Abstract
The aggregation structure and electro-optical properties of polymer/liquid crystal (LC) composite films were investigated. The aggregation structure of the composite film strongly depended on the components ratio of matrix polymer and low molecular weight liquid crystalline materials. The continuous LC phase was formed in a three dimensional polymer network when the LC weight fraction was above around 50 wt%. Also, the aggregation structure of the composite film could be controlled by controlling the solvent evaporation velocity during the film preparation process. The finer matrix polymer fibrils were formed in the case of the faster solvent evaporation velocity. The composite films exhibited reversible light scattering-light transmission switching upon electric field -OFF and -ON states, respectively. The light scattering properties of the composite film with a continuous LC phase were strongly dependent on the spatial distortion of nematic directors as well as the mismatch in refractive indices between matrix polymer and LC upon an electric field -OFF state. By controlling the polymeric wall thickness of the composite film below the wavelength (632.8 nm) of an incident He–Ne laser beam, the composite films which show a remarkably high transmittance and contrast were successfully realized.
Similar content being viewed by others
Article PDF
References
T. Kajiyama, Y. Nagata, E. Maemura, and Y. Takayanagi, Chem. Lett., 679 (1979).
T. Kajiyama, H. Kikuchi, M. Katayose, and S. Shinkai, New Polym. Mater., 1, 99 (1988).
M. Schadt and W. Helfrich, Appl. Phys. Lett., 18, 127 (1971).
R. Williams, U. S. Patent No. 3 322 485 (1962).
J. L. Fergason, SID Int. Symp. Dig. Technol., 16, 85 (1985).
J. W. Doane, N. V. Vaz, B. G. Wu, and S. Zumer, Appl. Phys. Lett., 48, 269 (1986).
T. Kajiyama, A. Miyamoto, H. Kikuchi, and Y. Morimura, Chem. Lett., 813 (1989).
A. Miyamoto, H. Kikuchi, Y. Morimura, and T. Kajiyama, New Polym. Mater., 2, 27 (1990).
A. Miyamoto, H. Kikuchi, S. Kobayashi, Y. Morimura, and T. Kajiyama, Macromolecules, 24, 3915 (1991).
T. Kajiyama and H. Kikuchi, J. Chem. Soc. Jpn., Chem. & Ind. Chem., 10, 1019 (1992).
T. Kajiyama, H. Kikuchi, and A. Takahara, Proc. SPIE, 1665, 20 (1992).
T. Kajiyama, K. Park, H. Usui, H. Kikuchi, and A. Takahara, Proc. SPIE, 1911, 122 (1993).
Will be submitted to Polym. J.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Park, K., Kikuchi, H. & Kajiyama, T. Component Dependence of Aggregation Structure and Light Scattering Properties of Polymer/Liquid Crystal Composite Films. Polym J 26, 895–904 (1994). https://doi.org/10.1295/polymj.26.895
Issue Date:
DOI: https://doi.org/10.1295/polymj.26.895
Keywords
This article is cited by
-
Simultaneous effects of external stimuli on preparation and performance parameters of normally transparent reverse mode polymer-dispersed liquid crystals—a review
Journal of Materials Science (2021)
-
Relaxation behavior of random copolymers containing rigid fumarate and flexible acrylate segments by dynamic mechanical analysis
Polymer Journal (2019)
-
Adamantane-containing poly(dialkyl fumarate)s with rigid chain structures
Polymer Journal (2019)
-
Electro-optical properties of the normally transparent type anisotropic polymer dispersed liquid crystal films
Journal of Polymer Research (1998)