Abstract
Metal Chalcogenides (MCs) have emerged as an extremely important class of nanomaterials with applications ranging from lubrication to energy storage devices. Here we report our discovery of a universal, ultrafast (60 seconds), energy-efficient, and facile technique of synthesizing MC nanoparticles and nanostructures, using microwave-assisted heating. A suitable combination of chemicals was selected for reactions on Polypyrrole nanofibers (PPy-NF) in presence of microwave irradiation. The PPy-NF serves as the conducting medium to absorb microwave energy to heat the chemicals that provide the metal and the chalcogenide constituents separately. The MCs are formed as nanoparticles that eventually undergo a size-dependent, multi-stage aggregation process to yield different kinds of MC nanostructures. Most importantly, this is a single-step metal chalcogenide formation process that is much faster and much more energy-efficient than all the other existing methods and can be universally employed to produce different kinds of MCs (e.g., MoS2, and WS2).
Similar content being viewed by others
Introduction
During the past decades, intense interests have been aroused in metal chalcogenides because of their unique properties and promising applications1,2,3,4. The first closed-cage inorganic fullerene-like nanoparticles (IFs), layered MoS2 and WS2, were reported around 1990’s1,2,3. After a decade-long effort, many other layered compounds, such as transition metal chalcogenides MX2 (M = W, Mo, Sn, Ti, Re, Nb, Ta, Hf and Zr, etc, X = S, Se)5, are now achievable. Recently, MX2 has been investigated extensively because of their unique layered structures and excellent physical and chemical properties, which make them ideal candidates for use as lubricants6,7,8,9, heterogeneous catalysts10,11,12, solar cells13, lithium-ion batteries14,15, hydrogen storage elements16,17 and high performance protective composites18,19,20.
There has been significant progress made in synthetic methods for MS2 production, characterization, and in investigation of its physical and chemical properties as well as various applications. Synthetic methods for MS2 production mainly consist of (1) chemical methods such as solid-gas or gas-phase reactions3,21, thermal decomposition22,23, hydrothermal or solvothermal synthesis24,25, and template synthesis26 and (2) other instant stimulation methods such as laser ablation27, arc discharge7,28, and electron beam irradiation29,30. Despite major progress, there are still several limitations and disadvantages associated with the existing MS2 fabrication techniques. Some of them include the presence of extreme reaction conditions (high temperature, argon protection), involvement of many toxic and hazardous gases (e.g. H2S) and complicated processes, requirement of intense facilities (e.g., furnace, laser, arc discharge, and high voltage beams), and many more31,32,33,34,35. These challenges warrant the need to develop a method that can synthesize high-purity but low cost products of MS2 at industrial scales.
Very recently, there has been a major surge in employing microwave-based ultrafast, energy-efficient, and facile approaches for synthesizing multi-component nanostructures (e.g. metal oxides, metal sulfides)36,37,38,39,40,41,42,43. There are still some limitations in previous reports of microwave-assisted preparations for metal oxides/sulfides. Firstly, the effective microwave-assisted strategy has been developed for assisting other synthesis methods, such as solvothermal approach, which means the microwave heating is not the only or main tool during products preparation36,37. Secondly, the microwave irradiation has to treat the sample for relative long time (more than 30 min or several hours)38,39. Lastly, the selection of useful and effective precursor is the key to uniform growth of metal oxides/sulfides. The directly mixture of Mo (or W) with S could not lead to the formation of MoS2 (or WS2) by microwave heating41. Synthesis of precursor involved multi-step processing in some studies, which were not the simple and cost-effective processing way42.
In this communication, we report our discovery of a facile and energy-efficient route with multi-scale aggregation dynamics for the microwave-assisted synthesis of IF-MS2 nanoparticles. Our technique represents a clean, ultrafast (60 seconds) nano-manufacturing approach using microwave heating without any inert gas protection and intense facilities44,45,46,47. Figure 1 provides the schematic of our hypothesized mechanism of the process. We start with a uniform blend of polypyrrole nanofibers (PPy-NF) and M(CO)6 (M = Mo, W) forming homogenous dark powder composites. This blend is mixed with sulfur (S) powder or S/CS2 solution, and is subjected to microwave irradiation (frequency 2.45 GHz, power 1250 W MW) for 60 seconds. Polypyrrole nanofibers has been synthesized using our previously developed seeding polymerization methods48,49 and serves as a substrate owing to its low cost, relatively high electrical conductivity, tunable doping/de-doping characteristics, and long-term environmental stability. Microwave heating triggers reaction between M(CO)6 and sulfur or S/CS2 solution. This reaction first leads to the formation of MS2 nanoparticles, with M(CO)6 providing the metal element. These nanoparticles undergo intense heating which promotes molecular collisions and the formation of aggregates. In this first stage of aggregation, where the nanoparticle sizes being too small (~few nms), van der Waals (vdW) interactions govern the aggregation of particles leading to spherical growth of the aggregate. The second stage of aggregation involves nanoparticles with much larger diameters (~100 nms) and the difference in respective surface energies (nanoparticle-air and nanoparticle-nanoparticle) becomes dominant to lead to directional growth of the aggregate. This results in a ring-like growth of MoS2 aggregates (see Fig. 1), but a spherical growth of MoOx aggregates (not depicted in Fig. 1), which is the product of microwave heating the mixture of PPy-NF and M(CO)6.
Results
Synthesis of MoOx nanoparticles by microwave approach
The proposed microwave-based nano-manufacturing set up is first calibrated by producing MoOx nanoparticles (the corresponding figures are in the Supplementary Information or SI). Figure S1 shows the SEM images of MoOx particles decorated on the PPy nanofibers, using the microwave reaction with Mo(CO)6 precursor. The MoOx particles uniformly distribute on the PPy network. On a given PPy-NF, the MoOx particles fully cover the surface of fiber. The PPy-NF serves to conduct the microwave heat to Mo(CO)6, yielding MoOx. The inserted EDS spectrum is used to confirm the particles are mainly composed of molybdenum and oxygen and the presence of gold (Au) is due to the gold coating for SEM imaging. The XPS result in Figure S2 shows the ratio of molybdenum and oxygen. The spectra are similar to the literature reference XPS spectra for pure polypyrrole50, with the addition of small amount of Si, which is related to a surface contaminant and/or associated with the deposition method. The signals from O1s are larger than the reference spectrum, while that from the N1s are smaller. The literature reports the polypyrrole surface composition as: C: 72%, O: 14%, N: 11%. The polypyrrole investigated here is: C: 75%, O: 21%, N: 2%. The larger signal of O is due to the presence of the MoOx particles and adventitious O due to atmospheric exposure. The Mo3d5/2 BE (Bond Energy) is close to MoO3 and/or native MoO2. Figure S3 shows the X-ray diffraction (XRD) patterns of MoOx particles. According to MoO3 (JCPDS No. 05-0508), the diffraction peaks at following angle, such as 14°, 33°, 39°, and 58° correspond to the (020), (111), (060), and (171) planes of the MoO3, respectively. According to MoO2 (JCPDS No.86-0135), for example, the merged peaks at 37° and 54° are attributed to the ,, (200) and , (220) planes of the MoO2, respectively. The x in MoOx cannot be exactly confirmed which has a mixed Mo4+ and Mo6+ valence states. This is similar to a previous report in synthesis of mixed-valence MoOx on carbon nanotube51 and synthesis of WOx from W(CO)633.
Synthesis of IF-MS2 nanoparticles by microwave heating
Using the same conditions and process, MoS2 particles can be easily produced by only adding sulfur powder to the initial mixture. Figure 2(a,b) shows the SEM images of MoS2 particles on the “bed” of PPy-NF. The MoS2 particles are aggregated together on PPy-NF. The EDS result shown in Fig. 2(c) indicates that particles are primarily composed of molybdenum and sulfur. The XPS results in Figure S4 indicates the Mo3d5/2 BE (Bond Energy) aligns favorably with both MoS2 and MoO2 and the S2p BE aligns favorably with the BE for a standard XPS spectrum of MoS2. The XRD patterns of the MoS2 display diffraction peaks in the range from 10° to 80°, as shown in Fig. 2(d). The patterns can be indexed to the standard hexagonal 2H–MoS2 structure (JPCDS no. 37-1492), which indicates the MoOx composites with different ratio of MoO2/MoO3 will completely become MoS2. Advanced TEM has been widely utilized as a very powerful instrument for the analysis of nanoparticle synthesis in recent studies to determine the crystal structure and for surface reconstruction in both particles and thin films52,53,54. Figure 3(a) shows the typical assortment of IF-MoS2 nanoparticles obtained directly by microwave heating. A closer look at these nanoparticles (Fig. 3(b,c)) reveals the particles are hexagonal or heptagonal in shape and possess a compact multiwall structure (>25 walls) with a prominent oxide nanoparticle core, as shown in Fig. 3(b). The line profile of the framed area (box 1) indicates that the spacing distance of the interlayer is around 0.62 nm (6.172 nm of 10 layers) [see Fig. 3(d)], which is very close to the separation of the (002) planes of MoS2 (c/2 lattice spacing). The hexagonal atomic arrangement shown Fig. 3(f) and the FFT pattern indicate that the basal plane of the synthesized thin film is (001), i.e. the c-axis of MoS2 materials perpendicular to the thin film. Each sulfur center is pyramidal and is connected to three Mo centers. The lattice constant is a = b = 0.315 nm. Along the wall, the distance between the Mo is which is very close to the measured value of 0.261 nm [see Fig. 3(e)]. The results discussed above show that the microwave nano-manufacturing can easily prepare the inorganic fullerene-like MoS2 in a single step. To confirm its robustness, we employ this method to prepare other metal chalcogenides (e.g., IF-WS2 from W(CO)6 and sulfur source). The TEM images of IF-WS2 thus prepared are shown in Figure S5. The size of both IF-WS2 and IF-MoS2 metal chalcogenides is similar, but the shape of IF-WS2 nanoparticles is more spherical. The size of metal-oxide core is much smaller than the core in IF-MoS2 nanoparticles. The multiwall structure is not well compacted and well-organized, and the number of layers can be more than 40. The interlayer spacing is around 0.613 nm and the distance between layers of W in one plane is around 0.220 nm, both of the values are smaller than the value of IF-MoS2 nanoparticles.
Mechanism of IF-MS2 formation
To the best of our knowledge in all the existing studies, the synthesis of inorganic fullerene-like MS2 is performed as a two-step process, with the synthesis of nanoparticles being followed by annealing in inert atmosphere in a conventional tube furnace4,55. In this novel microwave approach, the temperature generated by microwave heating can reach above 1000 °C for synthesizing MoS2 directly56. The reaction is similar to the MOCVD which involves the reaction between organic gas and metal particles at very high temperature (>700 °C)55. The schematic experimental procedure is shown in Fig. 1. The particles of M(CO)6 and particles of sulfur contact well with each other on the networks of PPy. The PPy networks provide the channel of conduction and pathway of heating. When microwave energy is applied, the reactions occur and the amorphous nuclei are formed. Tangential MS2 layers are gradually formed from the edges. As shown in Fig. 4, there are many different shapes and intermediates of MoS2, such as needle-like (N), onion-like (O), and irregular (S) shaped particles, which is consistent to the prior report, that uses MOCVD technique and post-steps (i.e., annealing under argon protection)56,57. Comparing to this MOCVD method, the microwave approach can directly synthesize these segments of multi-layers in different stages of growth of MoS2, such as crystallization, assembly and formation discussed in Fig. 1. The presence of this mechanism can also be proved in growth of WS2. Figure 5 clearly shows the intermediates of WS2 in the process of assembly. Very thin layers (3–5 layers) are assembled from the edges of amorphous particles and form irregular boundaries as shown in Fig. 5(a–c). The crystallization process was shown to start at the outer surface of the round nanoparticle and propagate inwards. High temperature or thermal stress may initiate bending or faceting of the crystals. The strong inter-layer covalent bonding causes the crystal (layers) to close by itself and the structure is expected to be stable, as observed in Fig. 5(d–f). Finally, closed-cage inorganic fullerene-like nanoparticles of WS2 are formed. It should be mentioned that, particles in Fig. 5(a) are all in stages of growth and assembly while the particles in Fig. 5(d) exhibit the IF morphology. It indicates that these particles undergo uniform microwave heating and concurrent morphological change.
Recently, metal chalcogenides nanoparticles, tubes, and sheets were generated by a synthetic pathway that employs CS2 as the source of sulfur instead of H2S4. In this study, CS2 was also selected as co-precursor to obtain the metal chalcogenides. Figure S6 shows the TEM images of IF-MoS2 and IF-WS2 nanoparticles synthesized from Mo(CO)6 or W(CO)6 with S/CS2 solution. Compared with products obtained from pure sulfur powders, both metal chalcogenides are not well faceted. The number of layer is less than those produced by sulfur powders. These cage-like materials possess different morphologies such as perfect spheres, semispherical particles or structures in which crystalline directions were evident and resulted in polyhedral shapes. For IF-MoS2 in Figure S6(a–c), due to the incomplete closure of the outermost layers, hair-like outgrowths were evident in the structure. For IF-WS2 in Figure S6(d–f), the structure is loose and the metal-oxide core is much larger than those obtained from the reaction with sulfur powders. The results indicate that the use of S/CS2 solution for the generation of MS2 is very different from the use of S powder only. Firstly, the S powders are homogeneously dispersed in CS2 solvent, which can improve the uniformity of reaction between metal and sulfur. Secondly, CS2 vapor may serve as additional sulfur source to obtain these MCs. Thirdly, using S/CS2 solution may provide a potential way to synthesize MCs with few layers or even single layer.
Discussion
Central to this single-step formation of the microwave-assisted metal chalcogenides nanostructures is the two-step aggregation process. The first stage of aggregation involves the just-formed MoS2 and MoOx nanoparticles of dimensions of only few nanometers. These nanoparticles are at a thermally excited state, they vibrate rapidly and as a consequence two of these nanoparticles come to close enough proximity of each other to allow van der Waals (vdW) attractive interactions to become influential triggering the aggregation of these two nanoparticles. This aggregation displays no directional preference, as a result, the nanocluster grows in a spherical form. Things change when these nanoclusters have grown sufficiently large (~100nm). As shown in Fig. 6, when two typical spherical nanoclusters, each of 100 nm in diameter, come in close enough proximity, vdW effects dictate their possible aggregation. However, when a third nanocluster attempts to join this newly formed aggregate, two arrangements are possible, as illustrated in Fig. 6. For case A, two contact zones (each of area δ) are being created and the consequent change in the surface energy is ΔU = 2δ(γpp − γpa), on the other hand for case B, only one contact zone (of area δ) is formed and the consequent change in the surface energy is ΔU = δ(γpp − γpa). Here γpp and γpa are the particle-particle and particle-air surface tension values. When γpp < γpa, case A occurs, since this leads to larger energy decrease (as compared to case B) due to aggregation – this typically occurs for MoOx. On the other hand, when γpp > γpa, case B occurs, since this leads to less energy increase (as compared to case A) due to aggregation – this typically occurs for MoS2. Therefore, we see MoOx growing as a bulk cluster [Figure S1], whereas MoS2 growing as a ring.
To conclude, in this communication we have reported our discovery of a single-step, universal microwave–assisted technique for producing different kinds of MC nanostructures. The process is ultrafast and extremely energy efficient. The process is based on three key steps: (a) microwave-heating assisted reaction yielding MC nanoparticles, (b) thermal vibration of these NPs to trigger aggregation and formation of larger sized nanoclusters and (c) preferential growth of the these nanoclusters, dictated by the relative preference of surface interactions forming different nanostructures. Results indicate that the morphological specifications of these nanostructures strongly depend on the nature of the MCs as well as the reactants used to obtain these MCs. We anticipate that our discovery of this new technique for preparing MCs will catalyze substantial development in more widespread uses of MCs in a more energy-efficient and easily-accessible approach.
Methods
Synthesis of MOx nanoparticles by PPy NF and M (CO)6
Polypyrrole nanofibers (PPy NF) were synthesized via previously reported methods. PPy NF and Mo(CO)6 (or W(CO)6) were uniformly blended to form homogenous dark powder composites, specifically 50 mg PPy NF and 50 mg Mo(CO)6 (or W(CO)6) were blended by speed mixer at 3500 rpm for 2 min.
The aforementioned mixture of PPy NF and Mo(CO)6 (or W(CO)6) was transferred into a glass vial and loosely capped, and then placed into the microwave chamber. The solid mixture was continuously irradiated by 1250 W MW power for 60 seconds. Vigorous sparking was observed within the first 3 seconds of microwave irradiation. Particular attention ought to be given to the fast microwave reaction with extreme high temperature (approximately 1000 °C). The mixture was kept reacting (burning) for another 40 s before becoming stable in the glass vial, and showing no further signs of reaction. Eventually, after microwaving, the vials were removed and allowed to cool naturally to room temperature. The remaining solids were collected with a steel spatula and stored for further tests and characterizations.
Synthesis of IF-MS2 nanoparticles by adding sulfur
A tri-component system (I) was prepared by mixing PPy NF, Mo(CO)6 (or W(CO)6) and elemental sulfur, in order to generate MoS2 or WS2 on PPy substrate. Specifically, PPy NF (50 mg), Mo(CO)6 (50 mg) and sulfur (50 mg) were homogenously mixed in speed mixer at 3500 rpm for 2 min. The mixtures were transferred into glass vials, loosely capped and placed into the MW chamber. The mixture was continuously irradiated by 1250 W MW power for 1 min. The reaction indicated by vigorous evolution of yellow smoke within 5 s, while taking an average of 20–30 s for these samples to start burning and glowing. The mixture continued to burn for the next 40 s, after which the sample was allowed to cool to room temperature. The as-obtained samples were collected from the glass vial bottom with a steel spatula and stored for further tests and characterizations.
Synthesis of IF-MS2 nanoparticles by adding CS2
Another tri-component system (II) of 50 mg PPy NF, 50 mg Mo(CO)6 (or W(CO)6) and 50 mg elemental sulfur has been mixed homogeneously via speed mixer at 3500 rpm for 2 min. The mixtures were transferred into glass vials and were soaked in 2mL CS2 to fully dissolve the sulfur for better homogeneity and to provide more C and S into the reaction. The overall reaction was more vigorous due to the high activity of CS2 under heating. The mixture was then continuously irradiated by 1250 W MW power for 60 s, within 10 s the samples began reacting, indicated by the presence of bluish flames. It took an avg. of 20–30 s for samples to start burning, with glowing and evolution of bluish smoke continuing for the next 40 s. Finally the as-obtained samples were cooled and collected from the glass vial bottom with a steel spatula and stored for further tests and characterizations.
Characterization
Scanning electron microscopy (SEM) characterization was performed on a JEOL JSM-7000F instrument. The morphology of nanoparticles was also observed by high resolution transmission electron microscopy (TEM) in JEOL 2100 microscopes at an acceleration voltage of 200 kV. The X-ray photoelectron spectroscopic (XPS) elemental analysis of the samples was conducted with a Kratos XSAM 800 instrument. The X-ray diffraction (XRD) patterns of nanoparticles were performed on a Bruker D8 Advance diffractometer.
Additional Information
How to cite this article: Liu, Z. et al. Ultrafast Microwave Nano-manufacturing of Fullerene-Like Metal Chalcogenides. Sci. Rep. 6, 22503; doi: 10.1038/srep22503 (2016).
References
Tenne, R., Margulis, L., Genut, M. & Hodes, G. Polyhedral and cylindrical structures of tungsten disulfide. Nature 360, 444–446 (1992).
Margulis, L., Salitra, G., Tenne, R. & Talianker, M. Nested fullerene-like structures. Nature 365, 113–114 (1993).
Feldman, Y., Wasserman, E., Srolovitz, D. J. & Tenne, R. High-rate, gas-phase growth of MoS2 nested inorganic fullerenes and nanotubes. Science 267, 222–225 (1995).
Tenne, R. & Redlich, M. Recent progress in the research of inorganic fullerene-like nanoparticles and inorganic nanotubes. Chem. Soc. Rev. 39, 1423–1434 (2010).
Shi, Y. F., Wan, Y. & Zhao, D. Y. Ordered mesoporous non-oxide materials. Chem. Soc. Rev. 40, 3854–3887 (2011).
Rapoport, L. et al. Hollow nanoparticles of WS2 as potential solid-state lubricants. Nature 387, 791–793 (1997).
Chhowalla, M. & Amaratunga, G. A. Thin films of fullerene-like MoS2 nanoparticles with ultra-low friction and wear. Nature 407, 164–167 (2000).
Huang, H. D., Tu, J. P., Zou, T. Z., Zhang, L. L. & He, D. N. Friction and wear properties of IF-MoS2 as additive in paraffin oil. Tribol. Lett. 20, 247–250 (2005).
Adini, A. R., Redlich, M. & Tenne, R. Medical application of inorganic fullerene-like nanoparticles. J. Mater. Chem. 21, 15121–15131 (2011).
Chinaelli, R. R., Berhault, G. & Torres, B. Unsupported transition metal sulfide catalysts: 100 years of science and application. Catal. Today 147, 275–286 (2009).
Afanasiev, P., Rawas, L. & Vrint, M. Synthesis of dispersed Mo sulfides in the reactive fluxes containing liquid sulfur and alkali metal carbonates. Mater. Chem. Phys. 73, 295–300 (2002).
Mdleleni, M. M., Hyeon, T. & Suslick, K. S. Sonochemical synthesis of nanostructured molybdenum sulfide. J. Am. Chem. Soc. 120, 6189–6190 (1998).
Levy, M. et al. Synthesis of Inorganic Fullerene-like Nanostructures by Concentrated Solar and Artificial Light. Isr. J. Chem. 50, 417–425 (2010).
Wang, Z. et al. CTAB-assisted synthesis of single-layer MoS2-graphene composites as anode materials of Li-ion batteries. J. Mater. Chem. A 1, 2202–2210 (2013).
Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nat. Nanotechnol. 6, 147–150 (2011).
Chen, J., Li, S. L., Tao Z. L. & Gao, F. Low-temperature synthesis of titanium disulfide nanotubes. Chem. Commun. 8, 980–981 (2003).
Wang, D. Z. et al. Distorted MoS2 nanostructures: An efficient catalyst for the electrochemical hydrogen evolution reaction. Electrochem. Commun. 34, 219–222 (2013).
Zhu, Y. Q. et al. Shock-absorbing and failure mechanisms of WS2 and MoS2 nanoparticles with fullerene-like structures under shock wave pressure. J. Am. Chem. Soc. 127, 16263–16272 (2005).
Zhu, Y. Q. et al. Shock-wave resistance of WS2 nanotubes. J. Am. Chem. Soc. 125, 1329–1333 (2003).
Cook, J., Rhyans, S., Roncase, L., Hobson, G. & Luhrs, C. C. Microstructural study of IF-WS2 failure modes. Inorganics 2, 377–395 (2014).
Rothschild, A., Sloan J. & Tenne, R. Growth of WS2 Nanotubes Phases. J. Am. Chem. Soc. 122, 5169 (2000).
Nath, M., Mukhopadhyay K. & Rao, C. N. R. Mo1−xWxS2 nanotubes and related structures. Chem. Phys. Lett. 35, 163–168 (2002).
Nath, M., Govindaraj, A. & Rao, C. N. R. Simple Synthesis of MoS2 and WS2 Nanotubes. Adv. Mater. 13, 283–286 (2001).
Li, Y. D., Li, X. L., He, R. R., Zhu, J. & Deng. Z. X. Artificial lamellar mesostructures to WS2 nanotubes. J. Am. Chem. Soc. 124, 1411–1416 (2002).
Berntsen, N. et al. A solvothermal route to high-surface-area nanostructured MoS2 . Chem. Mater. 15, 4498–4502 (2003).
Zelenski, C. M. & Dorhout, P. K. Template synthesis of near-monodisperse microscale nanofibers and nanotubules of MoS2 . J. Am. Chem. Soc. 120, 734–742 (1998).
Parilla, P. A. et al. The first true inorganic fullerenes? Nature 397, 114 (1999).
Hu, J. J., Bultman, J. E. & Zabinski, J. S. Inorganic fullerene-like nanoparticles produced by arc discharge in water with potential lubricating ability. Tribol. Lett. 17, 543–546 (2004).
Yacaman, M. J. et al. Studies of MoS2 structures produced by electron irradiation. Appl. Phys. Lett. 69, 1065–1067 (1996).
Golberg, D., Bando, Y., Stephan, O. & Kurashima, K. Octahedral boron nitride fullerenes formed by electron beam irradiation. Appl. Phys. Lett. 73, 2441–2443 (1998).
Li, X. L. & Li, Y. D. Formation of MoS2 inorganic fullerenes (IFs) by the reaction of MoO3 nanobelts and S. Chem. Eur. J. 9, 2726–2731 (2003).
Yang, H. B. et al. Synthesis of inorganic fullerene-like WS2 nanoparticles and their lubricating performance. Nanotechnology 17, 1512–1519 (2006).
Leonard-Deepak, F., Castro-Guerrero, C. F., Mejia-Rosales, S. & Jose-Yacaman, M. Structural transformation of tungsten oxide nanourchins into IF–WS2 nanoparticles: an aberration corrected STEM study. Nanoscale 3, 5076–5082 (2011).
Tian, Y. et al. A facile route to synthesis of MoS2 nanorods. Mater. Lett. 59, 3452–3455 (2005).
Wiesel, I. et al. Synthesis of WS2 and MoS2 fullerene-like nanoparticles from solid precursors. Nano. Res. 2, 416–424 (2009).
Murugan, A. V., Sonawane, R. S., Kale, B. B., Apte, S. K. & Kulkarni, Aarti V. Microwave–solvothermal synthesis of nanocrystalline cadmium sulfide. Mater. Chem. Phys. 71, 98–102 (2001).
Mao, L. Y., Wang, Y. R., Zhong, Y. J., Ning, J. Q. & Hu, Y. Microwave-assisted deposition of metal sulfide/oxide nanocrystals onto a 3D hierarchical flower-like TiO2 nanostructure with improved photocatalytic activity. J. Mater. Chem. A, 1, 8101–1804 (2013).
Liao, X. H., Zhu, J. J. & Chen, H. Y. Microwave synthesis of nanocrystalline metal sulfides in formaldehyde solution. Mater. Sci. Eng. B 85, 85–89 (2001).
Pang H. et al. Microwave-assisted synthesis of NiS2 nanostructures for supercapacitors and cocatalytic enhancing photocatalytic H2 production. Sci. Rep. 4, 3577 (2014).
Di C. et al. Microwave-assisted synthesis of metal sulfides in ethylene glycol. Mater. Chem. Phys. 82, 206–209 (2003).
Ouerfelli, J., Srivastava, S. K., Bernède, J. C. & Belgacem, S. Effect of microwaves on synthesis of MoS2 and WS2 . Vacuum 83, 308–312 (2009).
Liu, N. et al. Microwave-assisted synthesis of MoS2/graphene nanocomposites for efficient hydrodesulfurization. Fuel 119, 163–169 (2014).
Jiang, Y. & Zhu, Y. J. Microwave-assisted synthesis of sulfide M2S3 (m = Bi, Sb) nanorods using an ionic liquid. J. Phys. Chem. B 109, (2005).
Zhang, X. Y. & Liu, Z. Recent advances in microwave initiated synthesis of nanocarbon materials. Nanoscale 4, 707–714 (2012).
Zhang, X. Y. & Manohar, S. K. Microwave synthesis of nanocarbons from conducting polymers. Chem. Commun. 23, 2477–2479 (2006).
Liu, Z. et al. An ultrafast microwave approach towards multicomponent and multi-dimensional nanomaterials. RSC Adv. 4, 9308–9313 (2014).
Liu, Z. et al. Ultrafast Cr(VI) removal from polluted water by microwave synthesized iron oxide submicron wires. Chem. Commun. 50, 8036–8039 (2014).
Zhang, X. Y., Goux, W. J. & Manohar, S. K. Synthesis of polyaniline nanofibers by “nanofiber seeding”. J. Am. Chem. Soc. 126, 4502–4503 (2004).
Zhang, X. Y. & Manohar, S. K. Bulk synthesis of polypyrrole nanofibers by a seeding approach. J. Am. Chem. Soc. 126, 12714–12715 (2004).
Tarcha, P. J., Salvati, L. & Johnson, R. W. Polypyrrole latex: surface analysis by XPS, surface science spectra. Surf. Sci. Spectra. 8, 323–328 (2001).
Jegal, J. P., Kim, H. K., Kim, J. S. & Kim, K. B. One-pot synthesis of mixed-valence MoOx on carbon nanotube as an anode material for lithium ion batteries. J Electroceram 31, 218–223 (2013).
Kim, Y. J., Tao, R. Z., Klie, R. F. & Seidman, D. N. Direct atomic-scale imaging of hydrogen and oxygen interstitials in pure niobium using atom-probe tomography and aberration-corrected scanning transmission electron microscopy. ACS Nano 7, 732–739 (2013).
Zhang, K. et al. Water-free Titania–Bronze thin films with superfast lithium-ion transport. Adv. Mater. 26, 7365–7370 (2014).
Xin, H. L. et al. Revealing the atomic restructuring of Pt–Co nanoparticles. Nano. Lett. 14, 3203–3207 (2014).
Luo, W., Hu, X. L., Sun, Y. M. & Huang, Y. H. Electrospinning of carbon-coated MoO2 nanofibers with enhanced lithium-storage properties. Phys. Chem. Chem. Phys. 13, 16735–16740 (2011).
Liu, X. L., Ji, W. X., Liang, J. Y., Peng, L. M. & Hou, W. H. MoO2@carbon hollow microspheres with tunable interiors and improved lithium-ion battery anode properties. Phys. Chem. Chem. Phys. 16, 20570–20577 (2014).
Zink, N. et al. In situ heating tem study of onion-like WS2 and MoS2 nanostructures obtained via MOCVD. Chem. Mater. 20, 65–71 (2008).
Acknowledgements
We gratefully acknowledge financial support from NASA LEARN II NNX14AF49A. We thank Dr. Runzhe Tao for technical assistance for this experiment.
Author information
Authors and Affiliations
Contributions
Z.L. and X.Y.Z. conceived the method and designed the study, S.P. and J.C. produced the samples. S.P. and L.Z. carried out SEM and EDS measurement, R.G.W. carried out TEM measurements, and M.J.B. carried out XPS measurements. L.Z. and S.D. analyzed the results and led theoretical interpretation, X.Y.Z., Z.L., L.Z. and S.D. wrote the manuscript, Z.L., X.Y.Z. and L.B.H. coordinated the research. All authors commented on the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Liu, Z., Zhang, L., Wang, R. et al. Ultrafast Microwave Nano-manufacturing of Fullerene-Like Metal Chalcogenides. Sci Rep 6, 22503 (2016). https://doi.org/10.1038/srep22503
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep22503
This article is cited by
-
High-performance supercapacitors based on Ni2P@CNT nanocomposites prepared using an ultrafast microwave approach
Frontiers of Chemical Science and Engineering (2021)
-
Facile microwave approach towards high performance MoS2/graphene nanocomposite for hydrogen evolution reaction
Science China Materials (2020)
-
Immobilization of penicillin G acylase on a novel paramagnetic composite carrier with epoxy groups
Advanced Composites and Hybrid Materials (2019)
-
One-step microwave synthesis of MoS2/MoO3@graphite nanocomposite as an excellent electrode material for supercapacitors
Advanced Composites and Hybrid Materials (2019)
-
Recent progress on nanostructured conducting polymers and composites: synthesis, application and future aspects
Science China Materials (2018)