Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Modification of Ni-Rich FCG NMC and NCA Cathodes by Atomic Layer Deposition: Preventing Surface Phase Transitions for High-Voltage Lithium-Ion Batteries



The energy density of current lithium-ion batteries (LIBs) based on layered LiMO2 cathodes (M = Ni, Mn, Co: NMC; M = Ni, Co, Al: NCA) needs to be improved significantly in order to compete with internal combustion engines and allow for widespread implementation of electric vehicles (EVs). In this report, we show that atomic layer deposition (ALD) of titania (TiO2) and alumina (Al2O3) on Ni-rich FCG NMC and NCA active material particles could substantially improve LIB performance and allow for increased upper cutoff voltage (UCV) during charging, which delivers significantly increased specific energy utilization. Our results show that Al2O3 coating improved the NMC cycling performance by 40% and the NCA cycling performance by 34% at 1 C/−1 C with respectively 4.35 V and 4.4 V UCV in 2 Ah pouch cells. High resolution TEM/SAED structural characterization revealed that Al2O3 coatings prevented surface-initiated layered-to-spinel phase transitions in coated materials which were prevalent in uncoated materials. EIS confirmed that Al2O3-coated materials had significantly lower increase in the charge transfer component of impedance during cycling. The ability to mitigate degradation mechanisms for Ni-rich NMC and NCA illustrated in this report provides insight into a method to enable the performance of high-voltage LIBs.


The USABC (“USABC Goals for Advanced Batteries for EVs - CY 2020 Commercialization”, USCAR, 2015) and U.S. Department of Energy (“Grid Energy Storage”, U.S. Department of Energy, December 2013) have set aggressive battery performance targets for EVs and grid storage applications, respectively1,2. Such emerging battery applications demand higher voltage and higher energy density than currently commercially available lithium-ion battery (LIB) technologies, with simultaneous improvements to cost, cycle life, and safety3,4. For a practical system to be compelling at least a 67% reduction in cell cost and more than a 150% increase in volumetric energy density compared to current state-of-the-art Ni-Mn-Co or NMC/graphite and Ni-Co-Al or NCA/graphite cells, while retaining at least 80% of initial capacity after 1000 100% Depth of Discharge (DoD) cycles1. As graphite anode materials have a relatively high specific capacity >300 mAh/g and lower cost per unit weight, cathode materials are the limiting component to both energy density and cost per unit energy. Common high-energy commercial layered-structure cathodes like NMC and NCA achieve specific capacities in the range 150–200 mAh/g with moderate charge upper cutoff voltages (UCV) ~4.2 V5,6; however using higher voltages to realize higher utilization of these materials towards their theoretical capacities ~275 mAh/g causes increased rate of capacity fade and resistance growth (i.e., lower cycle life) symptomatic of cathode-based degradation mechanisms including phase transitions7,8,9,10 particle amorphization/pulverization11, transition metal dissolution12, and electrolyte decomposition13.

Electrolyte decomposition at the cathode surface at high voltage, leading to surface passivation and charge transfer impedance growth with negative impact on cycle life, is highly emphasized in the literature; however, the significant contribution of phase transitions to impedance growth has not been as widely recognized, and indeed may be more dominant at higher voltage. Under higher states of delithiation (i.e., high voltage charging), Ni and/or Mn cations are known to migrate to lithium layer tetrahedral and eventually octahedral sites14, forming defect spinel and rock salt structures7,8,15. Also at higher voltages, higher metal redox potentials overlap with oxygen 2p energies leading to oxygen anion oxidation and molecular oxygen release8,16. The resulting oxygen vacancies may also accelerate phase transitions by providing low-energy diffusion pathways for transition metal (TM) migration from TM layer to Li-layer, as is also known for high-voltage lithium-manganese-rich (LMR-NMC) chemistries14,17,18,19,20. Collectively, the phase transitions create grain boundaries and block Li diffusion pathways and intercalation sites, which cause a charge-transfer impedance increase, and capacity fade. In order to achieve reasonable cycle life utilizing the high capacities gained via high voltage, phase instability is a key problem that must be addressed.

Extensive research on layered-structure oxides has revealed that phase transitions initiate at particle surfaces7,20,21,22,23,24,25,26. Surface amorphization, cracking, and pulverization have also been observed to initiate at the surface, and have been directly associated with the above reported phase transitions27. Therefore, the compounded charge transfer impedance increase at particle surfaces limits the utilization of the bulk, and, moreover, over time and/or cycling structural degradation can propagate into the particle bulk. These phenomena suggest that if the particle surface structure and phase can be preserved, the associated capacity fade and resistance growth may be averted.

Several surface modification and coating methods have been reported to stabilize the surface of layered oxides, including a gradient structure22,23,24, doping28, and surface coatings29. Al2O3 surface coatings applied by aqueous, sol-gel, and atomic layer deposition (ALD) have often been reported to mitigate electrolyte decomposition and associated impedance increase29,30,31, and recently researchers have begun to investigate the effects of Al2O3 surface coatings on “NMC111” phase stability. Kim et al. coated the surface of NMC111 particles with Al2O3 via atomic layered deposition (ALD), and found that charge transfer impedance growth and capacity fade were significantly slower in half-cells cycled at 1 C/−1 C in 3.0–4.5 V vs. Li+/Li21. Using selected area electron diffraction (SAED) to characterize the surface structure of a pristine and a surface-coated particle after 100 cycles, they showed that the pristine particle surface became polycrystalline and exhibited spinel cubic rings, whereas the coated particle surface exhibited single-crystal layered structure. Yano et al. modified the surface 2–3 nm of NMC111 with Al via a sol-gel technique, retaining a continuous layered structure with LiAlO232. They found similar results, that charge transfer impedance growth and capacity fade were significantly decreased in half-cells cycled at 1 C/−1 C in 2.5–4.7 V vs. Li+/Li, however no post-cycling structural analysis was shown to confirm structure stability. While these studies have shown initially promising results for the capability of alumina coatings to stabilize the surface structure, the direct observation of coating chemistry, surface/bulk structure stability, and coating stability during cycling has not been shown. Furthermore, most studies have limited their investigation to coin half-cells rather than full cells (i.e., vs. graphite anode) with limited Li and electrolyte supply, making the behavior of bare and surface-modified cathodes difficult to assess for commercial applications. Finally, coating studies on layered oxide materials to date have focused mostly on NMC with equal quantities of Ni and Mn, but the capability of surface coatings to stabilize the structure of higher energy but much less stable Ni-rich NMC and NCA has not been shown.

Here we demonstrate the effects of ALD Al2O3 and TiO2 surface coatings on the structure stability and electrochemical performance of layered Ni-rich NMC81122 (referred to as NMC here onwards) and NCA, in 2 Ah pouch cells. The motivation of this work is to obtain fundamental insights into the relationship between electrochemical performance and structural stability of coated NMC811 and NCA. Al2O3 and TiO2 surface coatings on NMC and NCA both uniformly covered particle surfaces, yet exhibited distinct electrochemical and structural rearrangement phenomena. Our findings were that i) Al2O3 coating enhanced capacity retention of NMC-based cells during low and high rate cycling, whereas TiO2 coating caused accelerated capacity fade of NMC-based cells during high rate cycling; ii) Al2O3 and TiO2 coatings each enhanced the capacity retention of NCA-based cells during high rate cycling; iii) Al2O3 coating remained a distinct phase on NMC and NCA particles after cycling at 4.35 V/4.4 V UCV (for NMC and NCA, respectively), preserving the particle surface from phase transformation, associated with a significantly lower rate of charge transfer impedance growth of both NMC and NCA electrodes during 1 C/−1 C cycling; and iv) changes in thickness and uniformity of TiO2 coatings on NMC and NCA particle surfaces were observed after cycling at 4.35 V/4.4 V UCV, while the thickness and uniformity of Al2O3 coatings remained relatively unchanged under these conditions.

To demonstrate the validity and scalability of this approach for use in the manufacture of commercial lithium-ion cells, 2 Ah pouch cells (95 × 64 mm format) were made with ALD-coated and uncoated NMC and NCA cathode materials and used for electrochemical performance and cycling tests with 4.35 and 4.4 UCV, respectively. XALT Energy33 experience has shown that 95 × 64 mm pouch cell performance projects reliably to larger formats such as 255 × 255 mm. Prototype large format 255 mm × 255 mm cells are currently under construction in XALT’s Midland Battery Park using a scaled up 450 kg lot of Al2O3 ALD-coated NMC811 material produced in PneumatiCoat Technologies’ semi-continuous pilot-scale ALD system, and these cells are projected to have an energy density exceeding 500 Wh/L.



Full concentration gradient (FCG) NMC81122 oxide powder was purchased from Posco®, and NCA powder was purchased from Toda America®. Al2O3 and TiO2 ALD coating on NMC and NCA powders was performed by PneumatiCoat Technologies34. Powders were loaded into a batch fluidized bed reactor, heated and dried under vacuum, then iteratively dosed with i) the trimethylaluminum (for Al2O3) or titanium tetrachloride (for TiO2) precursor, ii) inert N2, iii) water vapor, and iv) inert N2. NMC and NCA uncoated materials are denoted as “NMC-Uncoated” and “NCA-Uncoated”. Al2O3 and TiO2 coated samples are denoted as “X-Y”, where X is NMC or NCA and Y is Al2O3 or TiO2.

Cathode electrodes with ALD-coated and uncoated NMC and NCA were fabricated at XALT Energy’s R&D facility with 15 mg/cm2 loading using NMP-based slurries and 92:4:4 active material:Super P:PVDF formulation. Graphite anode electrodes were fabricated with 11 mg/cm2 loading using NMP-based slurries and 93:7 active material:PVDF formulation.

The composition of NMC and NCA were determined to be LiNi0.77Mn0.11Co0.12O2 and LiNi0.79Co0.16Al0.05O2 by inductive coupled plasma atomic emission spectroscopy (ICP-AES) and particle morphology of oxides were evaluated by scanning electron microscopy and energy dispersive x-ray maps were obtained (see the supplementary information). ICP results also showed that Ti was clearly added by ALD coating to NCA-TiO2 and NMC-TiO2 samples; and Al was clearly added to NMC-Al2O3; Al addition to NCA-Al2O3 could not be confirmed by ICP due to the relatively high Al content in the uncoated material.

Coin cell and 2 Ah pouch cell fabrication

Half coin cells were assembled using a 12 mm diameter disk of NMC and NCA electrodes as the cathode, lithium metal as the anode, a Celgard 2325 separator (19 mm diameter disk), and 1.2 M LiPF6 3:7 EC/DEC as the electrolyte.

2 Ah pouch cells were fabricated by punching 95 × 64 mm electrodes, welding tabs, stacking alternately 9 cathodes and 10 anodes with Z-folded separator, and pouch sealing. The cells were filled with 1.2 M LiPF6 1:9 EC/DEC as the electrolyte before aging and formation.


Rate capability tests from the fresh half coin cells were conducted with different UCV (4.35 V or 4.4 V vs. Li+/Li for NMC and NCA, respectively) and LCV of 3.0 V vs. Li+/Li at discharge current densities of 0.1 C, 0.2 C, 0.5 C, 1 C, 2 C, 5 C, and 0.1 C (where 1 C = 180 mA/h for NMC and 195 mA/h for NCA electrodes). At each discharge rate, 5 charge-discharge cycles were collected, and for statistics 3 coin cells replicates were used for each electrode test. The capacity fade or cycle life (CL) tests were performed in 2 Ah pouch cells at 0.3 C/−0.3 C and 1 C/−1 C cycling rates with voltage windows of 3–4.35 V for NMC and 3–4.4 V for NCA cells. 2 pouch cell replicates were used for each cathode material and at each rate. NMC cells were each cycled to 80% capacity retention at each rate, and NCA cells were each cycled 300 times.

After completion of 1 C/−1 C CL tests, the 2 Ah pouch cells were disassembled in argon filled glove box, cathodes were extracted, washed with ethanol, and stored in an argon atmosphere for electrochemical and structural characterization. Rate capability tests were performed in half coin cells in a voltage window of 3–4.8 V vs. Li+/Li, and discharge current densities of 0.1 C, 0.2 C, 0.5 C, 1 C, 2 C, 5 C, and 0.1 C.

Impedance spectra (400 kHz to 10 mHz, 5 mV perturbation) of each electrode were recorded for fresh and extracted electrodes in half coin cells with a VSP potentiostat (Bio-Logic®), after charging to 4.35 V vs. Li+/Li for NMC and 4.4 V vs. Li+/Li for NCA. Data points at each frequency were averaged by three measurements, and two half coin cell replicates were tested.


A PANalytical X’Pert Pro system with a molybdenum source (λ = 0.76 Å) and automatic divergence and anti-scatter slits operated at 60 kV and 45 mA was used to collect XRD patterns from the pristine and cycled oxide electrodes. A Hitachi HF3300 TEM at 300 kV was used to collect high-resolution TEM images and selected-area electron diffraction (SAED) patterns. TEM specimens of the pristine materials were prepared by dispersing the NMC and NCA powders in ethanol and adding a few drops of the resulting suspension to a holey TEM copper grid. For 1 C/−1 C cycled materials, the powder was scraped from extracted electrodes, ground, dispersed in ethanol, and sonicated for 10–15 minutes. A few drops of the solution were added to the holey Cu grid for TEM observation. Approximately, 15–20 particles were images for each sample to enhance the statistical significance of the observations. SAED were simulated by WebEMAPS (Note: J.M. Zuo and J.C. Mabon, Web-based Electron Microscopy Application Software: Web-EMAPS, Microsc Microanal 10 (Suppl 2), 2004; URL: using the unit cell of LiMO2 structure (M = Ni, Mn, or Co) with space group, and spinel structure with space group as reported elsewhere35. Fast Fourier Transformation (FFT) was collected from the high-resolution TEM images. Scanning electron microscopy (SEM) images and energy dispersive X-ray spectroscopy (EDS) data were obtained by Hitachi S4800 FEG-SEM at 20 kV. DC magnetization was measured as a function of temperature, using a Quantum Design Magnetic Property Measurement System. Each sample was first cooled to 5 K in zero field, then a field of 100 Oe was applied and the data were collected from 5 K to 320 K (zero field cooling mode, represented as ZFC). The sample was also cooled in the applied field from 320 K down to 5 K, while measuring magnetization (field cooling, represented as FC).



Al2O3 coating improved NMC capacity retention during low rate (0.3 C/−0.3 C) and high rate (1 C/−1 C) cycling

Table 1 summarizes the discharge capacities obtained at beginning of life (BOL) from 2 Ah pouch cells. The BOL 2 Ah pouch cell capacities were similar, 2.41 Ah for NMC-Uncoated, 2.42 Ah for NMC-Al2O3, and 2.47 Ah for NMC-TiO2 electrodes at lower discharge rate (0.3 C). The capacity values decreased with higher discharge rate (1 C) as expected. Figure 1 represents the cycle life performance of 2 Ah pouch cells with coated and uncoated NMC cathodes cycled at low rate (0.3 C/−0.3 C, a) and high rate (1 C/−1 C, b) in a 3–4.35 V voltage window. NMC-Al2O3 cells had a much lower rate of capacity fade compared to NMC-Uncoated and NMC-TiO2 cells at both cycling rates. NMC-TiO2 experienced a sudden capacity loss at cycle 425 which terminated the test. At higher rate, the NMC-TiO2 had the fastest capacity degradation as compared to uncoated and Al2O3-coated NMC samples. For all NMC-based cells, coulombic efficiencies were greater than 99.9%, and differences between cells with coated and uncoated cathodes were less than the error limitations of the testing channels used.

Table 1 The beginning of life (BOL) discharge capacity from NMC 2 Ah cells at different C-rates and in different voltage windows.
Figure 1
figure 1

Cycling performance (cycle life) from NMC electrodes in 2 Ah pouch cells at (a) low disharge rate (0.3 C/−0.3 C) and (b) high discharge rate (1 C/−1 C) with voltage window 3.0–4.35 V. Rate capability of NMC half coin cells with 3.0–4.8 V vs. Li+/Li voltage window from (c) fresh electrodes and (d) electrodes extracted from 2 Ah pouch cells after 1 C/−1 C cycling.

Al2O3 and TiO2 coatings improved NCA capacity retention during high rate (1 C/−1 C) cycling

Table 2 shows the BOL capacities from coated and uncoated NCA cathodes tested in 2 Ah pouch cells. Interestingly, both Al2O3 and TiO2 coatings gave a significantly higher 1 C capacity although the 0.3 C capacities were similar. This may be caused by a higher rate capability of Al2O3- and TiO2-coated NCA, or because certain capacity fade mechanisms occurred immediately in NCA-based cells cycled at 1 C/−1 C. Indeed, the observation of improved rate capability of ALD-coated cathode materials compared to uncoated materials after electrochemical cycling is a common result21, and this effect may have been accelerated for NCA. Figure 2 represents the cycle life performance of 2 Ah pouch cells with coated and uncoated NCA cathodes cycled at low rate (0.3 C/−0.3 C, a) and high rate (1 C/−1 C, b) in a 3–4.4 V voltage window. At lower rate, the capacity retention trend was similar up to approximately 70 cycles, with subsequently faster degradation observed for NCA-Al2O3 up to 300 cycles. At higher rate, the better initial capacity retention with Al2O3 and TiO2 coatings led to 34% and 70% longer cycle life, respectively, relative to the initial capacity of uncoated NCA. During the first 100 cycles, NCA-Al2O3 had a faster rate of capacity fade than NCA-TiO2 and NCA-Uncoated. While coulombic efficiencies of NCA-based cells were very high (>99.8%), and coulombic efficiency differences between cells with coated and uncoated cathodes were generally within the error limitations of the testing channels used, the only statistically significant difference observed was a 0.1–0.2% lower coulombic efficiency for NCA-Al2O3 compared to NCA-TiO2 and NCA-Uncoated during the first 100 cycles.

Table 2 The BOL discharge capacities of NCA electrodes at different C-rates and in different voltage windows.
Figure 2
figure 2

Cycling performance (cycle life) from NCA electrodes in 2 Ah pouch cells at (a) low disharge rate (0.3 C/−0.3 C) and (b) high discharge rate (1 C/−1 C) with voltage window 3.0–4.4 V. Rate capability of NCA half coin cells with 3.0–4.8 V vs. Li+/Li voltage window from (c) fresh electrodes and from (d) electrodes extracted from 2 Ah pouch cells after 1 C/−1 C cycling.

Rate capability measurements were performed in half coin cells cycled in the voltage window 3–4.8 V vs. Li+/Li with fresh electrodes and with electrodes extracted from 2 Ah pouch cells after 1 C/−1 C cycling, and the results are shown in Fig. 1(c,d) for NMC and Fig. 2(c,d) for NCA electrodes. At BOL, NMC-Al2O3 had a very similar rate capability profile to NMC-Uncoated samples. However, NMC-TiO2 showed comparatively lower rate capability in all the NMC materials at similar ALD thicknesses to the Al2O3 coatings. More significant differences were observed in fresh NCA electrodes, with NCA-Al2O3 showing worse rate capability than both NCA-TiO2 and NCA-Uncoated materials for the thicknesses studied here.

Examining the relative capacity fades evident from half-cell measurements with fresh electrodes and with electrodes extracted from 2 Ah pouch cells cycled at 1 C/−1 C, NMC-Al2O3 experienced 2.2% 1 C discharge capacity loss in 760 cycles compared to 8.1% in 530 cycles for NMC-Uncoated and 14% in 290 cycles for NMC-TiO2. Both NMC-based full cells were cycled to 20% capacity fade; therefore the cathode had a larger contribution to overall capacity fade in NMC-Uncoated cells compared to the NMC-Al2O3 cells, and cathode-based degradation rates were 5-fold slower with the Al2O3 ALD coating. Other capacity loss mechanisms should be considered as well, including electrolyte decomposition at the cathode surface, which can result in Li loss and impedance increase; solid-electrolyte interphase (SEI) growth on the anode surface, possibly affected by electrolyte decomposition and transition metal dissolution at the cathode, causing further Li loss and impedance increase. ALD coating on the cathode has been shown to affect both electrolyte decomposition on the cathode and SEI growth on the anode in full cells31. However, the rate of non-cathode-based capacity fade with NMC-Uncoated cells (0.022%/cycle) is consistent with NMC-Al2O3 cells (0.023%/cycle) and NMC-TiO2 cells (0.021%/cycle), indicating that these other degradation mechanisms were not significantly affected by the Al2O3 and TiO2 coating thicknesses used in this study.

NCA cathodes were surprisingly seen to experience higher capacity fade than the cells from which they were extracted; NCA-Al2O3 cathodes experienced 52% 1 C capacity fade in 300 cycles compared to 58% in 300 cycles for NCA-Uncoated, whereas NCA-Al2O3 cells experienced 40% capacity fade compared to 34% for NCA-Uncoated cells. This may be due to greater instability of the NCA electrodes during the 3–4.8 V vs. Li+/Li rate capability cycles prior to the 1 C discharge capacity measurements compared to NMC electrodes. However, NCA-Al2O3 and NCA-TiO2 electrodes both had lower capacity fade than NCA-Uncoated, and similar to the conclusion for NMC, cathode degradation mechanisms likely had a relatively larger contribution to overall capacity fade in NCA-Uncoated cells compared to the NCA-Al2O3 and NCA-TiO2 cells.

Al2O3 coating on NMC and NCA showed lower impedance growth during 1 C/−1 C cycling

Figures 3 and 4 represent the EIS results from fresh NMC and NCA electrodes and from electrodes extracted from 2 Ah pouch cells after 1 C/−1 C cycling, charged in half-cells to 4.35 V and 4.4 V vs. Li+/Li, respectively. The EIS data exhibited four resistance components: (1) a time-independent IR resistance, (2) a high-frequency interfacial resistance (Rint) from the surface passivation layer, (3) an intermediate-frequency charge transfer resistance (Rct), and (4) a low-frequency mass transfer resistance (W) in the electrode. Rct is highly dependent on surface structure, and Rct growth at high voltages (>4.3 vs. Li+/Li) has been associated with structural instability7. These resistance components were calculated using the circuit model shown in Fig. 3. The results revealed that coated cathodes have similar Rint and Rct at BOL. All NMC and NCA electrodes experienced an increase in Rct at 4.35 V and 4.4 V vs. Li+/Li, respectively, after 1 C/−1 C cycling in 2 Ah pouch cells; however, the Al2O3 ALD-coated NMC and NCA had much lower growth of Rct. Al2O3 coating gave the slowest rate of Rct increase per cycle, for NCA and particularly for NMC, consistent with the conclusions from half-cell rate capability measurements showing that degradation of NMC and NCA cathodes was slower with the presence of an Al2O3 ALD coating. These data suggest the principle cathode-based degradation mechanism is surface structure instability causing growth of Rct.

Figure 3
figure 3

(a,b) Representative Nyquist plots and (c,d) impedance components fitted with (e) a circuit model for coated and uncoated NMC half-cells after charging to 4.35 V vs. Li+/Li for (a,c) fresh electrodes and (b,d) electrodes extracted from 2 Ah pouch cells after 1 C/−1 C cycling.

Figure 4
figure 4

(a,b) Representative Nyquist plots and (c,d) impedance components fitted with the circuit model in Fig. 3(e) for coated and uncoated NCA half-cells after charging to 4.4 V vs. Li+/Li for (a,c) fresh electrodes and (b,d) electrodes extracted from 2 Ah pouch cells after 1 C/−1 C cycling.

The EIS data for NMC-TiO2 suggests further complexity. Although NCA-TiO2 electrodes extracted from cycled 2 Ah cells had intermediate Rct as well as intermediate 1 C discharge capacities in half-cells compared to NCA-Al2O3 and NCA-Uncoated, NMC-TiO2 had intermediate Rct while also having the fastest rate of capacity loss per cycle compared to NMC-Al2O3 and NMC-Uncoated. The unique behavior of TiO2 ALD coating may be related to the evident modification in its chemistry as shown by TEM analysis presented in a later section, and there may be an additional cathode degradation mechanism with NMC-TiO2 that causes Li site loss but relatively less Rct growth. As noted above, the superior capacity retention of NCA-TiO2 compared to NCA-Al2O3 despite the latter’s lowest Rct growth may be related to the lower coulombic efficiency observed with NCA-Al2O3 cells during the first 100 cycles.

In summary, (i) Al2O3 ALD coating on NMC particles mitigated the capacity fade during 0.3 C/−0.3 C and 1 C/−1 C cycling; (ii) TiO2 ALD coatings on NMC particles accelerated capacity fade, especially during 1 C/−1 C cycling; (iii) Al2O3 and TiO2 ALD coatings on NCA particles increased cell capacities at higher cycling rate (1 C/−1 C); (iv) Al2O3 and TiO2 ALD coatings decreased the rate of Rct growth at 4.35 V and 4.4 V vs. Li+/Li for NMC and NCA cathode electrodes, respectively, compared to the uncoated material, with Al2O3 ALD giving the best performance for the thicknesses selected in this study, and (v) the most important mechanism of cathode capacity loss appeared to be surface structure instability causing charge transfer impedance growth, which was mitigated most by Al2O3 ALD coating.

Structural rearrangements

The above electrochemical results provide evidence of the effects of Al2O3 and TiO2 ALD coatings on the electrochemical performance of NMC and NCA cathodes. The cycle life results from 2 Ah pouch cells revealed that the extent of capacity fade at high discharge rates for NMC and NCA-based cells were both improved when cathode particles were coated with Al2O3 ALD layers. The results for TiO2 ALD coatings were different for NMC and NCA, which suggests this coating material can actively interact with these Ni-rich substrates, with NMC experiencing faster capacity fade during high rate cycling with TiO2 coating but NCA experiencing significantly slower rate of capacity fade during high rate cycling with TiO2 coating. Comparison of cathode rate capabilities and EIS behavior between fresh electrodes and electrodes extracted from 2 Ah pouch cells after 1 C/−1 C cycling strongly suggests that Al2O3 ALD coating greatly improves the surface structure stability of both NMC and NCA. This section presents a detailed structural investigation to understand this mechanism. Before discussing the structural changes in the cycled cathodes, structure characterization via magnetic susceptibility of fresh, uncoated NMC and NCA powders is shown.

NMC and NCA exhibited layered structure, and magnetic ordering observed in pristine NMC suggested unique surface structure

The temperature dependent magnetic susceptibility at field cooling (FC) and zero field cooling (ZFC), from NMC and NCA samples (at 100 Oe) along with the XRD patterns are shown in Fig. 5(a,b). All the peaks in the XRD patterns (insets in Fig. a,b) for both NMC and NCA could be assigned to rhombohedral or trigonal ( space group, represented as O3 phase). No “cationic ordering” peaks were observed in the XRD patterns of NMC or NCA, as expected. The SAED patterns from the uncoated NMC and NCA materials are shown in the Fig. 5(c,d). The SAED patterns consisted of only fundamental O3-type reflections along the [0001], zone axes confirming the O3-type layered structures. At higher temperature (>80 K), magnetic susceptibility from NMC and NCA materials showed the paramagnetic behavior where the magnetic moments of metal ions are randomly oriented again conforming the layered O3-type structure.

Figure 5
figure 5

Temperature-dependent magnetic moment at zero filled (filled grey spheres) and field cooling method (filled black spheres) from (a) uncoated pristine NMC and (b) uncoated pristine NCA at 100 Oe; and SAED from uncoated (c) NMC and (d) uncoated NCA. The insets in (a,b) show the corresponding XRD patterns.

At lower temperature (<40 K), in the case of NCA, the FC and ZFC followed the same path down to T = 5 K, however in NMC, the FC and ZFC showed a bifurcation at T ≈ 50 K. The observation from NCA is very similar to the reported data for layered stoichiometric LiMO2 type structure. The bifurcation of FC and ZFC in NMC observed in this study was different than previously reported data and indicate a “magnetic ordering” in the structure. Typically this type of bifurcation is observed in Mn-rich NMC phases such as LiMnO2 where onset of “spin-canting”36 or lithium-manganese rich NMC materials, where a second Li2MnO3 phase is present (including a layered LiMO2 (O3) phase) and an anti-ferromagnetic interaction between Mn4+-O2−-Mn4+ in Li2MnO3 phase generates antiferromagnetic ordering37,38. An antiferromagnetic ordering is not observed if the magnetic moments of M atoms are randomly oriented (in case of O3-type layered structure). The bifurcation in FC and ZFC in NMC in the present study suggests that the atomic arrangements in the layered NMC concentration gradient structure is different than “NMC” with no concentration gradient (see section C for detailed explanation).

Al2O3 ALD coating preserved the particle morphology by protecting the surface during the lithium intercalation/de-intercalation process

Figure 6 shows representative bright field (BF) TEM images of pristine NMC (a–c) and NCA (g–i) particles. The NMC-Uncoated and NCA-Uncoated particles showed smooth particle surfaces. Coated NMC and NCA particles showed a distinct, smooth, homogeneous phase on particle surfaces with no interfacial contact gaps, confirming that uniform ALD coatings of Al2O3 and TiO2 were effectively applied on NMC and NCA particles. The thickest applied Al2O3 and TiO2 coating layer thicknesses appeared to be on the order of 10 nm. Figure 6 also shows representative images of coated and uncoated NMC (d–f) and NCA (j–l) particles extracted from cycled 2 Ah pouch cells after 1 C/−1 C cycling. NMC-Uncoated and NCA-Uncoated particles showed corroded surfaces, and cracks had developed in most of the examined particles. In the case of NMC-Al2O3 and NCA-Al2O3 particles, the particle surface was preserved in most of the particles, and no cracking and/or particle disintegration was observed. Interestingly, in NMC-TiO2 samples, a distinct uniform TiO2 coating layer did not remain in many areas. Furthermore, in the NCA-TiO2 samples, cracks had developed at some particle surfaces where the remaining presence of a TiO2 layer was not apparent. The results showed that the Al2O3 ALD coating stabilized the particle surface from pulverization and cracking, while TiO2 coatings did not form an inert, robust layer phase on these NMC and NCA particles. In order to confirm this hypothesis, full coin cells from NCA-Uncoated, NCA-Al2O3, and NCA-TiO2 were cycled at 1 C/−1 C for 100 cycles at higher voltage (3–4.8 V vs. Li+/Li). The representative TEM images from these particles are presented in Fig. 6(m–o). The results revealed that the NCA-Uncoated particle experienced cracking during 1 C cycling (Fig. 6(m)), however the Al2O3 coating arrests the propagation of cracking (Fig. 6(n)). TiO2 coating was observed to have a similar effect where it remained intact (Fig. 6(o)).

Figure 6
figure 6

BFTEM images of NMC-Uncoated, NMC-Al2O3, and NMC-TiO2 particles in ((ac) respectively) fresh powders and ((df) respectively) extracted from 2 Ah pouch cells after 530, 760, and 290 1 C/−1 C cycles, respectively. BFTEM images of NCA-Uncoated, NCA-Al2O3, and NCA-TiO2 in ((gi) respectively) fresh powders and ((jl) respectively) extracted from 2 Ah pouch cells after 300 1 C/−1 C cycles. BFTEM images of (m) NCA-Uncoated, (n) NCA-Al2O3, and (o) NCA-TiO2 extracted from full coin cells after 100 1 C/−1 C cycles in a 3–4.8 V vs. Li+/Li voltage window.

Al2O3 ALD coating prevents structural rearrangements at NMC and NCA particle surfaces during cycling, but TiO2 ALD coating does not

Figure 7 shows representative high-resolution (HR) TEM images from coated and uncoated NMC samples extracted from 2 Ah pouch cells after cycling at 1 C/−1 C in a 3–4.35 V voltage window. Figure 7(a–c) shows HRTEM images collected for NMC-Uncoated sample. NMC-Uncoated particles exhibited two different phases in single particles marked as Region #1 (towards bulk) and Region #2 (towards surface). As seen in Fig. 7(a), Region #1 was a typical O3-type lattice confirming the layered phase (LiMO2-type). However, Region #2 was a spinel-type lattice (AB2O4-type). The high-magnification view from Region #2 (see Fig. 7(b)) clearly shows the typical spinel-type lattice fringes (indicated by arrows). The spinel-type lattice was observed in several particles, and a second example is shown in Fig. 7(c), where the presence of transition metal atoms in Li-layers was clearly observed. An SAED pattern collected from an NMC-Uncoated particle is shown in Fig. 7(d). The diffraction pattern showed two sets of reflections: bright fundamental O3-type spots correspond to layered trigonal LiMO2 phase (indicated by green dotted circles), and faint reflections correspond to a spinel-type phase (indicated by red dotted circles).

Figure 7
figure 7

High-resolution TEM images of (ac) NMC-Uncoated, (e,f) NMC-Al2O3, and (h) NMC-TiO2 particles extracted from 2 Ah pouch cells after 530, 760, and 290 1 C/−1 C cycles, respectively; and SAED patterns from (d) NMC-Uncoated, (g) NMC-Al2O3, and (i) NMC-TiO2 particles. Scale bar in (b) 2 nm.

HRTEM images of NMC-Al2O3 particles are shown in Fig. 7(e,f), and the SAED pattern from a representative NMC-Al2O3 particle is shown in Fig. 7(g). The HR-TEM shows that both the Al2O3 coating layer and the layered structure of NMC was preserved. The SAED pattern from the [0001] zone axis showed the fundamental O3 reflections from the layered trigonal LiMO2 phase (indicated by green dotted circle) and superlattice reflections, often called “forbidden reflections”, that appeared in the middle of the triangle containing O3 spots (indicated by yellow dotted circle). The presence of “forbidden reflections” indicates the presence of Ni in the Li-Layer as reported elsewhere35,39.

Figure 7(h,i) shows a representative HRTEM image of an NMC-TiO2 particle and a representative SAED pattern. The HRTEM image showed the loss of a distinct TiO2 coating phase from the particle surface; the FFT processed from the corresponding HRTEM image showed the fundamental reflections (indicated by green arrow), and the spinel reflections (indicated by red arrow). The SAED pattern was in agreement with these results, where fundamental layered O3 spots from the trigonal phase (indicated by green dotted circles) and faint spinel spots (indicated by red dotted circles) were observed. Spinel-type reflections were observed in most of the examined NMC-TiO2 particles.

Figure 8(a,b) shows a representative HRTEM image and SAED pattern for NCA-Uncoated particles extracted from 2 Ah pouch cells after 300 1 C/−1 C cycles. Lattice fringes from an O3 layered phase (Region #1) and spinel phase (Region #2) were separated by a distinct boundary. FFT from a magnified view from Region #1 (Fig. 8(c)) confirmed the O3 lattice (hexagonal pattern), whereas FFT from a magnified view from Region #2 (Fig. 8(d)) clearly showed the spinel lattice. The SAED pattern for this region (Fig. 8(c)) showed fundamental O3 reflections from the layered LiMO2 phase (indicated by green dotted circles), spinel-type reflections (indicated by red dotted circle), and “forbidden reflections” (indicated by yellow dotted circle).

Figure 8
figure 8

Representative HRTEM images of (a,b,d) NCA-Uncoated, (e) NCA-Al2O3, and (g,h) NCA-TiO2 particles extracted from 2 Ah cells after 300 1 C/−1 C cycles; and SAED patterns from representative (c) NMC-Uncoated, (f) NMC-Al2O3, and (i) NMC-TiO2 particles.

Figure 8(e) shows a representative HRTEM image of a NCA-Al2O3 particle extracted from a cycled 2 Ah pouch cell. Similar to NMC-Al2O3, NCA-Al2O3 sample does not show any phase transition, and the layered lattice was observed in most of the analyzed particles. The Al2O3 coating layer was preserved, however in these images, the thickness of the Al2O3 coating appeared to have decreased during cycling as compared to the cycled NMC-Al2O3 particles. This observation merits a further ALD film thickness dependence study, which is currently underway. A representative SAED pattern for an NCA-Al2O3 particle (Fig. 8(f)) showed the fundamental O3 spots from the layered LiMO2 phase (indicated by green dotted circles) and “forbidden reflections” (indicated by yellow dotted circle).

In contrast, NCA-TiO2 showed very different behavior compared to NCA-Al2O3 and NCA-Uncoated. In some of the NCA-TiO2 particles, the coating remained intact over the entire particle surface, however in other particles the coating had disappeared. On particles where the coating had disappeared, lattice fringes with different orientations were observed near the surface as compared to the bulk (indicated by green dotted circles in Fig. 8(g)). A second representative HRTEM image of a NCA-TiO2 particle showed the absence of a distinct TiO2 coating layer, and a spinel-type phase on the surface (Fig. 8(h)). A representative SAED pattern (Fig. 8(i)) from NCA-TiO2 showed fundamental O3 spots from the layered trigonal LiMO2 phase (indicated by dotted green circles) and spinel spots (indicated by dotted red circle).


The results above show that ALD surface coating, particularly Al2O3 coating, stabilized the NMC and NCA phase structures at particle surfaces, causing slower charge transfer impedance growth in cathode electrodes and higher capacity retention of cells with both NMC and NCA cathodes during high rate cycling. The fresh NMC and NCA cathode materials have a layered structure in which lithium atoms occupy octahedral sites (LiOct) in lithium layers and TM atoms (Co, Mn, Ni, Al) occupy octahedral sites (TMOct) in transition metal layers in a hexagonal structure (O3-type) with trigonal symmetry ( space group). The structure of NMC is slightly different than NCA due to the concentration gradient distribution of Mn and Ni between surface towards the bulk in NMC. Specifically, the observation of magnetic ordering (antiferromagnetic behavior) in the magnetic susceptibility data indicates the presence of Mn-rich clusters (amorphous/crystalline) of Li2MnO3 or LiMnO2 likely in surface regimes where Mn concentration was higher. There was no sign of “cationic ordering” peaks or “C2/m” reflections in XRD and SAED patterns, respectively. Therefore the observation of antiferromagnetic behavior in the magnetization data suggests that the clusters were amorphous, and therefore were not able to be detected in XRD and SAED. However, detailed investigation is needed to confirm this hypothesis. The Mn-rich phase likely concentrated at FCG NMC particle surfaces in this study is very little, so that phase restructuring only contributes towards the impedance rise, and may not cause cell-voltage fade as it occurs in Li-Mn-rich oxides (LMR oxides).

During charging and discharging, LiOct cations are de-intercalated from and intercalated into, respectively, the host NCM/NCA structure. Charging to higher UCV (≥4.3 V in full cells) may induce oxygen loss selectively from the surface that decreases the bonding interaction among the metal atoms and subsequently causes metal cations to migrate from the metal layer to the lithium layer, rearranging the host oxide structure and triggering structural transformation. The results discussed above show the degradation phenomena in particle morphology and phase transformations that occur in NMC/NCA-Uncoated samples. This result is surprising for NMC-Uncoated given that FCG NMC materials used in this work have been engineered to provide a more stable surface structure than conventional NMC materials with a homogeneous metal distribution, based on the relative stability of Mn4+ compared to Ni4+ and Co4+ to oxygen release, electrolyte oxidation, and phase transformations22,24. But Figs 6(d) and 7(a–d) clearly show that surface degradation occurred in full 2 Ah pouch cells during 1 C/−1 C cycling in the 3–4.35 V voltage window, including layered-to-spinel phase transitions. Sun et al. reported that no cubic phase could be detected via SAED in concentration gradient NMC (with similar Ni content to the NMC in this study) after 50 0.2 C/−0.2 C cycles with 4.3 V vs. Li+/Li UCV in half cells (equivalent to approximately 4.2 V in a full cell with graphite anode) at 55 °C, while conventional distribution NMC had a prevalent cubic phase at the particle surface after cycling. However, the conditions used in that study24 were much less severe than the 4.35 V UCV, 1 C/−1 C rate, and 530 cycles used in the current study for NMC-Uncoated in 2 Ah pouch cells. Moreover, in the previous studies22,23,24, the capacity fade rate of gradient NMC increased with UCV in the range 4.3–4.5 V vs. Li+/Li in half cells at similar C-rates and temperatures, although 4.3 V vs. Li+/Li was the only UCV for which structure analysis was performed after cycling.

ALD surface coatings on NMC and NCA particles may restrict oxygen release at high voltages, thereby stabilizing their surface structure. However, different coatings must be expected to have unique interactions with different cathode chemistries, and coatings may or may not suppress phase transformations. Structural rearrangement and transformation occurred in the cases of NCA-Uncoated, NMC-Uncoated, NCA-TiO2, and NMC-TiO2 samples, whereas the structures of NCA-Al2O3 and NMC-Al2O3 remained mostly layered and had the lowest growth of charge transfer impedance. The unique stabilizing effect of Al2O3 coating compared to TiO2, which are each amorphous in the as-deposited state, is likely associated with its capability to maintain intimate bonding with the oxide surface while remaining a distinct phase over hundreds of cycles, excluding transition metal cations from the surface. It should be noted that the TiO2 ALD coating did indeed stabilize the surface structure locally where it remained a distinct phase, particularly for NCA, corresponding to intermediate charge transfer impedance growth, further suggesting that the key difference between Al2O3 and TiO2 coatings is the sustained robustness of a distinct coating phase. A unique interaction between NMC and TiO2 was suggested by the result that NMC-TiO2 electrodes extracted from 2 Ah pouch cells cycled at 1 C/−1 C had relatively low charge transfer impedance but also relatively low capacity, suggesting a Li site loss mechanism in addition to the surface structural degradation mechanisms that explain other results. It can be hypothesized that a distinct TiO2 coating phase may be lost due to a complex process of local lithiation of the coating phase as has been shown for Al2O340, Ti cation migration into the substrate structure, and/or the formation of new phases that may occur in the TiO2 ALD coating itself. Carefully designed in-situ electrochemical experiments and high resolution ex-situ atomic mapping and diffraction are required to characterize the evolved surface chemistry. The value of understanding any underlying phenomena would be to aid in the design and optimization of more complex or multifunctional ALD coatings that are tailored to achieve the performance metrics of high energy cathode materials across a spectrum of end-use applications.

Cathode structural instability and associated impedance growth is accelerated by higher cycling rates due to the relatively greater state of surface delithiation at particle surfaces at end of charge12, as well as the higher mechanical stresses11,27. Therefore at higher cycling rates, similar to the effect of higher voltages, cathode degradation mechanisms will constitute a larger component of total cell capacity loss. This is consistent with the results for coated NMC cathodes, where Al2O3 ALD coatings increased cycle life by 25% and 40% during lower rate and higher rate cycling, respectively; and also coated NCA cathodes, where both Al2O3 and TiO2 coating increased cycle life during higher rate cycling but had little or negative effect on cycle life during lower rate cycling. The result that TiO2 coating on NCA had a positive effect only for high rate cycling while TiO2 coating on NMC had a negative effect even at higher rate suggests that surface phase transitions and particle cracking of NCA was prevented during initial high rate cycles while the TiO2 coating phase was more intact, whereas these cathode degradation processes occurred more slowly for NMC. Moreover, TEM analysis showed that the TiO2 coating phase was more stable on NCA particles than on NMC particles, and as noted above, a unique interaction between TiO2 and NMC may have caused an additional Li site loss degradation mechanism not observed with Al2O3-coated and uncoated NMC. Finally, particle cracking was clearly more severe for NCA particles than NMC particles, as seen in TEM images of samples extracted from NMC-Uncoated electrodes after 530 cycles (Fig. 6(d)) and NCA-Uncoated electrodes after 300 cycles (Fig. 6(j)), and the capability of TiO2 coating to mitigate crack propagation during initial cycles for NCA may be more important than mitigating surface phase transitions.

Overall, the structural and phase stability of Al2O3 ALD-coated NMC and NCA was evident in the low rate of charge transfer impedance growth during cycling, consistent with the preservation of a single phase and lack of grain and/or phase boundaries at particle surfaces. Interestingly, the fact that Al2O3 coating stabilized the surface structure of gradient NMC at high UCV (approximately 4.45 V vs. Li+/Li) and high rate (1 C/−1 C) for 760 cycles shows that a simple Al2O3 ALD coating has a much more significant impact on structure stability than the gradient metal distribution within the highly-engineered substrate cathode particles. Capacity measurements for NMC-Uncoated and NMC-Al2O3 electrodes extracted from 2 Ah pouch cells cycled at 1 C/−1 C (530 and 760 cycles, respectively) indicated that 8.1% of total capacity fade over 530 cycles in NMC-Uncoated cells was due to the cathode, compared to only 2.2% of total capacity fade over 760 cycles in NMC-Al2O3 cells, a 5-fold improvement.


Surface structure degradation mechanisms including surface-initiated phase transitions and crack propagation cause charge transfer impedance growth during electrochemical cycling, particularly for Ni-rich NMC and NCA at high C-rate and high UCV, and ultimately capacity fade. This work demonstrates the capability of Al2O3 surface coatings applied by ALD on Ni-rich NMC and NCA particles to significantly slow or prevent these mechanisms. Although NMC811 with a concentration gradient experienced layered-to-spinel phase transitions at particle surfaces when cycled in 2 Ah pouch cells with 4.35 V UCV at 1 C/−1 C, Al2O3-coated NMC particles exhibited only layered structure even after 40% more cycles to the same capacity loss. Likewise, Al2O3-coated NCA particles exhibited only the layered phase after 300 1 C/−1 C cycles and gave 34% longer cycle life than uncoated NCA with 4.4 V UCV in 2 Ah pouch cells, whereas uncoated NCA particles experienced extensive layered-to-spinel phase transitions and particle cracking during the same number of cycles. Based on the promising results of this study for NMC-Al2O3, 450 kg of NMC-Al2O3 powder was manufactured in PneumatiCoat Technologies’ high-throughput semi-continuous ALD system (Fig. 9(b)), which is currently being scaled to achieve a 1,000+ metric ton per year capacity in a single system. The powder will be used to produce XALT large format 255 mm × 255 mm pouch cells. The representative TEM images of the scaled up ALD-coated material shown in Fig. 9(a) showed the same high quality coating as for the smaller NMC-Al2O3 batches used to produce 2 Ah pouch cells.

Figure 9
figure 9

(a) Representative BFTEM image of Al2O3-coated NMC811 particles in a powder specimen from a 450 kg lot produced in (b) PneumatiCoat Technologies’ 20 ft high-throughput semi-continuous system, planned for use in XALT large format 255 mm × 255 mm pouch cells.

While the benefits of Al2O3 ALD coating for NMC are remarkable, and the same structural stabilizing effects are present for Al2O3-coated NCA, the benefits of Al2O3 coating and particularly TiO2 coating on NCA particles for high rate cycling requires further study. For example, neutron diffraction analysis is planned to confirm the nature of new phases that may have formed in NMC-TiO2 and NCA-TiO2 samples, and to quantify the amount of layered and spinel phases in coated and uncoated materials after cycling. These results will be presented in a future publication.

This work highlights the dominant effects of surface chemistry on active material performance. Continued development of surface coatings promises to open new pathways to tune properties and performance of a wide range of active materials. The new functionality of surface coatings to stabilize surface structure of Ni-rich NMC811 and NCA demonstrated in this study appears to have greater impact than metal composition or distribution, and is critical for the ability to cycle these Ni-rich materials with higher upper cutoff voltages to achieve significantly greater energy densities without sacrifice to cell cost or cycle life.

Phase transformation mitigation strategies for layered oxides by ALD coatings (Broader Impact)

The atomic layer deposition (ALD) technique has served as the most versatile coating technology for oxides. In the realm of energy storage research, it is important to maintain the coating homogeneity on the electrode oxide particle in order to restrict the undesired phenomena such as phase transformations, oxygen gas release, particle cracking, and transition metal ion dissolution that occur at the oxide particle surface that eventually diffuse towards the bulk during subsequent charge, discharge cycles. The ALD coating technique offers the unique strategy to coat the oxide particle homogenously and uniformly to mitigate these degradation phenomena. This study shows how the ALD coatings were indispensable in restricting phase transformation in layered LiMO2 (M = Mn/Al, Co, Ni). This strategy can be extended to other high-voltage, and high capacity electrodes for high-energy-density lithium-ion battery applications such as Li-Mn-rich NMC and polyionic oxides. However, selection of the coating chemistry, and understanding the interfacial effect of coating and the active oxide particles are vital as described in this present work. Therefore, this research demands a simultaneous investigation by computation and experiments to obtain the deeper insights into the effect of ALD coatings on lithium-ion battery performance.

Additional Information

How to cite this article: Mohanty, D. et al. Modification of Ni-Rich FCG NMC and NCA Cathodes by Atomic Layer Deposition: Preventing Surface Phase Transitions for High-Voltage Lithium-Ion Batteries. Sci. Rep. 6, 26532; doi: 10.1038/srep26532 (2016).


  1. (Date of access: 04/06/2016).

  2. (Date of access: 04/06/2016).

  3. G. Crabtree, E. Kócs & L. Trahey . The energy-storage frontier: Lithium-ion batteries and beyond. MRS Bull. 40, 1067 (2015).

    CAS  Article  Google Scholar 

  4. J. R. Croy, M. Balasubramanian, K. G. Gallagher & A. K. Burrell . Review of the US Department of Energy’s “Deep Dive” Effort to Understand Voltage Fade in Li- and Mn-Rich Cathodes. Acc. Chem. Res. 48, 2813 (2015).

    CAS  Article  Google Scholar 

  5. B. Xu, D. Qian, Z. Wang & Y. S. Meng . Recent progress in cathode materials research for advanced lithium ion batteries. Mater. Sci. and Eng.: R: Reports 73, 51 (2012).

    CAS  Article  Google Scholar 

  6. K. Kang, Y. S. Meng, J. Bréger, C. P. Grey & G. Ceder . Electrodes with High Power and High Capacity for Rechargeable Lithium Batteries. Science 311, 977 (2006).

    CAS  ADS  Article  Google Scholar 

  7. F. Lin et al. Surface reconstruction and chemical evolution of stoichiometric layered cathode materials for lithium-ion batteries. Nat. Commun. 5, 4529 (2014).

    ADS  Article  Google Scholar 

  8. S.-M. Bak et al. Correlating Structural Changes and Gas Evolution during the Thermal Decomposition of Charged LixNi0.8Co0.15Al0.05O2 Cathode Materials. Chem. Mater. 25, 337 (2013).

    CAS  Article  Google Scholar 

  9. D. Mohanty, J. Li, S. C. Nagpure, D. L. I. Wood & C. Daniel . Understanding the structure and structural degradation mechanisms in high-voltage, lithium-manganese–rich lithium-ion battery cathode oxides: A review of materials diagnostics. MRS Energy & Sustainability - A Review Journal 2, E15 (2015).

    Article  Google Scholar 

  10. Y. Li et al. Understanding Long-Term Cycling Performance of Li1.2Ni0.15Mn0.55Co0.1O2–Graphite Lithium-Ion Cells. J. Electrochem. Soc. 160, A3006 (2013).

    CAS  Article  Google Scholar 

  11. J. Xu, R. D. Deshpande, J. Pan, Y.-T. Cheng & V. S. Battaglia . Electrode Side Reactions, Capacity Loss and Mechanical Degradation in Lithium-Ion Batteries. J. Electrochem. Soc 162, A2026 (2015).

    CAS  Article  Google Scholar 

  12. I. Buchberger et al. Aging Analysis of Graphite/LiNi1/3Mn1/3Co1/3O2 Cells Using XRD, PGAA, and AC Impedance. J. Electrochem. Soc 162, A2737 (2015).

    CAS  Article  Google Scholar 

  13. A. J. Smith, N. N. Sinha & J. R. Dahn . Narrow Range Cycling and Storage of Commercial Li Ion Cells. J. Electrochem. Soc. 160, A235 (2013).

    CAS  Article  Google Scholar 

  14. J. Reed, G. Ceder & A. Van Der Ven . Layered-to-Spinel Phase Transition in Li × MnO2. Electrochem. Solid-State Lett. 4, A78 (2001).

    CAS  Article  Google Scholar 

  15. B. Song et al. High rate capability caused by surface cubic spinels in Li-rich layer-structured cathodes for Li-ion batteries. Sci. Rep. 3, 3094 (2013).

    Article  Google Scholar 

  16. J. B. Goodenough & K.-S. Park . The Li-Ion Rechargeable Battery: A Perspective. J. Am. Chem. Soc. 135, 1167 (2013).

    CAS  Article  Google Scholar 

  17. D. Mohanty et al. Unraveling the Voltage-Fade Mechanism in High-Energy-Density Lithium-Ion Batteries: Origin of the Tetrahedral Cations for Spinel Conversion. Chem. Mater. 26, 6272 (2014).

    CAS  Article  Google Scholar 

  18. A. R. Armstrong et al. Demonstrating Oxygen Loss and Associated Structural Reorganization in the Lithium Battery Cathode Li[Ni0.2Li0.2Mn0.6]O2. J. Am. Chem. Soc. 128, 8694 (2006).

    CAS  Article  Google Scholar 

  19. A. R. Armstrong, N. Dupre, A. J. Paterson, C. P. Grey & P. G. Bruce . Combined Neutron Diffraction, NMR, and Electrochemical Investigation of the Layered-to-Spinel Transformation in LiMnO2. Chem. Mater. 16, 3106 (2004).

    CAS  Article  Google Scholar 

  20. B. Xu, C. R. Fell, M. Chi & Y. S. Meng . Identifying surface structural changes in layered Li-excess nickel manganese oxides in high voltage lithium ion batteries: A joint experimental and theoretical study. Energy & Environ. Sci. 4, 2223 (2011).

    CAS  Article  Google Scholar 

  21. J. W. Kim et al. Unexpected high power performance of atomic layer deposition coated Li[Ni1/3Mn1/3Co1/3]O2 cathodes. J. Power Sources 254, 190 (2014).

    CAS  ADS  Article  Google Scholar 

  22. Y.-K. Sun et al. Nanostructured high-energy cathode materials for advanced lithium batteries. Nat. Mater. 11, 942 (2012).

    CAS  ADS  Article  Google Scholar 

  23. Y.-K. Sun et al. High-energy cathode material for long-life and safe lithium batteries. Nat. Mater. 8, 320 (2009).

    CAS  ADS  Article  Google Scholar 

  24. Y.-K. Sun et al. A Novel Cathode Material with a Concentration-Gradient for High-Energy and Safe Lithium-Ion Batteries. Adv. Funct. Mater. 20, 485 (2010).

    Article  Google Scholar 

  25. J. Zheng et al. Mitigating Voltage Fade in Cathode Materials by Improving the Atomic Level Uniformity of Elemental Distribution. Nano Lett. 14, 2628 (2014).

    CAS  ADS  Article  Google Scholar 

  26. Y. Cho, P. Oh & J. Cho . A New Type of Protective Surface Layer for High-Capacity Ni-Based Cathode Materials: Nanoscaled Surface Pillaring Layer. Nano Lett. 13, 1145 (2013).

    CAS  ADS  Article  Google Scholar 

  27. M. Gu et al. Formation of the Spinel Phase in the Layered Composite Cathode Used in Li-Ion Batteries. ACS Nano 7, 760 (2013).

    CAS  Article  Google Scholar 

  28. S. Wolff-Goodrich et al. Tailoring the surface properties of LiNi0.4Mn0.4Co0.2O2 by titanium substitution for improved high voltage cycling performance. Phys. Chem. Chem. Phys. 17, 21778 (2015).

    CAS  Article  Google Scholar 

  29. L. A. Riley et al. Electrochemical effects of ALD surface modification on combustion synthesized LiNi1/3Mn1/3Co1/3O2 as a layered-cathode material. J. Power Sources 196, 3317 (2011).

    CAS  ADS  Article  Google Scholar 

  30. A. M. Wise et al. Effect of Al2O3 Coating on Stabilizing LiNi0.4Mn0.4Co0.2O2 Cathodes. Chem. Mater. 27, 6146 (2015).

    CAS  Article  Google Scholar 

  31. Y. S. Jung et al. Unexpected Improved Performance of ALD Coated LiCoO2/Graphite Li-Ion Batteries. Adv. Ener. Mater. 3, 213 (2013).

    CAS  Article  Google Scholar 

  32. A. Yano et al. Surface Structure and High-Voltage Charge/Discharge Characteristics of Al-Oxide Coated LiNi1/3Co1/3Mn1/3O2 Cathodes. J. Electrochem. Soc. 162, A3137 (2015).

    CAS  Article  Google Scholar 

  33. (Date of access: 04/06/2016).

  34. (Date of access: 04/06/2016).

  35. D. Mohanty et al. Investigating phase transformation in the Li1.2Co0.1Mn0.55Ni0.15O2 lithium-ion battery cathode during high-voltage hold (4.5 V) via magnetic, X-ray diffraction and electron microscopy studies. J. Mater. Chem. A 1, 6249 (2013).

    CAS  Article  Google Scholar 

  36. J. E. Greedan, N. P. Raju & I. J. Davidson . Long Range and Short Range Magnetic Order in Orthorhombic LiMnO2. J. Solid State Chem. 128, 209 (1997).

    CAS  ADS  Article  Google Scholar 

  37. P. Strobel & B. L. Andron . Journal of Solid State Chemistry 75, 90 (1988).

    CAS  ADS  Article  Google Scholar 

  38. D. Mohanty et al. Neutron Diffraction and Magnetic Susceptibility Studies on a High-Voltage Li1.2Mn0.55Ni0.15Co0.10O2 Lithium Ion Battery Cathode: Insight into the Crystal Structure. Chem. Mater. 25, 4064 (2013).

    CAS  Article  Google Scholar 

  39. H. Gabrisch, T. Yi & R. Yazami . Transmission Electron Microscope Studies of LiNi1/3Mn1/3Co1/3O2 before and after Long-Term Aging at 70 °C. Electrochem. Solid-State Lett. 11, A119 (2008).

    CAS  Article  Google Scholar 

  40. S. C. Jung, H.-J. Kim, J. W. Choi & Y.-K. Han . Sodium Ion Diffusion in Al2O3: A Distinct Perspective Compared with Lithium Ion Diffusion. Nano Letters 14, 6559 (2014).

    CAS  ADS  Article  Google Scholar 

Download references


The research at Oak Ridge National Laboratory, managed by UT Battelle, LLC, for the U.S. Department of Energy (DOE) under contract No. DE-EE0005384, subcontracts Nos NFE-11-03678, TSA 14-587 and LS-111201A-MMW, was sponsored by the Office of Energy Efficiency and Renewable Energy for the Vehicle Technologies Office (Program Managers: Dave Howell and Peter Faguy). Work performed at PneumatiCoat Technologies under contract No. DE-SC0010230 was also sponsored by the Vehicle Technologies Office (Program Manager: Brian Cunningham). Microscopy was conducted at the Center for Nanophase Materials Sciences, which is a DOE Office of Science User Facility at the Center for Nanophase Materials Sciences, which is a DOE Office of Science User Facility. Part of this research was supported by the DOE Basic Energy Sciences (BES), Materials Sciences and Engineering Division. The authors also acknowledge BASF for supply of the electrolyte for pouch cell scale up.

Author information

Authors and Affiliations



All authors reviewed the manuscript. D.M. performed structural and electrochemical characterization, analyzed the structural data, prepared figures, and wrote the manuscript. K.D. wrote/edited the manuscript, analyzed electrochemical data and prepared figures, designed ALD coating and 2 Ah pouch cell experiments, helped design other experiments. D.M.K. helped write/edit, designed and made ALD coatings. S.D. allocated company resources for project (in-kind resources) and aided in the data analysis/discussion. V.M. designed and made 2 Ah cells, selected electrolyte, filled and formed 2 Ah cells, and tested cells. M.L. designed and made 2 Ah cells. F.A. helped write/edit and aided in the data analysis/discussion. L.A.D. performed and collected coin-cell electrochemical data and prepared figures. A.S.S. performed magnetic measurements. D.L.W. and C.D. helped write/edit the manuscript and aided in data analysis/discussion.

Corresponding authors

Correspondence to Debasish Mohanty, Kevin Dahlberg or David L. Wood.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Mohanty, D., Dahlberg, K., King, D. et al. Modification of Ni-Rich FCG NMC and NCA Cathodes by Atomic Layer Deposition: Preventing Surface Phase Transitions for High-Voltage Lithium-Ion Batteries. Sci Rep 6, 26532 (2016).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing