The environmental impact of shale oil and gas production by hydraulic fracturing (fracking) is of increasing concern. The biggest potential source of environmental contamination is flowback and produced water, which is highly contaminated with hydrocarbons, bacteria and particulates, meaning that traditional membranes are readily fouled. We show the chemical functionalisation of alumina ceramic microfiltration membranes (0.22 μm pore size) with cysteic acid creates a superhydrophilic surface, allowing for separation of hydrocarbons from frac and produced waters without fouling. The single pass rejection coefficients was >90% for all samples. The separation of hydrocarbons from water when the former have hydrodynamic diameters smaller than the pore size of the membrane is due to the zwitter ionically charged superhydrophilic pore surface. Membrane fouling is essentially eliminated, while a specific flux is obtained at a lower pressure (<2 bar) than that required achieving the same flux for the untreated membrane (4–8 bar).
Although the long-term solution to global energy needs must be based on renewable sources, the present demand for oil and gas shows no sign of a reduction. Unfortunately this comes at a price in terms of resource consumption and possible environmental hazards1,2,3,4,5. The introduction of horizontal drilling coupled with hydraulic fracturing or ‘fracking’ has increased the cost of effective access to oil and gas resources, but water usage and wastewater remains controversial issues6,7. Hydraulic fracturing uses on average 20 million litres of water per well, of which only 10–15% is typically recovered during the flowback stage8. Flowback water as well as post-well completion water (production or produced water) are contaminated with hydrocarbons9, many of which are classified as hazardous, which along with significant bacteriological content means that this water cannot be reused without significant treatment10. The recovery of clean water for recycling and reuse has been viewed in the past by industry as being economically untenable as produced water is notoriously difficult to purify. As a consequence in most cases the waste water is either evaporated or disposed of through deep injection into abandoned gas or oil wells11. In either case storage and transportation of enormous volumes is required, with the potential risk of spillage. Since fresh water is a valuable commodity, wastage is not acceptable, especially in regions of continued drought. Thus, the recyclability of frac (and produced) water is a desirable goal from the environmental and economic viewpoint12.
Recyclability of many industrial wastes has been undertaken using ceramic filtration membranes, primarily for their robust nature and the ability to have select pore sizes with narrow distributions. Unfortunately, their capacity to purify or otherwise separate material has many drawbacks, such as membrane fouling leading to low permeate flux13. These drawbacks have precluded treatment of flowback and produced water because of submicrion particles, colloids, and hydrophobic organics14. Oil emulsions are generally removed by particle filtration (10–1000 μm pore size) and certainly by microfiltration (0.1–10 μm pore size). Shale gas produced water contains 1,000–50,000 mg/L of hydrocarbons, which are divided into the saturate, aromatic, resin and asphaltene (SARA) groupings9. While the emulsions represent a challenge with regard to fouling14, the solubilized SARA chemicals pose an issue for separation since their molecular weights are much lower than the cut-off for microfiltration. Use of a microfiltration membrane is FDA approved for bacteria removal from water, but hydrocarbons (even high molecular weights) pass through such membranes. Natural organic matter is generally in the 0.001–0.1 μm size, which requires ultrafiltration (0.005–1.0 μm pore size) or nanofiltration (0.0005–0.005 μm pore size). Produced water contains natural organic matter, as well as sugars derived from guar gum (used in frac fluids)15,16. If cost and energy consumption were not an issue, then the removal of these impurities may be possible using a multi-stage process to remove each component. It has been suggested that membrane distillation (MD) is an attractive treatment option for shale gas produced water because of its ability to handle high salinity as well as the inherent geothermal heat available to this process17,18.
What is needed is a process that removes hydrocarbons and resins at the same time as bacteria and particulates. Due to fouling ultrafiltration and nanofiltration are not suitable14. The interaction between membrane surfaces and solutes plays an important role in determining the extent of membrane fouling, explained by the mechanisms of pore blocking, cake formation or hydrophobic interaction19,20. Hydrophobic interaction between solutes and membrane material is frequently accepted as one of the predominant mechanisms. Membrane fouling is expected to be less severe with hydrophilic than hydrophobic membranes21,22,23. In addition, the high permeate flux for aqueous eluants is superior to hydrophobic membranes24.
There have been various approaches to alter ceramic membranes to be more hydrophilic with antifouling properties: coatings25, graft polymerization26, and metal substitution27,28. However, the chemistry of alumina microfiltration membranes offers the ability to create direct functionalization of the surface (using carboxylic acids) without changing pore size or membrane stability29. Furthermore, the use of different functional groups on alumina surfaces allows for changes in the wettability of the surface30,31. Cysteic acid (HO2CCH(NH2)CH2SO3H) functionalization (Fig. 1a) forms a super hydrophilic surface (contact angle of 5°, see Fig. 1b,c)32. Functionalization of the surface of a ceramic membrane also controls the flux rate through the membrane: generally, the more hydrophilic a surface the higher the flux32. Our goal is to show that functionalization of an alumina ceramic membrane with cysteic acid should increase the flux through the membrane for a particular pore size and that cysteic acid-functionalized alumina membranes can separate oil emulsions from frac and produced water.
Results and Discussion
A membrane average pore size of 0.22 μm was chosen since this is in the high end of the ultrafiltration range and low end of the microfiltration range. The membrane should reject oil emulsion, bacteria and particulates by size exclusion; however, sugars and other soluble organic compounds should not be rejected. The pore size is sufficiently small that fouling occurs rapidly with types of components in produced water.
The membranes were functionalized by reacting at 85 °C with cysteic acid in DI water. Reactions were initially carried out in a static reaction vessel; however, it was found that for more than one membrane it is easier to perform the reaction by flowing the cysteic acid solution through the membrane. The treated membranes are very hygroscopic and will attain a wet appearance, even after being dried, even if they are stored in a low humidity environment. The surface area of the membrane (0.358 m2/g) is unchanged upon surface functionalization.
SEM analysis of the surface of the functionalized membranes is indistinguishable from the untreated membrane, but the difference can be seen from EDS analysis. In the EDS spectrum both sulphur and nitrogen peaks are observed for the functionalized membrane (Fig. 1e,f), which are absent for the un-functionalized membrane (Fig. 1d). Mapping of the functionalized membrane for nitrogen and sulfur showed even coverage across the entire cross section (Fig. 1h–l). Nitrogen and sulphur signals were not diminished after the membrane was washed repeatedly or after treatment of multiple batches of frac or produced water, confirming that the cysteic acid is covalently bound to the alumina surface33.
Produced water analysis
The total carbon (TC), non-purgeable organic carbon (NPOC, also known as total organic content or TOC), and total inorganic carbon (TIC) for each produced water sample were measured (Table 1). In our previous report of the quantitative analysis of produced water samples, we found that the TOC of a shale produced water from wells recently drilled varies between 3 and 58 g/L9. Some of the samples studied herein are from dry gas wells and thus represent examples of water with lower initial carbon content. The NPOC is significantly higher than the TIC for most of the samples; however, both Roosevelt (Utah) and Scott Sugg (Texas) samples show a TIC:NPOC ratio >1, i.e., the carbonate content is higher than the organic content. There is no relationship between TIC and NPOC, which is consistent with the variation of geology between various shale reservoirs. The important point from this observation is that the source waters vary considerably and any process for treatment will have to deal with a range of feed compositions.
Qualitative and quantitative analyses were undertaken using the setup described in the Fig. 2. Initial analysis by inspection clearly demonstrated the ability of the membrane to screen colloidal hydrocarbons. The clarity of the permeate sample compared to the feed and the concentrated samples indicated that the membrane successfully removes large amounts of water contaminate (Fig. 3a). Analysis of the carbon content of both permeate and concentrate samples in comparison to the feed sample showed that there was significant removal of carbon material in the production water. The carbon of the permeate sample was in the low ppm range (Table 1). The same extremely low carbon content was evident for all types of water analysed. It is worth noting that while only the Roosevelt produced water comes close to being within EPA limits (0.01–1.0 mg/L) after purification, all of the samples are cleaned sufficiently for re-use in a hydraulic fracture or a water flood, allowing for re-use.
The percentage retention of carbon content by the membrane (a measure of the ability of the membrane to remove carbon from the permeate) was calculated using R = 1−(Cp/Cr), where R = rejection coefficient, Cp = permeate concentration and Cr = retentate concentration. For TC and NPOC the rejection coefficient was generally in the range 0.95–0.99 for produced water samples (Table 2). The Scott Sugg flowback sample shows the lowest rejection coefficients. The carbonate concentration (IC) in the feed is higher than the organic content (NPOC); however, NPOC in the permeate is reduced compared to the feed. The sample taken from the evaporation pit also showed a slightly lower rejection coefficient for a single pass; however, analysis of several samples collected from different locations in the pit showed a variation from 0.78–0.92. The rejection coefficient for TIC (>90%) for the samples, except the Scott Sugg, which is one of the highest TIC:NPOC ratio materials, and the low rejection is possibly associated with the low level of organic present.
A chemical analysis of the feed, concentrate and permeate water was undertaken using GC-MS analysis9. The GC traces for Marcellus produced water feed (Fig. 3b) and retentate (Fig. 3c) are almost identical, consistent with the NPOC results. In contrast, the trace for the permeate (Fig. 3d) shows only a few small peaks (in addition to the reference peak CHCl3 used for the solvent extraction9). The assignment for these peaks was based upon the fitting of the integrated mass spectrum for each peak. The detectable organic components that pass through the cysteic acid functionalized membrane are acetone, methylcyclohexane, and ethylcyclohexane. While acetone is miscible in water, the cyclohexanes are slightly soluble (16 and 3.8 mg/L, respectively), but below the NPOC measured in the permeate of the Marcellus shale produced water. Similar analysis of the permeate from the Barnett and Eagle Ford waters indicates that hydroxyacetonitrile, 1,1-dimethylcyclopropane, and 2-methyl-1-butene are potentially not rejected by the membrane. While hydroxyacetonitrile is highly soluble in water, the other two have very low solubility. These low molecular weight hydrocarbons have been observed in the permeate using un-functionalized membranes with a similar pore size as the membrane utilized here (0.22 µm).
The normal definition of flowback and produced is that the latter occurs once gas or oil have started to be produced. However, it is difficult to chemically differentiate the water. One potential differentiator is the presence of guar gum (or degradation components thereof). Gels of guar gum cross-linked with borax or a transition metal compounds are used in hydraulic fracturing fluids to provide viscosity15,34. The polysaccharide guaran (Mw ≈ 106 Da) is the major component of guar gum. The ability to remove guar gum from flowback or produced water has proven difficult due to the higher amounts of TDS contained in water which contribute to membrane surface fouling. In addition, the solubility of hydrolyzed guar gum in water contributes to the difficulty in separating using microfiltration. However, this has proven to not be the case with our functionalized alumina membrane. For continual filtration (i.e., with return of both the concentrate and permeate to the feed) the rejection coefficient shows a slow decrease only after 2 hours of treatment (Fig. 4a).
The chemistry of a shale reservoir is unlike that of a conventional oil or gas reservoir that is flushed with transient water resulting in the equilibration of the rock and other components. The salt content of produced waters have been extensively reported35, and there is no direct relationship between the conductivity and pH indicating that the conductivity is a function of salt content and identity rather than acidity9. The conductivity of the retentate and permeate change slightly with respect to the feed as shown in Fig. 4b. Given the high organic rejection by the membrane, it is expected that the retentate have a lower conductivity, which was observed. Typical results for the inorganic components (determine by ICP-OES), shown in Fig. 4c, and remains more or less unaffected by the separation process except for iron. We believe iron retention is indicative of the membrane screening of bacterial colonies contained in the feed water, since the membrane does not reject soluble Fe3+. The reduction of iron is important since if the water is to be reused for hydraulic fracking then the iron concentration must be carefully controlled to inhibit premature cross-linking of gel based frack fluids32. Percentages of rarer metals are observed only in the concentrate but not in the feed or permeate, presumably as a result of retention of functionalized organic molecules that may ligate these metals, and should not be attributed to some form of reverse osmosis or ion exchange process.
The bacterial content of selected samples was determined before and after treatment with the cysteic acid functionalized 0.22 μm α-alumina membrane. Akob et al.36 has reported the typical microbiology of produced waters from Pennsylvania shale gas wells found that microbial viability were highly variable in the range of 66–9400 cells/mL. As seen in Table 3, the produced water shows bacteria counts in the region of 103–106 bacterial per mL (CFU/mL); however, as expected the removal is >99% because of the pore size not the functionalization.
Membrane fouling and performance
One of the goals of using the cysteic acid functionalized super hydrophilic membrane was to minimize fouling and hence flux decline as compared to an un-functionalized membrane which suffers a decay on the permeate flow due to fouling from organics. Evolution of permeate flux rate (Qp) as a function of time (Fig. 5a) the permeate flux decreases initially but then stabilizes and remains so for the duration of the measurement. This is in complete contrast to analogous data for an unfunctionalized membrane that shows a dramatic decrease in permeate flux rate within 18 hours (Fig. 5a), under identical conditions. For the cysteic acid functionalized membranes the trans-membrane pressure (Fig. 5b) shows an initial build-up of pressure, which then subsides. The pressure then remains steady for the period of the measurement. This initial build up is a result of ‘saturation’ of the membrane with water and can be attributed to two factors. Firstly, due to the purging of the pores of air, which can block a pore and result in a lower area for permeate to pass through thus resulting in higher pressures and secondly, the establishment of a steady-state water layer (or layers) on the membrane surface. These water layers have been attributed to the reason for the extended lifetime of the functionalized membrane and its ability to avoid surface fouling. This means that the membranes can run longer and are more effective over a longer period of time.
The aligned orientation of the sulfonyl and amine moieties away from the membrane surface results in the membrane displaying significant hydrophilicity27. With the surface functionalization of the entire membrane the pore size has not been altered to any significant extent, i.e., the cysteic acid molecule is minuscule (ca. 9 Å) compared to the pore size of the membrane (2200 Å). The ability of the functionalized membrane to separate hydrocarbons from water when the hydrocarbon molecules have hydrodynamic diameters significantly smaller than the pore size of the membrane can be interpreted in several ways. Hydrophilic surfaces on membranes have been shown to be superior for the rejection of organic molecules as well as showing a reduction in membrane fouling21,22,23,24. This study has shown that the cysteic acid functionalization is not just on the exterior surface of the channels, but also on the internal surface of the pores as well (Fig. 1), and thus creates a highly ordered zwitter ionically charged super hydrophilic membrane surface, which repels the oil components when the quantities are sufficient to form globules (a second phase).
Separation of water and hydrocarbons is only one issue that the cysteic acid functionalization appears to address. Fouling of membranes is a complex phenomenon and involves the deposition of solute or particles onto the membrane surface or into the pores. Fouling is usually enhanced with high membrane surface roughness, increased feed concentration, increased membrane flux and is dependent on the nature of the membrane surface and solute interaction forces. Therefore, efforts have been made to create highly uniform membrane surfaces to limit fouling21,22,23,24. The low fouling of the cysteic acid functionalized alumina membrane can be related to the zwitter ionic nature of the surface creating a super hydrophilic layer that is wetted with water. When organic globules contact this wetted layer they are repelled and do not have access to the membrane surface in order for deposition to occur. The modified surface of the membrane significantly increases the membrane flux (e.g., 1130 L/h.m2 @ 1 bar DI water) when compared to the original membrane (504 L/h.m2 @ 1 bar DI water). The flux obtained at low pressure (<2 bar) for the modified membrane is the same magnitude for the untreated membrane operating at >4 bar. As the flux is the same, there will be no impact on fouling. However, the lower operating pressure means reduced operational cost as the pump needed is smaller and consumes less electricity. Each of these factors has a corresponding environmental benefit and could be quantified by a reduced carbon footprint.
The present work shows that it is possible to treat frack flowback and produced water from shale oil and gas wells to reduce the hydrocarbon content to levels that are acceptable for re-use using a single pass through the membrane without pretreatment37. The high performance of this large pore size functionalized membrane with regards to hydrocarbon screening, high flux, low operating pressures, anti-fouling properties as well as ease of synthesis point to a new generation of hybrid inorganic membranes. The cysteic acid functionalization alters the properties of the membrane on the macro scale. The ability of this membrane to screen hydrocarbons of hydrodynamic diameters orders of magnitude smaller than the pore size appears a function of the solubility coefficient of the hydrocarbons and the resulting emulsified droplet rather than being attributed to direct separation as would result from a nano filtration membrane38.
All chemicals were purchased in high purity form from Sigma-Aldrich (Reference) and were used without further purification. Alumina membranes (0.22 μm nominal pore size) were purchased from Pall Corporation (Reference) and washed with DI water prior to treatment. All water used was purified via Millipore filtration to 18 MΩ deionized (DI). ICP standards (IV-ICPMS-71A) were obtained from Inorganic Ventures (Reference). Whatmann filters No. 40 were obtained from Fisher Scientific (Reference). Thermo Scientific 50 mL and 15 mL sterilized graduated conical centrifuge tubes were obtained from Fischer Scientific. Frac flowback and produced water samples were drawn from wells in the Marcellus (Pennsylvania), Eagle Ford (Texas), Barnett (New Mexico), Humble (Texas), Permian (Texas), Scott Sugg (Texas) and Roosevelt (Utah). Water samples were collected in 1-L mason jars. All jars used for sample collection were cleaned using detergent and rinsed thoroughly with DI water. The jars were then soaked in a base bath containing KOH in isopropyl alcohol for one week then rinsed thoroughly with ethanol then DI, followed by soaking in concentrated nitric acid for three days and again rinsed thoroughly with DI. All glassware used the same cleaning procedure. Samples were collected directly from frac tanks into which the produced water was directly piped. No mixing with other water sources was observed. All samples were collected without a headspace to reduce oxidation of the sample. All samples were stored and transported in sealed containers under refrigeration. Blank samples were tested using DI water. These showed that no chemicals were leached from the O-rings in the jar or contamination from other sources during handling and storage.
The reaction of the alumina membrane with cysteic acid was performed using a variation of previously reported procedures32. The alumina membranes were placed in an airtight glass container. The container was filled with DI water and placed under vacuum until the membrane stopped effervescing. This ensured removal of air from the interstitial pores. Vacuum was then removed and the glass column was heated to 85 °C for 24 hrs. The deionized water was drained from the container. The membrane was covered in a 1 M aqueous solution of cysteic acid; again vacuum was placed on the container until the membrane stopped effervescing. The solution was brought to gentle reflux for 2 days. The membrane was then allowed to return to room temperature. The membrane was again covered with DI and pumped down until the membrane stopped effervescing and gently heated to 50 °C then allowed to completely drain. This process was repeated three times, or until the water displayed pH = 6.
Thermogravimetric analysis (TGA) was conducted on a TA Instruments Q-600 simultaneous TG/DTA instrument, under argon using platinum pans. Analysis was conducted on TA Instruments analysis software. Infrared spectroscopy (IR) of functionalized and un-functionalized membranes was analysed on a Nicolet FTIR Infrared Microscope with diamond window. Bruaneaur-Emmet-Teller (BET) analysis was performed using the Quantachrome Autosorb-3B Surface Analyser. Samples were broken from the membrane and heated under vacuum at 80 °C for 24 hrs to remove any excess water. The samples were then purged with helium and analysed at 77 K under nitrogen. Scanning electron microscopy (SEM) analysis was conducted on FEI Quanta 400 a multiple stage high resolution field emission environmental scanning electron microscope (ESEM), both in scanning electron (SE) mode and energy dispersive X-ray scattering (EDS) mode, analysis was undertaken where stated either in Hi-Vac or Low-Vac mode. An acceleration voltage of 30 keV was used as well as a spot size of 4.0 to ensure a dwell time of approximately 30% for the EDS detector and to reduce charging. Samples were immobilized on an aluminium stub with carbon tape.
Produced water treatment
Filtration experiments were conducted on a single pass-closed loop batch system. The membranes were subjected to filtration of produced water. The flow rates of permeate and concentrate as well as assembly pressures and substituent temperatures were monitored. Sampling of the original production water, permeate, and the concentrate were taken at specified times. These samples were analysed for carbon content, conductivity, elemental composition, and finally molecular composition.
Bacteriological analyses were performed by Lance Energy Services, Inc. (Houston, TX). The water sample jars were decanted and pre-filtered three times with Whatmann Filter No. 40 before analysis to remove any samples containing visible particulate matter or non-dissolved matter. The filtered water was added to a glass 20 mL scintillation vial. Conductivity was measured on a calibrated pH/CON 510 Oakton analyser (WD-35610–10) using the protocol described previously4. Metal content of the produced and filtered water was analysed using ICP-OES (Inductively Coupled Plasma Optical Emission Spectrometer) carried out using an Optima 4300 DV spectrophotometer analyser with an AS-93 + auto sampler9. Carbon analysis was analysed using a Shimadzu TOC analyser (TOC-VCSH) using an auto-sampler (ASi-V) in TC and NPOC mode. Gas chromatography/mass spectroscopy (GC/MS) analyses were performed on an Agilent Technologies 5973 network mass selective detector with a quadrupole mass spectrometer with an Agilent Technologies 5973 network GC system, using a 30-m DB-1 capillary column (0.25-mm I.D., 0.25-μm film) and helium as the carrier gas. All samples were injected using an Agilent 7693 A Automatic Liquid Sampler with split/splitless injections of 1.0 μL, injection temperature was set at 285 °C.
Stephenson, E., Doukas, A. & Shaw, K. Greenwashing gas: might a ‘transition fuel’ label legitimize carbon-intensive natural gas development? Energ. Policy 46, 452–459 (2012).
Field, R. A., Soltis, J. & Murphy, S. Air quality concerns of unconventional oil and natural gas production. Environ. Sci.: Processes Impacts 16, 954–969 (2014).
Camarillo, M. K., Domen, J. K. & Stringfellow, W. T. Physical-chemical evaluation of hydraulic fracturing chemicals in the context of produced water treatment. J. Environ. Manage. 183, 164–174 (2016).
Annevelink, M. P. J. A., Meesters, J. A. J. & Hendriks, A. J. Environmental contamination due to shale gas development. Sci. Total Environ. 550, 431–438 (2016).
Drollette, B. D. et al. Elevated levels of diesel range organic compounds in groundwater near Marcellus gas operations are derived from surface activities. P. Natl. Acad. Sci. USA 112, 13184–13189 (2015).
Lampert, D., Cai, H. & Elgowainy, A. Wells to wheels: water consumption for transportation fuels in the United States. Energy Environ. Sci. 9, 787–802 (2016).
DiGiulio, D. C. & Jackson, R. B. Impact to underground sources of drinking water and domestic wells from production well stimulation and completion practices in the Pavillion, Wyoming, field. Environ. Sci. Technol. 50, 4524–4536 (2016).
Nicot, J. P. & Scanlon, B. R. Water use for shale-gas production in Texas, U.S. Environ. Sci. Technol. 46, 3580–3586 (2012).
Maguire-Boyle, S. J. & Barron, A. R. Organic compounds in produced waters from shale gas wells. Environ. Sci.: Processes Impacts 16, 2237–2248 (2014).
Vengosh, A., Jackson, R. B., Warner, N., Darraĥ, T. H. & Kondash, A. A critical review of the risks to water resources from unconventional shale gas development and hydraulic fracturing in the United States. Environ. Sci. Technol. 48, 8334–8348 (2014).
Johnston, J. E., Werder, E. & Sebastian, D. Wastewater disposal wells, fracking, and environmental injustice in southern Texas. Am. J. Public Health 106, 550–556 (2016).
Riley, S. M., Chan, K. E., Spear, J. R. & Cath, T. Y. Simplifying treatment for complex waste streams: oil and gas produced water and fracturing flowback wastewater. Proceedings of the Water Environment Federation, WEFTEC 2016, 4441–4446 (2016).
Padaki, M. et al. Membrane technology enhancement in oil-water separation. A review. Desalination 357, 197–207 (2015).
Xiong, B., Zydney, A. L. & Kumar, M. Fouling of microfiltration membranes by flowback and produced waters from the Marcellus shale gas play. Water Res. 99, 162–170 (2016).
Bishop, M., Shahid, N., Yang, J., Barron, A. R. Determination of the mode and efficacy of the cross-linking of guar by borate using MAS 11B NMR of borate cross-linked guar in combination with solution 11B NMR of model systems. Dalton Trans. 2621-2634 (2004).
Sharma, M. M. & Wunderlich, R. W. The alteration of rock properties due to interactions with drilling-fluid components. J. Petrol. Sci. Eng. 1, 127–143 (1987).
Kim, J., Kwon, H., Lee, S., Lee, S. & Hong, S. Membrane distillation (MD) integrated with crystallization (MDC) for shale gas produced water (SGPW) treatment. Desalination 403, 172–178 (2017).
Rao, G. & Li, Y. Feasibility study of flowback/produced water treatment using direct-contact membrane distillation. Desalin. Water Trea. 57, 21314–21327 (2016).
Scholtz, W. & Fuchs, W. Treatment of oil contaminated wastewater in a membrane bioreactor. Water Res. 34, 3621–3629 (2000).
Judd, S. & Till, S. W. Bacterial rejection in crossflow microfiltration of sewage. Desalination 127, 251–260 (2000).
Sun, Q., Su, Y., Ma, X., Wang, Y. & Jiang, Z. Improved antifouling property of zwitterionic ultrafiltration membrane composed of acrylonitrile and sulfobetaine copolymer. J. Membr. Sci. 285, 299–305 (2006).
Mohammad, A. W. et al. Nanofiltration membranes review: Recent advances and future prospects. Desalination 356, 226–254 (2015).
Cheng, S., Oatley, D. L., Williams, P. M. & Wright, C. J. Characterisation and application of a novel positively charged nanofiltration membrane for the treatment of textile industry wastewaters. Water Res. 46, 33–42 (2012).
Su, Y.-L., Cheng, W., Li, C., Chao, J. & Jiang, Z. Preparation of antifouling ultrafiltration membranes with poly(ethylene glycol)-graft-polyacrylonitrile copolymers. J. Membrane Sci. 329, 246–252 (2009).
Ba, C., Ladner, D. A. & Economy, J. Using polyelectrolyte coatings to improve fouling resistance of a positively charged nanofiltration membrane. J. Membrane Sci. 347, 250–259 (2010).
Faibish, R. S. & Cohen, Y. Fouling and rejection behavior of ceramic and polymer-modified ceramic membranes for ultrafiltration of oil-in-water emulsions and microemulsions. Colloid. Surface. A 191, 27–40 (2001).
Ma, W. et al. Spray- and spin-assisted layer-by-layer assembly of copper nanoparticles on thin-film composite reverse osmosis membrane for biofouling mitigation. Water Res. 99, 188–199 (2016).
DeFriend, K. A., Wiesner, M. R. & Barron, A. R. Alumina and aluminate ultrafiltration membranes derived from alumina nanoparticles. J. Membrane Sci. 224, 11–28 (2003).
Alexander, S., Morrow, L., Lord, A. M., Dunnill, C. W. & Barron, A. R. pH-responsive octylamine coupling modification of carboxylated aluminium oxide surfaces. J. Mater. Chem., A 3, 10052–10059 (2015).
Maguire-Boyle, S. J., Liga, M. V., Li, Q. & Barron, A. R. Alumoxane/ferroxane nanoparticles for the removal of viral pathogens: the importance of surface functionality to nanoparticle activity. Nanoscale 4, 5627–5632 (2012).
Alexander, S., Eastoe, J., Lord, A. M., Guittard, F. & Barron, A. R. Branched hydrocarbon low surface energy materials for superhydrophobic nanoparticle derived surfaces. ACS Appl. Mater. Interfaces 8, 660–666 (2016).
Maguire-Boyle, S. J. & Barron, A. R. A new functionalization strategy for oil/water separation membranes. J. Membrane Sci. 382, 107–115 (2011).
Bethley, C. E. et al. Structural characterization of dialkylaluminum carboxylates: models for carboxylate alumoxanes. Organometallics 16, 329–341 (1997).
Schechter, R. Oil Well Stimulation, Prentice-Hall Inc., Englewood Cliffs, NJ (1992).
Andrew, A. S., Whitford, D. J., Berry, M. D., Barclay, S. A. & Giblin, A. M. Origin of salinity in produced waters from the Palm Valley gas field, Northern Territory, Australia. Appl. Geochem. 20, 727–747 (2005).
Akob, D. M., Cozzarelli, I., Dunlap, M., Rowan, D. S. & Lorah, E. L. M. M. Organic and inorganic composition and microbiology of produced waters from Pennsylvania shale gas wells. Appl. Geochem. 60, 116–125 (2015).
Michel, M. M., Reczek, L., Granops, M., Rudnicki, P. & Piech, A. Pretreatment and desalination of flowback water from the hydraulic fracturing. Desalin. Water Treat. 57, 10222–10231 (2016).
Pendergast, M. T. M. & Hoek, E. M. V. A review of water treatment membrane nanotechnologies. Energy Environ. Sci. 4, 1946–1971 (2011).
Financial support was provided by the Welsh Government Sêr Cymru Programme, FLEXIS, which is part-funded by the European Regional Development Fund (ERDF) through the Welsh Government, and the Robert A. Welch Foundation (C-0002). The assistance of Waymon Votaw and Jake Davies in sample collection is acknowledged.
The authors declare that they have no competing interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Maguire-Boyle, S.J., Huseman, J.E., Ainscough, T.J. et al. Superhydrophilic Functionalization of Microfiltration Ceramic Membranes Enables Separation of Hydrocarbons from Frac and Produced Water. Sci Rep 7, 12267 (2017). https://doi.org/10.1038/s41598-017-12499-w
Modifying ceramic membranes with in situ grown iron oxide nanoparticles and their use for oily water treatment
Journal of Membrane Science (2021)
Ultrasound assisted large scale fabrication of superhydrophilic anodized SnOx films with highly uniformed nanoporous arrays
Materials Chemistry and Physics (2020)
Integrated preparation of alumina microfiltration membrane with super permeability and high selectivity
Journal of the European Ceramic Society (2019)
Glutaraldehyde inhibits biological treatment of organic additives in hydraulic fracturing produced water
Science of The Total Environment (2019)
Potential and implemented membrane-based technologies for the treatment and reuse of flowback and produced water from shale gas and oil plays: A review