Direct measurement of the exciton binding energy and effective masses for charge carriers in organic–inorganic tri-halide perovskites

Nature Physics volume 11, pages 582587 (2015) | Download Citation

Subjects

Abstract

Solar cells based on the organic–inorganic tri-halide perovskite family of materials have shown significant progress recently, offering the prospect of low-cost solar energy from devices that are very simple to process. Fundamental to understanding the operation of these devices is the exciton binding energy, which has proved both difficult to measure directly and controversial. We demonstrate that by using very high magnetic fields it is possible to make an accurate and direct spectroscopic measurement of the exciton binding energy, which we find to be only 16 meV at low temperatures, over three times smaller than has been previously assumed. In the room-temperature phase we show that the binding energy falls to even smaller values of only a few millielectronvolts, which explains their excellent device performance as being due to spontaneous free-carrier generation following light absorption. Additionally, we determine the excitonic reduced effective mass to be 0.104me (where me is the electron mass), significantly smaller than previously estimated experimentally but in good agreement with recent calculations. Our work provides crucial information about the photophysics of these materials, which will in turn allow improved optoelectronic device operation and better understanding of their electronic properties.

Access optionsAccess options

Rent or Buy article

Get time limited or full article access on ReadCube.

from$8.99

All prices are NET prices.

References

  1. 1.

    Best research cell efficiencies. NREL (2015);

  2. 2.

    et al. Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%. Sci. Rep. 2, 591 (2012).

  3. 3.

    et al. Sequential deposition route to high performance perovskite-sensitized solar cells. Nature 499, 316–320 (2013).

  4. 4.

    , , , & 6.5% efficient perovskite quantum-dot-sensitized solar cell. Nanoscale 3, 4088–4093 (2011).

  5. 5.

    et al. Efficient inorganic–organic hybrid heterojunction solar cells containing perovskite compound and polymeric hole conductors. Nature Photon. 7, 487–492 (2013).

  6. 6.

    , , , & Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643–647 (2012).

  7. 7.

    , & Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 501, 395–398 (2013).

  8. 8.

    et al. Low-temperature processed electron collection layers of graphene/TiO2 nanocomposites in thin-film perovskite solar cells. Nano Lett. 14, 724–730 (2014).

  9. 9.

    et al. Carbon nanotube/polymer composites as a highly stable hole collection layer in perovskite solar cells. Nano Lett. 14, 5561–5568 (2014).

  10. 10.

    & Perovskite solar cells: From materials to devices. Small 11, 10–25 (2015).

  11. 11.

    et al. Excitons versus free charges in organo-lead tri-halide perovskites. Nature Commun. 5, 3586 (2013).

  12. 12.

    , , , & Magnetoabsorptin of the lowest exciton in perovskite-type compound (CH3NH3)PbI3. Physica B 201, 427–430 (1994).

  13. 13.

    et al. Comparative study on the excitons in lead-halide-based perovskite-type crystals CH3NH3PbBr3 CH3NH3PbI3. Solid State Commun. 127, 619–623 (2003).

  14. 14.

    , , & Self-consistent relativistic band structure of the CH3NH3PbI3 perovskite. Phys. Rev. B 90, 045207 (2014).

  15. 15.

    , & Analysis of multi-valley and multi-bandgap absorption and enhancement of free carriers related to exciton screening in hybrid perovskites. J. Phys. Chem. C 118, 11566–11572 (2014).

  16. 16.

    , , , & Photoelectronic responses in solution-processed perovskite CH3NH3PbI3 solar cells studied by photoluminescence and photoabsorption spectroscopy. IEEE J. Photovolt. 5, 401–405 (2015).

  17. 17.

    , , , & Electro-optics of perovskite solar cells. Nature Photon. 9, 106–112 (2014).

  18. 18.

    , & Relativistic GW calculations on CH3NH3PbI3 and CH3NH3SnI3 perovskites for solar cell applications. Sci. Rep. 4, 4467 (2014).

  19. 19.

    et al. Synthesis and crystal chemistry of the hybrid perovskite (CH3NH3)PbI3 for solid-state sensitised solar cell applications. J. Mater. Chem. A 1, 5628–5641 (2013).

  20. 20.

    et al. Photophysics of organic-inorganic hybrid lead iodide perovskite single crystals. Adv. Funct. Mater. 25, 2378–2385 (2015).

  21. 21.

    & Energy levels of a neutral hydrogen-like system in a constant magnetic field of arbitrary strength. J. Phys. C 19, 873–885 (1986).

  22. 22.

    , & Magneto-optical effects observed for GaSe in megagauss magnetic fields. Phys. Rev. B 68, 155312 (2003).

  23. 23.

    , & Warping and inversion asymmetry induced cyclotron harmonic transitions in InSb. Phys. Rev. B 17, 3269–3283 (1979).

  24. 24.

    , , & Relativistic quasiparticle self-consistent electronic structure of hybrid halide perovskite photovoltaic absorbers. Phys. Rev. B 89, 155204 (2014).

  25. 25.

    , , , & Charge carrier dynamics in vapour-deposited films of the organolead halide perovskite CH3NH3PbI3−xClx. Energ. Environ. Sci. 7, 2269–2275 (2014).

  26. 26.

    , , , & Charge carrier recombination channels in the low-temperature phase of organic–inorganic lead halide perovskite thin films. APL Mater. 2, 081513 (2014).

  27. 27.

    & Electronic band structure, phonons, and exciton binding energies of halide perovskites CsSnCl3, CsSnBr3, and CsSnI3. Phys. Rev. B 88, 165203 (2013).

  28. 28.

    et al. Photoluminescence study of polycrystalline CsSnI3 thin films: Determination of exciton binding energy. J. Lumin. 132, 345–349 (2012).

  29. 29.

    et al. Organometal halide perovskite solar cell materials rationalized: Ultrafast charge generation, high and microsecond-long balanced mobilities, and slow recombination. J. Am. Chem. Soc. 136, 5189–5192 (2014).

  30. 30.

    , , , & High charge carrier mobilities and lifetimes in organolead trihalide perovskites. Adv. Mater. 26, 1584–1589 (2013).

  31. 31.

    , & Origin of the variation of exciton binding energy in semiconductors. Phys. Rev. Lett. 110, 016402 (2013).

  32. 32.

    et al. High-efficiency solution-processed perovskite solar cells with millimeter-scale grains. Science 347, 522–525 (2015).

  33. 33.

    , & Ultra-high magnetic field study of the layer split bands in graphite. Phys. Rev. Lett. 111, 096802 (2013).

  34. 34.

    et al. Megagauss magnetic fields in single-turn coils: New frontiers for scientific experiments. J. Phys. D 32, 2354–2366 (1999).

Download references

Acknowledgements

The authors thank: Meso-superstructured Hybrid Solar Cells—MESO NMP-2013-SMALL7-604032 project. H.J.S. thanks for financial support the Engineering and Physical Sciences Research Council (EPSRC), and the European Research Council (ERC-StG 2011 HYPER Project no. 279881). S. Stranks thanks Worcester College, Oxford, for additional financial support. P.P. thanks ANR JCJC project milliPICS, Region Midi-Pyrenee contract MESR 13053031. A. Miyata thanks the JSPS postdoctoral fellowships for research abroad for support. This work was supported by EuroMagNETII under the EU contract No. 228043.

Author information

Author notes

    • Atsuhiko Miyata
    •  & Anatolie Mitioglu

    These authors contributed equally to this work.

Affiliations

  1. Laboratoire National des Champs Magnetiques Intenses, CNRS-UJF-UPS-INSA, 143 Avenue de Rangueil 31400 Toulouse, France

    • Atsuhiko Miyata
    • , Anatolie Mitioglu
    • , Paulina Plochocka
    •  & Oliver Portugall
  2. University of Oxford, Clarendon Laboratory, Parks Road Oxford OX1 3PU, UK

    • Jacob Tse-Wei Wang
    • , Samuel D. Stranks
    • , Henry J. Snaith
    •  & Robin J. Nicholas

Authors

  1. Search for Atsuhiko Miyata in:

  2. Search for Anatolie Mitioglu in:

  3. Search for Paulina Plochocka in:

  4. Search for Oliver Portugall in:

  5. Search for Jacob Tse-Wei Wang in:

  6. Search for Samuel D. Stranks in:

  7. Search for Henry J. Snaith in:

  8. Search for Robin J. Nicholas in:

Contributions

A.Miyata, A.Mitioglu, P.P., O.P. and R.J.N. collected and analysed the data. J.T-W.W. and S.D.S. prepared the samples. All authors contributed to the interpretation and the manuscript preparation. R.J.N. supervised and initiated the project.

Competing interests

The authors declare no competing financial interests.

Corresponding author

Correspondence to Robin J. Nicholas.

About this article

Publication history

Received

Accepted

Published

DOI

https://doi.org/10.1038/nphys3357

Further reading