Thermoelectric power generation can play a key role in a sustainable energy future by converting waste heat from power plants and other industrial processes into usable electrical power. Current thermoelectric devices, however, require energy intensive manufacturing processes such as alloying and spark plasma sintering. Here, we describe the fabrication of a p-type thermoelectric material, copper selenide (Cu2Se), utilizing solution-processing and thermal annealing to produce a thin film that achieves a figure of merit, ZT, which is as high as its traditionally processed counterpart, a value of 0.14 at room temperature. This is the first report of a fully solution-processed nanomaterial achieving performance equivalent to its bulk form and represents a general strategy to reduce the energy required to manufacture advanced energy conversion and harvesting materials.
We are in urgent need of strategies for sustainable manufacturing, particularly for sectors related to energy production and storage1. The U.S. Department of Energy 2015 Quadrennial Technology Review (QTR)2 highlights a number of challenges to be overcome as well as approaches to be followed that will be necessary to bring about a more sustainable energy and manufacturing future. There are many approaches to minimizing the amount of energy and material wasted during manufacturing, including the reduction of processing temperatures as well as the number of heating steps, increased use of additive manufacturing techniques, production of combined heat and power systems, development of more efficient direct energy conversion materials, and deployment of widely distributed sensor networks for real time process monitoring and control. Thermoelectric power generators (TEGs) are solid-state, direct heat to electrical energy devices that can address the above issues in multiple ways. Firstly, the broad deployment of TEG-powered sensors in industrial facilities can provide more real-time process information. And secondly, improvements in the manufacture of TEGs themselves is necessary to facilitate their broader application.
Current state-of-the-art TEG devices are made of rare and/or toxic elements, such as tellurium, bismuth, and lead and are produced using wasteful and labor-intensive manufacturing techniques2. The composition and processing of the TEG material we describe in this work addresses both of these shortcomings. The constituent elements we use, copper and selenium, are relatively Earth-abundant and relatively non-toxic. The manufacture of current TEG components involves a series of energy-intensive processing steps including high temperature alloying, ball milling, and spark plasma sintering. For example, the production of bulk Cu2Se involves alloying the material at temperatures above 700 °C for more than a week and spark plasma sintering the material at a temperature above 400 °C while applying mechanical pressure of 65 MPa3. Once blocks of the material are produced, they are sawn into small pieces, resulting in a significant amount of kerf waste, and then assembled by hand into the final devices2. The nanocrystal solution we study lends itself to solution-processing based fabrication techniques and is therefore amenable to additive manufacturing processes which waste very little active material.
While the possibility of solution processed manufacturing of TEGs is exciting, one must not neglect the fundamental performance of the active materials. In the case of thermoelectric materials, material performance is most frequently assessed with the figure of merit, ZT = S 2 σT/κ, where S is the Seebeck coefficient, σ is the electrical conductivity, T is the absolute temperature, and κ is the thermal conductivity. As we can see from the ZT formula, an ideal material would be a poor heat conductor and a good electrical conductor, properties that are captured by the so-called “phonon glass, electron crystal” concept advanced by Slack and coworkers4, 5. One of the most confounding problems in maximizing ZT is the inherent coupling of thermal and electrical conductivities: materials with good electrical conductivity tend to have high thermal conductivity as well. Historically, a common strategy has been to engineer crystal domain sizes to scatter as many long mean free path (>100 nm) phonons6 without infringing on the transport of relatively short mean free path (<10 nm) charge carriers. Towards this end, researchers aiming to improve the thermoelectric performance of different materials incorporate nanoscale features such as grain boundaries to enhance scattering of long mean free path phonons without greatly perturbing the transport of shorter mean free path electrons7,8,9,10,11,12.
Since its emergence in the early 1990s, colloidal synthesis of nanocrystals has been regarded as a promising way to make device building blocks because of the exquisite control over composition, size, shape, and crystallographic phase it provides13. Indeed, the proliferation of recipes for metallic and semiconducting nanocrystals we have witnessed over the past few decades has enabled the solution-processing based manufacture of a wide variety of inorganic and inorganic/organic hybrid materials10. Examples in the literature are abundant and include reports of photovoltaics14,15,16 and other optoelectronic devices17, 18, electronic devices such as field-effect transistors19,20,21,22, and, of particular relevance to this work, thermoelectrics8, 12, 23,24,25,26,27,28.
In addition to potential economic and manufacturing efficiency gains, solution processing lends itself to the production of devices that are of arbitrary geometry and mechanically flexible. In the case of thermoelectrics, novel geometries and flexibility will broaden the horizon for the application of thermoelectric power generators, assuming efficient heat exchangers can be applied2, 8. An already emerging market of devices that utilize TEGs is body-powered electronics such as watches, as well as devices for medical monitoring and diagnostics29, 30. While traditionally manufactured TEGs are generally rigid and flat, some efforts have been made to manufacture flexible devices using pixelated, paneled devices, but at the expense of several additional processing steps31, 32. The direct, bottom-up production of TEGs that solution processing enables is actively being developed in our and other groups22, 23, 33,34,35.
In this manuscript, we describe the synthesis and thermoelectric properties of copper selenide (Cu2Se) nanocrystals which combine the advantages of solution processing with the benefits of an inherently nanostructured material. Ultimately, we demonstrate that solution-processed thin films of these nanocrystals achieve a material ZT of 0.14 at room temperature, which is as high as their bulk counterparts3, which also have a ZT of 0.14 at 290 K, while exploiting solution processing and mild thermal annealing.
Synthesis of Cu2Se Nanocrystals
Cu2Se nanocrystals were synthesized via a modified version of a previously published protocol36; the details of our protocol are described in the methods section. The product of our synthesis is a suspension of oleylamine-coordinated nanocrystals in hexane. The Cu2Se nanocrystals have an average diameter of 12 +/− 1 nm, as determined from analysis of low-resolution TEM images.
The particles themselves are crystalline, as evidenced by the lattice fringes visible under high-resolution TEM imaging (see Fig. 1j). While we refer to our copper selenide particles as stoichiometric (Cu2Se), copper selenide actually has a stable monoclinic structure in compositions ranging from Cu2Se to Cu1.8Se. We are confident that our material is in the monoclinic phase because the XRD pattern matches the monoclinic structure determined by Gulay et al. (see Fig. 1a)37. Furthermore, by comparing the room temperature Hall carrier concentration of our film annealed at 300 °C, n Hall ≈ 9 × 1020 cm−3 (see Supplementary Figure 1), to data in recent work by Kang et al.38, we estimate that our material has a composition of Cu1.94Se, assuming that the concentration of holes is proportional to degree of copper deficiency and that the hole mobility is constant in this range of compositions. In the end, we do not know the precise stoichiometry of our material and will refer to it as Cu2Se in this manuscript.
Thin Film Preparation and Characterization
In order to assess Cu2Se nanocrystals as a thermoelectric material, we spin cast them from a suspension in a mixture of hexane and octane via a multi-step deposition procedure to fabricate uniform and crack-free films that are between 50 and 100 nm thick (see Fig. 2, panels a and b). Our use of a multi-step spin casting procedure is inspired by a technique which has been used to create dense films of lead selenide nanocrystals for photovoltaic applications20.
We then thermally anneal the films for 45 minutes under a N2 atmosphere at a temperature between 100 °C and 600 °C. After annealing, the films are generally reduced in thickness, but remain crack-free (see Fig. 2, panels c and d and Supplementary Figures 2 and 3). Annealing at temperatures up to 200 °C appears to densify the films, but the individual nanocrystals remain visible in the SEM, as can be seen in Fig. 1, panels f-g and in Supplementary Figures 2 and 3. After annealing at temperatures of 300 °C and above, the individual nanocrystals are no longer distinct, as can be seen in the SEM images Fig. 1, panels b-e, and confirmed by the disappearance of the form factor peaks in the low q region of GIWAXS patterns (Supplementary Figure 4). Transmission FTIR spectra shown in Supplementary Figure 13 indicate a significant amount of EDT in the not annealed films and a significant loss of EDT after annealing at 200 °C. Samples annealed at even higher temperatures, 400 °C and 600 °C, show no absorption from EDT, indicating that the ligands have been effectively removed at these elevated annealing temperatures.
While the morphology of the films clearly changes during the annealing procedure, the room temperature crystallographic structure of the material remains consistent through the entire range of annealing temperatures used in this work. The powder XRD spectra shown in Fig. 1a were recorded from drop-cast and annealed samples because the thin films do not scatter strongly enough to get acceptable signal-to-noise ratios on our XRD system. GIWAXS patterns, which were obtained using synchrotron X-rays, confirm that the crystallographic structure of our thin films is maintained throughout the annealing series (see Supplementary Figure 4). The individual nanocrystals appear to merge and grow into larger crystallites with higher annealing temperature, but we cannot estimate the crystallite size from our XRD data because reflections from multiple lattice planes contribute to many of the peaks, as can be seen in Fig. 1a.
The apparent changes in the structure of the films correlate with changes in the measured thermoelectric properties (Fig. 3). The non-annealed and 100 °C annealed samples both have Seebeck coefficients of approximately 80 µV K−1 and have electrical conductivities below 10 S cm−1. The sample annealed at the next higher temperature, 200 °C, displays a roughly 75% drop in the magnitude of the Seebeck coefficient and a greater than two order of magnitude increase in electrical conductivity. This sample is also the lowest annealing temperature sample to lose the form factor fringes in GIWAXS (see Supplementary Figure 4), implying that the material contrast of the particle-particle interfaces has been dramatically reduced.
At the same time as the thermopower and the electrical conductivity, both measured in-plane, are undergoing significant changes, the cross-plane thermal conductivity as measured by time domain thermal reflectance (TDTR) is also changing (Fig. 3c). Annealing the sample at 200 °C results in its thermal conductivity increasing roughly 250%, from 0.4 W m−1 K−1 to 1.4 W m−1 K−1, relative to the 100 °C sample. Interestingly, the thermal conductivity drops as the annealing temperature is raised to 300 °C and beyond. Determining the cause of the behavior of the sample annealed at 200 °C is beyond the scope of this manuscript, but we emphasize that the trends in Fig. 3 are characteristic of films made from Cu2Se nanocrystals, as shown in Supplementary Figure 12. We believe that combining in-plane (Seebeck and electrical conductivity) and cross-plane (thermal conductivity) measurements to compute ZT is valid in this case because our material is built of randomly oriented spherical particles. Ultimately, taking the annealing temperature evolution of the transport parameters into account and computing ZT for our material reveals an optimal annealing temperature of 400 °C for room temperature performance, with a ZT of 0.14 (Fig. 3d).
We have demonstrated that mild thermal annealing can transform a film of isolated nanocrystals into a continuous thin film with thermoelectric properties rivaling those of intensively-processed bulk materials of the same composition. To our knowledge this is the first report of the complete characterization of a fully solution-processed nanocrystalline material that achieves a ZT, 0.14 in this case, as high as its bulk counterpart. These results prove the viability of nanocrystal-based inks as a component of solution-processed, additively-manufactured thermoelectric devices. The further development of this and similar materials will drive the efficient and economical manufacturing of energy harvesting devices which will in turn increase the efficiency of industrial processes.
Cu2Se nanocrystals were synthesized following a slightly modified previously published synthesis36. A solution of copper(I) chloride in oleylamine (OAm) and 1-octadecene (ODE) at 110 °C was injected into a solution of selenium dissolved in the same solvents at a temperature of 310 °C. The reaction was allowed to proceed for 20 minutes at 300 °C. The 12 +/− 1 nm diameter nanocrystals were washed by precipitating with ethanol and resuspended in hexane twice. The nanocrystals were kept in hexane and stored in a N2 glove box for future use.
Thin Film Deposition, Ligand Exchange, and Annealing
Thin films of Cu2Se nanocrystals were prepared by spin casting onto clean, 1 cm × 1 cm substrates (doped silicon for SEM imaging and thermal conductivity or glass for DC conductivity and thermopower) from a 3:2 volume ratio mixture of hexane and octane. Films were produced by pipetting 30 µl of a dilute suspension (~15 mg/ml) of nanocrystals and spinning at 2000 rpm for 30 seconds, resulting in an incomplete monolayer. Ligand-exchanged thin films of Cu2Se were prepared by repeated spin coating of sub-monolayers of OAm-coordinated nanocrystals from a solution of hexane and octane. After each deposition of OAm-coordinated NCs, 60 µl of an ethanedithiol (EDT) solution (1% by volume in acetonitrile, ACN) was pipetted onto the film. The EDT solution was left in contact with the film for approximately 30 seconds while the original OAm ligands were displaced by the EDT ligands. After the ligand exchange step, the film was spun to remove the excess solution and was rinsed once with neat ACN. As a result of the ligand exchange, the nanocrystals in the film were no longer soluble in the original non-polar solvents, allowing for multiple depositions of OAm-coordinated NCs to reach the target thickness. After the target thickness was achieved, the films were annealed at the specified temperature for 45 minutes in a nitrogen glove box.
Powder XRD patterns were recorded using a Bruker AXS D8 Discover GADDS X-Ray Diffractometer using Co K α radiation (λ = 1.789 Å). The reference pattern was calculated with CrystalMaker (CrystalMaker Software Limited) software using the structural parameters from ref. 37.
SEM and TEM Imaging
SEM images were obtained with a Zeiss Gemini Ultra-55 Analytical Field Emission Scanning Electron Microscope operated at 5 kV using an in-lens detector. TEM images were recorded using a JEOL 2100-F Field-Emission Analytical TEM at 200 kV. TEM samples were prepared by placing a single drop of dilute nanocrystal solution onto a TEM grid (400-mesh Cu on ultrathin carbon – Ted Pella 01822-F) and the hexane was allowed to evaporate. Image-J software was used to analyze TEM images to determine the particle size distribution (n = 76).
FTIR Transmission Spectra
FTIR transmission spectra were collected using a Perkin Elmer Spectrum One FT-IR system for a set of four EDT-exchanged films: not annealed, and annealed at 200 °C, 400 °C, and 600 °C. These films were produced in the same manner as the other samples in this study with the exception of the use of a different substrate. Samples for FTIR were spin cast onto undoped double-side polished silicon to allow for collection of spectra in transmission mode. The films were annealed in a nitrogen glovebox. The spectra were recorded in air immediately after removing them from the glovebox.
Thermoelectric Transport Characterization
Before performing electrical and thermoelectric measurements, 100 nm thick gold contacts were thermally evaporated onto each of the four corners of the thin film samples. Sheet resistance for each film was measured in a 4-point Van der Pauw configuration with two Keithley 2400 sourcemeters. Electrical conductivity was determined from the sheet resistance and the thickness for each film. Film thickness was measured from cross section SEM images like those shown in Fig. 2, panels b and d, and in Supplementary Figure 3. Thermopower (Seebeck coefficient) was measured using a homemade probe station which features two Peltier devices (Ferrotec) placed approximately 4 mm apart with a single current passed through the devices in opposite polarities. As a result, one device heats and the other device cools in approximately the same amount relative to room temperature. A thermal gradient was induced in the sample by laying the thin film across the gap between the two devices. Thermal paste (Wakefield Thermal S3 Solutions) was used to ensure good thermal contact. The open circuit voltage that developed was measured using an Agilent 34401 multimeter. The thermal gradient in the sample was monitored with two T-type thermocouples mounted in micromanipulators. For each sample, five different temperature gradients were established and allowed to equilibrate for 200 seconds between temperature changes with 10 voltage measurements taken and averaged at each temperature difference. All samples showed a linear dependence of open circuit voltage on the magnitude of the temperature gradient; this trend was used to extract thermopower values. Homemade LabVIEW programs were used to collect both electrical conductivity and thermopower data. Our Seebeck measurement procedure was verified by measuring the Seebeck coefficient of thermally evaporated nickel films on glass substrates.
Thermal Conductivity Characterization
We measured the cross-plane thermal conductivity of the Cu2Se samples by the time-domain thermoreflectance (TDTR) method39, 40. A mode-locked Ti:Sapphire laser generated a train of pulses at 80 MHz with wavelength centered at 783 nm. The pulses were split into pump and probe beams traveling along different optical paths. The pump beam was modulated at 9.2 MHz by an electro-optic modulator and induced heat excursion on the sample surface, which was interrogated by the time-delayed probe beam. The 1/e2 radius of the focused beam on the sample surface was about 10 μm. Nb0.43V0.57 alloy with thickness around 70 nm was deposited as an optical transducer on the samples by magnetron sputtering. Prior to depositing the optical transducer, the films were coated with 5 nm of Al2O3 via room temperature ALD to protect the samples against oxidation and to physically isolate the nanocrystal film from the transducer layer. The reflected probe beam at the sample surface was detected by a Si photodiode connected to a radio-frequency lock-in amplifier referenced to 9.2 MHz. We compared the ratio of the in-phase voltages to the out-of-phase voltages across time delay with modeling to find the best fit for the thermal conductivity of Cu2Se and the interface thermal conductance. We use the Dulong-Petit limit of heat capacity for Cu2Se, 2.51 J cm−3 K−1, derived from its theoretical molar volume41, in the thermal model. See a summary of the raw data in Supplementary Figures 5–11.
The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.
Chu, S. & Majumdar, A. Opportunities and challenges for a sustainable energy future. Nature 488, 294–303, doi:10.1038/nature11475 (2012).
Quadrennial Technology Review. US DOE Available at: http://energy.gov/sites/prod/files/2015/09/f26/Quadrennial-Technology-Review-2015_0.pdf. (Accessed: 27 October 2016).
Liu, H. et al. Copper ion liquid-like thermoelectrics. Nat. Mater. 11, 422–425, doi:10.1038/nmat3273 (2012).
Slack, G. In CRC Handbook of Thermoelectrics (CRC Press), doi:10.1201/9781420049718.ch34 (1995).
Cohn, J. L., Nolas, G. S., Fessatidis, V., Metcalf, T. H. & Slack, G. A. Glasslike heat conduction in high-mobility crystalline semiconductors. Physical Review Letters 82, 779–782, doi:10.1103/PhysRevLett.82.779 (1999).
Yang, F. & Dames, C. Mean free path spectra as a tool to understand thermal conductivity in bulk and nanostructures. Physical Review B 87, 035437, doi:10.1103/PhysRevB.87.035437 (2013).
Vineis, C. J., Shakouri, A., Majumdar, A. & Kanatzidis, M. G. Nanostructured thermoelectrics: big efficiency gains from small features. Advanced Materials 22, 3970–3980, doi:10.1002/adma.201000839 (2010).
Urban, J. J. Prospects for thermoelectricity in quantum dot hybrid arrays. Nature Nanotechnology 10, 997–1001, doi:10.1038/nnano.2015.289 (2015).
Biswas, K. et al. High-performance bulk thermoelectrics with all-scale hierarchical architectures. Nature 489, 414–418, doi:10.1038/nature11439 (2012).
Cho, E. S. et al. Engineering synergy: energy and mass transport in hybrid nanomaterials. Advanced Materials 27, 5744–5752, doi:10.1002/adma.v27.38 (2015).
Yang, J., Yip, H.-L. & Jen, A. K. Y. Rational design of advanced thermoelectric materials. Advanced Energy Materials 3, 549–565, doi:10.1002/aenm.v3.5 (2013).
Zhao, Y., Dyck, J. S. & Burda, C. Toward high-performance nanostructured thermoelectric materials: the progress of bottom-up solution chemistry approaches. Journal of Materials Chemistry 21, 17049, doi:10.1039/c1jm11727k (2011).
Alivisatos, A. P. Nanocrystals: building blocks for modern materials design. Endeavour 21, 56–60, doi:10.1016/S0160-9327(97)01018-1 (1997).
Gur, I., Fromer, N. A., Geier, M. L. & Alivisatos, A. P. Air-stable all-inorganic nanocrystal solar cells processed from solution. Science 310, 462–465, doi:10.1126/science.1117908 (2005).
Graetzel, M., Janssen, R. A. J., Mitzi, D. B. & Sargent, E. H. Materials interface engineering for solution-processed photovoltaics. Nature 488, 304–312, doi:10.1038/nature11476 (2012).
Sargent, E. H. Colloidal quantum dot solar cells. Nature Photonics 6, 133–135, doi:10.1038/nphoton.2012.33 (2012).
Caruge, J. M., Halpert, J. E., Wood, V., Bulović, V. & Bawendi, M. G. Colloidal quantum-dot light-emitting diodes with metal-oxide charge transport layers. Nature Photonics 2, 247–250, doi:10.1038/nphoton.2008.34 (2008).
Keuleyan, S., Lhuillier, E., Brajuskovic, V. & Guyot-Sionnest, P. Mid-infrared HgTe colloidal quantum dot photodetectors. Nature Photonics 5, 489–493, doi:10.1038/nphoton.2011.142 (2011).
Ridley, B., Nivi, B. & Jacobson, J. M. All-inorganic field effect transistors fabricated by printing. Science 286, 746–749, doi:10.1126/science.286.5440.746 (1999).
Luther, J. M. et al. Structural, optical, and electrical properties of self-assembled films of PbSe nanocrystals treated with 1,2-ethanedithiol. ACS Nano 2, 271–280, doi:10.1021/nn7003348 (2008).
Liu, Y. et al. Dependence of carrier mobility on nanocrystal size and ligand length in PbSe nanocrystal solids. Nano Letters 10, 1960–1969, doi:10.1021/nl101284k (2010).
Choi, J. H. et al. Exploiting the colloidal nanocrystal library to construct electronic devices. Science 352, 205–208, doi:10.1126/science.aad0371 (2016).
See, K. C. et al. Water-processable polymer−nanocrystal hybrids for thermoelectrics. Nano Letters 10, 4664–4667, doi:10.1021/nl102880k (2010).
Cadavid, D. et al. Organic ligand displacement by metal salts to enhance nanoparticle functionality: thermoelectric properties of Ag2Te. Journal of Materials Chemistry A 1, 4864, doi:10.1039/c3ta01455j (2013).
Lynch, J. et al. Ligand coupling symmetry correlates with thermopower enhancement in small-molecule/nanocrystal hybrid materials. ACS Nano 8, 10528–10536, doi:10.1021/nn503972v (2014).
Ibáñez, M. et al. Electron doping in bottom-up engineered thermoelectric nanomaterials through HCl-mediated ligand displacement. Journal of the American Chemical Society 137, 4046–4049, doi:10.1021/jacs.5b00091 (2015).
Lee, M.-J. et al. Thermoelectric materials by using two-dimensional materials with negative correlation between electrical and thermal conductivity. Nature Communications 7, doi: 10.1038/ncomms12011 (2016).
Ibáñez, M. et al. High-performance thermoelectric nanocomposites from nanocrystal building blocks. Nature Communications 7, 10766, doi:10.1038/ncomms10766 (2016).
Paradiso, J. A. & Starner, T. Energy scavenging for mobile and wireless electronics. IEEE Pervasive Computing 4, 18–27, doi:10.1109/MPRV.2005.9 (2005).
Leonov, V. & Vullers, R. J. M. Wearable thermoelectric generators for body-powered devices. Journal of Electronic Materials 38, 1491–1498, doi:10.1007/s11664-008-0638-6 (2009).
Settaluri, K. T., Lo, H. & Ram, R. J. Thin thermoelectric generator system for body energy harvesting. Journal of Electronic Materials 41, 984–988, doi:10.1007/s11664-011-1834-3 (2011).
Weber, J. et al. Coin-size coiled-up polymer foil thermoelectric power generator for wearable electronics. Sensors and Actuators A: Physical 132, 325–330, doi:10.1016/j.sna.2006.04.054 (2006).
Russ, B. et al. Power factor enhancement in solution-processed organic n-type thermoelectrics through molecular design. Advanced Materials 26, 3473–3477, doi:10.1002/adma.v26.21 (2014).
Coates, N. E. et al. Effect of interfacial properties on polymer-nanocrystal thermoelectric transport. Advanced Materials 25, 1629–1633, doi:10.1002/adma.201203915 (2013).
Russ, B., Glaudell, A., Urban, J. J., Chabinyc, M. L. & Segalman, R. A. Organic thermoelectric materials for energy harvesting and temperature control. Nature Reviews Materials 1, 16050, doi:10.1038/natrevmats.2016.50 (2016).
Kriegel, I. et al. Tuning the excitonic and plasmonic properties of copper chalcogenide nanocrystals. Journal of the American Chemical Society 134, 1583–1590, doi:10.1021/ja207798q (2012).
Gulay, L., Daszkiewicz, M., Strok, O. & Pietraszko, A. Crystal structure of Cu2Se. Chemistry of Metals and Alloys 4, 200–205, doi:10.1107/S0108270111005889 (2011).
Kang, S. D. et al. Apparent critical phenomena in the superionic phase transition of Cu2-xSe. New Journal of Physics 18, 013024, doi:10.1088/1367-2630/18/1/013024 (2016).
Cahill, D. G. Analysis of heat flow in layered structures for time-domain thermoreflectance. Review of Scientific Instruments 75, 5119–5122, doi:10.1063/1.1819431 (2004).
Kang, K., Koh, Y. K., Chiritescu, C., Zheng, X. & Cahill, D. G. Two-tint pump-probe measurements using a femtosecond laser oscillator and sharp-edged optical filters. Review of Scientific Instruments 79, 114901, doi:10.1063/1.3020759 (2008).
Brown, D. R. et al. Phase transition enhanced thermoelectric figure-of-merit in copper chalcogenides. APL Materials 1, 052107, doi:10.1063/1.4827595 (2013).
The authors acknowledge support from the AFOSR-MURI on Controlling Thermal and Electrical Transport in Organic and Hybrid Materials, AFOSR MURI FA9550-12-1-0002, as well as the Molecular Foundry, a LBNL user facility supported by the Office of Science, BES, US DOE, under Contract DE-AC02-05CH11231. GIWAXS experiments were performed at beamline 7.3.3 at the Advanced Light Source, supported by the Director, Office of Science, Office of Basic Energy Sciences, of the U.S. Department of Energy under Contract No. DE-AC02-05CH11231.
The authors declare that they have no competing interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
About this article
Cite this article
Forster, J.D., Lynch, J.J., Coates, N.E. et al. Solution-Processed Cu2Se Nanocrystal Films with Bulk-Like Thermoelectric Performance. Sci Rep 7, 2765 (2017). https://doi.org/10.1038/s41598-017-02944-1
Materials Today Energy (2021)
Chemical Engineering Journal (2021)
Modelling a Segmented Skutterudite-Based Thermoelectric Generator to Achieve Maximum Conversion Efficiency
Applied Sciences (2020)