Abstract
Light-emitting diodes (LEDs) based on perovskite quantum dots (QDs) have produced external quantum efficiencies (EQEs) of more than 25% with narrowband emission1,2, but these LEDs have limited operating lifetimes. We posit that poor long-range ordering in perovskite QD films—variations in dot size, surface ligand density and dot-to-dot stacking—inhibits carrier injection, resulting in inferior operating stability because of the large bias required to produce emission in these LEDs. Here we report a chemical treatment to improve the long-range order of perovskite QD films: the diffraction intensity from the repeating QD units increases three-fold compared with that of controls. We achieve this using a synergistic dual-ligand approach: an iodide-rich agent (aniline hydroiodide) for anion exchange and a chemically reactive agent (bromotrimethylsilane) that produces a strong acid that in situ dissolves smaller QDs to regulate size and more effectively removes less conductive ligands to enable compact, uniform and defect-free films. These films exhibit high conductivity (4 × 10−4 S m−1), which is 2.5-fold higher than that of the control, and represents the highest conductivity recorded so far among perovskite QDs. The high conductivity ensures efficient charge transportation, enabling red perovskite QD-LEDs that generate a luminance of 1,000 cd m−2 at a record-low voltage of 2.8 V. The EQE at this luminance is more than 20%. Furthermore, the stability of the operating device is 100 times better than previous red perovskite LEDs at EQEs of more than 20%.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
References
Wang, K. et al. Suppressing phase disproportionation in quasi-2D perovskite light-emitting diodes. Nat. Commun. 14, 397 (2023).
Jiang, J. et al. Red perovskite light‐emitting diodes with efficiency exceeding 25% realized by co‐spacer cations. Adv. Mater. 34, 2204460 (2022).
Won, Y. H. et al. Highly efficient and stable InP/ZnSe/ZnS quantum dot light-emitting diodes. Nature 575, 634–638 (2019).
Wang, Y. K. et al. Bifunctional electron-transporting agent for red colloidal quantum dot light-emitting diodes. J. Am. Chem. Soc. 145, 6428–6433 (2023).
Jang, E. & Jang, H. Review: quantum dot light-emitting diodes. Chem. Rev. 123, 4663–4692 (2023).
Han, T.-H. et al. A roadmap for the commercialization of perovskite light emitters. Nat. Rev. Mater. 7, 757–777 (2022).
Lu, M. et al. Metal halide perovskite light‐emitting devices: promising technology for next‐generation displays. Adv. Funct. Mater. 29, 1902008 (2019).
Song, J. et al. Quantum dot light-emitting diodes based on inorganic perovskite cesium lead halides (CsPbX3). Adv. Mater. 27, 7162–7167 (2015).
Li, X. et al. CsPbX3 quantum dots for lighting and displays: room-temperature synthesis, photoluminescence superiorities, underlying origins and white light-emitting diodes. Adv. Funct. Mater. 26, 2435–2445 (2016).
Ahn, S. et al. Fine control of perovskite crystallization and reducing luminescence quenching using self‐doped polyaniline hole injection layer for efficient perovskite light‐emitting diodes. Adv. Funct. Mater. 29, 1807535 (2019).
Prakasam, V. et al. Large area perovskite light-emitting diodes by gas-assisted crystallization. J. Mater. Chem. C 7, 3795–3801 (2019).
Kim, Y.-H. et al. Comprehensive defect suppression in perovskite nanocrystals for high-efficiency light-emitting diodes. Nat. Photon. 15, 148–155 (2021).
Chen, W. et al. Highly bright and stable single-crystal perovskite light-emitting diodes. Nat. Photon. 17, 401–407 (2023).
Zhao, L., Lee, K. M., Roh, K., Khan, S. U. Z. & Rand, B. P. Improved outcoupling efficiency and stability of perovskite light‐emitting diodes using thin emitting layers. Adv. Mater. 31, 1805836 (2019).
Mu, Y., He, Z., Wang, K., Pi, X. & Zhou, S. Recent progress and future prospects on halide perovskite nanocrystals for optoelectronics and beyond. iScience 25, 105371 (2022).
Vashishtha, P. & Halpert, J. E. Field-driven ion migration and color instability in red-emitting mixed halide perovskite nanocrystal light-emitting diodes. Chem. Mater. 29, 5965–5973 (2017).
Zhao, L. et al. Thermal management enables bright and stable perovskite light‐emitting diodes. Adv. Mater. 32, 2000752 (2020).
Dong, Y. et al. Bipolar-shell resurfacing for blue LEDs based on strongly confined perovskite quantum dots. Nat. Nanotechnol. 15, 668–674 (2020).
Wang, Y. K. et al. All-inorganic quantum-dot LEDs based on a phase-stabilized alpha-CsPbI3 perovskite. Angew. Chem. Int. Ed. 60, 16164–16170 (2021).
Wang, Y.-K. et al. Self-assembled monolayer–based blue perovskite LEDs. Sci. Adv. 9, eadh2140 (2023).
Zhou, C. et al. Quantum dot self-assembly enables low-threshold lasing. Adv. Sci. 8, e2101125 (2021).
Peng, C. et al. A demulsification–crystallization model for high-quality perovskite nanocrystals. Adv. Mater. 35, 2206969 (2023).
Jiang, Y. et al. Synthesis-on-substrate of quantum dot solids. Nature 612, 679–684 (2022).
Choi, M.-J. et al. Cascade surface modification of colloidal quantum dot inks enables efficient bulk homojunction photovoltaics. Nat. Commun. 11, 103 (2020).
Bian, K. et al. Shape-anisotropy driven symmetry transformations in nanocrystal superlattice polymorphs. ACS Nano 5, 2815–2823 (2011).
Tan, W. L. & McNeill, C. R. X-ray diffraction of photovoltaic perovskites: Principles and applications. Appl. Phys. Rev. 9, 021310 (2022).
Lee, S. et al. Dipole engineering through the orientation of interface molecules for efficient InP quantum dot light-emitting diodes. J. Am. Chem. Soc. 144, 20923–20930 (2022).
Wang, Y. K. et al. All‐inorganic quantum‐dot LEDs based on a phase‐stabilized α‐CsPbI3 perovskite. Angew. Chem. Int. Ed. 60, 16164–16170 (2021).
Zhang, J. et al. A multifunctional “halide‐equivalent” anion enabling efficient CsPb(Br/I)3 nanocrystals pure‐red light‐emitting diodes with external quantum efficiency exceeding 23%. Adv. Mater. 35, 2209002 (2023).
Liu, Z. et al. Deep‐red perovskite light‐emitting diodes with external quantum efficiency exceeding 21% enabled by ligand‐modulated dimensionality control. Adv. Opt. Mater. 10, 2201123 (2022).
Xie, M. et al. High-efficiency pure-red perovskite quantum-dot light-emitting diodes. Nano Lett. 22, 8266–8273 (2022).
Wang, Y. K. et al. In situ inorganic ligand replenishment enables bandgap stability in mixed‐halide perovskite quantum dot solids. Adv. Mater. 34, 2200854 (2022).
Chiba, T. et al. Anion-exchange red perovskite quantum dots with ammonium iodine salts for highly efficient light-emitting devices. Nat. Photon. 12, 681–687 (2018).
Zhang, J. et al. Ligand‐induced cation–π interactions enable high‐efficiency, bright, and spectrally stable Rec. 2020 pure‐red perovskite light‐emitting diodes. Adv. Mater. 35, e2303938 (2023).
Xie, M. et al. Suppressing ion migration of mixed-halide perovskite quantum dots for high efficiency pure-red light-emitting diodes. Adv. Funct. Mater. 33, 2300116 (2023).
Hassan, Y. et al. Ligand-engineered bandgap stability in mixed-halide perovskite LEDs. Nature 591, 72–77 (2021).
Ke, Y. et al. Efficient and bright deep‐red light‐emitting diodes based on a lateral 0D/3D perovskite heterostructure. Adv. Mater. 16, 2207301 (2023).
Guo, B. et al. Ultrastable near-infrared perovskite light-emitting diodes. Nat. Photon. 16, 637–643 (2022).
Liu, Y. et al. Bright and stable light-emitting diodes based on perovskite quantum dots in perovskite matrix. J. Am. Chem. Soc. 143, 15606–15615 (2021).
Acknowledgements
We acknowledge the financial support from the National Natural Science Foundation of China (NSFC) (62205230 and 62175171), the Suzhou Key Laboratory of Functional Nano and Soft Materials, the Collaborative Innovation Center of Suzhou Nano Science and Technology (CIC-Nano), the 111 Project and the Joint International Research Laboratory of Carbon-Based Functional Materials and Devices. We acknowledge the Sargent group at the University of Toronto for providing access to the experimental facilities. This publication is based, in part, on the work supported by the Natural Sciences and Engineering Research Council of Canada.
Author information
Authors and Affiliations
Contributions
L.-S.L. supervised the project; L.-S.L. and Y.-K.W. conceived the idea and wrote the Article; Y.-K.W. and H.W. prepared the perovskite QDs, fabricated LEDs and performed the characterization of LEDs; S.T. and L.G. performed the GIWAXS and GISAXS measurements; Z.Z. performed the conductivity measurements under the supervision of S.-D.W.; F.Z. and H.-W.D. performed the optical measurements; F.Z., H.-W.D. and M.I. took the TEM measurements and performed the other morphology characterizations; and S.H. contributed to data analyses and provided instructive suggestions. All authors discussed the results and assisted in the preparation of the Article.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature thanks Kumar Sudhir, Lintao Hou and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data figures and tables
Extended Data Fig. 1 Property of original sample and thermal stability comparison.
a–c, Photoluminance spectra (a), excitation-dependent PLQY (b) and field-effect transistors (c) of original film. d, The emission peak dependence on aging time Inset: initial PL spectra of the original, control and treated perovskite films, and after 50 min.
Extended Data Fig. 2 In situ PL spectra measurements.
a, Scheme illustrating the system for the in situ PL measurement. It consists of 405 nm LED as a light source, optical fibers, a QE-Pro spectrometer (Ocean Optics) and a laptop. b, In situ time-dependent PL spectra of a QD solution during ligand exchange. The red arrow indicates the time the TMSBr was added. c, Extracted peak positions and FWHM from b.
Extended Data Fig. 3 Analysis of QD composition and arrangement.
a, XPS analysis showing the control and treated films have a similar composition with Br/I ratio difference <5%. b, FTIR results of original, control and treated films. c–d, TEM images of control (c) and treated (d) QDs supporting the claim of long-range order films for the treated CsPbBrxI3−x.
Extended Data Fig. 4 DFT calculation and crystal arrangement analysis.
a, Binding structure of OAc/OAm, AnHI and TMSBr on the surface of the nanocrystals. b, Electrostatic potential distribution in the AnHI and TMSBr molecules. c, Calculated binding affinity energy of AnHI and TMSBr, using OAc/OAm ligands as the control. d, The assigned Brag spots to CsPbBr3 with an extended lattice constant due to Iodine incorporation using GIXSGUI.
Extended Data Fig. 5 QD film stability and thickness analysis of LEDs.
a–c, PL mapping (a), SEM images (b) and AFM images (c) of original, control and treated CsPbBrxI3−x films. d, Cross-sectional TEM images show the thickness of each layer (the elemental distribution of Al, Pb and O as reference). e–f, AFM images with the thickness measurement details of the control films. g–h, AFM images with the thickness measurement details of the treated films.
Extended Data Fig. 6 Device performance of original and control LEDs.
a,b, Current density-voltage, luminance-voltage, EQE versus luminance curves of original (a) and control (b) LEDs.
Extended Data Fig. 7 LED performance emitting in the pure-red region.
a–d, Current density-voltage (a), luminance-voltage (b), EL spectra (c) and EQE versus luminance curve (d) of the pure-red LEDs with EL peak in the range of 630–640 nm. e–f, Quantitative statics and standard deviation for batch-to-batch (e) and performance variation within one batch (f).
Extended Data Fig. 8 Device interface engineering.
a, Device structure using PEDOT:PSS as the HIL and TPBI as the ETL, and the current density-voltage, luminance-voltage, EQE versus luminance curves of the LEDs. b, Device structure using NiOx/SAM as the HIL and TPBI as the ETL, and the current density-voltage, luminance-voltage, EQE versus luminance curves of the LEDs. c, Device structure using PEDOT:PSS as the HIL and CNT2T as the ETL, and the current density-voltage, luminance-voltage, EQE versus luminance curves of the LEDs.
Extended Data Fig. 9 Extracted LED stability.
a, Measured stability at luminance of 1100 cd m−2, 2200 cd m−2, 3150 cd m−2 and 4200 cd m−2. b, Extracted stability from the measured “n” derived from (a). c–f, Input voltage change during the operational lifetime measurements.
Extended Data Fig. 10 Analysis of aged control and treated LEDs.
a,b, TOF-SIMS depth profiles of the control (a) and treated (b) CsPbBrxI3−x LEDs before (a,d) and after electrical stress (continuous electrical aging at 1000 cd m−2 for 30 min) (b,e). c,d, Scheme illustrating the Br/I migration to the adjacent layers in control and the suppressed Br/I ion migration in the treated LEDs. e,f, EL spectra of original and control LEDs held at a current density of 10 mA cm−2 for 30 min. g, EL spectra of treated LEDs held at different current densities.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Wang, YK., Wan, H., Teale, S. et al. Long-range order enabled stability in quantum dot light-emitting diodes. Nature 629, 586–591 (2024). https://doi.org/10.1038/s41586-024-07363-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41586-024-07363-7
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.