Abstract
A clean and efficient way to overcome the limited supply of fossil fuels and the greenhouse effect is the production of hydrogen fuel from sunlight and water through the semiconductor/water junction of a photoelectrochemical cell, where energy collection and water electrolysis are combined into a single semiconductor electrode. We present a highly active photocathode for solar H2 production, consisting of electrodeposited cuprous oxide, which was protected against photocathodic decomposition in water by nanolayers of Al-doped zinc oxide and titanium oxide and activated for hydrogen evolution with electrodeposited Pt nanoparticles. The roles of the different surface protection components were investigated, and in the best case electrodes showed photocurrents of up to −7.6 mA cm−2 at a potential of 0 V versus the reversible hydrogen electrode at mild pH. The electrodes remained active after 1 h of testing, cuprous oxide was found to be stable during the water reduction reaction and the Faradaic efficiency was estimated to be close to 100%.
This is a preview of subscription content, access via your institution
Access options
Subscribe to this journal
Receive 12 print issues and online access
$259.00 per year
only $21.58 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
References
Khaselev, O. & Turner, J. A. A monolithic photovoltaic-photoelectrochemical device for hydrogen production via water splitting. Science 280, 425–427 (1998).
Aharon-Shalom, E. & Heller, A. Efficient p-InP(Rh-H alloy) and p-InP(Re–H alloy) hydrogen evolving photocathodes. J. Electrochem. Soc. 129, 2865–2866 (1982).
Marsen, B., Cole, B. & Miller, E. L. Photoelectrolysis of water using thin copper gallium diselenide electrodes. Sol. Energy Mater. Sol. Cells 92, 1054–1058 (2008).
Fernandez, A. M. et al. Photoelectrochemical characterization of the Cu(In,Ga)S2 thin film prepared by evaporation. Sol. Energy Mater. Sol. Cells 85, 251–259 (2005).
Hara, M. et al. Cu2O as a photocatalyst for overall water splitting under visible light irradiation. Chem. Commun. 357–358 (1998).
de Jongh, P. E., Vanmaekelbergh, D. & Kelly, J. J. Photoelectrochemistry of electrodeposited Cu2O. J. Electrochem. Soc. 147, 486–489 (2000).
Siripala, W., Ivanovskaya, A., Jaramillo, T. F., Baeck, S. H. & McFarland, E. W. A Cu2O/TiO2 heterojunction thin film cathode for photoelectrocatalysis. Sol. Energy Mater. Sol. Cells 77, 229–237 (2003).
Hu, C. C., Nian, J. N. & Teng, H. Electrodeposited p-type Cu2O as photocatalyst for H-2 evolution from water reduction in the presence of WO3. Sol. Energy Mater. Sol. Cells 92, 1071–1076 (2008).
Nian, J. N., Hu, C. C. & Teng, H. Electrodeposited p-type Cu2O for H-2 evolution from photoelectrolysis of water under visible light illumination. Int. J. Hydrog. Energy 33, 2897–2903 (2008).
Barreca, D. et al. The potential of supported Cu2O and CuO nanosystems in photocatalytic H-2 production. ChemSusChem 2, 230–233 (2009).
Morales, J. et al. Electrodeposition of Cu2O: An excellent method for obtaining films of controlled morphology and good performance in Li-ion batteries. Electrochem. Solid State Lett. 8, A159–A162 (2005).
Lee, Y. H. et al. Fabrication and characterization of Cu2O nanorod arrays and their electrochemical performance in Li-ion batteries. Electrochem. Solid State Lett. 9, A207–A210 (2006).
Bijani, S. et al. Nanostructured Cu2O thin film electrodes prepared by electrodeposition for rechargeable lithium batteries. Thin Solid Films 515, 5505–5511 (2007).
Katayama, J., Ito, K., Matsuoka, M. & Tamaki, J. Performance of Cu2O/ZnO solar cell prepared by two-step electrodeposition. J. Appl. Electrochem. 34, 687–692 (2004).
Akimoto, K. et al. Thin film deposition of Cu2O and application for solar cells. Sol. Energy 80, 715–722 (2006).
Jeong, S. S., Mittiga, A., Salza, E., Masci, A. & Passerini, S. Electrodeposited ZnO/Cu2O heterojunction solar cells. Electrochim. Acta 53, 2226–2231 (2008).
Cui, J. B. & Gibson, U. J. A simple two-step electrodeposition of Cu2O/ZnO nanopillar solar cells. J. Phys. Chem. C 114, 6408–6412 (2010).
Graetzel, M. Photoelectrochemical cells. Nature 414, 338–344 (2001).
de Jongh, P. E., Vanmaekelbergh, D. & Kelly, J. J. Cu2O: Electrodeposition and characterization. Chem. Mater. 11, 3512–3517 (1999).
Sculfort, J. L., Guyomard, D. & Herlem, M. Photoelectrochemical characterization of the p-Cu2O-non aqueous electrolyte junction. Electrochim. Acta 29, 459–465 (1984).
Engel, C. J., Polson, T. A., Spado, J. R., Bell, J. M. & Fillinger, A. Photoelectrochemistry of porous p-Cu2O films. J. Electrochem. Soc. 155, F37–F42 (2008).
George, S. M. Atomic layer deposition: An overview. Chem. Rev. 110, 111–131 (2010).
Hwang, Y. J., Boukai, A. & Yang, P. High density n-Si/n-TiO2 core/shell nanowire arrays with enhanced photoactivity. Nano Lett. 9, 410–415 (2009).
Shan, C. X., Hou, X. H. & Choy, K. L. Corrosion resistance of TiO2 films grown on stainless steel by atomic layer deposition. Surf. Coat. Technol. 202, 2399–2402 (2008).
Guidi, F. et al. Electrochemical anticorrosion performance evaluation of Al2O3 coatings deposited by MOCVD on an industrial brass substrate. Electrochim. Acta 50, 4609–4614 (2005).
Du, X. H., Zhang, K., Holland, K., Tombler, T. & Moskovits, M. Chemical corrosion protection of optical components using atomic layer deposition. Appl. Opt. 48, 6470–6474 (2009).
Galliano, P., De Damborenea, J. J., Pascual, M. J. & Duran, A. Sol–gel coatings on 316L steel for clinical applications. J. Sol–Gel Sci. Technol. 13, 723–727 (1998).
Heller, A. Hydrogen-evolving solar cells. Science 223, 1141–1148 (1984).
Standridge, S. D., Schatz, G. C. & Hupp, J. T. Toward plasmonic solar cells: Protection of silver nanoparticles via atomic layer deposition of TiO2 . Langmuir 25, 2596–2600 (2009).
Elam, J. W., Routkevitch, D. & George, S. M. Properties of ZnO/Al2O3 alloy films grown using atomic layer deposition techniques. J. Electrochem. Soc. 150, G339–G347 (2003).
Agashe, C. et al. Efforts to improve carrier mobility in radio frequency sputtered aluminium doped zinc oxide films. J. Appl. Phys. 95, 1911–1917 (2004).
Lee, D-J. et al. Structural and electrical properties of atomic layer deposited Al–doped ZnO films. Adv. Funct. Mater. 21, 448–455 (2011).
Yasomanee, J. P. & Bandara, J. Multi-electron storage of photoenergy using Cu2O–TiO2 thin film photocatalyst. Sol. Energy Mater. Sol. Cells 92, 348–352 (2008).
Xiong, L. B. et al. Visible-light energy storage by Ti3+ in TiO2/Cu2O bilayer film. Chem. Lett. 38, 1154–1155 (2009).
O’Regan, B., Grätzel, M. & Fitzmaurice, D. Optical electrochemistry I: Steady-state spectroscopy of conduction-band electrons in a metal oxide semiconductor electrode. Chem. Phys. Lett. 183, 89–93 (1991).
Howe, R. F. & Gratzel, M. EPR observation of trapped electrons in colloidal titanium dioxide. J. Phys. Chem. 89, 4495–4499 (1985).
Kaise, M. et al. Electron spin resonance studies of photocatalytic interface reactions of suspended M/TiO2 (M=Pt, Pd, Ir, Rh, Os, or Ru) with alcohol and acetic acid in aqueous media. Langmuir 10, 1345–1347 (1994).
Nadesalingam, M. P. et al. Effect of vacuum annealing on the surface chemistry of electrodeposited copper(I) oxide layers as probed by positron annihilation induced auger electron spectroscopy. Langmuir 23, 1830–1834 (2007).
Acknowledgements
The research leading to these results has received funding from the European Community’s Seventh Framework Programme (FP7/2007-2013) under grant agreement no. 227179 (‘NanoPEC’). We would also like to thank the Swiss Federal Office of Energy (Project number 102326, PECHouse) and the Energy Center at EPFL for financial support. We acknowledge N. Xanthopoulos from the Interdisciplinary Centre for Electron Microscopy (CIME) at EPFL for helping in the XPS characterization. E.T. would also like to thank A. Martinson at Argonne National Laboratory for helpful discussions about aluminium-doped zinc oxide synthesized by ALD.
Author information
Authors and Affiliations
Contributions
A.P. and E.T. designed the experiments. A.P. carried out electrodeposition, PEC measurements, SEM and XRD. ALD was carried out by E.T. Faradaic efficiency measurements were carried out by K.S. XPS was carried out by V.L. M.G. supervised the project. All of the authors discussed and analysed the data.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Information (PDF 1486 kb)
Rights and permissions
About this article
Cite this article
Paracchino, A., Laporte, V., Sivula, K. et al. Highly active oxide photocathode for photoelectrochemical water reduction. Nature Mater 10, 456–461 (2011). https://doi.org/10.1038/nmat3017
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/nmat3017
This article is cited by
-
High carrier mobility along the [111] orientation in Cu2O photoelectrodes
Nature (2024)
-
Improving the photovoltage of Cu2O photocathodes with dual buffer layers
Nature Communications (2023)
-
Epitaxially grown silicon-based single-atom catalyst for visible-light-driven syngas production
Nature Communications (2023)
-
Non-graphitized carbon/Cu2O/Cu0 nanohybrids with improved stability and enhanced photocatalytic H2 production
Scientific Reports (2023)
-
Recent Advancements in Photoelectrochemical Water Splitting for Hydrogen Production
Electrochemical Energy Reviews (2023)