Abstract
STUDIES of the anion deficient phases of titanium and vanadium perovskites showed that the perovskite SrTiO3−x has a wide range of composition extending from x = 0 to x = 0.5 (ref. 1). The nonstoichiometry was inferred from the monophasic behaviour of the solid within this compositional range as obtained by means of powder X-ray diffraction. The same cubic structure was found for both Sr Ti O2.5 and Sr Ti O3. Perovskites have been widely studied recently in view of the very interesting and useful properties of these oxides2. The physiochemical properties of Sr Ti O3 include semiconductivity3,4 and superconductivity5 as well as peculiar phase transitions6. Of particular interest in this, and other7, systems is the presence of point defects and their influence on those properties. It seems that, at small degrees of reduction, doubly ionised oxygen vacancies are the main defects present on Sr Ti O3−x (ref. 8). Although in that case, the oxygen vacancies, being at small numbers, are probably distributed at random, the presence of so many empty oxygen positions as the stoichiometry of SrTiO2.5 implies—one in every six oxygens missing—automatically suggests the possibility of ordering. This possibility seems to be realised under the synthesis conditions that we have used and we report here some of the results so far obtained in the system SrO–Ti2O3–TiO2.
This is a preview of subscription content, access via your institution
Access options
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
References
Kestigian, M., Dickinson, J. G. & Ward, R. J. Am. chem. Soc. 5, 5598–5601 (1957).
Goodenough, J. B. & Longo, J. M. Crystallographic and Magnetic Properties of Perovskite and Perovskite Related Compounds. Landolt. Börnstein New Series. Group III, Vol 4a. New York: Springer Verlag (1970) p 126–314.
Cardona, M. Phys. Rev. 140, A651–A655 (1965).
Lee, C., Yahia, J. & Brebner, J. L. Phys. Rev. B3, 2525–2533 (1971).
Koonce, C. S., Cohen, M. L., Schooley, J. E., Hosler, W. R. & Pfeiffer, E. R. Phys. Rev. 163, 380–390 (1967).
Chang, T. S., Holzkichter, J. S., Jmbusch, G. F. & Schawlow, A. L. Solid state Commun. 8, 1179–1181 (1970).
Anderson, J. S. in Surface and Defect Properties of Solids (eds Roberts, M. W. & Thomas, J. M.) 1, 1–53 (Chemical Society, London, 1972).
Yamada, H. & Miller, G. R. J. Solid State Chem. 6, 169–177 (1973).
Anderson, J. S. in Modern Aspects of Solid State Chemistry (ed. Rao, C. N. R.) 29–106 (Plenum, New York, 1970).
Gorter, E. W. Proc. Intern. Congr. Pure and Appl. Chem. 17th Congr. 1, 300–306 (1959).
Negas, T. & Roth, R. S. Proc. 5th Materials Research Symp. Solid State Chem. N. B. S. Spec. Publ. 364, 233–263 (1972).
Jacobson, A. J. & Horrox, A. J. W. Acta Crystallogr. B32, 1003–1008 (1976).
Jacobson, A. J. Acta Crystallogr. B32, 1087–1090 (1976).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
FRANCO, M., REGÍ, M. Anion deficiency in strontium titanate. Nature 270, 706–708 (1977). https://doi.org/10.1038/270706a0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/270706a0
This article is cited by
-
Anion deficiency in strontium titanate
Nature (1978)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.