Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Hazy Transparent Cellulose Nanopaper


The aim of this study is to clarify light scattering mechanism of hazy transparent cellulose nanopaper. Clear optical transparent nanopaper consists of 3–15 nm wide cellulose nanofibers, which are obtained by the full nanofibrillation of pulp fibers. At the clear transparent nanopaper with 40 μm thickness, their total transmittance are 89.3–91.5% and haze values are 4.9–11.7%. When the pulp fibers are subjected to weak nanofibrillation, hazy transparent nanopapers are obtained. The hazy transparent nanopaper consists of cellulose nanofibers and some microsized cellulose fibers. At the hazy transparent nanopaper with 40 μm thickness, their total transmittance were constant at 88.6–92.1% but their haze value were 27.3–86.7%. Cellulose nanofibers are solid cylinders, whereas the pulp fibers are hollow cylinders. The hollow shape is retained in the microsized cellulose fibers, but they are compressed flat inside the nanopaper. This compressed cavity causes light scattering by the refractive index difference between air and cellulose. As a result, the nanopaper shows a hazy transparent appearance and exhibits a high thermal durability (295–305 °C), and low thermal expansion (8.5–10.6 ppm/K) because of their high density (1.29–1.55 g/cm3) and crystallinity (73–80%).


Cellulose nanofibers isolated from plant cell walls have high mechanical strength and modulus, high thermal properties, and are lightweight1,2,3. When films are fabricated with only cellulose nanofibers without any plastics, they exhibit high mechanical properties due to their nanofiber networks and their hydrogen bonding4,5. These films are termed “nanopapers”. Nanopapers are lightweight and highly foldable, which are similar to conventional paper. However, their appearance is transparent or translucent and not opaque like conventional white paper6,7,8,9,10,11,12,13,14,15,16,17,18,19,20,21,22,23.

When transparent materials scatter incident light, their appearance becomes translucent or opaque. This light scattering is called haze. Materials with low haze are clear transparent, and ones with a high haze are hazy transparent (translucent). When 3–15-nm-wide cellulose nanofibers are densely packed, the nanopaper does not scatter light inside the sheet, and their appearance becomes clear transparent4,5. Due to their low haze and high thermal properties, clear transparent nanopapers have been developed for optoelectronic device substrates such as transparent electrodes or transistor substrates6,7,8,9,10. When 3–4-nm wide TEMPO-oxidized cellulose nanofibers were used, the nanopaper had a low haze (less than 1%) and was used as an enhanced gas barrier, which allowed selective permeation of hydrogen gas11,12.

Some nanopapers have a hazy transparent appearance, which can be applied as high-strength paper and advanced electronic substrates such as organic solar cell and foldable circuits13,14,15,16,17,18,19. Frosted glasses are hazy despite their transparent body, because their rough surface scatters incident light. However, hazy transparent nanopaper does not scatter light at their surface, because their surface is as smooth as transparent glass or plastic. Therefore, their light scattering occurs from inside the nanopaper. Previous studies proposed that the light scattering is increased by wider cellulose nanofibers20,21 or by lower density nanopapers9,22,23. However, the scattering mechanism is still unclear.

In this study, the reasons for scattered transmitting light in hazy transparent nanopaper are discussed. There are many cellulose nanofibers made using mechanically or chemically nanofibrillations. Among them, nanopaper produced from mechanically nanofibrillated cellulose nanofibers are the most promising because of their higher thermal resistance8. Moreover, this nanopaper shows various appearance as clear transparent, hazy transparent, and opaque. Thus, using mechanically nanofibrillated nanopaper, their light scattering is presented, and a fabrication method and application of hazy transparent nanopaper is developed.


Cellulose pulps

Five cellulose pulps were used: a never-dried holocellulose pulp with alkali treatment from softwood (Japanese cedar) or hardwood (eucalyptus) chips, a never-dried softwood or hardwood bleached sulfite pulp, and dried cellulose pulp (KC FLOCK W100-GK). The bleached sulfite pulps and dried cellulose pulps were gifts from Nippon Paper Group. Inc. These pulps had α-cellulose contents over 90% and Klason lignin of 0%. The procedure for the alkali treatment of holocellulose pulp is as follows8. Wood chips (50 g) were delignified by heating in an acetic anhydride/hydrogen peroxide mixture (1,000 mL: 1,000 mL) at 90 °C for 4 h. The holocellulose pulp was treated with 5 wt% potassium hydroxide at 20 °C for overnight, and then at 80 °C for 2 h. The alkali-treated holocellulose pulps had α-cellulose contents of 70–85% and Klason lignin of 0%.


All of the cellulose pulps were fibrillated using a water-jet nanofibrillation system5,8. In this system, a 0.5 wt% pulp water dispersion of 2,000 g was homogenized using a high-pressure water-jet system (Star Burst, HJP-25008, Sugino Machine Co., Ltd.) equipped with a ball-collision chamber. The dispersion was ejected from a small nozzle with a diameter of 0.17 mm under a high pressure of 245 MPa. The water dispersions were passed through this nozzle up to 100 times. After mechanical nanofibrillation, additional treatments such as centrifugation and filtering are often applied to remove unfibrillated or aggregated fibers. In this study, however, obtained dispersions were directly used for the starting materials of nanopaper without any post treatment.


The 40-μm-thick nanopapers were prepared as follows. The nanofiber dispersions (0.4 wt%, 60 g) were vacuum filtered with a glass filter (KG-90, Toyo Roshi Kaisha, Ltd.) and using a mixed cellulose ester membrane filter (A020A090C, Toyo Roshi Kaisha, Ltd. pore size: 0.2 μm). The wet nanofiber sheets were dried at 110 °C for 10 min under an applied pressure of 0.01 MPa. The thickness of nanopaper was measured by a micrometer.


The cellulose nanofiber/water dispersion was adjusted to 0.1 wt%. The dispersions do not contain any sediments after standing for 1 h. The transmittance of the dispersions were measured at a wavelength of 550 nm using a UV-visible spectrometer (U-3900, Hitachi High-Technologies Corp.) with distilled water as a reference.

Total transmittance and haze of the nanopapers were measured under a D65 light source (HZ-V3, Suga Test Instruments Co., Ltd.). X-Ray diffraction patterns were recorded using a Rigaku MiniFlex600 with Cu-Kα radiation and a scanning angle (2θ) range of 10–30°, at 40 kV voltage and 15 mA current. The crystallinity index of cellulose I was calculated from the (200) reflection (2θ = ca. 22.6°) following the procedure from previous reports24,25. The thermal durability of the nanopaper was evaluated using the 5% weight loss point. The coefficient of thermal expansion (CTE) was measured using a thermomechanical analyzer (TMA/SS7100, SII Nanotechnology Inc.). The CTE values were determined as the mean values at 20–150 °C in the second run. Thermogravimetric analysis was measured under a nitrogen atmosphere (60 mL/min) at a heating rate of 10 °C/min (TGA Q50N2, TA Instruments).

The nanofiber papers were observed using a field emission scanning electron microscopy (FE-SEM) (SU8020, Hitachi High Technologies Corp.) at the 2,000 or 30,000 times magnification. Before the FE-SEM observation, the samples were platinum coated in an ion sputter coater (Mild Sputter E-1045, Hitachi High Technologies Corp.). For the FE-SEM observation, an accelerating voltage of 1.5 kV and a working distance of 7–8 mm were used.

Results and Discussion

The cellulose nanopaper was fabricated by drying the cellulose nanofiber/water dispersions. When the water dispersion with 15-nm-wide cellulose nanofibers was dried, the cellulose nanofibers densely packed together, and air voids inside the sheets were removed4,5. As a result, the high-density cellulose nanopaper (1.48 g/cm3) became clear transparent with a small haze of 4.2% (Fig. 1 left). Because native cellulose nanofibers are hydrophilic, they do not homogeneously disperse in organic solvents such as ethanol, methanol, and acetone26. Therefore, after drying the nanofiber/organic solvent suspensions, numerous air voids remain inside the sheet. Because the air voids cause light to scatter, the nanopaper become translucent or white appearance. For example, when the cellulose nanofiber suspension with the mixture of 50% ethanol/50% water were dried, the density of cellulose was 1.15 g/cm3, and the nanopaper was translucent (haze: 49.3%) (Fig. 1 center). Increasing the ethanol to 90% decreased the density to 0.81 g/cm3, and the appearance was white translucent (haze: 90.1%) (Fig. 1 right). However, all the samples maintained high total transmittances of 90.3–90.7% because the incident light was transmitted with or without light scattering. Although the samples were fabricated with the same width of cellulose nanofibers, the density of cellulose nanopaper changed their appearance from clear transparent to hazy transparent, which has been reported in previous studies9,22,23. However, the low-density nanopapers show low mechanical properties because these characteristics are related to highly dense cellulose nanofibers. Thus, we propose a method of customizing nanopaper haze to maintain their high density.

Figure 1: Various appearances of cellulose nanopaper consisting of 15-nm-wide nanofibers.

Left: Clear transparent nanopaper with a density of 1.48 g/cm3. Center: Translucent nanopaper with a density of 1.15 g/cm3. Right: Opaque nanopaper with a density of 0.81 g/cm3.

We prepared three cellulose pulps of “low purity cellulose wet pulp from softwood or hardwood”, “high purity cellulose wet pulp from softwood or hardwood”, and “high purity cellulose dried pulp from hardwood”. Low purity cellulose wet pulps were never-dried wood fibers after removal of all the lignin and most of the hemicellulose. The pulps were suitable to provide 15–nm-wide cellulose nanofibers using mechanical nanofibrillation27,28. The transmittance of cellulose nanofiber dispersions reached 90% after 20 nanofibrillation cycles (Fig. 2 circles). After removal of all the lignin and almost all of the hemicellulose, the high purity cellulose wet pulps were never-dried and high purity cellulose dried pulps were dried. In these pulps, the cellulose nanofibers were coalesced by irreversible hydrogen bonding from hornification28. Thus, despite repeated (100 times) mechanical nanofibrillation, the dispersions transmittances were around 80% for high purity cellulose wet pulps (Fig. 2 triangle) and less than 60% for high purity cellulose dried pulps (Fig. 2 square). Nanofiber dispersions from softwood and hardwood showed the same transmittance under the same conditions of pulp purification or drying (Fig. 2 open and filled circles, open and filled triangles). Nanofiber dispersions with a wide range of transparencies were obtained from various pulp sources by repeated mechanical nanofibrillations.

Figure 2: Transparency of a 0.1 wt% cellulose nanofiber dispersion.

: Low purity cellulose wet pulp from softwood, : low purity cellulose wet pulp from hardwood, : high purity cellulose wet pulp from softwood, ▲: high purity cellulose wet pulp from hardwood, ■: high purity cellulose dried pulp from hardwood.

When these dispersions were vacuum filtered and dried, 40-μm-thick nanopapers were obtained. The haze value of nanopaper shows a liner relationship with the dispersion transparency (Fig. 3a). A large haze nanopaper was fabricated from a turbid dispersion using pulp from softwood or hardwood. As mentioned above, nanopapers from ethanol dispersions increased their hazes from 4.1% to 90.1% with decreasing densities from 1.48 to 0.81 g/cm3. However, these nanopapers show hazes that increased from 4.9% to 86.7%, while maintaining a high density of 1.29–1.55 g/cm3 (Fig. 3b). In these hazy transparent nanopaper, their density were less effective to their haze value.

Figure 3

(a) Increasing nanopaper haze decreases with transparency for 0.1 wt% cellulose nanofiber dispersions. (b) Density of nanopaper is constant against nanopaper haze. : Low purity cellulose wet pulp from softwood, : low purity cellulose wet pulp from hardwood, : high purity cellulose wet pulp from softwood, ▲: high purity cellulose wet pulp from hardwood, ■: high purity cellulose dried pulp from hardwood.

Nanopaper haze was previously reported to increase from 20% to 49% when the nanofiber width was increased from 10 to 50 nm, because of the light scattering at the cross-section of cellulose nanofibers20. Therefore, cellulose nanofibers in 86.6%, 38.3% and 5.5% haze nanopapers were observed using FE-SEM at the 30,000 times magnification. However, no nanofibers wider than 50 nm were observed in the hazy transparent nanopaper, and uniform width nanofibers around 15 nm were present in all the nanopapers (Fig. 4a–c). Starting pulp fibers are microsized hollow cylindrical shapes, which are composed of 15–nm-wide cellulose nanofibers. Therefore, when any cellulosic fiber materials were observed at high magnifications, the FE-SEM images show only homogeneous wide cellulose nanofibers around 15 nm. In our previous studies, we propose that light scattering inside the nanopaper was caused by the difference of refractive index between cellulose nanofiber and the air cavities4,5. The cavity size and their number in these nanopapers were carefully observed, and they were the same size (around 50 nm) and distribution in the hazy and clear transparent nanopapers (Fig. 4a–c). Thus, the nano-order observations did not present any evidence of increasing light scattering in hazy transparent nanopapers.

Figure 4: FE-SEM images of cellulose nanopaper of various hazes.

(a,d) 86.6% Haze nanopaper from high purity cellulose dried pulp from hardwood, (b,e) 38.3% haze nanopaper from high purity cellulose wet pulp from softwood, and (c,f) 5.5% haze nanopaper from low purity cellulose wet pulp from softwood.

Uetani et al. reported that pulp fibers were broken into microsized fragments, and the 15-nm-wide nanofibers peeled away from the fragments during mechanical nanofibrillation29. To observe microsized fragments in the nanopaper, lower magnifications of 2,000 times were used (Fig. 4d–f). In the clear transparent nanopaper, fragments were not observed from the top, and densely laminated layers were observed from the side (Figs 4f and 5b). In the hazy transparent nanopaper, microsized fragments were observed, and they increased with increasing nanopaper haze (Fig. 4d,e). From the cross-sectional observations, the microsized fibers were compressed, and the cylindrical hollow shape became flat (Fig. 5a). These results show that hazy transparent nanopaper causes light scattering inside the film, and they can maintain their high density as follows. Hazy transparent nanopapers consist of mainly cellulose nanofibers and some microsized cellulose fibers. The microsized fibers were hollow cylinders, but they are compressed and flattened in the nanopaper. The flattened cavities cause light scattering inside the nanopaper, without decreasing the paper density. As a result, the nanopaper is hazy transparent and of a high density.

Figure 5: Cross-sectional FE-SEM images of cellulose nanopaper.

(a) A microsized pulp fiber showing compressed hollow cylinder in the hazy transparent nanopaper (Haze 86.6%), (b) Densely laminated layers in the clear transparent nanopaper (haze 5.5%).

The hazy transparent nanopaper shows another advantage of short fabrication time. Nanopapers were fabricated by vacuum filtering the nanofiber/water dispersion, and the wet sheet was hot-pressed for 10 min. Clear transparent nanopaper was fabricated using the dispersion containing 15-nm-wide cellulose nanofibers. The nanofiber dispersion was a low concentration (0.4 wt%), but of a high viscosity. Thus, the filtration step required over 30 min (Fig. 6a). However, the starting dispersion of hazy transparent nanopaper was not highly viscous because the mixture contained microsized fibers and 15-nm-wide nanofibers. Therefore, their filtering time decreased by one-third to 10 min (Fig. 6a). The hazy transparent nanopaper shows a high density at 1.29–1.55 g/cm3 (Fig. 3b) and high crystallinity at 73–80% (Fig. 6b). The CTE was low at 8.5–10.6 ppm/K (Fig. 6c), and the thermal stability was high at 295–305 °C (Fig. 6d), which were similar to the clear transparent nanopaper.

Figure 6

Hazy transparent nanopaper decreases filtration time with increasing haze (a), maintains a high crystallinity (b), shows low CTEs (c), and exhibits a high heat resistance under nitrogen (d). : Low purity cellulose wet pulp from softwood, : low purity cellulose wet pulp from hardwood, : high purity cellulose wet pulp from softwood, ▲: high purity cellulose wet pulp from hardwood, ■: high purity cellulose dried pulp from hardwood.

A new application of hazy transparent nanopaper is presented. The hazy transparent nanopaper shows a short fabrication time, high thermal resistance, and low CTE. Furthermore, the hazy transparent nanopaper transmits around 90% incident light (Fig. 7a). These characteristics are a good match for optical diffusors in light emitting diode (LED) lighting. When LEDs were covered with the hazy transparent nanopapers, the nanopaper homogeneously spread the dazzling LED light without losing high light intensity (Fig. 7b). LED lighting has become widespread rapidly, because they have advantages over incandescent light sources including lower energy consumption, longer lifetime, and smaller size. In the near future, ecofriendly lighting with low energy consumptions will be realized using LEDs and hazy cellulose nanopaper.

Figure 7

Total light transmittance and haze value of nanopaper (a), and the application of hazy transparent nanopaper as optical diffusers (b). Far left: an LED light without diffuser, from second-to-left to right: increasing nanopaper haze, which homogeneously spreads the light through the nanopaper and maintains light intensity.


There are two transparent nanopapers, one is clear transparent with low light scattering, and the second is hazy transparent with higher light scattering. Hazy transparent nanopaper is produced by reducing of the density of fibers. In this study, a hazy transparent nanopaper with a high density is fabricated using various wood pulps from softwood or hardwood in a dry or wet state. When 15–50-μm-wide cellulose pulp fibers were mechanical nanofibrillated, most fibers became 4–15 nm wide, but some fibers became microsized fragments. These microsized fragments show a hollow cylindrical shape that becomes flat in the nanopaper. The nanopaper shows high density, low CTE, and high thermal durability similar to that of the clear transparent nanopaper. The haze value of nanopaper increases with the number of microsized fragments because the compressed hollow cylinders cause light scattering inside the nanopaper. The hazy transparent nanopaper scatters the incident light without losing light intensity. Therefore, the hazy transparent nanopaper is a promising candidate for optical diffusors in LED lighting.

Additional Information

How to cite this article: Hsieh, M.-C. et al. Hazy Transparent Cellulose Nanopaper. Sci. Rep. 7, 41590; doi: 10.1038/srep41590 (2017).

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1

    Yano, H. et al. Optically Transparent Composites Reinforced with Networks of Bacterial Nanofibers. Adv. Mater. 17, 153–155 (2005).

    CAS  Article  Google Scholar 

  2. 2

    Saito, T., Kuramae, R., Wohlert, J., Berglund, L. A. & Isogai, A. An ultrastrong nanofibrillar biomaterial: the strength of single cellulose nanofibrils revealed via sonication-induced fragmentation. Biomacromolecules 14, 248–253 (2013).

    CAS  Article  PubMed  Google Scholar 

  3. 3

    Diaz, J. A. et al. Thermal Conductivity in Nanostructured Films: From Single Cellulose Nanocrystals to Bulk Films. Biomacromolecules 15, 4096–4101 (2014).

    CAS  Article  PubMed  Google Scholar 

  4. 4

    Nogi, M., Iwamoto, S., Nakagaito, A. N. & Yano, H. Optically Transparent Nanofiber Paper. Adv. Mater. 21, 1595–1598 (2009).

    CAS  Article  Google Scholar 

  5. 5

    Nogi, M. et al. High thermal stability of optical transparency in cellulose nanofiber paper. Appl. Phys. Lett. 102, 181911 (2013).

    ADS  Article  Google Scholar 

  6. 6

    Fujisaki, Y. et al. Transparent Nanopaper-Based Flexible Organic Thin-Film Transistor Array. Adv. Funct. Mater. 24, 1657–1663 (2014).

    CAS  Article  Google Scholar 

  7. 7

    Koga, H. et al. Uniformly Connected Conductive Networks on Cellulose Nanofiber Paper for Transparent Paper Electronics. NPG Asia Mater. 6, e93 (2014).

    CAS  Article  Google Scholar 

  8. 8

    Yagyu, H., Saito, T., Isogai, A., Koga, H. & Nogi, M. Chemical Modification of Cellulose Nanofibers for the Production of Highly Thermal Resistant and Optically Transparent Nanopaper for Paper Devices. ACS Appl. Mater. Interfaces 7, 22012–22017 (2015).

    CAS  Article  PubMed  Google Scholar 

  9. 9

    Toivonen, M. S., Kaskela, A., Rojas, O. J., Kauppinen, E. I. & Ikkala, O. Ambient-Dried Cellulose Nanofibril Aerogel Membranes with High Tensile Strength and Their Use for Aerosol Collection and Templates for Transparent, Flexible Devices. Adv. Func. Mater. 25, 6618–6626 (2015).

    CAS  Article  Google Scholar 

  10. 10

    Nogi, M., Karakawa. M., Komoda, N., Yagyu, H. & Nge, T. T. Transparent Conductive Nanofiber Paper for Foldable Solar Cells. Scientific Reports 5, 17254 (2015).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  11. 11

    Fukuzumi, H., Saito, T., Iwata, T., Kumamoto, Y. & Isogai, A. Transparent and High Gas Barrier Films of Cellulose Nanofibers Prepared by TEMPO-Mediated Oxidation. Biomacromolecules 10, 162–165 (2009).

    CAS  Article  PubMed  Google Scholar 

  12. 12

    Fukuzumi, H., Fujisawa, S., Saito, T. & Isogai, A. Selective Permeation of Hydrogen Gas Using Cellulose Nanofibril Film. Biomacromolecules 14, 1705–1709 (2013).

    CAS  Article  PubMed  Google Scholar 

  13. 13

    Aulin, C., Gallstedt, M. & Lindstrom, T. Oxygen and oil barrier properties of microfibrillated cellulose films and coatings. Cellulose 17, 559–574 (2010).

    CAS  Article  Google Scholar 

  14. 14

    Hsieh, M.-C., Kim, C., Nogi, M. & Suganuma, K. Electrically Conductive Lines on Cellulose Nanopaper for Flexible Electrical Devices. Nanoscale 5, 9289–9295 (2013).

    ADS  CAS  Article  PubMed  Google Scholar 

  15. 15

    Zhu, H., Fang, Z., Preston, C., Lia, Y. & Hu, L. Transparent paper: fabrications, properties, and device applications. Energy Environ. Sci. 7, 269–287 (2014).

    CAS  Article  Google Scholar 

  16. 16

    Fang, Z., Zhu, H., Preston, C. & Hu, L. Development, application and commercialization of transparent paper. Translational Materials Research 1, 015004 (2014).

    Article  Google Scholar 

  17. 17

    Inui, T., Koga, H., Nogi, M., Komoda, N. & Suganuma, K. A Miniaturized Flexible Antenna Printed on a High Dielectric Constant Nanopaper Composite. Adv. Mater. 27, 1112–1116 (2015).

    CAS  Article  PubMed  Google Scholar 

  18. 18

    Yei Hwan Jung et al. High-performance green flexible electronics based on biodegradable cellulose nanofibril paper. Nature Communications 6, 7170 (2015).

    Article  Google Scholar 

  19. 19

    Kang, W., Yan, C., Foo, C. Y. & Lee, P. S. Foldable Electrochromics Enabled by Nanopaper Transfer Method. Adv. Funct. Mater. 25, 4203–4210 (2015).

    CAS  Article  Google Scholar 

  20. 20

    Zhu, H. et al. Transparent nanopaper with tailored optical properties. Nanoscale 5, 3787–3792 (2013).

    ADS  CAS  Article  PubMed  Google Scholar 

  21. 21

    Qing, Y., Sabo, R., Wu, Y., Zhu, J. Y. & Cai, Z. Self-assembled optically transparent cellulose nanofibril films: effect of nanofibril morphology and drying procedure. Cellulose 22, 1091–1102 (2015).

    CAS  Article  Google Scholar 

  22. 22

    Kobayashi, Y., Saito, T. & Isogai, A. Aerogels with 3D ordered nanofiber skeletons of liquid-crystalline nanocellulose derivatives as tough and transparent insulators. Angew. Chem. Int. Ed. 53, 10394–10397 (2014)

    CAS  Article  Google Scholar 

  23. 23

    Nemoto, J., Saito, T. & Isogai, A. Simple Freeze-Drying Procedure for Producing Nanocellulose Aerogel-Containing, High-Performance Air Filters. ACS Appl. Mater. Interfaces 7, 19809–19815 (2015).

    CAS  Article  PubMed  Google Scholar 

  24. 24

    Alexander, L. E. In X-Ray Diffraction Methods in Polymer Science Krieger, New York, pp. 423–424. (1979).

  25. 25

    Segal, L., Creely, J. J., Martin, A. E. & Conrad, C. M. Text. Res. J. 29, 786–794 (1959).

    CAS  Article  Google Scholar 

  26. 26

    Nogi, M., Kurosaki, F., Yano, H. & Takano, M. Preparation of nanofibrillar carbon from chitin nanofibers. Carbohydrate Polymers 81, 919–924 (2010).

    CAS  Article  Google Scholar 

  27. 27

    Abe, K., Iwamoto, S. & Yano H. Obtaining cellulose nanofibers with a uniform width of 15 nm from wood. Biomacromolecules 8, 3276–3278 (2007).

    CAS  Article  PubMed  Google Scholar 

  28. 28

    Iwamoto, S., Yano, H. & Abe, K. The Effect of Hemicelluloses on Wood Pulp Nanofibrillation and Nanofiber Network Characteristics. Biomacromolecules, 9, 1022–1026 (2008).

    CAS  Article  PubMed  Google Scholar 

  29. 29

    Uetani, K. & Yano, H. Nanofibrillation of Wood Pulp Using a High-Speed Blender. Biomacromolecules, 12, 348–353 (2011).

    CAS  Article  PubMed  Google Scholar 

Download references


M.N. was supported by the Grants-in-Aid for Scientific Research (Grant No. 26220908) from the Japan Society for the Promotion of Science (JSPS).

Author information




M.H. carried out the experiments and prepared the manuscript. H.K. and K.S. provided advice and expertise. M.N. designed this work and prepared the manuscript. All authors discussed the results and implications and commented on the manuscript at all stages.

Corresponding author

Correspondence to Masaya Nogi.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Hsieh, MC., Koga, H., Suganuma, K. et al. Hazy Transparent Cellulose Nanopaper. Sci Rep 7, 41590 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing