Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Lead-substituted barium hexaferrite for tunable terahertz optoelectronics

Abstract

Due to their outstanding dielectric and magnetic properties, hexaferrites are attracting ever-increasing attention for developing electronic components of next-generation communication systems. The complex crystal structure of hexaferrites and the critical dependences of their electric and magnetic properties on external factors, such as magnetic/electric fields, pressure, and doping, open ample opportunities for targeted tuning of these properties when designing specific devices. Here we explored the electromagnetic properties of lead-substituted barium hexaferrite, Ba1−xPbxFe12O19, a compound featuring an extremely rich set of physical phenomena that are inherent in the dielectric and magnetic subsystems and can have a significant effect on its electromagnetic response at terahertz frequencies. We performed the first detailed measurements of the temperature-dependent (5–300 K) dielectric response of single-crystalline Ba1−xPbxFe12O19 in an extremely broad spectral range of 1 Hz–240 THz. We fully analyzed numerous phenomena with a corresponding wide distribution of specific energies that can affect the terahertz properties of the material. The most important fundamental finding is the observation of a ferroelectric-like terahertz excitation with an unusual temperature behavior of its frequency and strength. We suggest microscopic models that explain the origin of the excitation and its nonstandard temperature evolution. Several narrower terahertz excitations are associated with electronic transitions between the fine-structure components of the Fe2+ ground state. The discovered radio-frequency relaxations are attributed to the response of magnetic domains. Gigahertz resonances are presumably of magnetoelectric origin. The obtained data on diverse electromagnetic properties of Ba1−xPbxFe12O19 compounds provide information that makes the entire class of hexaferrites attractive for manufacturing electronic devices for the terahertz range.

Introduction

The terahertz (THz) frequency region has been the “dark horse” for the scientific community as far as technology and application are concerned. Although the theoretical predictions were rather exciting, the experimental potential did not allow to explore the proposed effects directly1. This has changed, however, and the extensive search for materials in recent years has begun to cover the demands of the newly developed field of THz electronics. Currently, the field of THz technologies is one of the most promising directions for the development of electronics2. The recently promoted 5G standard for broadband cellular networks operates at frequencies of tens of gigahertz. The upcoming 6G standard aims at even higher frequencies3, and the subsequent generations will inevitably move toward the THz region. The application of THz frequencies is not limited to telecommunications, but it spans radar systems, ultrafast computer memories, nondestructive testing, safe bioscanning, security imaging, and many others4,5,6. The crucial need for materials with desired properties for particular applications has become a bottleneck for the development of THz technology. Since it is in the THz region that characteristic electronic, magnetic, and mixed-type excitations are often found, the important scientific challenge that needs to be addressed involves the search for materials whose fundamental physical properties would most adequately meet the requirements of modern technological development.

In this respect, hexaferrites recently drew considerable interest due to their distinct dielectric, magnetic, and mainly magnetoelectric properties (tunability of losses and dielectric constant, giant magnetoelasticity, multiferroicity, quantum paraelectricity)7,8,9,10,11,12,13 suitable for microwave and THz applications14,15,16,17. For example, ferromagnetic BaFe12O19 with an M-type hexaferrite crystal structure (denoted as BaM in the following) is the most widely commercially produced magnetic material, with overall yearly market sales of billions of dollars18. The functional characteristics of substituted hexaferrites show outstanding sensitivity to doping, making these materials future candidates for novel devices of THz optoelectronics. Doped M-type hexaferrites exhibit superior magnetic characteristics, including the ferromagnetic resonance (FMR) frequency located in the THz range, record values of the coercive force of up to 40 kOe19, and formation of a new type of Jahn–Teller sublattice20. Doping BaM with lead is expected to systematically change its dielectric properties. In fact, BaM is relatively transparent in the THz range21, whereas lead ferrite PbFe12O19 effectively shields THz radiation22. Despite constituting a core material for the magnetic device market, hexaferrites are rather poorly studied from the dielectric standpoint. In other words, the practical development of this promising class of materials calls for thorough studies of their fundamental physical properties. In particular, this concerns fundamental processes that determine the electromagnetic properties of hexaferrites at THz frequencies. However, data on their electromagnetic responses, including those in the THz range, are lacking to date.

To fill this gap, we report here the characterization of the electromagnetic properties in the Hz to THz frequency range of one of the most well-known representatives of the hexaferrite family, lead-substituted barium hexaferrite Ba1−xPbxFe12O19 (x = 0.1, 0.2). For the studies, we managed to synthesize a series of unique high-quality single crystals of the compounds; synthesis, characterization, and sample preparation procedures are described in detail in Supplemental Information (Chapter SI1). We found that their THz dielectric responses include strong soft excitations that can be easily tuned by temperature variation. The discovered THz resonance (soft mode) exhibits a highly unusual temperature behavior never detected in hexaferrites or other incipient ferroelectrics. We propose approaches that explain the nonclassical temperature dynamics of this “soft mode” on a microscopic level. Moreover, in the Hz–MHz region, several temperature-activated relaxation processes were detected. In addition, we observed signs of an almost temperature-independent narrow resonance in the gigahertz region. Together with infrared (IR) lattice vibrations, the observed broadband electromagnetic response in the studied hexaferrites spans over 14 decades in frequency, and it involves processes of different natures; this enables us to draw a global picture of the microscopic mechanisms responsible for the observed phenomena. In this work, we demonstrate that admixing Pb dramatically alters the THz response of the BaM. The possibility of effective targeted tuning of the functional characteristics of substituted hexaferrites by doping significantly extends the area of their applications in THz electronics.

Results and discussion

In the following, we first focus on a detailed consideration of the spectra and spectral features that we observed at different frequencies and at different temperatures, offer an interpretation of the phenomena that are the origin of these features, and in the concluding section, we consider our results in the context of the possibility of their practical use.

THz spectra, the soft mode

The most intriguing fundamental result of the present study is the observation of an excitation at THz frequencies whose frequency position and dielectric strength reveal strong and highly unusual dependences on the temperature, as seen in Fig. 1 in the THz (5–70 cm−1) spectra of real ε′(ν) and imaginary ε″(ν) permittivity. For the experimental details, see the “Methods” section. The growth and characterization of the crystals are presented in chapter SI1 (see also Figs. SI1SI5 and Tables 1 and 2 therein) of the Supplementary Information (SI). The crystal structure is described in chapter SI2 of the SI and presented in Fig. SI2–1.

Fig. 1: Broadband (RF–THz–IR) spectra of the complex dielectric permittivity of Ba1−xPbxFe12O19, x = 0.2, measured at selected temperatures for polarization Ec .
figure1

Panel (a) represents real part of the permittivitty, panels (b, c) illustrates logarithmic and linear scaled spectra of imaginary part of the permittivity. Dots correspond to experimental data; lines correspond to results of model processing using Eqs. (1) and (4) for resonances and overdamped absorptions, respectively. Open squares represent the THz data obtained at frequencies of interference maxima in the THz transmission coefficient of the plane-parallel sample, providing an enhanced accuracy in the determination of the sample’s dielectric parameters80. Four relatively weak absorption lines resolved at 10 K (shown by arrows in b, c) correspond to electronic transitions of Fe2+, also known from other Pb-substituted compound BaFe12O1923,24,25,81. The broad THz absorption band reveals a dramatic frequency softening upon cooling, as it shifts from ≈30 cm−1 at 298 K to ≈10 cm−1 at 10 K. The symbols below 10−2 cm−1 represent the results from dielectric spectroscopy at 1 Hz–300 MHz (open circles: from the frequency-response analysis; closed circles: from the reflectometric coaxial technique). The marked frequency–temperature-dependent response observed at these frequencies is discussed in the text. Note the changes of scale at the frequency axes. c shows linear scaled THz–IR spectra.

Figure 2a, b demonstrates that, in the x = 0.1 compound, a drastic change in the resonance frequency position of the soft mode occurs (Fig. 2a), which strongly contrasts with the temperature-independent behavior of the position of the lowest-frequency optical phonon at 92 cm−1 (Fig. 2b and Fig. SI2–2 in Supplementary Information). Before discussing the behavior and the origin of the discovered soft excitation in more detail, we comment on four narrower absorption lines that are resolved at the lowest temperatures on the high-frequency wing of the excitation; they are marked by arrows in Fig. 1b, c. Comparing the frequency positions, intensities, and temperature evolution of these lines with those seen in the THz spectra of isostructural compounds, i.e., in Ba1−xPbxFe12O19 with x = 0.723, x = 0.6 and 0.824,25, we conclude that the four resonances observed in Ba1−xPbxFe12O19 with x = 0.1 (x = 0.2) at 64 (68), 47 (48), 34 (34), 22 (21) cm−1 have the same origin. We associate these resonances with electronic transitions between the fine-structure components of the 5E ground state of tetrahedrally coordinated Fe2+. The presence of Fe2+ ions in BaM and in Pb-substituted BaM is due to both growth defects (mainly oxygen vacancies) and sharing the outer 6s2 electron pair of Pb2+ with the Fe3+ ion. A similar effect was observed in Ti4+-substituted hexaferrites26, where Fe2+ ions maintain the charge neutrality of the compound with aliovalent doping. In addition, in Ti-substituted BaM (BaTi0.75Fe11.25O19)20, calculations of the adiabatic potential showed that, for Fe2+ in the BaM matrix, tetrahedral coordination was the most energetically favorable. We note that the intensities of the lines are higher at x = 0.2 Ba1−xPbxFe12O19 compound compared to the compound with x = 0.1, which is in agreement with our assumption on the nature of these absorption lines due to the presence of the Pb2+ ions.

Fig. 2: The THz soft mode.
figure2

2D plots of temperature-dependent spectra of the real part of AC conductivity (νε″) of the THz soft excitation (a) and the lowest E1u optical phonon (b) for the Ba1−xPbxFe12O19 crystal, x = 0.1. cf: parameters of the soft THz excitation as a function of temperature for Ba1−xPbxFe12O19, x = 0.1 and x = 0.2 crystals: dielectric strength (c), resonance frequency (d), damping factor (e), and oscillator strength (f). The black line in d shows a fit of the resonance frequency for x = 0.1 with the power-law dependence \(\nu ^2 = A\left( {T - T_{\rm{C}}} \right)^\delta\), yielding δ = 0.5–0.6, Tc ≈ 3.3 K.

To determine whether some magnetic excitation can be the origin of the discovered THz soft mode, similar to Y- and Z-type hexaferrites27,28, we performed THz spectral measurements in external magnetic fields of up to 7 T (Faraday geometry) at temperatures of 4–300 K. No influence of the magnetic field on the spectra was detected, indicating a purely dielectric nature of the soft excitations in both x = 0.1 and x = 0.2 compounds. An additional confirmation of their dielectric origin is provided by the shape of the reflection coefficient spectrum, as demonstrated and discussed in Supplementary Information, Chapter SI3 and illustrated in Fig. SI31. This justifies the use of the dielectric Lorentzian expression (1) for least-square processing of the THz spectra ε′(ν) and ε″(ν) to obtain parameters of the soft modes observed in both Ba1−xPbxFe12O19 samples, x = 0.1 and x = 0.2:

$$\varepsilon ^ \ast \left( \nu \right) = \varepsilon ^\prime \left( \nu \right) + i\varepsilon ^{\prime\prime} \left( \nu \right) = \mathop {\sum}\nolimits_j {\frac{{f_j}}{{\nu _j^2 - \nu ^2 + i\nu \gamma_j}}} + \varepsilon _\infty ,$$
(1)

In Eq. (1), fj = Δεjνj2 is the oscillator strength of the jth resonance, Δεj is its dielectric strength, νj represents the resonance frequency, γj is the damping factor, and ε is the high-frequency dielectric constant. We used the high-frequency dispersion-free parts of IR reflectivity spectra (Fig. SI22) to determine the ε values: \(\varepsilon _\infty = 7.06\) for x = 0.1 and \(\varepsilon _\infty = 6.92\) for x = 0.2. The temperature dependences of the THz soft mode parameters (dielectric strength Δε, peak frequency ν, damping γ, and oscillator strength Δεν2) for both compounds are presented in Fig. 2c–f). Note that the modes are not of relaxational but of resonance type, which is evidenced by the dispersion in the real permittivity ε′(ν), typical of underdamped excitations, and by the small values of relative damping, γ/ν < 1. The frequency positions of the modes in both compounds nearly coincide, and they reveal significant decreases upon cooling down, from ≈30 cm−1 at room temperature to ≈10 cm−1 at 10 K (see Fig. 2d). This softening of the frequency is accompanied by a strong increase in the dielectric strengths Δε that differ slightly in the two materials.

The dependences of the resonance frequency positions ν(T) and dielectric strengths Δε(T) of the excitations resemble the temperature behavior of ferroelectric soft modes originating in structural phase transitions in ferroelectric materials29,30. However, in the present case, the ν(T) and Δε(T) temperature evolutions do not obey the corresponding Cochran, \(\nu ^2 = A\left( {T - T_{\rm{C}}} \right),\) and Curie–Weiss, \({\Delta}\varepsilon = C\left( {T - T_{\rm{C}}} \right)^{ - 1},\) laws (TC—Curie temperature, A—Cochran constant, C—Curie constant) typical of ferroelectrics. Instead, the temperature behavior of the resonance frequencies clearly follows power-law dependences

$$\nu ^2 = A\left( {T - T_{\rm{c}}} \right)^\delta$$
(2)

with the best fit parameters \(\delta = 0.5 - 0.6\) and critical temperatures Tc ≈ 3.3 K for x = 0.1 and Tc ≈ 1.5 K for x = 0.2 compounds. In addition, the damping constants remain, within the experimental uncertainty, temperature independent in the entire temperature range; this is also unusual for “standard” ferroelectric soft modes. One more specific feature of the soft excitations observed in the Ba1−xPbxFe12O19 compounds should be pointed out: their oscillator strengths strongly decrease as the temperature is lowered (Fig. 2f), which is in strong contrast to regular ferroelectrics, wherein the soft modes usually maintain their oscillator strengths constant with temperature. Such a weakening could occur if the excitation was coupled to an additional vibrational process. Since no noticeable change with temperature in the total dielectric contributions of all IR-active phonons (Fig. 1c) was detected, the strengths of the soft modes might be transferred to the lower-frequency gigahertz resonance seen in Fig. SI41 or to acoustical phonons. Unfortunately, parameters of the gigahertz resonance could only be determined from the data extrapolated from THz and radiofrequency ranges (see below), and consequently, its oscillator strength is found with a rather large uncertainty. Nevertheless, it is clearly seen from Fig. SI42 (panel d) that the excitation strength does not show any sign of increase upon cooling. Therefore, we exclude its coupling to the soft mode. Further detailed microwave dielectric measurements are required to gain additional information on this resonance. Possible coupling of the mode to acoustic phonons is discussed below.

We note that the discovered soft excitation is observed for polarization \(E \bot c\), i.e., when the electric field component of the probing THz radiation couples to the electric dipole moments that exist within the ab-plane. Previous studies on hexaferrites revealed temperature-dependent excitations in another geometry, E||c. For example, in ref. 21, a soft excitation (though at slightly higher frequencies) and the corresponding incipient ferroelectric temperature behavior of the low-frequency dielectric permittivity were observed in undoped BaM in the E||c response, with no indications of any soft mode-like effects in the orthogonal polarization \(E \bot c\), as in the present case.

We suggest the following two mechanisms that can be responsible for the appearance of the unusual soft mode in Pb-doped hexaferrites.

In the hexaferrite lattice, the Ba cuboctahedron is symmetrically surrounded by three bipyramids. The Ba ions occupy central positions in the oxygen cuboctahedron with six oxygen ions surrounding each Ba ion in the ab-plane (Fig. SI2–1b, top). When Ba is substituted with Pb, the interaction of the lone 6s2 electron pair of Pb2+ with neighboring oxygens leads to the shortening of Pb-O bonds22 in comparison to Ba-O bonds31, which manifests itself in an off-center shift of Pb2+ toward one of the oxygen vertices22 (Fig. SI2–1b, bottom). This, in turn, leads to a distortion of the ionic surroundings, redistribution of electron density, and the appearance of a net electric dipole moment in the ab-plane. (If the Pb ions were located in the center of its oxygen coordination, the dipole moments induced in the three surrounding trigonal bipyramids would compensate for each other, and the net dipole moment would be zero). Since the Pb ion is surrounded by six oxygen atoms, at low enough temperature, it can find itself in one of six local minima within the ab-plane.

At sufficiently high temperatures, the Pb ion will be able to hop between the six potential wells, which can be effectively regarded as if the corresponding induced dipole moment changes its direction during the whole 360 degree rotation within the ab-plane. Due to the long-range character of the electric dipole–dipole interaction, separate dipoles of the described type will interact, with the tendency toward ordering at certain low temperatures, as happens in paraelectric phases of ferroelectrics. One can expect that the dielectric response of such coupled dipolar systems can be expressed in the form of soft excitation analogous to the paraelectric soft modes in systems with a crossover from the displacive to the order–disorder type of ferroelectric phase transition (see, e.g., refs. 29,30). When the temperature decreases and the thermal energy kBT becomes smaller than the energy barrier A between the potential wells (here kB is the Boltzmann constant), a certain fraction of the Pb ions progressively resides in the wells, and the fraction of quasi-free dipoles decreases in accordance with the Boltzmann exponential factor exp(−A/kBT). The dielectric response of such a system of coupled rotating electric dipoles was analyzed within the mean-field approach in refs. 32,33 for the rotational potential felt by a dipole containing two and four potential minima, respectively. According to ref. 32, for the case of a potential with two wells, at high temperatures, when the thermal energy exceeds the barrier height A separating the wells (kBT > A), there will be an optical soft mode in the dielectric spectra that originates in freely interacting rotating dipoles. During cooling, the number of these dipoles that are responsible for the soft mode-like response will decrease proportionally to the Boltzmann exponent exp(−A/kBT), and correspondingly, progressively more dipoles will be localized within the wells and respond via librations (restricted rotations) to external perturbations. Depending on the coupling strength and barrier height, the soft mode dielectric strength Δε (its contribution to the static permittivity) can follow the Curie–Weiss dependence Δε = C(T − TC)γ, γ = −1, or exhibit certain deviations from it toward lower absolute values of the exponent, |γ| < 1. Along with that, the temperature dependence of the soft mode frequency is also expected to reveal deviations from the Cochran law \(\nu ^2 = A\left( {T - T_{\rm{C}}} \right)\), as demonstrated in ref. 34 for the case of interacting classical anharmonic oscillators in the two-well potential. Since the abovementioned mean-field results predict the existence of the two principal features we observe in our experiments—the soft mode and the decrease in its strength upon cooling—we suggest that the described considerations can be qualitatively applied to our case when the rotating dipoles are produced by Pb ions experiencing six-well potential. It is worth noting that the described model was effectively used to interpret the paraelectric response of isolated nanoconfined polar water molecules embedded in beryl crystals35.

As an alternative explanation, the peculiar dependence of the THz soft mode on temperature, \(\nu \propto \left( {T - T_{\rm{c}}} \right)^\delta\) with \(\delta \approx 0.25\), observed in our experiment can be explained by ion oscillations in the quartic potential of the form \(V\left( Q \right) = \left( {a/2} \right)Q^2 + \left( {b/4} \right)Q^4\) (here a and b are constants, Q is a coordinate). Indeed, for large values of the coordinate \(Q\), a thermally averaged harmonic part of the potential \(V\left( {Q + {\Delta}Q} \right)\) as a function of the fluctuation \({\Delta}Q\) can be written as \(V_{\rm{h}}\left( {{\Delta}Q} \right) = \left( {a + 3bQ^2} \right){\Delta}Q^2/2\). For small values of the coefficient a, \(a \approx 0\), which can be expected for small values of \(T_{\rm{c}}\), the thermal average of the coordinate in the classical limit (at high temperatures) is given by the equipartition theorem as \(bQ^4 = k_{\rm{B}}T\). Thus, we can estimate \(Q^2 = \left( {k_{\rm{B}}T/3b} \right)^{1/2}\) (where we have assumed \(Q^4 = 3Q^{22}\) as for the normal distribution), and we obtain a temperature dependence of the soft mode frequency, \(\omega ^2 \approx \left( {3bk_{\rm{B}}T} \right)^{1/2}/m\), close to that observed experimentally. According to recent X-ray diffraction data36, only Pb and Fe(2) ions have large mean square displacements in the ab-plane, which may indicate anharmonicity of their potentials: for x = 0.23, 0.44 and 0.8, the square displacements are 0.0252, 0.0436, and 0.0687 Å2 for the Ba/Pb ions and 0.0097, 0.0114, and 0.0155 Å2 for the Fe(2) ions, respectively. We assume that the largest displacements correspond to the Pb- and Fe-ion potentials, while the smaller displacements are due to the presence of Ba ions and statistical averaging. Given the measured phonon frequency of approximately \(\omega = 2\pi \cdot 30\) cm−1 at \(T = 300\) K, we estimate \(b = 8054\) meV Å−4 for Pb ions and \(b = 584\) meV Å−4 for Fe(2) ions. The calculated ground state square displacement of \(0.0219\) Å2 for the Fe(2) ion in the potential with the above coefficients \(b\) and \(a = 0\) is consistent with the experimental data. At the same time, the calculated square displacement for the Pb ion, \(0.0059\) Å2, turns out to be significantly smaller. Thus, we conclude that the observed soft mode may be due to the anharmonic softening of Fe(2) ion oscillations. These ions lie in the same plane as Ba/Pb ions and can be affected by the nearest Ba/Pb substitution.

With the energy spectrum \(E_n\) and wave functions of the Fe(2) ions in the quartic potential, we calculate the corresponding imaginary part of the dielectric susceptibility37

$$\alpha ^{\prime\prime} = \frac{1}{{\hbar Z}}{\sum} {\left( {e^{ - E_n/k_{\rm{B}}T} - e^{ - E_m/k_{\rm{B}}T}} \right)} \frac{{\left| {x_{nm}} \right|^2\gamma _{nm}}}{{\left( {\nu + \nu _{nm}} \right)^2 + \gamma _{nm}^2}},$$
(3)

where \(Z = {\sum} {e^{ - E_n/k_{\rm{B}}T}}\) is the partition function, \(\nu _{nm} = \left( {E_n - E_m} \right)/\hbar\) is the transition frequency between states \(n\) and \(m\), \(x_{nm}\) is the matrix element of the coordinate along the electric field (which we suppose coincides with the coordinate \(Q\)), and \(\gamma _{nm}\) is the sum of the widths of the two states. The calculated real part of the alternating current (AC) conductivity, \(\sigma ^\prime = \nu \alpha ^{\prime\prime}\), for \(\gamma _{nm} = 10\) cm−1, is shown in Figure SI51 (AC conductivity characterizes electromagnetic absorption due to ionic oscillation). The calculated peak conductivity (which is related to the mode strength) value becomes larger at low temperatures, in contrast to our experiment. At the same time, our calculations are consistent with the available optical conductivity calculations in the q quantum38,39,40 and classical32,34,35,41 approximations for an ion in the quartic potential. We explain the experimentally observed decrease in the strength of the THz soft mode at low temperature by its interaction with acoustic phonons (see, e.g., refs. 42,43).

Making the final verdict regarding the microscopic mechanism of THz soft excitation needs more experimental and theoretical efforts. Note also that there are additional factors that can add to the observed exotic temperature variations of the soft mode frequencies and dielectric strengths, for instance, the rather complex structure of the studied compounds. Such complexity can make the soft mode couple to the magnetic subsystem (the possibility of spin–phonon coupling in hexaferrites has been reported in, e.g., refs. 9,44,45,46,47,48). Additionally, we cannot exclude a coupling between the soft mode and the transitions within fine-structure components of the 5E ground state of tetrahedrally coordinated Fe2+, since the frequencies of both types of excitations are close or even overlap, as discussed above (see Fig. 1).

One more aspect should be considered for the physics of the studied hexaferrites: there are indications that quantum critical phenomena can play a significant role in their dynamic properties. First principles calculations along with Monte Carlo simulations using the dipole–dipole interaction model7 indicate the possibility of a phase transition in BaM at Tc = 3 K into a geometrically frustrated antiferroelectric state. Kumar and Pandey49 claimed an observation of a phase transition in Ca-substituted BaM at similar temperatures. They showed that the temperature of the phase transition rises with the concentration of the dopant in a manner characteristic of the phase transitions in a quantum critical regime. Ca2+ generates a positive chemical pressure within the BaM matrix, and as a result, it leads to a decrease in the unit cell parameters. The rise of the transition temperature Tc is connected with an increasing dipole–dipole interaction strength in and out of the ab-plane with shortening of bonds in the trigonal bipyramids due to the effect of positive chemical pressure. Accordingly, the positive chemical pressure can stabilize a quantum electric dipolar glass state and drive the system away from the quantum critical point49. It was further predicted that a negative chemical pressure should decrease the critical temperature of the transition and bring the substituted BaM closer to the quantum critical point. Negative chemical pressure can be produced in the BaM matrix by the substitution of Ba2+ with Pb2+, resulting in the Ba1−xPbxFe12O19 materials studied here. According to our X-ray analysis (see Section SI1 in Supplemental Information), the addition of Pb2+ favors an expansion of the ab face in the unit cell of the Ba1–xPbxFe12O19 compounds, indicating that Pb2+ indeed generates a negative chemical pressure. When modeling the temperature dependences of the THz soft mode frequency by Eq. 2, the critical temperature Tc is lower in the compound with a larger content of Pb2+, in agreement with the suggestions of Kumar and Pandey49. Rowley et al.50 found evidence of the proximity of pure hexaferrites BaM and SrFe12O19 to the quantum critical point, which was indicated by a pronounced rise in the dielectric permittivity upon cooling. They also showed that, although pure BaM is expected to change its phase from paraelectric to antiferroelectric at approximately 6 K, this transition is suppressed due to quantum fluctuations and does not occur at finite temperature. Evidence of the existence of quantum paraelectric phases in M-type hexaferrites was also reported in refs. 7,12,13,49.

With the above taken into account, we consider the THz soft mode observed in the studied compounds as a possible fingerprint of a (quantum) phase transition that could happen in Ba1−xPbxFe12O19, if not suppressed by quantum fluctuations, below the lowest temperatures of 4 K used in our experiments. It might be that doping with Pb destabilizes the coupled spin–phonon system in the material and brings it close to a quantum phase transition that can be driven by Pb doping, wherein the critical concentration can be close to x(Pb) = 0.2. This is evidenced by the critical temperatures obtained by fitting our data using Eq. 2, yielding a decrease from Tc ≈ 3.3 K for x = 0.1 to Tc ≈ 1.5 K for x = 0.2. It is known that, in the critical temperature region around the phase transition, when quantum effects come into play, the inverse dielectric constant of the corresponding soft excitation obeys a power law (Δε)−1 ~ Tγ with a critical exponent γ = 2 for multiaxial dipole orientations when polarization is allowed to change along any direction51,52,53. Because we could not determine the soft mode dielectric strength precisely enough, we cannot make a firm conclusion on this theoretical prediction in the case of our hexaferrites. To clarify this matter, systematic and more detailed investigations on the spectroscopic properties of Ba1−xPbxFe12O19 crystals with a series of x(Pb) and in both polarizations, \(E \bot c\) and E||c, are in progress.

Phonon resonances in Ba1−xPbxFe12O19

For the Ba1−xPbxFe12O19, x = 0.2 sample, the spectrum of complex dielectric permittivity in the range from 1 Hz to 30 THz (10−11–103 cm−1) is shown in Fig. 1a, b. One can see that IR phonon resonances (sharp peaks >80 cm−1) are nearly temperature independent down to T = 10 K: all IR spectra practically coincide at frequencies above ≈100 cm−1. The low-temperature drop in the intensity of the phonon peak at ≈90 cm−1 is caused by the softening of the THz absorption mode, as discussed above in Section 2.1. For an extended description of the IR phonon resonances for both compounds under study, see Supplemental Information, section SI2. The spectral response of the lattice vibrations observed in our compound is in line with the results obtained in other isostructural phases, such as pure BaM21 and Pb-substituted Ba0.3Pb0.7Fe12O1923.

Radiofrequency and microwave relaxations

Figure 1 clearly shows that the dielectric response of Ba1−xPbxFe12O19, x = 0.2, compound at low frequencies, 1 Hz–300 MHz, strongly depends on both frequency and temperature. A similar behavior was found for the x = 0.1 compound. The multiple steps in ε′(ν) and the peaks and corresponding shoulders in the ε″(ν) spectra indicate a rather complex relaxational behavior. The spectra at the highest temperature shown (297 K) reveal a noticeable mismatch between the results from the frequency response (ν 1 MHz; open circles) and those from the reflectometric techniques (ν 1 MHz; closed circles), performed with the different types of electrodes and sample geometries. This points to an extrinsic origin of the relaxations observed at high temperatures54, as discussed in detail below. However, the limiting plateau value on the order of ε′ = 30, approached at low temperature and high frequencies, should be of intrinsic nature, and it reflects the ionic and electronic polarizability of the material (termed ε in dielectric spectroscopy). Its offset (on the order of 20) compared to the low-frequency values of the THz data indicates additional processes occurring in the frequency gap between 10−2 and 4 cm−1.

The low-frequency dielectric spectra are shown in more detail in Fig. 3, where it is seen that there are at least three temperature-dependent relaxational processes in the radiowave and microwave ranges. Upon cooling from room temperature down to 60–70 K, two relaxational loss peaks (marked as I and II in Fig. 3c) pass through the frequency window of our experiment (1 Hz–4 MHz), accompanied by the corresponding step-like features in the spectra of the real permittivity ε′(ν) (Fig. 3a). A third process (termed III) enters the experimental window when the temperature is lowered down to approximately 40 K, and it removes the window at T < 7 K (Fig. 3b, d). In contrast to processes I and II (cf. Fig. 1), its behavior as detected by frequency-response analysis (up to approximately 1 MHz) is consistent with that detected by the reflectometric technique (beyond 1 MHz, see Fig. 3b), pointing to an intrinsic origin. In the spectra at T = 15 and 19 K (Fig. 3b), a small additional ε′(ν) step is superimposed on the main relaxation at low frequencies. This indicates a fourth process, discussed in more detail below. At 33 and 43 K, only the low-frequency wings of the loss peaks are detected (Fig. 3d). Employing a closed-cycle refrigerator with shorter coaxial lines allowed reliable measurements up to approximately 200 MHz; however, the temperature was limited to 33 K.

Fig. 3: RF relaxations in lead-substituted BaM.
figure3

Radiofrequency spectra of the real (a, b) and imaginary (c, d) parts of the dielectric permittivity of Ba1−xPbxFe12O19, x = 0.2, measured at different temperatures for polarization \(E \bot c\). Solid lines represent the results of least-square fitting with Eq. (4). The Roman numerals in circles denote the three relaxational processes clearly visible in this figure. The dashed lines are guides to the eye.

The three relaxation features were modeled using the empirical Havriliak–Negami expression for the complex dielectric permittivity (solid lines in Fig. 3):

$$\varepsilon ^ \ast \left( \nu \right) = \varepsilon ^\prime \left( \nu \right) + i\varepsilon ^{\prime\prime} \left( \nu \right) = \mathop {\sum }\limits_k \frac{{{\Delta}\varepsilon _k}}{{\left( {1 + \left( {i2\pi{v}{\tau}_k} \right)^{1 - \alpha}} \right)^\beta }}.$$
(4)

Here Δεk is the dielectric strength of the k-th relaxation; τk is the mean relaxation time of the relaxation process, and α and β are coefficients describing the broadening and asymmetry of the relaxational spectral response, respectively; their temperature dependences are presented in Fig. SI61 in the Supplementary Information. The fits were only performed for temperatures wherein peak frequencies (in ε″) and/or points of inflection (in ε′) could be clearly discerned in the spectra.

The relaxation processes are often revealed more clearly in temperature-dependent plots of the permittivity, especially if the relaxations appear close to the device operation limit, as is the case for process III (cf. Fig. 3d). Figure 4a, b displays the temperature dependences of the real ε′ and imaginary ε″ parts of the dielectric permittivity measured at various fixed frequencies (solid lines). These plots reveal four pronounced anomalies with shapes typical of relaxational processes (peaks in ε″ and steps in ε′). Their frequency-dependent character is better visible in a plot of the temperature-dependent AC conductivity σ′(T) (Fig. SI62), wherein the different curves exhibit less overlap due to the offset caused by the relation σ′(T) ~ νε″(T). The inset of Fig. 4b provides a magnified view of ε′(T) for the two low-temperature relaxations, revealing a weak but significant increase in their static real permittivity with decreasing temperature, in accordance with the temperature-dependent static dielectric constant becoming obvious in Fig. 3b. Comparing the frequencies and temperatures of the occurrence of these four processes with those in Fig. 3, three of them can be clearly identified with relaxations I, II, and III, discussed above. The features emerge when, during cooling, the relaxational peaks in ε″(ν) and the corresponding points of inflection in the ε′(ν) spectra of processes I, II, and III shown in Fig. 3 move into the measurement frequency interval. Interestingly, in Fig. 4, a weak additional process (IV) is detected between approximately 20 and 40 K and depends on the frequency. We note that the temperature-dependent plots in Fig. 4 point to the absence of any phase transition at low temperatures down to T ≈ 2 K, which is also evident from the smooth temperature dependence of the specific heat (see Fig. SI71 in the Supplementary Information) and from IR spectra (Figs. 1c and SI22) where no extra (folding) phonons were observed that would indicate structural changes in the lattice.

Fig. 4: Parameters of the RF relaxations.
figure4

Temperature dependences of the real (a) and imaginary (b) parts of the dielectric permittivity of Ba1−xPbxFe12O19, x = 0.2, measured for polarization \(E \bot c\) at different frequencies (solid lines). The crosses in b show results at 0.95 MHz as measured in a different set-up and for a sample with different geometry and electrodes. The Roman numerals denote the four detected relaxation processes (extrinsic: I and II; intrinsic: III and IV). The comparison between the data obtained on different samples utilizing different set-ups clearly illustrates the intrinsic character of relaxations III and IV (see text). c, d show Arrhenius plots of the temperature dependences of the relaxation times that correspond to the relaxational excitations observed in the low-frequency complex dielectric permittivity spectra of Ba1−xPbxFe12O19 with x = 0.2. The values correspond to the four peaks I–IV seen in the ε″(ν,T) data (b and Fig. 3). The closed spheres were deduced from fits of the ε′(ν) and ε″(ν) spectra (Fig. 3), whereas the open symbols were derived from the temperature-dependent data of b and Fig. SI6–2, which only provided an estimate of τ. The straight lines evidence a temperature-activated behavior with the activation energies as indicated. The temperature dependences of the dielectric strengths of relaxations I–III are shown in e, f. The dashed lines are guides to the eye.

The pluses in Fig. 4b represent ε″(T) results for 0.95 MHz as measured independently in a special experimental set-up (Using a Janis He-flow cryostat in Prague instead of the Cryovac He-bath cryostat in Augsburg) for another sample with different geometries and contacts. The agreement in the region of relaxations III and IV clearly points to their intrinsic origin. In contrast, marked differences in the region of high-temperature relaxations I and II are observed, which we also found for various other measurements performed with different set-ups and for various samples with particular types of electrodes. As already suggested above based on Fig. 1, this proves the extrinsic, most likely contact-related origin of these processes. It is well known that extrinsic, so-called Maxwell–Wagner relaxations can arise, e.g., due to the formation of Schottky barriers at the sample–electrode interfaces, which leads to deviations, as observed in the present case54.

The temperature-dependent results of Fig. 4 (and in Fig. SI6–2) provide an additional way to estimate relaxation times as a function of temperature by determining the loss peak temperatures Tp for a given measurement frequency ν. For T = Tp, the relaxation time is given by τ(T) = 1/(2πν). This enables an extension of the covered temperature and frequency range for τ(T), albeit with a somewhat reduced precision compared with the relaxation times deduced from fits of the frequency-dependent data (Figs. 1 and 3). Figure 4c, d give an Arrhenius presentation of the relaxation times τ of the four detected processes. The τ(T) data follow an activated behavior with four activation energies: 110 meV (process I), 150 meV (process II), 18 meV (process III), and 43 meV (process IV). According to Fig. 4e, f, the dielectric strengths Δε of relaxations II and III do not change with temperature in the shown temperature intervals. The dielectric strength of relaxation I reveals a strong decrease upon cooling down to 150 K, but it levels off at lower temperatures. The dielectric strength of process IV is too weak to allow for any unequivocal determination of its temperature dependence. The Δε results for process III (Fig. 4f) are also of limited precision because of the superimposed contribution of process IV, which was not considered in the fits.

Whereas relaxations I and II are extrinsic, intrinsic relaxations III and IV might manifest the dynamic response of dielectric or magnetic domains, similar to a related compound with a higher concentration of Pb, Ba0.3Pb0.7Fe12O1923. In that compound, pronounced dielectric and magnetic relaxational dynamics were detected in the radiofrequency range; both relaxations exhibited similar characteristic relaxation times, evidencing the birelaxor-like nature of Ba0.3Pb0.7Fe12O1923. Our magnetic/electrostatic force microscopic experiments clearly indicate the presence of magnetic domains in pure BaM (Fig. SI8–1, SI8–2, SI8–3 in Supplementary Information). Thus, relaxation-like dispersion was observed in the magnetic susceptibility spectra of Ba0.8Pb0.2Fe12O19 (Fig. SI9–1, SI9–2) should be associated with magnetic domain dynamics. Regarding dielectric relaxations III and IV, we suggest that their origin should be related to the response of magnetic domain walls, which are electrically polar in the present compound. The mechanism of the emergence of electric polarization in magnetic domain walls is analyzed in ref. 55 taking iron garnet as an example. We firmly detect the electrical polarity at the boundaries of magnetic domains in undoped BaM (Fig. SI8–2). At the same time, in Pb-doped Ba0.8Pb0.2Fe12O19, along with the clearly visible magnetic domain structure (Fig. SI8–3), we were not able to detect any sign of the domain polarity, which is most likely beyond the sensitivity of the technique used. This last suggestion is confirmed by the low values of dielectric strengths of the two relaxations, III and IV, Δε < ≈10, which is by orders of magnitude less than those seen in pure BaM (Δε ≈ 1000)23. We also note a considerable difference in the activation energies of these relaxations, 18 meV (III) and 43 meV (IV).

Gigahertz resonances

Although our experiments did not cover the spectral range between several GHz and ~100 GHz, our measurements indicate that some excitations exist in this frequency interval. First, this is evidenced by a “step” in the spectra of the real permittivity between the radiofrequencies and THz frequencies, as seen in Fig. 1a. In addition, below 20 cm−1, there is a clear decrease in the real part of permittivity ε′(ν) and, below 10 cm−1, an increase in its imaginary part ε″(ν) (see Fig. SI4–1). Both of these features are linked together, and they strongly suggest the existence of a resonant absorption band located below 3 cm−1 (90 GHz). Assuming its purely dielectric nature, we were able to apply expression (1) to model its spectral response with a dielectric Lorentzian, which let us estimate the values and the temperature dependences of its parameters. Examples of the corresponding least-square fits of the room-temperature spectra are given in Fig. SI4–1. As demonstrated in Fig. SI4–2, there are no strong changes with temperature in the frequency position and damping parameter of the excitation; additionally, its dielectric and oscillator strengths show signs of a decrease in cooling. Note that the dielectric strength of the resonance practically matches the “step” between the radiofrequency and THz values of real permittivity (Fig. 1a), signifying that there are no additional absorption bands in the range except the one at 2–3 cm−1. For the microscopic origin of the detected GHz band, we cannot exclude that it can be of mixed magnetoelectric origin56,57. Some evidence for that is given by the coincidence (within experimental uncertainties) of its frequency position with the value of the frequency of FMR in the Ba0.9Pb0.1Fe12O19 crystal obtained by the extrapolation of the magnetic field-dependent frequency of the resonance to zero magnetic field (Fig. SI10–1); the oscillator strength of the FMR remains constant (Fig. SI10–2).

Conclusions and prospects for use in THz electronics

Our thorough spectroscopic studies of the broad-band (1 Hz up to 240 THz) temperature-dependent (5–300 K) electromagnetic properties of Ba1−xPbxFe12O19 single crystals found a rich variety of strongly temperature- and doping-dependent electric, magnetic, and possibly magnetoelectric excitations. Most intriguing from both fundamental and applied points of view is the complex electromagnetic response of the compounds at THz frequencies that is determined by electronic transitions between the fine-structure components of the 5E ground state of tetrahedrally coordinated Fe2+ ions, which overlap with a soft excitation whose temperature evolution resembles that of a ferroelectric soft mode. A close inspection reveals, however, that the temperature dependences of the resonance frequency and strength do not follow the corresponding Cochran and Curie–Weiss laws known to describe soft modes in classical ferroelectrics. We proposed microscopic models that qualitatively explain the observed nonstandard behavior of the excitation. The radiofrequency electrodynamic characteristics of the studied compounds are fully determined by relaxational processes that are related to the Maxwell–Wagner polarization and to the dynamics of magnetic domain walls. Our findings are an important step toward a deep understanding of the physics behind the electromagnetic response of the studied hexaferrites from radiofrequency all the way up to THz and IR.

A few words on applicational aspects of the studied materials are in order. The rapidly developing field of forthcoming THz electronics motivates the search for materials that satisfy the ever-increasing requirements; see, e.g., ref. 58 and references therein59. With the results presented here, we demonstrate that hexaferrites are among the most promising candidates. Being planar, self-biased, and low-loss materials, hexaferrites meet the requirements for the development of microwave and THz circulators, phase shifters, filters, isolators, and millimeter-wave resonator antennas15,16,56,60. These compounds are considered one of the most promising material classes for telecommunication systems61. In ref. 61, it was shown that a BaFe12O19-polydimethylsiloxane nanocomposite exhibits a zero-bias (no external magnetic field) FMR at a frequency of 46.6 GHz and is thus proposed for the design of a circulator with an operating frequency of 35 GHz. The absorption resonances at even higher frequencies of approximately 50 and 100 GHz that we discovered in the present study in single crystalline Pb-doped hexaferrites Ba1−xPbxFe12O19 make these compounds promising candidates for manufacturing self-biased devices with working frequencies meeting standards of higher generations in telecommunications. Considerations of the possibilities of the intentional tuning of the resonance frequency with dopant content x or (moderate) external magnetic fields are in progress, as well as the characterization of ceramic, sputtered films and nanocomposite forms of the compounds. Metamaterials and composites based on hexaferrites are also used to develop circulators for 5G technology62,63, low-loss sub-THz isolators, resonators, filters, and phase shifters64. Hexaferrite-piezoelectric and hexaferrite-ferroelectric composites have been proposed for tunable devices to control THz radiation65, particularly for dual electric and magnetic field tunable resonators, filters, and phase shifters operating at THz frequencies. Dielectric anisotropy of BaM is employed in millimeter-wave resonators56,66. There are still some problems to overcome. For example, when thin films of lead-substituted barium hexaferrite are used, one has to sustain a proper and homogeneous substitution level over the film surface, as lead substitutes barium in the crystal lattice rather chaotically. Such a problem is not inherent in bulk materials owing to the averaging of the lead content throughout the volume.

Information on the broad-band electronic and/or dielectric properties of hexaferrites is also in demand when developing devices based on monitoring the direct current resistivity or AC impedance of thin films of diverse morphologies. One of the hottest and most promising areas today includes the development of chemical or biological sensors; see, e.g., refs. 67,68,69. Additionally, in this area, barium hexaferrite and corresponding substituted compounds reveal encouraging results. Corresponding perspectives include ozone sensors70, ammonia sensors71, and acetone and ethanol sensors72. Considering ammonia detection, sensors based on hexaferrites71 reveal much higher sensitivity (lowest targeted gas concentration) than MO3-based sensors69.

The growth of high-quality single crystals with desirable (enhanced) size remains a challenge. Methods to synthesize powder, ceramic, and polycrystalline forms of hexaferrites are well developed. However, fundamental studies and specific applications (e.g., optically active media, polarizers, phase shifters) require relatively large single crystals with reproducible properties independent of the growth technique, a feature that is not inherent to noncrystalline forms of the material. On the other hand, there are a number of advantages that make Ba-Pb hexaferrites attractive. They are nontoxic (even despite the presence of toxic lead in the chemical formula) and corrosion-stable. They are cheap to produce since the oxides needed in the synthesis are waste from machinery fabrication, which in turn makes production eco-friendly. Although the production of hexaferrites is a billion dollar income business, they are currently used mainly in the microwave magnetic device market. The lack of information on THz characteristics discourages their wide application for the development of forthcoming THz devices. At the same time, the number of yearly publications on the THz physics of hexaferrites is growing rapidly, which will trigger their use in the electronic industry. In this respect, a significant result of the present work is the quantitative information on the electrodynamic properties of hexaferrites in an extremely wide frequency range, including bands that are most attractive from the viewpoint of the development of next-generation subTHz–THz communication systems and the fabrication of THz-tunable electronic components, such as band-stop filters, phase shifters, and attenuators, surpassing existing analogs in their characteristics56,73,74. We have unveiled the fundamental physical mechanisms that determine these properties. Taking into account the multiferroic properties of barium hexaferrites75,76,77, the area of their possible applications can expand remarkably.

Methods

Sample preparation

Single crystals of Pb-substituted barium hexaferrite with chemical compositions Ba1−xPbxFe12O19 (x = 0.1 and 0.2) were grown using the flux method. Crystal growth and characterization are described in section SI1 of the Supplemental Information. For spectroscopic THz and IR measurements, the crystals were carefully oriented (see section SI1 in Supplemental Information) and then prepared as plane-parallel (to within a few micrometers) plates with the crystallographic c-axis oriented perpendicular to plate surfaces; this geometry allowed for measurements with the linear polarization of the electric field E-vector of the probing radiation lying within the ab-planes, \(E \bot c\). Both sides of the prepared plates were carefully polished with diamond lapping films to meet the requirements of THz–IR measurements. The sizes of the samples for THz and IR measurements were approximately 3 mm × 4 mm with thicknesses of 335 µm (x = 0.1) and 452 µm (x = 0.2). For measurements at frequencies from 1 Hz up to the microwave range (1 GHz), specimens were fabricated as thin plane-parallel polished plates with thicknesses of 174 μm (Augsburg) and 758 μm (Prague) with the c-axis parallel to the plate surfaces, thus allowing for measurements in the \(E \bot c\) geometry.

THz–IR spectroscopy

Experiments in the THz range (at frequencies ν = 8–100 cm−1, 0.24–3 THz) were conducted with the help of two time-domain spectrometers, Menlo Tera K15 and TeraView TPS 3000. The spectra of the complex transmission coefficient (amplitude and phase) of the plane-parallel samples were measured, and the spectra of complex dielectric permittivity ε*(ν) = ε′(ν) + ″(ν) were calculated using standard Fresnel equations78. In the far-IR and mid-IR spectral regions (30–8000 cm−1, 0.9–240 THz), a standard Fourier transform spectrometer Bruker Vertex 80 was utilized for the measurements of reflectivity spectra. To measure reflectivity at the lowest frequencies (25–80 cm−1), a Bruker 113v Fourier transform spectrometer with a helium-cooled bolometer was used. The experiments were performed over a wide range of temperatures (5–300 K) using exchange-gas and cold-finger cryostats. For the experiments in external magnetic fields of up to 7 T, Spectromag Oxford cryomagnets attached to a Fourier transform IR spectrometer Bruker 113v and to a custom-made time-domain THz spectrometer were employed.

Radio frequency impedance spectroscopy

At frequencies from ≈1 Hz to ≈200 MHz and at temperatures from 5 K to 300 K, the dielectric response of the samples was measured using a Novocontrol Alpha frequency-response analyzer and a Keysight 4991B impedance analyzer. For cooling, a closed-cycle refrigerator (CTI-Cryogenics), a He-flow cryostat (JANIS ST-100), and a He-bath cryostat (Cryovac) were used. For the measurements at frequencies of up to approximately 4 MHz, Pt-Au electrodes were evaporated using a Bal-Tex SCD 050 sputter coater onto the principal faces of the samples or silver paste layers were directly applied as electrodes. The connections for applying the AC electric field were provided by silver or copper wires fixed to the electrodes by silver paste. For frequencies above approximately 1 MHz, a coaxial reflectometric set-up was used, employing the impedance analyzer as described in ref. 79. Here the sample was mounted between two metal plates at the end of a coaxial line. Depending on the cooling devices used, the dielectric response of the samples was measured in vacuum or helium atmospheres, which did not significantly influence the measured dielectric properties. The precise determination of the absolute values of the complex dielectric permittivity is hampered by the occurrence of stray capacitances and geometrical uncertainties, which play a role, especially for rather small single crystals, as investigated in the present work. For the frequency-response measurements below approximately 4 MHz, the largest samples were available. Here different samples with different geometries and contact configurations were independently measured by the Prague and Augsburg groups, yielding comparable absolute values in the frequency/temperature ranges dominated by intrinsic effects. The less precise high-frequency results obtained by the reflectometric method were scaled to the low-frequency results by a single factor for all data obtained during a measurement run.

Heat capacity measurements

The temperature dependence of the heat capacity cP was measured (via the standard relaxation method) using the heat capacity option of the Physical Property Measurement System (Quantum Design).

Magnetic force microscopy

With scanning probe microscopy, we investigated two samples, BaFe12O19 and Ba1−xPbxFe12O19 (x = 0.2), to prove the multiferroiс nature of the crystals. We used magnetic force microscopy to observe the magnetic domain structure under low temperature (4.5 K) and ambient conditions. For low-temperature measurements, the AttoDRY 1000 system with the possibility of applying a magnetic field was used. For room-temperature investigations, we used the NT-MDT AFM device. These magnetic force measurements were performed with a Bruker MESP-V2 cantilever. Both crystals show similar domain structures with negligible temperature dependences and a clear magnetic response to the external magnetic field. After that, we used a conductive (PtIr coated, Bruker) cantilever to check the electrostatic response of the samples. In BaM, an electrostatic polarization of magnetic domain boundaries is clearly observed, whereas in the Pb-doped crystal, no such effect was detected.

References

  1. 1.

    Sakai, K. & Tani, M. in Terahertz Optoelectronics 1–30 (Springer-Verlag, 2005).

  2. 2.

    Aghasi, H. et al. Terahertz electronics: application of wave propagation and nonlinear processes. Appl. Phys. Rev. 7, 021302 (2020).

    CAS  Article  Google Scholar 

  3. 3.

    Romanczyk, B. et al. W-band power performance of SiN-passivated N-polar GaN deep recess HEMTs. IEEE Electron Device Lett. 41, 349–352 (2020).

    CAS  Article  Google Scholar 

  4. 4.

    Song, H.-J. & Nagatsuma, T. Present and future of terahertz communications. IEEE Trans. Terahertz Sci. Technol. 1, 256–263 (2011).

    Article  Google Scholar 

  5. 5.

    Tonouchi, M. Cutting-edge terahertz technology. Nat. Photonics 1, 97–105 (2007).

    CAS  Article  Google Scholar 

  6. 6.

    Williams, B. S. Terahertz quantum-cascade lasers. Nat. Photonics 1, 517–525 (2007).

    CAS  Article  Google Scholar 

  7. 7.

    Wang, P. S. & Xiang, H. J. Room-temperature ferrimagnet with frustrated antiferroelectricity: promising candidate toward multiple-state memory. Phys. Rev. X 4, 011035 (2014).

    CAS  Google Scholar 

  8. 8.

    Kimura, T. Magnetoelectric hexaferrites. Annu. Rev. Condens. Matter Phys. 3, 93–110 (2012).

    CAS  Article  Google Scholar 

  9. 9.

    Laguta, V. et al. Magnetoelectric coupling in multiferroic Z-type hexaferrite revealed by electric-field-modulated magnetic resonance studies. J. Mater. Sci. 55, 7624–7633 (2020).

    CAS  Article  Google Scholar 

  10. 10.

    Zhai, K. et al. Giant magnetoelectric effects achieved by tuning spin cone symmetry in Y-type hexaferrites. Nat. Commun. https://doi.org/10.1038/s41467-017-00637-x (2017).

  11. 11.

    Chun, S. H. et al. Electric field control of nonvolatile four-state magnetization at room temperature. Phys. Rev. Lett. 108, 177201 (2012).

    Article  CAS  Google Scholar 

  12. 12.

    Shen, S.-P. et al. Quantum electric-dipole liquid on a triangular lattice. Nat. Commun. 7, 10569 (2016).

    CAS  Article  Google Scholar 

  13. 13.

    Shen, S.-P. et al. Magnetic-ion-induced displacive electric polarization in FeO5 bipyramidal units of (Ba,Sr)Fe12O19 hexaferrites. Phys. Rev. B 90, 180404 (2014).

    Article  CAS  Google Scholar 

  14. 14.

    Harris, V. G. Modern microwave ferrites. IEEE Trans. Magn. 48, 1075–1104 (2012).

    CAS  Article  Google Scholar 

  15. 15.

    Zuo, X., How, H., Somu, S. & Vittoria, C. Self-biased circulator/isolator at millimeter wavelengths using magnetically oriented polycrystalline strontium M-type hexaferrite. In IEEE Transactions on Magnetics 3160–3162 (IEEE, 2003).

  16. 16.

    Song, Y.-Y. Y., Sun, Y., Lu, L., Bevivino, J. & Wu, M. Self-biased planar millimeter wave notch filters based on magnetostatic wave excitation in barium hexagonal ferrite thin films. Appl. Phys. Lett. 97, 173502 (2010).

    Article  CAS  Google Scholar 

  17. 17.

    Harris, V. G. et al. Recent advances in processing and applications of microwave ferrites. J. Magn. Magn. Mater. https://doi.org/10.1016/j.jmmm.2009.01.004 (2009).

  18. 18.

    Pullar, R. C. Hexagonal ferrites: a review of the synthesis, properties and applications of hexaferrite ceramics. Prog. Mater. Sci. 57, 1191–1334 (2012).

    CAS  Article  Google Scholar 

  19. 19.

    Gorbachev, E. A. et al. Hexaferrite materials displaying ultra-high coercivity and sub-terahertz ferromagnetic resonance frequencies. Mater. Today 32, 13–18 (2020).

    CAS  Article  Google Scholar 

  20. 20.

    Gudkov, V. V. et al. Sub-lattice of Jahn-Teller centers in hexaferrite crystal. Sci. Rep. 10, 7076 (2020).

    CAS  Article  Google Scholar 

  21. 21.

    Mikheykin, A. S. et al. Lattice anharmonicity and polar soft mode in ferrimagnetic M-type hexaferrite BaFe12O19 single crystal. Eur. Phys. J. B 87, 232 (2014).

    Article  CAS  Google Scholar 

  22. 22.

    Zhukova, E. S. et al. Crucial influence of crystal site disorder on dynamical spectral response in artificial magnetoplumbites. Solid State Sci. 62, 13–21 (2016).

    CAS  Article  Google Scholar 

  23. 23.

    Alyabyeva, L. N. et al. Influence of chemical substitution on broadband dielectric response of barium-lead M-type hexaferrite. N. J. Phys. 21, 063016 (2019).

    CAS  Article  Google Scholar 

  24. 24.

    Ahmed, A. et al. Effect of aluminium substitution on low energy electrodynamics of barium-lead M-type hexagonal ferrites. J. Phys. Conf. Ser. 1389, 012044 (2019).

    CAS  Article  Google Scholar 

  25. 25.

    Alyabyeva, L. et al. Terahertz-infrared electrodynamics of lead-doped single crystalline Bal−xPbxFe12O19 M-type hexagonal ferrite. in Proc. 43rd International Conference on Infrared, Millimeter, and Terahertz Waves, IRMMW-THz 18227333 (IEEE, 2018).

  26. 26.

    Alyabyeva, L. et al. Terahertz-infrared spectroscopy of Ti4+-doped M-type barium hexaferrite. J. Alloy. Compd. 820, 153398 (2020).

    CAS  Article  Google Scholar 

  27. 27.

    Kadlec, F. et al. Electromagnon in the Z-type hexaferrite (BaxSr1-x)3Co2Fe24O41. Phys. Rev. B 94, 024419 (2016).

    Article  CAS  Google Scholar 

  28. 28.

    Vít, J. et al. Electromagnon in the Y-type hexaferrite BaSrCoZnFe11AlO22. Phys. Rev. B 97, 134406 (2018).

    Article  Google Scholar 

  29. 29.

    Lines, M. E., Glass, A. M. & Burns, G. Principles and applications of ferroelectrics and related materials. Phys. Today 31, 56–58 (1978).

    Article  Google Scholar 

  30. 30.

    Kamba, S. Soft-mode spectroscopy of ferroelectrics and multiferroics: a review. APL Mater. 9, 020704 (2021).

    CAS  Article  Google Scholar 

  31. 31.

    Obradors, X., Collomb, A., Pernet, M., Samaras, D. & Joubert, J. C. X-ray analysis of the structural and dynamic properties of BaFe12O19 hexagonal ferrite at room temperature. J. Solid State Chem. 56, 171–181 (1985).

    CAS  Article  Google Scholar 

  32. 32.

    Nakajima, Y. & Naya, S. Orientational phase transition and dynamic susceptibility of hindered-rotating dipolar system –a librator-rotator model–. J. Phys. Soc. Jpn. 63, 904–914 (1994).

    CAS  Article  Google Scholar 

  33. 33.

    Normand, B. G. A., Giddy, A. P., Dove, M. T. & Heine, V. Bifurcation behaviour in structural phase transitions with multi-well potentials. J. Phys. Condens. Matter 2, 3737–3745 (1990).

    Article  Google Scholar 

  34. 34.

    Onodera, Y. Dynamical response of ferroelectrics in terms of a classical anharmonic-oscillator model. J. Phys. Soc. Jpn. 73, 1216–1221 (2004).

    CAS  Article  Google Scholar 

  35. 35.

    Gorshunov, B. P. et al. Incipient ferroelectricity of water molecules confined to nano-channels of beryl. Nat. Commun. 7, 12842 (2016).

    CAS  Article  Google Scholar 

  36. 36.

    Vinnik, D. et al. Magnetic and structural properties of barium hexaferrite BaFe12O19 from various growth techniques. Materials 10, 578 (2017).

    Article  CAS  Google Scholar 

  37. 37.

    Landau, L. D. & Lifshitz, E. M. in Statistical Physics, Vol. 5 p. ii (Elsevier, 1968).

  38. 38.

    Mashiyama, H., Eric Mkam Tchouobiap, S. & Ashida, M. Order–disorder and displacive transitions in a quantum Ising model. J. Phys. Soc. Jpn. 77, 084709 (2008).

    Article  CAS  Google Scholar 

  39. 39.

    Matsumoto, H. et al. Optical conductivity from local anharmonic phonons. Phys. Rev. B 79, 214306 (2009).

    Article  CAS  Google Scholar 

  40. 40.

    Mori, T. et al. Optical conductivity of rattling phonons in type-I clathrate Ba8G16Ge30. Phys. Rev. B 79, 212301 (2009).

    Article  CAS  Google Scholar 

  41. 41.

    Onodera, Y. Dynamic susceptibility of classical anharmonic oscillator. Prog. Theor. Phys. 44, 1477–1499 (1970).

    Article  Google Scholar 

  42. 42.

    Hlinka, J. et al. Origin of the “waterfall” effect in phonon dispersion of relaxor perovskites. Phys. Rev. Lett. 91, 107602 (2003).

    CAS  Article  Google Scholar 

  43. 43.

    Delaire, O. et al. Giant anharmonic phonon scattering in PbTe. Nat. Mater. 10, 614–619 (2011).

    CAS  Article  Google Scholar 

  44. 44.

    Silva Júnior, F. M. & Paschoal, C. W. A. Spin-phonon coupling in BaFe12O19 M-type hexaferrite. J. Appl. Phys. 116, 244110 (2014).

    Article  CAS  Google Scholar 

  45. 45.

    Chen, X.-B. et al. Raman studies of spin-phonon coupling in hexagonal BaFe12O19. J. Appl. Phys. 114, 013912 (2013).

    Article  CAS  Google Scholar 

  46. 46.

    Izadkhah, H., Zare, S., Somu, S. & Vittoria, C. Effects of cobalt substitutions on the magnetoelectric coupling of M-type hexaferrite films. Appl. Phys. Lett. 106, 142905 (2015).

    Article  CAS  Google Scholar 

  47. 47.

    Ebnabbasi, K., Mohebbi, M. & Vittoria, C. Room temperature magnetoelectric effects in bulk poly-crystalline materials of M- and Z-type hexaferrites. J. Appl. Phys. 113, 17C703 (2013).

    Article  CAS  Google Scholar 

  48. 48.

    Mohebbi, M., Ebnabbasi, K. & Vittoria, C. First observation of magnetoelectric effect in M-type hexaferrite thin films. J. Appl. Phys. 113, 17C710 (2013).

    Article  CAS  Google Scholar 

  49. 49.

    Kumar, K. & Pandey, D. Quantum phase transitions in Ba(1−x)CaxFe12O19 (0≤x≤0.10). Phys. Rev. B 96, 024102 (2017).

    Article  Google Scholar 

  50. 50.

    Rowley, S. E. et al. Uniaxial ferroelectric quantum criticality in multiferroic hexaferrites BaFe12O19 and SrFe12O19. Sci. Rep. 6, 25724 (2016).

    CAS  Article  Google Scholar 

  51. 51.

    Rowley, S. E. et al. Ferroelectric quantum criticality. Nat. Phys. 10, 367–372 (2014).

    CAS  Article  Google Scholar 

  52. 52.

    Khmel’nitskii, D. E. & Shneerson, V. L. Russian version. Sov. Phys. Solid State 13, 687 (1971).

    Google Scholar 

  53. 53.

    Khmel’nitskii, D. E. & Shneerson, V. L. Phase transitions of the displacement type in crystals at very low temperatures. Sov. J. Exp. Theor. Phys. 37, 164 (1973).

    Google Scholar 

  54. 54.

    Lunkenheimer, P. et al. Colossal dielectric constants in transition-metal oxides. Eur. Phys. J. Spec. Top. 180, 61–89 (2009).

    Article  Google Scholar 

  55. 55.

    Pyatakov, A. P. et al. Magnetically switched electric polarity of domain walls in iron garnet films. EPL 93, 17001 (2011).

    Article  CAS  Google Scholar 

  56. 56.

    Popov, M. A., Zavislyak, I. V. & Srinivasan, G. Current tunable barium hexaferrite millimeter wave resonator. Microw. Opt. Technol. Lett. 60, 458–462 (2018).

    Article  Google Scholar 

  57. 57.

    Bierlich, S., Gellersen, F., Jacob, A. & Töpfer, J. Low-temperature sintering and magnetic properties of Sc- and In-substituted M-type hexagonal barium ferrites for microwave applications. Mater. Res. Bull. 86, 19–23 (2017).

    CAS  Article  Google Scholar 

  58. 58.

    Shi, J. et al. THz photonics in two dimensional materials and metamaterials: properties, devices and prospects. J. Mater.Chem C 6, 1291–1306 (2018).

    Google Scholar 

  59. 59.

    Lv, T. T. et al. Hybrid metamaterial switching for manipulating chirality based on VO2 phase transition. Sci. Rep. 6, 23186 (2016).

  60. 60.

    Harris, V. G. et al. Ba-hexaferrite films for next generation microwave devices (invited). J. Appl. Phys. 99, 08M911 (2006).

    Article  CAS  Google Scholar 

  61. 61.

    Bowrothu, R., Kim, H.-I. I., Smith, C. S., Arnold, D. P. & Yoon, Y.-K. K. 35-GHz barium hexaferrite/PDMS composite-based millimeter-wave circulators for 5G applications. IEEE Trans. Microw. Theory Tech. 68, 5065–5071 (2020).

    Article  Google Scholar 

  62. 62.

    Zhang, G. & Jiang, Y. A novel CMOS hexaferrite circulator with 25 GHz operating frequency. AIP Adv. 11, 045022 (2021).

  63. 63.

    Sai, R., Shivashankar, S. A., Yamaguchi, M. & Bhat, N. Magnetic nanoferrites for RF CMOS: enabling 5G and beyond. Electrochem. Soc. Interface 26, 71 (2017).

  64. 64.

    Srinivasan, G., Popov, M. A. & Zavislyak, I. V. Chapter 10. Dielectric resonance in ferrites for sub-thz signal-processing devices. Solid State Phys 64, 349–363 (2013).

    CAS  Article  Google Scholar 

  65. 65.

    Vendik, I. B. et al. Tunable metamaterials for controlling THz radiation. In IEEE Transactions on Terahertz Science and Technology 538–549 (IEEE, 2012).

  66. 66.

    Popov, M. A., Zavislyak, I. V., Movchan, N. N., Gudim, I. A. & Srinivasan, G. Mode splitting in 37-42 GHz barium hexaferrite resonator: theory and device applications. IEEE Trans. Magn. 50, 4004507 (2014).

  67. 67.

    Wan, P. et al. Flexible transparent films based on nanocomposite networks of polyaniline and carbon nanotubes for high-performance gas sensing. Small 11, 5409–5415 (2015).

    CAS  Article  Google Scholar 

  68. 68.

    Liu, J. et al. MXene-enabled electrochemical microfluidic biosensor: applications toward multicomponent continuous monitoring in whole blood. Adv. Funct. Mater. 29, 1807326 (2019).

  69. 69.

    Yang, S. et al. High sensitivity and good selectivity of ultralong MoO3 nanobelts for trimethylamine gas. Sensors Actuators B Chem 226, 478–485 (2016).

    CAS  Article  Google Scholar 

  70. 70.

    Ziegler, D., Marchisio, A., Montanaro, L., Palmero, P. & Tulliani, J. M. Barium hexaferrite thick-films for ozone detection at low temperature. Solid State Ionics 320, 24–32 (2018).

    Article  Google Scholar 

  71. 71.

    Das, T. et al. Novel barium hexaferrite based highly selective and stable trace ammonia sensor for detection of renal disease by exhaled breath analysis. Sensors Actuators B Chem. 325, 128765 (2020).

  72. 72.

    Karmakar, M., Mondal, B., Pal, M. & Mukherjee, K. Acetone and ethanol sensing of barium hexaferrite particles: a case study considering the possibilities of non-conventional hexaferrite sensor. Sensors Actuators B Chem 190, 627–633 (2014).

    CAS  Article  Google Scholar 

  73. 73.

    Antonio-Lopez, J. E., Castillo-Guzman, A., May-Arrioja, D. A., Selvas-Aguilar, R. & LiKamWa, P. Tunable multimode-interference bandpass fiber filter. Opt. Lett. 35, 324 (2010).

    CAS  Article  Google Scholar 

  74. 74.

    Uher, J. & Hoefer, W. J. R. Tunable microwave and millimeter-wave band-pass filters. IEEE Trans. Microw. Theory Tech. 39, 643–653 (1991).

    Article  Google Scholar 

  75. 75.

    Tan, G. & Chen, X. Structure and multiferroic properties of barium hexaferrite ceramics. J. Magn. Magn. Mater. 327, 87–90 (2013).

    CAS  Article  Google Scholar 

  76. 76.

    Trukhanov, A. V. et al. Multiferroic properties and structural features of M-type Al-substituted barium hexaferrites. Phys. Solid State 59, 737–745 (2017).

    CAS  Article  Google Scholar 

  77. 77.

    Karpov, D. et al. Nanoscale topological defects and improper ferroelectric domains in multiferroic barium hexaferrite nanocrystals. Phys. Rev. B 100, 054432 (2019).

    CAS  Article  Google Scholar 

  78. 78.

    Born, M. & Wolf, E. Principles of Optics (Cambridge University Press, 1999).

  79. 79.

    Böhmer, R., Maglione, M., Lunkenheimer, P. & Loidl, A. Radio‐frequency dielectric measurements at temperatures from 10 to 450 K. J. Appl. Phys. 65, 901–904 (1989).

    Article  Google Scholar 

  80. 80.

    Gorshunov, B. et al. Terahertz BWO-spectrosopy. Int. J. Infrared Millim. Waves 26, 1217–1240 (2005).

    Article  Google Scholar 

  81. 81.

    Alyabyeva, L. et al. Bi-relaxor behavior and Fe2+ fine structure in single crystalline Ba0.3Pb0.7Fe12O19M-type hexaferrite. In 2018 43rd International Conference on Infrared, Millimeter, and Terahertz Waves (IRMMW-THz) 18227420 (IEEE, 2018).

Download references

Acknowledgements

The authors are grateful to Professor A. Mukhin and Professor G. Komandin for fruitful discussions. The THz cryogenic study was supported by the Russian Science Foundation, grant 19–72–00055; IR measurements were supported by the RFBR (grant 20–32–90034), LNA acknowledges support of the Russian Ministry of Higher Education and Science, state contract 1740–20 and system of President’s scholarships for young researchers (SP-777.2021.5). Czech coauthors were supported by the Czech Science Foundation (Project No. 21–06802S) and by the MŠMT Projects LM2018096 and SOLID21—CZ.02.1.01/0.0/0.0/16_019/0000760. Single crystal growth was supported at SUSU by the RFBR (grant 20–08–00716), and DAV was partially supported by President’s grants for young doctors of science (MD-5612.2021.4). A theoretical study at IA&E SB RAS was supported by RFBR (grants 20–02–00314 and 20–42–540002). Work done at the University of Augsburg was supported by the DFG via the TRR 80 (ID 107745057).

Author information

Affiliations

Authors

Contributions

L.N.A. conceived, planned, and performed the experiments, data analysis and interpretation of the results and wrote the paper in consultation with A.S.P., P.L., and B.P.G.; D.A.V. provided single crystals and their characterization; V.B.A., C.K., F.K., J.P., S.K., M.D., and A.V.P. provided access to the facility; A.G.A., A.M., P.B., F.K., C.K., E.d.P., P.P., A.V.P., and S.S. assisted in the experiments; V.A.A. provided theoretical model; V.V.D. performed EFM/MFM experiments; M.S. and P.L. held RF experiments, and P.L. wrote the RF part of the manuscript; B.P.G. analyzed the results, managed and advised the research, and edited the manuscript. All authors reviewed the manuscript.

Corresponding author

Correspondence to L. N. Alyabyeva.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Alyabyeva, L.N., Prokhorov, A.S., Vinnik, D.A. et al. Lead-substituted barium hexaferrite for tunable terahertz optoelectronics. NPG Asia Mater 13, 63 (2021). https://doi.org/10.1038/s41427-021-00331-x

Download citation

Search

Quick links