Abstract
Reported steady-state microwave emission in magnetic tunnel junction (MTJ)-based spin transfer torque nano-oscillators (STNOs) relies mostly on very thin insulating barriers [resulting in a resistance × area product (R × A) of ~1 Ωμm2] that can sustain large current densities and thus trigger large orbit magnetic dynamics. Apart from the low R × A requirement, the role of the tunnel barrier in the dynamics has so far been largely overlooked, in comparison to the magnetic configuration of STNOs. In this report, STNOs with an in-plane magnetized homogeneous free layer configuration are used to probe the role of the tunnel barrier in the dynamics. In this type of STNOs, the RF modes are in the GHz region with integrated matched output powers (P
out
) in the range of 1–40 nW. Here, P
o
u
t
values up to 200 nW are reported using thicker insulating barriers for junctions with R × A values ranging from 7.5 to 12.5 Ωμm2, without compromising the ability to trigger self-sustained oscillations and without any noticeable degradation of the signal linewidth (Γ). Furthermore, a decrease of two orders of magnitude in the critical current density for spin transfer torque induced dynamics (J
STT
) was observed, without any further change in the magnetic configuration.
Similar content being viewed by others
Introduction
The spin transfer torque (STT) effect1,2,3,4,5,6,7,8 allows the effective and selective manipulation of the magnetization of nano-magnets using local spin polarized electrical currents. It has been suggested as a key mechanism enabling a large number of spintronic devices, including magnetic random access memories (MRAM)9, domain wall based storage10 or spin transfer torque nano-oscillators (STNOs)11,12,13,14,15,16,17,18,19. With respect to STNOs, these devices take advantage of the STT effect to achieve RF emission from persistent magnetic precession, driven by DC currents. They show major advantages over conventional complementary metal-oxide-semiconductor (CMOS) and crystal based oscillators, such as being tunable by both electrical currents and magnetic fields, working in a large range of temperatures, having a broadband output and a nanometric footprint while keeping the compatibility with a CMOS backend process. STNOs are thus versatile and compact RF oscillators that can be vertically integrated with CMOS, making them highly attractive for applications such as chip-to-chip or wireless communications, microwave sources for nanosensors or phase-array transceivers11, 20.
There have been several proposals for alternative magnetic arrangements with different advantages explored in the context of specific applications. These include, homogenous in-plane oscillators21, vortex oscillators16, 22, oscillators integrating perpendicular polarizers23 or oscillators using free layers with canted magnetization24, 25 and point-contact nano-oscillators26, 27.
The STNOs with the largest reported integrated matched output power (P out ) are fabricated starting from magnetic tunnel junction (MTJ) stacks based on CoFeB/MgO/CoFeB which benefit from their high tunnel magnetoresistance ratio (TMR)11, 24, 25, 28, 29. However, the MTJ endurance is limited by the dielectric breakdown of the MgO insulating layer. This is a critical point for STNOs wherein, to observe persistent oscillations, one must apply large and continuous current densities. This is a fundamental difference with respect to other applications exploring the STT phenomena, such as MRAM, which can use short pulses of very large current (and voltage) amplitude to excite the free layer magnetization. The barrier can sustain large pulsed voltages with amplitudes well above the DC breakdown value whilst large angle magnetization dynamics can still be excited. For STNO applications, the excitation current must be maintained in the steady state and therefore large current densities, capable of exciting persistent dynamics, must be reached with DC voltages that the MgO barrier can endure.
Despite the fact that a small number of reports achieved large P out values with relatively thick MgO barriers [resistance × area product (R × A) > 4 Ωµm2]23,24,25, 28, most works still rely on very thin MgO barriers (R × A ~ 1 Ωµm2)16, 20, 21, 30,31,32,33,34. Hence, the consensus solution to excite STT excitations in nanofabricated MTJ stacks has been the use of ultra-low R × A barriers. In that respect, these ultra-thin MgO barriers can sustain high current densities but the so far unavoidable presence of a large density of defects and pinholes at such low barrier thicknesses (and low R × A) results in smaller TMR, lower breakdown voltage and an overall decrease in reliability and reproducibility35. Apart from the requirement of having ultra-low R × A, the role of the tunnel barrier on the properties of STNOs has been so far critically overlooked. The large majority of reported results rely in MTJs where the MTJ transport properties are dominated by defects. These defects are present already on the as-deposited state29 or, in some cases, are created prior to the dynamic characterization of the system by applying large currents that irreversibly change the transport properties of the device in a non-controlled way, which is required in order to observe STT persistent oscillations36. The effect of such defects on the dynamics is still not well accounted and, on top of that, the higher TMR and resistance of thicker MgO barriers should increase P out . The assessment of such large unexplored region for STNO operation could reveal crucial operating conditions to boost their applicability and offer new fundamental physical insights.
In in this work, the role of the tunnel barrier on the STNO dynamics is studied using homogeneous in-plane magnetized STNOs. Such STNOs have output powers in in the range of 1–40 nW and critical current densities required to excite auto-oscillations (J STT ) are often larger than 106 A/cm2 24, 28. The STNOs were nanofabricated from MTJ stacks, deposited on 200 mm diameter wafers, and incorporating an MgO wedge (resulting in measured R × A values in the range 1–40 Ω µm2). Two wedge samples have been processed into nano-pillars with diameters of 200 nm which were characterized statically (TMR, low bias R × A and transfer curves, DC voltage/current breakdown) and dynamically (frequency spectrum versus bias current at fixed applied field). The results obtained in the two fabricated samples are consistent and clearly show that there is a trade-off between endurance to large currents (maximized for low R × A MTJs) and large TMR (maximized for large R × A MTJs), with an optimal R × A region showing the largest P out in the 7.5–12.5 Ωµm2 range. In this region, STNOs with large impedance matched P out values up to 200 nW are consistently found. This optimal R × A region was corroborated by micromagnetic simulations that revealed a good agreement with the experimental data. Furthermore, a decrease by 2 orders of magnitude of J STT was observed when going from very thin (below 5 Ωµm2) to thicker MgO barriers. As a result, very small J STT values (down to 1.17 × 105 A/cm2) are achieved in the large R × A and large TMR region, resulting in an enhancement of the STNOs operational window. More precisely, as the R × A increases, the operational window [J STT onset to breakdown current density (J break )] increases, contributing to an enhancement of the device robustness. Thus, the modification of the tunnel barrier thickness alone provides a mechanism to decrease the value of J STT , and simultaneously increasing P out , something of fundamental importance for all types of STNOs.
Sample Nanofabrication
Two MTJ stacks incorporating MgO wedges were deposited over 200 mm Si 〈100〉 wafers in a Timaris Singulus tool, leading to a variable R × A over the wafer from below 1 Ωµm2 up to 40 Ωµm2 (corresponding to MgO thicknesses from ~0.6 to ~0.9 nm). The MgO barriers were deposited from MgO targets without subsequent oxidation. The two stacks deposited were S1: Substrate/100 Al2O3/5 Ta/50 CuN/10 Ru/50 CuN/20 Ru/17 Pt38Mn62/2 CoFe30/0.85 Ru/2.6 CoFe40B20/MgO wedge/2 CoFe40B20/10 Ru/150 Cu/30 Ru and S2: Substrate/100 Al2O3/3 Ta/30 CuN/5 Ta/17 Pt38Mn62/2 CoFe30/0.85 Ru/2.6 CoFe40B20/MgO wedge/1.4 CoFe40B20/10 Ru/150 Cu/30 Ru (thicknesses in nm). Despite other differences in the stack, the main variation between the two deposited wafers concern the free layer thickness: for S1, t CoFeB = 2.0 nm and for S2, t CoFeB = 1.4 nm. Both CoFeB layers have their magnetization in-plane, although in the case of S2 the CoFeB is already close to the transition between in-plane to out-of-plane magnetization (observed at ~1.1 nm of CoFeB). Most results reported here were collected from wafer S1, with S2 being mainly used to corroborate and demonstrate the reproducibility of the observed results. Upon deposition, the wafers were annealed for 2 h at 330 °C and cooled down under a magnetic field of 1 T along the easy axis defined during deposition.
Both stacks were then patterned into circular devices with diameters of 200 nm. To that end, a nanofabrication method based on ion milling of the MTJ nano-pillars and an ion beam planarization step of an Al2O3 insulating layer was used. Each nano-pillar has four dedicated contact pads which were used to measure the TMR and R × A without any contribution of contact resistances. All the nano-pillars produced were measured under quasi-static magnetic field sweeps (up to 16 kA/m) in an automatic prober. Figure 1(a) shows the R × A values obtained from these transport measurements performed on the MTJ pillars along the MgO wedge position. The R × A values extracted from transport measurements in patterned nano-pillars follow the same trend observed in the current in-plane tester (CIPT) measurements. As the R × A decreases so does the dispersion of the measured R × A. This is attributed to the existence of intrinsic defects in the MgO layer. This interpretation is reinforced when the TMR values obtained from the patterned nano-pillars are plotted against the measured R × A value, as shown in Fig. 1(b). Below 10 Ωµm2 a strong linear correlation between TMR and R × A, which crosses the plot origin, is observed. This correlation is the signature of the presence of leakage currents through conduction channels that do not preserve the spin of the electrons. In nanometric sized nano-pillars this role is usually attributed to re-deposited material in the nano-pillar side-walls formed during the nano-pillar ion milling etching. In this case, however, an effort to monitor and remove the extra material in the nano-pillar sidewall was made during the nanofabrication process. The data in Fig. 1(b) indicates that this effort was successful: notice that the linear correlation between TMR and R × A exists only in the region bellow 10 Ωµm2. If re-deposited material were present in the nano-pillars produced, it would affect all nano-pillars, regardless of the R × A value. In fact, it should lead to a much larger TMR reduction in pillars with a large R × A compared to those with a small R × A. Still, a distribution of data points linking the high R × A data points to the plot origin is not observed. The conclusion is clear: the nanofabrication process was successful in preventing the formation of redeposited material shorting the tunnelling current through the MgO layer, but below the 10 Ωµm2 value, the thin MgO barrier contains intrinsic defects that partially de-polarize the current that crosses it37. As result, there is a cross-over R × A below which the TMR starts to decrease with respect to that obtained in thick barriers. Large TMR values can still be achieved in this region21, but the defects are still present and their effect in the electronic transport can be detected37. The TMR values achieved in sample S2 were larger than those achieved in sample S1. This is unexpected, since the free layer of sample S2 is thicker, and it is likely due to small variations in the nanofabrication process. Still, both samples show consistent trends.
Characterization of the RF output in the frequency domain
To characterize the RF emission caused by STT excited oscillations of the free layer magnetization, a sub-set of the available MTJ nano-pillars was selected. The emission was studied at room temperature in the frequency window 3 Hz–10 GHz under a static bias current (I bias ) and bias field (H bias ) which were systematically swept within the limits of the experimental setup. As reported by other groups12, it was verified that P out is maximized when applying a large static magnetic field in a direction close, but with a slight offset from the direction that sets the free layer in the anti-parallel direction. In the case of the results reported here, an external applied field H bias = 16 kA/m applied along the plane (large enough to saturate the MTJ nano-pillars in the anti-parallel direction) was applied. The I bias was then ramped up until STT persistent oscillations were observed in the frequency spectrum and then a small tilt of the magnetic field direction was introduced with the purpose of maximizing P out . Once the magnetic field direction was optimized, the systematic characterization of the output spectrum was performed, sweeping I bias at constant H bias .
An example of a frequency spectrum can be seen in Fig. 2(a). This result concerns a nano-pillar from wafer S1 with an R × A of 11.5 Ωµm2 and a TMR of 87.8% exhibiting a P out of 200 nW at I bias = −2 mA. As shown, the spectrum is highly asymmetric with respect to the bias current polarity. Large amplitude, small linewidth peaks consistent with STT enabled auto-oscillations are observed only for negative bias currents (negative current is defined here as electrons traveling from the pinned to the free layer). In such configuration, the STT destabilizes the anti-parallel configuration which is set by the magnetic field. Besides the large P out , the device also exhibits a reasonable linewidth (below 100 MHz). On the other hand, low power RF emissions with large linewidths consistent with thermal excitations are observed for positive currents, a configuration for which STT stabilizes the anti-parallel configuration. The small precession mode at 4 GHz might be caused by structural inhomogeneities or magnetic grains.
To compare the output power of nano-pillars with different R × A, care must be taken concerning the impedance mismatch in the acquired spectrum. The emission spectrum of the MTJ nano-pillars is amplified by an amplifier with a 50 Ω input impedance before being injected into the spectrum analyser where the spectrum is collected [Fig. 2(f)]. Due to the resistance mismatch between the amplifier input impedance (R L ~ 50 Ω) and the MTJ, the measured output power is only a fraction of that actually emitted by the MTJ. The fraction of power amplified depends on the absolute resistance of the MTJ. For this reason, the output power collected in the amplifier for nano-pillars with different resistance values are not directly comparable. To account for the effect of the impedance mismatch the integrated matched output power P out of each device was computed. To that end, for each measurement of the voltage [V(f)] at a certain I bias and H bias (and corresponding R), the integrated non-matched power (P m e a s u r e d ) collected at the amplified input was calculated using:
Here \({V}_{0}(f)\) is the voltage measured at \({I}_{bias}=0\), BW the measurement bandwidth (the value used in these measurements was 3 MHz) and g(f) the gain of the amplifier. The integrated matched output power P out considering the measurement setup circuit is then calculated from38:
The effect of this correction can be seen in Fig. 2(e). For a nano-pillar with a resistance between 400 Ω and 600 Ω (depending on I b i a s ), P o u t can be larger by a factor of 2 than P measured at the amplifier input.
Relation between TMR, R × A and P out
To clarify the role of the MgO thickness in the RF emission of the final devices, the RF emission of a sub-set of the devices represented in Fig. 1 was characterized. Figure 3(a) shows the position of the selected devices in the TMR vs. R × A phase space together with the maximum measured P out value which is represented as a colour scale. The size of each dot encodes the linewidth information at the I bias value that maximizes the quality factor (Q = P out /Γ) with larger dots representing larger linewidths. It is important to note that the maximum P out represented in Fig. 3(a) were obtained under different I bias values for different devices. Due to the different impedance values of the patterned nano-pillars (which have all the same area, but different MgO thicknesses) the optimum current that maximizes P out depends on the position of the devices on the wafer.
It is clear from Fig. 3(a) that P out is maximized precisely in the R × A region between 7.5–12.5 Ωµm2. In this region, P out is larger by a factor of 5 when compared to that obtained in the ultra-low R × A region close to 1 Ωµm2 which is usually targeted in STNO devices. At a first look, one could argue that the optimal R × A region that maximizes P out is just the region that displays higher TMR with the lowest possible R × A. However, if we compare the STNO with the highest TMR in the region below 5 Ωµm2 (69%) with the oscillator with the lowest TMR in the optimal region (73%) the P out values are still higher in the optimal region (65 and 121 nW, respectively). Furthermore, even though there is some variability in the P out of oscillators with similar positions in the TMR vs R × A plot, the lowest measured P out value in the optimal region is always larger than the highest P out for the small R × A samples (below 5 Ωµm2). Therefore, even though lower R × A values allow the use of higher currents that may excite larger oscillations, the decrease of R × A is not always the best option to achieve optimal STNOs. In fact, the higher resistance characteristic of a thicker MgO results in a larger voltage variation of the oscillator even for similar TMR ratios. A similar conclusion can be extracted if the P out for STNOs in the optimum R × A region is compared with that of devices in the larger R × A range. This occurs because for more resistive MTJs, J break is achieved before the excitation of large magnetic precessions, leading to an optimal R × A region. The observed variation of the P out values likely results from the unavoidable process variability (small differences in sizes, density of defects or edge roughness). Despite this factor, the large number of characterized devices allowed us to determine clear trends as a function of R × A. This behaviour was observed and reproduced in the two wedge wafers nanofabricated, despite the different magnetic configurations (t CoFeB = 2.0 nm for S1 t CoFeB = 1.4 nm for S2).
To further corroborate the observation of an optimal R × A region where P out is maximized, these experimental results were compared with micromagnetic simulations of the STT-induced dynamics. The simulations were performed using the object oriented micromagnetic framework (OOMMF)39 to solve the Landau-Lifshitz-Gilbert-Slonczewski (LLGS) equation1. A 2.0 nm thick CoFeB free layer patterned in a 200 nm diameter pillar was considered (matching the stack and geometry of S1 devices). Apart from the geometry, the remaining parameters that were kept constant in the simulations were: Gilbert damping α = 0.01, free layer magnetization Ms = 1.36 × 106 A/m and applied field H bias = 16 kA/m. The interfacial perpendicular magnetic anisotropy induced by the MgO layer was also considered (interfacial anisotropy constant of 1.5 × 10−3 J/m2 extracted from magnetic measurements).
The simulations were performed with a bias current density of \(\,{J}_{bias}={V}_{break}/(R\times A)\), that were measured experimentally as a function of R × A using a ramp procedure (in a sub-set of devices of Fig. 1). The applied current was successively increased until dielectric breakdown is observed and the measurements fitted to an exponential law. This is the maximum possible current density that can be reached and, theoretically, the current that maximizes P out (within the range of the experimentally achievable values). On the other hand, the spin current polarization (P) was determined using the TMR value and Jullière’s model40 \([TMR=\,2{P}^{2}/(1-{P}^{2})\)]. Hence, the STT-induced dynamics could be computed using the TMR and R × A as input parameters which were swept systematically within the limits of Fig. 3(a).
Then, the P out delivered to a load with impedance R L was then calculated from the induced dynamics using11, 41:
Here, \({V}_{out}(t)={\rm{\Delta }}R\cdot \,\cos (wt){I}_{bias}\) is the RF output voltage, R stands for resistance of the STNO and ΔR stands for the peak-to-peak amplitude of the STNO impedance variation during an oscillation period.
Therefore, the input R × A value will set the I bias used, along with the value of R and ΔR (this last parameter also depends on the TMR). As for the input TMR value, it has a twofold influence on P out . On one hand, ΔR for a given oscillation amplitude is proportional to the TMR value. On the other hand, the oscillation amplitude for a given current density depends on the spin current polarization which is also linked to the TMR value.
During the simulations, the P out values delivered to a matched load were computed from equation (3) by setting R L = R, with the result of this procedure being plotted in Fig. 3(b). Remarkably, the optimal R × A region where P out is maximized was also observed in the simulated case, although with the optimal region occurring for smaller R × A values (maximum around 8 Ωµm2). The calculated P out values (up to 100 nW) are also lower than the ones that were experimentally measured (up to 200 nW). A part of this discrepancy can be attributed to the thermally-induced precessions that were neglected in the simulations. Note that an overall increase of the magnetization oscillation amplitude would increase P out more significantly for larger R × A values, moving the optimal R × A region to values closer to the experimental data. Nevertheless, the simulations corroborate the observation of an R × A region that maximizes P out .
Critical current densities for STT
To achieve very large amplitude oscillations before the dielectric breakdown of the MTJ, a very low critical current density for STT-induced magnetic precession J STT is required. In fact, it was shown theoretically that P out increases with J/J STT 42. The fact that STT excited oscillations are observed in the full measured R × A range is surprising. Since these oscillations can only be obtained when the condition \(\,{J}_{STT} < {J}_{break}\) is met, the observation of oscillations even for R × A values of ~40 Ωµm2 can only be understood if, in this large R × A range, J STT is unexpectedly small or J break is unexpectedly large.
The values of J STT can be calculated by identifying the deviation from the linear dependence of the inverse power on the bias current. An example of this derivation is plotted in Fig. 4(a), where the value of the critical current density J STT was extracted by extrapolating the inverse power times the current squared (\({{I}_{bias}}^{2}/{P}_{out}\to 0\)). J STT can be derived using the relation \(({{J}_{bias}}^{2}/{P}_{out})\propto ({J}_{STT}-{J}_{bias})\), valid in the thermally activated region and noting that, as the inverse power approaches zero, \({J}_{bias}\to {J}_{STT}\,\) 24, 42. Thus, J STT is determined by the x-axis intercept with the linear fit in the thermally excited region. In Fig. 4(b) and (c) the calculated values of J STT are shown as a function of R × A and TMR, respectively. From the R × A dependence of S1 [Fig. 4(b); red triangles] one can observe that J STT sharply decreases by 2 orders of magnitude as the MgO thickness is increased. In fact, the TMR dependence [Fig. 4(c)] indicates that large TMR values, characteristic of continuous MgO barriers, depict significantly lower values of J STT with smaller error bars (note the logarithmic scale). The values of J STT obtained for S2 (blue circles) corroborate the observed tendencies but with larger values of J STT . Further work is still required to understand the reason of this discrepancy. Nevertheless, despite the sample-to-sample variation, the observed J STT dependence (as a function of R × A and TMR) is consistent in both samples. This result unveils the possibility to decrease the value of J STT just by using thicker MgO barriers.
In the macrospin approximation, the critical current density for STT oscillations (J STT ) can be written as43:
where e is the charge of the electron, \({\mu }_{0}\) is the permeability of free space, ħ the Planck constant, M s the magnetization saturation, α the Gilbert damping constant, d the thickness of the free layer, M eff the effective demagnetizing field (given by the demagnetizing factor minus the interface perpendicular magnetic anisotropy) and P the spin polarization.
The value of J STT is expected to be inversely proportional to the spin polarization of the current. Jullière’s model was used to correlate the TMR with the spin polarization and, in conjugation with equation (4), the expected trend of J STT as a function of TMR was estimated. This was performed, using the value of J STT measured for S1, with the calculated trend represented by the green line in Fig. 4(c). Even though the predicted trend indeed reveals a decrease of J STT with the TMR, the experimentally observed dependence is not completely consistent with the model. The discrepancy between the model and the experimental data can be attributed to different effects not accounted for in this simple model. As a first possibility, the TMR value used to perform the fit was measured at low bias and decreases for higher bias voltages. The TMR at J STT could not be determined since the RF characterization was performed with 2-point contacts (associated contact resistance) and the measurements were destructive (performed until MTJ breakdown). It is expected that in conditions consistent with STT excitations the spin polarization of the current being injected in the free layer decreases compared to a low bias condition. However, this decrease in the spin polarization under STT conditions should be more pronounced for devices in the large R × A range when compared to devices in the low R × A range (which have lower breakdown voltages and therefore a smaller TMR decrease with increasing I bias ). So, this effect should have a contribution which opposes the trend observed experimentally. Either this effect has a small contribution or there are some other factors playing a more important role. A second possibility consists on the ferromagnetic coupling (H F ) which depends on the MgO thickness due to the orange peel coupling44. The H F field is larger for thinner barriers, and it can easily reach values of the order of 8 kA/m near the 1 Ωµm2 range, which is comparable to the applied field H bias = 16 kA/m, meaning that the effective field acting on the free layer can have a non-negligible dependence on R × A as well. However, this effect is expected to be small since H F is around one order of magnitude smaller than the effective demagnetizing field. Finally, as discussed previously, the data of Fig. 1 indicates that for devices with R × A < 10 Ωµm2 there are intrinsic defects in the MgO barrier which provide alternative conduction channels dominated by transport mechanisms other than tunneling37. Only the fraction of current which crosses the MgO barrier through tunnelling is described by Jullière’s model. In the presence of such defects, the fraction that is not described by this model and does not conserve the spin of the electrons increases as R × A decreases. This is perceived as a decrease in the spin polarization which results in larger J STT values compared to a scenario where spin conservative tunnelling is the only transport mechanism. This effect is consistent with the mismatch observed in Fig. 4(c), although a better understanding of the different transport mechanisms and the fraction of current carried by each of them is required for a quantitative analysis.
Operational window
For STNOs to reach commercial applications it is important to have a large P out and a small bandwidth but also stable devices that achieve large oscillations for safe conditions with currents well below breakdown. To determine this range of operation, in Fig. 5 it is depicted the current density values at which the Q factor (P out /Γ) is maximized (white diamonds) along with J break (red circles) and J STT (blue triangles) for each STNO characterized in wafer S1.
For low R × A (below 5 Ωµm2) the current density that optimizes Q and the J break values are quite large. However, the J STT values are also significantly large so that the region for STNO operation (STNO region) is particularly thin. The reason for this is that despite the large J break , the breakdown voltage (V break ) is smaller in this region. In fact, while for R × A values below 5 Ωµm2 one has V break ~ 0.35 V (due to the presence of small defects in the insulating layer), above 5 Ωµm2, V break increases to ~1 V. As R × A increases, the MgO barrier gets thicker and its quality improves (more continuous and better defined crystalline texture), the voltage endurance of the MTJ is higher and simultaneously the values of J STT get significantly lower. Thus, although the maximum current density endured by the tunnel barriers decreases with R × A, the value of J STT also decreases but at an even faster rate which results in a broader STNO operating region.
Moreover, the higher resistance of these MTJs gives rise to larger voltage variations for the same magnetic precession amplitude leading to larger P out values observed in the intermediate R × A region. When R × A further increases, J break steadily decreases. For high R × A the currents that maximize Q are close to (or even coincide) with the breakdown, while for lower R × A values, they are closer to the bottom limit of the STNO region. This means that, for R × A values above ~20 Ωµm2, only small amplitude oscillations can be achieved before breakdown occurs. This leads to a new decrease of P out and confirms the optimal R × A region between 7.5 and 12.5 Ωµm2.
Open prospects
Despite the large effort of the STNOs community to work in the lowest possible R × A range, this work presents a large set of consistent data showing that thicker MgO barriers increase the P out of these oscillators. From an application point of view this is a twofold advantage since P out is increased and thicker and more homogeneous MgO barriers have less defects and higher reproducibility. This optimal R × A region is situated within 7.5–12.5 Ωµm2 where P out values up to 200 nW were observed, which are a factor of 5 larger than those obtained from devices with R × A ~ 1 Ωµm2. The results were corroborated by micromagnetic simulations and by a second fabricated MTJ incorporating an MgO wedge, both depicting the optimal region for maximized P out . The main fact responsible for this large output is the low J STT (down to 1.17 × 105 A/cm2) obtained for the more continuous and crystalline MgO. Further investigation is still required to fully understand the mechanisms responsible for the low values of J STT . Another worthwhile aspect of the results shown here is that the intermediate thickness of the MgO barrier can be applied to different STNOs geometries. The increase of the MgO thickness had no other discernible impact in the main operational figures of merit of the STNOs apart from the increase of P out (frequency of operation and linewidth remained unchanged). It is therefore expected that the reported P out increase in the intermediate MgO thickness range reported here could have a cumulative effect when combined with other improvements of magnetic nature (such as vortex oscillators, STNOs incorporating perpendicular magnetic anisotropy or perpendicular polarizers) or device configurations (synchronized oscillators) that are also known to result in an increase of P out when compared to homogeneous in-plane magnetization STNOs.
Methods
Nanofabrication process
The MTJ nano-pillars were patterned in a 3-step ion milling process which is monitored in real time by a secondary ion mass spectrometer (SIMS). During the 1st step, a capping layer is patterned (150 nm Cu/30 nm Ru), using high etch rate conditions. During the 2nd step the magnetic layers and MgO tunnel barrier are patterned using low etch rate and low energy conditions (with an incoming ion energy of 150 eV) that minimize the amount of damage created in the nano-pillar by ion bombardment. This step is stopped between 10–50 nm (depending on the stack) below the bottom layer of the antiferromagnetic layer, ensuring that all the ferromagnetic layers are confined within the nano-pillar shape. During the 3rd. step a grazing angle milling is used to clean the redeposited material from the nano-pillar sidewalls. The nano-pillar shape and amount of redeposited material are evaluated using HR-SEM conducted between steps 2 and 3. After a first side-wall cleaning step, new HR-SEM images of the nano-pillars are collected and if necessary the sidewall cleaning step is extended. This cycle is repeated until the HR-SEM images reveal nano-pillar images free of any noticeable extra material. Upon defining the nano-pillar, an 800 nm Al2O3 insulating layer is deposited. The electrical contact to the top part of the nano-pillar is established by an ion milling planarization process where the oxide layer is bombarded, planarized and thinned down until the buried sacrificial contact layer is exposed. The stop point for this process is established by monitoring the evolution of the oxide topography on top of the nano-pillar using HR-SEM.
References
Slonczewski, J. Current-driven excitation of magnetic multilayers. J. Magn. Magn. Mater. 159, 1–7 (1996).
Tsoi, M. et al. Excitation of a Magnetic Multilayer by an Electric Current. Phys. Rev. Lett. 80, 4281–4284 (1998).
Myers, E. B. Current-Induced Switching of Domains in Magnetic Multilayer Devices. Science (80-.). 285, 867–870 (1999).
Katine, J., Albert, F., Buhrman, R., Myers, E. & Ralph, D. Current-driven magnetization reversal and spin-wave excitations in Co/Cu/Co pillars. Phys. Rev. Lett. 84, 3149–52 (2000).
Tsoi, M. et al. Generation and detection of phase-coherent current-driven magnons in magnetic multilayers. Nature 406, 46–48 (2000).
Iwasaki, J., Koshibae, W. & Nagaosa, N. Colossal spin transfer torque effect on skyrmion along the edge. Nano Lett. 14, 4432–4437 (2014).
Mellnik, A. R. et al. Spin-transfer torque generated by a topological insulator. Nature 511, 449–451 (2014).
Urazhdin, S. et al. Nanomagnonic devices based on the spin-transfer torque. Nat. Nanotechnol. 9, 509–13 (2014).
Bradley, D. A new spin on magnetic control. Mater. Today 14, 580 (2011).
Parkin, S. S. P., Hayashi, M. & Thomas, L. Magnetic Domain-Wall Racetrack Memory. Science (80-.). 320, 190–195 (2008).
Zeng, Z., Finocchio, G. & Jiang, H. Spin transfer nano-oscillators. Nanoscale 5, 2219–31 (2013).
Kiselev, S. I. et al. Microwave oscillations of a nanomagnet driven by a spin-polarized current. Nature 425, 380–3 (2003).
Kaka, S. et al. Mutual phase-locking of microwave spin torque nano-oscillators. Nature 437, 389–92 (2005).
Rippard, W. H. et al. Injection locking and phase control of spin transfer nano-oscillators. Phys. Rev. Lett. 95, 10–13 (2005).
Sani, S. et al. Mutually synchronized bottom-up multi-nanocontact spin-torque oscillators. Nat. Commun. 4, 2731 (2013).
Dussaux, A. et al. Large microwave generation from current-driven magnetic vortex oscillators in magnetic tunnel junctions. Nat. Commun. 1, 8 (2010).
Pribiag, V. S. et al. Magnetic vortex oscillator driven by dc spin-polarized current. Nat. Phys. 3, 498–503 (2007).
Houssameddine, D. et al. Spin-torque oscillator using a perpendicular polarizer and a planar free layer. Nat. Mater. 6, 441–7 (2007).
Johansen, Ø. & Linder, J. Current driven spin – orbit torque oscillator: ferromagnetic and antiferromagnetic coupling. Sci. Rep. 6, 33845 (2016).
Choi, H. S. et al. Spin nano-oscillator-based wireless communication. Sci. Rep. 4, 1–7 (2014).
Houssameddine, D. et al. Spin transfer induced coherent microwave emission with large power from nanoscale MgO tunnel junctions. Appl. Phys. Lett. 93, 2006–2009 (2008).
Locatelli, N. et al. Efficient Synchronization of Dipolarly Coupled Vortex-Based Spin Transfer Nano-Oscillators. Sci. Rep. 5, 17039 (2015).
Dussaux, A. et al. Large amplitude spin torque vortex oscillations at zero external field using a perpendicular spin polarizer. Appl. Phys. Lett. 105, 022404 (2014).
Zeng, Z. et al. High-power coherent microwave emission from magnetic tunnel junction nano-oscillators with perpendicular anisotropy. ACS Nano 6, 6115–21 (2012).
Zeng, Z. et al. Ultralow-current-density and bias-field-free spin-transfer nano-oscillator. Sci. Rep. 3, 1426 (2013).
Houshang, A. et al. Spin-wave-beam driven synchronization of nanocontact spin-torque oscillators. Nat. Nanotechnol. 11, 280–286 (2015).
Maehara, H. et al. Large emission power over 2 μW with high Q factor obtained from nanocontact magnetic-tunnel-junction-based spin torque oscillator. Appl. Phys. Express 6, 113005 (2013).
Deac, A. M. et al. Bias-driven high-power microwave emission from MgO-based tunnel magnetoresistance devices. Nat. Phys. 4, 803–809 (2008).
Kubota, H. et al. Quantitative measurement of voltage dependence of spin-transfer torque in MgO-based magnetic tunnel junctions. Nat. Phys. 4, 37–41 (2008).
Zeng, Z. M. et al. Enhancement of microwave emission in magnetic tunnel junction oscillators through in-plane field orientation. Appl. Phys. Lett. 99, 032503 (2011).
Martin, S. Y. et al. Parametric oscillator based on nonlinear vortex dynamics in low-resistance magnetic tunnel junctions. Phys. Rev. B 84, 144434 (2011).
Quinsat, M. et al. Modulation bandwidth of spin torque oscillators under current modulation. Appl. Phys. Lett. 105 (2014).
Tamaru, S. et al. Magnetic field angle dependence of the self-oscillation of spin torque oscillators having a perpendicularly magnetized free layer and in-plane magnetized reference layer. Appl. Phys. Express 7 (2014).
Tamaru, S. et al. Observations of thermally excited ferromagnetic resonance on spin torque oscillators having a perpendicularly magnetized free layer. J. Appl. Phys. 115, 2014–2017 (2014).
Zaleski, A. et al. The study of conductance in magnetic tunnel junctions with a thin MgO barrier: The effect of Ar pressure on tunnel magnetoresistance and resistance area product. J. Appl. Phys. 111, 13–18 (2012).
Devolder, T. et al. Auto-oscillation and narrow spectral lines in spin-torque oscillators based on MgO magnetic tunnel junctions. J. Appl. Phys. 106, 103921 (2009).
Ventura, J., Araujo, J. P., Sousa, J. B., Ferreira, R. & Freitas, P. P. Competing spin-dependent conductance channels in underoxidized tunnel junctions. Appl. Phys. Lett. 90, 3–5 (2007).
Bowick, C., Blyler, J. & Ajluni, C. RF circuit design. J. Chem. Inf. Model. 53, (Elsevier, 2008).
Donahue, M. J. & Porter, D. G. OOMMF User’s Guide version 1.0. 6376 (1999).
Moodera, J. S., Kinder, L. R., Wong, T. M. & Meservey, R. Large Magnetoresistance at Room Temperature in Ferromagnetic Thin Film Tunnel Junctions. Phys. Rev. Lett. 74, 3273–3276 (1995).
Russek, S. E., Rippard, W. H., Cecil, T. & Heindl, R. Handbook of Nanophysics: Functional Nanomaterials. (CRC PrIlic, 2010).
Slavin, A. & Tiberkevich, V. Nonlinear auto-oscillator theory of microwave generation by spin-polarized current. IEEE Trans. Magn. 45, 1875–1918 (2009).
Stiles, M. D. & Miltat, J. Spin Dynamics in Confined Magnetic Structures III. Top. Appl. Phys. 101, 225–308 (2006).
Costa, J. D. et al. Impact of MgO thickness on the performance of Spin Transfer Torque Nano-Oscillators. IEEE Trans. Magn. 9464, 1–1 (2015).
Acknowledgements
The authors would like to thank U. Ebels for fruitful discussions concerning these results and to N.A. Garcia-Martinez for technical help in regard of the micromagnetic simulations. J.D.C. is thankful for the support of FCT grant SFRH/BD/7939/2011. This work was possible thanks to the support of EU FP7-ICT project MOSAIC (grant n.317950), ON2 project INTEGRATION (grant NORTE-07-0124-FEDER-000050) and FCT project SCOMagNO (grant PTDC-CTM-NAM-112672-2009) which were used in the development of different aspects of the overall work.
Author information
Authors and Affiliations
Contributions
J.D.C., E.P. and R.F. were responsible for the work related with the optimization, deposition and bulk characterization of the MTJ stacks with the MgO wedges. J.D.C. and J.B. performed the nanofabrication process of the MTJ stacks, using a nanofabrication process which was developed by R.F., J.B., M.T. and J.D.C. and supported by F.L.D. who carried out the inspection of the nanofabricated devices with a focused ion beam-SEM. The quasi-static transport characterization of the devices upon patterning were performed by J.D.C. and R.F. J.D.C. was responsible for the high frequency transport characterization of the devices upon patterning, using a setup and data analysis algorithms developed and maintained by S.S. and T.B. B.L. and A.S.J. contributed to the micromagnetic simulations and had a fundamental role in the discussion and interpretation of the experimental results. R.F., J.V. and P.P.F. were responsible for the scientific coordination of the work. All authors discussed and made contributions for the content of this report.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Costa, J.D., Serrano-Guisan, S., Lacoste, B. et al. High power and low critical current density spin transfer torque nano-oscillators using MgO barriers with intermediate thickness. Sci Rep 7, 7237 (2017). https://doi.org/10.1038/s41598-017-07762-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-07762-z
This article is cited by
-
Temperature effect on a weighted vortex spin-torque nano-oscillator for neuromorphic computing
Scientific Reports (2024)
-
Spin–orbit torque flash analog-to-digital converter
Scientific Reports (2023)
-
Second harmonic injection locking of coupled spin torque vortex oscillators with an individual phase access
Communications Physics (2023)
-
Granular vortex spin-torque nano oscillator for reservoir computing
Scientific Reports (2023)
-
Electrical characterisation of higher order spin wave modes in vortex-based magnetic tunnel junctions
Communications Physics (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.