Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Rupture stress of liquid metal nanoparticles and their applications in stretchable conductors and dielectrics

Abstract

Few works had systematically investigated the relationship between the rupture stress of the oxide shell and the diameter of liquid metal nanoparticles (LMNPs). Here, we fabricated a series of elastomer/LMNPs composites, which were based on various polyurethanes with different shore hardness and LMNPs with different diameters, to systematically study the rupture stress of LMNPs. We established a reliable and guidable relationship between the stress–strain curves of elastomers with different shore hardness and rupture stress of LMNPs with various diameters by both experiments and numerical calculations. Based on this guidance, we can facilely prepare stretchable conductors with remarkable stretchability and conductivity (i.e., 24,130 S · cm−1 at 500% strain) and stretchable dielectrics with excellent stretchability and permittivity (i.e., dielectric constant of 76.8 with 580% strain) through controlling the shore hardness of elastomers and diameter of LMNPs. This work will facilitate the systematic study of LMNPs and expand their use in stretchable electronics.

Introduction

Stretchable functional materials have attracted much attention recently due to their wide use in deformable electronics ranging from robotic sensory skins and wearable communication electronics to bio-integrated devices1,2,3,4. The most promising approach for the preparation of stretchable functional materials is to embed functional fillers into elastomers, thus integrating the complementary advantages of the inorganics’ functionality with the elastomers’ mechanical stretchability5,6,7. Unfortunately, the reported mechanical performance of these composites decreases with increasing loading of inorganic fillers due to their mechanical stiffness and brittleness8,9,10,11,12. This has motivated an extensive research effort focused on the development and use of functional materials with large stretchability and low modulus.

Liquid metal (LM), particularly eutectic gallium indium (EGaIn), appear to be the most promising candidate for resolving the trade-off between functionality and stretchability7,13,14,15,16,17. On the one hand, EGaIn possesses properties of fluids such as negligible vapor pressure, low viscosity (2 mPa · s)18, low melting point (~14.5 °C)15, high surface tension (~550 mN/m)19, liquid-like conformability, and self-repairing ability at room temperature20,21. Recently, Parida et al. developed an extremely stretchable and healable conductor based on EGaIn by exploiting its fluidity property22. On the other hand, EGaIn also has many metallic characteristics such as high thermal conductivity (λ = 26.4 W m−1 K−1, T = 30 °C)23 and electrical conductivity (σ = 34,000 S · cm−1)14. Exploiting its metallic properties, some researchers have fabricated stretchable electrodes through the formation of EGaIn conductive channels inside the composites. For example, Wang et al. reported an intrinsically stretchable conductor with a working range of ~1,000%, initial conductivity of 8,331 S · cm−1, and high mechanical stability that was prepared by mixing ethylene vinyl acetate copolymer, silver flakes, and LM nanoparticles (LMNPs)24. Tang et al. obtained printable, stretchable (~500%), highly conductive (~2,316 S · cm−1), and durable electrodes for which electrical pathways were formed by peeling off the polymers from the patterned EGaIn particles25. Yang et al. fabricated stretchable energy-harvesting tactile interactive interface with high performance using mechanical sintered, LM-based stretchable electrodes26. Moreover, LMNPs were also adopted to construct dielectrics. Bartlett et al. incorporated 50% by volume (hereafter referred to as 50 vol%) of EGaIn droplets into elastomers to create all-soft dielectric films. The film with 50 vol% LMNPs inclusion could endure 600% strain and showed high dielectric constant of 42 across the frequency range from 1 to 200 kHz18.

The structure of insulating solid shell and conductive liquid core for the LMNPs enables their use in the fabrication of stretchable conductors and stretchable dielectrics. In the typical synthesis, bulk EGaIn is ruptured into nanoparticles via tip sonication27,28. The stretchable conductors or dielectrics are obtained by mixing LMNPs with hyperelastic elastomers28,29. Although the sizes of the synthesized LMNPs vary, all LMNPs have similar core-shell structure consisting of a spontaneously formed dielectric solid Ga2O3 shell and highly conductive liquid EGaIn core14,30,31,32. However, the integrity of the outer dielectric Ga2O3 shells used in stretchable conductors and dielectrics is quite different. In the LM-based stretchable conductors, Ga2O3 shells are broken and the encapsulated EGaIn flows out to coalesce, providing a dynamic and robust electrical pathway5,28. By contrast, Ga2O3 shells remain intact in the LM-based stretchable dielectrics. The Ga2O3 shells serve as powerful dielectric barriers between neighboring LMNPs18,33. Based on the above discussion, the integrity of the outer dielectric Ga2O3 shells determines the LMNPs functionality and applications. However, few works had systematically investigated the relationship between the rupture stress of the oxide shell and the diameter of LMNPs5,28,29,34.

In this work, we fabricated a series of elastomer/LMNPs composites, which were based on a range of polyurethane (PU) matrix with different shore hardness and LMNPs with different diameters, to systematically study the rupture stress of LMNPs. Furthermore, we established a reliable and guidable relationship between the stress–strain curves of elastomers with different shore hardness and rupture stress of LMNPs with various diameters by both experiments and numerical calculations. Based on this guidance, we can facilely prepare stretchable conductors with remarkable stretchability and conductivity (i.e., 24,130 S · cm−1 at 500% strain) and stretchable dielectrics with excellent stretchability and permittivity (i.e., dielectric constant of 76.8 with 580% strain) through controlling the shore hardness of elastomer and diameter of LMNPs.

Results and discussion

Theoretical calculation and experimental verification

In the experiments performed to measure the LMNPs activation stress, the direct application of stress to the LMNPs is inconvenient. Therefore, we adopted elastic PU to supply the stress and read the loaded stress from its stress–strain curve. The typical experimental procedure was as follows: First, EGaIn was broken up into nanoparticles via tip sonication28. A dielectric Ga2O3 shell with a thickness of 0.5–3 nm forms spontaneously upon the exposure of the nanoparticles to air as shown in Fig. 1a and revealed by TEM (Supplementary Fig. 1)14,35. The particle size can be tuned from 1.8 µm to 0.3 µm by prolonging the sonication time from 0.5 min to 30 min as shown in Supplementary Fig. 227,36. Specifically, LMNPs with different average diameters were donated as LMNPs-x, where x represented the average diameter (µm) of the obtained LMNPs after sonication for certain time. Commercially available PU with different shore hardness (85PU, 65PU, and 55PU where the number represents its shore hardness) was selected as the elastic matrix and stress supplier. Following material selection, all LMNPs/PU composites were fabricated by screen printing. Unless otherwise noted, the stretchable composites were denoted as yLMNPs-x/zPU (for instance, 80%LMNPs-1.4/85PU means 80 vol% LMNPs-1.4 dispersed in 85PU matrix). The composites were fabricated with a length, width, and thickness of about 20 mm, 3.5 mm, and 20 μm, respectively. All the samples were mounted on a motorized linear stage connected to a Keithley 2000 digital multimeter used to monitor the resistance change. Displacement tests coupling with electrical measurements were performed simultaneously at a constant strain rate of 0.1% · s−1. We assumed that the specimen was dielectric until the Keithley 2000 digital multimeter could detect its resistance and recorded the mechanical strain as the specimen activation strain. The LMNPs activation stress was obtained from the stress–strain curve of the corresponding PU. Based on the previous reports27,34, the force for breaking the particles was calculated as:

$$f = \frac{{d^2}}{{D^2}} \times F \times P$$
(1)

where F is the measured force applied by the circular punch, f is the force for breaking the particles, D is the diameter of the circular polystyrene punch, d is the average particle diameter, and P is the three-dimensional packing factor of the particles. When the sample is stretched to the activation strain, the activation stress is calculated as

$$S = \frac{{6.16d + 3.04 \times 10^{ - 7}}}{{\pi d^2}}$$
(2)

where S is the activation stress of LMNPs. More details could be obtained in Supplementary Note 1. Fig. 2a shows the activation stress plotted as a function of LMNPs diameter (red solid curve) obtained according to Eq. (2). To facilitate comparison, the stress–strain curves of various PUs are also plotted. As depicted in Fig. 2a, the activation stress of LMNPs is inversely proportional to their size so that larger LMNPs break more easily than smaller LMNPs. To clearly show the shell integrity of the LMNPs of various sizes under different stress, Fig. 2a is divided into two regions by the activation stress–LMNPs diameter curve. In the orange area, LMNPs will rupture under the overloaded stress and the leaked EGaIn will form a continuous network inside the composite. However, in the purple area, the external stress does not reach the activation stress of the corresponding LMNPs, so that their shells remain intact and act as electron barriers. Taking LMNPs-1.4 and LMNPs-0.3 as examples, the activation stress of LMNPs-1.4 is 1.5 × 106 Pa and once the applied stress exceeds this value, the LMNPs-1.4 become conductive. On the other hand, the activation stress of LMNPs-0.3 (9.5 × 106 Pa) is much higher than that of LMNPs-1.4, indicating that LMNPs-0.3 are more robust than LMNPs-1.4. When the external stress is lower than 9.5 × 106 Pa, the LMNPs-0.3 remain insulating and are suitable for use in dielectric composites.

Fig. 1: Design of LM-based stretchable conductors and dielectrics.
figure1

a The LMNPs preparation process and core-shell structure. b Schematic illustration of morphology changes of LMNPs-1.4 and LMNPs-0.3 applied in stretchable conductors and dielectrics. LMNPs-1.4/PU or LMNPs-0.3/PU samples are obtained by mixing LMNPs-1.4 or LMNPs-0.3 with corresponding PU, respectively.

Fig. 2: Verification of calculated results.
figure2

a Stress–strain curves of various PU coupled with calculated LMNPs activation stress. Theoretical and experimental activation strain of b 50%LMNPs-1.4/85PU and 50%LMNPs-0.3/85PU and c 50%LMNPs-1.4/65PU and 50%LMNPs-0.3/65PU. The error bars show the standard deviation. Top view SEM images of 50%LMNPs-1.4/85PU under d original state, e 30% strain, and f relaxed state and 50%LMNPs-0.3/85PU under g original state, h 200% strain, and i relaxed state. Outflowed EGaIn is emphasized in white box with dashed lines of e. The scale bars in di are 4 μm.

Two factors determine the integrity of the Ga2O3 shells: (1) the inherent activation stress of LMNPs; and (2) the external applied stress. The accuracy of Eq. (2) is validated by varying the size of LMNPs and the modulus of the PU matrix. As revealed in Fig. 2b, the experimental activation strains of 50%LMNPs-1.4/85PU and 50%LMNPs-0.3/85PU composites were 11.7% and 224.2%; these values are almost identical to the calculated activation strain values of 11.9% and 228.1%, respectively. SEM images of 50%LMNPs-1.4/85PU and 50%LMNPs-0.3/85PU composites provided morphological insight into the LMNPs changes during the multiple steps of the stretching-releasing process. In the original state, both spherical LMNPs-1.4 and LMNPs-0.3 (Fig. 2d, g) had closed-cell geometry and were dispersed uniformly in the 85PU matrix, differing only with respect to their size. Then, the 50%LMNPs-1.4/85PU sample was stretched to 10% strain and released. The Ga2O3 shells were not broken and inner EGaIn was still encapsulated as revealed in Supplementary Fig. 3a. After the strain was further increased to 30% (much larger than its activation strain of 11.9%), the outer Ga2O3 shells were broken and the inner EGaIn flowed out to form electrical channels as emphasized in the white box marked by dashed lines in Fig. 2e. Finally, the EGaIn microchannels formed inside the matrix and the 50%LMNPs-1.4/85PU composites functioned as stretchable conductors after releasing back to the 0% strain state as depicted in Fig. 2f.

By contrast, 50%LMNPs-0.3/85PU composites remained insulating and endured much larger strain. As revealed in Fig. 2h, the nonconductive shells of LMNPs-0.3 were intact for the 50%LMNPs-0.3/85PU composites even under 200% strain. This is because the LMNPs-0.3 can endure stress that is as high as 9.5 × 106 Pa and the activation strain of 50%LMNPs-0.3/85PU increased to 228.1%. Finally, the LMNPs-0.3 returned to its original spherical shape as illustrated in Fig. 2i and the 50%LMNPs-0.3/85PU composites remained insulating after releasing back to original state. However, large stress will tear the oxidized shells once the strain value exceeds 230%, in agreement with the SEM results (Supplementary Fig. 3b). These above experimental results are consistent with our calculated results and validated the effectiveness and accuracy of Eq. (2). Subsequently, 85PU was replaced by 65PU that has a much lower Young’s modulus to validate the influence of the matrix modulus. As shown in Fig. 2c, the experimental activation strain increased to 27.1% and 540.4% for 50%LMNPs-1.4/65PU and 50%LMNPs-0.3/65PU, respectively, matching the corresponding calculated activation strain values of 23.0% and 558.2%, respectively. Even though 85PU was replaced by 65PU, the activation stress values of 50%LMNPs-1.4/65PU (1.47 × 106 Pa) and 50%LMNPs-0.3/65PU (9.52 × 106 Pa) were essentially the same as those of 50%LMNPs-1.4/85PU (1.46 × 106 Pa) and 50%LMNPs-0.3/85PU (9.53 × 106 Pa), further confirming the accuracy of Eq. (2).

LM-based stretchable conductors

The integrity of the LMNPs shells and their suitability for applications can be easily determined by the comparison of the LMNPs threshold activation stress to the stress supplied by the polymer matrix. Once the supplied stress was larger than activation stress, LMNPs became conductive fillers and were suitable for use in stretchable conductors. In the following steps, to resolve the trade-off between conductivity and stretchability, we focused our effort on the development and optimization of LM-based stretchable electrodes using these broken LMNPs. It was easily concluded from the above calculations that the modulus of the elastomer matrix and strain influenced the supplied stress while the activation stress depended solely on the diameter of LMNPs. Fig. 3a shows the obtained conductivity (σ) after certain strains for the composites adopting 85PU, 65PU, and 55PU as the polymer matrix. An examination of the cross-section SEM images of the samples (Supplementary Fig. 4) shows that greater fusing area of broken LMNPs was obtained with larger strain and matrix modulus. The specimens with 85PU as the polymer matrix obtained the highest conductivity after 500% strain due to its high modulus. Furthermore, the relationship between the conductivity after certain strains and LMNPs diameter was demonstrated in Fig. 3b. As revealed in the cross-sectional SEM images of the specimens with different LMNPs diameters (Supplementary Fig. 5), the specimens containing LMNPs-1.4 obtained the highest conductivity. Further increase in the diameter (about 1.8 μm in Supplementary Fig. 5a) will lead to poor dispersion of the LMNPs in the composites. The relationship between the sample conductivity after certain strains and amount of LMNPs is shown in Fig. 3c. It is observed that an excessive amount of LMNPs lowered the conductivity due to the insufficient PU coverage on the particles surface, while an inadequate amount of LMNPs resulted in a longer distance between the adjacent particles. Consequently, thicker matrix shells hindered the agglomeration of the particles as demonstrated in Supplementary Fig. 6.

Fig. 3: Electrical performance of LM-based stretchable conductors.
figure3

Relationship of conductivity in the releasing state (0% strain) after certain strains with a PU, b LMNPs diameters, and c LMNPs volume percentage. d Fitting of the experiment data with the percolation theory. e Conductivity-applied strain curve of 85%LMNPs-1.4/85PU. f Normalized resistance changes of 85%LMNPs-1.4/85PU subjection to 300% strain for 20,000 cycles at various rates (0.12, 0.16, 0.24, 0.30, and 0.01 Hz). The error bars show the standard deviation.

To summarize, the 85%LMNPs-1.4/85PU specimen optimized the highest conductivity (11,702 S · cm−1). In fact, the broken LMNPs can be regarded as conductive fillers and obey the percolation theory relationship8,37

$$\it A = A_0\left( {V_f - V_c} \right)^{\mathrm{b}}$$

where A and A0 denote the conductivities of the composites and bulk EGaIn, respectively, and Vf, Vc, and b are the volume fraction of conductive fillers, the volume fraction of the percolation threshold, and the fitting exponent, respectively. As depicted in Fig. 3d, the results obtained using 0.38, 1.48, and 34,000 for Vc, b, and A0, respectively, in computer-aided calculation showed a good agreement with the experimental data. Additional calculation details are provided in Supplementary Note 2. The stretching state conductivity decrease is the fatal weakness that leads to device performance degradation38. Unlike for the other types of stretchable conductors, the initial conductivity of the 85%LMNP-1.4/85PU composite was 11,702 S · cm−1 and increased gradually to 24,130 S · cm−1 at 500% strain as revealed in Fig. 3e. This unusual phenomenon was attributed to the conformal characteristic of LM that induced an enhancement of the conductivity along the stretching direction5. Supplementary Fig. 7 shows a comparison of the electrical conductivity and working range of the 85%LMNPs-1.4/85PU electrodes to other previously reported stretchable and printable conductors8,9,10,11,12,24,25,39,40,41,42,43,44,45,46,47,48,49.

To cope with challenging external environmental conditions, the reliability of stretchable electrodes at different stretching frequencies is also crucial. As shown in Fig. 3f, normalized resistance (R/R0) of the 85%LMNPs-1.4/85PU stretchable electrodes at 300% strain remains constant at ~3.3 as the stretching frequency increases from 0.01 to 0.30 Hz. The electrodes also showed no obvious degradation in normalized resistance (Fig. 3f) and conductivity (Supplementary Fig. 8) even after a total of 20,000 stretching-releasing cycles under 300% strain, demonstrating their mechanical robustness and reliability for practical applications. A normalized resistance change of the 85%LMNPs-1.4/85PU stretchable electrodes subjected to 200% and 100% strains at various rates is presented in Supplementary Fig. 9.

LM-based stretchable dielectrics

The intact LMNPs can be used in the dielectric materials as specific capacitance (Ca) and permittivity (ε) enhancing fillers on the premise of high stretchability. According to the calculations, the outer Ga2O3 shells of LMNPs-0.3 can encapsulate EGaIn and prevent its outward flow for stresses of up to 9.53 × 106 Pa, far more than the tensile stress of 55PU (5.40 × 106 Pa at 580% strain). The sample remained insulating until rupture. As plotted in Fig. 4a, the specific capacitance of the LMNPs-0.3/55PU dielectric film increased monotonically with more LMNPs-0.3 addition and reached nearly 1,200% [Ca (50%LMNPs-0.3/55PU, 100 kHz) = 64.7 nF · cm−2] compared to that of the blank control [Ca (55PU, 100 kHz) = 5.4 nF · cm−2]. Moreover, the dissipation (D) of all specimens in the frequency range of 10–100 kHz was lower than 0.1, well within the threshold for dielectric functionality. The low dissipation of all specimens was attributed to the dielectric property of outside insulating Ga2O3 and negligible conductivity of samples50. Fig. 4b presents the dielectric constant plotted versus LMNPs-0.3 volume percentage of the LMNPs-0.3/55PU dielectric film at the frequency of 100 kHz and 0% strain. The dielectric constant increased to nearly 1,240% that of 55PU and could be easily tuned from 6.2 with 0 vol% LMNPs-0.3 to 76.8 with 50 vol% LMNPs-0.3. Furthermore, the electromechanical properties of dielectric layers are also significant parameters for the evaluation of stretchable dielectrics. Fig. 4c depicts the normalized capacitance (C/C0) of the 50%LMNPs-0.3/55PU dielectric films at a frequency range of 10–100 kHz under various strains. Their C/C0 values remained relatively stable within the entire measured frequency range. However, C/C0 increased monotonically with stretching and reached 1.9 at 200% strain. This phenomenon can be attributed to: (1) the expanded area and (2) the thinner dielectric layer caused by stretching.

Fig. 4: Electrical performance of LM-based stretchable dielectrics.
figure4

a Comparison of specific capacitance and dissipation of LMNPs-0.3/55PU with various LMNPs-0.3 volume percentage under 10–100 kHz. b Dielectric constant of LMNPs-0.3/55PU with various LMNPs-0.3 volume percentage under 100 kHz. The error bars show the standard deviation. c Normalized capacitance of 50%LMNPs-0.3/55PU subjection to various strain under 10–100 kHz. d Normalized capacitance and dissipation of 50%LMNPs-0.3/55PU subjection to 100% strain for 1,000 cycles.

To test the reliability of the 50%LMNPs-0.3/55PU dielectric films, we performed fatigue measurements under 100% strain for 1,000 cycles (Fig. 4d). During cyclic test, the stretching C/C0 and D/D0 values remained 1.5 and 1.3, manifesting the high stability of LMNPs-0.3 inside the dielectrics and the accurate guidance provided by the results of our calculation. The results of the electrical, electromechanical, and fatigue tests of other LMNPs-0.3/55PU samples are presented in Supplementary Fig. 10. To highlight the performance of our dielectric films, we compared the specific capacitance, dielectric constant, working range, and durability of 50%LMNPs-0.3/55PU with those of the state-of-the-art stretchable dielectrics18,51,52,53,54,55 as shown in Supplementary Table 1.

In conclusion, we calculated the rupture stress of LMNPs with different sizes and verified the validity of the calculations through experiments. Following the guidance provided by the calculated results, we fabricated LM-based, ultra-stable, hyperelastic, and highly conductive electrodes adopting coalesced broken LMNPs-1.4. As stretchable conductors, the 85%LMNPs-1.4/85PU composites demonstrated large stretchability (>500%) and high electrical conductivity (11,702 S · cm–1 at 0% strain and 24,130 S · cm–1 at 500% strain). Moreover, we fabricated dielectric films with high permittivity and specific capacitance by using intact LMNPs-0.3. As dielectric layers, the 50%LMNPs-0.3/55PU dielectric films remained insulating under 580% strain. Specific capacitance and dielectric constant reached 64.7 nF · cm−2 and 76.8 corresponding to enhancements of 1,200% and 1,240%, respectively, compared to blank control. Fatigue measurements revealed that the dielectric films were stable under 100% strain for 1,000 cycles. This demonstrated the high stability of LMNPs-0.3 inside the dielectrics and provided an additional confirmation of the accuracy of the guidance provided by our calculations. Taken together, these results will guide the systematic study of LM as well as advance the development of next-generation deformable electronics.

Methods

Raw materials

N,N-dimethylformamide (Sigma Aldrich) were purchased and used without further purification. PU (85PU, 65PU, 55PU) was obtained from Yantai Wanhua Polyurethane Co. Ltd. (China). EGaIn was fabricated by mixing melted gallium and indium (75% Ga/25% In, by weight) overnight.

Preparation of LMNPs/PU ink

LMNPs were synthesized using a tip sonicator (Hielscher UP400S, Germany). EGaIn (6 g) and DMF (150 ml) were added into 250 ml beaker and treated at 90% sonication amplitude for different time length (0.5, 1, 2, 5, 10, and 30 min) to obtain particles with the target size. Then, the LMNPs were collected by centrifugation at 4,000 rpm for 5 min. PU (1 g) was added to DMF (5 ml) and stirred for 8 h to obtain a clear solution. Finally, LMNPs/PU ink was obtained by mixing LMNPs and PU solution overnight.

Fabrication of LMNPs/PU dielectric film

Glass slides were cleaned with ultrasonication sequentially in acetone, isopropyl alcohol, and deionized water. Nanocomposite dielectric film was coated on glass substrates using a Mayer rod, followed by drying on a hot plate at 80 °C for 10 min. The amount of LMNPs varied from 15 to 50 vol%. The printed composite film with a thickness of ~1 µm was obtained by adjusting the concentration of the dielectric film ink. For dielectric analysis, EGaIn was deposited on the film top surface using a blunt syringe needle. Subsequently, ReoFlex elastomer was poured and cured to transfer the bottom structure from the rigid substrate. Finally, EGaIn was patterned as another electrode to obtain a stretchable parallel plate capacitor and a wire probe was placed into the EGaIn contact. At least five individual measurements were performed to characterize the dielectric film.

Characterization

Resistance-strain and fatigue tests were carried using a motorized linear stage with a built-in controller (Zolix Inc., China) while a Keithley 2000 digital multimeter (Keithley Instruments, America) was used to simultaneously monitor the resistance change. The dielectric film capacitance and dissipation were measured using a precision LCR meter (TongHui 2338H, Changzhou Tonghui Electronic Co., Ltd.) from 10 to 100 kHz at 5 V adopting the sandwich structure mentioned above. Capacitance and dielectric constant were measured at a frequency of 100 kHz. SEM characterizations were carried out using a field-emission scanning electron microscope (JSM-7800, Japan) at an accelerating voltage of 5.0 kV. TEM images were obtained using a transmission electron microscope (JEM-2800, Japan). Electric conductivity was calculated according to the equation σ = L/(RS), where L is the length of the tested sample, R is the sample resistance, and S is its cross-section area. At least five samples were tested for each conductivity value. The stress–strain curves of 85PU, 65PU, and 55PU were measured using a universal tensile testing machine (SHIMADZU TRAPEZIUM-X, Japan). The optical photographs were obtained using a Leica ICC50W camera (Leica Microsystems, Germany). Particle size statistics were obtained using Nano Measure (China) and the irregular graphic area was integrated using the Image J software (China). A 3D profiler (Filmetrics, America) was used to measure the thicknesses of the composite film. Dielectric constants were calculated from the measured capacitances, thicknesses, and cross-section area of the electrodes. All capacitance, dielectric constant, and conductivity values were averaged from the measurements performed for at least five devices, and the error bars denote the standard deviations.

Data availability

The datasets generated and analyzed during the current study are available from the corresponding author on reasonable request.

References

  1. 1.

    Forrest, S. R. The path to ubiquitous and low-cost organic electronic appliances on plastic. Nature 428, 911–918 (2004).

    CAS  Article  Google Scholar 

  2. 2.

    Kim, D.-H. & Rogers, J. A. Stretchable electronics: materials strategies and devices. Adv. Mater. 20, 4887–4892 (2008).

    CAS  Article  Google Scholar 

  3. 3.

    Leber, A. et al. Soft and stretchable liquid metal transmission lines as distributed probes of multimodal deformations. Nat. Electron. 3, 316–326 (2020).

    Article  Google Scholar 

  4. 4.

    Wang, S. et al. Skin electronics from scalable fabrication of an intrinsically stretchable transistor array. Nature 555, 83–88 (2018).

    CAS  Article  Google Scholar 

  5. 5.

    Fassler, A. & Majidi, C. Liquid-phase metal inclusions for a conductive polymer composite. Adv. Mater. 27, 1928–1932 (2015).

    CAS  Article  Google Scholar 

  6. 6.

    Ma, R., Chou, S.-Y., Xie, Y. & Pei, Q. Morphological/nanostructural control toward intrinsically stretchable organic electronics. Chem. Soc. Rev. 48, 1741–1786 (2019).

    CAS  Article  Google Scholar 

  7. 7.

    Tee, B. C. K. & Ouyang, J. Soft electronically functional polymeric composite materials for a flexible and stretchable digital future. Adv. Mater. 30, 1802560 (2018).

    Article  CAS  Google Scholar 

  8. 8.

    Chun, K.-Y. et al. Highly conductive, printable and stretchable composite films of carbon nanotubes and silver. Nat. Nanotechnol. 5, 853–857 (2010).

    CAS  Article  Google Scholar 

  9. 9.

    Liang, J., Tong, K. & Pei, Q. A water-based silver-nanowire screen-print ink for the fabrication of stretchable conductors and wearable thin-film transistors. Adv. Mater. 28, 5986–5996 (2016).

    CAS  Article  Google Scholar 

  10. 10.

    Matsuhisa, N. et al. Printable elastic conductors with a high conductivity for electronic textile applications. Nat. Commun. 6, 7461–7471 (2015).

    CAS  Article  Google Scholar 

  11. 11.

    Park, M. et al. Highly stretchable electric circuits from a composite material of silver nanoparticles and elastomeric fibres. Nat. Nanotechnol. 7, 803–809 (2012).

    CAS  Article  Google Scholar 

  12. 12.

    Sekitani, T. et al. Stretchable active-matrix organic light-emitting diode display using printable elastic conductors. Nat. Mater. 8, 494–499 (2009).

    CAS  Article  Google Scholar 

  13. 13.

    Dickey, M. D. Stretchable and soft electronics using liquid metals. Adv. Mater. 29, 1606425 (2017).

    Article  CAS  Google Scholar 

  14. 14.

    Kazem, N., Hellebrekers, T. & Majidi, C. Soft multifunctional composites and emulsions with liquid metals. Adv. Mater. 29, 1605985 (2017).

    Article  CAS  Google Scholar 

  15. 15.

    Daeneke, T. et al. Liquid metals: fundamentals and applications in chemistry. Chem. Soc. Rev. 47, 4073–4111 (2018).

    CAS  Article  Google Scholar 

  16. 16.

    Lin, Y., Genzer, J. & Dickey, M. D. Attributes, fabrication, and applications of gallium-based liquid metal particles. Adv. Sci. 7, 2000192 (2020).

    CAS  Article  Google Scholar 

  17. 17.

    Ren, L., Xu, X., Du, Y., Kalantar-Zadeh, K. & Dou, S. X. Liquid metals and their hybrids as stimulus–responsive smart materials. Mater. Today 34, 92–114 (2020).

    CAS  Article  Google Scholar 

  18. 18.

    Bartlett, M. D. et al. Stretchable, high-k dielectric elastomers through liquid-metal inclusions. Adv. Mater. 28, 3726–3731 (2016).

    CAS  Article  Google Scholar 

  19. 19.

    Chen, S., Wang, H.-Z., Zhao, R.-Q., Rao, W. & Liu, J. Liquid metal composites. Matter 2, 1446–1480 (2020).

    Article  Google Scholar 

  20. 20.

    Markvicka, E. J., Bartlett, M. D., Huang, X. & Majidi, C. An autonomously electrically self-healing liquid metal-elastomer composite for robust soft-matter robotics and electronics. Nat. Mater. 17, 618–624 (2018).

    CAS  Article  Google Scholar 

  21. 21.

    Li, X. et al. Evaporation-induced sintering of liquid metal droplets with biological nanofibrils for flexible conductivity and responsive actuation. Nat. Commun. 10, 3514–3522 (2019).

    CAS  Article  Google Scholar 

  22. 22.

    Parida, K. et al. Extremely stretchable and self-healing conductor based on thermoplastic elastomer for all-three-dimensional printed triboelectric nanogenerator. Nat. Commun. 10, 2158–2166 (2019).

    Article  CAS  Google Scholar 

  23. 23.

    Yun, G. et al. Liquid metal-filled magnetorheological elastomer with positive piezoconductivity. Nat. Commun. 10, 1300–1308 (2019).

    Article  CAS  Google Scholar 

  24. 24.

    Wang, J. et al. Printable superelastic conductors with extreme stretchability and robust cycling endurance enabled by liquid-metal particles. Adv. Mater. 30, 1706157 (2018).

    Article  CAS  Google Scholar 

  25. 25.

    Tang, L. et al. Printable metal-polymer conductors for highly stretchable bio-devices. iScience 4, 302–311 (2018).

    CAS  Article  Google Scholar 

  26. 26.

    Yang, Y. et al. Stretchable energy-harvesting tactile interactive interface with liquid-metal-nanoparticle-based electrodes. Adv. Funct. Mater. 30, 1909652 (2020).

    CAS  Article  Google Scholar 

  27. 27.

    Zhang, W. et al. Liquid metal/metal oxide frameworks. Adv. Funct. Mater. 24, 3799–3807 (2014).

    CAS  Article  Google Scholar 

  28. 28.

    Lin, Y. et al. Handwritten, soft circuit boards and antennas using liquid metal nanoparticles. Small 11, 6397–6403 (2015).

    CAS  Article  Google Scholar 

  29. 29.

    Ren, L. et al. Nanodroplets for stretchable superconducting circuits. Adv. Funct. Mater. 26, 8111–8118 (2016).

    CAS  Article  Google Scholar 

  30. 30.

    Song, H. et al. Ga-based liquid metal micro/nanoparticles: recent advances and applications. Small 16, 1903391 (2020).

    CAS  Article  Google Scholar 

  31. 31.

    Dickey, M. D. et al. Eutectic gallium-indium (EGaIn): a liquid metal alloy for the formation of stable structures in microchannels at room temperature. Adv. Funct. Mater. 18, 1097–1104 (2008).

    CAS  Article  Google Scholar 

  32. 32.

    Chiechi, R. C., Weiss, E. A., Dickey, M. D. & Whitesides, G. M. Eutectic gallium–indium (EGaIn): a moldable liquid metal for electrical characterization of self-assembled monolayers. Angew. Chem. Int. Ed. 47, 142–144 (2008).

    CAS  Article  Google Scholar 

  33. 33.

    Pan, C. et al. A liquid-metal-elastomer nanocomposite for stretchable dielectric materials. Adv. Mater. 31, 1900663 (2019).

    Article  CAS  Google Scholar 

  34. 34.

    Boley, J. W., White, E. L. & Kramer, R. K. Mechanically sintered gallium-indium nanoparticles. Adv. Mater. 27, 2355–2360 (2015).

    CAS  Article  Google Scholar 

  35. 35.

    Regan, M. J. et al. X-ray study of the oxidation of liquid-gallium surfaces. Phys. Rev. B 55, 10786–10790 (1997).

    CAS  Article  Google Scholar 

  36. 36.

    Suslick, K. S. Sonochemistry. Science 247, 1439–1445 (1990).

    CAS  Article  Google Scholar 

  37. 37.

    Li, J. & Kim, J.-K. Percolation threshold of conducting polymer composites containing 3D randomly distributed graphite nanoplatelets. Compos. Sci. Technol. 67, 2114–2120 (2007).

    CAS  Article  Google Scholar 

  38. 38.

    Sekitani, T. et al. A rubberlike stretchable active matrix using elastic conductors. Science 321, 1468–1472 (2008).

    CAS  Article  Google Scholar 

  39. 39.

    Araki, T., Nogi, M., Suganuma, K., Kogure, M. & Kirihara, O. Printable and stretchable conductive wirings comprising silver flakes and elastomers. IEEE Electrron Device Lett. 32, 1424–1426 (2011).

    CAS  Article  Google Scholar 

  40. 40.

    Ma, R., Kang, B., Cho, S., Choi, M. & Baik, S. Extraordinarily high conductivity of stretchable fibers of polyurethane and silver nanoflowers. ACS Nano 9, 10876–10886 (2015).

    CAS  Article  Google Scholar 

  41. 41.

    Kim, Y. et al. Stretchable nanoparticle conductors with self-organized conductive pathways. Nature 500, 59–63 (2013).

    CAS  Article  Google Scholar 

  42. 42.

    Stoyanov, H., Kollosche, M., Risse, S., Waché, R. & Kofod, G. Soft conductive elastomer materials for stretchable electronics and voltage controlled artificial muscles. Adv. Mater. 25, 578–583 (2013).

    CAS  Article  Google Scholar 

  43. 43.

    Matsuhisa, N. et al. Printable elastic conductors by in situ formation of silver nanoparticles from silver flakes. Nat. Mater. 16, 834–840 (2017).

    CAS  Article  Google Scholar 

  44. 44.

    Ma, R., Lee, J., Choi, D., Moon, H. & Baik, S. Knitted fabrics made from highly conductive stretchable fibers. Nano Lett. 14, 1944–1951 (2014).

    CAS  Article  Google Scholar 

  45. 45.

    Park, Y.-G. et al. Three-dimensional, high-resolution printing of carbon nanotube/liquid metal composites with mechanical and electrical reinforcement. Nano Lett. 19, 4866–4872 (2019).

    CAS  Article  Google Scholar 

  46. 46.

    Wang, Y. et al. Standing enokitake-like nanowire films for highly stretchable elastronics. ACS Nano 12, 9742–9749 (2018).

    CAS  Article  Google Scholar 

  47. 47.

    Sun, H., Han, Z. & Willenbacher, N. Ultrastretchable conductive elastomers with a low percolation threshold for printed soft electronics. ACS Appl. Mater. Interfaces 11, 38092–38102 (2019).

    CAS  Article  Google Scholar 

  48. 48.

    Wang, Y. et al. A highly stretchable, transparent, and conductive polymer. Sci. Adv. 3, 10–19 (2017).

    CAS  Google Scholar 

  49. 49.

    Yao, B. et al. Highly stretchable polymer composite with strain-enhanced electromagnetic interference shielding effectiveness. Adv. Mater. 32, 1907499 (2020).

    CAS  Article  Google Scholar 

  50. 50.

    Dang, Z.-M. et al. Fundamentals, processes and applications of high-permittivity polymer–matrix composites. Prog. Mater. Sci. 57, 660–723 (2012).

    CAS  Article  Google Scholar 

  51. 51.

    Liang, J. et al. Intrinsically stretchable and transparent thin-film transistors based on printable silver nanowires, carbon nanotubes and an elastomeric dielectric. Nat. Commun. 6, 7647–7656 (2015).

    CAS  Article  Google Scholar 

  52. 52.

    Zhang, Z., Du, C., Jiao, H. & Zhang, M. Polyvinyl alcohol/SiO2 hybrid dielectric for transparent flexible/stretchable all-carbon-nanotube thin-film-transistor integration. Adv. Electron. Mater. 6, 1901133 (2020).

    CAS  Article  Google Scholar 

  53. 53.

    Kim, J. O. et al. Network structure modification-enabled hybrid polymer dielectric film with zirconia for the stretchable transistor applications. Adv. Funct. Mater. 30, 1906647 (2020).

    CAS  Article  Google Scholar 

  54. 54.

    Feng, P., Zhong, M. & Zhao, W. Stretchable multifunctional dielectric nanocomposites based on polydimethylsiloxane mixed with metal nanoparticles. Mater. Res. Express 7, 015007 (2019).

    Article  CAS  Google Scholar 

  55. 55.

    Rao, Y.-L. et al. Stretchable self-healing polymeric dielectrics cross-linked through metal-ligand coordination. J. Am. Chem. Soc. 138, 6020–6027 (2016).

    CAS  Article  Google Scholar 

Download references

Acknowledgements

The work reported here was supported by NSFC (51872146, 51673099), the “Fundamental Research Funds for the Central Universities,” Nankai University (63191520), and Tianjin Municipal Science and Technology Commission (17JCZDJC30200) in China.

Author information

Affiliations

Authors

Contributions

Y.L. designed, fabricated, characterized the devices, and analyzed the data. X.J. helped with manuscript figures. J.L. conceived of the work and coordinated the research. All authors read and approved the final manuscript.

Corresponding authors

Correspondence to Xinyi Ji or Jiajie Liang.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Liu, Y., Ji, X. & Liang, J. Rupture stress of liquid metal nanoparticles and their applications in stretchable conductors and dielectrics. npj Flex Electron 5, 11 (2021). https://doi.org/10.1038/s41528-021-00108-w

Download citation

Search

Quick links