Hidden Magnetic States Emergent Under Electric Field, In A Room Temperature Composite Magnetoelectric Multiferroic


The ability to control a magnetic phase with an electric field is of great current interest for a variety of low power electronics in which the magnetic state is used either for information storage or logic operations. Over the past several years, there has been a considerable amount of research on pathways to control the direction of magnetization with an electric field. More recently, an alternative pathway involving the change of the magnetic state (ferromagnet to antiferromagnet) has been proposed. In this paper, we demonstrate electric field control of the Anomalous Hall Transport in a metamagnetic FeRh thin film, accompanying an antiferromagnet (AFM) to ferromagnet (FM) phase transition. This approach provides us with a pathway to “hide” or “reveal” a given ferromagnetic region at zero magnetic field. By converting the AFM phase into the FM phase, the stray field, and hence sensitivity to external fields, is decreased or eliminated. Using detailed structural analyses of FeRh films of varying crystalline quality and chemical order, we relate the direct nanoscale origins of this memory effect to site disorder as well as variations of the net magnetic anisotropy of FM nuclei. Our work opens pathways toward a new generation of antiferromagnetic – ferromagnetic interactions for spintronics.


In recent years, the ever increasing need for large scale data storage in computing systems has kindled significant interest in new materials and new physical phenomena that could lead to denser and more energy efficient memory systems. One approach is the heat assisted magnetic recording (HAMR) for which low Neel temperature AFMs have been suggested to play a key role1. In this context, the AFM to FM phase transition makes FeRh a serious contender for insertion into heterostructures utilizing exchange bias. Typically, in magnetic systems, defects impede domain wall motion, increase the coercivity, lower magnetization, and decrease spin polarization. Going beyond this traditional thinking, in this work we demonstrate that it is possible to exploit crystalline defects in FeRh to induce a voltage driven phase transition in FeRh that leads to a mixed AFM/FM state. This mixed phase can then be read out through a strong magnetoresistance (MR) effect. The presence of the mixed phase hints to a potential source of rich physical phenomena and the ability to control and probe the transition electrically. This furthermore suggests that an electrically assisted magnetic recording (EAMR) is achievable in a single magnetic material.

We employ a thin layer of Fe0.50Rh0.50 (FeRh) which is an intermetallic compound that exhibits an antiferromagnetic (AFM) to ferromagnetic (FM) phase transition that can be controlled by strain, heat, or magnetic field2,3,4,5,6,7,8,9. Concurrent with this metamagnetic phase transition, FeRh displays a very large change in resistivity (~30–40%)2 which can be triggered by any of the aforementioned stimuli. Our device is comprised of a piezoelectric substrate (for example, (0.72)PbMg1/3Nb2/3O3 - (0.28)PbTiO3 (PMN-PT) or BaTiO3(BTO)) which allows the tuning of the strain exerted on the magnetic material. This combination of materials has achieved, in previous work, an electrically driven modulation of magnetization6,9,10 by as large as 70 emu/cm3 (~21% isothermal magnetization modulation)6 and resistivity modulation of 8–22%7,8 thus proving the magnetoelectric coupling of the heterostructure. Specific details for the very same samples employed in this work are found elsewhere7,8.

Our model system consists of a 30 nm thick FeRh layer that is deposited by ultrahigh vacuum sputtering onto a single crystal of PMN-PT at a deposition temperature of 350 °C. To demonstrate the generality of this approach, a single crystal BaTiO3 was also used as a piezoelectric substrate. Prior to our magnetoelectric studies, we characterized the crystalline quality of the FeRh layer (a sampling is shown in Supplementary Figure S1). 4-probe transport measurements were carried out as a function of temperature and electric field, using a test structure shown schematically in Fig. 1(a). Armed with this baseline, we now present results of temperature and electric field dependent magnetic and magnetotransport studies. Figure 1(b) presents temperature dependent SQUID magnetic hysteresis loops for the FeRh, measured in-plane and out-of-plane at 27 °C and 127 °C (more detailed magnetic data is presented in Supplemental Figure S2 for the PMNPT substrate and in Figure S3 for the BaTiO3 substrate). Upon lowering the temperature, two changes occur. First, the absolute magnetic moment is reduced, consistent with the emergence of the antiferromagnetic phase. Second, and perhaps more importantly, the magnetization is now directed significantly more out-of-plane, as illustrated in the comparison of the in-plane versus out-of-plane magnetic hysteresis loops. This out-of-plane component of the magnetization is key to the detectability of this state (in our case through anomalous Hall resistance measurements11,12 [AHR, Rxy], described below).

Figure 1

FeRh Magnetic Anisotropy and Electric Field Control (a) Transport device geometry. (b) In-plane and out-of-plane magnetization hysteresis loops measured by Superconducting Quantum Interference Device (SQUID) at 27 °C and 127 °C. (c) Electric field dependence of the longitudinal resistance of FeRh (30 nm)/PMN-PT. (d) A step-wise illustration of how the memory element is programmed into a magnetic state (step 1 or 1′), “cloaked” by the application of an electric field (step 2 or 2′) and “uncloaked” by the application of an opposite polarity electric field (step 3 or 3′) of our proposed cloaked magnetic memory device functions. (e) Electric-field dependences of the anomalous Hall resistance (AHR) for the two magnetic states.

In the mixed AFM-FM state (for example at a temperature of 60 °C) application of an out-of-plane electric field to the heterostructure leads to a strong change in the (longitudinal) resistance, Fig. 1(c) (for simplicity, the corresponding data for the BaTiO3 substrate is shown in Supplemental Figure S4), which is directly attributed to the electric field control of the magnetic state (FM vs. AFM)6,7,8. Positive (negative) electric fields produce an increase (decrease) of electrical resistance, corresponding to an increase in the AFM (FM) phase fraction due to the strain-induced preference for this phase6,7,8. The temperature dependence of the longitudinal and transverse (i.e., Anomalous Hall) resistances for the two types of substrates are shown in Supplemental Figure S5. Using this as the starting point, we now describe how such a heterostructure can be used to cloak the written magnetic state. The strategy we propose is schematically summarized in Fig. 1(d). The memory element is programmed into the UP and DOWN states, [step 1 or 1′] with a magnetic field; a subsequent electric field [step 2 or 2′] converts it into the AFM phase thus cloaking and protecting it from external perturbation. An electric field of opposite polarity [step 3 or 3′] converts it back to the original FM state. The main experimental result to validate this protocol is summarized in Fig. 1(e) which shows the AHR of the FeRh layer as a function of the electric field applied to the underlying piezoelectric. After magnetizing the FeRh into the UP (or DOWN) states, a negative electric field, favors ferromagnetism (state 1 or 1′), while a positive field converts it into the AFM state with a lower AHR (state 2 or 2′), which are essentially the same.

In order to understand the effects of in-plane strain and the relative volume fraction of the FM phase on the magnetic moment orientation, we have carried out ab-initio electronic structure calculations of the volume-averaged magnetic anisotropy energy (MAE), \({\bar{K}}_{V}(\varepsilon ,x)=(1-x){K}_{V}^{AFM}(\varepsilon )+x\,{K}_{V}^{FM}(\varepsilon )\). Here, \(\varepsilon =(a-{a}_{o}^{FM})/{a}_{o}^{FM}\), is the strain relative to the equilibrium FM-FeRh lattice constant, \({a}_{o}^{FM}\), \({K}_{V}^{AFM(FM)}(\varepsilon )\) is the strain dependent intrinsic bulk MAE for the AFM (FM) FeRh phase and \(x=\frac{{V}^{FM}}{{V}^{FM}+{V}^{AFM}}\) is the relative volume fraction of the FM phase. In order to investigate the effect of magnetic shape anisotropy energy (MSAE) on the FM thin film, we have also calculated the effective MAE, \({K}_{eff}^{FM}(\varepsilon )={K}^{FM}(\varepsilon )-2\pi {M}^{2}(\varepsilon ,x)\), where \(M\,(\varepsilon ,x)=x({m}_{Fe}(\varepsilon )+{m}_{Rh}(\varepsilon ))/V(\varepsilon )\), \({m}_{Fe}(\varepsilon )\), \({m}_{Rh}(\varepsilon )\), and \(V(\varepsilon ),\) are the weakly strain-dependent magnetic moments of the Fe and Rh atoms, and the volume of the formula unit cell, respectively.

In Fig. 2(a) we show the variation of the volume-averaged MAE, \({\bar{K}}_{V}\) with strain and relative volume fraction of the FM phase. We find that the MAE is positive (negative) under compressive (tensile) strain for the FM phase, indicating an out-of-plane (in-plane) orientation of the magnetic moments. In sharp contrast, the strain dependence of the MAE in the AFM phase is reversed, consistent with previous results13. The variation of the effective MAE, \({K}_{eff}^{FM}\), of the FM phase is shown in Fig. 2(b). Interestingly, for x = 1, the MSAE renders \({K}_{eff}^{FM} < 0\) in the entire strain range, demonstrating that when the entire volume is in the FM phase, the spin orientation is in-plane. As the relative volume fraction of the FM phase decreases, the effect of MSAE also decreases and \({K}_{eff}^{FM}\) is determined primarily by \({K}_{V}^{FM}\) yielding an out-of-plane spin orientation under compressive strain.

Figure 2

Ab-initio calculations results of the FeRh magnetic anisotropy as a function of strain. (a) The volume-averaged magnetic anisotropy energy, \({\bar{K}}_{V}\), as a function of strain and FM/AFM volume fraction. (b) The net magnetic anisotropy energy of the FM phase is shown, including demagnetization effects.

Supporting evidence for the electric field modulation of the magnetic state described in Fig. 1(e) comes from analogous temperature dependence of the magnetic state, as shown in Fig. 3(a), which shows the sequence of steps in which the FeRh layer is oriented in a magnetic field of +(−) 500 mT, then cooled from the FM state (state 1 or 1′) at 127 °C in to an essentially AFM state at 27 °C (state 2 or 2′). Upon heating back to 127 °C, the same ferromagnetic “polarity” is retrieved (i.e. state 3 or 3′), suggesting the existence of FM kernels within the AFM phase, which contain the directional magnetic information and assist in attaining the originally written FM state upon heating. Indeed, XMCD-PEEM studies of such films through the same thermal cycling (Supplemental Figure S6) reveal that the same ferromagnetic state is attained as the sample is heated into the ferromagnetic state, cooled into the antiferromagnetic state and then returned to the high temperature ferromagnetic state. Figure 3(b) demonstrates that such a reversal can be carried out over several cycles. The corresponding electric field cycling results are presented in Fig. 3(c) which shows the AHR as a function of time at positive, zero and negative magnetic fields as a function of electric field cycling at 60 °C. It is clear that the ability to distinguish the two magnetic states is electric field polarity dependent and stable over several cycles. The horizontal line in Fig. 3(c) indicates the AFM or “cloaked” state, while the data significantly above or below the line represent a positive or negative magnetization state. With a negative applied electric field, the magnetization direction of this “cloaked” state is revealed. To establish the robustness of this data against external magnetic fields, we deliberately probed the magnetic field dependence of the AHR in both the FM and AFM states at zero electric field, as shown in Fig. 3(d). The fact that the magnetic field dependence for the two states do not crossover implies that the AFM state is stable in an external magnetic field, at least up to 300 mT at a temperature of 27 °C.

Figure 3

Phase Modulation and Invisible Memory Proof of Concept (a) Magnetization versus temperature loops measured at 0 mT, after saturating the sample (±500 mT) at 127 °C. Arrows indicate increasing or decreasing temperature. (b) Magnetic moment at 127 °C (solid symbols) and 27 °C (open symbols) measured after successive thermal cycling at 0 mT. (c) Anomalous Hall resistance as a function of time (at 60 °C) at positive (200 mT), zero, and negative (−200 mT) magnetic fields through a series of different voltage cycles. Between the 0 and −200 mT fields, a field cooling was carried out. (d) AHR as a function of magnetic field for the two 0 electric-field states at 25 °C. The magnetic response is due to the ordinary Hall effect, and are separated due to differing magnetization states, AFM and FM.

We establish the generality of this approach by carrying out the same set of experiments using a single crystal BaTiO3 as the substrate. Figure 4(a) shows the magnetic hysteresis loops as a function of temperature, again indicating the emergence of the AFM state from the high temperature FM state. Normal and anomalous Hall transport measurements, Fig. 4(b), show a strong electric field driven hysteresis, consistent with what was observed with PMNPT substrates. The temperature dependence of the normalized anomalous Hall resistance for the two piezoelectric substrates are compared in Fig. 4(c); the overall trend is similar, although the films on BaTiO3 substrates show a larger modulation and a sharper temperature dependence, reflective of the better crystalline quality. Finally, the stability of the “protected” state to external magnetic fields is demonstrated in Fig. 4(d), which is again consistent with that measured with PMNPT as the piezoelectric substrate. These results demonstrate the generality of this approach.

Figure 4

(a) Temperature dependence of the magnetic hysteresis; (b) normal and anomalous Hall resistance at 60 °C; (c) a comparison of the normalized anomalous Hall resistance for FeRh films grown on PMNPT and BaTiO3 substrates; (d) demonstration of the robustness of the “protected” state to external magnetic fields.

We now probe the microscopic details of such a directional magnetic memory, using magnetic force microscopy (MFM) as a function of applied electric field. We observed measurable changes in the image contrast upon the application of positive and negative electric fields. Figure 5(a), obtained with a positive electric field of 7.3 kV/cm shows an essentially “uniform” contrast, indicative of an essentially antiferromagnetic state (i.e., no significant magnetic moment); upon the application of a −7.3 kV/cm electric field (Fig. 5(b)), the image contrast changes with the emergence of regions with strong contrast (in blue and red), indicative of the emergence of the ferromagnetic state. It is particularly important to note that the contrast for a given location in the sample is reversibly changed from red (or blue) to green, again providing supporting evidence to the notion that a specific ferromagnetic polarity is retained in that location. The corresponding data for FeRh on BaTiO3 is shown in Supplemental Figure S7 and it is generally consistent with the observations in Fig. 5.

Figure 5

Local Memory of Directionality. Magnetic force microscopy of the FeRh layer at 60 °C under a DC electric field of ± 7.3 kV/cm is applied. Images are labeled sequentially with their corresponding electric field. The magnetic response in (a) and (c) are drastically diminished, when compared with the same region in (b) and (d). The local magnetic memory effect is observed here as the local magnetization is reversibly modified with electric field.

It has been reported earlier that the FM state set at high temperature can be imprinted in the AFM state at room temperature by fixing the direction of the antiferromagnetic axis by in-field magnetic cooling from the high temperature FM phase down to the low temperature AFM phase14. Therefore, the observed memory effect can be attributed to a reciprocal effect, in which the magnetic orientation is frozen in the AFM state and drives the magnetization orientation in the FM state upon subsequent warming (or the application of a negative electric field). The role of localized structural and antisite defects in the FeRh film structure is likely a key element for such a memory effect. Indeed, a dependence on the low temperature ferromagnetic phase fraction is observed. FeRh films deposited on single-crystalline MgO show an annealing dependence on the memory effect that is magnified for FeRh/PMN-PT. The high quality films on MgO do not show a retained magnetic moment at room temperature and, in agreement with prior work15, we observe no memory effect. Therefore, we conclude that the coexistence of FM/AFM phases at room-temperature is required to store the magnetic information and that the minority FM domains present at room temperature must play a crucial role in the observed memory effect. The coexistence of magnetic phases has been long exploited in the well-known magnetic shape-memory alloys that show magnetic memory while crossing the austenite to martensite phase transition at which the magnetic state changes15,16. It appears that a similar phenomenology is at play here, with the advantage that the room-temperature AFM phase can mask the coexisting FM nuclei. It is worth noting that, in contrast to most common situations where single crystalline substrates are a demand for optimal thin film properties, here poly-domain substrates are advantageous and thus we expect to observe similar memory effects utilizing a wide range of inexpensive substrates. Finally, exploiting memory effects such as those described here require materials that display near room temperature AFM to FM transitions. Fortunately several alloys, such as Mn2Sb and related compounds17,18,19 are already known.


Thin films were prepared by DC magnetron sputtering onto PMN-PT and BaTiO3 substrates that were heated up to 300 °C in a base pressure of 10−8  Torr. Subsequently, Ar gas was introduced (3 mTorr) and films were grown using 50 W power at a rate of 1 nm min−1 using a stoichiometric FeRh target.

Magnetic characterization with magnetic fields up to 1 T was carried out in a superconducting quantum interference device by Quantum Design using the Reciprocating Sample Option.

Transport experiments utilized four-probe resistance contacts with additional transverse contacts, perpendicular to the current direction separated by 500 μm in a magnet. Longitudinal and transverse resistances are averages of the positive and negative current values. Currents were applied along the [100] directions. Electric fields were applied between a current lead and the back side of the sample.

The ab-initio electronic structure calculations have been carried out within the framework of the projector augmented-wave formalism20 as implemented in the Vienna ab-initio simulation package (VASP)21,22, with the generalized gradient approximation for the exchange-correlation functional parameterized by Perdew-Burke-Ernzerhof (PBE)23. The plane-wave cutoff energy is 500 eV and the tetrahedron method is used for the Brillouin zone integration with Γ centered k -mesh of 24 × 24 × 24 grid. Spin-orbit coupling is included using the second-variation method24 employing the scalar-relativistic eigenfunctions of the valence states. The bulk MAE per formula unit for FM (AFM) phase is determined from \({K}_{V}^{AFM(FM)}=({E}_{[100]}-{E}_{[001]})\), where \({E}_{[100]}\) and \({E}_{[001]}\) are the total energies with magnetization along the [100] and [001] directions, respectively.

Magnetic Force Microscopy images were acquired using an Asylum MFP3D AFM with a magnetic CoCr coated tip. The sample was heated to 60 °C using Asylum’s polymer heater. Voltage was applied between the grounded sample surface and the back side of the sample during measurement.


  1. 1.

    Evans, R. F. L., Yanes, R., Mryasov, O., Chantrell, R. W. & Chubykalo-Fesenko, O. On beating the superparamagnetic limit with exchange bias. EPL 88, 57004

  2. 2.

    Zsoldos, L. Lattice Parameter Change of FeRh Alloys due to Antiferromagnetic‐Ferromagnetic Transformation. phys. stat. sol. (b) 20, K25–K28 (1967).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Suzuki, I., Naito, T., Itoh, M., Sato, T. & Taniyama, T. Clear correspondence between magnetoresistance and magnetization of epitaxially grown ordered FeRh thin films. J. Appl. Phys. 109, 07C717 (2011).

    Article  CAS  Google Scholar 

  4. 4.

    Maat, S., Thiele, J. U. & Fullerton, E. Temperature and field hysteresis of the antiferromagnetic-to-ferromagnetic phase transition in epitaxial FeRh films. Phys. Rev. B 72, 214432 (2005).

    ADS  Article  CAS  Google Scholar 

  5. 5.

    de Vries, M. A. et al. Hall-effect characterization of the metamagnetic transition in FeRh. New J. Phys. 15, 013008 (2013).

    Article  CAS  Google Scholar 

  6. 6.

    Cherifi, R. O. et al. Electric-field control of magnetic order above room temperature. Nature Materials 13, 345–351 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  7. 7.

    Lee, Y. et al. Large resistivity modulation in mixed-phase metallic systems. Nature Communications 6, 5959 (2015).

    CAS  Article  PubMed  Google Scholar 

  8. 8.

    Liu, Z. Q. et al. Full Electroresistance Modulation in a Mixed-Phase Metallic Alloy. Phys. Rev. Lett. 116, 097203 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  9. 9.

    Ignasi, F. et al. Electric-Field-Adjustable Time-Dependent Magnetoelectric Response in Martensitic FeRh Alloy. ACS Applied Materials & Interfaces 9(18), 15577–15582 (2017).

  10. 10.

    Phillips, L. C. et al. Local electrical control of magnetic order and orientation by ferroelastic domain arrangements just above room temperature. Sci. Rep. 5, 10026 (2015).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  11. 11.

    Nagaosa, N., Sinova, J., Onoda, S., MacDonald, A. H. & Ong, N. P. Anomalous hall effect. Reviews of modern physics 82, 1539 (2010).

    ADS  Article  Google Scholar 

  12. 12.

    MacDonald, A. H. & Tsoi, M. Antiferromagnetic metal spintronics. Philosophical Transactions of the Royal Society A: Mathematical, Physical and Engineering Sciences 369, 3098–3114 (2011).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Bordel, C. et al. Fe Spin Reorientation across the Metamagnetic Transition in Strained FeRh Thin Films. Phys. Rev. Lett. 109, 117201 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  14. 14.

    Martí, X. et al. Room-temperature antiferromagnetic memory resistor. Nature Materials 13, 367–374 (2014).

    ADS  Article  PubMed  CAS  Google Scholar 

  15. 15.

    Baldasseroni, C. et al. Temperature-driven growth of antiferromagnetic domains in thin-film FeRh. J. Phys.: Condens. Matter 27, 256001 (2015).

    ADS  CAS  Google Scholar 

  16. 16.

    Chatterjee, S., Giri, S., Majumdar, S. & De, S. K. Metastability and magnetic memory effect in Ni 2 Mn 1.4 Sn 0.6. Phys. Rev. B (2008).

  17. 17.

    Ryzhkovskii, V. M., Dymont, V. P. & Erofeenko, Z. L. Ferromagnetic-antiferromagnetic phase transition in Mn2Sb(Sn) solid solutions. Phys. Stat. Sol. (a) 130, 163–168 (1992).

    ADS  CAS  Article  Google Scholar 

  18. 18.

    Wijngaard, J. H., Haas, C. & de Groot, R. A. Ferrimagnetic-antiferromagnetic phase transition in Mn2−xCrxSb: Electronic structure and electrical and magnetic properties. Phys. Rev. B 45, 5395–5405 (1992).

    ADS  CAS  Article  Google Scholar 

  19. 19.

    Caron, L., Miao, X. F., Klaasse, J. C. P., Gama, S. & Bruck, E. Tuning the giant inverse magnetocaloric effect in Mn2-xCrxSb compounds. Appl. Phys. Lett. 103 (2013).

  20. 20.

    Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).

    ADS  Article  Google Scholar 

  21. 21.

    Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Computational Materials Science 6, 15–50 (1996).

    CAS  Article  Google Scholar 

  22. 22.

    Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initiototal-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).

    ADS  CAS  Article  Google Scholar 

  23. 23.

    Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized Gradient Approximation Made Simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    ADS  CAS  Article  PubMed  Google Scholar 

  24. 24.

    Koelling, D. D. & Harmon, B. N. Technique for Relativistic Spin-Polarized Calculations. Journal of Physics C: Solid State Physics 10, 3107–3114 (1977).

    ADS  CAS  Article  Google Scholar 

Download references


The work at Berkeley was supported in part by FAME, one of six centers of STARnet, a Semiconductor Research Corporation program sponsored by MARCO and DARPA was supported by the SRC-FAME program. Financial support by the Spanish Government (Project MAT2014-56063-C2-1-R, MAT2015-73839-JIN, MAT2017-85232-R and associated FEDER) and Generalitat de Catalunya (2014 SGR 734) is acknowledged. ICMAB-CSIC authors acknowledge financial support from the Spanish Ministry of Economy and Competitiveness, through the “Severo Ochoa” Programme for Centres of Excellence in R&D (SEV- 2015-0496). IF acknowledges Juan de la Cierva – Incorporación postdoctoral fellowship (IJCI-2014-19102) from the Spanish Ministry of Economy and Competitiveness of Spanish Government. XMCD-PEEM experiments were performed at CIRCE beamline at ALBA Synchrotron with the acknowledged collaboration of ALBA staff. Partial financial support from the 2014-Consolidator Grant "SPIN-PORICS" (Grant Agreement nº 648454) from the European Research Council is acknowledged. XM acknowledges support from the Grant Agency of the Czech Republic Grant no. 14-37427. Work at ORNL was sponsored by the Laboratory Directed Research and Development (LDRD) Programs of ORNL managed by UT-Battelle, LLC. Work at CSUN was supported by NSF under Grant No. 1205734, NSF Partnerships for Research and Education in Materials (PREM), and by NSF under Grant No. 1160504 NSF Nanosystems Engineering Research Center for Translational Applications of Nanoscale Multiferroic Systems (TANMS).

Author information




Z.Q.L., Y.L. and H.M.C. carried out the synthesis. J.D.C., I.F., Z.Q.L., Y.L., J.S., J.T.H., S.S., J.F., R.R., and X.M. planned and analyzed the thermomagnetic experiments. J.D.C., I.F., Z.Q.L., Y.L., K.C., S.W., F.S., L.A., and M.F. executed and contributed to the samples preparation for the thermomagnetic experiments. J.D.C., Z.Q.L., Y.L., and C.F. performed complementary X-ray characterization. S.L.H. performed T.E.M. experiments. J.K. and N.K. planned and performed the ab initio calculations. J.D.C., Z.Q.L., Y.L., J.T.H., R.R., and X.M. planned the magnetoelectric transport experiments and J.D.C., Z.Q.L., Y.L. and J.T.H. performed the experiments. J.D.C. and Y.L. planned and performed the M.F.M. experiments and J.D.C., Y.L., and C.K. performed the M.F.M. experimental switching under the supervision of J.W. J.D.C., I.F., J.K., S.S., N.K., R.R., D.G.S. H.M.C. and X.M. co-wrote the text.

Corresponding author

Correspondence to R. Ramesh.

Ethics declarations

Competing Interests

The authors declare that they have no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Clarkson, J.D., Fina, I., Liu, Z.Q. et al. Hidden Magnetic States Emergent Under Electric Field, In A Room Temperature Composite Magnetoelectric Multiferroic. Sci Rep 7, 15460 (2017). https://doi.org/10.1038/s41598-017-13760-y

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.