Abstract
A ferromagnetic (FM)-metal/oxide stack is the key structure determining the performance of spintronic devices. However, the effect of the electronic polarity of the oxide on the magnetic properties of the adjacent FM-metal has not been investigated previously. Here, we report the magnetic and structural properties of Co ultra-thin films sputter deposited directly on the Zn- and O-polar surfaces of ZnO substrates. The magnetic anisotropy and Curie temperature exhibit dramatic polarity-dependent differences for films on these surfaces. Structural analyses reveal that the heterointerface of the Co/O-polar surface is rather diffusive, whereas that of the Co/Zn-polar surface is atomically flat. These results suggest that the surface polarity plays a key role in determining the properties of the film. This novel FM-metal/polar-oxide system is expected to add new functionality to spintronic devices and provide an ideal basis for investigating the effect of a built-in electric field on the magnetism in a metallic monolayer.
Similar content being viewed by others
Introduction
The combination of a ferromagnetic (FM) thin metal with a non-magnetic (NM) oxide layer has played a central role in the recent development of spintronic devices. For example, a single-crystal MgO layer interfaced with a 3d-FM metal results in giant tunnel magnetoresistance1,2 and perpendicular magnetic anisotropy (PMA) in the FM metal layer3. The ferromagnet/oxide heterostructure is also crucial for studies of the effects of an electric field on magnetism4,5,6,7,8,9,10 and novel phenomena or the magnetic structure in systems with structure inversion asymmetry11,12,13,14,15. Although the spin-filtering effect in tunnel junctions with an oxide multiferroic barrier has been reported16, the magnetism of a FM metal deposited directly on a polar oxide with a normal dielectric property has not been intensively explored. Thus, this system may present an exciting opportunity to add further magnetic functionality or controllability to FM metals.
To date, the polarity of a material has been positively used in oxide-oxide combinations. The polar discontinuity at perovskite interfaces can be a source of nontrivial local atomic and electronic structure17,18,19. In addition to perovskite interfaces, ZnO/MgZnO polar interfaces yield high-mobility two-dimensional electron gas without impurity doping or the application of external electric fields20,21. Here, we focus on the combination of a FM metal and a ZnO substrate with Zn- and O-polar surfaces (Fig. 1a) at its front and back sides, respectively, because of the broken inversion symmetry in the wurtzite crystal structure along the [0001] direction22. The surface termination of ZnO substrates also depends on the (0001) or (000) surface plane corresponding to the Zn-polar and O-polar faces, respectively23. When a FM metal is deposited directly on its surfaces, a built-in electric field should be introduced at the interface FM atoms, whose directions depend on the polar surface termination, as schematically shown in Fig. 1b. In this system, the built-in electric field effect on the magnetic properties (e.g., polarity-dependent magnetic anisotropy7,24, Curie temperature TC8,25, or Rashba spin-orbit-related phenomena11,13) is expected. In addition to its fundamental significance, exploring and developing such a system would provide new insights into material design in future spintronic devices. In this study, we investigate the magnetic and structural properties of FM Co thin films deposited directly on different ZnO polar surfaces. Dramatically different magnetic properties were observed for ZnO surfaces with different polarities.
Sets of samples with three different nominal Co layer thicknesses (tCo = 0.40, 0.48, and 0.60 nm) were deposited on Zn- and O-polar surfaces (see Methods). For the structural analyses, a sample with a thickness tCo of 3.6 nm was also prepared. All samples were capped by a 2.4-nm-thick Pt layer. The magnetic moment m for each sample was measured using a superconducting quantum interference device (SQUID) magnetometer (Magnetic Property Measurement System, Quantum Design inc.). The anomalous Hall effect, where the Hall resistance RHall is proportional to the perpendicular component of the magnetization, was also used to determine the magnetic properties of each sample (see Methods). The surface and structural characteristics of the samples were determined by x-ray diffraction (XRD) (Empyrean, PANalytical), atomic force microscopy (AFM) (AFM5000, Hitachi High-Technologies Cooporation), and scanning transmission electron microscopy (STEM). The possibility of intermixing between the layers and the substrate was examined by STEM-energy-dispersive x-ray spectroscopy (STEM-EDS). The scanning transmission electron microscope used in this study was aberration-corrected JEM-ARM200F (200 keV) equipped with Centurio SDD EDS detector (JEOL Co. Ltd.).
The magnetic properties differed dramatically depending on the polarity of the ZnO surface. Figure 2a and b show the m/S-μ0H curves for Zn- and O- polar samples, respectively, with tCo = 0.4 nm, where μ0H and S are an external magnetic field and the area of the sample piece, respectively. Both the in-plane and perpendicular directions of m were measured to determine the magnetic easy axis of the sample. The magnetic anisotropy differs clearly between the samples types; i.e., the Zn-polar sample has an in-plane magnetic easy axis, whereas the O-polar sample clearly shows PMA. The dependence of the saturation m per area (ms/S) on tCo at 10 K for the three samples with tCo = 0.4–0.6 nm is plotted in Fig. 2c. The ms/S of both types of samples increases linearly with increasing tCo. The dashed-line in Fig. 2c is the linear fit to the data. The intercept of the linear fit was found to be non-zero, indicating an induced magnetic moment in the Pt cap layer attributed to the FM proximity effect26.
In addition to magnetic anisotropy, TC also differed between the two types of samples. Figure 2d and e show the temperature dependence of the remanent magnetic moment mr for both types of samples. A sharp transition from the FM state to the paramagnetic state is observed in the mr-T curves measured along the easy axis. No spin-reorientation transition (switching of the easy axis) is observed in either sample at any temperature. Figure 2f summarizes the TC for Zn- and O-polar samples, where TC is defined as the temperature at which mr became zero along the easy axis. Based on this result, the TC of the Zn-polar sample is higher (by approximately 60 K) than that of the O-polar sample. Notably, the two-dimensionality effect explains the increase of TC with tCo, and its value is much lower than that in bulk-Co (~1400 K)27.
The value of RHall was measured to determine the magnetic anisotropy energy of the samples. Figure 3a shows the normalized RHall (RHalln)-μ0H⊥ curve for three O-polar samples with tCo = 0.4–0.6 nm at 10 K, where H⊥ is the magnetic field applied perpendicular to the film plane. The coercivity decreases with increasing tCo, suggesting that the PMA energy decreases with increasing tCo. The inset shows the RHalln curve for the sample with tCo = 0.6 nm obtained as the magnetic field increased along the hard-axis (in-plane) direction (H||). RHalln decreased with μ0H||, showing that the magnetization of the sample tilts from being perpendicular to the plane to the in-plane direction. Based on the RHalln-μ0H|| curve, the normalized magnetization along the hard axis (Mhardn) is obtained using the following relationship: Mhardn = sin[arccos(RHalln)](refs 28, 29, 30). The results at 10 K for the three samples are shown in Fig. 3b. The saturation field of Mhardn decreases with increasing tCo, in agreement with the coercivity variation with respect to tCo. The data shown in Fig. 3c of Mhardn for Zn-polar samples at 10 K presents the same trend for the saturation field. Here, Mhardn is the same as RHalln because the perpendicular direction is the hard axis for the Zn-polar samples.
The magnetic anisotropy energy per unit area E⊥tCo, where E⊥ is the effective perpendicular anisotropy energy density, is determined from the hard axis magnetization curves using the following equation (see for example ref. 28):
The values of E⊥tCo as a function of tCo for the Zn- and O-polar samples at 10 K are plotted in Fig. 3d, showing that the E⊥tCo is linearly proportional to tCo. E⊥tCo of the present system can be expressed as follows (see for example ref. 7).
where Ms and Kc are the saturation magnetization and the uniaxial crystalline anisotropy energy constant, respectively. ksZnO/Co and ksCo/Pt are the surface magnetic anisotropies attributed to the ZnO/Co and Co/Pt interfaces, respectively; their sum can be obtained from the intercept of the linear fitting in Fig. 3d. The slope of the linear fitting gives the sum of the demagnetization energy [(−1/2)μ0Ms2] and Kc. Based on these results, ksZnO/Co + ksCo/Pt = 1.1 mJ/m2 and (−1/2)μ0Ms2 + Kc = −1.2 MJ/m3 are obtained in the O-polar sample. The surface and crystalline anisotropies are approximately two or more times larger than the previously reported values determined in a Co/Pt system at room temperature31,32. However, the signs of the energy sums in the Zn-polar sample are opposite (−1.2 mJ/m2 and 0.48 MJ/m3, respectively). This result indicates that if ksCo/Pt is positive (as in the general case), then ksurf.ZnO/Co will be negative in the Zn-polar sample. In addition, Kc (Zn-polar) > (1/2)μ0Ms2 > Kc (O-polar).
Importantly, the Co thin films deposited on the same material (ZnO) but with different polarization show completely different magnetic properties. To understand this phenomenon, the structural properties were investigated. Figure 4a shows the XRD profiles for Zn- and O-polar samples with tCo = 3.6 and 0.6 nm obtained by the θ-2θ method using Cu-Kα1 radiation (wavelength: 0.15406 nm). The vertical dashed and dotted lines indicate the expected positions of the diffraction peak for the (111) plane of fcc Pt and Co crystals, respectively. Notably, the peak expected from Co with hcp (0002) structure resides at almost the same position as that of fcc(111). The Zn-polar sample with thicker tCo (=3.6 nm) has clear peaks from the Pt and Co layers close to the expected positions. In addition, the thickness fringe is observed at the lower 2θ range (<10o), suggesting that sharp interfaces are formed. In contrast, no thickness fringe and no clear peaks other than the peak from the ZnO substrate are observed in the O-polar sample with tCo = 3.6 nm. In samples with smaller tCo values (=0.6 nm), the clear peak expected from Pt(111) and the thickness fringe are observed in both types of samples. A peak near the position expected from Co(111) is observed only in the Zn-polar sample, suggesting that the intermixing between Co and Pt is minor in this sample.
The AFM images for both samples are shown in Fig. 4b. In the Zn-polar sample with thicker tCo (=3.6 nm), a flat surface with an average roughness height (Ra) of 0.10 nm is observed. The O-polar sample shows a rough surface with Ra = 0.20 nm, in agreement with the XRD result. The Ra obtained in samples with thinner tCo (=0.4 nm) is lower than one-monolayer (ML)-thick Co, showing that the sample surfaces are atomically flat. In the Zn-polar sample, an atomic step and terrace remain, even after the deposition of the Co/Pt layers.
The STEM images of the Zn- and O- polar samples with tCo = 3.6 and 0.6 nm are summarized in Fig. 5. Samples with thicker tCo (=3.6 nm) are discussed first (Fig. 5a and b). The Co and Pt layers on the Zn-polar surface have abrupt interfaces and much higher crystallinity than those on the O-polar sample, as expected from the XRD profiles. Figure 6a shows the magnified STEM image for the Zn-polar sample. The averaged results of the two-dimensional fast Fourier transformation (2D FFT) for the square areas indicated by the coloured squares in Fig. 6a are shown in Fig. 6b–d. Judging from the experimental (Fig. 6b–d) and simulated 2D FFT (Fig. 6e and f), the Pt layer (blue square) and the Co layer near the Co/Pt interface (light-green square) have a fcc(111) structure. Alternatively, a hcp(0001) texture appears to be dominant in the Co layer near the ZnO/Co interface (pink square) excluding the first ML just above the Zn-polar surface (we call the corresponding atomic layer “interface Co”). The interface Co atoms shows no dislocations in the observed length scale (over ~16 nm). Moreover, the number of atoms in the interface Co is exactly the same as that of the surface Zn atoms, indicating that the lateral atomic distances (LADs) of the Co and Zn atoms are almost equal (~0.32 nm). Therefore, in the Zn-polar sample, the LAD of the interface Co is approximately 30% larger than the bulk value. As shown in Fig. 7b, the in-plane LAD of each atomic layer was calculated by performing the FFT for each lateral pixel of the corresponding STEM image (Fig. 7a). The result evidences the fact that the LADs of the interface Co and Zn atoms are the same. From Fig. 7b and c(averaged intensity of the lateral pixels of STEM image in Fig. 7a), the lattice relaxation in the Co layer occurs in the first 2–3 MLs. The reasons that we can decide the ZnO/Co interface from the STEM image are the follows: (i) A clear dark region (gap) is observed just below the corresponding atomic layer in the STEM image (Fig. 7c). (ii) The atomic images below the “interface Co” has an ellipse-like shape, suggesting the existence of tilted Zn-O bonding, whereas the those of the “interface Co” atoms shows a spherical shape. Figure. 7d and e depict the schematic image of the position of the Co atoms on the Zn-polar surface expected based on the STEM image. The Co atom prefers the H3 site over the T4 or on-top of the Zn atoms. This observation is partially consistent with the result of an ab initio calculation33, in which the Co atom adsorbed on a Zn-polar surface avoids the on-top position.
The Co layer on the O-polar surface (Fig. 5b) shows an amorphous or poly-crystalline texture with rough interfaces with both the ZnO surface and the Pt layer. In both samples with thinner tCo (=0.6 nm) (Fig. 5c and d), a clear fcc(111) texture is observed in the Pt layer. The darker region on the ZnO surface likely indicates Co atoms. The Pt/Co interface is not sharp, even in the Zn-polar sample, probably because the Co on the surface exhibited a non-perfect fcc structure at this thickness, as mentioned above.
The ZnO/Co interface in the O-polar samples (Fig. 5b and d) does not appear to be sharper than that in the Zn-polar samples (Fig. 5a and c). This phenomenon may be attributed to the mutual diffusion of Co and ZnO. To determine the atom distribution, STEM-EDS was performed. Figure 8a and b show the results of the STEM-EDS mapping of each element in the Zn- and O-polar samples with tCo = 3.6 nm, respectively. The graphs on the right show the averaged line profiles along the deposition direction for each detected element in atomic %. In addition, a sharp ZnO/Co interface is observed in the Zn-polar sample. In the O-polar sample, clear intermixing between Co and O atoms occurs, particularly in the vicinity of the ZnO/Co interface. One possibility is that the mutual diffusion of Co and O facilitates the formation of Co-O bonds34 or decreases the surface-formation energy of the absorbed Co on the O-terminated surface35. The much weaker tolerance of the O-polar surface for chemical etching36 may be related to this phenomenon. Notably, the thermal stability of the Pd/Zn polar interface was experimentally confirmed using the polar interfaces of ZnO precipitates distributed in a single-crystal Pd matrix37,38. Nevertheless, further studies, including investigations of the nontrivial effects attributed to the polarity of the ZnO surface, such as polar discontinuity18, may be required to clarify the structural difference.
Finally, we comprehensively discuss the differences in the observed magnetic properties. The interface magnetic anisotropy is expected to decrease when the interface is not sharp. The present O-polar sample shows a rough Co/Pt interface but relatively strong PMA, suggesting that the existence of the Co-O bonding exerts an influence39. However, the Zn-polar sample shows a very sharp Zn/Co interface and clear in-plane interface anisotropy, indicating that the Zn/Co interface plays an important role in the magnetic anisotropy in this system. The negative ksurf.ZnO/Co may be explained by the different electronic structure of the ML-Co on the Zn-polar surface33,35 and the anomalously larger atomic distance observed at the first ML-Co compared with the bulk (and/or its relaxation in the above layer). The TC variation may be related to the difference in the degrees of intermixing between Co and Pt40 and between Co and O. The anisotropy difference may also affect the value of TC in the present two-dimensional FM film41. The electrical charge-accumulation effect induced by the built-in electric field may also explain the observed differences. The electron density of Co is expected to increase (decrease) at the Zn-(O-)polar surface (Fig. 1b) because of the polarization effect21,42. Thus, from the perspective of charge accumulation, we note that the directions of the changes in magnetic anisotropy and TC are consistent with our previous results obtained in the Pt/Co system under an applied external electric field8,25,28,30.
In summary, we found that the polarity of the surface of a NM polar oxide strongly affects the magnetic properties of a metallic thin film deposited on it. Merely depositing FM Co on either the front or back side (the Zn- or O-polar surface) of a ZnO substrate by sputtering under identical growth conditions completely changed the magnetic properties (the magnetic anisotropy and Curie temperature) of the Co film. The differences in crystallinity and/or electronic structure in the MLs of Co on the polar surfaces are expected to be relevant to the magnetic properties of the system. In particular, the Co on the Zn-polar surface shows high crystallinity and sharp interfaces. The structure considered here is expected to emerge as an ideal test platform for advanced spintronics research studies, e.g., the development of novel magnetic structures in which the Dzyaloshinskii–Moriya interaction is significant because of the lack of structural inversion symmetry12,14,15 or the Rashba spin-orbit-related phenomena11,13 originating from the built-in electric field at the Co atomic layer. Moreover, the results observed here constitute valuable information because the interface of a FM thin metal with an oxide has played and will probably continue to play a central role in the development of spintronic devices.
Methods
Sample preparation
The base pressure of the sputtering chamber used here (ES-280, EIKO Engineering Co. Ltd.) is the order of 10−7 Pa. RF-sputtering with Ar gas (0.7 Pa) was performed to deposit the Co and Pt cap layers on the ZnO substrates (Tokyo Denpa Co., Ltd.). The RF powers for the Co and Pt depositions were 60 W and 40 W, respectively. One ZnO substrate (1.5 × 1.5 cm2) was cut into two pieces. The metal layers were simultaneously deposited onto the front side of one piece and the back side of another (Zn- and O-polar samples) to ensure that the deposition conditions of each sample were the same. The nominal thickness was determined from the deposition rate of each layer.
Hall effect measurement
The Hall measurement was performed using a Physical Property Measurement System (Quantum Design, inc.). To measure RHall, a 30-μm-wide Hall bar structure was fabricated via photolithography and Ar-ion milling. In the RHall curves shown in Fig. 3a, an odd-function component was extracted from the raw data, and then, the ordinary Hall resistance was removed from the extracted component.
Additional Information
How to cite this article: Chiba, D. et al. Co thin films deposited directly on ZnO polar surfaces. Sci. Rep. 6, 38005; doi: 10.1038/srep38005 (2016).
References
Parkin, S. S. P. et al. Giant tunnelling magnetoresistance at room temperature with MgO (100) tunnel barriers. Nature Mater. 3, 862–867 (2004).
Yuasa, S., Nagahama, T., Fukushima, A., Suzuki, Y. & Ando, K. Giant room-temperature magnetoresistance in single-crystal Fe/MgO/Fe magnetic tunnel junctions. Nature Mater. 3, 868–871 (2004).
Ikeda, S. et al. A perpendicular-anisotropy CoFeB–MgO magnetic tunnel junction. Nature Mater. 9, 721–724 (2010).
Ohno, H. et al. Electric-field control of ferromagnetism. Nature 408, 944–946 (2000).
Chiba, D., Yamanouchi, M., Matsukura, F. & Ohno, H. Electrical manipulation of magnetization reversal in a ferromagnetic semiconductor. Science 301, 943–945 (2003).
Chiba, D. et al. Magnetization vector manipulation by electric fields. Nature 455, 515–518 (2008).
Maruyama, T. et al. Large voltage-induced magnetic anisotropy change in a few atomic layers of iron. Nature Nanotech. 4, 158–161 (2009).
Chiba, D. et al. Electrical control of the ferromagnetic phase transition in cobalt at room temperature. Nature Mater. 10, 853–856 (2011).
Shiota, Y. et al. Y. Induction of coherent magnetization switching in a few atomic layers of FeCo using voltage pulses. Nature Mater. 11, 39–43 (2012).
Matsukura, F., Tokura, Y. & Ohno, H. Control of magnetism by electric fields. Nature Nanotechnol. 10, 209–220 (2015).
Mihai Miron, I. et al. Current-driven spin torque induced by the Rashba effect in a ferromagnetic metal layer. Nature Mater. 9, 230–234 (2010).
Emori, S. et al. Current-driven dynamics of chiral ferromagnetic domain walls. Nature Mater. 12, 611–616 (2013).
Barnes, S. E., Ieda, J. & Maekawa, S. Rashba Spin-Orbit Anisotropy and the Electric Field Control of Magnetism. Scientific. Rep. 4, 4105 (2014).
Boulle, O. et al. Room-temperature chiral magnetic skyrmions in ultrathin magnetic nanostructures. Nature Nanotechnol. 11, 449–454 (2016).
Woo, S. et al. Observation of room-temperature magnetic skyrmions and their current-driven dynamics in ultrathin metallic ferromagnets. Nature Mater. 15, 501–506 (2016).
Gajek, M. et al. Tunnel junctions with multiferroic barriers. Nature Mater. 6, 296–302 (2007).
Ohtomo, A. & Hwang, H. Y. A high-mobility electron gas at the LaAlO3/SrTiO3 heterointerface. Nature 427, 423–426 (2004).
Nakagawa, N., Hwang, H. Y. & Muller, D. A. Why some interfaces cannot be sharp. Nature Mater. 5, 204–209 (2006).
Brinkman., A. et al. Magnetic effects at the interface between non-magnetic oxides. Nature Mater. 6, 493–496 (2007).
Tsukazaki, A. et al. Quantum Hall-effect in polar oxide heterostructures. Science 315, 1388–1391 (2007).
Kozuka, Y., Tsukazaki, A. & Kawasaki, M. Challenges and opportunities of ZnO-related single crystalline heterostructures. Appl. Phys. Rev. 1, 011303 (2014).
Goniakowski, J., Finocchi, F. & Noguera, C. Polarity of oxide surfaces and nanostructures. Rep. Prog. Phys. 71, 016501 (2008)
Kato, H., Sano, M., Miyamoto, K. & Yao, T. High-quality ZnO epilayers grown on Zn-face ZnO substrates by plasma-assisted molecular beam epitaxy. J. Cryst. Growth 265, 375–381 (2004).
Weisheit, M. et al. Electric field-induced modification of magnetism in thin-film ferromagnets. Science 315, 349–351 (2007).
Shimamura, K. et al. Electrical control of Curie temperature in cobalt using an ionic liquid film. Appl. Phys. Lett. 100, 122402 (2012).
Suzuki, M. et al. Depth profile of spin and orbital magnetic moments in a subnanometer Pt film on Co. Phys. Rev. B 72, 054430 (2005).
Schneider, C. M. et al. Curie temperature of ultrathin films of fcc-cobalt epitaxially grown on atomically flat Cu(100) surfaces. Phys. Rev. Lett. 64, 1059–1062 (1990).
Yamada, K. et al. Electric Field Modulation of Magnetic Anisotropy in MgO/Co/Pt Structure. Appl. Phys. Express 6, 073004 (2013).
Hibino, Y. et al. Electric-field modulation of magnetic anisotropy in perpendicularly magnetized Pt/Co structure with a Pd top layer. Appl. Phys. Express 8, 113002 (2015).
Hirai, T. et al. Control of magnetic anisotropy in Pt/Co system using ionic liquid gating. Appl. Phys. Express 9, 063007 (2016).
Carcia, P. F. Perpendicular magnetic anisotropy in Pd/Co and Pt/Co thin-film layered structures. J. Appl. Phys. 63, 5066–5073 (1988).
Zeper, W. B., Greidanus, F. J. A. M., Carcia, P. F. & Fincher, C. R. Perpendicular magnetic anisotropy and magneto-optical Kerr effect of vapor-deposited Co/Pt-layered structures. J. Appl. Phys. 65, 4971–4975 (1989).
Kim, Y.-S., Lee, S.-H., IM, J.-I. & Chung, Y.-C. Magnetic Properties and Electronic Structure of Transition Metal Adsorbed Polar-ZnO Surfaces: Ab initio Calculations. Jpn. J. Appl. Phys. 46, 6312–6314 (2007).
Hyma, M. P., Martono, E. & Vohs, J. M. Studies of the Structure and Interfacial Chemistry of Co Layers on ZnO(0001). J. Phys. Chem. C 114, 16892–16899 (2010).
Chen, X., Huang, D., Deng, W.-J. & Zhao, Y.-J. Structural stability and magnetic properties of Co-doped or adsorbed polar-ZnO surface. Phys. Lett. A 373, 391 (2009).
Mriano, A. N. & Hannemam, R. E. Crystallographic Polarity of ZnO Crystals. J. Appl. Phys. 34, 384–388 (1963).
Sakaguchi, N. et al. A HRTEM and EELS study of Pd/ZnO polar interfaces. Phil. Mag. 88, 1493–1509 (2008).
Watanabe, K., Kunisada, Y. & Sakaguchi, N. Stability of {111}Pd/{0002}ZnO polar interface formed by internal oxidation of Pd–Zn alloys. Microscopy 63, 463–467 (2014).
Manchon, A. et al. Analysis of oxygen induced anisotropy crossover in Pt/Co/MOx trilayers. J. Appl. Phys. 104, 043914 (2008).
Kashyap, A., Garg, K. B., Solanki, A. K., Nautiyal, T. & Auluck, S. Phys. Rev. B 60, 2262 (1999).
Bruno, P. Spin-wave theory of two-dimensional ferromagnets in the presence of dipolar interactions and magnetocrystalline anisotropy. Phys.Rev. B 43, 6015–6021 (1991).
Allen, M. W., Miller, P., Reeves, R. J. & Durbin, S. M. Influence of spontaneous polarization on the electrical and optical properties of bulk, single crystal ZnO. Appl. Phys. Lett. 90, 062104 (2007).
Acknowledgements
The authors thank Y. Sasakawa, T. Koyama, S. Ono, H. Oshikawa, A. Kumamoto, and ELIONIX Inc. for their technical help. This work was partly supported by a Grants-in-Aid for Challenging Exploratory Research (15K13359), Scientific Research (S) (25220604), and Specially Promoted Research (15H05702) from JSPS and the Spintronics Research Network of Japan. A portion of this work was performed under the Inter-University Cooperative Research Program of the IMR, Tohoku University, and involved the use of the facilities of the Cryogenic Research Center of the University of Tokyo. STEM observations were conducted at Research Hub for Advanced Nano Characterization and “Nanotechnology Platform” at the University of Tokyo, supported by MEXT of Japan.
Author information
Authors and Affiliations
Contributions
D.C. and A.T. planned the study. A.T. supplied the high-quality ZnO substrates and measured the XRD profiles of the Co and Pt films deposited on them. N.S. obtained the STEM images and EDS mapping. D.C. performed the magnetization and transport measurements and analysed the data. D.C. wrote the manuscript with A.T. and N.S. All authors discussed the results.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Chiba, D., Shibata, N. & Tsukazaki, A. Co thin films deposited directly on ZnO polar surfaces. Sci Rep 6, 38005 (2016). https://doi.org/10.1038/srep38005
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep38005
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.