High-resolution stereolithography using a static liquid constrained interface

  • Aftab A. Bhanvadia
  • Richard T. Farley
  • Toshikazu Nishida
Article

Announcements

Advertisement

  • Spin-orbit coupling in non-centrosymmetric crystals gives rise to interesting spin-momentum locking of the Fermi surface. Here, the electronic structure of polar metals BaMnX2 (X = Bi, Sb) reveals a high sensitivity to X sublattice distortions, resulting in a chemically tunable spin-valley coupling of Dirac fermions.

    • Masaki Kondo
    • Masayuki Ochi
    • Hideaki Sakai
    Article Open Access
  • Most alloys become mechanically brittle at very low temperatures. Here, an austenitic Fe-30Mn-0.11C steel exhibits high toughness, strength and elongation at liquid nitrogen temperatures, reaching a Charpy impact toughness of 453 J.

    • Yuhui Wang
    • Yubin Zhang
    • Xiaoxu Huang
    Article Open Access
  • Adiabatic demagnetization refrigeration is an efficient technique for reaching mK temperatures. Here, the water-free frustrated magnet KBaYb(BO3)2 is shown to combine cooling efficiency with stability upon exposure to air, vacuum, and heating, providing an alternative to the commonly used water-rich paramagnetic salts.

    • Yoshifumi Tokiwa
    • Sebastian Bachus
    • Philipp Gegenwart
    Article Open Access
  • Exposing spider silk to wet conditions can cause supercontraction. Here, tyrosine amino acid residues within the amorphous regions are found to contribute to supercontraction, which can be controlled by protein engineering.

    • Gabriele Greco
    • Tina Arndt
    • Anna Rising
    Article Open Access
  • Silicon-based electronic-photonic integrated circuits are promising for various applications, but their mid-infrared optical modulation is elusive. Here, tunable mid-infrared electro-absorption modulation, with broadband operation range >140 nm, is achieved in GeSn alloys on Si by controlling the Sn content.

    • Yun-Da Hsieh
    • Jun-Han Lin
    • Guo-En Chang
    Article Open Access
  • Stiction between polymerized layers and the constraining solid interface during stereolithography limits resolution. Here, a static inert liquid is used as a constraining interface to mitigate stiction, enabling high resolution parts to be fabricated with feature sizes spanning tens to thousands of microns.

    • Aftab A. Bhanvadia
    • Richard T. Farley
    • Toshikazu Nishida
    Article Open Access