Abstract
Thermoelectrics have great potential for use in waste heat recovery to improve energy utilization. Moreover, serving as a solid-state heat pump, they have found practical application in cooling electronic products. Nevertheless, the scarcity of commercial Bi2Te3 raw materials has impeded the sustainable and widespread application of thermoelectric technology. In this study, we developed a low-cost and earth-abundant PbS compound with impressive thermoelectric performance. The optimized n-type PbS material achieved a record-high room temperature ZT of 0.64 in this system. Additionally, the first thermoelectric cooling device based on n-type PbS was fabricated, which exhibits a remarkable cooling temperature difference of ~36.9 K at room temperature. Meanwhile, the power generation efficiency of a single-leg device employing our n-type PbS material reaches ~8%, showing significant potential in harvesting waste heat into valuable electrical power. This study demonstrates the feasibility of sustainable n-type PbS as a viable alternative to commercial Bi2Te3, thereby extending the application of thermoelectrics.
Similar content being viewed by others
Introduction
Thermoelectric (TE) materials have garnered significant attention due to their capability of converting heat into electricity directly and reversibly1,2,3,4,5,6, which has great potential to use for waste heat recovery to improve the energy utilization and sustainability. Additionally, TE cooling technology plays a crucial role in heat dissipation for electronic products, due to its high reliability and ease of miniaturization7,8,9,10. To assess the performance of TE materials, a dimensionless figure of merit ZT = S2σT/κtot was used. It is defined by the Seebeck coefficient S, electrical conductivity σ, total thermal conductivity κtot (including electrical thermal conductivity κele, and lattice thermal conductivity κlat) and Kelvin temperature T. A good thermoelectrics need to possess a large S and high σ, together with a low κ. However, these physical parameters σ, S and κtot are inherently interconnected through carrier concentration n, which makes the TE performance optimization be challenging11,12,13,14,15.
As one of the earliest discovered thermoelectric semiconductors, Bi2Te3-alloy has dominated the commercial thermoelectric material for over half a century3. After years of continuous research, currently, the ZT of commercially applied Bi2Te3 materials is close to 1.0 at room temperature (Supplementary Fig. 1). However, in recent years, with in-depth research on this material system, it has been found that there is limited room for improvement in thermoelectric performance of Bi2Te3 materials3,6. Additionally, the small bandgap of Bi2Te3, approximately 0.15 eV, results in intrinsic excitations occurring around 50 °C, leading to a sharp decrease in thermoelectric performance with increasing temperature and limiting its application in thermoelectric power generation16.
Moreover, as shown in Fig. 1a, tellurium is an extremely scarce element with a crustal abundance of only 0.001 ppm17. The global annual production of Te is currently only about 470 tons18. The rapid development of thermoelectric technology has driven a surge in demand for tellurium raw materials, which, in turn, limits the further widespread application of thermoelectric technology. Therefore, it is imperative to develop earth-abundant and high-performance thermoelectric materials that can replace Bi2Te3.
Lead chalcogenide, including PbTe, PbSe and PbS, is a group of traditional medium-temperature TE materials with impressive performance19,20,21,22,23,24,25,26,27,28,29,30,31,32,33,34,35. Among them, PbS has drawn wide attention because of its decent TE performance and earth-abundant composition (depicted in Fig. 1a)17,36. Because of the strong chemical bonding and light constitution of sulfur, pristine PbS possesses an intrinsic high κlat and low n, which hinders its development in thermoelectrics21. To address these issues, numerous strategies have been developed to optimize the transport properties of PbS, such as forming solid solution37, nano-structuring38,39,40, band sharpening41, conduction band alignment42 and Fermi level pinning43. These efforts have resulted in a maximum ZT of ~1.7 at 850 K for PbS40. Nevertheless, because of the inferior TE performance at low temperature, for a long time, PbS was thought to be a medium-temperature thermoelectrics that can only operate at relatively high temperature. The investigation of its room temperature TE performance has long been neglected21, and the PbS had never been considered as a feasible TE cooling material21,37,38,39,40,41,42,43,44,45,46.
In this work, we demonstrate that the thermoelectric performance of PbS can be significantly improved in the low temperature region, making it possible to work as a solid-state heat pump and could be a viable alternative to commercial Bi2Te3 material. As depicted in Fig. 1b, our optimal PbS sample exhibits a high power factor (PF), which is comparable to that of n-type commercial Bi2Te3 (COML BT), and possesses a higher ZT than the COML BT above 373 K. Owing to the high TE performance and abundance in raw material6,17, our PbS sample exhibits a higher ZTave and much higher cost effectiveness (the ratio of ZTave and cost) than the COML BT, as shown in Fig. 1c. The TE performance optimization route for PbS is shown in Fig. 1d, e. Here, we focus on improving the carrier mobility μ and low temperature TE performance of PbS through lattice plainification and Cu interstitial doping based on a PbS matrix with low thermal conductivity. Additional Pb was added to the matrix to realize lattice plainification, which compensates for the intrinsic cation vacancy and reduces the carrier scattering, achieving the simultaneous optimization of carrier mobility and carrier density. Furthermore, interstitial Cu was introduced to denote free electron, optimizing the carrier density and improving the electrical transport properties over a wide temperature range. Through lattice plainification and interstitial doping, the optimized Pb1.004S0.6Se0.4 + 0.001Cu polycrystal exhibits a decent room temperature ZT of ~0.45. To further improve the carrier mobility and TE performance, the Pb1.004S0.6Se0.4 + 0.001Cu compound was grown into high quality crystals (Fig. 1f). This results in a substantial increase in mobility and consequently enhances its PF to ~31.5 μW cm−1 K−2 at room temperature. The promotion of electrical transport properties lead to the enhancement of ZT in the whole investigated temperature range. Ultimately, the Pb1.004S0.6Se0.4 + 0.001Cu crystal achieved a record high room temperature ZT of ~0.64 and an average ZT of ~0.92 in the temperature range of 300–823 K, see Fig. 1e. Based on this, the single-leg efficiency of our sample reached ~8% when subjected to a temperature difference of 474 K. (Fig. 1g) And a 7-pair TE module (shown in Fig. 1f) had been prepared by using the n-type Pb1.004S0.6Se0.4 + 0.001Cu crystal and p-type commercial Bi2Te3 (Supplementary Fig. 1), which exhibits a cooling temperature difference of ~36.9 K when the hot end temperature at 303 K (Fig. 1g).
Results
Se alloying to suppress the thermal conductivity
Compared with PbSe and PbTe, PbS has a higher κlat, which limits the improvement of its ZT17. In order to optimize its thermal conductivity, we substituted part of S with Se and synthesized a series of PbS1-xSex by combining the high temperature melting with Spark Plasma Sintering (SPS). The powder X-ray diffraction (PXRD) results in Supplementary Fig. 2a shows that all PbS1-xSex (x = 0–0.5) samples are single phase and can be well indexed to the rock salt structure. Because of the larger atomic radius of Se than that of S, the diffraction peaks gradually shift to the low angle with increasing Se amount. The calculated lattice parameter in Supplementary Fig. 2b shows a linear dependence with increasing Se content, following the Vegard’s law. This indicating the Se is successfully alloying into the PbS matrix.
Transport properties of PbS1-xSex (x = 0–0.5) samples were shown in Supplementary Figs. 3 and 4. The electrical transport properties of the materials are basically not affected by Se alloying (Supplementary Fig. 3a). However, heavy Se alloying makes the κlat of the material greatly reduced due to the mass fluctuation and strain field fluctuation37,47. The room temperature κlat reduces from 2.24 W m−1 K−1 of PbS to 1.13 W m−1 K−1 of PbS0.6Se0.4, representing a 50% reduction, and an extremely low κlat of 0.82 W m−1 K−1 was obtained in PbS0.6Se0.4 at 823 K, see Supplementary Fig. 3b. Comparing the κlat of our PbS0.6Se0.4 sample with other reported lead chalcogenide materials, the PbS0.6Se0.4 shows a relatively low κlat, especially at room temperature37,42,43,44,46,47,48,49 (Supplementary Fig. 3c). Finally, the highest room temperature ZT of ~0.35 is obtained in PbS0.6Se0.4, as shown in Supplementary Fig. 3d, and its ZT value improves in the whole investigated temperature range due to the decrease in κlat. Thus, the PbS0.6Se0.4 was chosen as the starting matrix for further optimization.
Pb compensation for lattice plainification
It has been reported that fine tuning on eigenelements could contribute to the improvement in mobility and result in an enhanced ZT value at room temperature both in theoretically and experimentally48,49,50,51. To optimize the electronic transport properties of the PbS0.6Se0.4 matrix, we conducted Pb compensation in this compound, and a series of polycrystalline Pb1+yS0.6Se0.4 (y = 0–0.006) samples were synthesized. PXRD results in Supplementary Fig. 5a shows that all Pb1+yS0.6Se0.4 samples are single phase. Lattice parameters of the samples are almost constant with increasing Pb, as shown in Supplementary Fig. 5b. The Scanning transmission electron microscopy (STEM) results of PbS0.6Se0.4 and Pb1.004S0.6Se0.4 are shown in Fig. 2a, b. Obviously, some dark areas were observed in PbS0.6Se0.4, indicating the presence of intrinsic Pb vacancies in the material. With adding extra Pb, these dark areas disappear in Pb1.004S0.6Se0.4, implying the Pb vacancies were compensated. The line profile obtained from the zoom in area of PbS0.6Se0.4 and Pb1.004S0.6Se0.4 is shown in Fig. 2c. The peak with weaker intensity indicated by the arrow corresponds to the presence of Pb vacancy. The densities of Pb vacancies in PbS0.6Se0.4 and Pb1.004S0.6Se0.4 have also been directly counted from the STEM image, as shown in Supplementary Fig. 6. The density of Pb vacancy in PbS0.6Se0.4 is 0.28 nm−2, and the number reduces to 0.03 nm−2 after Pb compensation. These results support the conclusion that Pb compensation is an effective tool for reducing the intrinsic cation vacancy in PbS0.6Se0.4.
The electrical transport properties of Pb1+yS0.6Se0.4 are demonstrated in Fig. 2d–g. By adding the extra Pb, the intrinsic cation vacancies were compensated, which reduces the carrier scattering brought by the cation vacancies. This improvement is reflected in the increase in μ from ~580 cm−2 V−1 s−1 in the matrix to ~633 cm−2 V−1 s−1 in Pb1.002S0.6Se0.4, and it remains at ~614 cm−2 V−1 s−1 in Pb1.004S0.6Se0.4. In addition, the reduction in Pb vacancy also increases the electron density, from ~2.32 × 1018 cm−3 in the matrix to ~3.71 × 1018 cm−3 in Pb1.004S0.6Se0.4, representing a 60% increase. (Fig. 2d) The realization of lattice plainification significantly improve the electrical conductivities of Pb1+yS0.6Se0.4, particularly in the low temperature range. The highest room temperature σ of 365 S cm−1 was obtained in Pb1.004S0.6Se0.4, representing a 70% enhancement compared to the pristine PbS0.6Se0.4. Although the increase in n slightly lowers the S, the significant improvement in σ result in the improved PF over a wide temperature range, see Fig. 2g. The average PF (PFave) at 300–823 K increased from ~7.7 μW cm−1 K−2 in PbS0.6Se0.4 to ~10.4 μW cm−1 K−2 in Pb1.004S0.6Se0.4. The temperature dependent κtot and κlat of Pb1+yS0.6Se0.4 are shown in Fig. 2h. Because of the reduction in cation vacancies and the phonon scattering, the κtot and κlat increases with adding extra Pb. The κlat increases 10% in Pb1.004S0.6Se0.4 compared with that of matrix. This in turn, supports the idea that the introduction of extra Pb is effective to cause the lattice plainification effect.
Although introducing the extra Pb reduces the intrinsic cation vacancy and enhances the κ, this effect also increases the μ and significantly improves the electrical transport properties. As a result, the TE performance has been improved over a wide temperature range, as shown in Fig. 2i. The ZTave increased from ~0.36 in PbS0.6Se0.4 to ~0.47 in Pb1.004S0.6Se0.4 in the temperature range of 300–823 K. The Pb1.004S0.6Se0.4, exhibits highest PF and ZT, was chosen for further optimization.
Interstitial Cu to optimize the carrier concentration
It has been proved that interstitial Cu plays an important role in wide temperature range ZT enhancement for n-type lead chalcogenide52,53,54. Here, extra Cu was introduced to the Pb1.004S0.6Se0.4 to optimize its electron density. PXRD result in Supplementary Fig. 8a shows that the diffraction peaks of all Pb1.004S0.6Se0.4 + zCu (z = 0–0.006) samples can be indexed to the rock salt structure, and no obvious second phase has been observed. Because the additional Cu is in a tiny amount, the lattice parameters of all samples are almost constant, as shown in Supplementary Fig. 8b. The results of STEM demonstrate that Cu atoms form tiny cluster at nanoscale. (Fig. 3a) The amplified picture of Cu-rich area in Fig. 3b clearly shows that Cu atom occupy at interstitial site in the lattice. The line intensity scan profile shown in Supplementary Fig. 9a distinctly reveals the presence of Cu interstitial and prove it has an equal distance to the surrounding Pb/S atoms, indicating Cu occupies in the center of the cube made up of Pb and S/Se atoms. The multi-slice simulation of ADF-STEM image based on the crystal model is consistent with experimental results, as shown in Supplementary Fig. 9b.
To further reveal the formation mechanism of Cu interstitial, corresponding point defect formation energy was calculated. The details for the calculation method are shown in Supplementary information. Figure 3c and Supplementary Fig. 10 exhibit the point defect formation energy as a function of Fermi energy (EF) in Pb-rich and S-rich conditions, respectively. Considering the Pb compensation carried out in our work, attention should be paid to the Pb-rich condition. As shown in Fig. 3c, when Cu enters the lattice interstitial, the system possesses the lowest formation energy. This indicates that Cu prefers to occupy the interstitial site in Pb-rich condition rather than replaces the Pb atom. Similar results has been observed in PbSe systems53. The defect formation energy calculation consolidates the STEM results, indicating the additional Cu atom occupied in the interstitial site, which donates free electron into the PbS matrix and optimizes the n. The calculated band gap results and optical band gap results show that the interstitial Cu has little impact on the band gap of Pb-S-Se system. Moreover, the adding Cu would make the Fermi level move toward the conduction band, as shown in Supplementary Fig. 11a–c.
Cu interstitial would denote free electrons to the matrix and the sample exhibits heavily doped degenerate semiconductor transport characteristics, as shown in Supplementary Fig. 11d and Supplementary Fig. 12. As Cu interstitial doping could optimize the n of Pb1.004S0.6Se0.4 + zCu, the σ was dramatically enhanced and the S decreased gradually with increasing Cu content, as shown in Fig. 3d–f. The room temperature PF climbs up from ~17.6 μW cm−1 K−2 in Pb1.004S0.6Se0.4 to ~20.6 μW cm−1 K−2 in Pb1.004S0.6Se0.4 + 0.001Cu and then declines when further increasing the Cu content. Moreover, in the temperature range of 450 − 823 K, the PF of Pb1.004S0.6Se0.4 + zCu had been significantly improved with adding Cu, which goes from ~5.3 μW cm−1 K−2 in Pb1.004S0.6Se0.4 to ~13.2 μW cm−1 K−2 in Pb1.004S0.6Se0.4 + 0.006Cu at 823 K (Fig. 3g). The interstitial Cu not only contribute to the enhancement of electrical transport properties, but also lead to the reduction in κlat due to the enhanced phonon scattering. Figure 3h shows the thermal transport properties of Pb1.004S0.6Se0.4 + zCu. Obviously, the effect of extra Cu on reducing κlat become more pronounced as the temperature rises. We believe this is account for the dissolve of interstitial Cu, which has been previously reported54. The increased κtot depicted in Fig. 3h is caused by the increased κele (Supplementary Fig. 13d). The simultaneous optimization of both electrical and thermal transport properties is acquired as a result of Cu interstitial doping, and the ZT was enhanced in the whole investigated temperature range, see Fig. 3i. Among the Cu interstitial doped samples, Pb1.004S0.6Se0.4 + 0.001Cu possesses the highest ZTave of ~0.74 in the temperature range of 300–823 K, and it also obtained a peak ZT value of ~1.0 at 773 K.
Growing crystal to improve the carrier mobility and thermoelectric performance
To further enhance the electrical transport properties of Pb1.004S0.6Se0.4 + 0.001Cu, we conducted crystal growth via vertical Bridgman method to reduce the carriers scattering on grain boundaries. The bulk XRD of the crystal cleavage plane for the crystal sample exhibits only the (200) and (400) diffraction peaks, in contrast to the polished SPS sample, which possesses the entire diffraction pattern of the rock salt structure. This implies the Pb1.004S0.6Se0.4 + 0.001Cu crystal is well crystallized. Laue diffraction patterns in the insert of Fig. 4a and the picture of the crystal sample in Fig. 1f also confirmed the good quality of the crystal samples.
Scanning electron microscope (SEM) results exhibit the microstructure contrast between polycrystalline sample (Fig. 4b) obtained through SPS and crystal sample (Fig. 4c) obtained through vertical Bridgman method. In the SEM result of SPSed sample, obvious grain boundaries could be observed, the black spots are the holes formed during the sintering process. On the contrary, the crystal sample shows no grain boundary at the same magnification scale. Figure 4d shows the significant improvement of μ in the crystal sample compared with the SPSed sample. The μ reaches ~552 cm−2 V−1 s−1 in crystal sample and realizes ~60% increase. This high μ in crystal sample is caused by the reduction of carrier scattering on grain boundary.
On account of the optimized μ, the crystal sample shows extraordinary TE performance compared with the SPSed sample. Figure 4e–g exhibits the electrical transport properties of SPSed sample and crystal sample. The crystal sample has a higher σ, this increase is caused by the improved μ, which resulted from the reduction of carriers scattering on the grain boundaries. In addition, the lower n leads to the enhancement in S, thus making the crystal sample exhibit a higher PF, especially in low temperature region, the crystal obtained a peak PF of ~31.5 μW cm−1 K−2 at room temperature. The crystal sample also reduces the phonon scattering on the grain boundaries, so the κlat of crystal sample is a slightly higher than that of the SPS sample, as shown in Fig. 4h. Owing to the elevated PF, the ZT of crystal sample achieves improvement over a wide temperature range. As shown in Fig. 3i, the crystal sample obtains a room temperature ZT of ~0.64 and a peak ZT of ~1.1 at 823 K.
As depicted in Fig. 5a, compared with other PbS-based materials, our sample has a higher weighted mobility μW, especially in low temperature range. Due to the high μW, our sample shows a significant advantage in PF below 523 K, as shown in Fig. 5b. The PFave between 300 and 523 K reaches ~24.7 μW cm−1 K−2, which is a fairly high value for the PbS-based compound. (Fig. 5c) The value of μW/κlat indicates that the low κlat brought by Se alloying and Cu interstitial doping also matters for the elevated ZT compared with other PbS-based materials, as shown in Fig. 5d, e. Finally, because of the improvement in TE performance at room temperature, the ZTave of our sample reaches ~0.92 at the temperature range of 300–823 K, as depicted in Fig. 5f, which is the highest ZTave among PbS-based material systems21,37,38,39,40,41,42,43,44,45,46.
To further evaluate the TE performance of the Pb1.004S0.6Se0.4 + 0.001Cu crystal, we built a 7-pair TE module based on our n-type material and commercial p-type Bi2Te3. The maximum cooling temperature difference of this module reached ~36.9 K at the hot end temperature of 303 K, (Supplementary Fig. 14) which is close to the reported maximum cooling temperature difference of ~42.6 K for PbTe-based device49, indicating that PbS also has the potential to serve as a TE cooling material. The high ZTave of ~0.92 shown in the crystal sample also implies that our work has an advantage in power generation. Thus, we conducted a single-leg energy conversion efficiency test to evaluate its performance. Supplementary Fig. 15 and Fig. 5g, h show the experiment data of single-leg power generation with the Tc of 295 K, including output voltage U, output power P and conversion efficiency η as a function of the electric current I. The y-axis value in Supplementary Fig. 15 shows an open-circuit voltage that relates to the Seebeck voltage of the single-leg device, which rises from ~5 mV at a ΔT of 33 K to ~110 mV at a ΔT of 474 K. The P–I plot in Fig. 5g indicates the single-leg device possesses a maximum P of ~38 mV. The power generation capacity increases with the elevated ΔT owing to the continuously increasing ZTave of the crystal sample in the investigated temperature range, and it achieves a high efficiency of ~8% when I = 0.7 A, ΔT = 474 K (Fig. 5h). Figure 5i shows a comparison of the TE power generation efficiency of our sample with other TE materials. Compared with other sulfur-based TE materials39,55,56,57,58, our work shows outstanding performance and achieves a high efficiency at a temperature difference of 474 K.
Discussion
More than 60% of energy generated by fossil fuels is dissipated as waste heat, which is challenging to directly recover and utilize1. Thermoelectric materials, by converting heat directly into electrical energy, enable the recovery and utilization of low-grade waste heat resources, thereby improving the energy utilization and sustainability, reducing the energy costs and carbon emissions. Additionally, thermoelectric cooling technology is considered an ideal choice for temperature control of electronic devices due to its high reliability, rapid response, precise temperature control, and ease of miniaturization. Despite the promising applications of thermoelectric technology, existing commercial thermoelectric material contain the rare element tellurium, hindering the sustainable and widespread application of thermoelectric technology.
In this study, we demonstrate the low-cost and earth-abundant PbS holds great potential for use in both thermoelectric cooling and power generation. Lattice plainification and interstitial doping strategies were employed to optimize the electronic transport properties of PbS, and a remarkable power factor of ~31.5 μW cm−1 K−2 and a record high room temperature ZT of ~0.64 have been achieved in the Pb1.004S0.6Se0.4−0.001Cu crystal. Based on this, the first thermoelectric cooling module based on n-type PbS was fabricated, gaining a maximum temperature difference of ~36.9 K when the hot end temperature is 303 K. Furthermore, a single-leg device using our PbS material demonstrates a relatively high power generation efficiency of ~8% at a temperature difference of 474 K, indicating that PbS holds significant potential for harvesting waste heat into valuable electrical power. This study presents a systematic approach to optimizing the low temperature thermoelectric performance of PbS, and demonstrates that PbS could be a viable alternative to commercial Bi2Te3. This development contributes to the sustainability of thermoelectric technology.
Methods
Sample synthesis
All samples were weighted with nominal ratio using high-purity raw material, put in quartz tubes and flame-sealed after vacuum. They were heated to 723 K in 12 h, then took 7 h from 723 K to 1403 K, kept at 1403 K for 6 h, finally the polycrystalline ingots were obtained after furnace cooling. Compact polycrystalline samples were obtained through Spark Plasma Sintering (SPS-211Lx) at 873 K for 6 min under 50 MPa compressive stress using the powder of the polycrystalline ingots. The crystal samples were obtained through the vertical Bridgman method, they were first synthesized with the same procedure as polycrystal, then the obtained ingot was grounded into powder. The powder was loaded into silica tubes and flame sealed at a residual pressure under 10−4 Pa. Then it was heated to 1403 K in 11 h, kept for 3 h and cooled at a rate of 1 K per h from 1403 K to 1303 K. Then the furnace was shut down and cooled to room temperature.
Structural characterization
The PXRD patterns of all samples were obtained using D/max2200PC instrument operating at 40 KV and 40 mA with Cu Kα (λ = 1.5418 Å) radiation. The Laue pattern was obtained on a diffractometer operating at 20 KV and 20 mA.
Microstructure investigation
The Scanning electron microscopy (SEM) was carried out through a field emission SEM (JEOL, JSM-7000F) with an acceleration voltage of 20 KV. The High-resolution Scanning transmission electron microscopy (HR-STEM) was carried out through JEM F200 with a Schottky hot field gun at 200 KV. The high-resolution images in Figs. 2c and 3b and Supplementary Fig. 9a were Gaussian blurred for better visualization.
Hall measurements
Hall coefficient (RH) of all samples with thickness of ~0.7 mm was measured through Lake Shore 8400 Series with invertible magnetic field of 0.9 T and current of 15 mA applied. The carrier density (nH) and carrier mobility (μH) were calculated through nH = 1/(eRH), μH = σRH, respectively.
Thermoelectric transport properties measurements
All samples were cut into cuboids with sample size of ~10 × 3 × 3 mm3 and slices with sample size of ~8 × 8 × 1.5 mm3 for electrical and thermal properties measurements, respectively. The Seebeck coefficient S and electrical conductivity σ were obtained concurrently through Cryoall CTA instrument under a low-pressure helium atmosphere. Total thermal conductivity κtot was calculated through κtot = DρCp. Thermal diffusivity D was obtained through Cryoall CLA1000 and analyzed using Cowan model with pulse correction. Sample density ρ was calculated through sample mass and dimensions. The specific heat capacity Cp was calculated through Debye model. The combined uncertainty for all measurements involved in the calculation of ZT was less than 20%.
Single leg conversion efficiency test
The single leg power generation efficiency is conducted by Mini-PEM instrument (Advance Riko) under vacuum, using a nominal hot-side temperature at 300–773 K. The hot and cold sides of the single-leg were galvanized to form Ni-based barrier layer using commercial nickel-plating solution, and copper wires were soldered by Ag-based solder.
Thermoelectric module fabrication and cooling performance test
The optimized PbS ingot and commercial p-type Bi2Te3 were cut into cuboids with size of 2 × 2 × 4 mm3 and then put into ethyl alcohol for ultrasonic cleaning. Then the cuboids were galvanized to form Ni-based barrier layer using commercial nickel-plating solution, and then the cuboids were welded on Cu electrode using Sn48Bi52 solder paste. Finally, the n-type PbS-based thermoelectric cooling module was fabricated and the cooling performance was test using Z-meter DX4090.
Data availability
The authors declare that the data supporting the findings of this study are available on reasonable request.
References
Yan, Q. & Kanatzidis, M. G. High-performance thermoelectrics and challenges for practical devices. Nat. Mater. 21, 503–513 (2022).
Zhang, X. & Zhao, L.-D. Thermoelectric materials: energy conversion between heat and electricity. J. Materiomics 1, 92–105 (2015).
Han, Z. et al. Room-temperature thermoelectric materials: challenges and a new paradigm. J. Materiomics 8, 427–436 (2022).
Ge, Z.-H. et al. Highly stabilized thermoelectric performance in natural minerals. Joule 8, 129–140 (2024).
Xie, H., Zhao, L.-D. & Kanatzidis, M. G. Lattice dynamics and thermoelectric properties of diamondoid materials. Interdiscip. Mater. 3, 5–28 (2024).
Shi, X.-L., Zou, J. & Chen, Z.-G. Advanced thermoelectric design: from materials and structures to devices. Chem. Rev. 120, 7399–7515 (2020).
Cai, B., Zhao, S. & Liu, F. Micro TEC manufacture: the importance and challenges. Mater. Lab 2, 230011 (2023).
Wu, Z., Zhang, S., Liu, Z., Mu, E. & Hu, Z. Thermoelectric converter: strategies from materials to device application. Nano Energy 91, 106692 (2022).
Sun, W., Liu, W.-D., Liu, Q. & Chen, Z.-G. Advances in thermoelectric devices for localized cooling. Chem. Eng. J. 450, 138389 (2022).
Zhao, D. & Tan, G. A review of thermoelectric cooling: materials, modeling and applications. Appl. Therm. Eng. 66, 15–24 (2014).
Qin, B., Wang, D. & Zhao, L.-D. Slowing down the heat in thermoelectrics. InfoMat 3, 755–789 (2021).
Toberer, E. S., May, A. F. & Snyder, G. J. Zintl chemistry for designing high efficiency thermoelectric materials. Chem. Mater. 22, 624–634 (2010).
Zeier, W. G. et al. Thinking like a chemist: intuition in thermoelectric materials. Angew. Chem. Int. Ed. 55, 6826–6841 (2016).
Liu, W. et al. Uplimit (ZT)max and effective merit parameter B* of thermoelectric semiconductors. Mater. Today Phys. 31, 100989 (2023).
Wang, L., Zhang, X. & Zhao, L.-D. Evolving strategies toward Seebeck coefficient enhancement. Acc. Mater. Res. 4, 448–456 (2023).
Resendiz-Hernandez, G. et al. Structural properties, bandgap, and complex dielectric function in Bi2Te3 thermoelectric by valence electron energy loss spectroscopy (VEELS) analysis. J. Alloys Compd. 965, 171420 (2023).
Ge, Z.-H. et al. Low-cost, abundant binary sulfides as promising thermoelectric materials. Mater. Today 19, 227–239 (2016).
Calvo, G. & Valero, A. Strategic mineral resources: availability and future estimations for the renewable energy sector. Environ. Dev. 41, 100640 (2022).
Xiao, Y. & Zhao, L.-D. Charge and phonon transport in PbTe-based thermoelectric materials. npj Quantum Mater. 3, 55 (2018).
Sun, J., Zhang, Y., Fan, Y., Tang, X. & Tan, G. Strategies for boosting thermoelectric performance of PbSe: a review. Chem. Eng. J. 431, 133699 (2022).
Liu, W., Xu, L., Xiao, Y. & Zhao, L.-D. Strategies to advance earth-abundant PbS thermoelectric. Chem. Eng. J. 465, 142785 (2023).
Zhou, C. & Chung, I. Nanoscale defect structures advancing high performance n-type PbSe thermoelectrics. Coord. Chem. Rev. 421, 213437 (2020).
Chang, C. et al. High performance thermoelectrics from earth-abundant materials: enhanced figure of merit in PbS through nanostructuring grain size. J. Alloys Compd. 664, 411–416 (2016).
Li, M. et al. Room temperature aqueous-based synthesis of copper-doped lead sulfide nanoparticles for thermoelectric application. Chem. Eng. J. 433, 133837 (2022).
Zhang, J. et al. Extraordinary thermoelectric performance realized in n-type PbTe through multiphase nanostructure engineering. Adv. Mater. 29, 1703148 (2017).
Zhou, C. et al. High-performance n-type PbSe–Cu2Se thermoelectrics through conduction band engineering and phonon softening. J. Am. Chem. Soc. 140, 15535–15545 (2018).
Wu, Y. et al. Lattice strain advances thermoelectrics. Joule 3, 1276–1288 (2019).
Biswas, K. et al. Strained endotaxial nanostructures with high thermoelectric figure of merit. Nat. Chem. 3, 160–166 (2011).
Biswas, K. et al. High-performance bulk thermoelectrics with all-scale hierarchical architectures. Nature 489, 414–418 (2012).
Luo, Z.-Z. et al. Extraordinary role of Zn in enhancing thermoelectric performance of Ga-doped n-type PbTe. Energy Environ. Sci. 15, 368–375 (2022).
Rathore, E. et al. Enhanced covalency and nanostructured-phonon scattering lead to high thermoelectric performance in n-type PbS. Mater. Today Energy 24, 100953 (2022).
Roychowdhury, S., Dutta, M. & Biswas, K. Enhanced thermoelectric performance in topological crystalline insulator n-type Pb0.6Sn0.4Te by simultaneous tuning of the band gap and chemical potential. J. Mater. Chem. A 6, 24216–24223 (2018).
Wu, Y. X. et al. Thermoelectric enhancements in PbTe alloys due to dislocation-induced strains and converged bands. Adv. Sci. 7, 1902628 (2020).
You, L. et al. Realization of higher thermoelectric performance by dynamic doping of copper in n-type PbTe. Energy Environ. Sci. 12, 3089–3098 (2019).
Zhao, L. D. et al. High performance thermoelectrics from earth-abundant materials: enhanced figure of merit in PbS by second phase nanostructures. J. Am. Chem. Soc. 133, 20476–20487 (2011).
Sun, F.-H. et al. Review of current ZT > 1 thermoelectric sulfides. J. Materiomics 10, 218–233 (2023).
Zhao, M., Chang, C., Xiao, Y. & Zhao, L.-D. High performance of n-type (PbS)1-x-y(PbSe)x(PbTe)y thermoelectric materials. J. Alloys Compd. 744, 769–777 (2018).
Hou, Z., Qiu, Y., Ren, D., Huang, Z. & Zhao, L.-D. Enhancing thermoelectric transport properties of n-type PbS through introducing CaS/SrS. J. Solid State Chem. 280, 120995 (2019).
Yang, J. et al. Dual-site doping and low-angle grain boundaries lead to high thermoelectric performance in n-type Bi2S3. Adv. Funct. Mater. 34, 2306961 (2024).
Ibáñez, M. et al. High-performance thermoelectric nanocomposites from nanocrystal building blocks. Nat. Commun. 7, 10766 (2016).
Xiao, Y. et al. Band sharpening and band alignment enable high quality factor to enhance thermoelectric performance in n-type PbS. J. Am. Chem. Soc. 142, 4051–4060 (2020).
Luo, Z.-Z. et al. Valence disproportionation of GeS in the PbS matrix forms Pb5Ge5S12 inclusions with conduction band alignment leading to high n-type thermoelectric performance. J. Am. Chem. Soc. 144, 7402–7413 (2022).
Luo, Z.-Z. et al. Enhancement of thermoelectric performance for n-type PbS through synergy of gap state and Fermi level pinning. J. Am. Chem. Soc. 141, 6403–6412 (2019).
Hou, Z. et al. Contrasting thermoelectric transport properties of n-type PbS induced by adding Ni and Zn. ACS Appl. Energy Mater. 4, 6284–6289 (2021).
Hou, Z. et al. Boosting thermoelectric performance of n-type PbS through synergistically integrating In resonant level and Cu dynamic doping. J. Phys. Chem. Solids 148, 109640 (2021).
Zhao, M. et al. Investigations on distinct thermoelectric transport behaviors of Cu in n-type PbS. J. Alloys Compd. 781, 820–830 (2019).
Cheng, R. et al. Bridging the miscibility gap towards higher thermoelectric performance of PbS. Acta Mater. 220, 117337 (2021).
Wang, S. et al. Fine tuning of defects enables high carrier mobility and enhanced thermoelectric performance of n-type PbTe. Chem. Mater. 35, 755–763 (2023).
Zhu, Y. et al. Large mobility enables higher thermoelectric cooling and power generation performance in n-type AgPb18+xSbTe20 crystals. J. Am. Chem. Soc. 145, 24931–24939 (2023).
Qin, B. & Zhao, L.-D. Moving fast makes for better cooling. Science 378, 832–833 (2022).
Qin, B. & Zhao, L.-D. Carriers: the less, the faster. Mater. Lab 1, 220004 (2022).
You, L. et al. Boosting the thermoelectric performance of PbSe through dynamic doping and hierarchical phonon scattering. Energy Environ. Sci. 11, 1848–1858 (2018).
Qian, X. et al. Contrasting roles of small metallic elements M (M = Cu, Zn, Ni) in enhancing the thermoelectric performance of n-type PbM0.01Se. J. Mater. Chem. A 8, 5699–5708 (2020).
Xiao, Y. et al. Remarkable roles of Cu to synergistically optimize phonon and carrier transport in n-type PbTe-Cu2Te. J. Am. Chem. Soc. 139, 18732–18738 (2017).
Zhang, Y.-X., Zhu, Y.-K., Feng, J. & Ge, Z.-H. Precious metal nanoparticles dispersing toward highly enhanced mechanical and thermoelectric properties of copper sulfides. J. Alloys Compd. 892, 162035 (2022).
Zhan, S. et al. Realizing high-ranged thermoelectric performance in PbSnS2 crystals. Nat. Commun. 13, 5937 (2022).
Chetty, R. et al. Power generation from the Cu26Nb2Ge6S32-based single thermoelectric element with Au diffusion barrier. J. Mater. Chem. C 7, 5184–5192 (2019).
Hu, H. et al. Thermoelectric Cu12Sb4S13-based synthetic minerals with a sublimation-derived porous network. Adv. Mater. 33, 2103633 (2021).
Acknowledgements
This work was primary supported by the National Science Fund for Distinguished Young Scholars (51925101), National Natural Science Foundation of China (52250090, 52371208, 52002042, 51772012, 51571007 and 12374023), the Beijing Natural Science Foundation (JQ18004), and the 111 Project (B17002). L.-D.Z. thanks for the support from Tencent Xplorer Prize.
Author information
Authors and Affiliations
Contributions
The manuscript was written through the contributions of all authors. All authors have approved the results and conclusions of this work. Lei Wang: investigation, data curation, writing, original draft; Yi Wen: conducted the SEM and STEM experiments; Shulin Bai: theoretical calculation; Cheng Chang, Shan Liu, Dongrui Liu, Siqi Wang, Zhe Zhao, Shaoping Zhan, Qian Cao, Xiang Gao: data analysis; Yichen Li: validation; Hongyao Xie and Li-Dong Zhao: research design, data analysis, draft writing and editing, and funding acquisition.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Biao Xu, Menghua Zhu, and the other anonymous reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, L., Wen, Y., Bai, S. et al. Realizing thermoelectric cooling and power generation in N-type PbS0.6Se0.4 via lattice plainification and interstitial doping. Nat Commun 15, 3782 (2024). https://doi.org/10.1038/s41467-024-48268-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-48268-3
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.