Abstract
Recent developments in terahertz technologies provide new tools for analysis, inspection, and nondestructive sensing. If a heavy atom is encapsulated in a cage of a porous material, the atom should vibrate slowly and resonate with a low-frequency terahertz light. From this perspective, a cyanide-bridged metal framework is a suitable system because it contains many cages that can adsorb Cs ions. Herein we show the vibration mode of a Cs ion in a cage of a cyanide-bridged metal framework. First-principles phonon mode calculations and terahertz time-domain spectroscopy (THz-TDS) measurements indicate that the vibration mode of a Cs ion in a cyanide-bridged manganese-iron framework is at 1.5 THz, which is significantly apart from other lattice vibrations. Taking advantage of this feature, we develop a THz-light detection method for Cs ions, which is useful for non-contact sensing of Cs ions in dangerous environments or harmful circumstances.
Introduction
Terahertz technologies are realizing innovative applications such as tests for illicit drugs in mail, quality management of medicine, semiconductor carrier density measurements, quality measurements of coating films, art conservation, and gas sensing at fire sites1,2,3,4,5,6. Terahertz technologies also provide fundamental information about the motions of free electrons, the rotation modes of molecules, the vibration modes of crystals, and precession of spins7,8,9,10,11,12,13,14,15,16,17. Recently, high-power terahertz sources and high-precision detectors have been developed to improve terahertz technologies. Additionally, high-resolution imaging using near-field imaging or terahertz tomography have been intensively studied1,2,3,4,5, 18,19,20. For example, field-enhancing arrays have been proposed for high-resolution imaging, enabling ultrasmall quantities of samples as small as tens of nanograms to be detected21, 22. Terahertz spectroscopy is a powerful tool. It can be used to measure various types of samples. For example, powder-form samples such as ceramics, proteins, and deoxyribonucleic acid have been measured using terahertz time-domain spectroscopy (THz-TDS)23,24,25,26.
If a heavy atom is encapsulated in a cage of a porous material, the atom is expected to vibrate slowly and to resonate with a low-frequency terahertz light. To confirm this idea, metal frameworks such as metal-organic framework and cyanide-bridged metal framework are suitable systems because these are porous materials. Applications of these metal frameworks for organic molecule adsorbent, hydrogen adsorbent, and drug capsules are actively studied27,28,29,30. A cyanide-bridged metal framework has many cages in its three-dimensional network31,32,33,34,35,36,37,38,39, and the cage size matches the ionic radius of the Cs ion40,41,42,43. For example, a cyanide-bridged metal framework has been used as medicine and adsorbent for radioactive Cs ions. If a non-contact sensing technique can monitor the capture of a Cs ion by the metal framework, it would be very useful for the recovery operation of radioactive Cs ions in dangerous environments. From this viewpoint, we focus on THz technology because a heavy Cs atom should vibrate slowly in a cage and resonate with low-frequency THz-light (Fig. 1a and Movie S1). In the present work, we study the vibration mode (phonon mode) of a Cs ion in a cage of a cyanide-bridged metal framework using THz-spectroscopy. Additionally, we propose a THz-light detection method for Cs ions, which monitors how a Cs ion is captured by a cyanide-bridged metal framework. As a proof of concept, a cyanide-bridged manganese-iron framework is prepared.
Concept of detecting the slow vibration of a heavy atom in a cage using THz-light. (a) Schematic illustration of a heavy atom encapsulated in a cage, which is expected to vibrate slowly and to resonate with low-frequency THz-light. This concept could be applied for non-contact sensing of heavy atoms. Input THz pulse (left) and transmitted THz pulse (right) are indicated with red lines. (b) Schematic crystal structure of the cesium-encapsulated cyanide-bridged manganese-iron framework. Red, blue green, green, dark gray, and light blue balls indicate Cs, Mn, Fe, C, and N atoms, respectively.
Results
Cs cyanide-bridged metal framework
The sample was synthesized by reacting an aqueous solution of cesium chloride and manganese chloride with an aqueous solution of potassium ferricyanide. The chemical formula of the sample is Cs0.90Mn[Fe(CN)6]0.93·1.9H2O (CsMnFe), which has a cubic crystal structure (space group F \(\overline{4}\)3 m) with a lattice constant of a = 10.57986(13) Å (Fig. 1b, Fig. S1, and Table S1). The electronic structure of CsMnFe was investigated by periodic structure calculations using the Vienna ab initio Simulation Package program (Methods section, Fig. S2).
Phonon mode calculations of the Cs vibration mode
First-principles phonon mode calculations were performed using the Phonon code program (Methods section). Figure 2a and Figure S3 show the phonon density of states with an energy width of 1.0 meV (0.25 THz) and phonon dispersions, respectively. Figure 2b shows the calculated absorption spectra due to the transition probabilities of the IR active optical phonon modes considering absorption line width. In the low-frequency THz region, an absorption peak should be observed at 1.3 THz. The atomic movement of this phonon mode indicates that this absorption originates from the vibration modes of the Cs ion encapsulated in the cage of the cyanide-bridged metal framework (Fig. 2b and Supplementary Movie S2). In the frequency region of 3–18 THz, the vibration modes due to the Mn–N≡C–Fe transverse translational mode and transverse librational mode appear at 5.5 THz and 12.4 THz, respectively (Movies S3 and S4). Additionally, the C≡N stretching modes are at a distant high frequency around 65.5 THz (Movie S5).
Phonon mode calculations of the vibration mode of Cs in a cyanide-bridged metal framework. (a) Phonon density of states of a Cs cyanide-bridged manganese-iron framework from first-principles phonon mode calculations (left). Enlarged view of the low frequency range of 0–7 THz (right). Black, red, green, light green, light blue, and blue lines indicate the total phonon density of states and the partial phonon density of states of Cs, Mn, Fe, C, and N, respectively. (b) Calculated optical transition probabilities of the phonon modes in the regions of 0–3 THz, 3–18 THz, and 63–69 THz. Black bars and red lines denote the transition probabilities and the calculated spectra considering the line width, respectively. Lower figure shows the atomic movements of the phonon modes at 1.3 THz, 5.5 THz, 12.4 THz, and 65.5 THz. Red and blue arrows indicate the movements of Cs and C≡N, respectively.
THz spectrum of Cs cyanide-bridged metal framework
Based on the theoretical calculations of the vibration modes of Cs, THz-TDS measurements of CsMnFe in the frequency region of 0–3 THz were performed. The temporal spectrum of the THz pulse wave was measured in the transmittance mode as shown in Fig. 3a (Methods section, Movie S6). A Fourier transformation of the temporal waveform yielded the frequency-dependent spectrum. The spectrum shows an absorption peak at 1.4 THz with a line-width of 0.3 THz (Fig. 3b). This absorption peak agrees well with the calculated Cs vibration mode, demonstrating that THz-TDS is useful to detect the Cs vibration mode in a cage. As for higher frequency vibration modes in the region of 3–19 THz, far-infrared measurements were performed; the observed spectrum is also consistent with the phonon mode calculations (Fig. 3c).
THz-TDS spectrum of CsMnFe. (a) Temporal waveforms of the input THz pulse (left) and transmitted THz pulse (right) for the THz-TDS measurement of the Cs vibration mode in the cyanide-bridged manganese-iron framework. (b) THz-TDS absorption spectrum of CsMnFe. (c) Absorption spectrum of CsMnFe measured by far-IR spectroscopy. Absorption peaks are assigned to the Mn–N≡C–Fe transverse translational or transverse librational modes.
The high Cs adsorption capacity monitored by THz light
Taking advantage of such a feature, we investigated whether THz-TDS can monitor the cyanide-bridged metal framework capturing a Cs ion from a cesium ion containing aqueous solution (Fig. 4a and Movie S7). In this trial, a cyanide-bridged manganese-iron framework without cesium ions K0.22Mn[Fe(CN)6]0.74·4.3H2O (MnFe) was used as an adsorbent. The powder-form MnFe sample (0.25 g) was immersed in cesium chloride aqueous solutions (50 mL) with various concentrations (C 0 = 0.665, 6.65, 13.3, 26.6, 39.9, 53.2, and 79.7 g/L). After 24 hours, the solution was filtered to collect the adsorbent sample.
Highly efficient Cs adsorption of MnFe measured by THz light. (a) Schematic illustration of the cyanide-bridged metal framework adsorbing the Cs ions from the solution. MnFe (green framework) is immersed in a Cs ion solution as an adsorbent (upper left), and Cs ions (orange balls) are captured into the interstitial sites of the metal framework (lower right). (b) THz spectra of the samples recollected from Cs solutions of various concentrations. The peak intensity at 1.5 THz increases (orange → light green → green → light blue → blue → navy → purple → red) with the increase of Cs concentration (C 0 = 0 → 79.7 g/L). (c) THz spectrum component due to the Cs vibration mode at 1.5 THz. (d) Cs composition (x) of the sample versus peak area for the samples recollected from various Cs solutions. Black line indicates the regression line. (e) q eq of the samples recollected from the Cs solution versus the concentration of the remaining Cs solution at the equilibrium condition, C eq, derived from the x values. Red line shows the fitted curve following the Langmuir isotherm. The fitted curve shows a large q max value of 511 mg/g. (f) Compositions of Cs+ (red), Fe2+ (light green), Fe3+ (green), and K+ (gray) for the samples after immersing in Cs solutions of various concentrations, C 0 = 0 g/L (sample number 0), 0.665 g/L (1), 6.65 g/L (2), 13.3 g/L (3), 26.6 g/L (4), 39.9 g/L (5), 53.2 g/L (6), and 79.7 g/L (7). (g) The structures schematically showing the reduction of Fe ions from Fe3+ to Fe2+ by adsorption of Cs+. This is the origin of the highly efficient Cs adsorption performance of MnFe.
The THz spectra of these precipitates were measured by THz-TDS using a polyethylene cell (Fig. S4). As a reference, the spectrum of the empty polyethylene cell was recorded. Figure 4b shows the obtained spectra. An absorption peak appears at 1.5 THz, which is due to the Cs vibration mode in the cage. Additionally, the weak broad peak at 2.2 THz is assigned to the water molecules inside the metal framework. The observed spectra were separated into these two components (Fig. S5). Figure 4c shows the absorption due to Cs ions at various Cs concentrations. Because each sample has a slightly different molar amount, the peak area of the Cs absorption was calibrated using the molar amount in the sample (See Methods). Figure 4d shows the Cs composition (x) of the chemical formula of the samples, Cs x Mn[Fe(CN)6]0.74·zH2O, plotted against the peak area of the Cs absorption. (The Methods section details the process to determine the chemical formulas and the peak area of Cs absorption.) The linear regression line corresponds to the conversion equation from the peak area of Cs absorption to the x values (Fig. 4d and Methods section). Using this conversion equation, the peak area of the Cs absorption for each sample can be converted to the x value. From the x values, the Cs adsorption capacity q eq (mg/g) of the Mn–N≡C–Fe metal framework and the C eq values can be obtained (Methods section). Figure 4e shows the q eq versus C eq plot. This plot is well fitted by the Langmuir equation, indicating that the saturated capability, q max, is 511 ± 55 mg/g. This q max value is remarkably high compared to that of Prussian blue Fe[Fe(CN)6]0.75·zH2O adsorbent44,45,46,47,48. Figure 4f shows the metal ion compositions. The ratios of the metals (Cs, K, Mn, and Fe) were obtained by inductively coupled plasma mass spectroscopy. The amounts of C, H, and N contained in the samples were determined by standard microanalytical methods. The chemical formula, KI a CsI b MnII[FeII(CN)6] c [FeIII(CN)6] d ·zH2O, was determined considering charge neutrality (Methods section). Cs adsorption decreases Fe3+ and increases Fe2+. This is reasonable because the reduced valence state of the Fe ions in the metal framework is preferred in order to accept Cs+ ions. The reduction of Fe3+ to Fe2+ is the origin of the highly efficient Cs adsorption performance of the present system without collapsing of the framework (Fig. 4f,g) (Movie S8). In addition, the metal framework of MnFe has a high durability in an aqueous solution. Almost all of the adsorbent (average = 99%) can be recollected from the Cs ion solution.
Recently, metal frameworks have been studied by terahertz spectroscopy, and the vibration modes contributing to the lattice vibration of the framework have been reported49. In the present work, we clarified that a heavy atom such as a Cs ion vibrates slowly in the cage of a metal framework, and the Cs ion vibration mode lies at a low THz frequency. Although THz generation due to Cs ions has been known50, there has not been any observations of Cs ion by THz spectroscopy. Based on this feature, we demonstrate that the cyanide-bridged metal framework can be a marker to monitor the amount of Cs by combining it with THz-TDS measurements as well as an adsorbent to efficiently encapsulate Cs ions from cesium ion solutions. It should be noted that the absorption peaks of other alkali cations are observed at different frequencies because the vibration mode frequency depends on the type of alkali cation. Diffusion of radioactive Cs to the environment has been a serious issue, and its decontamination is an important mission after the accidents at nuclear power plants, e.g., the 2011 Fukushima accident51, 52. From this viewpoint, the combined system of THz-TDS with a cyanide-bridged metal framework demonstrated in this work will provide an effective detection method for non-contact sensing of Cs ions.
Methods
Electronic structure calculations
The electronic structure was calculated by first-principles calculations using the Vienna ab initio simulation package (VASP) program. The wave functions based on the plane waves and the potentials of the core orbitals were represented by the projector-augmented wave of Blöchl. The exchange-correlation term was evaluated by the generalized gradient approximation of Perdew, Burke, and Ernzerhof. The U–J value was set to 4.0 eV. The calculated density of states and band structure are shown in Fig. S2.
Phonon mode calculations
The phonon mode was calculated based on the crystal structure of the cesium cyanide-bridged manganese-iron framework. The lattice parameters and atomic positions were calculated with an energy cut-off of 500 eV and 3 × 3 × 3 k mesh until satisfying a 10−5 eV pm−1 force tolerance. \(\sqrt{2}\times \sqrt{2}\times 1\) supercell of the optimized structure containing four Cs ions alternatively in the interstitial sites was used for the phonon mode calculations by the direct method implemented in Phonon code with displacements of 2 pm.
THz-TDS measurements
THz spectra were measured by a THz-TDS system of Advantest tas7500su, equipped with a Cherenkov type THz generator and emitter using a LiNbO3 waveguide and a 1550-nm fiber laser (50 fs, 150 mW) (Fig. S4). The THz pulse was condensed with a Si lens and paraboloidal mirrors and was irradiated into the sample, which was placed in a polyethylene cell. The electric fields of the transmitted THz pulse wave formed in the time domain were obtained, and the power spectrum was obtained by Fourier transformation. Absorbance was obtained from the power spectra of the reference and the sample.
Cs adsorption experiment
In the adsorption experiment, the cyanide-bridged manganese-iron framework without cesium ions MnFe was used as an adsorbent. The sample was prepared by reacting an aqueous solution of manganese chloride (0.1 mol L−1) with an aqueous solution of potassium ferricyanide (0.1 mol L−1), and its formula was K0.22Mn[Fe(CN)6]0.74·4.3H2O. The powder-form MnFe sample was immersed in a cesium chloride aqueous solution at various concentrations and then filtered. Their formulas were investigated by elemental analyses. The formulas of the collected samples after immersing were as follows: Cs0.12K0.19Mn[Fe(CN)6]0.74·zH2O, Cs0.33Mn[Fe(CN)6]0.74·zH2O, Cs0.48Mn[Fe(CN)6]0.74·zH2O, Cs0.73Mn[Fe(CN)6]0.74·zH2O, Cs0.81Mn[Fe(CN)6]0.74·zH2O, Cs0.88Mn[Fe(CN)6]0.74·zH2O, and Cs0.91Mn[Fe(CN)6]0.74·zH2O. The Supplementary information contains the results of elemental analyses. In the THz-TDS measurement, the peak intensity at 1.5 THz increases with the increase of composition of Cs ions in the formula, and the broad peak at 2.2 THz simultaneously disappears. The THz spectra were separated into the vibration modes at 1.5 and 2.2 THz. Because the molar amounts of the samples slightly differ (Fig. S4, caption), the absorption intensity (peak area) was calibrated with the mole number of the sample. The mole number of the THz-TDS–measured sample which had been collected from the cesium chloride aqueous solution of C 0 = 6.65 g/L (40.6 µmol) was used as a reference. The Cs composition (x) was plotted against the normalised peak area of the Cs absorption. The composition (x) is well fitted by a first-order regression function with a slope of 0.501. Hence, this relation was used as the conversion equation to transfer the peak area of the Cs absorption of the THz spectrum to the Cs composition for a collected sample.
Material characterization and physical property measurements
The chemical formulas of the samples were determined by elemental analyses. The ratios of the metals (Cs, K, Mn, and Fe) were obtained by inductively coupled plasma mass spectroscopy using Agilent 7700. The amounts of C, H, and N contained in the samples were determined by standard microanalytical methods. The chemical formula, KI a CsI b MnII[FeII(CN)6] c [FeIII(CN)6] d ·zH2O, was determined considering charge neutrality. Because the valences of KI, CsI, MnII, [FeII(CN)6], and [FeIII(CN)6] are +1, +1, +2, −4, and −3, respectively, a + b + 2 − 4c − 3d = 0 should be satisfied. For the far-infrared measurements, a JASCO 6100 spectrometer was used. XRD measurements were performed with a Rigaku Ultima IV diffractometer with a Cu K α radiation (λ = 1.5418 Å). The PDXL program of Rigaku was used for Rietveld analyses.
Adsorption analysis using Langmuir model
Using the x values obtained from the THz spectra by the conversion equation, the q eq and C eq values are calculated by \({q}_{{\rm{eq}}}=({M}_{{\rm{Cs}}}/{M}_{{\rm{MnFe}}})x\) and\({C}_{eq}={C}_{{\rm{0}}}-\) \((m{M}_{{\rm{Cs}}}/V{M}_{{\rm{MnFe}}})x\), where M Cs and M MnFe are the atomic weight of Cs and the formula weight of the adsorbent, respectively, m is the sample weight of the immersed adsorbent, and V is the volume of the Cs ion solution. The q eq versus C eq plot was fitted by the Langmuir model expressed by \({q}_{{\rm{eq}}}={q}_{{\rm{\max }}}a{C}_{{\rm{eq}}}/(1+a{C}_{{\rm{eq}}})\), where a is a constant. The THz-TDS measurement system has a dynamic range of 60 dB, and the measurement is possible up to Cs saturated solution under the present condition. The lower limit of the detection sensitivity is several ppm.
References
Tonouchi, M. Cutting-edge terahertz technology. Nature Photon. 1, 97–105 (2007).
Ferguson, B. & Zhang, X.-C. Materials for terahertz science and technology. Nature Mater. 1, 26–33 (2002).
Nagatsuma, T., Ducournau, G. & Renaud, C. C. Advances in terahertz communications accelerated by photonics. Nature Photon. 10, 371–378 (2016).
Hosako, I. et al. At the dawn of a new era in terahertz technology. Proc. IEEE 95, 1611–1623 (2007).
Jepsen, P. U., Cooke, D. G. & Koch, M. Terahertz spectroscopy and imaging - Modern techniques and applications. Laser Photon. Rev. 5, 124–166 (2011).
Liu, J., Dai, J., Chin, S. L. & Zhang, X. C. Broadband terahertz wave remote sensing using coherent manipulation of fluorescence from asymmetrically ionized gases. Nature Photon. 4, 627–631 (2010).
Kampfrath, T., Tanaka, K. & Nelson, K. A. Resonant and nonresonant control over matter and light by intense terahertz transients. Nature Photon. 7, 680–690 (2013).
Homes, C. C., Vogt, T., Shapiro, S. M., Wakimoto, S. & Ramirez, A. P. Optical response of high-dielectric-constant perovskite-related oxide. Science 293, 673–676 (2001).
Yan, H. et al. Damping pathways of mid-infrared plasmons in graphene nanostructures. Nature Photo. 7, 394–399 (2013).
Nguyen, K. L., Friščić, T., Day, G. M., Gladden, L. F. & Jones, W. Terahertz time-domain spectroscopy and the quantitative monitoring of mechanochemical cocrystal formation. Nature Mater. 6, 206–209 (2007).
Takahashi, Y., Yamasaki, Y. & Tokura, Y. Terahertz Magnetoelectric resonance enhanced by mutual coupling of electromagnons. Phys. Rev. Lett. 111, 037204/1–5 (2013).
Caviglia, A. D. et al. Ultrafast strain engineering in complex oxide heterostructures. Phys. Rev. Lett. 108, 136801/1–5 (2012).
Bovensiepen, U. Coherent and incoherent excitations of the Gd(0001) surface on ultrafast timescales. J. Phys.: Condens. Matter 19, 083201/1–55 (2007).
Namai, A. et al. Hard magnetic ferrite with a gigantic coercivity and high frequency millimetre wave rotation. Nature Commun. 3, 1035/1–6 (2012).
Ohkoshi, S. et al. Mesoscopic bar magnet based on ε-Fe2O3 hard ferrite. Sci. Rep. 6, 27212/1–10 (2016).
Zhang, K. et al. Resolving the spin reorientation and crystal-field transitions in TmFeO3 with terahertz transient. Sci. Rep. 6, 23648/1–7 (2016).
Kurihara, T. et al. Enhanced spin-precession dynamics in a spin-metamaterial coupled resonator observed in terahertz time-domain measurements. Phys. Rev. B 90, 144408/1–5 (2014).
Wang, K. & Mittleman, D. M. Metal wires for terahertz wave guiding. Nature 432, 376–379 (2004).
Cocker, T. L. et al. An ultrafast terahertz scanning tunnelling microscope. Nature Photon. 7, 620–625 (2013).
Watts, C. M. et al. Terahertz compressive imaging with metamaterial spatial light modulators. Nature Photon. 8, 605–609 (2014).
Park, H. R. et al. Colossal absorption of molecules inside single terahertz nanoantennas. Nano Lett. 13, 1782–1786 (2013).
Lee, D. K. et al. Highly sensitive and selective sugar detection by terahertz nano-antennas. Sci. Rep. 5, 1549/1–7 (2015).
Plusquellic, D. F., Siegrist, K., Heilweil, E. J. & Esenturk, O. Applications of terahertz spectroscopy in biosystems. Chem. Phys. Chem. 8, 2412–2431 (2007).
Namai, A. et al. Synthesis of an electromagnetic wave absorber for high-speed wireless communication. J. Am. Chem. Soc. 131, 1170–1173 (2009).
Markelz, A. G., Roitberg, A. & Heilweil, E. J. Pulsed terahertz spectroscopy of DNA, bovine serum albumin and collagen between 0.1 and 2.0 THz. Chem. Phys. Lett. 320, 42–48 (2000).
Shah, B., Kakumanu, V. K. & Bansal, A. K. Analytical techniques for quantification of amorphous/crystalline phases in pharmaceutical solids. J. Pharm. Sci. 95, 1641–1665 (2006).
Furukawa, H., Cordova, K. E., O’Keeffe, M. & Yaghi, O. M. The chemistry and applications of metal-organic frameworks. Science 341, 1230444/1–12 (2013).
Zhou, H. C., Long, J. R. & Yaghi, O. M. Introduction to metal-organic frameworks. Chem Rev. 112, 673–674 (2012).
Sumida, K. et al. Carbon dioxide capture in metal-organic frameworks. Chem. Rev. 112, 724–781 (2012).
Horcajada, P. et al. Metal-organic frameworks in biomedicine. Chem. Rev. 112, 1232–1268 (2012).
Keggin, J. F. & Miles, F. D. Structures and formulæ of the Prussian Blues and Related Compounds. Nature 137, 577–578 (1936).
Pyrasch, M., Toutianoush, A., Jin, W., Schnepf, J. & Tieke, B. Self-assembled films of Prussian blue and analogues: optical and electrochemical properties and application as ion-sieving membranes. Chem. Mater. 15, 245–254 (2003).
Mallah, T., Thiebaut, S., Verdaguer, M. & Veillet, P. High-T C molecular-nased magnets: ferrimagnetic mixed-valence chromium(III)-chromium(II) cyanides with T C at 240 and 190 Kelvin. Science 262, 1554–1557 (1993).
Ohkoshi, S., Arai, K., Sato, Y. & Hashimoto, K. Humidity-induced magnetization and magnetic pole inversion in a cyano-bridged metal assembly. Nature Mater. 3, 857–861 (2004).
Margadonna, S., Prassides, K. & Fitch, A. N. Zero thermal expansion in a Prussian blue analogue. J. Am. Chem. Soc. 126, 15390–15391 (2004).
Ohkoshi, S., Imoto, K., Tsunobuchi, Y., Takano, S. & Tokoro, H. Light-induced spin-crossover magnet. Nature Chem. 3, 564–569 (2011).
Beauvais, L. G., Shores, M. P. & Long, J. R. Cyano-bridged Re6Q8 (Q=S, Se) Cluster-Cobalt(II) framework materials: versatile solid chemical sensors. J. Am. Chem. Soc. 122, 2763–2772 (2000).
Verdaguer, M. et al. Molecules to build solids: high T C molecule-based magnets by design and recent revival of cyano complexes chemistry. Coord. Chem. Rev. 190–192, 1023–1047 (1999).
Ohkoshi, S. et al. 90-degree optical switching of output second harmonic light in chiral photomagnet. Nature Photon. 8, 65–71 (2014).
Itaya, K., Uchida, I. & Neff, V. D. Electrochemistry of polynuclear transition metal cyanides: Prussian blue and its analogues. Acc. Chem. Res. 19, 162–168 (1986).
Klausmeyer, K. K., Wilson, S. R. & Rauchfuss, T. B. Alkali metal-templated assembly of cyanometalate “boxes” (NEt4)3{M[Cp*Rh(CN)3]4[Mo(CO)3]4} (M=K, Cs). Selective binding of Cs+. J. Am. Chem. Soc. 121, 2705–2711 (1999).
Nuida, T. et al. Nonlinear magnetooptical effects caused by piezoelectric ferromagnetism in F3m-type Prussian blue analogues. J. Am. Chem. Soc. 127, 11604–11605 (2005).
Boyer, J. L., Kuhlman, M. L. & Rauchfuss, T. B. Evolution of organo-cyanometallate cages: suplamolecular architectures and new Cs+-specific receptors. Acc. Chem. Res. 40, 233–242 (2007).
Sangvanich, T. et al. Selective capture of cesium and thallium from natural waters and simulated wastes with copper ferrocyanide functionalized mesoporous silica. J. Hazard. Mater. 182, 225–231 (2010).
Avramenko, V. et al. Colloid stable sorbents for cesium removal: Preparation and application of latex particles functionalized with transition metals ferrocyanides. J. Hazard. Mater. 186, 1343–1350 (2011).
Torad, N. L., Hu, M., Imura, M., Naito, M. & Yamauchi, Y. Large Cs adsorption capability of nanostructured Prussian blue particles with high accessible surface areas. J. Mater. Chem. 22, 18261–18267 (2012).
Takahashi, A. et al. Efficient synthesis of size-controlled open-framework nanoparticles fabricated with a micro-mixer: route to the improvement of Cs adsorption performance. Green Chem. 17, 4228–4233 (2015).
Vipin, A. K. et al. Cellulose nanofiber backboned Prussian blue nanoparticles as powerful adsorbents for the selective elimination of radioactive cesium. Sci. Rep. 6, 37009/1–14 (2016).
Ryder, M. R. et al. Identifying the role of terahertz vibrations in metal-organic frameworks: from gate-opening phenomenon to shear-driven structural destabilization. Phys. Rev. Lett. 113, 215502/1–6 (2014).
Sun, X. & Zhang, X. C. Terahertz radiation in alkali vapor plasmas. Appl. Phys. Lett. 104, 191106/1–4 (2014).
Smith, J. A long shadow over Fukushima. Nature 472, 7 (2011).
Sugiyama, M., Sakata, I., Shiroyama, H., Yoshikawa, H. & Taniguchi, T. Five years on from Fukushima. Nature 531, 29–31 (2016).
Acknowledgements
The present research was supported in part by a JSPS Grant-in-Aid for specially promoted Research Grant Number 15H05697, JP16H06521 Coordination Asymmetry, Young Scientists (A) and (B); and the Shitagau Noguchi Foundation. We also recognize the Cryogenic Research Center, The University of Tokyo, and Nanotechnology Platform, which are supported by MEXT. We are grateful to Dr. Y. Umeta and Dr. K. Imoto for their technical support and valuable discussions.
Author information
Authors and Affiliations
Contributions
S.O. designed and coordinated this study, contributed to all measurements and calculations, and wrote the paper. M.Y. contributed to the analysis of the first-principles calculations and Cs adsorption experiment. A.N. carried out the analysis of the THz-TDS spectra and Cs adsorption experiments. K.N. conducted the elemental analyses. K.C. carried out the first-principles phonon mode calculations. R.F. prepared the samples and performed the elemental analyses, XRD, far-infrared, and THz-TDS measurements. H.T. prepared the samples and contributed to coordinate this study and to all measurements and calculations. All authors commented on the manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ohkoshi, Si., Yoshikiyo, M., Namai, A. et al. Cesium ion detection by terahertz light. Sci Rep 7, 8088 (2017). https://doi.org/10.1038/s41598-017-08551-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-08551-4
This article is cited by
-
Characterization of the remediation of chromium ion contamination with bentonite by terahertz time-domain spectroscopy
Scientific Reports (2022)
-
Charge transfer driven by ultrafast spin transition in a CoFe Prussian blue analogue
Nature Chemistry (2021)
-
A photoswitchable polar crystal that exhibits superionic conduction
Nature Chemistry (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.