Abstract
The emergence of two-dimensional metallic states at the LaAlO3/SrTiO3 (LAO/STO) heterostructure interface is known to occur at a critical thickness of four LAO layers. This insulator to-metal transition can be explained through the “polar catastrophe” mechanism arising from the divergence of the electrostatic potential at the LAO surface. Here, we demonstrate that nanostructuring can be effective in reducing or eliminating this critical thickness. Employing a modified “polar catastrophe” model, we demonstrate that the nanowire heterostructure electrostatic potential diverges more rapidly as a function of layer thickness than in a regular heterostructure. Our first-principles calculations indicate that for nanowire heterostructures a robust one-dimensional electron gas (1DEG) can be induced, consistent with recent experimental observations of 1D conductivity at LAO/STO steps. Similar to LAO/STO 2DEGs, we predict that the 1D charge density decays laterally within a few unit cells away from the nanowire; thus providing a mechanism for tuning the carrier dimensionality between 1D and 2D conductivity. Our work provides insight into the creation and manipulation of charge density at an oxide heterostructure interface and therefore may be beneficial for future nanoelectronic devices and for the engineering of novel quantum phases.
Similar content being viewed by others
Introduction
The unique physical properties of oxides, such as high dielectric constants and possible couplings between electric, magnetic and elastic degrees of freedom have long been explored for use in sensors and low power-high speed memories. Emergent phenomena, such as the appearance of a two-dimensional electron gas (2DEG) at oxide heterointerfaces1,2,3 have created the opportunity for application in transistors3,4,5,6,7,8,9,10 in addition to providing a platform for studying the confinement of electrons in two dimensions. For example, the prototypical heterostructure, LaAlO3(LAO)/SrTiO3(STO), exhibits a wealth of intriguing properties at the interface such as metallicity11,12, magnetism13 and novel quantum phases such as superconductivity14 that are absent in the parent compounds.
The emergence of a 2DEG in LAO/STO can be understood through the “polar catastrophe” model illustrated in Fig. 1(a,d)15,16,17. In an unreconstructed superlattice, the electrostatic potential diverges as the number of LAO layers increases due to the alternating nominal + 1/− 1 charges in the LaO and AlO2 layers, respectively. At roughly 4 layers, when the magnitude of the divergent potential is comparable to the STO band gap, half of an electron per AlO2 surface layer is transferred to the interface (see Fig. 1(d)) in order to compensate for the large surface potential3. Surprisingly, recent experiments demonstrate that this critical thickness can be significantly altered through nanostructuring; thereby producing interfacial conductivity below the 4 LAO layers required for the “polar catastrophe” mechanism. Here, the LAO nanowire was comprised of alternating one and three LaAlO3 unit cell nanowires, fabricated by standard lithography techniques and thought to result in conducting one-dimensional channels at the boundary between the 1 and 3 layer LAO step18.
Stimulated by this experimental study, we investigate a nanowire heterostructure model formed by placing a LAO nanowire on top of a STO (001) substrate. The stepped LAO surface can be regarded as consisting of adjacent one and m LAO layers, each 2 unit cells wide, repeated in one lateral direction (see Fig. 2). Therefore, we henceforth refer to this interface as a 1/m nanowire heterostructure; where a 1/3 nanowire is similar to the experimental setup of Ron et al.18. Similarly, a regular interface, e.g., four LAO layers on a STO substrate would be denoted as a 4/0 interface. We emphasize that our nanowire model differs from traditional heterostructures due to the imbalance in the layer-by-layer charge. As such, our model serves as the first prototype for understanding emerging nanowire heterostructures.
In this article, we explore the electronic structure origins of metallicity in stepped nanostructured LAO/STO interfaces (nanowires) using first-principles density functional theory. We demonstrate that signatures of a confined electron gas appear below the aforementioned threshold number in these nanostructures. To explain this phenomenon, we invoke a modified polar catastrophe model to understand the occurrence of metallic states in these nanowire heterostructures. Our results indicate that the larger charge difference between the La3O2 and Al2O5 layers in the non-stoichiometric nanowires causes a faster buildup of potential across the slab, thereby driving this charge transfer below the expected 4 layers. Interestingly, our results suggest the presence of tunable 1D conduction channels due to the nanowire geometry. Also, we find that because of the fact that the La3O2 and Al2O5 layers no longer have a + n/− n charge balance, as in traditional heterostructures, the potential across the slab continues to grow with increasing layers, resulting in an increase in carrier densities when going from the 1/2 to the 1/3 nanostructures. Furthermore, for 1/m nanostructures we find a crossover from 1D conducting channels to more 2D-like carrier densities as m decreases from 3 to 2.
Conversely, we observe no charge transfer in the stoichiometric nanostructures which have a + 1/− 1 charge balance and in fact the insulator-metal transition (IMT) occurs at a much higher value than 4-layers; closer to 8 layers. Again, this can be understood based on a simple electrostatic model which shows that the interfacial polar discontinuity and hence the interfacial charge density and the corresponding potential is directly proportional to the layer coverage; thus half-coverage leads to a transition occurring at nearly twice the critical thickness of 4 LAO layers found with full LAO coverage. This is consistent with the experimental study on the LAO-STO solid-solution overlayer, where the critical thickness was found to increase inversely proportional to the concentration of LAO in the solid-solution19. Ultimately, these results suggest that nanostructuring provides tremendous opportunities for tuning the number and dimensionality of carriers at an oxide interface; which has natural consequences for the design of novel devices based on oxide heterostructures.
Methods and Computational Details
We performed density-functional theory (DFT) calculations using the projector augmented wave (PAW) method as implemented in the Vienna Ab-initio Simulation Package (VASP)20,21,22. The Sr 4s4p5s, Ti 3p3d4s, La 5s5p5d6s, Al3s3p and O 2s2p electrons were treated as valence electrons. For all calculations, a cutoff energy of 400 eV was used to expand the electronic wave functions in the plane wave basis set. We used the Perdew-Burke-Ernzerhof (PBE) exchange-correlation functional23. To deal with the electron localizations of Ti d and La f orbitals in the LAO/STO heterostructure, we employed the Dudarev method with a rotationally invariant Ueff = U-J = 7.0 eV and 7.5 eV for Ti d and La f orbitals, respectively24. These parameters have also been used in a previous study25. In addition, with the selected U-J parameters, we confirm that the critical number of LAO layers for the insulator-to-metal transition at bulk interfaces is four, which agrees with previous theoretical studies26,27.
For all systems we considered 4 in-plane unit cells in the lateral direction along x and 1 unit cell in y (i.e., along the nanowire) (Fig. 2). The in-plane lattice constants in the x and y directions were fixed to 4a0 and a0 respectively, where a0 is the calculated PBE+ U lattice constant of bulk STO, i.e. a0 = 3.943 Å. Nine and a half unit cells of STO layers were used to model the STO (001) substrate. Similar to ref. 28, each supercell contained two symmetric surfaces. LAO nanowires were arranged such that the stepped LAO surface had an alternating pattern of two unit cells of one LAO layer and then two unit cells of m LAO layers (Fig. 2). A vacuum spacing of ~20 Å was used to ensure that the interactions between the two surfaces were negligible. We considered two types of nanowire structures: non-stoichiometric and stoichiometric. In the nonstoichiometric case, a complete unit cell was generated in the m layers of the nanowire, whereas in the stoichiometric case, ions were removed in order to retain charge neutrality by enforcing the LAO formula unit. The k-point sampling used the Monkhorst-Pack scheme29 and employed a Γ -point-centered 8 × 8 × 8 mesh for the bulk calculations and a Γ -point-centered 2 × 8 × 1 mesh for the interface calculations. For the band structure calculations, we used 40 k points along the high-symmetry paths. All atomic positions were relaxed until the Hellmann-Feynman forces were less than 0.03 eV/Å. To confirm the 1D nature of the electron gas, additional supercells containing 6 unit cells in the x direction were studied for both the 1/2 and 1/3 non-stoichiometric nanostructures. In these cases, an alternating pattern of 4 unit cells of 1 layer of LAO and 2 unit cells of m layers of LAO were modeled. This geometry was chosen since 4 unit cells is larger than the previously predicted electronic gas screening length of 2–3 unit cells in STO28,30,31,32,33,34. Notably, the largest supercell in this work consists of as many as 396 atoms.
Results
We start with the discussion of the electronic structure of the non-stoichiometric nanostructures. Figure 3 shows the band structure of the 1/2 and 1/3 non-stoichiometric nanostructures. In both cases, the interfacial Ti d bands cross the Fermi level demonstrating the unexpected metallicity. More interestingly, the metallic states of the nanostructures exhibit characteristics of a 2DEG35,36,37,38,39; as can be seen by the parabolic dispersions around Γ and the flat bands in the Γ -X and Γ -Y (not depicted here) directions. An orbital-resolved analysis shows that the metallic states just below the Fermi level are comprised of the three Ti t2g d bands, i.e. the light Ti dxy band and the significantly heavier (along Γ -X and Γ -Y) dxz and dyz bands. Note that the now occupied Ti d bands for the 1/3 non-stoichiometric structures are much lower in energy than those of the 1/2 nanostructure, suggesting a significant change in the carrier densities between the two systems; with more electrons at the interface of the 1/3 nanostructure.
Figure 4 shows the layer averaged spatial distribution of the excess electrons in the TiO2 layers in STO obtained by integrating the partial density of states within the energy window between − 1.0 eV and the Fermi level for each Ti atom. First, we see that there is a larger charge accumulation in the Ti layer near the interface in the non-stoichiometric 1/3 layer than in the 1/2 layer. Similar to regular LAO/STO heterostructures28,30,31,32,33,34, the transferred electrons are not strictly confined to the interface, but decay several layers into the STO (001) substrate. A summation of the total electron density gives 0.5 and 1.0 electrons per surface unit cell for the 1/2 and 1/3 nanostructures, respectively. This translates to 0.25 and 0.5 e− per interface unit cell.
To understand the driving force behind the electronic reconstruction in the 1/2 and 1/3 nanostructures, we propose a modified “polar catastrophe” model15. In the case of the unreconstructed non-stoichiometric systems, the layers are comprised of La1.5O and AlO2.5 layers with nominal charges of + 2.5 and − 2 respectively.
Even for the 1/2 case (see Fig. 1b,e), this would result in a large enough potential buildup across the LAO layers (comparable to the STO band gap and on the order of that in the standard LAO/STO heterostructures). To compensate for this charge buildup, a simple electrostatic model estimates the need for a total charge transfer of 0.5 e−/LAO surface unit cell (or rather 0.25 e−/interface unit cell). This estimate is in remarkable agreement with the charge density profile (i.e. the sum of the layer averaged charge densities) depicted in Fig. 4(a). However, due to the fact that the La1.5O layer has a much larger absolute charge than the AlO2.5 layer, the addition of an additional LAO layer once again would result in a diverging potential (Fig. 1c,f); requiring an additional 0.5 e−/LAO surface unit cell to be transferred to the interface. In this context, an electrostatic model would suggest the need for a total of 0.5 e−/interface unit cell to compensate for this potential divergence. This is once more consistent with our DFT findings for the 1/3 system. Furthermore, it suggests that the growth of additional layers may be useful in inducing even more charge transfer (electronic reconstruction) and thus could be important for tuning the carrier densities at this interface.
Interestingly, we find that within a layer the distribution of electrons is also not uniform. Figure 5 depicts the excess electronic charge on the Ti atoms at the interface in the 1/2 and 1/3 non-stoichiometric nanowire heterostructures. Here, we see that the ions below the nanowire layers have a larger charge accumulation, which seems to decay as we move away from the interface. A Gaussian fit (Fig. 5 solid black lines) to the data, assuming overlapping density from periodic wire images, suggests that the true system maybe one-dimensional with the typical 3 unit cell spread of electrons away from the nanowire overlayer; as commonly observed in oxide heterostructure 2DEGs28,30,31,32,33,34,37,38,39. This implies the existence of a 1DEG state brought about through the localization of the overlayer potential to just below the nanowire. Our results also suggest that the 1DEG state may be more clearly defined for nanowires separated by more than 2 unit cells; as was done in the recent experiments18. Furthermore, we also infer that the electron density at the interface would be tunable through modulation of the separation between the nanowires.
To further examine the 1D nature of the conducting states, we simulated larger supercells with 6 unit cells in the x direction, comprised of alternating 4 unit cell-wide steps of 1 layer LAO adjacent to 2 unit cell-wide steps of m layers of STO (i.e. a separation of 4 unit cells between nanowires). Indeed, for the 1/3 non-stoichiometric nanowires we find that the charge density is strongly confined to the layers below the 3 LAO step. Again we see that there should be a few unit cells dispersion of carrier density away from the 3 LAO layer step (Fig. 5 top). More interestingly, we see that in the case of the 1/2 layer, there is less confinement of electrons and carriers are now almost evenly smeared across the interface (Fig. 5 bottom). This implies the formation of a 2D electron gas rather than a 1D nanowire. In light of these results, we can reinterpret the previous experimental results as follows: for the 1/3 nanostructure the 1D-like conductivity measured in a similar LAO-STO step18 may be due to the large confinement within the nanowire of the electrons transferred from the surface layer of the 3 step LAO nanowire to the interface Ti-d orbitals. However, we would expect that for the 1/2 nanostructure, there would be nearly a factor of two drop in the number of carriers inside the nanowire. In the limit of a large nanowire diameter (as opposed to 2 u.c. diameter in our simulation) we therefore predict a weak 2D electron gas. This is consistent with the absence of a 1D-like repeated modulation in the experimental measurement of the conductivity under an applied voltage in recent experiments on the 1/2 stepped structure40.
Commensurate with the electronic reconstruction we observe significant atomic displacements away from the interface in the Ti layers in the 1/2 and 1/3 non-stoichiometric 4 unit cell-wide nanostructures. Figure 4(c) depicts the magnitude of the layer-averaged Ti displacements at the TiO2 layers near the interface. Furthermore, we find that the displacements in the 1/2 nanowire heterostructure is roughly half of that in the 1/3 case. These displacements are consistent with the notion of polar distortions assisting in charge screening due to electrostriction at the interface and with the idea that larger distortions are linked to larger charge densities at the interface16,17,28,41. In particular, the magnitude of the average interfacial displacement in the 1/3 interface is similar to that observed in previous studies of LAO/STO32,33,42,43,44,45 and La δ -doped STO superlattices37,38,39 where the interfacial charge density is also 0.5 e− per interface unit cell. Again, a survey of individual ionic displacements shows signatures of 1D behavior; with larger displacements directly below the nanowire (i.e. on ions with larger charge densities).
Given the large changes in carrier densities at the interfaces, a semiconductor physics-based interpretation would suggest significant changes in mobilities of the electrons at the interface (either due to changes in band effective masses or scattering lengths). To try to understand the effects on changes in carrier densities we evaluated the band effective masses of the two systems. (N.B. Scattering lengths are not accessible from DFT band structure calculations.) For both of the 1/2 and 1/3 nanowire heterostructures, the electron effective masses of the dxy band at the Γ point are nearly isotropic with 0.53 me, where me is the electron rest mass. In contrast, the electron effective masses of the dyz and dxz bands are anisotropic. For example, along the Γ to X direction, the flat dyz band shows much heavier electron masses of 4.47 and 4.50 me for the 1/3 and the 1/2 nanowire heterostructures, respectively. For the Γ to M direction the band effective masses for the dyz and dxz are 0.55 and 0.59 me, respectively. Previous work on La δ -doped STO superlattices and from ARPES measurements on the STO surfaces found band effective masses in the range of 0.50–0.60 me35,36,38,39,46. As such, our computed effective masses suggest that the electron mobilities should be comparable to standard LAO/STO heterostructures. It should be noted that recent work on oxide heterostructures suggests that the decoupling of the dopant layer from the charge carrier layers may result in minimal effects of carrier concentrations on scattering lengths in these materials39,47.
Additionally, it has been shown that the transport in these materials is via a two-carrier model, comprised of high density low mobility carriers (primarily dxy electrons) and low density high mobility carriers (dxz and dyz electrons). Although the dxy bands have the smallest effective mass, previous effective Hamiltonian studies have demonstrated that, due to orbital ordering, electrons in these bands are strongly localized and therefore are not mobile. Hence, the ratio of the density of these electrons may be useful in understanding the ultimate change in the mobilities in these materials. Therefore, to gain further insight into how the populated d (i.e. dxz, dyz and dxy) orbitals affect the carrier mobility of the 1/2 nanowire heterostructure. We calculate the fractional occupation f, which is defined as37,
where nxz, nyz and nxy are the number of electrons in the dxz, dyz and dxy orbital, respectively. The calculated f for each TiO2 layer is displayed in Fig. 4(b). Again, we see that there is very little difference in f between the two heterostructures. These results agree with previous results for the La δ -doped system37, again suggesting little changes in mobilities in these materials39,47.
Although the computed electron count (see Fig. 4(a)) at the interface is larger than typically observed in experiment, the number of mobile carriers is significantly less, i.e. only one tenth of the total d electrons. We therefore expect to obtain a combination of high density low mobility carriers and low density high mobility carriers-the latter of which are usually seen in transport measurements.
A final point to consider is the atomic and electronic structures of a stoichiometric nanostructure. Figure 2(b) shows the relaxed configuration of the stoichiometric 1/3 nanowire heterostructure. Similar atomic displacements are observed as in the non-stoichiometric 1/3 case. However, in this case we do not observe any significant electronic reconstruction at the interface. The reason for this lies in the fact that in the stoichiometric case, the alternating LaO and AlO2 layers have alternating + 1 and − 1 charges but with dimensions of only half of a layer; and therefore the potential across these slabs do not grow as quickly as in the non-stoichiometric case. By increasing the number of m stoichiometric LAO layers, we observe a critical thickness of 1/9 LAO layers for the interface to become marginally metallic. This can be seen from the charge profile shown in Fig. 4. In addition, the fractional occupation and the Ti off-center displacements are now similar to the 1/2 and 1/3 non-stoichiometric nanowire heterostructures. Here, the delayed crossover draws analogy with the experimental study on LAO-STO solid-solution overlayers where the nanowire LAO can be thought of as a 50/50 LAO-STO composition19. In this instance, the critical thickness was found to also double in experiment. It is important to note that even for thinner steps, such as 1/3 stoichiometric nanowires, we observe little difference in the band structures of the Ti t2g conduction states. This suggests that even in the cases where a gate voltage is applied to inject electrons into the system that the confinement of electrons within the 1D states should be similar. Nevertheless, these results hint at the fact that the control of stoichiometry may provide an alternative route for tuning the electronic properties of the LAO/STO heterostructures.
Conclusion
In conclusion, we have computationally examined a novel LAO/STO nanostructure. Our results suggest that for non-stoichiometric, fully oxidized nanowires, this architecture should give rise to a 1DEG with mobilities that are comparable to those in standard LAO/STO and La δ -doped systems. Moreover, we demonstrate that these δ -doped systems result in the emergence of interfacial metallic states well below the LAO/STO critical thickness of 4 LAO layers. This is the first time that a true 1D electron density profile is achieved by tuning the fundamental length scales for separation and thickness of the nanowires. In addition, we observe a fascinating phenomenon that the electrostatic potential continues to diverge and remains localized. To understand this observation, we invoke a modified “polar catastrophe” model demonstrating that, due to the larger layer-by-layer charges in the non-stoichiometric layer, the transfer of charge to the interface should occur for 1/2 nanowires with roughly 0.5 e−/per surface LAO transferred to the interface. Furthermore, the imbalance in layer-by-layer charge drives further movement of electrons to the interface, producing twice as many electrons at the interface for a second LAO nanowire layer. Our model establishes fundamental theoretical underpinnings for the tunability of conduction in oxide nanowires and provides novel insights into defects at the edge of wires that would lead to either charge imbalance and/or stoichiometric layers. Similar to experiments for LAO-STO solid solution overlayers, this charge transfer is delayed for stoichiometric layers due to the smaller effective concentration of LAO on the surface. Band effective mass and orbital fractional occupation analyses show that these values are very similar to previous observations for La δ -doped superlattices, indicating the possibility of similar mobilities in these materials. Given the nature of the emergent 1DEG interfacial states, these findings should be generalizable to other similar oxide nanowire heterostructures and for other materials combinations. These results provide useful insights into the origin of the 1DEG recently found in experiment18. Most importantly, we demonstrate how carrier dimensionality and densities can be modified through nanostructuring and precise control of stoichiometry, thereby identifying new opportunities for understanding and controlling the properties of electronic states at oxide heterostructure interfaces.
Additional Information
How to cite this article: Zhuang, H. L. et al. Tunable one-dimensional electron gas carrier densities at nanostructured oxide Interfaces. Sci. Rep. 6, 25452; doi: 10.1038/srep25452 (2016).
References
Hwang, H. Y. et al. Emergent phenomena at oxide interfaces. Nat. Mater. 11, 103–113 (2012).
Zubko, P., Gariglio, S., Gabay, M., Ghosez, P. & Triscone, J.-M. Interface Physics in Complex Oxide Heterostructures. Annu. Rev. Condens. Matter Phys. 2, 141–165 (2011).
Mannhart, J. & Schlom, D. G. Oxide Interfaces—An Opportunity for Electronics. Science 327, 1607–1611 (2010).
Cen, C., Thiel, S., Mannhart, J. & Levy, J. Oxide Nanoelectronics on Demand. Science 323, 1026–1030 (2009).
Reiner, J. W., Walker, F. J. & Ahn, C. H. Atomically Engineered Oxide Interfaces. Science 323, 1018–1019 (2009).
Sharma, P. et al. Mechanical Tuning of LaAlO3/SrTiO3 Interface Conductivity. Nano Lett. 15, 3547–3551 (2015).
Irvin, P. et al. Anomalous High Mobility in LaAlO3/SrTiO3 Nanowires. Nano Lett. 13, 364–368 (2013).
Bark, C. W. et al. Switchable Induced Polarization in LaAlO3/SrTiO3 Heterostructures. Nano Lett. 12, 1765–1771 (2012).
Chen, Y. et al. Creation of High Mobility Two-Dimensional Electron Gases via Strain Induced Polarization at an Otherwise Nonpolar Complex Oxide Interface. Nano Lett. 15, 1849–1854 (2015).
Mathew, S. et al. Tuning the Interface Conductivity of LaAlO3/SrTiO3 Using Ion Beams: Implications for Patterning. ACS Nano 7, 10572–10581 (2013).
Ohtomo, A. & Hwang, H. Y. A high-mobility electron gas at the LaAlO3/SrTiO3 heterointerface. Nature 427, 423–426 (2004).
Thiel, S., Hammerl, G., Schmehl, A., Schneider, C. W. & Mannhart, J. Tunable Quasi-Two-Dimensional Electron Gases in Oxide Heterostructures. Science 313, 1942–1945 (2006).
Brinkman, A. et al. Magnetic effects at the interface between non-magnetic oxides. Nat. Mater. 6, 493–496 (2007).
Reyren, N. et al. Superconducting Interfaces Between Insulating Oxides. Science 317, 1196–1199 (2007).
Nakagawa, N., Hwang, H. Y. & Muller, D. A. Why some interfaces cannot be sharp. Nat. Mater. 5, 204–209 (2006).
Stengel, M. First-Principles Modeling of Electrostatically Doped Perovskite Systems. Phys. Rev. Lett. 106, 136803 (2011).
Stengel, M. & Vanderbilt, D. Berry-phase theory of polar discontinuities at oxide-oxide interfaces. Phys. Rev. B 80, 241103 (2009).
Ron, A. & Dagan, Y. One-Dimensional Quantum Wire Formed at the Boundary between Two Insulating LaAlO3/SrTiO3 Interfaces. Phys. Rev. Lett. 112, 136801 (2014).
Reinle-Schmitt, M. L. et al. Tunable conductivity threshold at polar oxide interfaces. Nat Commun. 3, 932 (2012).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized Gradient Approximation Made Simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Dudarev, S. L., Botton, G. A., Savrasov, S. Y., Humphreys, C. J. & Sutton, A. P. Electron-energy-loss spectra and the structural stability of nickel oxide: An LSDA+ U study. Phys. Rev. B 57, 1505–1509 (1998).
Pentcheva, R. & Pickett, W. E. Ionic relaxation contribution to the electronic reconstruction at the n-type LaAlO3/SrTiO3 interface. Phys. Rev. B 78, 205106 (2008).
Schwingenschlögl, U. & Schuster, C. Exponential decay of relaxation effects at LaAlO3/SrTiO3 heterointerfaces. Chem. Phys. Lett. 467, 354–357 (2009).
Schwingenschlögl, U. & Schuster, C. Surface effects on oxide heterostructures. Euro. Phys. Lett. 81, 17007 (2008).
Pentcheva, R. & Pickett, W. E. Avoiding the Polarization Catastrophe in LaAlO3 Overlayers onSrTiO3 (001) through Polar Distortion. Phys. Rev. Lett. 102, 107602 (2009).
Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
Cantoni, C. et al. Electron Transfer and Ionic Displacements at the Origin of the 2D Electron Gas at the LAO/STO Interface: Direct Measurements with Atomic-Column Spatial Resolution. Adv. Mat. 24, 3952–3957 (2012).
Siemons, W. et al. Origin of Charge Density at LaAlO3 on SrTiO3 Heterointerfaces: Possibility of Intrinsic Doping. Phys. Rev. Lett. 98, 196802 (2007).
Okamoto, S., Millis, A. J. & Spaldin, N. A. Lattice Relaxation in Oxide Heterostructures: LaTiO3/SrTiO3 Superlattices. Phys. Rev. Lett. 97, 056802 (2006).
Okamoto, S. & Millis, A. J. Electronic reconstruction at an interface between a Mott insulator and a band insulator. Nature 428, 630–633 (2004).
Takizawa, M., Tsuda, S., Susaki, T., Hwang, H. Y. & Fujimori, A. Electronic charges and electric potential at LaAlO3/SrTiO3 interfaces studied by core-level photoemission spectroscopy. Phys. Rev. B 84, 245124 (2011).
King, P. D. C. et al. Subband Structure of a Two-Dimensional Electron Gas Formed at the Polar Surface of the Strong Spin-Orbit Perovskite KTaO3 . Phys. Rev. Lett. 108, 117602 (2012).
Meevasana, W. et al. Creation and control of a two-dimensional electron liquid at the bare SrTiO3 surface. Nat. Mater. 10, 114–118 (2011).
Cooper, V. R. et al. Transparent conducting oxides: A δ -doped superlattice approach. Sci. Rep. 4, 6021 (2014).
Choi, W. S., Lee, S., Cooper, V. R. & Lee, H. N. Fractionally δ -Doped Oxide Superlattices for Higher Carrier Mobilities. Nano Letters 12, 4590–4594 (2012).
Cooper, V. R. Enhanced carrier mobilities in two-dimensional electron gases at III-III/I-V oxide heterostructure interfaces. Phys. Rev. B 85, 235109 (2012).
Ron, A. & Dagan, Y. private communication.
Sivadas, N., Dixit, H., Cooper, V. R. & Xiao, D. Thickness-dependent carrier density at the surface of SrTiO3 (111) slabs. Phys. Rev. B 89, 075303 (2014).
Bristowe, N. C., Artacho, E. & Littlewood, P. B. Oxide superlattices with alternating p and n interfaces. Phys. Rev. B 80, 045425 (2009).
Hamann, D. R., Muller, D. A. & Hwang, H. Y. Lattice-polarization effects on electron-gas charge densities in ionic superlattices. Phys. Rev. B 73, 195403 (2006).
Okamoto, S. & Millis, A. J. Theory of Mott insulator-band insulator heterostructures. Phys. Rev. B 70, 075101 (2004).
Bristowe, N. C., Littlewood, P. B. & Emilio, A. The net charge at interfaces between insulators. J Phys.: Condens. Matter 23, 081001 (2011).
Santander-Syro, A. F. et al. Two-dimensional electron gas with universal subbands at the surface of SrTiO3 . Nature 469, 189–193 (2011).
Zou, K. et al. LaTiO3/KTaO3 interfaces: A new two-dimensional electron gas system. APL Mater. 3, 036104 (2015).
Acknowledgements
The authors thank A. Ron and Y. Dagan for helpful discussions and feedback. This research was sponsored by the Laboratory Directed Research and Development Program (LDRD) of Oak Ridge National Laboratory, managed by UT-Battelle, LLC, for the U.S. Department of Energy and (HX, LZ) The University of Tennessee (UT) Science Alliance Joint Directed Research and Development Program (JDRD) and UT/ORNL Joint Institute of Advanced Materials (JIAM). This research used resources of the National Energy Research Scientific Computing Center, which is supported by the Office of Science of the U.S. Department of Energy under Contract No. DE-AC02-05CH11231.
Author information
Authors and Affiliations
Contributions
P.G. conceived the original idea and H.L.Z. performed all the calculations and made all the figures. H.L.Z., L.Z., H.X., P.R.C.K., P.G. and V.R.C. discussed and interpreted the results. V.R.C. led the writing and analysis effort.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Zhuang, H., Zhang, L., Xu, H. et al. Tunable one-dimensional electron gas carrier densities at nanostructured oxide interfaces. Sci Rep 6, 25452 (2016). https://doi.org/10.1038/srep25452
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep25452
This article is cited by
-
Metallicity at interphase boundaries due to polar catastrophe induced by charge density discontinuity
NPG Asia Materials (2018)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.