The strong adhesion of sub-micron sized particles to surfaces is a nuisance, both for removing contaminating colloids from surfaces and for conscious manipulation of particles to create and test novel micro/nano-scale assemblies. The obvious idea of using detergents to ease these processes suffers from a lack of control: the action of any conventional surface-modifying agent is immediate and global. With photosensitive azobenzene containing surfactants we overcome these limitations. Such photo-soaps contain optical switches (azobenzene molecules), which upon illumination with light of appropriate wavelength undergo reversible trans-cis photo-isomerization resulting in a subsequent change of the physico-chemical molecular properties. In this work we show that when a spatial gradient in the composition of trans- and cis- isomers is created near a solid-liquid interface, a substantial hydrodynamic flow can be initiated, the spatial extent of which can be set, e.g., by the shape of a laser spot. We propose the concept of light induced diffusioosmosis driving the flow, which can remove, gather or pattern a particle assembly at a solid-liquid interface. In other words, in addition to providing a soap we implement selectivity: particles are mobilized and moved at the time of illumination, and only across the illuminated area.
In modern semiconductor industry the production of microchips must be conducted in high-level class clean rooms in order to avoid the adsorption of dust (organic or inorganic micron- to submicron sized particles) on structured surfaces. The reason is simple: small particles adsorb rather tightly to a flat surface due to strong adhesion forces. There is up to now no macroscopic brush-like device that is suitable for gentle particle removal. Conventional mechanical approaches to clean surfaces, e.g., high pressure gas or liquid flow tend to destroy functional elements along with driving the contaminants in an uncontrollable manner.
For (re-)moving or manipulating objects on a nano- and micro- meter scale there is no immediate concept such as a “miniaturized brush” that one could use to gently move a collection of objects within a selected, possibly very small area. Controlled motion of micro/nano- objects has been achieved with probing single particles at a time as with the tip of an Atomic Force Microscope (AFM)1,2,3. In fact, AFM is to date the only method for controlled relocation of adsorbed sub-micron sized objects, but not suitable for assemblies exceeding but a few particles.
For freely movable objects, e.g., dispersed in solution, a number of other concepts has been devised. For instance, one has made use of molecular motors as found in nature4,5,6,7; externally actuated motion employing optical tweezers8,9; optically induced dielectrophoresis10,11,12; and other techniques that utilize gradients of electric or magnetic fields13,14. However, all these methods cease to work as soon as the objects to be manipulated become trapped at some interface or surface, and one is essentially led back to the AFM approach.
Several years ago we have explored a different path towards moving and manipulating large ensembles of small objects. We demonstrated that particles otherwise firmly attached to a thin polymer film can be moved without explicit external contact, just by inducing local shape changes and changes in composition of an underlying polymer film, triggered by an external stimulus15,16,17. The particle simply follows the changing landscape in surface energy. Although the approach works well, it requires a sophisticated modification of the solid substrate that might be feasible only in a few situations.
Our work has clearly shown that in pursuing this idea further, one ideally would like to have remote, contactless control over a large ensemble of particles at arbitrary interfaces. From a general point of view, one has to solve the following problems all at once: minimizing the surface/particle interaction, generating forces locally to address only a selected set of particles, and employing a convenient remote trigger such as light. To achieve this we propose in this work the concept of a photo-sensitive soap. While being similar to applying a conventional soap, we shall additionally make explicit use of the functional properties of a photo-responsive unit incorporated into surfactant molecules.
The properties of many molecules can be modified with optical stimuli by incorporating a suitable photosensitive group into their structure. One of the best known molecules for this purpose is azobenzene (Fig. 1a). Azobenzene undergoes reversible photo-isomerization between a more stable trans- and a metastable cis- conformation during illumination with light of appropriate wavelength. Along with the conformational changes, the physical properties of the molecules are also altered: their shape switches from rod-like to “Γ -like” with a corresponding increase in free volume, the dipole moment increases from 0 Debye in the trans- to ~3 Debye in the cis- conformation. When incorporated into the hydrophobic tail of a surfactant molecule, photoisomerization can thus alter the hydrophobicity/hydrophilicity of the whole surfactant structure18, and can be toggled by alternating illumination with UV and blue light19. In this way, azobenzene containing surfactant bears an enormous potential for practical applications. One can, for instance, trigger compaction and decompaction of a DNA molecule by light in a reversible way20,21,22,23,24,25,26,27,28,29,30, or remotely control the size of microgels by applying periodically UV and blue irradiation31,32,33. One can modify polymer brushes with these molecules and make them photoresponsive with respect to topography and surface energy34,35,36. Geared towards applications in microfluidics, it was shown that a Marangoni-type flow can be induced by cis-trans isomerization of azobenzene solutes at the liquid-air or liquid-liquid interface; this effect has been used to steer oil droplets on an aqueous subphase37.
In contrast, working with particle based systems, we have discovered a peculiar phenomenon related to colloids located at a liquid-solid interface immersed into aqueous solution of photosensitive surfactant. Here we report on how small particles trapped at a solid/liquid interface can be moved by diffusioosmotic focusing initiated by the photoisomerization process. We will provide a theoretical account of how the local liquid flows emerge. It will turn out that the phenomenon is best understood as light-driven diffusioosmosis. In this way, the surfactant becomes a photo-soap in a new sense: not only particle-surface interaction is reduced, but also control over the “rinsing” of contaminants can be gained.
Figure 1a shows a scheme of the experimental set-up: a glass surface with silica micro-particles (2 μm in diameter) is immersed into an aqueous solution of azobenzene containing surfactant with concentration c = 1 mM (Fig. 1b). The critical micelle concentration (CMC) of the surfactant is equal to 0.5 mM. The irradiation direction is from below, the focal plane of the UV laser (λ = 355 nm, P = 1.5 μW) is at the level of the interface where the particles are adsorbed. Before irradiation the silica particles form a densely packed monolayer at the glass surface. When illumination with UV light is turned on (the red cycle in Fig. 1c indicates the center of the laser spot), the colloids are expelled from the illuminated spot leaving behind a completely clean area after 5 minutes of irradiation. The corresponding movie is presented in Supplementary Figure 1. Along with the local irradiation, we also create a spatially inhomogeneous distribution of trans- and cis- isomers, since under UV irradiation the surfactant molecules photo-isomerize correspondingly. Without the presence of the surfactant, the particle assembly does not change, ruling out heating effects or gradients in the electro-magnetic field as a possible driving mechanism.
We track the trajectory of each individual particle and compile corresponding statistics of particle velocities (Fig. 2).
To analyze the particle motion the micrograph was divided into ring elements of 30 μm thickness (Fig. 2a). The position of the particles enclosed in these rings was averaged and plotted as a function of time (Fig. 2e). As can be seen from Fig. 2e the particle motion differs depending on the initial position relative to the center of the laser spot. From these distance-time curves a maximal average velocity for each ring was calculated. A maximal average speed of 1.3 μm/s is obtained for particles in the ring between 30 μm and 60 μm from the center of irradiation (Fig. 2f).
The qualitative behavior of particle velocities can naturally be explained if we assume that a focused hydrodynamic flow pattern exists that drives the particles. Due to mass conservation, we expect the velocity (assuming a quasi-2D flow pattern) to drop proportionally to 1/r for increasing radial distance r from the center of irradiation. The low velocities measured directly in the vicinity of the center are then naturally explained by the necessary stagnation flow pattern there. We will come back to this point in more detail in the theoretical part presented below. We should note that particle removal is not restricted to monolayers. Also multilayers can be cleaned up locally in the very same way, and just as quickly (See Supplementary Video 2).
As demonstrated above, under UV irradiation the particles move out of the irradiated area. In all experiments we observe a saturation effect, e.g. starting from a certain time, the particle-free area does not grow any more. The direction of particle motion can be reversed by inverting the distributions of cis- and trans- isomers. This can be achieved by first bringing the majority of the surfactants in a cis- state by global irradiation with UV light, and then illuminating locally with green light that triggers the return to trans-, see Fig. 3. In this case, during irradiation with light of λ = 532 nm, the particles move towards the center of the laser spot (Fig. 3). The gathering of colloids at the center of the laser spot continues during the whole irradiation period and results in the formation of a pile of particles (Fig. 3). Corresponding movies for particles of 2 μm and 7 μm diameter are provided as Supplementary Videos 2 and 3. Note that there is no limitation to how long this process can be run, as the supply of cis- isomers can be kept constant by a simultaneous global illumination with UV light. With increasing amount of gathered particles the velocity distribution is naturally affected, but within the first stages of illumination (with only few particles accumulated), the trend of the particle velocity as a function of radial distance from the laser spot center is similar to that of the outward flow pattern (induced by UV irradiation). Particles situated somewhat off the center (in our examples roughly 50 μm) show a maximal velocity of 1.3 μm/sec (Supplementary Figure 1).
Although this phenomenon could just be used for local removal (cleaning) or gathering of particles, one may also use it for structuring particle assemblies. As a demonstration, we have patterned the logo of the University of Potsdam (UP) (Fig. 4a) or a “happy man” (Fig. 4b) into the particle assembly. Figure 4c shows the result of simultaneous illumination with UV and green light at two different, spatially separated areas. The shape is the result from a combination of particle gathering and expulsion.
As far as we know, the maximal velocity of particles is not affected by particle size, at least down to 1 μm and as large as 40 μm (see Supplementary Figure 2). But there is a strong dependence of the particle velocity on the surfactant concentration. Indeed, Fig. 5a shows the maximal radial velocity of the particles at different surfactant concentrations for two different directions of motion: outwards (induced by UV irradiation, λ = 355 nm) and inwards (during irradiation with green light, λ = 532 nm).
The velocity of the particles increases with azobenzene concentration peaking at roughly c = 1 mM. The behavior of vmax is similar for both, the inwards and outwards motion of the particles, under UV or green irradiation, respectively (Fig. 5a). Another parameter affecting the particle velocity is the ionic strength of the surfactant solution. With increasing salt concentration the particle speed decreases as shown in Fig. 5b.
Summarizing all experimental results, we suggest the following general picture of how particle motion is governed. Let us first consider the case of UV illumination. As can be seen in Fig. 6, during focused irradiation with UV light, a corresponding local excess of cis isomers is created. This results in a gradient of relative cis- and trans- isomer concentrations.
First, the light intensity distribution within the laser spot is inhomogeneous and in this way naturally generates a gradient of concentration of different isomers; second, newly created cis-isomers will diffuse out of the center of irradiation, modifying the laser induced distribution. At the solid-liquid interface this can in principle lead to a gradient of concentration of adsorbed surfactant, but this could not generate any classical Marangoni flow since adsorbed molecules are immobile. An explanation for emerging liquid flow can be obtained if we invoke diffusioosmosis, which originates due to gradients of cis- and trans- isomer concentrations in the lateral direction (Fig. 6) and is driven by an electrostatic diffuse layer (EDL) of thickness λD, i.e., the region where the surface charge is balanced by the cloud of counter-ions38,39,40,41,42.
Indeed, the spatially varying excess concentration of counter-ions near the solid leads to a corresponding osmotic pressure:
where c0(x) is the bulk concentration of surfactant molecules, local concentrations of ions within the EDL, kB is the Boltzmann constant, and T is the temperature. The lateral gradient in cis- concentration induced during illumination (along the x direction in Fig. 6) then causes an osmotic pressure gradient driving a hydrodynamic flow. The flow field ν satisfies Stokes’ equations:
with the EDL surface excess of ions given by
The gradient of surface excess in Eq. (3) can be expressed in terms of concentration of either trans- or cis-isomer generated by local irradiation:
where indices t and c correspond to trans- and cis- isomers. The quantities characterize the adsorption of trans- and cis- molecules (in thin layer near solid/liquid interface, Fig. 6) and can be estimated experimentally by measuring the surfactant adsorption isotherm and surface zeta potential. Note that we can relate to electrostatic surface potential, ϕ0, by employing the Boltzmann distribution of ions inside the EDL, which together with Grahame’s equation leads to:44,45
where we assume ϕ0 does not exceed 100 mV. It follows that the flow depends strongly on total surfactant concentration and on the adsorption strength of cis- and trans- isomers, which alters the surface zeta potential. We remark that this inner flow generates an outer flow shown on Fig. 6, and we refer the reader to Supplementary Information (Figure S3) for computational details.
We shall now focus on difference between situations below and above the CMC. Below the CMC c0 < ccmc, lower velocity is related to two types of opposite gradient of cis- and trans- molecules. Since below CMC cc = c0 − ct, we obtain
so that the velocities’ magnitude and sign depend on the difference of adsorption constants for cis and trans isomers. Above the CMC, the concentration of trans molecules stays nearly constant, due to micelle formation, and only is important, so we derive:
which suggests that an increase in velocity occurs for concentrations c0 > ccmc. In this case the concentration of single molecules is no longer described by cc = c0 − ct due to micelle decomposition. Let us now estimate the diffusioosmotic velocity by using the above arguments:
Here the diameter of the laser spot, L, is 60 μm, λD ~ 10 nm at c0 = 1 mM, and η ~ 1 mPa·s, and the value of ϕ0 = 70 mV is deduced from the experimental data on the zeta potential, see Fig. 7c. The value of 7 μm/s is of the order of the measured maximal velocity validating our model. We note that the magnitude of velocities is much lower than those for typical Marangoni flows found at liquid air interfaces46,47. This is mainly because scales with the screening length λD, but not with the film thickness as in the case of Marangoni flow.
In summary, we have shown that with the local gradients imposed on the distribution of cis- and trans- isomers close to a solid-liquid interface, sufficiently strong hydrodynamic forces can be generated in order to explain the observed velocity distributions of a particle assembly at the solid substrate. We should recall that the photo-soap is still acting in the conventional way, that is, it reduces the surface-particle interactions and renders the particles mobile.
We have demonstrated how a photosensitive surfactant was employed to generate sufficiently strong local hydrodynamic forces to move and pattern particle assemblies at a solid liquid interface. This photo-soap is to serve two purposes simultaneously: modification of interfacial energies and removing of particles by initiation of local hydrodynamic shear flow. Particles are moved at the time of illumination, and only within and in the vicinity of the illuminated area. Whether a flow in or out of the illuminated area occurs is governed by the wavelength employed: upon UV irradiation promoting trans-cis isomerization we observe outflow, whereas employing green light inducing back-isomerization from cis to trans inflow can be generated, which causes particles to pile up at the stagnation point at the center of the flow pattern.
Furthermore, moving a single laser spot across a dense particle layer can be used for straightforward spatial patterning; more complex operations are possible by employing several spots simultaneously.
We have shown that the resulting particle velocities do not depend on particle diameter (at least in the range of 1 μm to 10 μm), but are strongly impacted by surfactant concentration. The largest velocities are observed above the CMC, where micelles form effective reservoirs setting free a large amount of surfactant molecules at once upon irradiation. Our theoretical analysis of the phenomena described suggests that the initiation of flow can be understood with the concept of light driven diffusioosmosis. Here the spatial gradients in both, cis and trans isomers generate corresponding gradients in osmotic pressure that in the presence of the solid substrate leads to an effective shear flow. From a practical point of view, we hope that our approach of using a photosensitive soap can be turned into an application that alleviates some of the problems encountered in cleaning processes or in manipulating assemblies of adsorbed sub-micron sized particles.
Azobenzene containing cationic surfactant with a spacer of six methylene groups between the positively charged trimethylammonium bromide head group and the azobenzene unit was synthesized as described elsewhere48. The surfactant was dissolved in Milli-Q water and diluted to the required concentrations.
The photoisomerization behavior of the surfactant is described in detail elsewhere22. In short, in the dark state (trans conformation) of the surfactant is characterized by an absorption band with a maximum at 353 nm, while the cis isomer is characterized by two absorption bands with maxima at 313 nm and at 437 nm (Fig. 7a). The band with maximum at ~240 nm presented in both isomers corresponds to the absorption of the π-conjugated benzene rings. The lifetime of the cis isomer in the dark is 48 hours, while the photo-isomerization from cis- to trans-state under irradiation with green light (λ = 532 nm, P = 30 μW) takes place within a few seconds, approaching a photo-stationary state after 10 minutes of irradiation.
The surfactant solution was introduced into a flow chamber (μ-Slide VI 0.4 flow chamber, Ibidi, Germany) with a volume of 60 μl. Aqueous solution of silica particles of varying sizes (Micromod, Germany) was added to and mixed with the surfactant solution. To prevent evaporation, the chamber openings were sealed with Parafilm (Bemis Company, Inc., USA). Before measurement the samples are kept in dark for several minutes until the silica particles sediment to the bottom of the substrate.
The zeta potential of silica particles was measured using a Zetasizer (Nano-ZS, Malvern Instruments Ltd.). The azobenzene concentration was varied keeping the particle concentration fixed at 0.04 mg/ml. In water solution the silica particles are negatively charged with a zeta potential of −65 mV. With increasing surfactant concentration, the zeta potential rises up to a value of ca. +80 mV for c = 1 mM, irrespective of whether the surfactant is in trans- or cis- conformation (Fig. 7b). At concentrations starting from 0.1 mM the silica particles are positively charged for both, trans- and cis-isomers.
The surface zeta potential of a glass surface was measured using a surface zeta potential cell ZEN1020 (Malvern Instruments Ltd, UK). Azobenzene surfactant was dissolved in water and diluted to a certain concentration and mixed with polystyrene nano spheres (Thermo Fisher Scientific Inc. USA) so that the suspension was slightly milky. About 1.2 ml was filled into a plastic cuvette (DTS0012, Malvern Instruments Ltd, UK). A glass substrate was cut and broken to a width of ca. 4 mm to fit the size requirements of the cell.
An inverted Olympus IX71 was equipped with two lasers (Samba 532 nm, Cobolt, Sweden; 355 nm, Genesis CX, Coherent Inc., USA). The laser beams were focused through the objective of the microscope to the solid-liquid interface where the particles adsorbed. The laser power was measured at the solid/liquid interface by optical power meter 1918-R with sensor 918D-UV-OD3R (Newport Corporation,Irvine, CA, USA). Additionally, the setup was kept in the dark to prevent uncontrolled isomerization. Images were acquired with an Olympus XM10 monochrome camera at a speed of 1 frame per second.
Tracking and data analysis
Particles are tracked using the Mosaic Single Particle Tracking plugin for ImageJ (Rasband, W.S., ImageJ, U. S. National Institutes of Health, Bethesda, Maryland, USA, http://imagej.nih.gov/ij/, 1997–2015). The tracking algorithm was described by Koumoutsakos49. The particle tracks were analyzed using a self-written Matlab script: for each particle and frame the distance from the laser spot is calculated. The area around the spot is divided into ring segments of defined thickness of 30 μm. For each particle, the distance at t = 0 is calculated and averaged over all particles in one ring segment. In addition, the velocities are calculated by dividing the distance moved by the time interval Δt = 1 s. Maximal velocities are calculated with a time difference of Δt = 10 s smoothing the velocity profile.
How to cite this article: Feldmann, D. et al. Manipulation of small particles at solid liquid interface: light driven diffusioosmosis. Sci. Rep. 6, 36443; doi: 10.1038/srep36443 (2016).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Kim, S., Ratchford, D. C. & Li, X. Atomic force microscope nanomanipulation with simultaneous visual guidance. ACS Nano 3, 2989–2994 (2009).
Sun Y. & Liu X. (ed.). Micro- and Nanomanipulation Tools (Wiley-VCH: Weinheim, 2015).
Kolb, D. M., Ullmann, R. & Will, T. Nanofabrication of small copper clusters on gold(111) electrodes by a scanning tunneling microscope. Science 275, 1097–1099 (1997).
Hess, H. & Vogel, V. Molecular shuttles based on motor proteins: active transport in synthetic environments. Rev. Mol. Biotechnol. 82, 67–85 (2001).
Schliwa, M. & Woehlke, G. Molecular motors. Nature 422, 759–765 (2003).
Bath, J. & Turberfield, A. J. DNA nanomachines. Nat. Nanotechnol. 2, 275–284 (2007).
Hess, H., Clemmens, J., Qin, D., Howard, J. & Vogel, V. Light-controlled molecular shuttles made from motor proteins carrying cargo on engineered surfaces. Nano Lett. 1, 235–239 (2001).
Grier, D. G. A revolution in optical manipulation. Nature 424, 810–816 (2003).
Berthelot, J. et al. Three-dimensional manipulation with scanning near-field optical nanotweezers. Nat. Nano 9, 295–299 (2014).
Chiou, P. Y., Ohta, A. T. & Wu, M. C. Massively parallel manipulation of single cells and microparticles using optical images. Nature 436, 370–372 (2005).
Ruan, G. et al. Simultaneous magnetic manipulation and fluorescent tracking of multiple individual hybrid nanostructures. Nano Lett. 10, 2220–2224 (2010).
Donolato, M. et al. On-chip manipulation of protein-coated magnetic beads via domain-wall conduits. Adv. Mater. 22, 2706–2710 (2010).
Yang, A. H. J. et al. Optical manipulation of nanoparticles and biomolecules in sub-wavelength slot waveguides. Nature 457, 71–75 (2009).
Fennimore, A. M. et al. Rotational actuators based on carbon nanotubes. Nature 424, 408–410 (2003).
Santer, S. & Rühe, J. Motion of nano-objects on polymer brushes. Polymer 45, 8279–8297 (2004).
Santer, S., Kopyshev, A., Donges, J., Yang, H.-K. & Rühe, J. Dynamically Reconfigurable Polymer Films: Impact on Nanomotion. Adv. Mater. 18, 2359–2362 (2006).
Yadavalli, N. S., König, T. & Santer, S. Selective mass transport of azobenzene-containing photosensitive films towards or away from the light intensity. J. Soc. Info. Display 23, 154–162 (2015).
Rau, H. Photoisomerization of Azobenzenes; In Photochemistry and Photophysics, (ed. Rabek, J. ) 119–142 (CRC Press: Boca Raton, FL, USA, 1990).
Zakrevskyy, Y. et al. Interaction of photosensitive surfactant with DNA and poly acrylic acid. J. Chem. Phys. 140, 44907 (2014).
Zakrevskyy, Y., Roxlau, J., Brezesinski, G., Lomadze, N. & Santer, S. Photosensitive surfactants: micellization and interaction with DNA. J. Chem. Phys. 140, 44906 (2014).
Zakrevskyy, Y., Titov, E., Lomadze, N. & Santer, S. Phase diagrams of DNA-photosensitive surfactant complexes: effect of ionic strength and surfactant structure. J. Chem. Phys. 141, 164904 (2014).
Zakrevskyy, Y. et al. Interaction of photosensitive surfactant with DNA and poly acrylic acid. J. Chem. Phys. 140, 044907 (2014).
Zakrevskyy, Y. et al. DNA compaction by azobenzene-containing surfactant. Phys. Rev. E 84, 21909 (2011).
Le Ny, A.-L. M. & Lee, C. T. Conformation and dynamics of DNA molecules during photoreversible condensation. Biophys. Chem. 142, 76–83 (2009).
Sollogoub, M. et al. Photocontrol of single-chain DNA conformation in cell-mimicking microcompartments. Chem Bio Chem 9, 1201–1206 (2008).
Geoffroy, M., Faure, D., Oda, R., Bassani, D. M. & Baigl, D. Photocontrol of genomic DNA conformation by using a photosensitive gemini surfactant: binding affinity versus reversibility. Chem Bio Chem 9, 2382–2385 (2008).
Diguet, A., Mani, N. K., Geoffroy, M., Sollogoub, M. & Baigl, D. Photosensitive surfactants with various hydrophobic tail lengths for the photocontrol of genomic DNA conformation with improved efficiency. Chemistry 16, 11890–11896 (2010).
Rudiuk, S., Yoshikawa, K. & Baigl, D. Enhancement of DNA compaction by negatively charged nanoparticles. Application to reversible photocontrol of DNA higher-order structure. Soft Matter 7, 5854–5860 (2011).
Zinchenko, A. A., Tanahashi, M. & Murata, S. Photochemical modulation of DNA conformation by organic dications. ChemBioChem 13, 105–111 (2012).
Schimka, S. et al. Photosensitive peptidomimetic for light controlled reversible DNA compaction. Biomacromolecules 17, 1959–1968 (2016).
Zakrevskyy, Y. et al. Stimuli-Responsive Materials: Light-Controlled Reversible Manipulation of Microgel Particle Size Using Azobenzene-Containing Surfactant. Adv. Funct. Mater. 22, 5064–5064 (2012).
Rumyantsev, A. M., Santer, S. & Kramarenko, E. Y. Theory of Collapse and Overcharging of a Polyelectrolyte Microgel Induced by an Oppositely Charged Surfactant. Macromolecules 47, 5388–5399 (2014).
Richter, M. et al. Effect of pH, co-monomer content, and surfactant structure on the swelling behavior of microgel-azobenzene-containing surfactant complex. Polymer 55, 6513–6518 (2014).
Kopyshev, A., Galvin, C. J., Genzer, J., Lomadze, N. & Santer, S. Opto-mechanical scission of polymer chains in photosensitive diblock-copolymer brushes. Langmuir 29, 13967–13974 (2013).
Kopyshev, A., Galvin, C. J., Genzer, J., Lomadze, N. & Santer, S. Polymer brushes modified by photosensitive azobenzene containing polyamines. Polymer 98, 421–428 (2016).
Kopyshev, A., Lomadze, N., Feldmann, D., Genzer, J. & Santer, S. Making polymer brush photosensitive with azobenzene containing surfactants. Polymer 79, 65–72 (2015).
Diguet, A. et al. Photomanipulation of a Droplet by the Chromocapillary Effect. Ang Chem Intern Edition 48, 9281–9284 (2009).
Anderson, J. L. & Prieve, D. C. Diffusiophoresis caused by gradients of strongly adsorbing solutes. Langmuir 7, 403–406 (1991).
Keh, H. J. & Ma, H. C. Diffusioosmosis of Electrolyte Solutions along a Charged Plane Wall. Langmuir 21, 5461–5467 (2005).
Anderson, J. L. Colloid Transport by Interfacial Forces. Annual Review of Fluid Mechanics 21, 61–99 (1989).
Ajdari, A. & Bocquet, L. Giant amplification of interfacially driven transport by hydrodynamic slip: diffusioosmosis and beyond. Phys. Rev. Lett. 96, 186102 (2006).
Abecassis, B., Cottin-Bizonne, C., Ybert, C., Ajdari, A. & Bocquet, L. Boosting migration of large particles by solute contrasts. Nature Matterials 7, 785–789 (2008).
Prieve, D. C., Anderson, J. L., Ebel J. P. & Lowell, M. E. Motion of a particle generated by chemical gradients. Part 2. Electrolytes. Journal of Fluid Mechanics 148, 247–269 (1984).
Grahame, D. C. The electrical double layer and the theory of electrocapillarity. Chem. Rev. 41, 441–501 (1947).
Israelachvili, J. N. Intermolecular and Surface Forces (Academic Press, London, 1992)
Chevallier, E. et al. Pumping-out photo-surfactants from an air–water interface using light. Soft Matter 7, 7866–7874 (2011).
Varanakkottu, S. N. et al. Particle manipulation based on optically controlled free surface hydrodynamics. Angewandte Chemie - International Edition 52, 7291–7295 (2013).
Dumont, D., Galstian, T. V., Senkow, S. & Ritcey, A. M. Liquid Crystal Photoalignment using New Photoisomerisable Langmuir-Blodgett Films. Molecular Crystals and Liquid Crystals 375, 341–352 (2002).
Sbalzarini, I. F. & Koumoutsakos, P. Feature point tracking and trajectory analysis for video imaging in cell biology. J. Struct. Biol. 151, 182–195 (2005).
This research is supported by the Priority Program 1726 “Microswimmers-From Single Particle Motion to Collective Behaviour”, Germany; DFG (SA1657/8-1) and Helmholtz Graduate School on Macromolecular Bioscience (Teltow, Germany). We thank Prof. C. Beta and Dr. Mathias Gerhard (University of Potsdam) for the technical support during measurements with optical microscopy and fruitful discussions.
The authors declare no competing financial interests.
About this article
Cite this article
Feldmann, D., Maduar, S., Santer, M. et al. Manipulation of small particles at solid liquid interface: light driven diffusioosmosis. Sci Rep 6, 36443 (2016). https://doi.org/10.1038/srep36443
Journal of Colloid and Interface Science (2021)
Shaping the gradients driving phoretic micro-swimmers: influence of swimming speed, budget of carbonic acid and environment
The European Physical Journal E (2021)
Synthesis and surface activity of photoresponsive hybrid surfactants containing both fluorocarbon and hydrocarbon chains
Journal of Colloid and Interface Science (2021)
The impact of geometrical confinement in a slab on the behavior of tracer particles near active glucose oxidase micropump
Colloid and Polymer Science (2021)
Advanced Materials Interfaces (2021)