Preparation of porous Fe2O3 nanorods-reduced graphene oxide nanohybrids and their excellent microwave absorption properties


In this paper, α-Fe2O3 nanoparticles (NPs)-reduced graphene oxide (RGO), α-FeOOH nanorods (NRs)-RGO and porous α-Fe2O3 NRs-RGO could be selectively synthesized by hydrothermal method. The investigations indicated that the obtained α-Fe2O3 NPs, α-FeOOH NRs and porous α-Fe2O3 NRs were either attached on the surface of RGO sheets or coated uniformly by the RGO sheets. And the as-prepared nanohybrids exhibited excellent microwave absorption performance, which was proved to be ascribed to the quarter-wavelength matching model. The optimum reflection loss (RL) values for α-Fe2O3 NPs-RGO, α-FeOOH NRs-RGO and porous α-Fe2O3 NRs-RGO were ca. −32.3, −37.4 and −71.4 dB, respectively. Moreover, compared to the obtained α-Fe2O3 NPs-RGO and α-FeOOH NRs-RGO, the as-prepared porous α-Fe2O3 NRs-RGO nanohybrids exhibited enhanced microwave absorption properties because of their special structure and synergetic effect. The possible enhanced microwave absorption mechanisms were discussed in details. Our results confirmed that the geometrical morphology had a great influence on their microwave absorption properties, which provided a promising approach to exploit high performance microwave absorbing materials.


In recent decades, with the rapidly extensive application of wireless equipment, radar systems and local area networks, etc, electromagnetic (EM) interference, EM radiation and EM compatibility have become the serious problems, which not only are harmful to human and the operation of electronic devices, but also influence the development of modern military1,2,3,4. As a kind of functional material, microwave absorbing materials (MAMs) can effectively absorb EM waves by either dissipating EM wave loss or converting EM energy into thermal energy. Hence, high performance MAMs with light weight, strong absorption ability and wide absorption frequency are highly desired. According to EM energy conversion principle, the traditional single dielectric/magnetic loss absorbers such as ferrite, ZnO and Fe3O4 are difficult to meet this condition due to the mismatch in the values of complex permittivity \(({{\boldsymbol{\varepsilon }}}_{{\boldsymbol{r}}}={\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }}-j{\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime\prime} }})\) and complex permeability \(({{\boldsymbol{\mu }}}_{{\boldsymbol{r}}}={\boldsymbol{\mu }}{\boldsymbol{^{\prime} }}-{\boldsymbol{j}}{\boldsymbol{\mu }}{\boldsymbol{^{\prime\prime} }})\) 5,6,7,8. One of the effective ways to solve the problem is to couple dielectric materials with nanostructured materials9,10,11. Therefore, various hybrids have been investigated in order to reach the targets over the past years12,13,14,15,16. Among these hybrids, carbon-based hybrids own advantages such as low density, good chemical stability and high complex permittivity value, which may improve the microwave absorption properties and EM interference shielding effect17,18,19.

Recently, graphene (G), as a new kind of carbon material, has attracted tremendous scientific attention in recent years because of its outstanding physical and chemical properties such as the excellent thermal and electronic conductivity, huge specific surface area, and so on20,21,22. Therefore, anchoring transition metal oxides onto G-based matrix will be a promising strategy to develop high performance MAMs23. Moreover, the previous theoretical studies indicated that the interfacial electronic interaction between metal and G could make G show some novel magnetic and electric properties24, 25. Therefore, different categories of G-based nanohybrids have been developed to improve microwave absorption properties in the recent years26,27,28,29. However, the focus of these studies is mainly on the particles. And the recently reported results indicate that the crystal structure, size and special geometrical morphology also may have an influence on their microwave absorption properties, and these related studies were seldom reported before30, 31.

In this paper, we develop a simple strategy to selectively synthesize heterostructured α-Fe2O3 nanoparticles (NPs)-reduced graphene oxide (RGO), α-FeOOH nanorods (NRs)-RGO and porous α-Fe2O3 NRs-RGO nanohybrids by controlling the categories of the initial reactant, respectively. Through the detailed investigations, we find that the as-synthesized heterostructured nanohybrids improve greatly their microwave absorption capabilities compared with those of the single composition of FeOOH or graphene oxide (GO). More importantly, compared to α-Fe2O3 NPs-RGO and α-FeOOH NRs-RGO, the as-synthesized porous α-Fe2O3 NRs-RGO nanohybrids exhibit enhanced microwave absorption performance.


The preparation process of Fe based-RGO nanohybrids is illustrated in Fig. 1. When the solutions of FeSO4, NaHCO3 and GO are mixed, the redox reaction during the hydrothermal treatment brings the formation of heterostructured Fe2O3 NPs-RGO nanohybrids (denoted as C1). However, if only the solutions of FeSO4 and GO are mixed, heterostructured FeOOH NRs-RGO nanohybrids (denoted as C2) can be synthesized because Fe2+ cations from FeSO4 can favourably binding with oxygen-containing on GO sheets during the hydrothermal treatment. Similar to the previously reported results32, 33, porous Fe2O3 NRs-RGO nanohybrids (denoted as C3) could be obtained after the annealing treatment of C2. Moreover, for comparison, FeOOH NRs are also synthesized (detailed experiment, see supporting information). Figure 2 presents the TEM images of GO and C1. As shown in Fig. 2a and b, the wrinkled and transparent paper-like structures of GO can be observed clearly, indicating that GO is a few atomic layers in thickness and good quality34. The morphology of GO is very similar to the previous report35. The TEM observation (as shown in Fig. 2c and d) indicates that the obtained C1 consists of two-dimensional RGO sheets and Fe2O3 NPs, and the as-prepared heterostructured Fe2O3-RGO nanohybrids exhibit the wrinkled paper-like structure, same to the characteristic feature of GO sheets. Moreover, the Fe2O3 NPs with size in the range of 50–200 nm are well distributed and decorated on RGO or coated by the RGO sheets. There is no apparent aggregation of Fe2O3 NPs on the RGO sheets. Compared with the recently reported work by Zhang et al.36, the proposed route here is much more simple and effective.

Figure 1

Schematic diagram for the synthesis process of Fe based-RGO nanohybrids.

Figure 2

TEM images of (a,b) GO, and (c,d) C1.

Figure 3 displays the TEM images of the as-prepared C2 and C3. As shown in Fig. 3a and b, the flexible two-dimensional RGO sheets and FeOOH NRs can be observed clearly over the obtained C2. Similar to MnO2 NRs-RGO and MnO2@Fe-G reported elsewhere37, 38, the obtained FeOOH NRs, show very uniform sizes in diameter and length, load tightly on the thin flaky RGO sheets or are enwrapped by the RGO sheets. The TEM investigation (as shown in Fig. 3c and d) indicates that the as-synthesized C3 contains the wrinkled paper-like structure of RGO and porous Fe2O3 NRs (as indicated by the arrows in Fig. 3d). Same to those of C1 and C2, the obtained porous Fe2O3 NRs exhibit uniform sizes and are anchored on RGO surface or coated in the RGO sheets without serious aggregation. Moreover, as shown in Figure S1, the porous structure of Fe2O3 NRs can also be confirmed further by the N2 adsorption and desorption isotherms. Compared to that of C2, one can find that the as-prepared C3 exhibits an evidently enhanced BET surface area. Generally, compared to the previously reported iron oxides@RGO36, this proposed route not only can control the category of iron oxide, but also adjusts its morphology.

Figure 3

TEM images of (a,b) C2, and (c,d) C3.

Figure 4 presents the XRD patterns of as-synthesized GO and products. As shown in Fig. 4a, the diffraction peaks at 9.4 and 26.5° can be indexed to GO39, 40. The diffraction peaks of the as-prepared C1 (As shown in Fig. 4b) located at ca. 24.2, 33.2, 35.7, 41.0, 49.5, 54.1, 57.6, 62.5, 64.1 and 71.9° can be indexed to (012), (104), (110), (113), (024), (116), (122), (214), (300) and (119) facets of hexagonal phase α-Fe2O3 (JCPDS: 86–0550). For C2, as labeled in Fig. 4c, all the diffraction peaks can be assigned to orthorhombic phase of α-FeOOH (JCPDS: 29–0713). And all the diffraction peaks (as shown in Fig. 4d) appeared in the range of 20–90° can be indexed to hexagonal phase α-Fe2O3 (JCPDS: 86–0550). Compare the XRD patterns of C1 and C3, one can find that the strongest diffraction peak of C3 is at ca. 35.6° while the strongest one of C1 is at 33.2°. Combined with the TEM results (as shown in Figs 2 and 3), we think the change of the strongest diffraction position may be ascribed to the preferential growth of Fe2O3 NRs (C3). Based on the obtained TEM and XRD results, one can find that the obtained C1, C2 and C3 are α-Fe2O3 NPs-RGO, α-FeOOH NRs-RGO and porous α-Fe2O3 NRs-RGO nanohybrids, respectively.

Figure 4

XRD patterns of (a) GO, (b) C1, (c) C2, and (d) C3.

Figure 5 shows the IR and Raman spectra of the obtained samples. As shown in Fig. 5a, for GO, the peaks at 3440 and 1627 cm−1 can be attributed to the stretching vibration of O-H and C = C, respectively. And the other characteristic peaks appeared at 2927, 1726 and 1046 cm−1 are due to the stretching vibration of C-H, C = O and epoxy C-O, respectively. Compared to GO, one can find that the oxygen-containing functional groups at 3440, 1726 and 1046 cm−1 decrease in the FTIR spectra of the obtained C2 and these peaks almost vanish in the FTIR spectra of the obtained C3, which indicates that the obtained GO is reduced during the hydrothermal process. Figure 5b gives Raman spectra of the as-synthesized GO, C1 and C2, in which two sharp peaks are obviously in common: D band at ca. 1356 cm−1 originating from disordered carbon and the G band at ca. 1599 cm−1 corresponding to sp2 hybridized carbon. Compared with GO, the D band becomes more prominent and an increased D/G intensity ratio of the obtained C1 and C2 can be found, revealing a decrease in the average size of the sp2 domains upon further chemical reduction of the GO during thermal synthesis of C1 and C241, 42. We can coarsely evaluate the disorder degree in graphene by the rule: the higher ID/IG value, the more defects exist43. The increase of ID/IG also confirms the reduction of GO to RGO during the reaction process44. Furthermore, the 2D peak (2706 cm−1) and a combination mode of D + D´ at higher wave number (2937 cm−1) can also observed clearly over the as-synthesized samples. It is well known that the 2D band in the Raman spectra of graphene is a second-order double-resonance process whose line shape indicates the number of graphene layers in the sample45,46,47.

Figure 5

(a) FT-IR, and (b) Raman spectrum of GO and the as-prepared hybrids.

According to the transmission line theory, the values of reflection loss (RL) and attenuation constant (α) are calculated by the following equations48, 49:

$${{\boldsymbol{Z}}}_{{\boldsymbol{in}}}=\sqrt{\frac{{{\boldsymbol{\mu }}}_{{\boldsymbol{r}}}}{{{\boldsymbol{\varepsilon }}}_{{\boldsymbol{r}}}}}\,{\bf{\tanh }}({\boldsymbol{j}}\frac{{\bf{2}}{\boldsymbol{\pi }}\mathrm{fd}\sqrt{{{\boldsymbol{\mu }}}_{{\boldsymbol{r}}}{{\boldsymbol{\varepsilon }}}_{{\boldsymbol{r}}}}}{{\boldsymbol{c}}})$$
$${\boldsymbol{\alpha }}=\frac{\sqrt{{\bf{2}}}{\boldsymbol{\pi }}f}{{\boldsymbol{c}}}\sqrt{({\boldsymbol{\mu }}{\boldsymbol{^{\prime\prime} }}{\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime\prime} }}-{\boldsymbol{\mu }}{\boldsymbol{^{\prime} }}{\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }})+\sqrt{{({\boldsymbol{\mu }}{\boldsymbol{^{\prime\prime} }}{\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime\prime} }}-{\boldsymbol{\mu }}{\boldsymbol{^{\prime} }}{\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }})}^{2}+{({\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }}{\boldsymbol{\mu }}{\boldsymbol{^{\prime\prime} }}+{\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime\prime} }}{\boldsymbol{\mu }}{\boldsymbol{^{\prime} }})}^{2}}}$$

where f is the frequency of EM wave, d is the thickness of absorber, c is the velocity of light and Z in is the input impedance of absorber. Based on the equations (1) and (2), the RL values of GO, α-FeOOH NRs, the as-synthesized C1, C2 and C3 are obtained. As shown in Fig. 6. It can be seen clearly that: (1) the minimum RL values of the obtained samples move towards the lower frequency region with the increasing thickness; (2) compare GO with α-FeOOH NRs (as shown in Figure S2), the obtained nanohybrids exhibit evidently enhanced microwave absorption performances; (3) the minimum RL values for C1, C2 and C3 are ca. −32.3 dB at 9.4 GHz with the matching thickness of 9.99 mm, −37.4 dB at 12.2 GHz with the matching thickness of 8.29 mm and −71.4 dB at 14.36 GHz with a matching thickness of 7.48 mm, respectively; (4) RL values below −20 dB (99% of EM wave attenuation) for C1, C2 and C3 can be obtained in the frequency range of 12.6–15.1, 11.2–18.0, and 10.3–18.0 GHz, respectively; (5) RL values below −10 dB (90% of EM wave attenuation) for C1, C2 and C3 can be observed in the frequency range of 8.8–18.0, 9.6–18.0 and 9.6–18.0 GHz, respectively. As shown in Table 1, one can find clearly that the as-prepared porous α-Fe2O3 NRs-RGO hybrids show the superior absorption properties among other similar hybrids.

Figure 6

Two-dimensional representation RL values of (a) GO, (b) C1, (c) C2 and (d) C3, respectively.

Table 1 EM wave absorption properties of Fe-based nanohybrids reported in recent representative papers.


In order to analyze the difference in obtained RL results, the EM parameters, dielectric and magnetic loss abilities, attenuation constant and EM impedance matching are presented. Figure 7 gives the complex permittivity and complex permeability of GO and the as-prepared hybrids in the 2.0–18 GHz frequency range. As shown in Fig. 7a, besides some fluctuations, the \({\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }}\) values of the as-synthesized samples are found to decrease with the frequency in the tested region. On the basis of the Debye theory, \({\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }}\) can be described as57:

$${\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }}={{\boldsymbol{\varepsilon }}}_{\infty }+\frac{{{\boldsymbol{\varepsilon }}}_{{\boldsymbol{s}}}-{{\boldsymbol{\varepsilon }}}_{\infty }}{{\bf{1}}+{{\boldsymbol{\omega }}}^{{\bf{2}}}{{\boldsymbol{\tau }}}^{{\bf{2}}}}$$

where \({\varepsilon }_{s}\) is the static permittivity, \({\varepsilon }_{\infty }\) is the relative dielectric permittivity at the high frequency limit, ω is angular frequency, τ is polarization relaxation time. According to the equation (4), one can find that the decreases of \(\varepsilon ^{\prime} \) are mainly attributed to the increase of ω. As reported previously57, 58, the phenomenon can be considered as the polarization relaxation in the lower frequency range. It can be seen that the \({\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }}\) values of the obtained samples are as follows: α-FeOOH (as shown in Figure S3a) < GO < C3 < C2 < C1. Compared to the previous results of the G-based hybrids, the as-prepared Fe based-RGO nanohybrids exhibit a relatively low \({\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }}\) values, which may lead to high impedance matching behavior and good microwave absorption54, 55, 59. Although the obtained α-FeOOH and GO exhibit much lower values of \({\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }}\), according to the transmission line theory and previous results48, 60, single material such as FeOOH, Fe2O3 or GO cannot exhibit excellent microwave absorption performance. As for the imaginary part of the permittivity (as shown in Figs 7b and S3b), although it has some fluctuations, all in all, it can be seen that the \(\varepsilon ^{\prime\prime} \) values of the obtained samples are as follows: α-FeOOH < GO < C2 < C3 < C1. It is well known that the larger value of \(\varepsilon ^{\prime\prime} \) indicates an increased dielectric loss61. Unlike the dielectric behavior, the permeability properties of the obtained samples are shown in Fig. 7c and d. Overall, there are no significant changes of \(\mu ^{\prime} \) and \(\mu ^{\prime\prime} \) among the obtained samples, which should be related to their nonmagnetic properties at RT62. And the result indicates a small difference of magnetic loss among the obtained nanohybrids. Moreover, as shown in Fig. 7d, we can notice that the \(\mu ^{\prime\prime} \) values are negative in part of the frequency range, which may be ascribed to the magnetic energy being radiated out, noise, and/or the permeability-to-permittivity transform of EM wave in nanohybrids63,64,65,66,67.

Figure 7

EM characteristics of the obtained hybrids: (a,b) real and imaginary parts of permittivity, and (c,d) real and imaginary parts of permeability.

Figure 8 presents the dielectric and magnetic loss properties, attenuation constant and impedance matching of the obtained nanohybrids. As shown in Fig. 8a and b, one can find that all the obtained hybrids exhibit much larger values of \(\tan \,{\delta }_{{\rm{E}}}\) than those of \(\tan \,{\delta }_{m}\), which implies that the EM attenuation is mainly due to dielectric loss. And the dielectric loss performance of the hybrids presents the following tendency: C1 > C3 > C2. Moreover, the obtained hybrids display excellent mutual compensation between dielectric loss and magnetic loss, and this effective compensation is very beneficial to enhance their microwave absorption capabilities68. According to equation (3), the α values of hybrids are obtained and shown in Fig. 8c. It can be seen that the as-prepared C1 exhibits the highest α value while the α value of C2 is the lowest. In addition, compared to the previously reported MnO2@Fe-G37, the α value of the obtained ternary nanohybrids is much higher, and the high value of α is conducive to improve EM wave absorption capability49. Based on the measured complex permittivity and permeability, the impedance matching ratios of the as-prepared hybrids are obtained and displayed in Fig. 8d. As a whole, one can find that the impedance matching ratio of C3 is much higher than those of C1 and C2. It is well known that the excellent impedance matching ratio is favorable to absorb EM wave. Based on the aforementioned results, one can find that the enhanced microwave absorption capabilities of porous α-Fe2O3 NRs-RGO hybrid can be attributed to the good dielectric loss ability, high attenuation constant and excellent impedance matching ratio.

Figure 8

(a,b) Loss tangent, (c) attenuation loss, and (d) impedance matching ratios of the as-prepared hybrids.

Recently, two models have been proposed to interpret the excellent EM wave absorption properties of hybrids30, 49. The first model is zero reflection, according to the EM wave theory, the relationship \({{\boldsymbol{\mu }}}_{{\boldsymbol{r}}}={{\boldsymbol{\varepsilon }}}_{{\boldsymbol{r}}}\) should be satisfied. However, as shown in Fig. 7, the obtained samples exhibit much higher values of permittivity than their permeability. Therefore, the model cannot be used to explain the obtained results. The other one is geometrical effect, which occurs when the incident and reflected waves in the material are out of phase 180° at the particular thickness. This effect is strongly dependent on the \({\bf{1}}/{\bf{4}}\) wavelength equation69

$${{\boldsymbol{d}}}_{{\boldsymbol{m}}}={\boldsymbol{nc}}/{\bf{4}}{{\boldsymbol{f}}}_{{\boldsymbol{m}}}\sqrt{|{{\boldsymbol{\mu }}}_{{\boldsymbol{r}}}||{{\boldsymbol{\varepsilon }}}_{{\boldsymbol{r}}}|}\quad \quad ({\boldsymbol{n}}={\bf{1}},{\bf{3}},{\bf{5}}\cdots )$$

Here, d m and f m are the matching thickness and peak frequency, \(|{{\boldsymbol{\mu }}}_{{\boldsymbol{r}}}|\) and \(|{{\boldsymbol{\varepsilon }}}_{{\boldsymbol{r}}}|\) are the modulus of the measured \({\mu }_{r}\) and ε r at f m , respectively. According to equation (5), the d m can be simulated, which is denoted as \({d}_{m}^{sim}\), and the results are shownin Fig. 9. It is clearly found that the obtained \({d}_{m}^{sim}\) are in good agreement with the values of \({d}_{m}^{\exp }\) (directly achieved from the RL curves in Fig. 6b–d). Therefore, the excellent microwave absorption properties of Fe based-RGO nanohybrids can be explained by the quarter-wavelength matching model.

Figure 9

Comparison of the simulated matching thickness (\({d}_{m}^{sim}\)) under n = 3 to the \({d}_{m}^{\exp }\) obtained from RL values shown in Fig. 6b–d.

Based on the aforementioned results and previous models37, 55, the enhanced microwave absorption properties of α-FeOOH NRs-RGO and porous α-Fe2O3 NRs-RGO hybrids should be related to dielectric loss, conduction loss and multiple reflections in the porous structure of α-Fe2O3. As schematically shown in Fig. 10, according to the antenna mechanism and obtained results70, the rod structure of α-FeOOH and α-Fe2O3 can be seen as an antenna. When EM wave is projected on this structure, EM wave energy will transfer in form of microcurrent. When the generated current transmits along one rod structure to another, the RGO serves as an electrically conductive network, which can effectively attenuate the EM wave energy. Moreover, as shown in Fig. 5, there are residual oxygen functional groups and defects in the RGO which can act as polarized/scattering centers and enhance the absorption of EM energy. As shown in Figs 3, S1 and S4, the larger BET surface area of porous α-Fe2O3 NRs-RGO, the interface between RGO and α-Fe2O3 NRs causes the formation of mangy diploes, interfacial polarization and the associated relaxation, improving the possibility of EM to be absorbed. According to the previous result55, the porous α-Fe2O3 NRs offer an additional opportunity for multiple reflections of the incident wave, which can effectively enhance the ability of EM absorption and attenuation.

Figure 10

Schematic diagram for possible enhanced microwave absorption mechanism of porous α-Fe2O3 NRs-RGO hybrid.

In summary, by controlling the categories of the initial reactant, different kinds and morphologies of Fe based-RGO nanohybrids (such as α-Fe2O3 NPs-RGO, α-FeOOH NRs-RGO and porous α-Fe2O3 NRs-RGO) can be selectively synthesized by hydrothermal method without using any surfactant and toxic reduced agent. The investigations indicate that the as-prepared Fe based-RGO nanohybrids exhibit excellent microwave absorption properties due to the quarter-wavelength matching model. Moreover, the obtained porous α-Fe2O3 NRs-RGO nanohybrids exhibit an enhanced microwave absorption performance because of their special structure and synergetic effect, which makes the as-prepared hybrids exhibit good dielectric loss ability, high attenuation constant and excellent impedance matching ratio. The obtained results indicate that the geometrical morphology actually has an important influence on their microwave absorption properties, which may be extended to fabricate other types and morphologies of nanohybrids for high performance MAMs.


Synthesis of products

All the used chemical regents were analytically pure and used without further purification. Firstly, GO was prepared according to the modified Hummers method71, 72. After that, 0.05 g of the obtained GO was dispersed into 100 mL deionized water and ultrasonicated for 1 h at room temperature (RT) to obtain suspension liquid. 1.39 g of FeSO4·7H2O was dissolved in 100 mL deionized water to form a transparent solution. Then 0.084 g NaHCO3 was added into the aforementioned GO and FeSO4 mixed solution, and the as-synthesized solution was transferred into a 250 mL Teflon-lined stainless steel autoclave and heated at 140 °C for 6 h. After being cooling to RT, the product was separated by centrifugation, washed with distilled water and absolute ethanol, and dried at 60 °C. For easy description, the as-synthesized product was denoted as C1. For comparison, with the other experimental conditions unchanged, the aforementioned solutions of GO and FeSO4 (without the introduction of NaHCO3) were mixed and sealed into a Teflon-lined stainless steel autoclave for hydrothermal reaction at 140 °C for 6 h. After washed with distilled water, absolute ethanol and dried at 60 °C, the sample (C2) could be collected. Finally, the product (C3) was synthesized through heating C2 sample at 300 °C in N2 for 2 h.


The samples were examined on an X-ray powder diffractometer (XRD) at RT for phase identification using CuKα radiation (model D/Max-RA, Rigaku). Raman spectroscopic investigation was performed using a Jobin-Yvon Labram HR800 instrument with 514.5 nm Ar+ laser excitation. The morphology investigation was examined using a transmission electron microscope (TEM) (model Tecnai-G20, operated at an accelerating voltage of 20 kV). Fourier transform infrared (FT-IR) spectroscopy of samples (in KBr pellets) was recorded using a Nicolet 510 P spectrometer. For microwave measurement, 30 wt% of the as-prepared sample was mixed with paraffin and pressed into coaxial clapper in a dimension of outer diameter of 7.0 mm, inner diameter of 3.0 mm, respectively. The complex permittivity \(({{\boldsymbol{\varepsilon }}}_{{\boldsymbol{r}}}={{\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime} }}}_{{\boldsymbol{r}}}-{\boldsymbol{j}}{{\boldsymbol{\varepsilon }}{\boldsymbol{^{\prime\prime} }}}_{{\boldsymbol{r}}})\) and complex permeability \(({{\boldsymbol{\mu }}}_{{\boldsymbol{r}}}={{\boldsymbol{\mu }}{\boldsymbol{^{\prime} }}}_{{\boldsymbol{r}}}-{\boldsymbol{j}}{{\boldsymbol{\mu }}{\boldsymbol{^{\prime\prime} }}}_{{\boldsymbol{r}}})\) of the composites were measured in frequency range of 2–18 GHz over an Agilent E8363B vector network analyzer.


  1. 1.

    Girgert, R., Grundker, C., Emons, G. & Hanf, V. Electromagnetic fields alter the expression of estrogen receptor cofactors in breast cancer cells. Bioelectromagnetics 29, 169–176 (2008).

  2. 2.

    Liu, X. G. et al. Dual nonlinear dielectric resonance and strong natural resonance in Ni/ZnO nanocapsules. Appl. Phys. Lett. 94, 053119 (2009).

  3. 3.

    Wang, Y. M., Li, T. X., Zhao, L. F., Hu, Z. W. & Gu, Y. J. Research progress on nanostructured radar absorbing materials. Energy Power Eng. 3, 580–584 (2011).

  4. 4.

    Qin, F. & Peng, H. X. Ferromagnetic microwires enabled multifunctional composite materials. Prog. Mater. Sci. 58, 183–259 (2013).

  5. 5.

    Meshram, M. R., Agrawal, N. K., Sinha, B. & Misra, P. S. Characterization of M-type barium hexagonal ferrite-based wide band microwave absorber. J. Magn. Magn. Mater. 271, 207–214 (2004).

  6. 6.

    Chen, Y. J., Cao, M. S., Wang, T. H. & Wan, Q. Microwave absorption properties of the ZnO nanowire-polyester composites. Appl. Phys. Lett. 84, 3367 (2004).

  7. 7.

    Saini, P. et al. High permittivity polyaniline-barium titanate nanocomposites with excellent electromagnetic interference shielding response. Nanoscale 5, 4330–4336 (2013).

  8. 8.

    Sun, G. B., Dong, B. X., Cao, M. H., Wei, B. Q. & Hu, C. W. Hierarchical dendrite-like magnetic materials of Fe3O4, γ-Fe2O3, and Fe with high performance of microwave absorption. Chem. Mater. 23, 1587–1593 (2011).

  9. 9.

    Qi, X. S. et al. Heteronanostructured Co@carbon nanotubes-graphene ternary hybrids: synthesis, electromagnetic and excellent microwave absorption properties. Sci. Rep. 6, 37972 (2016).

  10. 10.

    Zhao, B., Shao, G., Fan, B. B., Zhao, W. Y. & Zhang, R. Investigation of The electromagnetic absorption properties of Ni@TiO2 and Ni@SiO2 composite microspheres with core-shell structure. Phys. Chem. Chem. Phys. 17, 2531–2539 (2015).

  11. 11.

    Che, R. C., Peng, L. M., Duan, X. F., Chen, Q. & Liang, X. L. Microwave absorption enhancement and complex permittivity and permeability of Fe encapsulated within carbon nanotubes. Adv. Mater. 16, 401–405 (2004).

  12. 12.

    Ren, Y. J. et al. Three-dimensional SiO2@Fe3O4 core/shell nanorod array/graphene architecture: synthesis and electromagnetic absorption properties. Nanoscale 5, 12296–12303 (2013).

  13. 13.

    Singh, V. K. et al. Microwave absorbing properties of a thermally reduced graphene oxide/nitrile butadiene rubber composite. Carbon 50, 2202–2208 (2012).

  14. 14.

    Saini, P., Choudhary, V., Vijayan, N. & Kotnala, R. K. Improved electromagnetic interference shielding response of poly(aniline)-coated fabrics containing dielectric and magnetic nanoparticles. J. Phys. Chem. C 116, 13403–13412 (2012).

  15. 15.

    Sun, Y. et al. Constructing two-, zero-, and one-dimensional integrated nanostructures: an effective strategy for high microwave absorption performance. ACS Appl. Mater. Interfaces 8, (31878–31886 (2016).

  16. 16.

    Liu, X. G., Geng, D. Y., Meng, H., Shang, P. J. & Zhang, Z. D. Microwave-absorption properties of ZnO-coated iron nanocapsules. Appl. Phys. Lett. 92, 173117 (2008).

  17. 17.

    Ren, Y. L. et al. Quaternary nanocomposites consisting of graphene, Fe3O4@Fe core@shell, and ZnO nanoparticles: synthesis and excellent electromagnetic absorption properties. ACS Appl. Mater. Interfaces 4, 6436–6442 (2012).

  18. 18.

    Wang, G. Z. et al. Microwave absorption properties of carbon nanocoils coated with highly controlled magnetic materials by atomic layer deposition. ACS Nano 6, 11009–11017 (2012).

  19. 19.

    Lv, H. L. et al. CoxFey@C composites with tunable atomic ratios for excellent electromagnetic absorption properties. J. Mater. Chem. A 5, 18249 (2015).

  20. 20.

    Novoselov, K. S. et al. Room-temperature electric field effect and carrier-type inversion in graphene films. Science 306, 666–669 (2004).

  21. 21.

    Dikin, D. A. et al. Preparation and characterization of graphene oxide paper. Nature 448, 457–460 (2007).

  22. 22.

    Kuila, T. et al. Chemical functionalization of graphene and its applications. Prog. Mater. Sci. 57, 1061–1105 (2012).

  23. 23.

    Balci, O., Polat, E. O., Kakenov, N. & Kocabas, C. Graphene-enabled electrically switchable radar-absorbing surfaces. Nat. Commun. 27, 2049 (2015).

  24. 24.

    Giovannetti, G. et al. Doping graphene with metal contacts. Phys. Rev. Lett. 101, 026803 (2008).

  25. 25.

    Khomyakov, P. A. et al. First-principles study of the interaction and charge transfer between graphene and metals. Phys. Rev. B. 79, 195425 (2009).

  26. 26.

    Liu, P. B., Huang, Y., Yan, J., Yang, Y. W. & Zhao, Y. Construction of CuS nanoflakes vertically aligned on magnetically decorated graphene and their enhanced microwave absorption properties. ACS Appl. Mater. Interfaces 8, 5536–5546 (2016).

  27. 27.

    Jani, R. K. & Kumar, S. R. N. Microwave absorbing properties of a thermally reduced graphene oxide/nitrile butadiene rubber composite original. Carbon 50, 2202–2208 (2012).

  28. 28.

    Qu, B., Zhu, C. L., Li, C. Y., Zhang, X. T. & Chen, Y. J. Coupling hollow Fe3O4-Fe nanoparticles with graphene sheets for high-performance electromagnetic wave absorbing material. ACS Appl. Mater. Interfaces 8, 3730–3735 (2016).

  29. 29.

    Wang, L. et al. Synthesis and microwave absorption enhancement of graphene@Fe3O4@SiO2@NiO nanosheet hierarchical structures. Small 6, 3157–3164 (2014).

  30. 30.

    Liu, J. W. et al. Microwave absorption enhancement of multifunctional composite microspheres with spinel Fe3O4 cores and anatase TiO2 Shells. Small 8, 1214–1221 (2012).

  31. 31.

    Chen, T. T. et al. Hexagonal and cubic Ni nanocrystals grown on graphene: phase-controlled synthesis, characterization and their enhanced microwave absorption properties. J. Mater. Chem. 22, 15190–15197 (2012).

  32. 32.

    Li, D. Y. et al. Goethite (alpha-FeOOH) nanopowders synthesized via a surfactant-assisted hydrothermal method: morphology, magnetic properties and conversion to rice-like alpha-Fe2O3 after annealing. RSC Adv. 5, 27091–27096 (2015).

  33. 33.

    Wang, J. et al. Controlled synthesis of α-FeOOH nanorods and their transformation to mesoporous α-Fe2O3, Fe2O3@C nanorods as anodes for lithium ion batteries. RSC Adv. 3, 15316–15326 (2013).

  34. 34.

    Hu, H., Zhao, Z., Zhou, B. Q., Gogotsi, Y. & Qiu, J. S. The role of microwave absorption on formation of graphene from graphite oxide. Carbon 50, 3267–3273 (2012).

  35. 35.

    Choucair, M., Thordarson, P. & Stride, J. A. Gram-scale production of graphene based on solvothermal synthesis and sonication. Nat. Nanotechnol. 4, 30–33 (2009).

  36. 36.

    Zhan, L. L. et al. Facile synthesis of iron oxides/reduced graphene oxide composites: application for electromagnetic wave absorption at high temperature. Sci. Rep. 5, 9298 (2015).

  37. 37.

    Lv, H. L., Ji, G. B., Liang, X. H., Zhang, H. Q. & Du, Y. W. A novel rod-like MnO2@Fe loading on graphene giving excellent electromagnetic absorption properties. J. Mater. Chem. C 3, 5056–5064 (2015).

  38. 38.

    Wang, Y., Guan, H. T., Du, S. F. & Wang, Y. D. A facile hydrothermal synthesis of MnO2 nanorods-reduced graphene oxide nanocomposites prossessing excellent microwave absorption properties. RSC Adv. 5, 88979–88988 (2015).

  39. 39.

    Ding, X., Huang, Y. & Zong, M. Synthesis and microwave absorption enhancement property of core-shell FeNi3@SiO2-decorated reduced graphene oxide nanosheets. Mater. Lett. 157, 285–289 (2015).

  40. 40.

    Wang, L. et al. Synthesis and microwave absorption enhancement property of graphene@Fe3O4@SiO2@NiO nanosheet hierarchical structures. Nanoscale 6, 3157–3164 (2014).

  41. 41.

    Stankovich, S. et al. Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide. Carbon 45, 1558–1565 (2007).

  42. 42.

    Xu, H. L., Bi, H. & Yang, R. B. Enhanced microwave absorption property of bowl-like Fe3O4 hollow spheres/reduced graphene oxide composites. J. Appl. Phys. 111, 07A522 (2012).

  43. 43.

    Luo, D. C., Zhang, G. X., Liu, J. F. & Sun, X. M. Evaluation criteria for reduced graphene oxide. J. Phys. Chem. C 115, 11327–11335 (2011).

  44. 44.

    Xiao, L. et al. Self-assembled Fe2O3/graphene aerogel with high lithium storage performance. ACS Appl. Mater. Interfaces 5, (3764–3769 (2013).

  45. 45.

    Stadler, J., Schmid, T. & Zenobi, R. Nanoscale chemical imaging of single-layer graphene. ACS Nano 5, 8442–8448 (2011).

  46. 46.

    Ferrari, A. C. et al. Raman spectrum of graphene and graphene layers. Phys. Rev. Lett. 97, 187401 (2006).

  47. 47.

    Venezuela, P., Lazzeri, M. & Mauri, F. Theory of double-resonant Raman spectra in graphene Intensity and line shape of defect-induced and two-phonon bands. Phys. Rev. B 84, 035433 (2011).

  48. 48.

    Michielssen, E., Sager, J. M., Ranjithan, S. & Mittra, R. Design of lightweight, broad-band microwave absorbers using genetic algorithms. Microwave Theory Tech. 41, 1024–1031 (1993).

  49. 49.

    Yusoff, A. N., Abdullah, M. H., Ahmad, S. H. & Jusoh, S. F. Electromagnetic and absorption properties of some microwave absorbers. J. Appl. Phys. 92, 876–882 (2002).

  50. 50.

    Chen, Y. et al. γ-Fe2O3-MWNT/poly(p-phenylenebenzobisoxazole) composites with excellent microwave absorption performance and thermal stability. Nanoscale 6, 6440–6447 (2014).

  51. 51.

    Lv, H. L. et al. Coin-like α-Fe2O3@CoFe2O4 core–shell composites with excellent electromagnetic absorption performance. ACS Appl. Mater. Interfaces 7, 4744–4750 (2015).

  52. 52.

    Wang, T. S. et al. Graphene-Fe3O4 nanohybrids: synthesis and excellent electromagnetic absorption properties. J. Appl. Phys. 113, 024314 (2013).

  53. 53.

    Ren, Y. L., Zhu, C. L., Qi, L. H., Gao, H. & Chen, Y. J. Growth of γ-Fe2O3 nanosheet arrays on graphene for electromagnetic absorption applications. RSC Adv. 4, 21510–21516 (2014).

  54. 54.

    Zhang, H. et al. Novel rGO/α-Fe2O3 composite hydrogel: synthesis, characterization and high performance of electromagnetic absorption. J. Mater. Chem. A 1, 8547–8552 (2013).

  55. 55.

    Wang, T. H. et al. Synthesis of graphene/α-Fe2O3 composites with excellent electromagnetic wave absorption properties. RSC Adv. 5, 60114–60120 (2015).

  56. 56.

    Zhang, H. et al. Novel rGO/a-Fe2O3composite hydrogel: synthesis,characterization and high performance of electromagnetic wave absorption. J. Mater. Chem. A 1, 8547–8552 (2013).

  57. 57.

    Wu, F., Xie, A. M., Sun, M. X., Wang, Y. & Wang, M. Y. Reduced graphene oxide (RGO) modified spongelike polypyrrole (PPy) aerogel for excellent electromagnetic absorption. J. Mater. Chem. A 3, 14358–14369 (2015).

  58. 58.

    Wang, Y. F. et al. Hybrid of MoS2 and reduced graphene oxide: a lightweight and broadband electromagnetic wave absorber. ACS Appl. Mater. Interfaces 7, 26226–26234 (2015).

  59. 59.

    Kong, L. et al. Electromagnetic wave absorption properties of reduced graphene oxide modified by maghemite colloidal nanoparticle clusters. J. Phys. Chem. C 117, 19701–19711 (2013).

  60. 60.

    Liu, X. G. et al. Dual nonlinear dielectric resonance and strong natural resonance in Ni/ZnO ranocapsules. Appl. Phys. Lett. 94, 053119 (2009).

  61. 61.

    Zhao, X. C. et al. Excellent microwave absorption property of graphene-coated Fe nanocomposites. Sci. Rep. 3, 3421 (2013).

  62. 62.

    Yang, Z. H., Li, Z. W., Yang, Y. H. & Xu, Z. C. J. Optimization of ZnxFe3-xO4 hollow spheres for enhanced microwave attenuation. ACS Appl. Mater. Interfaces 6, 21911–21915 (2014).

  63. 63.

    Liu, X. G. et al. (Fe, Ni)/C nanocapsules for electromagnetic-wave-absorber in the whole Ku-band. Carbon 47, 470–474 (2009).

  64. 64.

    Deng, L. J. & Han, M. G. Microwave absorbing performances of multiwalled carbon nanotube composites with negative permeability. Appl. Phys. Lett. 91, 023119 (2007).

  65. 65.

    Wang, C. et al. The electromagnetic property of chemically reduced graphene oxide and its application as microwave absorbing material. Appl. Phys. Lett. 100, 046102 (2012).

  66. 66.

    Zhang, X. F., Guan, P. F. & Dong, X. L. Transform between the permeability and permittivity in the close-packed Ni nanoparticles. Appl. Phys. Lett. 97, 033107 (2010).

  67. 67.

    Sun, Y. P. et al. A facile route to carbon-coated vanadium carbide nanocapsules as microwave absorbers. RSC Adv. 3, 18082–18086 (2013).

  68. 68.

    Wen, F. S., Zhang, F. & Liu, Z. Y. Investigation on microwave absorption properties for multiwalled carbon nanotubes/Fe/Co/Ni nanopowders as lightweight absorbers. J. Phys. Chem. C 115, 14025–14030 (2011).

  69. 69.

    Zhang, H. M., Zhu, C. L., Chen, Y. J. & Gao, H. Growth of Fe3O4 nanorod arrays on graphene sheets for application in electromagnetic absorption fields. ChemPhysChem 15, 2261–2266 (2014).

  70. 70.

    Zhuo, R. F. et al. Microwave absorption properties and the isotropic antenna mechanism of ZnO nanotrees. J. Appl. Phys. 104, 094101 (2008).

  71. 71.

    Hummers, W. S. & Offeman, R. E. Preparation of graphitic oxide. J. Am. Chem. Soc. 80, 1339 (1958).

  72. 72.

    Xu, Y. X., Sheng, K. X., Li, C. & Shi, G. Q. Self-assembled graphene hydrogel via a one-step hydrothermal process. ACS Nano 4, 4324–4330 (2010).

Download references


This work was supported by the Graduate Innovation Fund of Guizhou University (2016-015), the Innovation and Entrepreneurship Training Program for University Student (2016-004), the Excellent Talents of Guizhou Province (2014-239), the National Science Foundation of Guizhou province (2014-2059), the Postdoctoral Science Foundation of China (2015M570427), the Science and Technology Innovation Team of Guizhou province (2015-4017), the National Science Foundation of China (Grant Nos 11364005, 11474151 and 11604060), and the Foundation of the National Key Project for Basic Research (2012CB932304) for financial support.

Author information

L. Long, R. Xie, Z.C. Bai and Y. Jiang collected the experimental data. Results were analyzed and interpreted by X.S. Qi, S.J. Qin, W. Zhong and Y.W. Du. The manuscript was written by X.S. Qi and W. Zhong.

Correspondence to Xiaosi Qi or Wei Zhong.

Ethics declarations

Competing Interests

The authors declare that they have no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Hu, Q., Qi, X., Cai, H. et al. Preparation of porous Fe2O3 nanorods-reduced graphene oxide nanohybrids and their excellent microwave absorption properties. Sci Rep 7, 11213 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.