Experimental and theoretical studies on inhibition of mild steel corrosion by some synthesized polyurethane tri-block co-polymers

Polyurethane based tri-block copolymers namely poly(N-vinylpyrrolidone)-b-polyurethane-b-poly(N-vinylpyrrolidone) (PNVP-PU) and poly(dimethylaminoethylmethacrylate)-b-polyurethane-b-poly(dimethylaminoethylmethacrylate) (PDMAEMA-PU) were synthesized through atom transfer radical polymerization (ATRP) mechanism. The synthesized polymers were characterized using nuclear magnetic resonance (NMR) spectroscopy and gel permeation chromatography (GPC) methods. The corrosion inhibition performances of the compounds were investigated on mild steel (MS) in 0.5 M H2SO4 medium using electrochemical measurements, surface analysis, quantum chemical calculations and molecular dynamic simulations (MDS). Potentiodynamic polarization (PDP) measurements revealed that the polymers are mixed-type corrosion inhibitors. Electrochemical impedance spectroscopy (EIS) measurements showed that the polymers inhibit MS corrosion by adsorbing on MS surface to form pseudo-capacitive interface. The inhibitive effects of the polymers increase with increasing concentration and decrease with increasing temperature. The adsorption of both the polymers on MS surface obey the Langmuir adsorption isotherm and involves both physisorption and chemisorption mechanisms. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) analyses showed that the polymers formed protective film on MS surface and shield it from direct acid attack. Quantum chemical calculations and molecular dynamic simulations studies corroborate experimental results.

unhindered exposure to the aggressive/corrosive environment 14 . A number of studies that introduce polymers as good coating materials and corrosion inhibitors have been reported. Srivatsava et al. had reported grafted polyacrylamide derivatives as effective inhibitor of mild steel corrosion in acidic medium 15 . Grafted polymers exhibit significantly improved physical properties such as tensile strength, hardness and thermal stability 16 . Ni et al. had reported the enhanced performance of polyurethane coatings compared to chromated coatings 17 . A copolymer of polyurethane namely, polyurethane-polyoligomeric silsesquioxane has also been documented to show good coating characteristics 18 . Rashvand and Ranjbar had reported the improved corrosion resistance of polyurethane based waterborne coatings 19 . In this regards, polyurethane based polymers and its composite are gaining increased popularity in corrosion inhibition studies in the recent years due to their inherent film forming and corrosion prevention properties 20,21 .
In the present work, two polyurethane based tri-block co-polymers namely, poly(N-vinylpyrolidone)-bpolyurethane-b-poly(N-vinylpyrolidone) (PNVP-PU) and poly(dimethylaminoethyl methacrylate)-bpolyurethane-b-poly(dimethylaminoethylmethacrylate) (PDMAEMA-PU) have been synthesized, characterized and tested for their corrosion inhibition performances on mild steel (MS) in 0.5 M H 2 SO 4 . The corrosion inhibition performances of the synthesized polymers were investigated using electrochemical techniques, scanning electron microscopy (SEM), and atomic force microscopy (AFM) methods. Theoretical quantum chemical calculations and molecular dynamics simulations were also carried out on the studied polymers to corroborate experimental findings.

Experimental Details
Materials. Toluene diisocyanate (TDI; mixture of 80% 2,4 and 20% 2,6 isomers), dibutyltindilaurate, calcium hydride, and α -bromoisobutyryl bromide were used as received from Aldrich, USA. Analytical grade ethylene glycol (from Merck, India) was refluxed with calcium hydride and then vacuum-distilled before use. Analytical grade tri-n-butyl amine (from Spectrochem, India) was used as received. Analytical grade N,N-dimethylacetamide (DMAc) (from CDH, India) was distilled under reduced pressure and the middle portions were used after storing over type 4 Å molecular sieves. N-vinylpyrrolidone (NVP)-99% (from Aldrich, USA) was purified by distillation under reduced pressure to remove any impurities before use. Iron(II) bromide (FeBr 2 )-98% (from Aldrich, USA) was used without any further purification. Poly(tetramethyleneoxide) glycol (PTMG) of molecular weight 1000 (from Aldrich, USA) was purified by heating at 105 °C under vacuum for 3 hr just before use. All other chemicals were of analytical grades and were used as received.
Synthesis of the studied polymers: PNVP-PU and PDMAEMA-PU. The precursors, bromine terminated polyurethane (Br-PU-Br) and the bromine terminated poly(ethyleneoxide) based polyurethane (Br-PEOPU-Br) were synthesized as follows. The dried poly(tetramethyleneglycol) of molecular weight 1000 (20 g, 0.02 mol) (in the case of Br-PU-Br) or the dried poly(ethyleneglycol) of molecular weight 1000 (20 g, 0.02 mol) (in the case of Br-PEOPU-Br) was placed in a 250 ml three-necked round-bottom flask fitted with a mechanical stirrer, nitrogen inlet and a dropping funnel, and was placed in an oil bath and heated until the temperature attains 65 °C. TDI (6.96 g, 0.04 mol) was then added drop by drop whilst stirring. The temperature was then raised to 70 °C, and the reaction was allowed to proceed until the isocyanate content reached half of the initial value (as determined by dibutylamine titration). Then, 2-hydroxyethyl-2′ -methyl-2′ -bromopropionate (HMB) (8.44 g, 0.04 mol) in 15 ml DMF was added, followed by dibutyltindilaurate (2 mol % of NCO, 0.25 g). The reaction was allowed to proceed until the complete disappearance of isocyanate group. The precursors used in the synthesis of PNVP-PU and PDMAEMA-PU and the synthetic routes are given in Fig. 1 3 (0.1353 ml)] of 100:1:2:6 at 80 °C in 10 ml of DMF for 1 h. In each case, the reaction was performed in a 50 ml polymerization tube with a magnetic stirrer, under the typical conditions for ATRP 22,23 . A known quantity of Br-PU-Br or Br-PEOPU-Br as appropriate was dissolved in DMF and a known quantities of N(n-Bu) 3 , FeBr 2 , and NVP or tBA (for PNVP-PU or PDMAEMA-PU as appropriate) were added successively in the polymerization tube. The homogeneous reaction mixture was degassed by three alternate freeze-pump-thaw cycles, sealed under vacuum and placed in a thermo-stated oil bath controlled to ± 0.01 °C for a selected time. At the end of the stipulated period, the reaction mixture was removed from the oil bath and the reaction was quenched by dipping in an ice-salt mixture.
For PNVP-PU, the reaction mixture was diluted with THF and passed through a basic alumina column to remove ATRP catalyst. The resulting solution was then concentrated and the resultant tri-block copolymer (PNVP-PU) was precipitated into excess diethyl ether and dried under vacuum. In the case of PDMAEMA-PU, the coloured polymer was washed from acidified methanol and further passed through neutral aluminium oxide column after which pure white polymer was separated.
Characterization of the synthesized polymers. The 1 H-NMR spectra of the synthesized tri-block co-polymers were recorded on a Bruker DPX-300 NMR instrument using deuterated dimethyl sulfoxide (DMSO-D6) as solvent and tetramethylsilane (TMS) as internal standard. The number average molecular weight (M n ) of the polymers was determined by size exclusion chromatography using WATERS 515 gel permeation chromatography equipped with refractive index detector. THF (Merck, HPLC Grade) was used as the eluent, at a flow rate of 1.0 ml/min and the calibration curve was obtained using polystyrene. Fe (balance). The MS specimen used as the working electrode (WE) for the electrochemical studies was cut from the MS rod and soldered at one end with an insulated copper wire and embedded in chemical epoxy resin (ARALDITE) leaving the exposed surface area of 1 cm 2 . Prior to each electrochemical measurement, the MS specimens were abraded with emery papers of various grade sizes: 100, 150, 320, 400, 600, 1000 and 1500, rinsed with double distilled water, degreased with acetone and dried at room temperature.
The properly ground and polished MS specimens were also used for SEM and AFM studies. The blank acid solution (0.5 M H 2 SO 4 ) was prepared by diluting the analytical grade sulphuric acid with double distilled water. Various concentrations (400-1600 ppm) of the synthesized amphiphilic tri-block copolymers, PNVP-PU and PDMAEMA-PU were also prepared and used as inhibitors for mild steel corrosion in 0.5 M H 2 SO 4 .

Electrochemical measurements.
Electrochemical experiments were carried out using a conventional three-electrode electrochemical cell assembly. Freshly polished MS specimen with an exposed surface area of 1 cm 2 was used as the WE, platinum rod as counter electrode (CE) and saturated calomel electrode (SCE) as reference electrode (RE). The RE was coupled with a luggin capillary to ensure suitable geometry of cell electrodes with minimum potential drop. The WE was immersed in the test solution for 4-5 h to achieve a steady open circuit potential (OCP) before each electrochemical measurement. Potentiodynamic polarization and potentiostatic polarization measurements were performed using electrochemical analyzer CHI 6021B under aerated conditions. Potentiodynamic anodic and cathodic polarization curves were obtained at a scan rate of 0.001 Vs −1 in the potential range from − 1.0 to 0 V relative to the corrosion potential (E corr ) and the measurements were recorded at various temperatures (298-328 K). Potentiostatic polarization curves were obtained at a scan rate of 0.01 Vs −1 in the potential range from the OCP to 2 V. Electrochemical impedance spectroscopy (EIS) studies were performed using electrochemical analyzer CHI760C under aerated conditions at 298 K. Impedance spectra were recorded at E corr in the frequency range 10 kHz to 1 Hz with the ac voltage amplitude of 0.005 V.
Surface Analysis. The surface morphology of MS specimens immersed in 0.5 M H 2 SO 4 without and with 1600 ppm of inhibitors was investigated by using SEM and AFM analyses. SEM measurements were performed using Leo 435 VP in high vacuum mode, equipped with digital imaging and 35 mm photography system. SEM images were obtained by applying operating voltage of 15-30 kV. AFM measurements were performed using VEECO CPII atomic force microscope (MPP-11123) at resonance frequency, f o and spring constants k of 20-80 N/m. The topographic images were obtained with the AFM by applying force in nano-Newton between the sample and Al-coated conductive tip.

Computational Details
Quantum chemical calculations details. Quantum chemical calculations were carried out with the aid of Gaussian 09 software suite 24 . One part of the symmetric monomeric structure of each polymer was used as the representative structure of the corresponding polymer for computational studies. The initial molecular structures and geometries were obtained with the aid of ChemDraw Ultra 12.0 from CambridgeSoft. The initial structures were refined with Hartree-Fock calculations at HF/3-21 level of theory. The optimized structures obtained from the HF/3-21 calculations were later optimized by using the density functional theory approach, which involves the Becke's three-parameter hybrid functional and Lee-Yang-Paar correlation functional (B3LYP) combined with the 6-31 G(d) basis function 25,26 . The optimized structures and electron density graphical isosurfaces were visualized with the aid of GaussView 5.0 software. Quantum chemical parameters such as the energy of the highest occupied molecular orbital (E HOMO ), the energy of the lowest unoccupied molecular orbital (E LUMO ), the energy gap (∆ E = E LUMO − E LUMO ), global hardness (η = ∆ E/2) and dipole moment were recorded.

Molecular dynamic (MD) simulations details.
Quench MD simulations were performed using Forcite module in the Material Studio Software 7.0 from BIOVIA-Accelrys, USA 27,28 . The simulation was carried out on Fe (110) crystal in a 5 Å deep slab using the periodic boundary conditions in order to simulate a representative part of an interface that is devoid of any arbitrary boundary effects. The Fe (110) plane was then enlarged to a 13 × 13 supercell to provide an adequately large surface for the interactions of the studied polymer with the metallic surface. A vacuum slab of 50 Å thickness was later built above the Fe (110) plane and the Fe (110) surface was fixed before the simulations. The entire components of the systems, i.e. Fe (110)+ polymer were optimized using the Condensed-phase Optimized Molecular Potentials for Atomistic Simulation Studies (COMPASS) force field. The MD simulations were performed in NVT canonical ensemble at 298 K, a time step of 1.0 fs, and a total simulation time of 500 ps using Anderson thermostat. Similar procedure has been successfully employed in previous studies [27][28][29][30] .

Results and Discussion
Characterization of the synthesized polymers. The   -N-CH 3 protons of DMAEMA appeared at 2.4 ppm while -CO-O-CH 2 protons resonated at 3.78 ppm merging with the O-CH 2 -CH 2 peak. The 1 HNMR spectra of PNVP-PU and PDMAEMA-PU indicate that no peaks corresponding to C(CH 3 ) 2 and -OCH 2 groups were adjacent to ester group of HMB due to its presence at a lower concentration. It is also an evidence of polymer formation.  This observation suggests that the tested polymers reduce the rate of anodic MS dissolution in the acid as well as the cathodic hydrogen ion reduction. This effect can be attributed to the blockage of active sites on MS surface by the adsorbed film of the molecules of the studied polymers, PNVP-PU and PDMAEMA-PU 31 . The polarization curves in the presence of both PNVP-PU and PDMAEMA-PU show similar cathodic features as the blank, suggesting that the inhibitors do not change the mechanism of the cathodic hydrogen gas evolution associated with the corrosion process. Similar observations were noticed for the anodic arms of the polarization curves. However, the anodic arms of the polarization curves for PNVP-PU exhibit concave-like inflectional features at about − 400 mV, which is more pronounced at higher concentrations (800-1600 ppm) at 298 K, and also noticeable at 1600 ppm at 318 K. Similar features were observed for PDMAEMA-PU also at the concentration range of 800-1600 ppm and within the temperature range of 298-318 K. The appearance such inflectional regions at the anodic arms of the polarization curves in the presence of the inhibitor molecules at some concentrations and temperatures could be as a result of adsorbed inhibitor molecules or intermediate products such as Fe/Inhibitor complexes 32 , which can lead to passivation, as well as possible change in the mechanism of the anodic half-reaction of the active electrochemical corrosion. The relevant electrochemical kinetic parameters such as corrosion potential (E corr ), corrosion current density (I corr ) and Tafel slopes (anodic (b a ) and cathodic (b c )) were determined by extrapolating the Tafel regions of the curves to the E corr and the values are given in Table 1. The corrosion inhibition efficiency (%IE) was calculated using the relation: corr corr corr where I corr and ′ I corr are the corrosion current density values in the absence and presence of inhibitors respectively. Surface coverage (θ = %IE/100) was also calculated at different temperatures and listed in Table 1. The magnitude of the shift in E corr in the presence of the inhibitors compared to the blank is generally less than 85 mV, suggesting that the studied compounds act as mixed-type inhibitors 33,34 . Furthermore, the E corr tends to shift towards more anodic values in the presence of PNVP-PU, which suggests that the (mixed-type) inhibitive effect of this compound is more pronounced on anodic reaction. Similarly, a close observation of the results in Fig. 5 and Table 2 also revealed that PDMAEMA-PU may have greater influence on cathodic reaction. This is because the E corr is more cathodic compared to the blank in most cases within the studied inhibitor concentrations and reaction temperatures. The change in the values of b a and b c with at different concentrations of the inhibitors and different temperatures can be attributed to the occurrence of redox complexation reactions of Fe-inhibitor complexes involving different oxidation states of Fe in the electrochemical systems 35 . The values of I corr decrease with increasing concentrations of both PNVP-PU and PDMAEMA-PU but increase with increasing temperature of the system. The lower values of I corr at higher concentrations of the inhibitors might be due to increased number of inhibitor molecules leading to larger surface coverage of the molecules on MS surface. More so, the higher values of I corr at higher temperatures suggest that the dissociation of the inhibitor molecules adsorbed on metallic surface is favoured by increase in temperature and/or the formation of the activated Fe-inhibitor complex is exothermically controlled. Similarly, IE% values increase with increase in inhibitor concentration and decrease with increase in temperature due to the same reasons attributed to the variation in I corr values. PDMAEMA-PU exhibits a slightly higher corrosion inhibition performance than PNVP-PU, which can be associated to the difference in the atomic constituents, functional groups, number of heteroatoms and structure of the R-groups (vide Fig. 1) present in the two polymers.
Adsorption isotherms and thermodynamic parameters. The most probably mechanism by which organic compounds inhibit metal corrosion is the adsorption organic molecules on the metallic surface.
Adsorption isotherms can provide significant information about the nature of interactions that exist at the metal/ solution interface where both the water and inhibitor molecules are present. In the present study, several adsorption isotherms were tested in an attempt to fit the experimental data but only the Langmuir adsorption isotherm provided acceptable linear fits based on the near unity values of the correlation coefficient (R 2 ) values. The linear form of the Langmuir adsorption isotherm can be expressed as 36 : where C is the concentration of inhibitor, θ is the surface coverage and K ads is equilibrium constant for the adsorption/desorption process. The plots of C/θ against C for the studied polymers at different temperatures are shown in Fig. 6. The values of K ads were obtained at different temperatures from the intercepts of the corresponding isotherms. The values of the Gibb's free energy of adsorption (∆G ads o ) for PNVP-PU and PDMAEMA-PU were determined using the equation:  been widely discussed 35,37 . In the present study, the values of ∆G ads o for PNVP-PU range from − 37.68 to − 42.46, while those of PDMAEMA-PU are between − 40.86 and − 45.12 within the range of temperatures (298-328 K) considered in this study. These values of ∆G ads o suggest complex mode of interactions, which involve both physisorption and chemisorption mechanisms between MS and the studied polymer molecules 35 .
Activation parameters for the adsorption characteristics of the studied polymers on MS in 0.5 M H 2 SO 4 were calculated by assuming a direct relationship between i corr and the rate constant for the corrosion reaction. The values of the activation energy (E a ) were calculated from the plots of log i corr against 1/T (shown in Fig. 7) according to the Arrhenius type equation of the form: where A is the pre-exponential factor, R is gas constant, and T is absolute temperature. The Arrhenius plots for MS in 0.5 M H 2 SO 4 in the presence of various concentrations of PNVP-PU and PDMAEMA-PU are shown in Fig. 7. The enthalpy, ∆ H* and entropy, ∆ S* of activation for the adsorption process were derived from the plots of log i corr /T against 1/T (shown in Fig. 8) based on the transition state equation: where is h Planck's constant, N is Avogadro's number, while R and T retain their previous definitions. The calculated thermodynamic parameters such as E a , ∆ S* and ∆ H* are given in Table 3. The values of E a in the presence of inhibitors are generally greater than that of the acid blank ( Table 3 Table 4. The values of i p and i c in the presence of PNVP-PU and PDMAEMA-PU are generally lower than that of the blank system, suggesting that the inhibitor molecules adsorbed on MS surface and influence the passivating behaviour of MS in 0.5 M H 2 SO 4 . The results in Table 4 also show that the passivating effect of PDMAEMA-PU is only significant at higher concentrations 1200 ppm and 1600 ppm, while PNVP-PU shows passivation characteristics over the entire concentration range.    than the blank system. This observation suggests that the adsorbed film of the inhibitor molecules increases the pseudo-capacitive behaviour of the electrode interface 35,42 . The EIS spectra were fitted into the equivalent circuit shown in Fig. 10c, and the electrochemical parameters obtained from the fitting and simulation analysis are listed in Table 5. The %IE was calculated from the charge transfer resistance values as:

Electrochemical impedance spectroscopy (EIS) measurements.
where R ct and ′ R ct are the charge transfer resistances in the presence and absence of inhibitors respectively. The double layer capacitance, C dl values were calculated according to the equation: ct dl max where f(− ″ Z max ) is the maximum frequency on the imaginary impedance axis, and its values are also listed in Table 5. The R ct value may be interpreted as the resistance of the inhibitor to the charge transfer upon oxidation of the metal. It is apparent from the results in Table 5 that the addition of inhibitors increases the R ct values due to the formation of protective film of inhibitor molecules on the steel surface thereby reducing the transfer rate of charged species across the interface. The C dl values in the presence of the inhibitors are generally lower than that of the blank acid system. This suggests a decrease in local dielectric constant or an increase in the thickness of capacitive layer, which is attributed to the adsorption of inhibitor molecules on the MS surface 43 . The %IE increases with increasing concentration of the inhibitors but the trend of inhibitive performances obtained from the EIS data cannot be generalized.

Solutions
Conc. (ppm) i c (A/cm 2 ) i p (A/cm 2 ) E pp range (V)       Fig. 13. The RMS values that measure relative smoothness/ roughness of the surface are listed in Table 6. The surface of the acid treated MS specimen shows bumpy structure with a large area of rough portions due to unhindered acid attack. However, the MS specimens immersed in the inhibitor-containing solutions showed smoother surfaces and decreased RMS values (Table 6) due to adsorption of inhibitor molecules on metal surface. The RMS values in Table 6 also reveal that the surface roughness decreases with increasing concentration of the inhibitor such that the RMS at 400 ppm is greater than that at 1600 ppm.
Quantum chemical calculations. Gas phase optimized structures as well as HOMO and LUMO electron density isosurfaces of PNVP-PU and PDMAEMA-PU are shown in Fig. 14. The adsorption of inhibitor molecules on metallic surface is driven by donor-acceptor interactions between the organic compound (inhibitor) and the metal. The HOMO electron density distribution provides information about the region of the inhibitor molecule from where electrons can readily be donated to the appropriate vacant orbitals of the metal. The LUMO electron density isosurface reveals the molecular centres that are readily susceptible to electron acceptance from the appropriate occupied orbitals of the metal 44,45 . The HOMO of PNVP-PU is distributed over the entire aromatic ring of the phenyl-diurethane and also on the N and O heteroatoms of the diurethane (dicarmate) group. This suggests that PNVP-PU can interact with metal atom by donating charges from the electron-rich phenyl-diurethane centres to the suitable vacant orbitals of the metal. The LUMO of PNVP-PU is essentially distributed over the pi-electron centres of the pyrrolidinone group and also on the neighbouring Br heteroatom and the adjacent carboxylate group. This implies that PNVP-PU is capable of accepting charges using the electron-deficient centres around the unsaturated pyrrolidinone group and the electronegative Br atom. The HOMO of PDMAEMA-PU on the other hand is localized on the tertiary amine group, suggesting that the electron-donating effect of the methyl groups ensures electron abundance of the -N(CH 3 ) 2 group and the molecule can readily donate electrons to the metal atom via this centre during the donor-acceptor interactions with the metal. The LUMO of PDMAEMA-PU is centred around the region of the molecule that contains the Br atom and extended to the neighbouring O heteroatoms of the acetate group. PDMAEMA-PU is therefore capable of accepting charges from the metal in a retro-donation mechanism by using the electronegative Br atom and the adjoining electron-deficient sites.   Relevant quantum chemical parameters of the studied polymers including the HOMO energy (E HOMO ), the LUMO energy (E LUMO ), the energy gap (∆ E), the global hardness (η ), and dipole moment are listed and the dipole moment in Table 7. A high value of E HOMO , and/or a low value of E LUMO , and/or a small ∆ E, and/or a low value of η support(s) high inhibition performance of a molecule. The results in Table 7 suggest that PDMAEMA-PU, which has higher E HOMO , lower E LUMO , smaller ∆ E, and lower η values has higher tendency of inhibiting metal corrosion than PNVP-PU. This observation is in agreement with the results obtained from the potentiodynamic polarization measurements. The dipole movement is another important quantum chemical parameter for investigating the corrosion inhibition efficiency of organic molecules 46 . It is the measure of the polarity of the bonds in a molecule, which is related to the electron cloud distributed on molecular structure 47 . Though there are dissenting views on the use of dipole moment to explain relative inhibition performances 4,48 , the slightly lower dipole moment of PDMAEMA-PU compared to PNVP-PU probably favours better accumulation of PDMAEMA-PU molecules around the surface layer, and therefore supports its higher protection efficiency 4 .  tendency to inhibit Fe corrosion than PNVP-PU and this observation is in agreement with the trend of %IE obtained from potentiodynamic polarization measurements.

Conclusions
Two polyurethane based tri-block copolymers have been synthesized and characterized using NMR spectroscopy and GPC analysis. The synthesized compounds were tested for their corrosion inhibition performances on mild steel in 0.5 M H 2 SO 4 solution using electrochemical techniques, SEM and AFM analyses. Quantum chemical calculations and molecular dynamic simulations were also carried out on the synthesized polymers to corroborate experimental results. The following conclusions can be drawn from the study.
• Successful synthesis of poly(N-vinylpyrrolidone)-b-polyurethane-b-poly(N-vinylpyrrolidone) (PNVP-PU) and poly(dimethylaminoethylmethacrylate)-b-polyurethane-b-poly(dimethylaminoethylmethacrylate) (PDMAEMA-PU) were achieved through atom transfer radical polymerization (ATRP) mechanism. • PNVP-PU and PDMAEMA-PU showed appreciable corrosion inhibition performances for MS in 0.5 M H 2 SO 4 solution. • Inhibition efficiency of the studied polymers increases with increasing concentration and decreases with increase in temperature. • The adsorption behaviour of PNVP-PU and PDMAEMA-PU on MS in 0.5 M H 2 SO 4 obeys the Langmuir adsorption isotherm and involves both physical and chemical adsorption mechanisms. • SEM and AFM micrographs proved that the MS surface immersed in the aggressive media in the presence of PNVP-PU and PDMAEMA-PU is protected from direct acid attack. • Quantum chemical parameters such as E HOMO , E LUMO , energy gap, global hardness and dipole moment suggest that PDMAEMA-PU has higher corrosion inhibition strength than PNVP-PU and this is in agreement with the results obtained from potentiodynamic polarization study. • The MDS derived interaction energies for the polymer/Fe (110) systems also support the suggestion that PDMAEMA-PU is a better corrosion inhibitor than PNVP-PU.