Despite the rarity, large negative linear compressibility (NLC) was observed in metal-organic framework material Zn(HO3PC4H8PO3H)∙2H2O (ZAG-4) in experiment. We find a unique NLC mechanism in ZAG-4 based on first-principle calculations. The key component to realize its large NLC is the deformation of H3O+ tetrahedron. With pressure increase, the oxygen apex approaches and then is inserted into the tetrahedron base (hydrogen triangle). The tetrahedron base subsequently expands, which results in the b axis expansion. After that, the oxygen apex penetrates the tetrahedron base and the b axis contracts. The negative and positive linear compressibility is well reproduced by the hexagonal model and ZAG-4 is the first MOFs evolving from non re-entrant to re-entrant hexagon framework with pressure increase. This gives a new approach to explore and design NLC materials.
Most materials contract in all directions when hydrostatically compressed. That is the volume (), area () and linear () compressibility are all positive1. Negative volume compressibility is thermodynamically impossible2. Counterintuitively, negative linear compressibility (NLC) indeed occurs in rare and remarkable crystals1,3,4,5,6. After screening of reported elastic constant tensors from approximately five hundred crystals, Baughman et al. uncovered only 13 compounds showing negative compressibility in simple inorganic or organic compounds1. Among the thirteen crystals, 11 structures were of monoclinic or lower symmetry. The typical positive linear compressibility (PLC) for crystal material lies in the range Kl ≈ 5–20 TPa−1, with lattice parameter contracting 0.5~2% for each GPa increase in pressure7. Unfortunately, experimentally determined NLC, for a long time, had been below −2 TPa−1 (−0.2 TPa−1 for LaNbO48, −1.2 TPa−1 for Se9 and −2 TPa−1 for BAsO410). Until recently, stronger NLC behavior is found: −3.8 TPa−1 for methanol monohydrate from 0 to 0.5 GPa at 160K11, −6.4 TPa−1 for α-BiB3O6 from 0 to 6.5 GPa12, −12 TPa−1 for KMn[Ag(CN)2]3 from 0 to 2.2 GPa13, −41 TPa−1 for [Fe(dpp)2(NCS)2]∙py from 0 to 0.5 GPa14, −42 TPa−1 for Zn[Au(CN)2]2 from 0 to 1.8 GPa15 and −75 TPa−1 for Ag3[Co(CN)6] from 0 to 0.19 GPa7,16. Contrary to conventional materials, a specific direction of NLC material could not only increase with the increase of hydrostatic pressure, but also remain invariant15. Therefore, NLC is a highly desirable property exploitable in the development of artificial muscles17, extremely sensitive pressure detectors, shock resistance materials and etc.
Metal-organic frameworks (MOFs) with extreme surface area and tunable pore structure have revolutionized the field of crystal engineering18,19,20,21. They consist of metal ions and organic linkers, exhibiting various unique physical and chemical properties for diverse applications22,23,24. The crystalline order between metals and ligands combined with cooperative structural transformability, forming flexible and responsive MOFs, namely soft porous frameworks. These materials can respond to mechanical stimuli in a tunable and precise fashion by molecular design, which does not exist for other known solid-state materials25,26. The elastic behaviour of soft porous crystals is usually complex, such as anisotropic flexibility, negative Poisson’s ration and high NLC25,26,27. The investigation of MOFs structure deformation under pressure can not only reveal the mechanism of these behaviours, but also can help us design new MOFs with desired mechanical property. The research of the negative linear/area compressibility of framework materials started very recently28,29,30,31. The first case of NLC in MOFs was [NH4][Zn(HCOO)3], which showed a high degree of mechanical anisotropy and negative compressibility Kl = −1.8 TPa−1 along its c axis from 0 to 0.94 GPa32. After that, NLC was found in silver(I) 2-methylimidazolate with Kl = −4.3 TPa−1 (along c axis, from 0 to 1 GPa)33 and [Ag(en)]NO3-I with Kl = −28.4 TPa−1 (along a axis, from 0 to 0.92 GPa)34. Clearfield and others pioneered named the MOFs formed from the linker molecules with alkyl chains as zinc alkyl gate(ZAG) because of the likeness of the structure to a child safety gate (Fig. 1(a))21,35. Recently, Gagnon et al. measured the lattice parameters of ZAG-4 under pressure with single crystal X-ray diffraction and observed NLC36,37. The b axis of ZAG-4 increases almost 2% in the range of 1.65–2.81 GPa, indicating a strong NLC (Kl ≈ −16 TPa−1). Due to the inherently small atomic scattering factor of hydrogen, the exact positions of H2O in ZAG-4 can not be easily detected by X-ray diffraction technique38. Aurelie U Ortiz et al. calculated the ZAG-4 structure under pressure, found a proton transfer and attributed the NLC (from 1.65 to 2.81 GPa) to this structural transition39. However, PLC was observed after NLC in experiment. This explanation did not answer why NLC and PLC occurs subsequently after proton transfer. Therefore, an unambiguous mechanism for the NLC in ZAG-4 is still an unresolved matter.
Density functional calculation, an integral part of MOFs research, is complementary to experimental techniques and offers invaluable information in characterization and understanding of systems27,40,41,42. In order to elucidate the NLC mechanism of ZAG-4, we performed the density functional calculation using both PBE and Wu-Cohen (WC) functional43 as implemented in the Quantum Espresso package44 to determine their atomic structures under pressure. The PBE functional, usually overestimating lattice parameters, has been widely used in density functional calculations and the WC functional is known to be accurate in predicting solid volumes45,46,47. The wave function was expanded in a plane-wave basis set with an energy cutoff of 70 Ry and the first Brillouin zone was sampled on a 3 × 3 × 4 mesh. The ultra-soft pseudopotential was used to represent the electron-ion interaction.
The conventional unit cell of ZAG-4 is depicted in Fig. 121,35,36. It has a base-centered monoclinic lattice with the b axis perpendicular to the a-c plane. Herein, the three building blocks of ZAG-4 are the inorganic Zn-O-P-O chains and two bridging ligands (C4H8 and H2O). The 1D Zn-O-P-O chains orient along the c axis and are linked with each other along the b axis by H2O molecules. So as to give a detailed description of the linkage between H2O molecules and Zn-O-P-O chains, we enlarge the bridging zone in Fig. 1(c). The ZnO4 and PO3C tetrahedrons are linked along the c axis by sharing oxygen atoms and form the Zn-O-P-O chains. The water molecules are located between two Zn-O-P-O chains. As a result, Zn-O-P-O chains bridged by H2O form an inorganic 2D structure parallel to the b-c plane. Furthermore, the inorganic planes are linked with each other along the a axis by C4H8, which is directly bonded with the P cations. In brief, the 3D framework is established with the inorganic Zn-O-P-O chains extending along the c axis linked with each other by C4H8 chains and H2O molecules along the a and b axis, respectively.
Firstly, we use the experimental crystal structure at zero pressure as our initial point and fully relax the lattice parameters and atomic positions with PBE functional. The calculated lattice parameters (a = 19.00 Å, b = 8.41 Å, c = 8.18 Å and volume = 1214.27 Å3) agree well with experimental results (a = 18.51 Å, b = 8.29 Å, c = 8.27 Å and volume = 1160.55 Å3). As the calculated volume is slight larger than the experimental value, our calculated bulk modulus of (11.6 GPa) is slightly lower than the experimental result (11.7 GPa). Although it is about one thirty-fifth of the bulk modulus of sp3 carbon allotrope (around 400 GPa)48,49, this value is higher than that of porous MOFs MIL-53 and NH2-MIL-5330,50, but is lower than that of dense MOFs51,52,53,54.
In order to explore its NLC mechanism, we applied hydrostatic pressure to ZAG-4 and investigate its structure variation. The calculated lattice parameters, accompanied with available experimental data36, are shown in Fig. 2. We increase pressure and take the previously optimized structure as the initial point of higher pressure condition. In this way, we increase pressure to 8 GPa and optimize the structure step by step.
As can be seen in Fig. 2, the experimental lattice parameters are well reproduced by our calculation based on the PBE functional. It is well-known that PBE calculation typically overestimates the lattice parameters by 1–2%. As far as the overestimation is concerned, our calculated results agree excellently with the experimental data. As pointed by Gagnon et al., the alkyl chains serve like a spring cushion and hence contract much under pressure36. With pressure increasing from zero to 2 GPa, the calculated volume compressibility is around 71 TPa−1 and that of the experimental value from zero to 1.65 GPa is around 69 TPa−1. The calculated b and c axis have a jump from 2.25 to 2.5 GPa, which is accompanied with the proton transfer. Below 2.25 GPa, the H1 is close to the PCO3 octahedron and far away from the H2O (Fig. 1(c)). When pressure increases to 2.5 GPa, the proton turns to be close to the H2O and forms the H3O+ tetrahedron. Aurélie U Ortiz et al. also found this proton transfer and the H3O+ tetrahedron formation36,39. They used the wine-rack motif to explain the NLC of ZAG-4 after the proton transition. However, as show in Fig. 2b, NLC does not occur immediately after proton transfer. Instead, the b axis smoothly expands from 5 to 6.25 GPa (blue shaded area in Fig. 2(b)), which is far away from the proton transfer pressure (2.5 GPa). This indicates that proton transfer is not enough to lead to the NLC of ZAG-4. There must be something new.
We repeat these calculations with the WC functional, because the lattice constants of solids as determined by it are between LDA and PBE results and on average closer to experiment45,46,47. In the WC results of ZAG-4, the H3O+ tetrahedron is formed at zero pressure. Consequently, the jump from 2.25 to 2.5 GPa in Fig. 2 does not exist in WC functional results (Supplementary Information). Although the H3O+ is formed at zero pressure, the NLC does not take place immediately from zero pressure. Instead, the NLC of the b axis occurs in WC functional results from 3.5 to 4.75 GPa. This means the H3O+ tetrahedron and the NLC of b axis are reproduced in WC functional results as well.
We now pay our attention to the changes under pressure of the b axis. The experimentally observed NLC is from 1.65 to 2.81 GPa with the b axis increasing 1.8% (red shaded area in Fig. 2(b))36. The experimental data are too few (only two) to give a detailed description of the lattice parameters evolution. So as to draw a complete picture, we calculate the lattice parameters from 5 to 7 GPa with a small pressure step of 0.25 GPa. As shown in Fig. 3(a), the b axis increases from 5 GPa and reaches its maximum at 6.25 GPa. Accordingly, the average NLC from 5 to 6.25 GPa is −11 TPa−1, as strong as that of KMn[Ag(CN)2]3 (−12 TPa−1, from 0 to 2.2 GPa)13. After that, the b axis decreases with pressure increase and hence the linear compressibility turns to be positive.
It is the deformation of the H3O+ tetrahedron that leads to the NLC of the b axis. As shown in Fig. 1(d,e), the apex oxygen of the H3O+ tetrahedron is above the H triangle at 5 GPa. The distance (dO-H triangle) between the apex oxygen and the H triangle is defined to be positive at this condition (left inset of Fig. 3(a)). Comparing the left and right inset of Fig. 3(a) (or Fig. 1(e,f)), we find that dO-H triangle turns from positive to negative with pressure increase. At the same time, evolution of dO-H triangle is completely accompanied with the evolution of the b axis from expansion to contraction. We also calculate the structure of dehydrated ZAG-4. By deleting the H2O molecules in ZAG-4 at zero pressure, we get the initial structure of dehydrated ZAG-4. Following the process of Fig. 2, we increase pressure and optimize the structure step by step. The calculated results (Supplementary Information) show that the b axis of dehydrated ZAG-4 decreases smoothly with pressure increase. This means that the H3O+ tetrahedron deformation is essential to the NLC of ZAG-4.
It is easy to understand the NLC mechanism of ZAG-4 with the following picture in mind. Initially, dO-H triangle of the H3O+ tetrahedron is positive at low pressure. The apex oxygen moves towards the H triangle with pressure increase. It leads to the decrease of dO-H triangle (Fig. 3(a)), the area expansion of hydrogen triangle (Fig. 3(b)) and the expansion of the b axis (Fig. 3(a)). Therefore, the NLC of the b axis is directly results from the H3O+ tetrahedron deformation. With further pressure increase, the apex oxygen penetrates the H triangle and dO-H triangle turns to be negative (right inset of Fig. 3(a)). From then on, the apex oxygen moves away from the H triangle. Consequently, both the area of the H triangle and the b axis decrease with pressure increase. The calculated results using Wu-Cohen functional also show these characteristic features of H3O+ tetrahedron deformation. In brief, the b axis is expanded by the apex oxygen approaching the H triangle and is contracted by the apex oxygen moving away from the H triangle.
There are four microscopic mechanisms frequently used: (i) ferroelastic phase transition, (ii) polyhedral tilt, (iii) helical system and (iv) wine-rack, honeycomb or related topology.6 The NLC and PLC mechanism of ZAG-4 can be explained by the hexagonal model55,56. The non re-entrant and re-entrant hexagons are illustrated in the left and right inset of Fig. 4, respectively. The linear compressibility Kl of this mode can be given analytically as56
in which, as illustrated in the left inset of Fig. 4, i and h are the lengths of the inclined and horizontal ribs, respectively; θ is the angle between the inclined rib and the vertical direction; φh and φs are the hinging and stretching force constants per unit thickness of the hexagonal plane, respectively. The first term of equation (1) assumes that ribs are rigid along their lengths and the deflection totally originates from the change of angle θ, while the second one represents that hexagon deforms solely through stretching of ribs and θ does not change at all.
With pressure increase, θ deceases from positive to negative, which is similar to the H3O+ tetrahedron deformation depicted in the inset of Fig. 3(a). Figure 4 shows the calculated linear compressibility with i/h = 3 and φs/φh = 10. Similarly with the b axis evolution in Fig. 3(a), the left side of Fig. 4 is NLC (34° > θ > 3°) and the right side is PLC (θ < 3°). There are two H3O+ tetrahedrons with positive dO-H triangle in Fig. 1(d). This condition is similar to the non re-entrant hexagon with NLC. When dO-H triangle becomes negative, it turns to be similar to the re-entrant hexagon with positive NL. Therefore, the NLC mechanism of ZAG-4 can be simplified to the hexagonal model.
In conclusion, based on the first-principle calculations, we investigated the crystal structure of ZAG-4 under pressure. Our calculated evolutions of the lattice parameters with pressure excellently agree with the experimental results. The NLC of ZAG-4 occurs in the pressure span of 1.5 GPa (1.16 GPa) with the b axis increasing 1.2% (1.8%) in calculation (experiment). By inspecting the evolution of atomic position with pressure, we found that the H3O+ tetrahedron deformation is the key point of understanding the large NLC. Initially, with pressure increase, the apex oxygen moves toward the tetrahedron base and expands the H triangle and the b axis. After penetrating the H triangle, the apex oxygen moves away and then the b axis contracts with pressure increase. The NLC characteristic of ZAG-4 is well reproduced by the hexagonal model, which gives a vivid explanation for the linear compressibility switch from negative to positive values. Usually, crystal has either non re-entrant or re-entrant hexagon framework. ZAG-4 is the first MOFs evolving from non re-entrant to re-entrant hexagon framework with pressure increase. Our finding prescribes a general way to obtain the rare NLC property in complex structures. As H2O molecules abundantly exist in inorganic and organic materials, it will prompt more investigations on negative compressibility in complex materials57.
How to cite this article: Wang, H. et al. H3O+ tetrahedron induction in large negative linear compressibility. Sci. Rep. 6, 26015; doi: 10.1038/srep26015 (2016).
Baughman, R. H. Materials with Negative Compressibilities in One or More Dimensions. Science 279, 1522–1524 (1998).
Barnes, D. L., Miller, W., Evans, K. E. & Marmier, A. Modelling negative linear compressibility in tetragonal beam structures. Mech. Mater. 46, 123–128 (2012).
Kornblatt, A. J. Materials with Negative Compressibilities. Science 281, 143a–143 (1998).
Lakes, R. & Wojciechowski, K. W. Negative compressibility, negative Poisson’s ratio and stability. Phys. Status Solidi B 245, 545–551 (2008).
Coudert, F. X. Systematic investigation of the mechanical properties of pure silica zeolites: stiffness, anisotropy and negative linear compressibility. Phys. Chem. Chem. Phys. 15, 16012–16018 (2013).
Cairns, A. B. & Goodwin, A. L. Negative linear compressibility. Phys. Chem. Chem. Phys. 17, 20449–20465 (2015).
Goodwin, A. L., Keen, D. A. & Tucker, M. G. Large negative linear compressibility of Ag3[Co(CN)6]. Proc. Natl. Acad. Sci. USA 105, 18708–18713 (2008).
Mariathasan, J. W. E., Finger, L. W. & Hazen, R. M. High-pressure behavior of LaNbO4 . Acta Crystallogr., Sect. B: Struct. Sci. 41, 179–184 (1985).
McCann, D. R. Compressibility of Hexagonal Selenium by X-Ray and Neutron Diffraction. J. Appl. Phys. 43, 1432 (1972).
Haines, J. et al. Collapsing Cristobalitelike Structures in Silica Analogues at High Pressure. Phys. Rev. Lett. 91, 015503 (2003).
Fortes, A. D., Suard, E. & Knight, K. S. Negative linear compressibility and massive anisotropic thermal expansion in methanol monohydrate. Science 331, 742–746 (2011).
Kang, L. et al. Negative linear compressibility in a crystal of α-BiB3O6 . Sci. Rep. 5, 13432 (2015).
Cairns, A. B., Thompson, A. L., Tucker, M. G., Haines, J. & Goodwin, A. L. Rational design of materials with extreme negative compressibility: selective soft-mode frustration in KMn[Ag(CN)2]3 . J. Am. Chem. Soc. 134, 4454–4456 (2012).
Shepherd, H. J. et al. Antagonism between extreme negative linear compression and spin crossover in [Fe(dpp)2(NCS)2]py. Angew. Chem. Int. Ed. 51, 3910–3914 (2012).
Cairns, A. B. et al. Giant negative linear compressibility in zinc dicyanoaurate. Nat. Mater. 12, 212–216 (2013).
Calleja, M., Goodwin, A. L. & Dove, M. T. Origin of the colossal positive and negative thermal expansion in Ag3[Co(CN)6]: an ab initio density functional theory study. J. Phys.: Condens. Matter 20, 255226 (2008).
Aliev, A. E. et al. Giant-stroke, superelastic carbon nanotube aerogel muscles. Science 323, 1575–1578 (2009).
Graham, A. J., Allan, D. R., Muszkiewicz, A., Morrison, C. A. & Moggach, S. A. The Effect of High Pressure on MOF-5: Guest-Induced Modification of Pore Size and Content at High Pressure. Angew. Chem. Int. Ed. 50, 11138–11141 (2011).
Tan, J. C. & Cheetham, A. K. Mechanical properties of hybrid inorganic-organic framework materials: establishing fundamental structure-property relationships. Chem. Soc. Rev. 40, 1059–1080 (2011).
Costantino, F., Donnadio, A. & Casciola, M. Survey on the phase transitions and their effect on the ion-exchange and on the proton-conduction properties of a flexible and robust Zr phosphonate coordination polymer. Inorg. Chem. 51, 6992–7000 (2012).
Gagnon, K. J., Perry, H. P. & Clearfield, A. Conventional and unconventional metal-organic frameworks based on phosphonate ligands: MOFs and UMOFs. Chem. Rev. 112, 1034–1054 (2012).
Gu, Z. Y. & Yan, X. P. Metal-organic framework MIL-101 for high-resolution gas-chromatographic separation of xylene isomers and ethylbenzene. Angew. Chem. Int. Ed. 49, 1477–1480 (2010).
Gu, Z. Y., Yang, C. X., Chang, N. & Yan, X. P. Metal-organic frameworks for analytical chemistry: from sample collection to chromatographic separation. Acc. Chem. Res. 45, 734–745 (2012).
Gu, Z.-Y., Park, J., Raiff, A., Wei, Z. & Zhou, H.-C. Metal-Organic Frameworks as Biomimetic Catalysts. ChemCatChem 6, 67–75 (2014).
Schneemann, A. et al. Flexible metal–organic frameworks. Chem. Soc. Rev. 43, 6062–6096 (2014).
Li, W., Henke, S. & Cheetham, A. K. Research Update: Mechanical properties of metal-organic frameworks–Influence of structure and chemical bonding. APL Materials 2, 123902 (2014).
Ortiz, A. U., Boutin, A., Fuchs, A. H. & Coudert, F. X. Anisotropic elastic properties of flexible metal-organic frameworks: how soft are soft porous crystals? Phys. Rev. Lett. 109, 195502 (2012).
Jiang, X. et al. Isotropic Negative Area Compressibility over Large Pressure Range in Potassium Beryllium Fluoroborate and its Potential Applications in Deep Ultraviolet Region. Adv. Mater. 27, 4851–4857 (2015).
Qiao, Y., Wang, K., Yuan, H., Yang, K. & Zou, B. Negative Linear Compressibility in Organic Mineral Ammonium Oxalate Monohydrate with Hydrogen Bonding Wine-Rack Motifs. J. Phys. Chem. Lett. 6, 2755–2760 (2015).
Serra-Crespo, P. et al. Experimental evidence of negative linear compressibility in the MIL-53 metal–organic framework family. Cryst Eng Comm 17, 276–280 (2015).
Cai, W. et al. Giant negative area compressibility tunable in a soft porous framework material. J. Am. Chem. Soc. 137, 9296–9301 (2015).
Li, W. et al. Negative linear compressibility of a metal-organic framework. J. Am. Chem. Soc. 134, 11940–11943 (2012).
Ogborn, J. M., Collings, I. E., Moggach, S. A., Thompson, A. L. & Goodwin, A. L. Supramolecular mechanics in a metal–organic framework. Chem. Sci. 3, 3011 (2012).
Cai, W. & Katrusiak, A. Giant negative linear compression positively coupled to massive thermal expansion in a metal–organic framework. Nat. Commun. 5 1–8 (2014).
Fu, R.-B. et al. Crystal structures of five transition-metal 1,4-butylenediphosphonates. Polyhedron 22, 2739–2744 (2003).
Gagnon, K. J., Beavers, C. M. & Clearfield, A. MOFs under pressure: the reversible compression of a single crystal. J. Am. Chem. Soc. 135, 1252–1255 (2013).
Clearfield, A. Flexible MOFs under stress: pressure and temperature. Dalton Trans. 45, 4100–4112 (2016).
Wang, J. et al. Potassium-modified Mg(NH2)2/2 LiH system for hydrogen storage. Angew. Chem. Int. Ed. 48, 5828–5832 (2009).
Ortiz, A. U., Boutin, A., Gagnon, K. J., Clearfield, A. & Coudert, F. X. Remarkable pressure responses of metal-organic frameworks: proton transfer and linker coiling in zinc alkyl gates. J. Am. Chem. Soc. 136, 11540–11545 (2014).
Odoh, S. O., Cramer, C. J., Truhlar, D. G. & Gagliardi, L. Quantum-Chemical Characterization of the Properties and Reactivities of Metal-Organic Frameworks. Chem. Rev. 115, 6051–6111 (2015).
Coudert, F.-X. & Fuchs, A. H. Computational characterization and prediction of metal–organic framework properties. Coordin. Chem. Rev. 307, 211–236 (2016).
Fuentes-Cabrera, M., Nicholson, D. M., Sumpter, B. G. & Widom, M. Electronic structure and properties of isoreticular metal-organic frameworks: The case of M-IRMOF1 (M = Zn, Cd, Be, Mg and Ca). J. Chem. Phys. 123, 124713 (2005).
Wu, Z. & Cohen, R. More accurate generalized gradient approximation for solids. Phys. Rev. B 73, 235116 (2006).
Giannozzi, P. et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys. Condens. Matter 21, 395502 (2009).
Wu, Z. & Cohen, R. E. More accurate generalized gradient approximation for solids. Phys. Rev. B 73, 235116 (2006).
Tran, F., Laskowski, R., Blaha, P. & Schwarz, K. Performance on molecules, surfaces and solids of the Wu-Cohen GGA exchange-correlation energy functional. Phys. Rev. B 75, 115131 (2007).
Bhattacharjee, S., Bousquet, E. & Ghosez, P. Engineering Multiferroism in CaMnO3 . Phys. Rev. Lett. 102, 117602 (2009).
Bai, Y. et al. First-principles investigation in the Raman and infrared spectra of sp3 carbon allotropes. Carbon 78, 70–78 (2014).
Zhao, Z. et al. Tetragonal allotrope of group 14 elements. J. Am. Chem. Soc. 134, 12362–12365 (2012).
Serra-Crespo, P., Stavitski, E., Kapteijn, F. & Gascon, J. High compressibility of a flexible metal–organic framework.Rsc. Adv. 2, 5051–5053 (2012).
Tan, J. C. & Cheetham, A. K. Mechanical properties of hybrid inorganic–organic framework materials: establishing fundamental structure–property relationships. Chem. Soc. Rev. 40, 1059–1080 (2011).
Spencer, E. C. et al. Pressure‐Induced Bond Rearrangement and Reversible Phase Transformation in a Metal–Organic Framework. Angew. Chem. Int. Ed. 53, 5583–5586 (2014).
Sun, S. et al. Mechanical Properties of a Calcium Dietary Supplement, Calcium Fumarate Trihydrate. Inorg. Chem. 54, 11186–11192 (2015).
Feng, G. et al. High pressure behaviour and elastic properties of a dense inorganic–organic framework. Dalton Trans. 45, 4303–4308 (2016).
Masters, I. G. & Evans, K. E. Models for the elastic deformation of honeycombs. Compos. Struct. 35, 403–422 (1996).
Grima, J. N., Attard, D., Caruana-Gauci, R. & Gatt, R. Negative linear compressibility of hexagonal honeycombs and related systems. Scripta Mater. 65, 565–568 (2011).
Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272–1276 (2011).
This work is supported by the National Natural Science Foundation of China (U1404111, 11504089, 21505076) and the Young Scientist Foundation of Henan University of Science and Technology (2013QN026).
The authors declare no competing financial interests.
Electronic supplementary material
About this article
Cite this article
Wang, H., Feng, M., Wang, YF. et al. H3O+ tetrahedron induction in large negative linear compressibility. Sci Rep 6, 26015 (2016). https://doi.org/10.1038/srep26015