We demonstrate the fabrication of individual nanopores in hexagonal boron nitride (h-BN) with atomically precise control of the pore shape and size. Previous methods of pore production in other 2D materials typically create pores with irregular geometry and imprecise diameters. In contrast, other studies have shown that with careful control of electron irradiation, defects in h-BN grow with pristine zig-zag edges at quantized triangular sizes, but they have failed to demonstrate production and control of isolated defects. In this work, we combine these techniques to yield a method in which we can create individual size-quantized triangular nanopores through an h-BN sheet. The pores are created using the electron beam of a conventional transmission electron microscope; which can strip away multiple layers of h-BN exposing single-layer regions, introduce single vacancies, and preferentially grow vacancies only in the single-layer region. We further demonstrate how the geometry of these pores can be altered beyond triangular by changing beam conditions. Precisely size- and geometry-tuned nanopores could find application in molecular sensing, DNA sequencing, water desalination, and molecular separation.
Nanoporous materials have received significant attention due to intriguing basic science issues1 and a range of applications: molecular sensing2, DNA sequencing3,4,5, water desalination6, and molecular separation7,8 to name a few. Nanopores in 2D materials such as graphene9,10,11, hexagonal boron nitride (h-BN)12,13, molybdenum disulfide (MoS2)14, and tungsten disulfide (WS2)15 have gained particular attention, as limiting the pore’s channel length to a single or few atoms makes for more sensitive sensors16 or more energy efficient filters17,18. Additionally, the crystalline nature of layered materials creates pores in which the chemical groups at the pore’s edge differ from those of the rest of the sheet, allowing for chemical functionalization to improve performance19.
The performance in each of the applications mentioned above relies critically on precise control of pore size. In molecular sensing, a tighter pore size results in a larger signal as a target molecule more fully blocks the channel, leading to improved sensing accuracy20,21. DNA sequencing benefits from this improved signal, particularly for nanopores with diameters ranging from 1–3 nm, but also these smaller and more precise pore sizes help slow the passage of DNA through the pore – solving a common problem facing many solid state nanopore devices aimed at sequencing22,23. Atomically precise pore sizes would allow for molecular sieves and gas separation systems capable of isolating smaller molecules and separating species with atomic scale differences in size and shape8. While other techniques have had success in creating precise nanopores in 2D materials20,24,25,26,27, they have lacked the subnanometer precision and pore sizes necessary to realize their full potential in a range of applications.
In this work, we describe and establish a procedure for the fabrication of individual nanopores in few-layer h-BN with atomically precise control of pore size from few-atom vacancies to several nanometer side-length through careful control of transmission electron microscope (TEM) electron beam conditions. It has been previously demonstrated that when h-BN is exposed under 80 kV electron irradiation in TEM that regular atomically precise triangle defects form28,29,30,31,32,33. Due to the preferential ejection of boron, attributed either to electron knock-on effects or selective chemical etching by atomic species present in the TEM, metastable nitrogen terminated zig-zag edges form and preserve a triangular shape under the electron beam. As these undercoordinated nitrogen atoms are ejected a new nitrogen zig-zag edge is exposed allowing for the precise quantized growth of the triangle defect32,34. In all of the previous work, however, the defects studied, despite growing at precise increments, were not controlled in number or size; many defects were formed and the rate of growth was left uncontrolled. In other studies, in which the number and position of the defects in h-BN were controlled for nanopore studies, the defects formed were irregular in shape and larger than 5 nm due to the use of high currents or voltages in order to readily create single pores12,13.
Here, we develop a method that combines the strengths of these approaches by allowing for both the nucleation of single nanopores and for the precise growth of these defects in h-BN from few atom vacancies to several nanometer side-lengths. This process can be accomplished in a conventional TEM by only modifying the beam conditions and does not need an advanced aberration-corrected TEM. Our process for creating an individual nanopore is shown schematically in Fig. 1, and consists of two main steps. First, with a high current density focused electron beam, we strip away layers of h-BN over a small area until we are left with a single few-atom vacancy in a small single-layer region. Second, the electron beam is spread and the preferential growth of the nanopore under a diffuse electron beam is monitored, while the formation of additional vacancies and pores is suppressed.
Results and Discussion
In order to prepare individual nanopores in multilayer h-BN, we first strip away layers in a localized region by milling with a condensed electron beam in a JEOL 2010 TEM operated at 80 kV. As shown in Fig. 2(a–f), by using a beam condensed to a diameter of 10–20 nm at a current density of 37 A/cm2, vacancies are readily formed in each layer sequentially and steadily grow with dose (Fig. 2(g) and (h)), effectively stripping away layer by layer. Under these beam conditions, this process proceeds fairly slowly giving a good deal of control; Fig. 2(h) shows the area of the sample exposed for a given layer or below. In this experiment, a dose of approximately 6 × 106 e/Å2 or 4.5 minutes is required to strip to each successive layer under the condensed beam. Vacancies in the final single-layer region of the h-BN are identified by a larger contrast difference (Fig. 2(i)), allowing us to stop the milling after an isolated vacancy has been introduced in the single-layer region.
After a small vacancy has been produced, a lower energy density beam allows us to grow the nanopore in quantized triangles of precise size, while new vacancy formation is inhibited. As the nanopore grows, it favors a triangular geometry and is metastable at each quantized triangle size, allowing for easily reproducible, highly regular pore geometry, as shown in Fig. 3(a). Figure 3(b–i) show an example of the growth of a single nanopore from a few-atom vacancy to 8 nm2 with the beam current density reduced to 6 A/cm2, where the pore growth as a function of dose can be seen in Fig. 3(j). As has been described previously, electron knock-on effects and/or selective chemical etching due to gases present in the TEM column preferentially eject boron atoms and preserves nitrogen zig-zag edge termination28,29,30,31,32,35. Hence, each of the triangular pores created is reliably nitrogen terminated, desirable for many nanopore applications where controlling end-group chemistry is critical. When the nanopore has reached its desired size, the beam can be fully expanded or blanked to cease pore growth.
By further lowering the beam current density, the nanopore in the single-layer region can be preferentially grown while similar defects in the multilayer region remain static. This is possible because vacancies in multi-layer regions appear to be stabilized, with inhibited further evolution, by the supporting h-BN layers. This is shown in the inset in Fig. 3(j), where over the course of exposing the sample with a total electron dose of 1.8 × 106 e/Å2 over 16 minutes at beam current of 3 A/cm2, the pore that spans the bottom layer grows by 10-fold while the similar vacancy in the second layer (shown in Fig. S1) remains constant in size.
While this method of vacancy seeding and pore growth may be extended to other 2D materials, h-BN nanopores prepared in this manner hold key advantages. When a similar method is used on graphene, the pore geometry is highly irregular, as demonstrated in Fig. 4 and previous work20,25,36. When irradiating a graphene sample under a diffuse electron beam using HRTEM, the edges of defects (Fig. 4a) do not pick any specific orientation as compared to h-BN (Fig. 4b) which has atomically pristine zig-zag edges. These zig-zag edges can confer an additional stability to the material versus graphene which can suffer from the uncontrolled addition of functional groups on its irregular edges after exposure to air37,38. Initiating pore growth is also significantly more difficult for graphene, requiring a much higher energy or beam current and a fully condensed beam, which yields larger starting vacancies.
Due to the diatomic basis of the two-dimensional transition metal dichalcogenides (TMDs) such as MoS2 or WSe2, they may also be possible candidates for similar triangular nanopores. However, Komsa et al.39 have reported that under electron irradiation the formation and aggregation of chalcogenide vacancies occurs preferentially over metal ejection. Feng et al.14 report the formation of nanopores in MoS2 by irradiating with a condensed electron beam, but these nanopores do not appear to take on any special geometry.
For the applications requiring the nanopore to serve as a fluidic channel, such as DNA sequencing, h-BN has been shown to have additional advantages over other 2D materials, for example a h-BN nanopore is more hydrophilic than a graphene nanopore due to the BN polar bond structure13. This allows for improved wetting for h-BN membranes, and consequent ionic conduction and DNA translocation through h-BN nanopores12,13. The insulating nature of h-BN may also be an advantage over graphene and TMDs for reducing noise in transmembrane current measurements and in instances where integrating patterned electronics on the substrate is necessary such as in nanoribbon and nanowire or plasmonic nanoantenna detection of nanopores40,41,42.
While we demonstrate that high precision nanopores can be created using conventional TEM, the TEM irradiation process may be difficult to scale for applications requiring more than one nanopore. However, chemical routes such as hydrogen annealing have demonstrated the ability to form triangle vacancies in h-BN43. By optimizing such a chemical process or by applying local heating as Nam et al.40, number and size of defects could be controlled outside of the TEM at much larger throughput. Other groups have also shown that defects in h-BN can be produced at lower accelerating voltages using a scanning electron microscope (SEM)44; further studies of this process might allow standard electron beam lithography exposures to create precise nanopores in h-BN.
The nitrogen terminated triangular defect geometry described above is not the only stable geometry possible for h-BN under electron irradiation; other pore geometries and end groups can be formed under different conditions30,35,45,46. In particular, previous work has shown that by elevating the temperature of the h-BN while it is exposed that hexagonal defects can be formed35,45. The formation of these hexagonal defects is justified by the revelation that there is an energy barrier between the hexagonal and triangular states which the heat provides the energy to overcome in these prior works.
Here we show that by increasing the beam current density we are also able to form hexagonal defects using a conventional TEM. By using a smaller spot size to increase the condensed beam current to approximately 70 A/cm2, hexagonal defects are formed, as shown in Fig. 5. As has been described elsewhere, in order to create hexagonal defects, both boron and nitrogen edges must be present45. These hexagons likely form because the extra beam current compensates for the energy difference between boron and nitrogen zig-zag edge similar to how heating has provided this extra energy in the prior literature35,45. The hexagonal pores can be steadily increased in size if the beam current remains around 70 A/cm2; however, if the beam current is then reduced to a current favorable for triangular nanopore growth, the hexagonal pore will grow towards a triangular shape as shown in Figure S4.
In summary, we have developed a method for fabricating individual h-BN nanopores with pore sizes that can be controlled with atomic precision. By careful control of beam conditions, electron beam irradiation can be used to strip away h-BN layers and create vacancies and can be used for nanopore growth. Under the correct beam conditions, this pore growth is limited to pores in single-layer h-BN and is inhibited in multi-layer regions. The pore geometry and end-group chemistries are both highly regular and controllable. Furthermore, we demonstrate in this work that these atomically precise nanopores can be created using a conventional TEM. Using an aberration corrected TEM allows refined characterization. h-BN nanopores with tunable pore size and geometry can find application in DNA sequencing (e.g. the pores < 2 nm have approximately the same dimensions as single-strand DNA) and molecular sensing20,21 where smaller pores and more precise end-group functionalization could increase sensitivity and performance respectively, in water desalination where better tailored pore sizes and functionalization could improve performance and efficiency47, and in molecular separation, where precise pore size and end group control would allow for better discrimination between like chemical species8.
The h-BN for this work is prepared by chemical vapor deposition on copper. Prior to growth, a 1 cm × 4 cm copper foil (Sigma Aldrich) is placed in acetic acid for 10 min followed by rinsing in 3 DI water baths. The sample is then annealed at 1020 °C under a mixture of 100 sccm H2 and 300 sccm Ar environment for 2 hours. After annealing, the argon is shut off and 100 mg of ammonia-borane (Sigma Aldrich 97%) precursor is heated in a connected upstream one-end sealed quartz tube to 70–90 °C for 30 minutes. The precursor is then cooled quickly while the copper foil is allowed to cool slowly under 10 sccm H2. This process yields 3–5 layer h-BN.
The h-BN is then either transferred to SiN membranes containing a single 100 nm hole via a PMMA assisted transfer48 or to holey carbon TEM grids (Ted Pella) as in ref.49. For the polymer assisted transfer, PMMA A4 is spun onto the top side of the copper foil. The foil is then floated on a bath of sodium persulfate in order to etch away the underlying copper, leaving the h-BN/PMMA film floating at the surface. A commercial TEM window chip (Norcada) with a 500 × 500 µm, 50 nm thick membrane is prepared for nanopore suspension by creating a 20–100 nm pore in the suspended nitride membrane. The hole is either formed using a Helium Ion Beam at 25 kV or by electron beam milling using an 80 kV condensed beam for 30–60 min. The modified TEM grid is used to scoop up the h-BN/PMMA film to transfer it over the nitride membrane pore. The PMMA is removed by annealing the chip at 350 °C in an evacuated tube furnace under 300 sccm argon, 100 sccm hydrogen.
Individual nanopores in h-BN are prepared using a JEOL 2010 TEM operated at 80 kV as described in the text above. The electron beam is condensed to a 10–20 nm diameter at spot size 3, alpha = 3 with a beam current of 37 A/cm2. The beam is expanded periodically to check the progress of this step. Based on the data presented in Fig. 2, one pore forms in a newly exposed layer roughly every 5 minutes. It is therefore straightforward to monitor and observe the formation of new defects by frequently spreading the beam and acquiring images. After the formation of the first vacancy between the first layer and vacuum, as identified by the difference in contrast and the accelerated growth rate of the vacancy, the beam is left expanded at a beam current 3 A/cm2 at spot size 3 or 6 A/cm2 at spot size 1. The size and number of vacancies as described in Figs 2(g) and 3(j) are extracted in post-analysis based on the recorded images taken during the pore formation.
The datasets generated during the current study are available from the corresponding author on reasonable request.
Rasool, H. I., Ophus, C. & Zettl, A. Atomic Defects in Two Dimensional Materials. Adv. Mater. 27, 5771–5777 (2015).
Venta, K. E. et al. Gold Nanorod Translocations and Charge Measurement through Solid-State Nanopores. Nano Lett. 14, 5358–5364 (2014).
Heerema, S. J. & Dekker, C. Graphene nanodevices for DNA sequencing. Nat. Nanotechnol. 11, 127–136 (2016).
Li, J., Gershow, M., Stein, D., Brandin, E. & Golovchenko, J. A. DNA molecules and configurations in a solid-state nanopore microscope. Nat. Mater. 2, 611–615 (2003).
Storm, A. J., Chen, J. H., Ling, X. S., Zandbergen, H. W. & Dekker, C. Fabrication of solid-state nanopores with single-nanometre precision. Nat. Mater. 2, 537–540 (2003).
Cohen-Tanugi, D. & Grossman, J. C. Water Desalination across Nanoporous Graphene. Nano Lett. 12, 3602–3608 (2012).
Koenig, S. P., Wang, L., Pellegrino, J. & Bunch, J. S. Selective molecular sieving through porous graphene. Nat. Nanotechnol. 7, 728–732 (2012).
Wang, L. et al. Molecular valves for controlling gas phase transport made from discrete ångström-sized pores in graphene. Nat. Nanotechnol. 10, 785–790 (2015).
Merchant, C. A. et al. DNA Translocation through Graphene Nanopores, https://doi.org/10.1021/NL101046T (2010).
Schneider, G. F. et al. DNA Translocation through Graphene Nanopores, https://doi.org/10.1021/NL102069Z (2010).
Garaj, S. et al. Graphene as a subnanometre trans-electrode membrane. Nature 467, 190 (2010).
Zhou, Z. et al. DNA Translocation through Hydrophilic Nanopore in Hexagonal Boron Nitride. Sci. Reports, Publ. online 21 Novemb. 2013 3, 13770–13773, https://doi.org/10.1038/srep03287 (2013).
Liu, S. et al. Boron Nitride Nanopores: Highly Sensitive DNA Single-Molecule Detectors. Adv. Mater. 25, 4549–4554 (2013).
Feng, J. et al. Identification of single nucleotides in MoS2 nanopores. Nat. Nanotechnol. 10, 1070 (2015).
Danda, G. et al. Monolayer WS 2 Nanopores for DNA Translocation with Light-Adjustable Sizes. ACS Nano 11, 1937–1945 (2017).
Lin, Z. et al. 2D materials advances: from large scale synthesis and controlled heterostructures to improved characterization techniques, defects and applications. 2D Mater. 3, 42001 (2016).
Surwade, S. P. et al. Water desalination using nanoporous single-layer graphene. Nat. Nanotechnol. 10, 459–464 (2015).
Heiranian, M., Farimani, A. B., Aluru, N. R., Lee, R. & Agre, P. Water desalination with a single-layer MoS2 nanopore. Nat. Commun. 6, 8616 (2015).
Sint, K., Wang, B. & Král, P. Selective Ion Passage through Functionalized Graphene Nanopores. J. Am. Chem. Soc. 130, 16448–16449 (2008).
Garaj, S., Liu, S., Golovchenko, J. A. & Branton, D. Molecule-hugging graphene nanopores. Proc. Natl. Acad. Sci. 110, 12192–12196 (2013).
Kowalczyk, S. W. et al. Modeling the conductance and DNA blockade of solid-state nanopores. Nanotechnology 22, 315101 (2011).
Akahori, R. et al. Slowing single-stranded DNA translocation through a solid-state nanopore by decreasing the nanopore diameter. Nanotechnology 25, 275501 (2014).
Mirsaidov, U. et al. Slowing the translocation of double-stranded DNA using a nanopore smaller than the double helix. Nanotechnology 21, 395501 (2010).
Russo, C. J. & Golovchenko, J. A. Atom-by-atom nucleation and growth of graphene nanopores. Proc. Natl. Acad. Sci. USA 109, 5953–7 (2012).
Schneider, G. F. et al. Tailoring the hydrophobicity of graphene for its use as nanopores for DNA translocation. Nat. Commun. 4, 326–328 (2013).
Feng, J. et al. Electrochemical reaction in single layer MoS2: Nanopores opened atom by atom. Nano Lett. 15 (2015).
Robertson, A. W. et al. Atomic Structure of Graphene Subnanometer Pores, https://doi.org/10.1021/ACSNANO.5B05700 (2015).
Alem, N. et al. Atomically thin hexagonal boron nitride probed by ultrahigh-resolution transmission electron microscopy. Phys. Rev. B 80, 155425 (2009).
Kotakoski, J., Jin, C. H., Lehtinen, O., Suenaga, K. & Krasheninnikov, A. V. Electron knock-on damage in hexagonal boron nitride monolayers. Phys. Rev. B 82, 113404 (2010).
Warner, J. H., Rümmeli, M. H., Bachmatiuk, A. & Büchner, B. Atomic Resolution Imaging and Topography of Boron Nitride Sheets Produced by Chemical Exfoliation. ACS Nano 4, 1299–1304 (2010).
Meyer, J. C., Chuvilin, A., Algara-Siller, G., Biskupek, J. & Kaiser, U. Selective Sputtering and Atomic Resolution Imaging of Atomically Thin Boron Nitride Membranes. Nano Lett. 9, 2683–2689 (2009).
Ryu, G. H. et al. Atomic-scale dynamics of triangular hole growth in monolayer hexagonal boron nitride under electron irradiation. Nanoscale 7, 10600–5 (2015).
Jin, C., Lin, F., Suenaga, K. & Iijima, S. Fabrication of a Freestanding Boron Nitride Single Layer and Its Defect Assignments. Phys. Rev. Lett. 102, 195505 (2009).
Alem, N. et al. Vacancy growth and migration dynamics in atomically thin hexagonal boron nitride under electron beam irradiation. Phys. status solidi - Rapid Res. Lett. 5, 295–297 (2011).
Cretu, O., Lin, Y.-C. & Suenaga, K. Inelastic electron irradiation damage in hexagonal boron nitride. Micron 72, 21–27 (2015).
Girit, Ç. Ö. et al. Graphene at the Edge: Stability and Dynamics. Science (80-.). 323 (2009).
Bellunato, A., Arjmandi Tash, H., Cesa, Y. & Schneider, G. F. Chemistry at the Edge of Graphene. ChemPhysChem 17, 785–801 (2016).
Bayley, H. Nanotechnology: Holes with an edge. Nature 467, 164–165 (2010).
Komsa, H.-P., Kurasch, S., Lehtinen, O., Kaiser, U. & Krasheninnikov, A. V. From point to extended defects in two-dimensional MoS 2: Evolution of atomic structure under electron irradiation. Phys. Rev. B 88, 35301 (2013).
Nam, S. et al. Graphene Nanopore with a Self-Integrated Optical Antenna. Nano Lett. 14, 5584–5589 (2014).
Belkin, M., Chao, S.-H., Jonsson, M. P., Dekker, C. & Aksimentiev, A. Plasmonic Nanopores for Trapping, Controlling Displacement, and Sequencing of DNA. ACS Nano 9, 10598–10611 (2015).
Traversi, F. et al. Detecting the translocation of DNA through a nanopore using graphene nanoribbons. Nat Nanotechnol 8, 939–945 (2013).
Wang, L. et al. Growth and Etching of Monolayer Hexagonal Boron Nitride. Adv. Mater. 27, 4858–4864 (2015).
Choi, S. et al. Engineering and Localization of Quantum Emitters in Large Hexagonal Boron Nitride Layers. ACS Appl. Mater. Interfaces 8, 29642–29648 (2016).
Pham, T. et al. Formation and Dynamics of Electron-Irradiation-Induced Defects in Hexagonal Boron Nitride at Elevated Temperatures. Nano Lett. 16, 7142–7147 (2016).
Cretu, O. et al. Structure and Local Chemical Properties of Boron-Terminated Tetravacancies in Hexagonal Boron Nitride. Phys. Rev. Lett. 114, 75502 (2015).
O’Hern, S. C. et al. Selective ionic transport through tunable subnanometer pores in single-layer graphene membranes. Nano Lett. 14 (2014).
Suk, J. W. et al. Transfer of CVD-Grown Monolayer Graphene onto Arbitrary Substrates. ACS Nano 5, 6916–6924 (2011).
Regan, W. et al. A direct transfer of layer-area graphene. Appl. Phys. Lett. 96, 113102 (2010).
This work was supported in part by the Director, Office of Science, Office of Basic Energy Sciences, Materials Sciences and Engineering Division, of the U.S. Department of Energy under Contract No. DE-AC02-05-CH11231, within the sp2-Bonded Materials Program (KC2207) which provided for TEM characterization, and within the Nanomachines Program (KC1203) which provided for methodology for membrane suspension; by the Department of Defense, Defense Threat Reduction Agency under Grant No. HDTRA1-15-1-0036, which provided for He-beam irradiation (the content of the information does not necessarily reflect the position or the policy of the Federal Government, and no official endorsement should be inferred); and by the National Science Foundation under Grant No. DMR-1206512, which provided for additional structural characterization of the pristine membranes. SMG and BS acknowledge support from the National Science Foundation Graduate Fellowship Program.
The authors declare that they have no competing interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
About this article
Cite this article
Gilbert, S.M., Dunn, G., Azizi, A. et al. Fabrication of Subnanometer-Precision Nanopores in Hexagonal Boron Nitride. Sci Rep 7, 15096 (2017). https://doi.org/10.1038/s41598-017-12684-x
ACS Nano (2020)
npj Computational Materials (2020)
Physical Review Materials (2020)
Fast water desalination by carbon-doped boron nitride monolayer: transport assisted by water clustering at pores
Physical Review B (2019)