Abstract
In present work, the nano- and microscale tetrapods from zinc oxide were integrated on the surface of Aerographite material (as backbone) in carbon-metal oxide hybrid hierarchical network via a simple and single step magnetron sputtering process. The fabricated hybrid networks are characterized for morphology, microstructural and optical properties. The cathodoluminescence investigations revealed interesting luminescence features related to carbon impurities and inherent host defects in zinc oxide. Because of the wide bandgap of zinc oxide and its intrinsic defects, the hybrid network absorbs light in the UV and visible regions, however, this broadband photoabsorption behavior extends to the infrared (IR) region due to the dependence of the optical properties of ZnO architectures upon size and shape of constituent nanostructures and their doping by carbon impurities. Such a phenomenon of broadband photoabsorption ranging from UV to IR for zinc oxide based hybrid materials is novel. Additionally, the fabricated network exhibits strong visible light scattering behavior. The developed Aerographite/nanocrystalline ZnO hybrid network materials, equipped with broadband photoabsorption and strong light scattering, are very promising candidates for optoelectronic technologies.
Similar content being viewed by others
Introduction
Hybrid nanomaterials in the form of combination of several components equipped with different individual nanoscale features are very important material candidates from an application point of view because, in hybrid form, most of the desired properties are accumulated together, often resulting in the occurrence of entirely new characteristics1,2,3,4. Due to multifunctional properties, hybrid materials are leading the trends in materials synthesis and application communities1,3,4,5,6,7. Looking on their future technological potentials, many new strategies for fabricating various hybrid nanomaterials are being introduced and accordingly investigations are continuing, but this field still has to come up with further cost-effective approaches which can offer simple and mass-scale fabrication of desired materials in appropriate hybrid forms. At the same time, it is also important to overcome the utilization complexities related to the requirement of nanostructure’s integration on the micro-chip, e.g., focused ion beam, lithography, etc., have been mainly used to develop electronic devices based on individual nanowires8,9,10,11,12,13. To efficiently utilize the excellent nanoscale features, three-dimensional (3D) forms of nanomaterials are the most appropriate candidates and currently significant efforts are being undertaken for the purpose of fabricating different types of 3D nanomaterials, from inorganic components14,15,16,17,18, carbon/graphene8,9,10,11,12,19,20, and others along with their wide range of applications. The appropriate combination of inorganic and carbon materials in 3D architectures is very attractive, because, in this form, the important properties of all the nanoscale counterparts become easily accessible8,9,10,11,12,19,20. Although 3D nanomaterials, in the form of porous interconnected networks built from nanoscopic building blocks, are very relevant with respect to different technological applications, their cost-effective fabrication using simple processing steps is still an open issue, normally it requires complicated bottom-up or top-down strategies21,22. In contrast to conventional lithography techniques, recently a new approach based on flame synthesis has been introduced and it offers very simple and mass scale fabrication of highly porous 3D interconnected ceramic zinc oxide (ZnO) networks23,24. This flame based strategy involves direct synthesis of zinc oxide nano- and microscale tetrapods from metallic zinc microparticles in flame via solid-vapor-solid growth process25 and these tetrapod structures have already demonstrated their application potentials in various advanced technologies26,27,28,29,30,31.
From metal oxides family, ZnO is one of the most studied semiconductor compounds, and the number of publications devoted to this material continues to increase with time, especially those related to low-dimensional structures such as nanodots, nanorods, nanobelts, nanotubes, nanotetrapods, nano-multipods etc. Along with the industrial applications related to piezoelectric properties of zinc oxide, nanocrystalline ZnO represents a valuable perspective material for a variety of other applications32,33. An important emerging practical use of ZnO nanomaterial is related to biomedical applications, e.g., bioimaging, biosensing, drug delivery, gene delivery, antimicrobial effect, stimulation or inhibition of biological processes in living systems, from single cells to humans34,35. Over the recent years, various approaches have been applied for the purpose of building hierarchical three-dimensional nano-ZnO architectures with enhanced photocatalytic, photoelectric and gas-sensing performances, e.g., soft-chemical approach36,37, hydrothermal synthesis18,38,39, electrodeposition17, chemical vapour deposition40, thermal evaporation41,42, etc. In particular, Liu et al.42 thermally deposited the zinc oxide on bundles of the graphite fibers with the average diameter of 7 μm. As a result, the formation of graphite fiber/ZnO core-shell structures was realized, the ZnO shell consisting of microtubes was covered by rods with ~400 nm diameter and ~5-μm length. Later, these researchers succeeded in fabricating hollow ZnO microtube-nanorod structures by oxidizing the central graphitic fiber in air at 800 °C for 20 min42. In contrast to above mentioned synthesis process, the present flame based approach offers a simple 3D nanostructuring using ZnO tetrapods and these networks can be further functionalized with other metal oxides for multifunctional applications23,24 including fabrication of new varieties of 3D networks, for example, the carbon based highly porous 3D Aerographite (AG) material43 and its other variants in form of GaN-Aerographite hybrid networks44.
Stretchable materials equipped with interesting functionalities from nanoscale inorganic materials are becoming more and more important because of their interesting applications, for example, in bendable sensing devices and artificial skin45, etc., and they can be easily fabricated by using appropriate templates with desired porosity and flexibilities. Being very light in weight, extremely porous (>99.95%), and mechanically stable enough, these carbon based Aerographite networks could be used to fabricate smart 3D nanomaterials where functionalities and stretchability are simultaneously desired, e.g., in flexible 3D luminescent elements. Additionally, it is necessary to emphasize here, that even if the entire surface of Aerographite network is coated with inorganic nano- and microstructures, for example, GaN nanocrystals, etc., the resulting hybrid networks still retain a high degree of flexibility44 which is of paramount importance for many applications. Very recently, advanced scattering elements have received significant attention due to the upcoming developments in modern lighting technologies based on light emitting devices and laser diodes. If the Aerographite networks can be decorated with appropriate inorganic nanostructures having very high surface area in hybrid 3D form, the light scattering behaviour can then be simply tuned by compressing/expanding the hybrid network which could be useful for large range of optoelectronic or photodetector applications. Accordingly, here we report on the formation of hierarchical 3D Aerographite/nanocrystalline ZnO (AG/ZnO) architectures as a result of zinc oxide deposition on flexible Aerographite scaffolds by using RF magnetron sputtering techniques, and demonstrate that this hybrid 3D nanomaterial exhibits significant technological perspectives in terms of optical properties such as light emission, broadband photo-detection, and light scattering behaviour.
Results and Discussion
Figure 1(a) illustrates schematically an individual Aerographite micro-tetrapod before and after deposition of ZnO nanoscale tetrapods, while Fig. 1(b,c) shows the morphology of the as-grown Aerographite and of the Aerographite/ZnO hybrid nanomaterial. Aerographite represents an ultra-light weight, extremely porous, mechanically flexible, graphite based 3D network built from interconnected struts of hollow graphite tubes with micrometer-scale diameters and a nanoscopic (~15 nm) wall thickness43. The previous investigations44 carried out on Aerographite-GaN hybrid networks demonstrated that the Aerographite scaffold can sustain high loading densities of semiconductor nano-and microcrystallites on its huge specific surface without visible structural deformations.
The evolution of the morphology and micro-structure of the deposited ZnO nanostructures with respect to the duration of RF magnetron sputtering was studied by scanning electron microscopy (SEM) and the corresponding results are illustrated in Fig. 2(a–i). A 10 nm thick film deposition at 90 °C with subsequent heat treatment of the specimens at 490 °C results in the formation of nanoscopic crystallites from ZnO which are clearly seen in high resolution SEM image, see Fig. 2(c). With increase of the deposition time, the outer surface of the Aerographite microtubes in the network gets homogenously covered with a continuous film of nanocrystalline ZnO, see Fig. 2(d–f). It is evident from Fig. 2(f), that the deposited 150 nm thick ZnO film exhibits a nano-granular structure with the average nanocrystal size of about 100 nm.
Deposition of films with the thickness greater than or equal to 1 μm is accompanied by considerable changes in the morphology and micro-structure of the deposited ZnO layers (Fig. 2(g–i)). In such cases the outer part of the deposited ZnO film appears to be highly porous, mainly due to the formation of sub-micrometer-scale ZnO tetrapods, see the high-resolution image in Fig. 2(i). Note that the diameter of the tetrapod arms is of ~100 nm or less. Interestingly, long duration ZnO deposition with subsequent heat treatment of specimens at 490 °C leads to the formation of micron-scale tetrapods weakly bound to the Aerographite/ZnO hybrid architecture which leads to the possibility of detaching the ZnO nano- and micro-tetrapods and gathering them on a foreign substrate by simply shaking up the as-prepared AG/ZnO network (Supplementary Information, Figure S1). The tetrapod growth is initiated by the emergence of a nucleus with subsequent formation of four arms and the nature of nuclei depends upon the involved synthesis process. The growth mechanism of ZnO nano- and microscale tetrapods by different synthesis processes is already a long discussed topic in the literature25,46,47,48. The present results pave the way for the controlled fabrication of micrometer-scale ZnO tetrapods with sub 100 nm thickness of the constituent arms. It is worth mentioning in this regard, that the dimensions of the initial ZnO tetrapods/multipods used to fabricate the Aerographite network were of several tens of micrometers, the transverse dimensions of the constituent arms being of micrometer scale43. As in the case of GaN deposition44, the Aerographite network sustains a high amount of loading of nanocrystalline ZnO, in spite of the relatively thin nanoscopic walls (~15 nm thick) of the constituent graphitic microtubular architecture. In contrast to previously reported deposition of GaN on both the inner and outer surface of AG tubes44, the present results show that the ZnO deposition takes place only on the outer surface of graphitic microtubular structures.
The crystallinity of the ZnO deposited on the Aerographite scaffold was studied by micro-Raman scattering techniques. Note that the Raman spectrum of bulk wurtzite-type ZnO is characterized by the following Raman-active phonon modes: A1(TO) at 379 cm−1; E1(TO) at 410 cm−1; E2(high) at 439 cm−1 and E1(LO) at 591 cm−1 49. According to the micro-Raman results (see Figure S2, Supplementary Information), the vibrational modes mentioned above are inherent also to nanocrystalline ZnO deposited on the Aerographite network. The redshift of the LO peak in nanocrystalline ZnO in comparison with bulk ZnO can be attributed to local heating induced by the focused laser beam from Raman instrument. Local heating is also responsible for the observed red shift of the E2(high) mode in nanocrystalline ZnO (438.1 cm−1) in comparison to that of bulk ZnO. The two additional Raman peaks at low-frequencies of ~278 and 331 cm−1 are most likely attributed to the second order Raman processes involving acoustic phonons50,51. The deposited ZnO nanostructures in the present AG/ZnO hybrid network basically exhibit tetrapod morphology and it is important to mention here that previous studies, including those discussing the models of tetrapod growth, have demonstrated the wurtzite crystal structure of ZnO nanorods constituting the arms of ZnO tetrapods52. At the same time, the wurtzite structure of ZnO nanorods has also been confirmed by detailed X-ray diffraction, high resolution transmission electron microscopy and selected area electron diffraction studies25.
Taking into account that ZnO is an important optoelectronic material, detailed cathodoluminescence investigations on AG/ZnO 3D architectures have been performed. Figure 3(a) illustrates the SEM image and panchromatic CL image taken from a fragment of AG/ZnO network after deposition of 10 nm thick layer at 90 °C with subsequent heat treatment of the specimen at 490 °C, while Fig. 3(b,c) show the SEM images and the colour-composite (360 + 400 + 525) nm CL images taken from AG/ZnO hybrids with the thickness of the deposited ZnO layer of ~150 nm and ~1 μm, respectively. The analysis of CL spectra demonstrated in Fig. 3(d–f) is indicative of several stages of the formation of ZnO nano/micro-structures on the Aerographite scaffold. In the very first stage, the ZnO nanodots are formed at the interface, as shown in Fig. 3a. These nanodots as well as the interfacial layer are highly doped with carbon. The microstructural analysis suggests that the interfacial layer comprises ZnO and Carbon in form of a two phase nanocomposite material. A very weak and broad CL band is emitted from ZnO nanodots and interfacial layer in the visible range, as shown in Fig. 3d. With increasing the thickness of the ZnO granulated layer, the level of doping with carbon decreases and emission in the UV region emerges in the spectrum, as observed in Fig. 3e. The ratio of the UV to visible emission increases in the upper ZnO layer formed of nanotetrapods. This indicates the decrease in the level of doping with increasing distance from the Aerographite/ZnO interface, which can be attributed to the limited diffusion of carbon.
The analysis of the CL spectrum in Fig. 3e shows that the UV and violet emission consists of two bands located at ~3.28 eV and ~3.1 eV, while the emission in the visible range is composed of at least two bands with maxima around 1.8–1.9 eV and 2.2–2.3 eV, respectively. With increasing the thickness of the deposited ZnO layer, the emission band at 3.1 eV vanishes, while the relative intensity of the red band at 1.8–1.9 eV decreases substantially (Fig. 3f). It has been previously observed that the UV band at ~3.28 eV represents a superposition of the zero-phonon line and the phonon replicas of the free exciton emission41. The presence of the free exciton emission is indicative of the high crystalline quality of the ZnO nanotetrapods. As far as the emission band at 3.1 eV is concerned, the luminescence in this region was previously suggested to appear from recombinations involving the Zn interstitials (Zni) with the maximum at ~2.9 eV, or Zn vacancies (VZn) with the maximum at ~3.06 eV53. In addition, a blue and violet luminescence band around ~3.0 eV has been observed in carbon modified ZnO nanoparticles, and this emission is attributed to the carbon adsorbed at the O2− vacancies existing in large quantities at the ZnO nanoparticles surfaces, therefore creating carbon substitution of oxygen (CO)54. It has been suggested that the blue/violet emission may originate from the recombination of the electron in the conduction band or in a shallow donor with the CO acceptor. The carbon enhanced blue/violet luminescence at ~3 eV has also been observed in ZnO films grown by pulsed laser deposition techniques55. Note that similar blue/violet emission was reported for GaN doped with carbon which was assigned to CN acceptor56.
On the basis of the literature reports57,58,59,60,61, the luminescence band at ~2.9 eV is most likely due to Zn interstitials and the band at ~3.06 eV is associated to Zn vacancies. It has been concluded that the carbon impurities promote the zinc related native defects in ZnO and may also generate radiative recombination channels due to the carbon impurity incorporated in the ZnO lattice. Therefore, the following defects can be considered as the origin of the blue/violet emission from ZnO nanoparticles: Zni, VZn, and CO. However, the Zn interstitials have high formation energies in n-type ZnO57. In addition, these defects are unstable at room temperature58,59, and are easily annealed even below room temperature (at ~170 K)60. According to the McCluskey et al.59, the Zn vacancies are most probably responsible for the observed green emission at ~2.35 eV61, rather than for the blue/violet emission. The absence of the CL band at ~3.1 eV in the less doped nanoscale ZnO tetrapods in comparison with the highly carbon doped ZnO nanogranular layer closer to the Aerographite/ZnO interface, corroborates the suggestion that CO defects are a source of the blue/violet emission in this AG/ZnO hybrid nanomaterial.
The CL band at ~1.9 eV also seems to be related to the carbon impurity, in the form of a complex defect 2CO-VO-Zni with an energy level situated 1.9 eV below the conduction band of ZnO, according to the theoretical calculations by Lu et al.62. The green emission at ~2.3 eV does not seem to be influenced by carbon doping in AG/ZnO hybrid samples, since the ratio of its intensity to the intensity of the excitonic emission at ~3.28 eV is practically the same in ZnO nanotetrapods and in ZnO nanograins (comparing Fig. 3e,f). In this respect, the emission at ~2.3 eV can be attributed to the intrinsic defects, most probably to zinc vacancies as described above. Although it was believed in previous investigations that the green emission in ZnO is associated with Cu impurities63,64,65,66, oxygen vacancies67,68,69,70,71,72,73, or oxygen antisites53,74, the analysis carried out later by McCluskey et al., demonstrated that the green PL is not due to O vacancies59. The broad CL absorption band corresponding to Fig. 3f was deconvoluted into several peaks (shown in Figure S3, Supplementary Information) and they are in good agreement with the mentioned defect levels within the ZnO bandgap. It is worth noting here that defects such as O antisites, Zn antisites, and O interstitials have high formation energies, and therefore are probably not present in significant concentrations under normal conditions59. Figure 4 presents a scheme of defect levels responsible for CL bands observed in AG/ZnO hybrid nanomaterials.
Deposition of relatively thick nanostructured ZnO layers on Aerographite tubular networks results in the formation of hybrid nanomaterial with enhanced optical properties. Figure 5(a) presents a fragment of the Aerographite tetrapod-like structure covered by ZnO nano- and microtetrapods, while Fig. 5(b,c) show color-composite μ-CL images: (525 + 675) nm in (b), and (360 + 400 + 525) nm in (c). It has been found that the Aerographite/ZnO hybrid sample exhibits strong scattering of electromagnetic radiation in the whole visible region. Figure 5(d) illustrates the scattering of green light generated by a laser pointer. The reason for such strong scattering is obviously the correlation of the light wavelength with the dimensions of the deposited ZnO nano- and microtetrapods. Aerographite network does not exhibit any light scattering behavior (it is perfectly black and everything gets absorbed on it) and hence the observed large scattering of green light is mainly a contribution from complex shaped ZnO nano- and microscale tetrapods with very high surface area and large number of edges deposited over Aerographite scaffolds. Note that strong scattering usually leads to enhanced optical absorption in the medium due to the increase of the optical path of the electromagnetic radiation.
Photodetection is an important application of most of the wide bandgap metal oxide semiconductor nanostructures but they are mainly prone to exhibit current sensitivity in ultraviolet (UV) region26,75. However, it will be very helpful if the photodetection range of these materials is broadened which could be possible when they are in appropriate hybrid form. In order to investigate the photodetection, an Aerographite/ZnO hybrid network based electronic device was fabricated (device fabrication concept in Figure S4, Supplementary Information) and it’s current-voltage (I-V) characteristics (given in Figure S5, Supplementary Information) have been measured under different environmental (in dark/light, air/vacuum) conditions which reveals its strong sensitivity to surrounding environments. The resulting current switching behavior, shown in Fig. 6, demonstrates that the Aerographite/ZnO hybrid nanomaterial exhibits strong photosensitivity in a wide spectral range from the ultraviolet to infrared (UV to IR) wavelengths. ZnO nanomaterials typically exhibit photodetection behavior in the range from UV to visible region but the present AG/ZnO hybrid material shows interesting switching behavior in the infrared region too (up to around 2.5 μm) and therefore our material has the potential to be utilized as the universal photodetector device (which is not in general common for wide bandgap semiconductors based devices). It seems that different layers of the hybrid nanomaterial are responsible for observed cathodoluminescence and broadband (UV to IR) photoconductivity (PhC) behaviors. The main CL signal is emitted from the upper tetrapod layer with a higher crystalline quality, while the lower granular layers, including that at the interface with the Aerographite scaffold, are responsible for the PhC, since the granular morphology ensures the percolation pathway of current through the material. On the other hand, the huge surface-to-volume (S/V) ratio of the nanomaterial suggests the importance of surface effects and that of oxygen molecules in the photoconductivity. It is generally believed that adsorption (in the dark) and desorption (under UV illumination) of oxygen molecules govern the photoresponse of ZnO in air76,77,78,79,80. In the dark, free electrons of the n-type semiconductor are captured by the oxygen molecules adsorbed on the surface of ZnO nanograins: O2(g) + e− → O2−(ad). In consequence of this, a depletion layer appears in the immediate vicinity of the nanograin surface, resulting in an upward band bending near the surface. When the material is characterized by large surface-to-volume ratio, the adsorption of O2 significantly reduces its electrical conductivity. Excitation of ZnO by UV quanta with energies greater than Eg generates electron–hole pairs. Holes migrate to the surface along the potential slope caused by the band bending and recombine with O2-trapped electrons, thus releasing oxygen from the surface: O2−(ad) + h+ → O2(g). The unpaired electrons are either collected at the anode or recombine with holes generated when oxygen molecules are re-adsorbed and ionized at the surface.
It is clear from Fig. 6 that the conductivity in air is lower in comparison to that measured under reduced pressure (Figure S5, Supplementary Information). Cammi et al.81, recently explained a similar decrease as being associated with the adsorption of oxygen on the ZnO surface and trapping of electrons from the conduction band81. The photoconductivity is also higher under reduced pressure which is an indication that the exploitation of broadband photodetectors on the basis of AG-ZnO hybrid material in various devices, for instance in flame alarm systems or high-performance liquid chromatography devices, is even more favorable under vacuum. However, one should take into account additional costs related to evacuation and encapsulation of device structures.
The fact that the photoconductivity induced in the samples investigated here is not only due to the UV irradiation, but also due to the visible and near-infrared light irradiation, can be explained by the presence of a large amount of defect-induced energy levels within the ZnO bandgap which could also form extended band-edge tails of the density of states. As discussed above, the granular layer and the interfacial layer are highly doped with carbon, which can explain the generation of electron–hole pairs by radiation with a large spectrum of wavelengths. It is necessary to mention here that the pure Aerographite network does not exhibit any current switching behavior (Figure S6, Supplementary Information) with respect to wide range of light wavelengths (UV, white LED, white halogen lamp) and therefore the observed broadband photoswitching from the hybrid AG-ZnO network based device is mainly due to the presence of ZnO nano- and microstructures. So far the photoabsorption in ZnO has been mainly explained in terms of defects but other optical effects like whispering gallery modes (WGMs), second harmonic generation (SHG), etc. could also contribute to the broad (visible to infrared) photoabsorption. The WGM mainly depends upon the size and shape of the ZnO nano- and microstructures and WGM resonances lead to additional peaks over the broad ZnO defect luminescence peak82,83. The CL spectrum of AG-ZnO hybrid material does exhibit some additional peaks over broad ZnO defect peak which could be due to WGM resonances but further investigations are required for the explicit disclosure of their origin. As to the nonlinear optical properties, they depend upon the size of ZnO nano- and microstructures, crystalline quality, surface defects, grain boundaries as well as impurities84,85, and their contribution to the observed broadband photoabsorption in present AG-ZnO hybrid network cannot be ignored. Irrespective of the deep understanding of the origins, characteristic features of the stretchable AG-ZnO hybrid network material like tunable scattering of light and broadband (UV to IR) photoabsorption are technologically very promising for advanced optoelectronic applications.
Conclusion
In summary, our research demonstrates that Aerographite/ZnO hybrid nanomaterials with varying ZnO morphologies, i.e. from nanocrystallites to nanotetrapods on extremely porous and highly flexible Aerographite scaffolds, can be easily fabricated by controlled deposition of ZnO in a simple and cost-effective technological process. The deposition time also enables the controlled modification of light emission properties of the 3D hybrid architectures as evidenced by the detailed cathodoluminescence investigations. The difference in luminescence properties of wurtzite ZnO thin layers is discussed in detail in terms of native defects, free excitons, and carbon doping from the AG network which is also in agreement with Raman scattering analysis. The photosensitivity of the hybrid material is explained by the adsorption (in the dark) and desorption (under illumination) of oxygen molecules to/from the ZnO surface, while the broadband photoabsorption occurs mainly due to the presence of a large amount of defect levels in the material bandgap, which may also form extended band-edge tails of the density of states in the ZnO layer in close proximity to the Aerographite scaffold. The material with relatively thick nanostructured ZnO layers obtained after long duration deposition exhibits enhanced optical properties, such as strong scattering due to the correlation of the light wavelength with the dimensions of the deposited ZnO nanotetrapods, and enhanced optical absorption in the medium caused by the light trapping, i.e., increased optical path of the electromagnetic radiation. The proposed strategy provides a cost-effective method for the fabrication of nano- and micrometer scale ZnO tetrapods with sub 100 nm arm thickness which can be easily detached from the hybrid architecture, while the resultant stretchable hybrid material could be very promising for optoelectronic technologies.
Materials and Methods
The Aerographite networks have been synthesized by the one step chemical vapor deposition (CVD) process on metal oxide porous ceramic templates as described in a previous investigation43. Highly porous ceramic networks with a 3D architecture, which are entirely built up from interconnected micrometer-scale thick rods, often in the shape of tetrapods and multipods, are used as sacrificial templates23. The as-grown Aerographite networks have been used as templates for the growth of nanocrystalline ZnO by using RF magnetron sputtering method in a high vacuum chamber equipped with turbomolecular and mechanical pumps. The Aerographite template was mounted on a rotary support, and the distance from the target to the template was 8 cm. The base pressure was about 5 × 10−5 Pa, and the flow rate of Ar was kept at a constant value of 60 mL/min controlled by a mass flow controller. A disc of 99.99% pure zinc served as metal target for sputtering. The template temperature measured by using a chromel-alumel thermocouple was 90 °C. The AG scaffold was rotating during sputtering to provide conditions for uniform deposition of ZnO. The deposited film thickness was controlled during sputtering by using a MTM-10/10A high resolution thickness monitor quartz microbalance. After the deposition process, the specimens were annealed at 490 °C for 60 minutes in an oxygen atmosphere with a gas flow of ∼100 ml/min.
The morphology of AG/ZnO hybrid networks were investigated using scanning electron microscopes Zeiss Ultra Plus and VEGA TESCAN TS 5130MM. The compositional analysis of AG/ZnO networks was carried out using Energy Dispersive X-ray analysis (EDX), in combination with SEM. A JEOL 7001F Field Emission SEM equipped with a Gatan XiCLone CL microanalysis system was used for comparative morphological and CL characterization. The monochromatic CL images were collected using a Peltier cooled Hamamatsu R943-02 High Sensitivity Photomultiplier Tube. The CL spectra and images were generated from typical regions of the specimen using for excitation 10 keV, 10 nA electron beam. The CL spectra have been collected with a Princeton Instruments Pixis 100 UV optimized CCD. To carry out photoelectrical measurements, a 500 nm thick SnO2 film was deposited on top of ZnO layer by using RF magnetron sputtering approach described above. A target of SnO2 with 99.99% purity was used for this purpose. The frontal electrical contact was painted by conductive silver paste, while a transparent conductive oxide (TCO) served as rear contact. The schematic structure of TCO/aerographite/ZnO/SnO2/Ag specimen is illustrated in Supplementary Information, Figure S4.
Electromagnetic radiation from a Xenon lamp was used for the photoconductivity (PC) excitation. Optical filters were used to cut-off radiation from different spectral ranges (ultraviolet: 300–400 nm, power density at the sample surface 17.6 mW/cm2; visible 400–700 nm, power density 25.5 mW/cm2; and infrared 700–2500 nm, power density 134 mW/cm2). The current through the samples was measured by means of Keithley’s Series 2400 Source Measure Unit. Since the PC decay time is long enough, a mechanical shutter was used in the PC relaxation experiments. The signal from the Source Measure Unit was introduced in an IBM computer via IEEE-488 interface for further data processing.
Additional Information
How to cite this article: Tiginyanu, I. et al. Strong light scattering and broadband (UV to IR) photoabsorption in stretchable 3D hybrid architectures based on Aerographite decorated by ZnO nanocrystallites. Sci. Rep. 6, 32913; doi: 10.1038/srep32913 (2016).
References
Fahmi, A., Pietsch, T., Mendoza, C. & Cheval, N. Functional Hybrid Materials. Mater. Today 12, 44–50 (2009).
Wang, X., Chen, X., Thomas, A., Fu, X. & Antonietti, M. Metal‐Containing Carbon Nitride Compounds: A New Functional Organic–Metal Hybrid Material. Adv. Mater. 21, 1609–1612 (2009).
Fan, Z. et al. A Three Dimensional Carbon Nanotube/Graphene Sandwich and Its Application as Electrode in Supercapacitors. Adv. Mater. 22, 3723–3728 (2010).
Sanchez, C., Belleville, P., Popall, M. & Nicole, L. Applications of Advanced Hybrid Organic–inorganic Nanomaterials: From Laboratory to Market. Chem. Soc. Rev. 40, 696–753 (2011).
Parlak, O., Turner, A. P. & Tiwari, A. On/Off‐Switchable Zipper‐Like Bioelectronics on a Graphene Interface. Adv. Mater. 26, 482–486 (2014).
Tian, K., Alex, S., Siegel, G. & Tiwari, A. Enzymatic Glucose Sensor based on Au Nanoparticle and Plant-like ZnO Film Modified Electrode. Mater. Sci. Eng. C 46, 548–552 (2015).
Sharma, D. et al. Studies on Bacterial Proteins Corona Interaction with Saponin Imprinted ZnO Nanohoneycombs and Their Toxic Responses. ACS Appl. Mater. Interfaces 7, 23848–23856 (2015).
Tung, V. C. et al. Low-temperature Solution Processing of Graphene− carbon Nanotube Hybrid Materials for High-performance Transparent Conductors. Nano Lett. 9, 1949–1955 (2009).
Chen, W., Li, S., Chen, C. & Yan, L. Self‐Assembly and Embedding of Nanoparticles by In Situ Reduced Graphene for Preparation of a 3D Graphene/Nanoparticle Aerogel. Adv. Mater. 23, 5679–5683 (2011).
Wei, W. et al. 3D Graphene Foams Cross‐linked with Pre‐encapsulated Fe3O4 Nanospheres for Enhanced Lithium Storage. Adv. Mater. 25, 2909–2914 (2013).
Ananthanarayanan, A. et al. Facile Synthesis of Graphene Quantum Dots from 3D Graphene and Their Application for Fe3+ Sensing. Adv. Funct. Mater. 24, 3021–3026 (2014).
Dong, X. et al. 3D Graphene Foam as a Monolithic and Macroporous Carbon Electrode for Electrochemical Sensing. ACS Appl. Mater. Interfaces 4, 3129–3133 (2012).
Saini, S., Mele, P., Miyazaki, K. & Tiwari, A. On-chip Thermoelectric Module Comprised of Oxide Thin Film Legs. Energy Convers. Manage. 114, 251–257 (2016).
Vayssieres, L., Keis, K., Lindquist, S.-E. & Hagfeldt, A. Purpose-built Anisotropic Metal Oxide Material: 3D Highly Oriented Microrod Array of ZnO. J. Phys. Chem. B 105, 3350–3352 (2001).
Shi, J., Grutzik, S. & Wang, X. Zn Cluster Drifting Effect for the Formation of ZnO 3D Nanoarchitecture. ACS Nano 3, 1594–1602, doi: 10.1021/nn900388z (2009).
Joshi, R. K. & Schneider, J. J. Assembly of one dimensional inorganic nanostructures into functional 2D and 3D architectures. Synthesis, arrangement and functionality. Chem. Soc. Rev. 41, 5285–5312 (2012).
Wu, K. & Cui, J. Electrodeposition of 3D Hierarchical ZnO Nanoflowers and Their Optical Properties. ECS Solid State Lett. 2, R1–R4 (2013).
Alenezi, M. R., Henley, S. J., Emerson, N. G. & Silva, S. R. P. From 1D and 2D ZnO Nanostructures to 3D Hierarchical Structures with Enhanced Gas Sensing Properties. Nanoscale 6, 235–247 (2014).
Jiang, H., Lee, P. S. & Li, C. 3D Carbon based Nanostructures for Advanced Supercapacitors. Energy Environ. Sci. 6, 41–53 (2013).
Cao, X. et al. Preparation of Novel 3D Graphene Networks for Supercapacitor Applications. Small 7, 3163–3168 (2011).
Cheung, K. C. & Gershenfeld, N. Reversibly Assembled Cellular Composite Materials. Science 341, 1219–1221 (2013).
Jang, D., Meza, L. R., Greer, F. & Greer, J. R. Fabrication and Deformation of Three-dimensional Hollow Ceramic Nanostructures. Nat. Mater. 12, 893–898 (2013).
Mishra, Y. K. et al. Fabrication of Macroscopically Flexible and Highly Porous 3D Semiconductor Networks from Interpenetrating Nanostructures by a Simple Flame Transport Approach. Part. Part. Syst. Charact. 30, 775–783 (2013).
Gröttrup, J. et al. Three-dimensional Flexible Ceramics based on Interconnected Network of Highly Porous Pure and Metal Alloyed ZnO Tetrapods. Ceram. Int. 42, 8664–8676 (2016).
Mishra, Y. K. et al. Direct Growth of Freestanding ZnO Tetrapod Networks for Multifunctional Applications in Photocatalysis, UV Photodetection, and Gas Sensing. ACS Appl. Mater. Interfaces 7, 14303–14316 (2015).
Gedamu, D. et al. Rapid Fabrication Technique for Interpenetrated ZnO Nanotetrapod Networks for Fast UV Sensors. Adv. Mater. 26, 1541–1550 (2014).
I. Hölken, M. Hoppe, Y. K. Mishra, S. Gorb, R. Adelung & M. Baum. Complex Shaped ZnO Nano- and Microstructures based Polymer Composites: Mechanically Stable and Environmentally Friendly Coatings for Potential Antifouling Applications. Phys. Chem. Chem. Phys. 18, 7114–7123 (2016).
Mishra, Y. K. et al. Versatile Fabrication of Complex Shaped Metal Oxide Nano-microstructures and Their Interconnected Networks for Multifunctional Applications. KONA Powder Part. J. 31, 92–110 (2014).
Antoine, T. E. et al. Intravaginal Zinc Oxide Tetrapod Nanoparticles as Novel Immunoprotective Agents against Genital Herpes. J. Immunol. 196, 4566–4575 (2016).
Hölken, I. et al. Sacrificial Template Synthesis and Properties of 3-D Hollow-silicon Nano-and Microstructures. ACS Appl. Mater. Interfaces. 8, 20491–20498 (2016).
Jin, X. et al. A Novel Concept for Self-reporting Materials: Stress Sensitive Photoluminescence in ZnO Tetrapod Filled Elastomers. Adv. Mater. 25, 1342–1347 (2013).
Ozgur, U. et al. A Comprehensive Review of ZnO Materials and Devices. J. Appl. Phys. 98, 041301 (2005).
Tiwari, A. & Snure, M. Synthesis and Characterization of ZnO Nano-plant-like Electrodes. J. Nanosci. Nanotechnol. 8, 3981–3987 (2008).
Zhang, Y., Nayak, T. R., Hong, H. & Cai, W. Biomedical Applications of Zinc Oxide Nanomaterials. Curr. Mol. Med. 13, 1633 (2013).
Chen, Y., Tse, W. H., Chen, L. & Zhang, J. Ag Nanoparticles-decorated ZnO Nanorod Array on a Mechanical Flexible Substrate with Enhanced Optical and Antimicrobial Properties. Nanoscale Res. Lett. 10, 1–8 (2015).
Singh, S., Barick, K. & Bahadur, D. Shape-controlled Hierarchical ZnO Architectures: Photocatalytic and Antibacterial Activities. Cryst Eng Comm 15, 4631–4639 (2013).
Luo, J. et al. Ethanol Sensing Enhancement by Optimizing ZnO Nanostructure: From 1D Nanorods to 3D Nanoflower. Mater. Lett. 137, 17–20 (2014).
Zhang, X., Jiang, J. & Shi, W. Three-dimensional Hierarchical ZnO Nanostructures with Controllable Building Units: Hydrothermal Synthesis, Growth Process and Photocatalytic Activities for Organic Dyes. Micro Nano Lett. 9, 509–513 (2014).
Shi, R., Song, X., Li, J. & Yang, P. Hierarchical ZnO with Twinned Structure: Morphology Evolution, Formation Mechanism and Properties. Mater. Chem. Phys. 156, 61–68 (2015).
Chen, C. et al. Self-assembly Epitaxial Growth of Nanorods on Nanowalls in Hierarchical ZnO Hexagonal Nanocastle. J. Nanopart. Res. 16, 1–9 (2014).
Liu, X. et al. Fabrication and Photoluminescence Properties of Graphite Fiber/ZnO Nanorod Core–Shell Structures. J. Nanosci. Nanotechnol. 11, 6934–6939 (2011).
Liu, X. et al. Visible-light Photoresponse in a Hollow Microtube–nanowire Structure Made of Carbon-doped ZnO. Cryst Eng Comm 14, 2886–2890 (2012).
Mecklenburg, M. et al. Aerographite: Ultra Lightweight, Flexible Nanowall, Carbon Microtube Material with Outstanding Mechanical Performance. Adv. Mater. 24, 3486–3490 (2012).
Schuchardt, A. et al. Three-dimensional Aerographite-GaN Hybrid Networks: Single Step Fabrication of Porous and Mechanically Flexible Materials for Multifunctional Applications. Sci. Rep. 5, 8839 (2015).
Larson, C. et al. Highly Stretchable Electroluminescent Skin for Optical Signaling and Tactile Sensing. Science 351, 1071–1074 (2016).
Wang, F., Ye, Z., Ma, D., Zhu, L. & Zhuge, F. Rapid Synthesis and Photoluminescence of Novel ZnO Nanotetrapods. J. Cryst. Growth 274, 447–452 (2005).
Ronning, C., Shang, N., Gerhards, I., Hofsass, H. & Seibt, M. Nucleation Mechanism of the Seed of Tetrapod ZnO Nanostructures. J. Appl. Phys. 98, 34307–34307 (2005).
Iwanaga, H., Fujii, M. & Takeuchi, S. Growth Model of Tetrapod Zinc Oxide Particles. J. Cryst. Growth 134, 275–280 (1993).
Alim, K. A., Fonoberov, V. A., Shamsa, M. & Balandin, A. A. Micro-Raman Investigation of Optical Phonons in ZnO Nanocrystals. J. Appl. Phys. 97, 124313–124313 (2005).
Rajalakshmi, M., Arora, A. K., Bendre, B. & Mahamuni, S. Optical Phonon Confinement in Zinc Oxide Nanoparticles. J. Appl. Phys. 87, 2445–2448 (2000).
Lupan, O. et al. Synthesis and Characterization of ZnO Nanowires for Nanosensor Applications. Mater. Res. Bull. 45, 1026–1032 (2010).
Zalamai, V. et al. Impact of Size upon Lasing in ZnO Microtetrapods. Appl. Phys. B 99, 215–222 (2010).
Lin, B., Fu, Z. & Jia, Y. Green Luminescent Center in Undoped Zinc Oxide Films Deposited on Silicon Substrates. Appl. Phys. Lett. 79, 943–945 (2001).
Wang, Z., Zu, X., Yang, S. & Wang, L. Blue Luminescence from Carbon Modified ZnO Nanoparticles. J. Mater. Sci. 41, 3729–3733 (2006).
Mendelsberg, R., Kennedy, J., Durbin, S. & Reeves, R. Carbon Enhanced Blue–violet Luminescence in ZnO Films Grown by Pulsed Laser Deposition. Curr. Appl. Phys. 8, 283–286 (2008).
As, D. & Köhler, U. Carbon-an Alternative Acceptor for Cubic GaN. J. Phys.: Condens. Matter 13, 8923 (2001).
Janotti, A. & Van de Walle, C. G. Native Point Defects in ZnO. Phys. Rev. B 76, 165202 (2007).
Erhart, P. & Albe, K. Diffusion of Zinc Vacancies and Interstitials in Zinc Oxide. Appl. Phys. Lett. 88, 201918 (2006).
McCluskey, M. & Jokela, S. Defects in ZnO. J. Appl. Phys. 106, 071101 (2009).
Vlasenko, L. & Watkins, G. Optical Detection of Electron Paramagnetic Resonance for Intrinsic Defects Produced in ZnO by 2.5-MeV Electron Irradiation in-situ at 4.2 K. Phys. Rev. B 72, 035203 (2005).
Heo, Y., Norton, D. & Pearton, S. Origin of Green Luminescence in ZnO Thin Film Grown by Molecular-beam Epitaxy. J. Appl. Phys. 98, 073502 (2005).
Lu, Y., Hong, Z., Feng, Y. & Russo, S. Roles of Carbon in Light Emission of ZnO. Appl. Phys. Lett. 96, 091914 (2010).
Dingle, R. Luminescent Transitions Associated with Divalent Copper Impurities and the Green Emission from Semiconducting Zinc Oxide. Phys. Rev. Lett. 23, 579 (1969).
Garces, N. et al. Role of Copper in the Green Luminescence from ZnO Crystals. Appl. Phys. Lett. 81, 622–624 (2002).
Broser, I., Podlowski, L., Thurian, P., Heitz, R. & Hoffmann, A. Calorimetric Absorption Spectroscopy of Copper Centers in II–VI Semiconductors at mK Temperatures. J. Lumin. 60, 588–591 (1994).
Dahan, P. et al. Properties of the Intermediately bound and Excitons in ZnO: Cu. J. Phys.: Condens. Matter 10, 2007 (1998).
Jeong, S.-H., Kim, B.-S. & Lee, B.-T. Photoluminescence Dependence of ZnO Films Grown on Si (100) by Radio-frequency Magnetron Sputtering on the Growth Ambient. Appl. Phys. Lett. 82, 2625–2627 (2003).
Mo, C., Li, Y., Liu, Y., Zhang, Y. & Zhang, L. Enhancement Effect of Photoluminescence in Assemblies of Nano-ZnO Particles/silica Aerogels. J. Appl. Phys. 83, 4389–4391 (1998).
Wu, X., Siu, G., Fu, C. & Ong, H. Photoluminescence and Cathodoluminescence Studies of Stoichiometric and Oxygen-deficient ZnO Films. Appl. Phys. Lett. 78, 2285–2287 (2001).
Vanheusden, K., Seager, C., Warren, W. t., Tallant, D. & Voigt, J. Correlation Between Photoluminescence and Oxygen Vacancies in ZnO Phosphors. Appl. Phys. Lett. 68, 403–405 (1996).
Xu, H. et al. Photoluminescence of F-passivated ZnO Nanocrystalline Films made from Thermally Oxidized ZnF2 Films. J. Phys.: Condens. Matter 16, 5143 (2004).
Kang, H. S., Kang, J. S., Kim, J. W. & Lee, S. Y. Annealing Effect on the Property of Ultraviolet and Green Emissions of ZnO Thin Films. J. Appl. Phys. 95, 1246–1250 (2004).
Faraji, N. et al. Visible-Light Driven Nanoscale Photoconductivity of Grain Boundaries in Self-Supported ZnO Nano-and Microstructured Platelets. Adv. Electron. Mater 2, 1600138, doi: 10.1002/aelm.201600138 (2016).
Hur, T.-B., Jeen, G. S., Hwang, Y.-H. & Kim, H.-K. Photoluminescence of Polycrystalline ZnO under Different Annealing Conditions. J. Appl. Phys. 94, 5787–5790 (2003).
Chen, H., Hu, L., Fang, X. & Wu, L. General Fabrication of Monolayer SnO2 Nanonets for High-performance Ultraviolet Photodetectors. Adv. Funct. Mater. 22, 1229–1235 (2012).
Rose, A. Concepts in Photoconductivity and Allied Problems. (Interscience publishers, 1963).
Liu, Y. et al. Ultraviolet Detectors based on Epitaxial ZnO Films Grown by MOCVD. J. Electron. Mater. 29, 69–74 (2000).
Kumar, S., Gupta, V. & Sreenivas, K. Synthesis of Photoconducting ZnO Nano-needles using an Unbalanced Magnetron Sputtered ZnO/Zn/ZnO Multilayer Structure. Nanotechnology 16, 1167 (2005).
Soci, C. et al. ZnO Nanowire UV Photodetectors with High Internal Gain. Nano Lett. 7, 1003–1009 (2007).
Soci, C. et al. Nanowire Photodetectors. J. Nanosci. Nanotechnol. 10, 1430–1449 (2010).
Cammi, D. & Ronning, C. Persistent Photoconductivity in ZnO Nanowires in Different Atmospheres. Adv. Condens. Matter Phys. 2014 (2014).
Nobis, T., Kaidashev, E. M., Rahm, A., Lorenz, M. & Grundmann, M. Whispering Gallery Modes in Nanosized Dielectric Resonators with Hexagonal Cross Section. Phys. Rev. Lett. 93, 103903 (2004).
Reimer, T. et al. Single Step Integration of ZnO Nano-and Microneedles in Si Trenches by Novel Flame Transport Approach: Whispering Gallery Modes and Photocatalytic Properties. ACS Appl. Mater. Interfaces 6, 7806−7815 (2014).
Larciprete, M. C. & Centini, M. Second Harmonic Generation from ZnO Films and Nanostructures. Appl. Phys. Rev. 2, 031302 (2015).
Lo, K.-Y. et al. Optical Second Harmonic Generation from the Twin Boundary of ZnO Thin Films Grown on Silicon. Appl. Phys. Lett. 92, 091909 (2008).
Acknowledgements
R.A. would like to thank the financial support from German Research Foundation (DFG) for the financial assistance under scheme AD 183/17-1. M.M. and K.S. also acknowledge the SFB 986 TP B1 project from DFG. This work was also supported by the Supreme Council for Research and Technological Development of the Academy of Sciences of Moldova under the grant no 15.817.02.08A. Authors also thank the EU Graphene Flagship.
Author information
Authors and Affiliations
Contributions
IT, LG, MM, KS, RA, YKM designed the experiment. JG, MM, KS, RA, YKM synthesized the Aerographite templates. LG, VP, IT have grown the hybrid 3D networks. IT, LG, JG, VP, MM, MSAK, VU, NP, RF, YKM, RA characterized and analyzed the data. IT, RA, YKM wrote the paper.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Tiginyanu, I., Ghimpu, L., Gröttrup, J. et al. Strong light scattering and broadband (UV to IR) photoabsorption in stretchable 3D hybrid architectures based on Aerographite decorated by ZnO nanocrystallites. Sci Rep 6, 32913 (2016). https://doi.org/10.1038/srep32913
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep32913
This article is cited by
-
Enhanced room temperature ferromagnetism and green photoluminescence in Cu doped ZnO thin film synthesised by neutral beam sputtering
Scientific Reports (2019)
-
A facile synthesis of Au-nanoparticles decorated PbI2 single crystalline nanosheets for optoelectronic device applications
Scientific Reports (2018)
-
Hierarchical Aerographite 3D flexible networks hybridized by InP micro/nanostructures for strain sensor applications
Scientific Reports (2018)
-
A review on chemiresistive room temperature gas sensors based on metal oxide nanostructures, graphene and 2D transition metal dichalcogenides
Microchimica Acta (2018)
-
Effect of surface carbon contamination on the chemical states of N-doped ZnO thin films
Applied Physics A (2018)