Abstract
There has been much interest in developing a thin-film solar cell because it is lightweight and flexible. The GaAs thin-film solar cell is a top contender in the thin-film solar cell market in that it has a high power conversion efficiency (PCE) compared to that of other thin-film solar cells. There are two common structures for the GaAs solar cell: n (emitter)-on-p (base) and p-on-n. The former performs better due to its high collection efficiency because the electron diffusion length of the p-type base region is much longer than the hole diffusion length of the n-type base region. However, it has been limited to fabricate highly efficient n-on-p single-junction GaAs thin film solar cell on a flexible substrate due to technical obstacles. We investigated a simple and fast epitaxial lift-off (ELO) method that uses a stress originating from a Cr/Au bilayer on a 125-μm-thick flexible substrate. A metal combination of AuBe/Pt/Au is employed as a new p-type ohmic contact with which an n-on-p single-junction GaAs thin-film solar cell on flexible substrate was successfully fabricated. The PCE of the fabricated single-junction GaAs thin-film solar cells reached 22.08% under air mass 1.5 global illumination.
Similar content being viewed by others
Introduction
In the last few decades, much effort has gone into developing a thin-film solar cell to take advantage of its light weight and flexibility. A variety of light-absorbing materials such as amorphous Si (a-Si), compound semiconductors, and organic materials have been investigated for use in thin-film solar cells. In particular, a GaAs-based thin-film solar cell could be the leader of the future thin-film solar cell market because of its unrivaled high efficiency (28.8%, Alta Devices, Sunnyvale, CA, USA1), long-term stability, and reasonable cost2. Konagai et al.3 developed the Peeled Film Technology (PFT) as the epitaxial lift-off (ELO) method for fabricating GaAs thin-film solar cells firstly. In the ELO method, the thin film is separated from the substrate by selectively etching a sacrificial layer between the active region and the substrate. This allows the transfer of the thin film to a foreign carrier and makes detached bulk substrate reusable. Manufacturing costs are significantly reduced by reusing the GaAs substrate4,5,6. Because of these advantages, the ELO method for fabricating GaAs thin-film solar cells has been widely investigated. Wu et al. fabricated a GaAs thin-film solar cell with an electroplated Cu substrate via a cross-shape-patterned ELO method that included hydrofluoric (HF) acid solutions mixed with hydrophilic solvent7. However, a thin-film solar cell with an electroplated Cu substrate is not very flexible and has a low power-to-weight ratio8 due to its considerable weight, thus diminishing the advantages of the thin-film solar cell. Tatavarti et al. reported on an n-on-p single-junction GaAs thin-film solar cell grown by metal organic chemical vapor deposition (MOCVD)9. The fabricated thin film solar cell with a thick metal handler showed a power conversion efficiency (PCE) of 21.11%, but its weight is relatively heavy. Recently, Lee et al. described an ELO method that utilizes a tensile stress resulting from the deposition of Ir/Au on a 50-μm-thick Kapton sheet, and a cold-welding technique without adhesive10. Because of a lack of an HF-resistant p-contact metal this simple ELO method could be applied only to the p (emitter)-on-n (base) solar cell structure, where the Be-doped p-GaAs layer has to be grown prior to the n-GaAs layer using molecular beam epitaxy (MBE). Hence, a high diffusion of Be from the p-GaAs layer is inevitable while growing the n-GaAs layer at an elevated temperature11,12 and a resultant PCE was relatively low, 18.1%.
In the present paper, we have demonstrated a highly efficient GaAs thin-film solar cell fabricated on a flexible substrate using a simple and fast ELO method that utilizes the stress of a sputtered Cr/Au bilayer. In order to realize the highly efficient and flexible thin film solar cell, an HF-resistant AuBe/Pt/Au metal combination is employed as a new p-type ohmic contact, by which an n (emitter)-on-p (base) single-junction GaAs thin-film solar cell has been successfully fabricated. The inverted structures of GaAs solar cell grown using MOCVD becomes a conventional n-on-p structure after ELO process. The single-junction GaAs thin-film solar cell on a flexible substrate is made using the standard solar cell fabrication process.
Results
Figure 1 shows a cross-sectional scanning electron microscopy (SEM) image, obtained using focused ion beam (FIB) milling, of the fabricated GaAs thin-film solar cell on a flexible substrate. Both n- and p-ohmic metal layers are clearly seen as well as the GaAs active region. Although a few voids are observed at the metal bonding interface, they probably do not contribute to an increase in series resistance because most of the areas are in contact with a highly conducting metal layer.
Figure 2 shows the measured external quantum efficiency (EQE) and reflectance curves of the fabricated GaAs thin-film solar cell. The sudden increase in the spectral response of the EQE around 880 nm corresponds to the band gap energy of GaAs. The high EQE of >80% occurs in the wavelength range of 500–800 nm. The cutoff seen below about 470 nm is generally explained by the inefficient extraction of carriers generated near the window and emitter layers. In addition, the broad reflection peak seen in the figure is also responsible to make the EQE drop more rapidly. The delicate optimization of the antireflection coatings (ARCs) potentially improves the efficiency of the solar cell further.
Figure 3 shows the current density−voltage (J−V) characteristics of a complete single-junction GaAs thin-film solar cell measured at room temperature (25 °C) and AM 1.5 G illumination. The high FF is attributed to a low contact resistivity of p-ohmic contact. The contact resistivity measured by a transmission line model (TLM) method13 is 4 × 10−4 Ω·cm2. It is worth mentioning that the estimated PCE of 22.08% is much higher than that of the p-on-n solar cell fabricated on a flexible substrate10.
Discussion
Table 1 summarizes the characteristics and structures of GaAs thin-film solar cells reported in published studies and this work. In general, a single-junction solar cell consists of a highly doped emitter layer and a lightly doped base layer. Hence, a long minority-carrier diffusion length in the base region is an extremely important factor that determines the collection efficiency of photogenerated carriers. The minority-carrier diffusion length LD depends on the lifetime and mobility of the minority carrier and is expressed by , where μ is the carrier mobility, τ is the minority-carrier lifetime, and VT is the thermal voltage. Therefore, p-GaAs is preferred for the base region because electrons have greater mobility than holes in GaAs. Thus, the n-on-p structure has better collection efficiency in the GaAs p-n junction than the p-on-n structure14,15. Despite the advantages of the n-on-p structure, its implementation on a flexible substrate using the ELO method has been limited because of the absence of an HF-resistant p-ohmic contact with low contact resistance. It is worth noting that the work done by Lee et al.10 showed a relatively low efficiency and a low FF that are not only due to more growth defects in the MBE-grown layer16 but mostly due to an inherent low-collection efficiency in the p-on-n structure. Tatavarti et al. grew an n-on-p structure by MOCVD and then transferred the active layer onto the thick metal handle carrier9. The fabricated cell was relatively heavy and showed a lower PCE of 21.11%. The thin film solar cell fabricated in Alta devices has a high PCE17 and a remarkable Voc of 1.12 V probably due to photon recycling as well as the optimized design18, but its detailed structure has not been reported. In this work, we presented a new combination of AuBe/Pt/Au as the HF-resistant p-ohmic contact, where Pt acts as the barrier to impede Au diffusion during the bonding process19. In result, the thin film solar cell with the n-on-p structure was successfully fabricated on flexible substrate which exhibits a PCE of 22.08%. We have measured all the GaAs cells properly fabricated on 2 inch wafer. The efficiency was slightly varied from cell to cell over the whole wafer but the most of cells exhibit efficiencies of more than 21% and the minimum efficiency was at least 20.84%. Thus, these highly efficient GaAs solar cells are reliably demonstrated.
The heterostructure of the GaAs solar cell shown in Fig. 4 was not fully optimized as a thin-film solar cell to maximize the efficiency. Unlike with a bulk-type solar cell, optimizing photon management can enhance the collection efficiency of a thin-film solar cell20,21. A short base with a highly reflective back contact enables a long-wavelength photon to be absorbed near the p-n junction by reflection at the back contact. As a result, Voc and Jsc improve in accordance with the increase in collection efficiency, thus showing that the fabricated GaAs thin-film solar cell is a high-performance device. The GaAs thin-film solar cell presented here has a relatively thick base compared to that of the other cells, as found in Table 1. The long-wavelength photons might be absorbed further from the depletion region, upon which the collection efficiency exponentially decreases21. Therefore, it could have a higher conversion efficiency by reducing the thickness of the base region and enhancing the reflectivity of the p-ohmic contact.
Conclusions
We have successfully demonstrated the fabrication of a highly efficient n-on-p single-junction GaAs thin-film solar cell on a flexible substrate using the simple ELO method. The n-on-p structure is preferred over the p-on-n structure because of the higher charge collection efficiency of electrons with a long diffusion length in the p-base region. However, the typical p-ohmic contact is vulnerable to the HF-based etchant, which limits the implementation of the n-on-p structure on a flexible substrate. To address this problem, we used the combination of AuBe/Pt/Au as a new p-ohmic metal that can withstand the ELO process and has a contact resistivity as low as 4 × 10−4 Ω·cm2. The characteristics of the fabricated GaAs thin-film solar cell on flexible substrates were investigated by measuring the reflectance, EQE, and photovoltaic J−V curves. Its performance characteristics were, Jsc = 27.06 mA/cm2, Voc = 0.98 V, FF = 83.35%, and PCE = 22.08%. The efficiency can be increased by optimizing the base region and the metal reflector on the backside of the thin film. The optimized, high-efficiency thin-film GaAs solar cells fabricated using this mass-production-friendly technology will enable the widespread use of III-V thin-film solar cells in industrial and commercial applications.
Methods
The structures of the thin-film solar cell are grown via MOCVD on a Zn-doped, p-type GaAs (100) substrate with a misorientation of 2° off toward [111] direction. The heterostructure of the inverted single-junction GaAs solar cell is shown in Fig. 4. The buffer layers are grown on both the top and bottom of the 20-nm-thick AlAs, by doing so, both of the surface of the epilayer and the substrate are protected from byproducts generated after and during the ELO process6,22,23. For the active region, the n-GaAs layer is grown prior to the p-GaAs layer, resulting in an n-on-p structure after the ELO process. Hence, an HF-resistant p-ohmic contact must be deposited on top of the as-grown heterostructure. The p-ohmic contact widely used in GaAs solar cells includes Ti24,25,26,27, which is easily etched in an HF acid. To address the vulnerability of the p-ohmic contact, we use the AuBe/Pt/Au metal combination that remains intact in the HF solution during the ELO. After deposition of a Cr/Au bilayer on the 125-μm-thick flexible substrate, the metal-to-metal bonding is processed by controlling the temperature and pressure. The GaAs solar cell epilayer, bonded onto the flexible substrate, is separated from the substrate by etching an AlAs sacrificial layer in an HF-based etchant, as shown in Fig. 5(a). The Cr/Au bilayer-induced stress makes the transfer of the epilayer to the flexible substrate easier. The HF acid etchant mixed with hydrophilic substance increases the etch rate of the AlAs layer because the chemical reaction generates less residue, which helps the inward diffusion of the etchant7. After the ELO process, the buffer layers which are exposed on both the thin film and the detached substrate are selectively etched by a phosphoric acid, thereby preparing a fresh GaAs surface on which to deposit front n-metal structures and the substrate for reuse. Figure 5(b) shows the thin film transferred onto a flexible substrate and the growth-ready recycled substrate. A grid pattern of n-ohmic contact, consisting of AuGe/Ni/Au, is deposited on the thin film by e-beam evaporation. Then a citric acid is used to selectively remove the n-GaAs layer to expose an InGaP window layer, followed by mesa etching to isolate the cell. Finally, ARCs of MgF2/ZnS are deposited on the InGaP layer28. The fabricated cell size is 0.20 cm2. Figure 6 is a photograph of the fabricated GaAs thin-film solar cell, the performance of which was measured using a class A solar simulator with a xenon lamp under air mass 1.5 global (AM 1.5 G) illumination. The irradiance of the simulator was calibrated using a reference cell to verify the AM 1.5 G illumination before measuring the fabricated solar cell.
Additional Information
How to cite this article: Moon, S. et al. Highly efficient single-junction GaAs thin-film solar cell on flexible substrate. Sci. Rep. 6, 30107; doi: 10.1038/srep30107 (2016).
References
Greenu, M. A., Emery, K., Hishikawa, Y., Warta, W. & Dunlop, E. D. Solar cell efficiency tables (version 46). Prog. Photovoltaic: Res Appl. 23, 805–812 (2015).
Lin, Q. et al. Flexible photovoltaic technologies. J. Mater. Chem. C 2, 1233–1247 (2014).
Konagai, M., Sugimoto, M. & Takahashi, K. High efficiency GaAs thin film solar cells by peeled film technology. J. Crys. Growth 45, 277–280 (1978).
Adams, J. et al. Demonstration of multiple substrate reuses for inverted metamorphic solar cells, Paper presented at 38th IEEE PV Specialists Conf. (PVSC), Austin, Texas. New York, USA:IEEE. (10.1109/PVSC.2012.6656720) (2012, June 3–8).
Bauhuis, G. J. et al. Wafer reuse for repeated growth of III-V solar cells. Prog. Photovolt: Res Appl. 18, 155–159 (2010).
Lee, K., Zimmerman, J. D., Xiao, X., Sun, K. & Forrest, S. R. Reuse of GaAs substrates for epitaxial lift-off by employing protection layers. J. Appl. phys. 111, 033527–0033532 (2012).
Wu, F. L., Ou, S. L., Horng, R. H. & Kao, Y. C. Improvement in separation rate of epitaxial lift-off by hydrophilic solvent for GaAs solar cell applications. Sol. Energ. Mat. Sol. Cells. 112, 233–240 (2014).
Kayes, B. M., Zhang, L., Twist, R., Ding, I. K. & Higashi, G. S. Flexible thin-film tandem solar cells with >30% efficiency. IEEE J. Photovolt. 4, 729–733 (2014).
Tatavarti, R. et al. Lightweight, low cost GaAs solar cells on 4” epitaxial liftoff (ELO) wafers, Paper presented at 33rd IEEE PV Specialists Conf. (PVSC): Devices and Defects, San Diego, California. New York, USA:IEEE. (10.1109/PVSC.2008.4922900) (2008, May 11–16).
Lee, K., Zimmerman, J. D., Hughes, T. W. & Forrest, S. R. Non-destructive wafer recycling for low-cost thin-film flexible optoelectronics. Adv. Funct. Mater. 24, 4284–5291 (2014).
Pao, Y. C. Heterojunction and interface space charge effects on interstitial Be diffusion during molecular beam epitaxy (MBE) growth. J. Cryst. Growth 202, 201–202 (1999).
Ploog, K., Fischer, A. & Kunzel, H. J. The use of Si and Be impurities for novel periodic doping structures in GaAs grown by molecular beam epitaxy. Electrochem. Soc. 128, 400–401 (1981).
Jacobs, B., Kramer, M. C. J. C. M., Geluk, E. J. & Karouta, F. Optimisation of the Ti/Al/Ni/Au ohmic contact on AlGaN/GaN FET structures. J. Cryst. Growth. 241, 15–18 (2002).
Stan, M. A. et al. Design and production of extremely radiation-hard 26% InGaP/GaAs/Ge triple-junction solar cells, Paper presented at 28th IEEE PV Specialists Conf. (PVSC): Devices and Defects, Anchorage, Alask. New York, USA: IEEE. (10.1109/PVSC.2000.916148) (2000, September 15–22).
Parekh, R. H. & BarNett, A. M. Improved performance design of gallium arsenide solar cells for space. IEEE Trans. Electron Dev. 31, 689–695 (1984).
Tobin, S. P. et al. Assessment of MOCVD- and MBE-grown GaAs for high-efficiency solar cell applications. IEEE Trans. Electron Dev. 37, 469–477 (1990).
Green, M. A., Emery, K., Hishikawa, Y., Warta, W. & Dunlop, E. D. Solar cell efficiency tables (version 40). Prog. Photovolts 20, 606–614 (2012).
Steiner, M. A. et al. Optical enhancement of the open-circuit voltage in high quality GaAs solar cells. J. Appl. Phys. 113, 123109-1–11 (2013).
Xu, Q. & Yang, L. W. Influence of a barrier layer on the formation of AuBe ohmic contact with the p-GaAs bases of heterojunction bipolar transistors. IEEE Trans. Electron Dev. 58, 2582–2588 (2011).
Yablonovitch, E., Miller, O. D. & Kurtz, S. R. The opto-electronic physics that broke the efficiency limit in solar cells, Paper presented at 38th IEEE PV Specialists Conf. (PVSC): Devices and Defects, Austin, Texas. New York, USA:IEEE (10.1109/PVSC.2012.631891) (2012, June 3–8).
Bauhuis, G. J., Schermer, J. J., Mulder, P., Voncken, M. M. A. J. & Larsen, P. k. Thin film GaAs solar cells with increased quantum efficiency due to light reflection. Sol. Energ. Mat. Sol. Cells. 83, 81–90 (2004).
Cheng, C. W. et al. Epitaxial lift-off process for gallium arsenide substrate reuse and flexible electronics. Nat. Commun. 4, 1577–1583 (2013).
Smeenk, N. J. et al. Arsenic formation on GaAs during etching in HF solutions: relevance for the epitaxial lift-off process. ECS J. Solid States Sci. Technology 2, 58–65 (2013).
Baca, A. G., Ren, F., Zolper, J. C., Briggs, R. D. & Pearton, S. J. A survey of ohmic contacts to III-V compound semiconductors. Thin Solid Films 308–309, 599–606 (1997).
Stareev, G. Formation of extremely low resistance Ti/Pt/Au ohmic contacts to p-GaAs. Appl. Phys. Lett. 62, 2801 (1993).
Shimawaki, H., Furuhata, N. & Honjo, K. Ohmic contacts to p-GaAs with p+/p regrown structures formed by metalorganic molecular beam epitaxy. J. Appl. phys. 69, 7939 (1991).
Kim, K., Nguyen, H. D., Mho, S. & Lee, J. Enhanced efficiency of GaAs single-junction solar cells with inverted-cone-shaped nanoholes fabricated using anodic aluminum oxide masks. Int. J. Photoenergy 2013, 539765–539770 (2013).
Kim, Y. et al. InGaAsNSb/Ge double-junction solar cells grown by metalorganic chemical vapor deposition. Sol. Energy. 102, 126–130 (2014).
Acknowledgements
This work was supported by the New & Renewable Energy Core Technology Program of the Korea institute of Energy Technology Evaluation and Planning (KETEP) granted financial resource from the Ministry of Trade, Industry & Energy, Republic of Korea (No. 20123010010110). This research was also supported by Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education (NRF-2009-0094046) and the Ministry of Science, ICT and Future Planning (NRF-2013R1A1A1058044).
Author information
Authors and Affiliations
Contributions
S.M. and K.K. performed the device fabrication. Y.K. performed the growth and EQE measurements. S.M. performed the reflectance, efficiency measurement, and SEM characterization. S.M. and J.H. conducted the data analysis. S.M. wrote the manuscript. J.L. and J.H. reviewed the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Moon, S., Kim, K., Kim, Y. et al. Highly efficient single-junction GaAs thin-film solar cell on flexible substrate. Sci Rep 6, 30107 (2016). https://doi.org/10.1038/srep30107
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep30107
This article is cited by
-
Numerical Analysis of InGaN/GaN Intermediate Band Solar Cells Under X-sun Concentration, In-compositions, and Doping: Unlocking the Potential of Concentrated Photovoltaics
Arabian Journal for Science and Engineering (2024)
-
Applications of remote epitaxy and van der Waals epitaxy
Nano Convergence (2023)
-
Holistic yield modeling, top-down loss analysis, and efficiency potential study of thin-film solar modules
Communications Physics (2023)
-
Analytical modelling, simulation and comparative study of multi-junction (GaInP2/InGaAs/Ge) solar cell efficiency
Journal of Computational Electronics (2023)
-
An efficient and stable solar flow battery enabled by a single-junction GaAs photoelectrode
Nature Communications (2021)