Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Tuning the electrical conductance of metalloporphyrin supramolecular wires

Abstract

In contrast with conventional single-molecule junctions, in which the current flows parallel to the long axis or plane of a molecule, we investigate the transport properties of M(II)-5,15-diphenylporphyrin (M-DPP) single-molecule junctions (M=Co, Ni, Cu, or Zn divalent metal ions), in which the current flows perpendicular to the plane of the porphyrin. Novel STM-based conductance measurements combined with quantum transport calculations demonstrate that current-perpendicular-to-the-plane (CPP) junctions have three-orders-of-magnitude higher electrical conductances than their current-in-plane (CIP) counterparts, ranging from 2.10−2 G0 for Ni-DPP up to 8.10−2 G0 for Zn-DPP. The metal ion in the center of the DPP skeletons is strongly coordinated with the nitrogens of the pyridyl coated electrodes, with a binding energy that is sensitive to the choice of metal ion. We find that the binding energies of Zn-DPP and Co-DPP are significantly higher than those of Ni-DPP and Cu-DPP. Therefore when combined with its higher conductance, we identify Zn-DPP as the favoured candidate for high-conductance CPP single-molecule devices.

Introduction

Porphyrins offer a variety of desirable features as building blocks for future molecular-scale devices including their highly-conjugated structure, rigid planar geometry, high chemical stability and their ability to form metalloporphyrins by coordinating metal ions in the center of their macrocyclic and aromatic skeleton1,2,3,4,5. Following early work, which established their chemical and biological properties6,7,8,9, porphyrins have become a focus of interest both for experimental and theoretical investigations of molecular electronics10,11,12 and for the design of complexes using supramolecular chemistry, leading to a diverse array of structures available for nano-scale building blocks13. This unique combination of properties is exploited in nature, where for example metalloporphyrins acts as charge carriers in naturally occurring processes such as photosynthesis14,15,16,17 and in the respiratory chain18,19. In many of these processes, the plane of the porphyrin skeleton is stacked perpendicular to the direction of charge transport, whereas previous studies10,11,12 address conductance with the plane of the porphyrin skeleton aligned parallel to the direction of charge transport. In the latter “current in plane” (CIP) up-right configuration (Fig. 1a), the porphyrin skeleton was contacted to gold electrodes via thiol or pyridyl anchor groups and the electrical conductance was found to be low10,20 (of order nanosiemens). For the purpose of developing future single-molecule electronics and thermoelectrics, it is highly desirable to increase the electrical conductance, since this can lead to higher switching speeds and reduce the relative effect of parasitic phonons in thermoelectric devices. In what follows we develop a strategy for increasing the electrical conductance of porphyrin-based single-molecule wires by investigating their conductance with the current perpendicular to the plane (CPP) (Fig. 1b). We report a joint experimental and theoretical study of CPP conductance trends and binding configurations across a family of 5,15-diphenylporphyrins (DPPs), with a centrally-coordinated divalent metal ion of either Co(II), Ni, Cu or Zn and demonstrate that their conductance and stability can be tuned through the choice of metal atom. This is an extension of previous experimental measurement21 which showed that the CPP conductance of the flat-laying sandwiches of a Co(II)-DPP shows a large conductance value of three orders of magnitude higher than the measured in-plane conductance10.

Figure 1
figure1

(a) Porphyrin skeleton aligned parallel to the direction of charge transport “current in plane” (CIP) up-right configuration and (b) the optimised sandwich configuration of DPP junction with the current perpendicular to the plane (CPP).

Results and Discussion

Binding energies and relaxed configurations

To obtain theoretical results for binding energies and relaxed configurations, spin-polarised DFT calculations were carried out using SIESTA22 with the local density functional approximation parameterised by Ceperley and Adler23. Initially the geometry of each isolated porphyrin was optimised to a force tolerance less than 20 meV/Å using an extended double zeta polarised basis set of pseudo atomic orbitals for all atoms, and a mesh cutoff of 200 Ry to define the real space grid. Next, the binding energy EBof a single pyridine-4-yl-methanol (PY) with the porphyrin was calculated using the counterpoise method24,25 (see SI). For all four metallo-porphyrins, we find that the energetically-most-favorable configuration occurs when the PY nitrogen atoms are located above the metal atom of the porphyrin. For this most-favorable position of the PY nitrogen atoms, the results for all four binding energies and the corresponding nitrogen-metal distances are shown in Table 1.

Table 1 Shows optimum distance (d), and binding energies EB for all four metalloporphyrins.

Conductance measurements

The Co-DPP and Zn-DPP molecules were synthesized according to the procedure described by Song et al.26. The synthesis of Cu-DPP and Ni-DPP described by26 was modified by changing the solvent and reaction times (See SI for experimental details). PY was synthesized as described previously by Puigmarti-Luis et al.27 and the single-molecule transport measurements were conducted following the procedure described in ref. 21.

Briefly, an Au(111) surface and a STM Au-electrode tip were both functionalized with 1 mM PY solution in ethanol and incubated for 24 h (See Experiments SI for further details). Both electrodes were mounted onto the STM cell and the cell was filled with mesitylene, an inert, non-polar organic solvent, in which the target M(II)-porphyrin is solubilized in nano-molar concentrations25. Details about the STM-break junction (STM-BJ) measurements can be found elsewhere (see SI). Briefly, the STM-BJ experiments consist of repeatedly approaching and retracting the two pyridyl-functionalized electrodes, while monitoring the tunneling current flowing through the electrode-electrode STM junction under a low applied voltage bias (±10 and ±25 mV). ~5000 current traces were collected and 10–15% of them were used to build a conductance 1D histogram for each molecule, examples of which are shown in Fig. 2 insets. As control experiments, single-molecule conductance experiments in the absence of porphyrin molecules and in the presence of empty DPP were performed under the same experimental conditions (see details in Supporting Information). The absence of porphyrin molecules resulted in the lack of molecular junction events and the DPP showed no high conductance peak in the histograms. The fit of the observed high conductance peak in Fig. 2 histogram was used to extract a most-probable value of the single-molecule conductance for the flat-stacked metalloporphyrin21. The observed two low conductance peaks are commonly-observed for all porphyrins and they have been ascribed to molecular wires with more extended (tilted) conformations of the porphyrin bridging the gap at longer electrode-electrode separations25. The fact that the empty DDP uniquely displays the low conductance features is evidence that such conformations arise from the interaction between the PY and the porphyrin ring moieties. The conductance values extracted from Gaussian fits to the conductance histograms for each metalloporphyrin (Fig. 2) has been also supported by a static blinking STM approach, where the spontaneous formation of the porphyrin bridge is attained while holding a fixed electrode-electrode distance (see SI for more details on the blinking method).

Figure 2
figure2

(a,b,c and d) show the semi-log conductance histograms for the experimental STM single-molecule transport experiment for the Co-DPP, Zn-DPP, Cu-DPP and Ni-DPP systems, respectively. The inset shows representative single current decay curves used to build the conductance histograms. The applied BIAS was set to +25 mV. The sharp increase in counts in both left and right sides of the histograms correspond to the current amplifier baseline and saturation respectively.

Conductance calculations

To model an example of a blinking experiment in which the electrodes are held at a fixed separation, we fixed the PY-functionalised gold electrodes at separation corresponding to a 4.6 Å distance between the terminal N atoms of the PYs, as shown in Fig. 3. This distance is chosen to be slightly larger than the highest value of the distances d in table 1, such that all molecules can be accommodated within the electrode gap. We then allowed the porphyrin molecule to bind to the lower PY, with a N-to-metal-atom distance of d (see Table 1). The PY of the upper gold electrode was therefore more weakly bound to the metal atom of the porphyrin, as would be the case in a blinking experiment.

Figure 3
figure3

Scheme of contact of pyridine anchor above the porphyrin molecule.

The lower PY nitrogen is a distance d from the metal atoms, while the the upper PY nitrogen is placed a distance 4.6 Å above the lower PY nitrogen.

Before computing transport properties, we first examined the spin state of the metalloporphyrins. Numerous studies have examined the effect of the axial ligand on the redox28,29 and photovoltaic properties of metalloporphyrins30. Nickel porphyrin with coordinating axial ligands are paramaganetic (S = 1) in contrast to four-coordinate species (S = 0)31,32. Therefore, to accurately calculate the transport properties of these molecules spin polarized transport calculations must be carried out. We find in the case of the zinc-metalloporphyrin were there is no spin dependence the up spin and down spin transmission curves are almost identical (See Fig. S1).

The conductance was then calculated using the Gollum quantum transport code33, which utilizes the mean-field Hamiltonians provided by DFT. Starting from the SIESTA Hamiltonian, we use Gollum to calculate the transmission coefficient Tσ(E), describing electrons of energy E, spin σ = [↑, ↓] passing from one electrode to the other via the porphyrin, from which the finite-temperature electrical conductance G is obtained using the Landauer formula

In this expression, f(E, T) is the Fermi distribution function defined as where kB is Boltzmann’s constant and is the quantum of conductance.

Figure 4 shows the total transmission coefficients as a function of energy for Zn-DPP, Cu-DPP, Co-DPP and Ni-DPP respectively. The corresponding room-temperature conductances versus Fermi energy EF are shown in Fig. 5a. Since the Fermi energy predicted by DFT is not necessarily accurate34, to compare theory with experiment, we treat the Fermi energy EF as a single free parameter, chosen to determine four conductances, which are closest to the experimental trend. Figure 5b shows that the experimentally-measured order Ni < Co < Cu < Zn is obtained by choosing a Fermi energy .

Figure 4
figure4

The total transmission coefficient as a function of energy for (a) Zn-DPP, (b) Cu-DDP, (c) Co-DPP and (d) Ni-DDP. Each PY-porphyrin is in its relaxed configuration, with the metal atom a distance d from the N of the lower PY. The upper PY-functionalised gold electrode was then positioned such that distance between the upper and lower PY nitrogens was fixed at 4.6 Å.

Figure 5
figure5

The calculated room-temperature electrical conductances for Zn-DPP, Co-DPP, Cu-DPP and Ni-DPP, obtained from Fig. 4.

(b) Comparison between experimental (orange circles) and theoretical conductances (blue circles) obtained by choosing an optimum values of EF − EFDFT = −0.03 eV. The error bars in the experimental points (orange circles) represent the full width at half maximum from the corresponding conductance histogram peak in Fig. 2, which were obtained from the accumulation of hundreds of individual traces for every system.

Figure 5b shows that the chosen junction separation captures the experimental ordering of the Ni-DPP, Co-DPP, Cu-DPP and Zn-DPP. Furthermore, the computed magnitudes of the conductances are of the same order as the measured values and these conductances are far higher than those measured for CIP junctions, which are typically less than 10−4 G0.

Conclusion

We have investigated the electrical conductance with the current perpendicular to the plane (CPP) of supramolecular metalloporphyrin wires. Both theory and experiment reveal that the variation in conductance across this family of molecules increases in the order Ni < Co < Cu < Zn. Experimentally the conductance of Zn-DPP is found to be a factor of 4 greater than that of Ni-DPP. Crucially the CPP conductances are three orders of magnitude greater than their CIP counterparts. For example as reported in [10] for Zn-porphyrins, the CIP conductance is 2.7·10−5 G0, which is more than three orders of magnitude lower than our measured CPP conductance. Similarly in [2] the reported CIP conductances for Cu, Co and Ni porphyrins were 3.6 10−5 G0, 2.5 10−5 G0 and 1.9 10−5 G0 respectively. This supramolecularly-wired arrangement with the aromatic plane perpendicular to the current is therefore stable at room temperature and provides a unique family of high-conductance molecular wires, whose electrical conductances and binding energies can be tuned by metal substitution. From the point of view of stability, we find that the binding energies of Zn-DPP and Co-DPP are significantly higher than those of Ni-DPP and Cu-DPP and therefore in view of its higher conductance, we identify Zn-DPP as the favoured candidate for high-conductance CPP single-molecule devices.

Additional Information

How to cite this article: Noori, M. et al. Tuning the electrical conductance of metalloporphyrin supramolecular wires. Sci. Rep. 6, 37352; doi: 10.1038/srep37352 (2016).

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

References

  1. Li, Z., Smeu, M., Ratner, M. A. & Borguet, E. Effect of anchoring groups on single molecule charge transport through porphyrins. The Journal of Physical Chemistry C 117, 14890–14898 (2013).

    CAS  Article  Google Scholar 

  2. Liu, Z.-F. et al. Control of Single-Molecule Junction Conductance of Porphyrins via a Transition-Metal Center. Nano letters 14, 5365–5370 (2014).

    ADS  CAS  Article  Google Scholar 

  3. Suslick, K. S., Rakow, N. A., Kosal, M. E. & Chou, J.-H. The materials chemistry of porphyrins and metalloporphyrins. Journal of Porphyrins and Phthalocyanines 4, 407–413 (2000).

    CAS  Article  Google Scholar 

  4. Cárdenas-Jirón, G. I. Aza nitrogens effect on the electronic properties of cobalt porphyrine and derivatives. Journal of the Chilean Chemical Society 49, 101–104 (2004).

    Article  Google Scholar 

  5. Auwärter, W., Écija, D., Klappenberger, F. & Barth, J. V. Porphyrins at interfaces. Nature chemistry 7, 105–120 (2015).

    ADS  Article  Google Scholar 

  6. Dorough, G., Miller, J. & Huennekens, F. M. Spectra of the Metallo-derivatives of α, β, γ, δ-Tetraphenylporphine. Journal of the American Chemical Society 73, 4315–4320 (1951).

    CAS  Article  Google Scholar 

  7. Gust, D. & Roberts, J. D. Nitrogen-15 nuclear magnetic resonance studies of porphyrins. Journal of the American Chemical Society 99, 3637–3640 (1977).

    CAS  Article  Google Scholar 

  8. Vasilopoulou, M. et al. Large work function shift of organic semiconductors inducing enhanced interfacial electron transfer in organic optoelectronics enabled by porphyrin aggregated nanostructures. Nano Research 7, 679–693 (2014).

    CAS  Article  Google Scholar 

  9. Cudia, C. C. et al. Electronic structure and molecular orientation of a Zn-tetra-phenyl porphyrin multilayer on Si (111). Surface science 600, 4013–4017 (2006).

    ADS  Article  Google Scholar 

  10. Sedghi, G. et al. Long-range electron tunnelling in oligo-porphyrin molecular wires. Nature nanotechnology 6, 517–523 (2011).

    ADS  CAS  Article  Google Scholar 

  11. Li, Y., Yao, J., Zhong, S. & Zou, Z. Theoretical investigations on the orientational dependence of electron transport through porphyrin molecular wire. Current Applied Physics 11, 1349–1353 (2011).

    ADS  Article  Google Scholar 

  12. Ferradás, R., García-Suárez, V. M. & Ferrer, J. Symmetry-induced quantum interference effects in metalloporphyrin wires. Journal of Physics: Condensed Matter 25, 325501 (2013).

    PubMed  Google Scholar 

  13. Beletskaya, I., Tyurin, V. S., Tsivadze, A. Y., Guilard, R. & Stern, C. Supramolecular chemistry of metalloporphyrins. Chemical reviews 109, 1659–1713 (2009).

    CAS  Article  Google Scholar 

  14. McDermott, G. et al. Crystal structure of an integral membrane light-harvesting complex from photosynthetic bacteria. Nature 374, 517–521 (1995).

    ADS  CAS  Article  Google Scholar 

  15. Zhang, Z. et al. Electron transfer by domain movement in cytochrome bc1. Nature 392, 677–684 (1998).

    ADS  CAS  Article  Google Scholar 

  16. Regan, J. J., Ramirez, B. E., Winkler, J. R., Gray, H. B. & Malmström, B. G. Pathways for electron tunneling in cytochrome c oxidase. Journal of bioenergetics and biomembranes 30, 35–39 (1998).

    CAS  Article  Google Scholar 

  17. Jurow, M., Schuckman, A. E., Batteas, J. D. & Drain, C. M. Porphyrins as molecular electronic components of functional devices. Coordination chemistry reviews 254, 2297–2310 (2010).

    CAS  Article  Google Scholar 

  18. Gray, H. B. & Winkler, J. R. Electron flow through metalloproteins. Biochimica et Biophysica Acta (BBA)-Bioenergetics 1797, 1563–1572 (2010).

    CAS  Article  Google Scholar 

  19. Allen, J. W., Watmough, N. J. & Ferguson, S. J. A switch in heme axial ligation prepares Paracoccus pantotrophus cytochrome cd1 for catalysis. Nature Structural & Molecular Biology 7, 885–888 (2000).

    CAS  Article  Google Scholar 

  20. Simbeck, A. J., Qian, G., Nayak, S. K., Wang, G.-C. & Lewis, K. M. Gold–sulfur bond breaking in Zn (II) tetraphenylporphyrin molecular junctions. Surface science 606, 1412–1415 (2012).

    ADS  CAS  Article  Google Scholar 

  21. Aragones, A. C. et al. Highly Conductive Single-Molecule Wires with Controlled Orientation by Coordination of Metalloporphyrins. Nano letters 14, 4751–4756 (2014).

    ADS  CAS  Article  Google Scholar 

  22. Soler, J. M. et al. The SIESTA method for ab initio order-N materials simulation. Journal of Physics: Condensed Matter 14, 2745 (2002).

    ADS  CAS  Google Scholar 

  23. Ceperley, D. M. & Alder, B. Ground state of the electron gas by a stochastic method. Physical Review Letters 45, 566 (1980).

    ADS  CAS  Article  Google Scholar 

  24. Jansen, H. & Ros, P. Non-empirical molecular orbital calculations on the protonation of carbon monoxide. Chemical Physics Letters 3, 140–143 (1969).

    ADS  CAS  Article  Google Scholar 

  25. Boys, S. F. & Bernardi, F. d. The calculation of small molecular interactions by the differences of separate total energies. Some procedures with reduced errors. Molecular Physics 19, 553–566 (1970).

    ADS  CAS  Article  Google Scholar 

  26. Song, X.-Z. et al. Representation of nonplanar structures of nickel (II) 5, 15-disubstituted porphyrins in terms of displacements along the lowest-frequency normal coordinates of the macrocycle. Journal of the American Chemical Society 118, 12975–12988 (1996).

    CAS  Article  Google Scholar 

  27. Puigmartí-Luis, J., Saletra, W. J., González, A., Amabilino, D. B. & Pérez-García, L. Bottom-up assembly of a surface-anchored supramolecular rotor enabled using a mixed self-assembled monolayer and pre-complexed components. Chemical Communications 50, 82–84 (2014).

    Article  Google Scholar 

  28. Lever, A. & Wilshire, J. Redox potentials of metal phthalocyanines in non-aqueous media. Canadian Journal of Chemistry 54, 2514–2516 (1976).

    CAS  Article  Google Scholar 

  29. Takahashi, K., Komura, T. & Imanaga, H. Photoelectrochemical properties of thin films of zinc porphyrin derivatives with pyridyl group. Bulletin of the Chemical Society of Japan 62, 386–391 (1989).

    CAS  Article  Google Scholar 

  30. Langford, C. H., Seto, S. & Hollebone, B. R. Effect of axially coordinated pi-acid ligands on photovoltaic properties of Zn-tetraphenylporphyrin. Inorganica chimica acta 90, 221–224 (1984).

    CAS  Article  Google Scholar 

  31. Dommaschk, M. et al. Coordination-Induced Spin-State Switching with Nickel Chlorin and Nickel Isobacteriochlorin. Inorganic chemistry 54, 9390–9392 (2015).

    CAS  Article  Google Scholar 

  32. Thies, S. et al. Coordination‐Induced Spin Crossover (CISCO) through Axial Bonding of Substituted Pyridines to Nickel–Porphyrins: σ‐Donor versus π‐Acceptor Effects. Chemistry–A European Journal 16, 10074–10083 (2010).

    CAS  Article  Google Scholar 

  33. Ferrer, J. et al. GOLLUM: a next-generation simulation tool for electron, thermal and spin transport. New Journal of Physics 16, 093029 (2014).

    ADS  Article  Google Scholar 

  34. Lambert, C. Basic concepts of quantum interference and electron transport in single-molecule electronics. Chemical Society Reviews 44, 875–888 (2015).

    CAS  Article  Google Scholar 

Download references

Acknowledgements

This work is supported by UK EPSRC grants EP N017188/1, EP/M014452/1, the European Union Marie-Curie Network MOLESCO 606728 and the Ministry of Higher Education and Scientific Research, Thi-Qar University, IRAQ. I.D.-P. thanks the MINECO Spanish national projects CTQ2012-36090, CTQ2015-71406-ERC and RYC-2011-07951, and the EU Reintegration Grant FP7-PEOPLE-2010-RG-277182 for financial support. A.C.A. thanks the Spanish Ministerio de Educación, Cultura y Deporte for a graduate FPU fellowship. N.D. acknowledges the European Union for a Marie Curie IIF Fellowship. A.G.-C. thanks the MICINN Spanish national project MAT2013-47869-C4-P-2, financial support through the “Severo Ochoa” Programme for Centres of Excellence in R&D (SEV-2015-0496) and the JAE-DOC program (CSIC). DA thanks the EPSRC.

Author information

Affiliations

Authors

Contributions

M.N., S.W.D.B., Q.A. and I.G. performed numerical simulations. A.C.A., G.D.P., N.D., D.B.A. and A.G.-C. performed experiments. I.D.P. and C.J.L. conceptualised the project. All authors reviewed and contributed to the writing of the manuscript.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Electronic supplementary material

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Noori, M., Aragonès, A., Di Palma, G. et al. Tuning the electrical conductance of metalloporphyrin supramolecular wires. Sci Rep 6, 37352 (2016). https://doi.org/10.1038/srep37352

Download citation

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing