Article | Open | Published:

Synthesis and Application of Ferroelectric Poly(Vinylidene Fluoride-co-Trifluoroethylene) Films using Electrophoretic Deposition

Scientific Reports volume 6, Article number: 36176 (2016) | Download Citation

Abstract

In this study, we investigated the deposition kinetics of polyvinylidene fluoride copolymerized with trifluoroethylene (P(VDF-TrFE)) particles on stainless steel substrates during the electrophoretic deposition (EPD) process. The effect of applied voltage and deposition time on the structure and ferroelectric property of the P(VDF-TrFE) films was studied in detail. A method of repeated EPD and heat treatment above melting point were employed to fabricate crack-free P(VDF-TrFE) thick films. This method enabled us to fabricate P(VDF-TrFE) films with variable thicknesses. The morphology of the obtained films was investigated by scanning electron microscopy (SEM), and the formation of β-phase was confirmed by X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. P(VDF-TrFE) films prepared with various thicknesses showed remnant polarization (Pr) of around 4 μC/cm2. To demonstrate the applicability of our processing recipe to complex structures, we fabricated a spring-type energy harvester by depositing P(VDF-TrFE) films on stainless steel springs using EPD process. Our preliminary results show that an electrophoretic deposition can be applied to produce high-quality P(VDF-TrFE) films on planar as well as three-dimensional (3-D) substrates.

Introduction

Many research groups have studied ferroelectric polymers due to their light weight, high flexibility, nontoxicity, and easy processability1,2,3,4,5,6,7,8,9. Among them, polyvinylidene fluoride (PVDF) and its copolymer with trifluoroethylene (P(VDF-TrFE)) are considered to be candidate materials for nonvolatile memory, sensors, actuators, solar cells, and energy harvesting systems1,2,3,4,5 because of their highly compact structure, relatively large permanent dipole moment, and high chemical stability. P(VDF-TrFE) films are typically fabricated by spin coating6, Langmuir-Blodgett deposition7, dip coating8 and solution casting9. These methods are based on chemical solution deposition. They are useful for smooth and flat thin films, but they have limited application for very large area and complex-shaped structures, such as foam and porous substrates.

Meanwhile, electrophoretic deposition (EPD) has advantages over other methods of preparing P(VDF-TrFE) thick films on substrates with various shapes because the deposition rate of EPD is high, and the viscosity of the suspension is low10,11. More specifically, EPD is a colloidal process, which comprises two steps. The first step is to induce motion of charged particles in suspension under the influence of an applied electric field. The second step is to deposit the charged particles onto oppositely charged electrodes. Recently, EPD has attracted much attention because of its versatility, easy process, and need for a simple equipment, such as a power supply10,11. This method has been used to deposit metal12, polymer13, ceramic14, and biomaterial15 particles in the range from nanometers to a few micrometers on conducting substrates or even conducting substrates covered with a dielectric material16. In addition, it has been used to deposit two kinds of materials on substrates simultaneously17. Many different types of ferroelectric ceramics have been widely used in the EPD process, such as Pb(Zr,Ti)O318,19,20,21, K0.5Na0.5NbO322, BaTiO323,24,25 and BiFeO326. Moreover, the deposition of ferroelectric ceramics on complex substrates, such as helical structures27, individual fibers, fiber mats, and nichrome wires28 has been achieved using EPD.

However, there has been no report on the kinetics of EPD for the growth of ferroelectric polymer P(VDF-TrFE) films as well as its applications to complex structures. Although Foster et al. demonstrated P(VDF-TrFE) films fabricated by EPD on a silicon substrate29, the detailed kinetics involved in the EPD of P(VDF-TrFE) particles, such as deposited weight dependence on applied voltage and deposition time, has not been reported. In this study, we investigated the kinetics of P(VDF-TrFE) particles on stainless steel substrates and fabricated crack-free P(VDF-TrFE) thick films with thicknesses in the range of 21.4–34.8 μm by means of repeated EPD and heat treatment. Furthermore, we characterized the ferroelectric properties of P(VDF-TrFE) films as a function of the film thickness using XRD, FTIR, and polarization-electric field hysteresis loop measurements. Finally, we demonstrated that the P(VDF-TrFE) films could be coated on a complex structured substrate using repeated EPD and heat treatment.

Results and Discussion

The schematic illustration of the experimental apparatus shown in Fig. 1(a) depicts the transport and adhesion of P(VDF-TrFE) particles with negative zeta potential to the anode driven by the external electric field. We carried out P(VDF-TrFE) deposition on the stainless steel substrates for various times and at various voltages with a constant distance between the electrodes. The samples of P(VDF-TrFE) deposited using EPD are shown in Fig. 1(b). We observed that the anode was covered with P(VDF-TrFE) particles because the applied electric field pushes the electrophoretic motion of the negatively charged particles toward the anode. We further confirmed that the P(VDF-TrFE) suspension has a negative zeta potential of −26.94 mV by zeta potential analyzer. In addition, we could deposit thicker films on the stainless steel substrates as we increased the voltage to the anode from 10 to 50 V.

Figure 1
Figure 1

(a) Schematic illustration of the electrophoretic deposition process of P(VDF-TrFE) particles on a stainless steel substrate. (b) Photographic images of the substrates covered with P(VDF-TrFE) particles by the electrophoretic deposition process with applied voltages from 10 to 50 V for 2 min.

We measured the deposited weight per area (mg cm−2) as a function of the deposition time and the applied voltage during electrophoretic deposition of P(VDF-TrFE) particles in isopropyl alcohol. We found that the deposited weight per area increased with the deposition time as shown in Fig. 2(a). We also found that the deposited weight per area increased almost linearly with increasing applied voltage. Additionally, we observed that the deposition rate of P(VDF-TrFE) particles increased as the applied voltage increased from 10 to 50 V. However, if all other parameters were kept constant, the deposition rate of P(VDF-TrFE) particles, which is defined by the slope of the curve in Fig. 2(a), decreased with increasing deposition time except for a few points in 20 and 50 V. Figure 2(b) shows the current density as a function of the deposition time and the applied voltage. The current density slightly decreased as the deposition time increased and saturated at 80–90% of its initial value at 10 min. It has been often observed by other research groups30,31 that both the deposition rate and the current density decrease as the deposition time increases, which has been attributed to the higher resistance of the films as the film thickness increases or the concentration of the particles in solution decreases. Therefore, we speculate that the initial decreasing part of the current resulted from the combined contribution of the increase in the film resistance and the decrease in the concentration. However, the latter part where the current stayed constant can be explained only if the porosity remains high so that the current component related to the charge flow through the porous region contributes to the output current. Moreover, we observed that the deposition was close to zero when the applied voltage was 5 V even though we increased the deposition time up to 1 h. Based on this observation, we infer that there is a threshold electric field between 5 V/cm and 10 V/cm, below which no or very little electrophoretic deposition of P(VDF-TrFE) particles occurs on stainless steel substrates. This threshold value is different from that (32 V/cm) reported in the literature by Foster et al.29, where they used silicon as the substrate, indicating strong dependence of the threshold field on the substrate.

Figure 2
Figure 2

Plots of deposited weight per area as (a) a function of deposition time with different applied voltages and (b) current density versus deposition time at different applied voltages.

Figure 3(a) shows an SEM image of P(VDF-TrFE) particles deposited on a stainless steel substrate at 30 V for 2 min. We observed that the P(VDF-TrFE) films contained microcracks over their surfaces. When a P(VDF-TrFE) film dries, tensile stress develops due the capillary forces, and the stress is relieved by the formation and propagation of cracks32. In addition, compared to the applied voltages at 10 and 20 V, larger sized cracks were formed at 30, 40, and 50 V (Supplementary Information, Figs S1–S4). It should be noted that the P(VDF-TrFE) film in Fig. 3(a) peeled from the substrates when a weak force was applied, indicating poor adhesion between the coating and the substrate. To enhance the adhesion and remove the microcracks, we annealed the film at 150 °C for 6 h, which was above the melting point of 147 °C measured by differential scanning calorimetry (DSC). The film color changed from white to transparent. Furthermore, we found that the adhesion of the P(VDF-TrFE) film to the substrate was enhanced. However, we observed that part of the substrate was not covered completely due to the shrinkage of the film, as shown in Fig. 3(b). To overcome this problem, both deposition and heat treatment were repeated on the same substrate twice29,33. Current densities during the 2nd deposition were down to a very low level than those during the 1st deposition because the voltage drop existed across the P(VDF-TrFE) film formed by the 1st deposition and heat treatment (see Supplementary Information, Fig. S5). Figure 3(c) shows an SEM image of P(VDF-TrFE) film after repeated deposition and heat treatment. It can be seen that the whole substrate was covered with P(VDF-TrFE) film.

Figure 3
Figure 3

(a) SEM images of P(VDF-TrFE) films deposited on stainless steel substrates at 30 V for 2 min before heat treatment, (b) after heat treatment and (c) after second deposition and heat treatment.

Crack-free films with thickness of 21.4, 31.4, and 34.8 μm were obtained by repeated deposition at 30, 40, and 50 V for 2 min and heat treatment, respectively. To check the ferroelectric phase formation in the films, we conducted X-ray diffraction (XRD) and Fourier transform infrared (FTIR) analysis on P(VDF-TrFE) films with various thicknesses. It is well known that the prominent peak at 2θ = 19.7° is the sum reflections of (110) and (200) planes of the crystalline β phase34. In Fig. 4(a), we found that the peak exists on the films ranging from 21.4 to 34.8 μm and the position of the peak remains the same regardless of the film thickness, indicative of similar inter-chain spacing for all the films fabricated by EPD in this study. Figure 4(b) shows the FTIR results (from 1500 to 700 cm−1) of P(VDF-TrFE) films with various thicknesses in the range of 21.4–34.8 μm. There are six bands associated with the three axes of the crystal of the P(VDF-TrFE)35,36,37. The peaks at 890 cm−1 and 1184 cm−1 correspond to the a-axis, the 848 cm−1 and 1284 cm−1 peaks indicate the b-axis, and the 1078 cm−1 and 1400 cm−1 peaks are associated with the c-axis. Among them, the characteristic absorbance band of 848 cm−1 represents the symmetric vibration of CF2sCF2) coupled with the symmetric stretching vibration of C-C(νsCC), and that of 1284 cm−1 represents νsCF2 coupled with νsCC and the bending vibration of C-C-C(δCCC)35,36,37. Those at 848 cm−1 and 1284 cm−1 are associated with trans sequences longer than TTTT and TTT, respectively35,36,37. As shown in Fig. 4(b), the 1284 cm−1 and 848 cm−1 bands were nearly at the same position and the peak intensities were similar regardless of film thickness from 21.4 to 34.8 μm, indicating that the β phase crystal orientation does not change with thickness. Therefore, based on the FTIR and XRD results, we confirmed that the P(VDF-TrFE) films were composed of the crystalline β-phase with the same molecular chain structure regardless of film thickness from 21.4 to 34.8 μm.

Figure 4
Figure 4

(a) XRD patterns and (b) FTIR spectra of P(VDF-TrFE) films with different thickness.

The polarization-electric field (P-E) hysteresis loop was measured at 100 Hz to examine the ferroelectric properties of the P(VDF-TrFE) films fabricated by EPD. We also investigated whether there is any change in ferroelectric properties as a function of the film thickness. For the characterization of ferroelectric properties, we fabricated a metal-ferroelectric-metal (MFM) capacitor structure. Pt top electrodes were deposited on P(VDF-TrFE) films by sputtering using a shadow mask with holes of 400 μm in diameter. For the 21.4 μm thick film, the P-E loops showed a saturation polarization (Ps) of 5.1 μC/cm2 and remnant polarization (Pr) of 3.9 μC/cm2 with a coercive field Ec of approximately 42 MV/m. The Pr, Ps and Ec of the 31.4 μm-thick film in a saturated curve were approximately 4.0 μC/cm2, 5.0 μC/cm2, and 42 MV/m, respectively. We found Ps of 5.1 μC/cm2, Pr of 4.0 μC/cm2, and Ec of 47 MV/m for the 34.8 μm thick film. As shown in Fig. 5(d), the ferroelectric properties remained the same over a large range of thickness, and this trend is supported by the findings shown in Fig. 4, where the crystal and molecular structures remained the same regardless of the film thickness. Therefore, we developed a simple and cost effective process to fabricate thick P(VDF-TrFE) films with uniform ferroelectric properties, which provides a large processing window in terms of film thickness.

Figure 5
Figure 5

Polarization-electric field hysteresis of (a) 21.4 μm, (b) 31.4 μm, and (c) 34.8 μm thick P(VDF-TrFE) films measured at 100 Hz. (d) Saturation polarization and remnant polarization versus thickness in P(VDF-TrFE) films.

We applied repeated EPD and heat treatment above the melting point to the fabrication of P(VDF-TrFE) films on a stainless steel spring. The spring was 0.89 mm in wire diameter, 15.03 mm in outer spring diameter and 40.28 mm in length. The spring had 6 turns. The counter electrodes consisted of an outer cylindrical electrode and an inner cylindrical electrode as shown Fig. 6(a). The distance between the spring and each part of the counter electrodes was 3 mm. The applied voltage was 10 V and the deposition time was 1 min. Figure 6(b) is an SEM image showing the crack-free surface of the P(VDF-TrFE) films on the spring after EPD and heat treatment twice. The thickness of P(VDF-TrFE) films on the spring was 25 μm.

Figure 6
Figure 6

(a) Schematic illustration of the electrophoretic deposition on a spring. (b) SEM image of P(VDF-TrFE) films coated on the spring using repeated EPD and heat treatment.

We also measured the output voltage signal from the spring-type piezoelectric energy harvester (SPEH) as the SPEH was periodically pressed and released. To uniformly coat the top of the spring with the Al electrode by thermal evaporation, we repeated the coating process 3 times, rotating the spring by 120° about its long axis38. Teflon tape was used to mask both end of the spring to prevent two opposite electrodes from electrically being connected during the coating process. To enhance the output voltage of the SPEH, the poling process is an essential step, in which P(VDF-TrFE) films are poled under the electric field. The poling process was performed at 100 °C with a bias voltage of 500 V for 1 h using the power supply. After the poling process, the output voltage of the SPEH approximately enhanced by 4.4 times, as shown in the Supplementary Information, Fig. S6. When the output voltage was measured, the displacement of the spring from its resting position was about 10 mm. In order to prove that the output voltage was the genuine piezoelectric signal, we compared the output voltage of the SPEH under the forward and the reverse connections. The average output voltage under the forward connection and the reverse connection was 1.71 V and 1.79 V, respectively (Fig. 7). In the reverse connection, the polarity of the output voltage was reversed and the amplitude of the signal was almost identical with the forward connection. The results indicated that the measured output voltage was the true signal generated from the SPEH.

Figure 7
Figure 7

Schematic illustration of (a) forward connection and (b) reverse connection of SPEH. The output voltage of SPEH under (c) forward connection and (d) reverse connection during pressing and release.

Conclusions

In this study, ferroelectric polymer P(VDF-TrFE) films on stainless steel substrate were fabricated by electrophoretic deposition (EPD) in isopropyl alcohol. We found that the amount of the particles deposited on the substrates increased with the applied voltage and the deposition time. By means of repeated deposition and heat treatment above melting point, we could solve the surface coverage and adhesion problems. Furthermore, XRD and FTIR studies confirmed the presence of β-phase in the P(VDF-TrFE) films prepared by EPD. Finally, the P(VDF-TrFE) films prepared with various thicknesses showed a remnant polarization (Pr) of around 4 μC/cm2, indicative of uniform ferroelectric properties over the thickness range from 21.4 to 34.8 μm. We applied this method to the fabrication of P(VDF-TrFE) films on a spring and confirmed that SPEH can generate electrical energy by mechanical pressure. Therefore, we believe that electrophoretic deposition is a promising method to produce high-quality P(VDF-TrFE) thick films with low cost and simple apparatus.

Methods

Electrophoretic deposition of P(VDF-TrFE)

The powder used in this study was 80/20 P(VDF-TrFE) with an average particle size of 270 nm (Measurement Specialties, Inc.). To prepare the P(VDF-TrFE) suspension, 0.6 g P(VDF-TrFE) powder was dispersed in 60 mL of isopropyl alcohol by ultrasonication for 60 min to break up agglomeration. Stainless steel substrates with dimensions of 1 mm × 10 mm × 40 mm were used for both the cathode and the anode. Prior to the EPD experiment, the stainless steel substrates were cleaned with acetone, ethanol, and distilled water in an ultrasonic bath for 10 min, respectively. The deposition area was fixed as 10 mm × 20 mm, and the electrodes were separated by 10 mm. The EPD parameters, such as the applied voltage and the deposition time, were varied from 10 to 50 V and from 30 s to 10 min, respectively. A constant electric voltage was applied by a power supply (Glasman High Voltage, Inc). The obtained electrophoretic deposits were dried in air at room temperature for 100 min and weighed by an electric balance with an accuracy of 0.0001 g. The current density was recorded by a digital multimeter attached in series during the EPD process.

Characterization

The zeta potential of the suspension was estimated from the electrophoretic mobility measured using a zeta potential analyzer (Otsuka Electronics, ELS-Z2). The surface morphology was observed by scanning electron microscopy (SEM, S-4800, Hitachi). The film thickness was measured by an Alpha-step 500 surface profilometer (Tencor instruments). The formation of the ferroelectric β-phase in P(VDF-TrFE) films was confirmed by X-ray diffraction (XRD) (Rigaku D/Max-2500) and Fourier transform infrared (FTIR) spectroscopy in the attenuated total reflection mode (Bruker, IFS66V/S & HYPERION 3000) with a scanning resolution of 2 cm−1. The polarization-electric field (P-E) hysteresis loop was measured using a virtual-ground technique using an RT66A test system (Precision, RT-66A) equipped with a high-voltage amplifier (Trek Inc.). The output voltage of the spring type energy harvesters was monitored by a digital oscilloscope (DPO3034, Tektronix, Inc.). Input resistance and capacitance at the probe tip were 10 MΩ and <8 pF, respectively.

Additional Information

How to cite this article: Ryu, J. et al. Synthesis and Application of Ferroelectric Poly(Vinylidene Fluoride-co-Trifluoroethylene) Films using Electrophoretic Deposition. Sci. Rep. 6, 36176; doi: 10.1038/srep36176 (2016).

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

References

  1. 1.

    et al. All-polymer ferroelectric transistor, Appl. Phys. Lett. 87, 092903 (2005).

  2. 2.

    et al. Flexible dome and bump shape piezoelectric tactile sensors using PVDF-TrFE copolymer. J. Microelectromech. Syst. 17, 334–341 (2008).

  3. 3.

    , & High-performance micromachined unimorph actuators based on electrostrictive poly(vinylidene fluoride–trifluoroethylene) copolymer. Appl. Phys. Lett. 80, 1082 (2002).

  4. 4.

    et al. Ferroelectric nanodot formation from spin-coated poly(vinylidene fluoride-co-trifluoroethylene) films and their application to organic solar cells. J. Appl. Polym. Sci. 132, 41230 (2015).

  5. 5.

    , , , & The energy harvesting Eel: A small subsurface ocean/river power generator. IEEE J. Oceanic Eng. 26, 539–547 (2001).

  6. 6.

    et al. The effects of an alkaline treatment on the ferroelectric properties of poly(vinylidene fluoride trifluoroethylene) films. Electron. Mater. Lett. 11, 586–591 (2015).

  7. 7.

    & Ferroelectric nanomesa formation from polymer Langmuir-Blodgett films. Appl. Phys. Lett. 85, 3528 (2004).

  8. 8.

    et al. A spring-type piezoelectric energy harvester RSC Adv. 3, 3194–3198 (2013).

  9. 9.

    et al. Facile preparation of ferroelectric poly(vinylidene fluoride-co-trifluoroethylene) thick films by solution casting. Polym. Eng. Sci. 54, 466–471 (2013).

  10. 10.

    , & Electrophoretic deposition: From traditional ceramics to nanotechnology. J. Eur. Ceram. Soc. 28, 1353–1367 (2008).

  11. 11.

    & A review on fundamental and applications of electrophoretic deposition (EPD). Prog. Mater. Sci. 52, 1–61 (2007).

  12. 12.

    , & Surface enhanced Raman spectroscopy on silver-nanoparticle-coated carbon-nanotube networks fabricated by electrophoretic deposition. Electron. Mater. Lett. 10, 325–335 (2014).

  13. 13.

    & Uniform film of conjugated polymer for light-emitting device by electrophoretic deposition. J. Phys. D: Appl. Phys. 41, 032001 (2008).

  14. 14.

    , & Structural ceramic microlaminates by electrophoretic deposition. J. Am. Ceram. Soc. 75, 2907–2909 (1992).

  15. 15.

    , , , & Electrophoretic deposition of biomaterials. J. R. Soc. Interface 7, S581–S613 (2010).

  16. 16.

    , & Rapid and multi-step, patterned electrophoretic deposition of nanocrystals using electrodes covered with dielectric barriers. Appl. Phys. Lett. 104, 053113 (2014).

  17. 17.

    & Hydroxyapatite-anatase-carbon nanotube nanocomposite coatings fabricated by electrophoretic codeposition for biomedical applications. Zhang, B. & Kwok, C. T. J. Mater. Sci: Mater. Med. 22, 2249–2259 (2011).

  18. 18.

    , & (Pb, La)(Zr, Ti)O3 films by multiple electrophoretic deposition/sintering processing. Jpn. J. Appl. Phys. 30, 2170–2173 (1991).

  19. 19.

    & Electrophoretic deposition of ferroelectric thin films. Ferroelectrics 187, 57–73 (1996).

  20. 20.

    , & Hydrothermal and electrophoretic deposition of lead zirconate titanate (PZT) films. J. Eur. Ceram. Soc. 21, 1539–1542 (2001).

  21. 21.

    , & Ceramic processing strategies for thick films on copper foils. Acta Mater. 58, 2282–2290 (2010).

  22. 22.

    et al. Sodium potassium niobate (K0.5Na0.5NbO3, KNN) thick films by electrophoretic deposition. RSC Adv. 5, 4698–4706 (2015).

  23. 23.

    & Electrophoretic deposition and characterization of micrometer-scale BaTiO3 based X7R dielectric thin films. J. Am. Ceram. Soc. 83, 2417–2422 (2000).

  24. 24.

    & Fabrication of barium titanate ferroelectric layers by electrophoretic deposition. Mater. Chem. Phys. 79, 226–229 (2003).

  25. 25.

    & Fabrication and electricmechanical characterization of a piezoelectric structural fiber for multifunctional composites. Adv. Funct. Mater. 19, 592–598 (2009).

  26. 26.

    et al. Preparation and electric properties of BiFeO3 film by electrophoretic deposition. J. Alloys Comp. 605, 21–28 (2014).

  27. 27.

    , , & Electrophoretic deposition and characterization of helical piezoelectric actuator. Ceram. Inter. 34, 1–6 (2008).

  28. 28.

    & Lead zirconate titanate films on metallic substrates by electrophoretic deposition. Mater. Sci. Eng. B, 116, 208–214 (2005).

  29. 29.

    & Proc. Of 201st Meeting of The Electrochemical Society, Philadephia, 2002.

  30. 30.

    et al. Fabrication of chromium (III) oxide (Cr2O3) coating by electrophoretic deposition. J. Am. Ceram. Soc. 97, 3413–3417 (2014).

  31. 31.

    , & Electrophoretic deposition and constrained sintering of strontium titanate thick films. Mater. Chem. Phys. 149, 445–452 (2015).

  32. 32.

    , & Synthesis and microstructural manipulation of ceramics by electrophoretic deposition. J. Mater. Sci. 39, 819–823 (2004).

  33. 33.

    , , & Polyetheretherketone (PEEK) coatings on stainless steel by electrophoretic deposition. Adv. Eng. Mater. 10, 559–563 (2008).

  34. 34.

    et al. Nanoscale piezoresponse of 70 nm poly(vinylidene fluoride-trifluoro-ethylene) films annealed at different temperatures. Phys. Status Solidi RRL, 4, 94–96 (2010).

  35. 35.

    , & Infrared spectra and ferro-electricity of ultra-thin films of vinylidene fluoride and trifluoroethylene copolymer. Polym. Int. 56, 1254–1260 (2007).

  36. 36.

    , & Effect of thickness on the crystallinity and curie transition behavior in P(VDF/TrFE)(72:28) copolymer thin films using FTIR-transmission spectroscopy. Vib. Spectroc. 49, 101–109 (2009).

  37. 37.

    , , & Polarized Raman spectra and LO-TO splitting of poly(vinylidene fluoride) crystal form I. Macromolecules, 18, 2600–2606 (1985).

  38. 38.

    , , , & Selective current collecting design for spring-energy harvesters. RSC Adv. 5, 10662–10666 (2015).

Download references

Acknowledgements

This research was supported by the Mid-career Researcher Program (No. 2010-0015063) and Conversion Research Center Program (No. 2011K000674) through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (MEST) and Basic Science Research Program (No. 2015R1D1A1A01056983) through the National Research Foundation of Korea (NRF) funded by the Ministry of Education. Work at Argonne National Laboratory (S.H., data analysis and contribution to writing of manuscript) was supported by Laboratory Directed Research and Development (LDRD) funding from Argonne National Laboratory, provided by the Director, Office of Science, of the U.S. Department of Energy under contract DE-AC02-06CH11357.

Author information

Affiliations

  1. Department of Materials Science and Engineering, Korea Advanced Institute of Science and Technology, Daejeon 34141, Republic of Korea

    • Jeongjae Ryu
    • , Kwangsoo No
    • , Yeontae Kim
    •  & Seungbum Hong
  2. Materials and Energy Science and Engineering, Nelson Mandela African Institute of Science and Technology, Arusha 447, Tanzania

    • Eugene Park
  3. Materials Science Division, Argonne National Laboratory, Lemont, Illinois 60439, USA

    • Seungbum Hong

Authors

  1. Search for Jeongjae Ryu in:

  2. Search for Kwangsoo No in:

  3. Search for Yeontae Kim in:

  4. Search for Eugene Park in:

  5. Search for Seungbum Hong in:

Contributions

J.R. and S.H. conceived and designed the experiments. J.R. and Y.K. performed electrophoretic deposition experiments. J.R. and S.H. wrote the main manuscript text. All authors including J.R., K.N., Y.K., E.P. and S.H. discussed the results and commented on the manuscript.

Competing interests

The authors declare no competing financial interests.

Corresponding authors

Correspondence to Kwangsoo No or Seungbum Hong.

Supplementary information

About this article

Publication history

Received

Accepted

Published

DOI

https://doi.org/10.1038/srep36176

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.