Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Ultrahigh adsorption and singlet-oxygen mediated degradation for efficient synergetic removal of bisphenol A by a stable zirconium-porphyrin metal-organic framework


Bisphenol A (BPA), one of 23 most important endocrine disrupting chemicals, was efficiently removed and sequentially photodegraded by a zirconium-porphyrin metal–organic framework (MOF) catalyst under visible light for water treatment. Well control of photodegradation allows the kinetic separation of adsorption step and photodegradation step. Ultrahigh adsorption uptake of 487.69 ± 8.37 mg g−1 is observed, while efficient photodegradation could be observed within 20 min at the rate of 0.004 mg min−1. The synergetic effect boosts the photocatalytic efficiency and confirms that the catalysis happens inside the MOF pores other than in the solution phase. Furthermore, the mechanism was elucidated by diverse control experiments, such as in the conditions of 1O2 scavenger, in darkness and with the changes of light sensitizing ligands. It confirmed that BPA was oxidized by the 1O2 which was generated from porphyrin ligand within MOFs under visible-light. The excellent reusability and wide range of suitable pH range make the Zr-porphyrin MOFs practical for the photocatalytic water treatment processes.


Metal–organic frameworks (MOFs) with tunable pore size and modifiable pore surfaces have been extensively studied due to their promising applications in gas storage, separation, sensing, catalysis and environmental applications1,2,3,4,5,6,7,8,9,10,11,12,13,14,15,16,17,18,19,20,21. Photocatalysis is a convenient way to utilize the energy of sunlight or artificial illumination to achieve chemical transformation in the green earth and renewable energy projects22,23,24,25. Efficient photocatalysis with MOFs have been used for water splitting23,24,25,26 and CO2 reduction with the photogeneration of free radicals and electrons26,27,28. Recently, a different type of photocatalysis, the photogeneration of singlet oxygen (1O2) from light-sensitizing MOF attracted immense research efforts due to the potential applications in photodynamic therapy (PDT) and degradation of chemical warfare agent29,30,31,32,33,34,35,36,37.

Singlet oxygen (1O2) is the lowest excited state oxygen molecule, which can be obtained by the energy transfer from an excited triplet state of a photosensitizer to ground-state molecular oxygen (3O2)38,39,40,41,42. 1O2 is more eco-friendly and efficient than free radicals in the reaction with certain classes of organic compounds (e.g., furans and phenols)43, 44. Although the 1O2 is very promising in the degradation of contaminants from waste water45,46,47, there exists no report over the photodegradation of BPA by MOFs for organic pollutant treatment based on 1O2.

Porphyrin derivatives with high photosensitizing efficiency have been widely used in the production of singlet oxygen48,49,50,51,52,53,54,55. To explore the applications in aqueous solutions, zirconium based tetrakis (4-carboxyphenyl)-porphyrin (TCPP) MOFs have been synthesized37, 56. Although zirconium-porphyrin with exceptional stability has been applied in several heterogeneous catalysis26, 28, 37, 57, 58, the mechanism is still obscure. It is hard to kinetically distinguish the adsorption step and catalysis step within the normal MOF catalysis due to the simultaneous existence of permanent porosity and internal catalytic sites59. The controllable degradation via singlet oxygen under light irradiation in MOFs37, 60 kinetically separate the adsorption and catalysis processes. It gives a great opportunity to investigate their synergy effect, which has never been explored.

Bisphenol A (BPA) is the most widely used and industrially produced bisphenols, which is regarded as one of the most important 23 endocrine disrupting chemicals (EDCs) by World Health Organization (WHO)61. BPA is a good candidate molecule because its molecular kinetic diameter is smaller than the pore size of MOFs62,63,64. At the same time BPA is possibly degraded by singlet oxygen65,66,67.

Herein, to facilitate the adsorption, diffusion and photodegradation of BPA molecules, we have selected a mesoporous zirconium-porphyrin MOF PCN-222 (also named as MOF-545 or MMPF-6) with 3.7 nm permanent channels28, 37, 68, which is also highly stable in aqueous solution and capable of 1O2 generation under visible-light irradiation. The investigation of synergetic effects between stepwise adsorption and photodegradation could be achieved sequentially by adsorption under dark and degradation under visible light. Ultrahigh adsorption uptake of 487.69 ± 8.37 mg g−1 is observed, while efficient photodegradation could finish within 10 min. The synergetic effect boosts the photocatalytic efficiency as well as confirms that the catalysis happens inside the MOF pores other than in the solution phase. Furthermore, the mechanism was elucidated by the control experiments with 1O2 scavenger, darkness and changes of light sensitizing ligand. It confirmed that BPA was oxidized by the 1O2 which was generated by TCPP ligand in MOFs under visible-light irradiation. The reusability, stability and possible reaction pathway about photocatalytic degradation of BPA by PCN-222 were explored, we found PCN-222 had excellent reusability and wide range of suitable pH range.

Results and Discussion

Characterization of the PCN-222

The PCN-222 was synthesized according to the existing methods, and well characterized by XRD, N2 adsorption–desorption experiment and SEM (Fig. 1). The XRD measurements demonstrated that the synthesized PCN-222 experimental XRD pattern was consistent with the simulation diagram, which proved PCN-222 was successfully prepared. The size of single crystalline rod-like PCN-222 was in micro-meter scale (Fig. 1c). The SEM image of PCN-222 after catalysis was shown in Fig. 1d, confirming that the MOFs kept intact morphology even after 5-cycles catalysis. The prepared PCN-222 gave a BET surface area of 1914 m2 g−1 with a pore volume of 1.03 cm3 g−1. The pore size distribution of PCN-222 estimated by the Barrett–Joyner–Halenda method gave a pore diameter of 3.59 nm (Figure S1). The isostructural MOF with a different light sensitizing ligand, namely PCN-222-Fe(III)Cl was also successfully prepared and well characterized for further exploration of 1O2 generation mechanism (Figure S2).

Figure 1
figure 1

(a) The nitrogen adsorption-desorption isotherms of PCN-222 at 77 K. (b) PXRD patterns of PCN-222 for the simulated, pre-catalysis and post-catalysis samples. SEM images of (c) pre-catalysis PCN-222 and (d) PCN-222 after 5-cycles catalysis.

Adsorption for BPA on PCN-222: Thermodynamics, Kinetics and suitable pH range

To fully reveal the potential of the adsorption of BPA by PCN-222, the static adsorption of BPA with high concentrations were performed. Small amounts of organic phase of ethanol were added to water to increase BPA solubility as well as to evaluate the solvent effect in real applications. Therefore, the adsorption isotherms for BPA on PCN-222 were plotted to demonstrate the sorption capacities with two different BPA solutions, which are BPA of 100 ppm in water/ethanol (249:1, v/v) solution and BPA of 250 ppm in water/ethanol (245:5, v/v) solution, respectively (Fig. 2).

Figure 2
figure 2

Adsorption isotherms of (a) 100 ppm BPA and (b) 250 ppm BPA at 25 °C and pH 8.0 for 60 min. Langmuir and Freundlich models were fitted to isotherms, respectively.

The maximum adsorption capacity of PCN-222 (487.69 ± 8.37 mg g−1) is the highest record compared to the other sorbents in the previous reports (Table S1)62. It is because PCN-222 has a three-dimensional structure with high surface area and ultra-large one-dimensional channels in 3.6 nm diameter28. The uptake of 487.69 ± 8.37 mg g−1 reveals the adsorption information in molecular level that 15 BPA molecules were adsorbed per unit cell, corresponding to one meso-channel unit (3.7 nm i.d.) and two micro-channel units (1.1 nm i.d.). Stoichiometrically, the 15 BPA molecules were adsorbed to 6 photo-sensitizing porphyrin ligands through van der Waals interactions for further catalysis.

To clearly elucidate the thermodynamic adsorption of BPA in PCN-222, Langmuir and Freundlich models were employed to fit the isothermal adsorption plots, respectively. Comparing to the empirical Freundlich isotherm, the theoretical Langmuir isotherm assumes that maximum coverage of the solid surface with a monolayer of the adsorbate molecules (see Supplementary Information Section S5). The fitting results of the Langmuir and Freundlich models are compared and shown in Fig. 2 while the corresponding parameter values are shown in Table S2. For the BPA concentration of 100 ppm, both Langmuir and Freundlich models are not fitting well with the R2 values of 0.815 and 0.856, respectively. Meanwhile, for the high BPA concentration of 250 ppm, R2 values for the Langmuir and Freundlich sorption isotherm were 0.947 and 0.976, respectively. The fitting results were in accordance to the structural properties of PCN-222. Basically, there are two adsorption sites in PCN-222 for BPA molecules, meso-channels (3.7 nm i.d.) and micro-channels (1.1 nm i.d.). In this case, Freundlich isotherm describes better in the multisite adsorption isotherm for rough surfaces. However, the micro-channels are only big enough for the adsorption of single BPA molecule (1.1 nm × 0.6 nm) per unit cell. Therefore, the meso-channel is the primary adsorption site and possibly adsorbs up to 15 BPA molecules per unit cell, rendering the monolayer adsorption within meso-channels. The current ultrahigh adsorption uptake record could be broken by the increase of organic solvent concentrations. However, considering the synergetic effect, monolayer adsorption type is good to further need of the photocatalysis. Therefore, no higher than 250 ppm concentrations were selected for BPA in the all following experiments.

The adsorption removal efficiency for BPA was also calculated. It is impossible to reach high removal efficiency and adsorption uptake at the same time. More adsorbents or low BPA concentrations will result in high removal efficiency. To make a fair comparison, 1.0 mg PCN-222 was added to 1.0 mL BPA aqueous solution with different concentrations. It showed up to 99.9% removal efficiency at 100 ppm BPA as well as 86.8% at 250 ppm, respectively. As the environmental concentrations for BPA were 0.002–269 ppb69, the pre-enrichment is difficult step in the practical treatment of the environmental samples. The high adsorption capacity and removal efficiency indicate ultrahigh equilibrium constant K which will be very practical in the enrichment of BPA with low concentrations.

The adsorption kinetics of BPA on PCN-222 were also evaluated and illustrated in Fig. 3a. The sorption rate of BPA on PCN-222 changed with time. In the first 10 minutes, the adsorption amount of BPA increased significantly and the adsorption capacity of 407.14 ± 6.08 mg g−1 was reached. From 10 to 40 minutes, the adsorption amount of BPA increased slowly with final equilibrium at 40 minutes and adsorption capacity of 487.69 ± 8.37 mg g−1. To well understand the adsorption kinetics, the pseudo-second-order kinetics model and intra-particle diffusion model were employed to fit kinetic data.


in which q e and q t are the adsorption capacity (mg g−1) at equilibrium and at time t (min), respectively, while k 2 is the rate constant for pseudo-second-order adsorption (g mg−1 min−1). The dependence of time for the adsorption of BPA on PCN-222 can be well fitted by a general pseudo-second-order kinetic model with R2 of 0.9999 rather than other models (Fig. 3b, Table S3 and Figure S4). The theoretical saturation adsorption capacity of 490.1 ± 1.8 mg g−1 calculated by pseudo-second-order kinetic model is consistent with the experimental value of 487.69 ± 8.37 mg g−1. So BPA adsorption behaviour by PCN-222 is mainly physical adsorption, and its adsorption rate is affected by the concentration of BPA.

Figure 3
figure 3

(a) The kinetic curve for the adsorption of BPA on PCN-222 at 250 ppm of BPA at 25 °C and pH 8.0. (b) Data fitting with pseudo-second-order kinetics model. (c) Data fitting with intra-particle diffusion model. (d) Effect of pH on the adsorption of BPA on PCN-222 at 25 °C (Sorption conditions: C0 = 250 ppm, V = 1.0 mL, and mMOF = 1.0 mg). Insert shows the effect of pH on distribution of different BPA chemical forms.

In order to further analyze the dynamic diffusion mechanism, the intra-particle diffusion model was used, as the following equation:

$${q}_{t}={k}_{i}\times {t}^{\frac{1}{2}}+I$$

where q t (mg g−1) is the adsorption capacity at time t, k i (mg g−1 min−0.5) is the intra-particle diffusion rate constant, and I is the coefficient associated with the thickness of boundary layer. If I = 0, then the rate of adsorption is only restricted by intra-particle diffusion for the total adsorption process. The fitting plot of intra-particle diffusion shows two portions of straight lines (Fig. 3c). According to fitting parameters (Table S3), I ≠ 0, it indicates that boundary layer diffusion also affects the rate of adsorption while intra-particle diffusion itself was not solely rate-limiting step70.

The pH has important influence on the stability of PCN-222 and the chemical forms of BPA in aqueous solution62. Figure 3d shows the effect of pH on the adsorption of BPA by PCN-222. The removal efficiency of BPA by PCN-222 increased from 82.5% to 97.8% in the pH range of 2–6, while the removal efficiency remained high removal efficiency in the pH range of 6–10 with highest removal efficiency of 99.3%. The results indicated that PCN-222 has a wide pH range for applications. The removal efficiency was affected in the extreme pH. When the pH was larger than 12, the structure of PCN-222 would be instable and BPA was mostly ionized to divalent anions (BPA2−), thus reduced the sorption capacity. At the same time, the sorption capacity decreased in strong acid as the porphyrin in PCN-222 was protonated. Considering the structure of BPA molecules and adsorption capacity of adsorbents, all other experiments were carried out at pH 8.0.

Visible light photocatalytic degradation of BPA by PCN-222

In order to demonstrate the advantage of synergetic effects between adsorption and photodegradation of BPA in MOFs, the BPA solution (100 ppm) was first adsorbed by MOFs without visible light irradiation for 1 h to ensure the complete adsorption (Figure S5). To fully elucidate the degradation efficiency of BPA by PCN-222 under visible light irradiation, both the BPA concentration in aqueous solution and the residual BPA quantity within PCN-222 were monitored during the catalytic processes. Besides, for comparison, three controlled trials were prepared with the following procedures, which the samples were treated without illumination, replacing PCN-222 with PCN-222-Fe(III)Cl and adding singlet oxygen scavenger.

The BPA concentration in aqueous solution was monitored during the adsorption and catalytic processes. Due to high adsorption efficiency of MOFs (over 99%), the residual concentration of BPA in aqueous solution approached to 0.0006 mg after adsorption and all of the remaining BPA was adsorbed in porous channel of PCN-222. (Figure S6). The significant photodegradation of BPA was observed mainly on PCN-222 adsorbent by ethanol elution and GC-MS monitoring (red curve in Fig. 4). It was found that from 0 to 20 min, the mass of BPA in the PCN-222 channel decreased sharply, demonstrating a pseudo zero-order kinetic model with the degradation rate constant of 0.004 ± 0.0002 mg min−1 (see Supplementary Information Section S6). It is worth noting that our catalytic system follows pseudo zero-order kinetic while other materials obeys first-order kinetic71,72,73,74,75. It was mainly because of the high BPA concentrations and mesopore confinement, which originate from the pre-enrichment of BPA in PCN-222 that 15 BPA molecules were stoichiometrically pre-adsorbed to 6 photo-sensitizing porphyrin ligands along the mesoporous channels. The degradation rate gradually slowed down after 20 min.

Figure 4
figure 4

The synergetic adsorption and degradation of BPA with different conditions: PCN-222 in dark (black curve); PCN-222 under visible light (red curve); another isostructural MOF with a different sensitizing ligand PCN-222-Fe(III)Cl under visible light (blue curve) and PCN-222 with 1O2 scavenger DPBF (purple curve) at 25 °C. BPA initial concentration:100 ppm; the quantity of MOFs: 1.0 mg; pH: 8.0; solution volume: 1.0 mL.

The intermediate products in the process of photocatalytic degradation were screened using GC-MS analysis. In addition to the peak of BPA at m/z 213, one intermediate ion was discovered with m/z 108. The retention time of 5.158 min for the intermediate product with m/z 108 was significantly different from BPA (13.296 min) on HP-5 GC column. The intermediate product was identified as 1,4-benzoquinone by NIST database (Figure S7). To further confirm the intermediate and the catalytic pathway, the mass of BPA and 1,4-benzoquinone in the solution phase and adsorbed by PCN-222 were monitored with different irradiation time, respectively (Figure S8). The equilibrium concentration of the intermediate in aqueous solution reached the maximum after 20 min-irradiation, then it gradually decreased and tended to be constant. From Figure S8b, it can be seen that the trend of intermediate concentration in PCN-222 was similar to aqueous solution (Figure S8a) and the amount of intermediate in aqueous solution was higher than that extraction from PCN-222. This suggests that the intermediate of 1,4-benzoquinone formed in PCN-222 channels in the process of photocatalytic degradation and diffused from the channel into the aqueous solution.

To evaluate the effect of visible light irradiation, catalysis under dark condition was performed as control experiment and the results were shown as black curve in Fig. 4. No significant catalysis was observed under dark conditions within 120 min. The quantity of BPA in PCN-222 under dark conditions was 0.1 ± 0.007 mg and from 100 ppm BPA aqueous solution (1 mL), showing good recovery. The significant errors come from the extraction procedures of BPA from heterogeneous PCN-222 before GC analysis. Normalized data were shown to justify the comparison.

The porphyrinic MOFs are capable of generating 1O2 under photo irradiation for the oxidation of chemical warfare agent37. For PCN-222, the degradation of BPA could be effective due to the direct oxidation by 1O2 in the presence of visible light. The observation of only m/z 108 (1,4-benzoquinone) and no hydroxylated products were observed in the reaction process which may suggest that the reaction is not based on other free radicals73. Based on the results above, the process of photodegradation of BPA by PCN-222 is the direct oxidation by 1O2, which is generated from PCN-222 under visible light irradiation (Figure S5). As previously reported, the final products of 1O2 oxidation of BPA were CO2 and H2O71. It is highly practical in the water treatment for BPA oxidation by 1O2 since it is green and the final products would be CO2 and H2O.

Explore the catalytic mechanism by visible light photocatalytic degradation of BPA with PCN-222-Fe(III)Cl and TCPP ligand

Porphyrin as the photosensitizer have been extensively employed for 1O2 generation. In order to verify the catalytic mechanism, instead of TCPP, we synthesized another porphyrin ligand, iron(III) porphyrin chloride to form MOF PCN-222-Fe(III)Cl, which works as Fenton’s reagent for Type I catalysis pathway by generating hydroxyl radical53. We used PCN-222-Fe(III)Cl as catalyst to establish photocatalytic degradation of BPA under the same conditions as performed with PCN-222. No significant catalytic degradation of BPA under visible light irradiation was observed on PCN-222-Fe(III)Cl (blue curve in Fig. 4), at the same time, no intermediate (m/z 108, 1,4-benzoquinone) was detected during the photocatalytic process (Figure S9). To further confirm the role of porphyrin, it was found that BPA can also be rapidly degraded by only TCPP ligand (Figure S10), which proved that the degradation of BPA mainly occurs on the site of TCPP ligand in PCN-222. It is reasonable that PCN-222 with 3-D structure has better performance of high adsorption capacity and good stability comparing with TCPP ligand.

Explore the catalytic mechanism with 1O2 scavenger

To further confirm the 1O2 generation ability of TCPP in PCN-222, we choose 1,3-diphenylisobenzofuran (DPBF) as the 1O2 scavenger38. The absorbance of DPBF at λ = 410 nm would decrease when DPBF was oxidized by 1O2, which acted as a specific indicator of 1O2 generation. As shown in Fig. 5, the absorbance of DPBF (60 µM) in acetonitrile with PCN-222 at λ = 410 nm was rapidly decreased within 150 seconds under visible light irradiation, while the absorbance was kept without PCN-222 under the same irradiation as a control experiment. The control experiment in dark was also performed. It indicates PCN-222 is an excellent photosensitizer for generating 1O2. To well explore the reaction mechanism and further confirm the effect of 1O2, DPBF was added to eliminate 1O2 during the photodegradation. To guarantee the successful removal of 1O2, the 100 ppm BPA aqueous solution was first bubbled with nitrogen for 30 minutes. Then 10 µL DPBF acetonitrile solution of 1 mol L−1 was added to the catalytic solution after adsorption equilibrium with PCN-222. It can be observed from purple curve in Fig. 4 that the quality of BPA with the adding of DPBF was almost unchanged within 30 min under visible light irradiation compared to that without adding of DPBF. No intermediate products were detected during the first five minute (Figure S11). The photocatalytic degradation with DPBF was monitored for only 30 min because DPBF is unstable and sensitive to the external factors such as UV light and heat. It indicated that 1O2 generated by PCN-222 under visible light was shown to be an effective degradation reagent for BPA.

Figure 5
figure 5

(a) Absorbance decay of the reacted DPBF solution. (b) The corresponding spectra in the presence of PCN-222. In every experiment, 2 mg PCN-222 was added to 10 mL the initial concentration of 60 µM DPBF acetonitrile solution (with O2 bubbled). Visible light irradiation conditions: wavelength range of 480–700 nm.

Stability of PCN-222 under visible light irradiation

The stability of PCN-222 was investigated by recycling experiment. After the end of each adsorption-photocatalytic experiment, PCN-222 was recovered by centrifugation and then applied to the next adsorption-photocatalytic degradation experiment. After five cycles, the removal efficiency of PCN-222 still keeps at 99.2% for the adsorption-degradation of BPA (Figure S12). The PCN-222 after five cycles still keeps its rod-like shape and micrometer-scale size (Fig. 1d). The results indicated that PCN-222 has a stable and efficient catalytic performance for removal of BPA by combined action of adsorption and degradation under visible light irradiation.


In this work, Zr-porphyrin MOF PCN-222 was utilized as a dual function material for the adsorption and photocatalytic degradation of BPA under visible light irradiation. PCN-222 exhibits ultrahigh removal efficiency of BPA from aqueous phase and the maximum adsorption capacity is up to 487.69 ± 8.37 mg g−1. In addition, PCN-222 maintained the high adsorption capacity as well as chemical stability with wide pH range of 2–10. Under visible light irradiation, PCN-222 was demonstrated to generate 1O2, which presents excellent degradation performance towards BPA. More importantly, the permanent porosities and the high surface areas of PCN-222 can enhance the enrichment of BPA, thereby accelerating the catalytic process. We believe that the recyclable and environment-friendly PCN-222 with such superior performance will have a broad application in the removal and degradation of water pollutants.


Synthesis of PCN-222

For a typical preparation of PCN-222, ZrCl4 (50 mg), H2TCPP (50 mg) and benzoic acid (2700 mg) in 8 mL of DEF were ultrasonically dissolved in a 20 mL Teflon-lined autoclave. The mixture was heated at 120 °C for 48 h and then 130 °C for 24 h. After cooling down to room temperature, purple needle shaped crystals were harvested by centrifugation (12000 rpm) after 3 min. For the activation procedure, the obtained as-synthesized PCN-222 was suspended in a solution of 1.5 mL of 4 M HCl in 100 mL DMF and stirred at 120 °C for 12 h. Afterwards, the sample was centrifuged and washed for three times sequentially with DMF and acetone. Then the sample was dispersed in 100 mL acetone for 24 h and the sample was isolated by centrifugation (12000 rpm). Finally, the sample was dried in vacuum for 12 h at 120 °C.

Sorption assay

For exploring the adsorption ability of PCN-222 for BPA, we prepared 100 ppm and 250 ppm BPA aqueous solutions which were prepared the volume ratio of ethanol and water was 1:249 and 5:245, respectively. The adsorption experiments were carried out by added different amounts of PCN-222 in a serious of 1.0 mL BPA solution (100 ppm and 250 ppm) in 2.0 mL screw vial at room temperature in darkness. At given time intervals, in order to determine BPA concentration in solution phase, samples were filtered with 25 mm × 0.22 μm filter membranes. Then 1.0 mL dichloromethane was added to the residual BPA solution and well mixed to extract the BPA. Finally, 1 μL of BPA in dichloromethane was injected to GC-MS for quantitative analysis with SIM mode of m/z 213 for BPA. The amount of BPA adsorbed on the adsorbent, q e (mg g−1) at equilibrium and q t (mg g−1) at time t, respectively were calculated according to the following formula:


in which C 0 and C e are the initial and the equilibrium concentrations of BPA (mg L−1), respectively, C t (mg L−1) is the concentration of BPA at time t, V (L) is the volume of the BPA solution, and m (g) is the quantity of adsorbent.

$${\rm{Freundlich}}\,{\rm{model}}:{q}_{e}={K}_{F}\times {c}_{e}^{\frac{1}{{\rm{n}}}}$$

in which q e is the equilibrium adsorption capacity (mg g−1) while C e is the equilibrium concentrations of BPA (mg L−1). q m is the Langmuir monolayer maximum sorption capacity (mg g−1) while b is the Langmuir constant (L mg−1). K F (mg g−1) and 1/n are the capacity and intensity of sorption Freundlich constants, respectively.

Degradation experiments

The photocatalytic degradation of BPA by PCN-222 under visible light irradiation experiment was carried out in 2 mL screw vials under the light intensity of 109.2 mW·cm−2. After PCN-222 absorb BPA reaching the adsorption equilibrium, the samples were exposed to visible light, which was provided by a Xenon lamp (75 mV, 15 A) filtered from 400 nm to 700 nm. To fully elucidate the degradation efficiency, both the BPA concentration in aqueous solution and the residual BPA quantity within PCN-222 were monitored at certain time intervals after irradiation. For the determination of BPA concentrations in solution, the method is same as which used in sorption assay. For the quantitative analysis of BPA adsorbed in MOF, the solids were first filtered through 25 mm × 0.22 μm membrane, 0.5 mL of ethanol was used to wash twice for MOFs in the filter. Finally, 1 μL of BPA in ethanol was injected to GC-MS for quantitative analysis with SIM mode of m/z 213 for BPA. For the analysis of intermediates of BPA degradation, GC-MS with scan mode was employed. Normalization was performed according to the average recovery rate for the quantitation of BPA washed from MOFs.


  1. 1.

    Millward, A. R. & Yaghi, O. M. Metal−Organic Frameworks with Exceptionally High Capacity for Storage of Carbon Dioxide at Room Temperature. J. Am. Chem. Soc. 127, 17998–17999 (2005).

    CAS  Article  PubMed  Google Scholar 

  2. 2.

    Li, J.-R., Kuppler, R. J. & Zhou, H.-C. Selective gas adsorption and separation in metal- organic frameworks. Chem. Soc. Rev. 38, 1477–1504 (2009).

    CAS  Article  PubMed  Google Scholar 

  3. 3.

    Czaja, A. U., Trukhan, N. & Muller, U. Industrial applications of metal-organic frameworks. Chem. Soc. Rev. 38, 1284–1293 (2009).

    CAS  Article  PubMed  Google Scholar 

  4. 4.

    Hu, Z., Deibert, B. J. & Li, J. Luminescent metal-organic frameworks for chemical sensing and explosive detection. Chem. Soc. Rev. 43, 5815–5840 (2014).

    CAS  Article  PubMed  Google Scholar 

  5. 5.

    Chen, B., Xiang, S. & Qian, G. Metal−Organic Frameworks with Functional Pores for Recognition of Small Molecules. Acc. Chem. Res. 43, 1115–1124 (2010).

    CAS  Article  PubMed  Google Scholar 

  6. 6.

    Gascon, J. et al. Metal Organic Framework Catalysis: Quo vadis? ACS Catalysis 4, 361–378 (2014).

    CAS  Article  Google Scholar 

  7. 7.

    Farrusseng, D., Aguado, S. & Pinel, C. Metal-Organic Frameworks: Opportunities for Catalysis. Angew. Chem. Int. Ed. 48, 7502–7513 (2009).

    CAS  Article  Google Scholar 

  8. 8.

    Zhu, Q.-L. et al. Metal-Organic Framework-Derived Honeycomb-Like Open Porous Nanostructures as Precious-Metal-Free Catalysts for Highly Efficient Oxygen Electroreduction. Adv. Mater. 28, 6391–6398 (2016).

    CAS  Article  PubMed  Google Scholar 

  9. 9.

    Janiak, C. Engineering coordination polymers towards applications. Dalton Trans. 2781–2804 (2003).

  10. 10.

    Ma, L., Abney, C. & Lin, W. Enantioselective catalysis with homochiral metal-organic frameworks. Chem. Soc. Rev. 38, 1248–1256 (2009).

    CAS  Article  PubMed  Google Scholar 

  11. 11.

    An, B. et al. Confinement of Ultrasmall Cu/ZnOx Nanoparticles in Metal–Organic Frameworks for Selective Methanol Synthesis from Catalytic Hydrogenation of CO2. J. Am. Chem. Soc. 139, 3834–3840 (2017).

    CAS  Article  PubMed  Google Scholar 

  12. 12.

    Lin, Z.-J., Lu, J., Hong, M. & Cao, R. Metal-organic frameworks based on flexible ligands (FL-MOFs): structures and applications. Chem. Soc. Rev. 43, 5867–5895 (2014).

    CAS  Article  PubMed  Google Scholar 

  13. 13.

    Seo, P. W. et al. Adsorptive Removal of Pharmaceuticals and Personal Care Products from Water with Functionalized Metal-organic Frameworks: Remarkable Adsorbents with Hydrogen-bonding Abilities. Sci. Rep. 6, 34462 (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  14. 14.

    Zhai, Q.-G. et al. An ultra-tunable platform for molecular engineering of high-performance crystalline porous materials. Nature Commun. 7, 13645 (2016).

    ADS  CAS  Article  Google Scholar 

  15. 15.

    Yang, H. et al. Catalytically Active Bimetallic Nanoparticles Supported on Porous Carbon Capsules Derived From Metal–Organic Framework Composites. J. Am. Chem. Soc. 138, 11872–11881 (2016).

    CAS  Article  PubMed  Google Scholar 

  16. 16.

    Li, J.-R. et al. Porous materials with pre-designed single-molecule traps for CO2 selective adsorption. Nature Commun. 4, 1538 (2013).

    Article  Google Scholar 

  17. 17.

    Wang, B. et al. Highly Stable Zr(IV)-Based Metal-Organic Frameworks for the Detection and Removal of Antibiotics and Organic Explosives in Water. J. Am. Chem. Soc. 138, 6204–6216 (2016).

    CAS  Article  PubMed  Google Scholar 

  18. 18.

    Han, Y. et al. Size-exclusive and coordination-induced selective dye adsorption in a nanotubular metal-organic framework. J. Mater. Chem. A 3, 12804–12809 (2015).

    CAS  Article  Google Scholar 

  19. 19.

    Wang, B. et al. Tuning CO2 selective adsorption over N2 and CH4 in UiO-67 analogues through ligand functionalization. Inorg. Chem. 53, 9254–9259 (2014).

    CAS  Article  PubMed  Google Scholar 

  20. 20.

    Zhang, Y. et al. Preparation of Nanofibrous Metal–Organic Framework Filters for Efficient Air Pollution Control. J. Am. Chem. Soc. 138, 5785–5788 (2016).

    CAS  Article  PubMed  Google Scholar 

  21. 21.

    Chen, Y. et al. Roll-to-Roll Production of Metal-Organic Framework Coatings for Particulate Matter Removal. Adv. Mater. doi:10.1002/adma.201606221 (2017).

  22. 22.

    Deleu, W. P. R. et al. Metal–Organic Frameworks Encapsulated in Photocleavable Capsules for UV-Light Triggered Catalysis. Chem. Mater. 27, 5495–5502 (2015).

    CAS  Article  Google Scholar 

  23. 23.

    Gomes Silva, C. et al. Water Stable Zr–Benzenedicarboxylate Metal–Organic Frameworks as Photocatalysts for Hydrogen Generation. Chem. Eur. J. 16, 11133–11138 (2010).

    Article  PubMed  Google Scholar 

  24. 24.

    Meyer, K., Ranocchiari, M. & van Bokhoven, J. A. Metal organic frameworks for photo-catalytic water splitting. Energy Environ. Sci. 8, 1923–1937 (2015).

    CAS  Article  Google Scholar 

  25. 25.

    Zhang, T. & Lin, W. Metal-organic frameworks for artificial photosynthesis and photocatalysis. Chem. Soc. Rev. 43, 5982–5993 (2014).

    CAS  Article  PubMed  Google Scholar 

  26. 26.

    Wang, C., Xie, Z., deKrafft, K. E. & Lin, W. Doping Metal–Organic Frameworks for Water Oxidation, Carbon Dioxide Reduction, and Organic Photocatalysis. J. Am. Chem. Soc. 133, 13445–13454 (2011).

    CAS  Article  PubMed  Google Scholar 

  27. 27.

    Fu, Y. et al. An Amine-Functionalized Titanium Metal–Organic Framework Photocatalyst with Visible-Light-Induced Activity for CO2 Reduction. Angew. Chem. Int. Ed. 51, 3364–3367 (2012).

    CAS  Article  Google Scholar 

  28. 28.

    Xu, H.-Q. et al. Visible-Light Photoreduction of CO2 in a Metal–Organic Framework: Boosting Electron–Hole Separation via Electron Trap States. J. Am. Chem. Soc. 137, 13440–13443 (2005).

    Article  Google Scholar 

  29. 29.

    Chen, J. et al. In Rational design of a receptor-targeted photodynamic molecular beacon for the multilevel control of singlet oxygen production and PDT activity in cancer cells. pp 644906-644906-9 (2007).

  30. 30.

    Zhu, T.-C. & Finlay, J. C. The role of photodynamic therapy (PDT) physics. Med. Phys. 35, 3127–3136 (2008).

    CAS  Article  PubMed Central  Google Scholar 

  31. 31.

    DeRosa, M. C. & Crutchley, R. J. Photosensitized singlet oxygen and its applications. Chem. Rev. 233–234, 351–371 (2002).

    Google Scholar 

  32. 32.

    Gorman, A. et al. In Vitro Demonstration of the Heavy-Atom Effect for Photodynamic Therapy. J. Am. Chem. Soc. 126, 10619–10631 (2004).

    CAS  Article  PubMed  Google Scholar 

  33. 33.

    Nyman, E. S. & Hynninen, P. H. Research advances in the use of tetrapyrrolic photosensitizers for photodynamic therapy. J. Photochem. Photobiol. B. 73, 1–28 (2005).

    Article  Google Scholar 

  34. 34.

    Mostafa, S. & Rosario-Ortiz, F. L. Singlet Oxygen Formation from Wastewater Organic Matter. Environ. Sci. Technol. 47, 8179–8186 (2013).

    ADS  CAS  Article  PubMed  Google Scholar 

  35. 35.

    Ryan, C. C., Tan, D. T. & Arnold, W. A. Direct and indirect photolysis of sulfamethoxazole and trimethoprim in wastewater treatment plant effluent. Water Res. 45, 1280–1286 (2011).

    CAS  Article  PubMed  Google Scholar 

  36. 36.

    Razavi, B., Ben Abdelmelek, S., Song, W., O’Shea, K. E. & Cooper, W. J. Photochemical fate of atorvastatin (lipitor) in simulated natural waters. Water Res. 45, 625–631 (2011).

    CAS  Article  PubMed  Google Scholar 

  37. 37.

    Liu, Y., Howarth, A. J., Hupp, J. T. & Farha, O. K. Selective Photooxidation of a Mustard-Gas Simulant Catalyzed by a Porphyrinic Metal–Organic Framework. Angew. Chem. Int. Ed. 54, 9001–9005 (2015).

    CAS  Article  Google Scholar 

  38. 38.

    Park, J., Feng, D., Yuan, S. & Zhou, H.-C. Photochromic Metal–Organic Frameworks: Reversible Control of Singlet Oxygen Generation. Angew. Chem. Int. Ed. 54, 430–435 (2015).

    CAS  Article  Google Scholar 

  39. 39.

    Lemp, E., Cañete, A., Günther, G., Pizarro, N. & Zanocco, A. L. Photosensitized generation of singlet molecular oxygen by aryloxazinones. J. Photochem. Photobiol. A. 199, 345–352 (2008).

    CAS  Article  Google Scholar 

  40. 40.

    Baier, J. et al. Theoretical and experimental analysis of the luminescence signal of singlet oxygen for different photosensitizers. J. Photochem. Photobiol. B. 87, 163–173 (2007).

    CAS  Article  PubMed  Google Scholar 

  41. 41.

    Apel, K. & Hirt, H. Reactive oxygen species: metabolism, oxidative stress, and signal transduction. Ann. Rev. Plant. Biol. 55, 373–399 (2004).

    CAS  Article  Google Scholar 

  42. 42.

    DeRosa, M. C. & Crutchley, R. J. Photosensitized singlet oxygen and its applications. Coord. Chem. Rev. 233–234, 351–371 (2002).

    Article  Google Scholar 

  43. 43.

    Aubry, J. M. & Bouttemy, S. Preparative Oxidation of Organic Compounds in Microemulsions with Singlet Oxygen Generated Chemically by the Sodium Molybdate/Hydrogen Peroxide System1. J. Am. Chem. Soc. 119, 5286–5294 (1997).

    CAS  Article  Google Scholar 

  44. 44.

    Janssen, E. M. L., Erickson, P. R. & McNeill, K. Dual roles of dissolved organic matter as sensitizer and quencher in the photooxidation of tryptophan. Environ. Sci. Technol. 48, 4916–4924 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  45. 45.

    Guo, X. et al. Enhanced photocatalytic performance of N-nitrosodimethylamine on TiO2 nanotube based on the role of singlet oxygen. Chemosphere 120, 521–526 (2015).

    CAS  Article  PubMed  Google Scholar 

  46. 46.

    Zhang, D. et al. Role of oxygen active species in the photocatalytic degradation of phenol using polymer sensitized TiO2 under visible light irradiation. J. Hazard. Mater. 163, 843–847 (2009).

    CAS  Article  PubMed  Google Scholar 

  47. 47.

    Stylidi, M., Kondarides, D. I. & Verykios, X. E. Visible light-induced photocatalytic degradation of Acid Orange 7 in aqueous TiO2 suspensions. Appl. Catal. B-Environ 47, 189–201 (2004).

    CAS  Article  Google Scholar 

  48. 48.

    Zenkevich, E. I. et al. Quantitative Analysis of Singlet Oxygen (1O2) Generation via Energy Transfer in Nanocomposites Based on Semiconductor Quantum Dots and Porphyrin Ligands. J. Phys. Chem. C 115, 21535–21545 (2011).

    CAS  Article  Google Scholar 

  49. 49.

    Dědic, R., Kořínek, M., Molnár, A., Svoboda, A. & Hála, J. Singlet oxygen quenching by oxygen in tetraphenyl-porphyrin solutions. J. Lumin. 119–120, 209–213 (2006).

    Article  Google Scholar 

  50. 50.

    Ravanat, J. L., Cadet, J., Araki, K. & Mascio, P. D. Supramolecular cationic tetraruthenated porphyrin and light-induced decomposition of 2′-deoxyguanosine predominantly via a singlet oxygen-mediated mechanism. Photochem. Photobiol. 68, 698–702 (1998).

    CAS  PubMed  Google Scholar 

  51. 51.

    Fiel, R. J. Porphyrin—Nucleic acid interactions: A review. Biomol. Struct. Dyn. 6, 1259–1274 (1989).

    CAS  Article  Google Scholar 

  52. 52.

    Pineiro, M. et al. Photoacoustic measurements of porphyrin triplet-state quantum yields and singlet-oxygen efficiencies. Chem. Eur. J. 4, 2299–2307 (1998).

    CAS  Article  Google Scholar 

  53. 53.

    Feng, D. et al. Zirconium-Metalloporphyrin PCN-222: Mesoporous Metal–Organic Frameworks with Ultrahigh Stability as Biomimetic Catalysts. Angew. Chem. Int. Ed. 51, 10307–10310 (2012).

    CAS  Article  Google Scholar 

  54. 54.

    Sun, Y., Sun, L., Feng, D. & Zhou, H.-C. An In Situ One-Pot Synthetic Approach towards Multivariate Zirconium MOFs. Angew. Chem. Int. Ed. 55, 6471–6475 (2016).

    CAS  Article  Google Scholar 

  55. 55.

    Yuan, S. et al. Thermodynamically Guided Synthesis of Mixed-Linker Zr-MOFs with Enhanced Tunability. J. Am. Chem. Soc. 138, 6636–6642 (2016).

    CAS  Article  PubMed  Google Scholar 

  56. 56.

    Khan, N. A., Hasan, Z. & Jhung, S. H. Adsorptive removal of hazardous materials using metal-organic frameworks (MOFs): A review. J. Hazard. Mater. 244–245, 444–456 (2013).

    Article  PubMed  Google Scholar 

  57. 57.

    Wang, J.-L., Wang, C. & Lin, W. Metal–Organic Frameworks for Light Harvesting and Photocatalysis. ACS Catalysis 2, 2630–2640 (2012).

    CAS  Article  Google Scholar 

  58. 58.

    Liu, Y., Moon, S.-Y., Hupp, J. T. & Farha, O. K. Dual-Function Metal–Organic Framework as a Versatile Catalyst for Detoxifying Chemical Warfare Agent Simulants. ACS Nano 9, 12358–12364 (2015).

    CAS  Article  PubMed  Google Scholar 

  59. 59.

    Farha, O. K., Shultz, A. M., Sarjeant, A. A., Nguyen, S. T. & Hupp, J. T. Active-Site-Accessible, Porphyrinic Metal−Organic Framework Materials. J. Am. Chem. Soc. 133, 5652–5655 (2011).

    CAS  Article  PubMed  Google Scholar 

  60. 60.

    Zhao, F. Y. et al. Zn(ii) porphyrin based nano-/microscale metal-organic frameworks: morphology dependent sensitization and photocatalytic oxathiolane deprotection. RSC Advances 6, 26199–26202 (2016).

    CAS  Article  Google Scholar 

  61. 61.

    UNEP/WHO. State of the science of endocrine disrupting chemicals—2012. Geneva, Switzerland, United Nations Environment Programme/World Health Organization (2012).

  62. 62.

    Zhou, M. et al. The removal of bisphenol A from aqueous solutions by MIL-53(Al) and mesostructured MIL-53(Al). J. Colloid Interf. Sci. 405, 157–163 (2013).

    ADS  CAS  Article  Google Scholar 

  63. 63.

    Qin, F.-X., Jia, S.-Y., Liu, Y. & Wu, S.-H. Adsorptive removal of bisphenol A from aqueous solution using metal-organic frameworks. Desalin. Water Treat. 54, 93–102 (2015).

    CAS  Article  Google Scholar 

  64. 64.

    Zeng, T., Zhang, X., Wang, S., Niu, H. & Cai, Y. Spatial Confinement of a Co3O4 Catalyst in Hollow Metal–Organic Frameworks as a Nanoreactor for Improved Degradation of Organic Pollutants. Environ. Sci. Technol. 49, 2350–2357 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  65. 65.

    Ha, D. O. et al. Effects of Riboflavin Photosensitization on the Degradation of Bisphenol A (BPA) in Model and Real-Food Systems. J. Food Sci. 74, C380–C384 (2009).

    CAS  Article  PubMed  Google Scholar 

  66. 66.

    Zhan, M., Yang, X., Xian, Q. & Kong, L. Photosensitized degradation of bisphenol A involving reactive oxygen species in the presence of humic substances. Chemosphere 63, 378–386 (2006).

    CAS  Article  PubMed  Google Scholar 

  67. 67.

    Vandenberg, L. N., Hauser, R., Marcus, M., Olea, N. & Welshons, W. V. Human exposure to bisphenol A (BPA). Reprod. Toxicol. 24, 139–177 (2007).

    CAS  Article  PubMed  Google Scholar 

  68. 68.

    Deibert, B. J. & Li, J. A distinct reversible colorimetric and fluorescent low pH response on a water-stable zirconium-porphyrin metal-organic framework. Chem. Commun. 50, 9636–9639 (2014).

    CAS  Article  Google Scholar 

  69. 69.

    Huang, Y.-Q. et al. Bisphenol A (BPA) in China: A review of sources, environmental levels, and potential human health impacts. Environ. Int. 42, 91–99 (2012).

    CAS  Article  PubMed  Google Scholar 

  70. 70.

    Huo, S.-H. & Yan, X.-P. Metal-organic framework MIL-100(Fe) for the adsorption of malachite green from aqueous solution. J. Mater. Chem. 22, 7449–7455 (2012).

    CAS  Article  Google Scholar 

  71. 71.

    Ding, Y., Xia, X., Ruan, Y. & Tang, H. In situ H+-mediated formation of singlet oxygen from NaBiO3 for oxidative degradation of bisphenol A without light irradiation: Efficiency, kinetics, and mechanism. Chemosphere 141, 80–86 (2015).

    CAS  Article  PubMed  Google Scholar 

  72. 72.

    Xiao, X. et al. One-pot solvothermal synthesis of three-dimensional (3D) BiOI/BiOCl composites with enhanced visible-light photocatalytic activities for the degradation of bisphenol-A. J. Hazard. Mater. 233–234, 122–130 (2012).

    Article  PubMed  Google Scholar 

  73. 73.

    Wang, C., Zhang, H., Li, F. & Zhu, L. Degradation and Mineralization of Bisphenol A by Mesoporous Bi2WO6 under Simulated Solar Light Irradiation. Environ. Sci. Technol. 44, 6843–6848 (2010).

    ADS  CAS  Article  PubMed  Google Scholar 

  74. 74.

    Guo, C. et al. Directed Synthesis of Mesoporous TiO2 Microspheres: Catalysts and Their Photocatalysis for Bisphenol A Degradation. Environ. Sci. Technol. 44, 419–425 (2010).

    ADS  CAS  Article  PubMed  Google Scholar 

  75. 75.

    Katsumata, H., Kawabe, S., Kaneco, S., Suzuki, T. & Ohta, K. Degradation of bisphenol A in water by the photo-Fenton reaction. J. Photochem. Photobiol. A. 162, 297–305 (2004).

    CAS  Article  Google Scholar 

Download references


This work was financially supported by NSFC (No. 21505076), Young Elite Scientist Sponsorship Program by CAST (No. 2015QNRC001), the program of Jiangsu Specially-Appointed Professor, the NSF of Jiangsu Province of China (No. BK20150967), the program of Jiangsu Province Innovation Team, the Priority Academic Program Development of Jiangsu Higher Education Institutions.

Author information




Zhi-Yuan Gu and Ai-Na Meng prepared the main manuscript text. Ling-Xiao Chaihu and Huan-Huan Chen helped in synthesizing of tetrakis (4-carboxyphenyl) porphyrin (H2TCPP) ligand.

Corresponding author

Correspondence to Zhi-Yuan Gu.

Ethics declarations

Competing Interests

The authors declare that they have no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Meng, AN., Chaihu, LX., Chen, HH. et al. Ultrahigh adsorption and singlet-oxygen mediated degradation for efficient synergetic removal of bisphenol A by a stable zirconium-porphyrin metal-organic framework. Sci Rep 7, 6297 (2017).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing