Figure 7

From: Stability of retained austenite in high carbon steel under compressive stress: an investigation from macro to nano scale

Figure 7

EBSD measured KAM plots showing dislocation density in martensite and austenite structures in samples (a) before compression and after compression with (b) 500 MPa, (c) 1500 MPa, (d) 2000 MPa and (e) 2500 MPa load. Misorientation boundaries over 15° are plotted in black lines.