaffey, K. R. Toxicity of lead, cadmium, and mercury: considerations for total parenteral nutritional support. Bulletin of the New York Academy of Medicine 60, 196 (1984).

    CAS  PubMed  PubMed Central  Google Scholar 

  58. 58.

    Anderson, D., Howlett, J. & McNab, C. The amino acid composition of the proteinaceous component of gum arabic (Acacia Senegal (L.) Willd.)*. Food Additives & Contaminants 2, 159–164 (1985).

    CAS  Article  Google Scholar 

  59. 59.

    Saini, M., Saini, R., Roy, S. & Kumar, A. Comparative pharmacognostical and antimicrobial studies of acacia species (Mimosaceae). Journal of Medicinal Plants Research 2, 378–386 (2008).

    Google Scholar 

  60. 60.

    Ferreira, I. C. F. R., Calhelha, R. C., Estevinho, L. M. & Queiroz, M.-J. R. P. Screening of antimicrobial activity of diarylamines in the 2,3,5-trimethylbenzo[b]thiophene series: a structure–activity evaluation study. Bioorganic & Medicinal Chemistry Letters 14, 5831–5833, (2004).

    CAS  Article  Google Scholar 

  61. 61.

    Clark, D., Gazi, M., Cox, S., Eley, B. & Tinsley, G. The effects of Acacia arabica gum on the in vitro growth and protease activities of periodontopathic bacteria. Journal of clinical periodontology 20, 238–243 (1993).

    CAS  Article  PubMed  Google Scholar 

  62. 62.

    Onishi, T. et al. Remineralization effects of gum arabic on caries-like enamel lesions. archives of oral biology 53, 257–260 (2008).

    CAS  Article  PubMed  Google Scholar 

  63. 63.

    Tyler, V., Brady, L. & Robbers, J. Pharmacognosy. (Lea & Febiger, 1977).

  64. 64.

    Basu, B. D., Kirtikar, K. R. & Basu, K. Indian Medicinal Plants: Plates. (Bishen Singh Mahendra Pal Singh, 1991).

  65. 65.

    Montenegro, M. A. Gum Arabic: More Than an Edible Emulsifier. (Universidad Tecnológica Nacional- Facultad Regional Villa María, 2012).

  66. 66.

    Kochkodan, V. & Hilal, N. A comprehensive review on surface modified polymer membranes for biofouling mitigation. Desalination 356, 187–207, (2015).

    CAS  Article  Google Scholar 

Download references


The authors are grateful to the financial support of Qatar Environmental and Energy Research Institute.

Author information




Y.M. and E.M. performed the experiments and wrote the manuscript, V.K. and D.J. contributed to data analysis and edition of the manuscript, A.W.M. and M.A.A. designed the experiments and supervised the project. All authors contributed to the discussion of the results.

Corresponding author

Correspondence to Muataz Ali Atieh.

Ethics declarations

Competing Interests

The authors declare that they have no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Manawi, Y., Kochkodan, V., Mahmoudi, E. et al. Characterization and Separation Performance of a Novel Polyethersulfone Membrane Blended with Acacia Gum. Sci Rep 7, 15831 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing