Abstract
Shape memory alloys are typical temperature-sensitive metallic functional materials due to superelasticity and shape recovery characteristics. The conventional shape memory effect involves the formation and deformation of thermally induced martensite and its reverse transformation. The shape recovery process usually takes place over a temperature range, showing relatively low temperature-sensitivity. Here we report novel Cu-Al-Fe-Mn shape memory alloys. Their stress-strain and shape recovery behaviors are clearly different from the conventional shape memory alloys. In this study, although the Cu-12.2Al-4.3Fe-6.6Mn and Cu-12.9Al-3.8Fe-5.6Mn alloys possess predominantly L21 parent before deformation, the 2H martensite stress-induced from L21 parent could be retained after unloading. Furthermore, their shape recovery response is extremely temperature-sensitive, in which a giant residual strain of about 9% recovers instantly and completely during heating. At the same time, the phenomenon of the jumping of the sample occurs. It is originated from the instantaneous completion of the reverse transformation of the stabilized 2H martensite. This novel Cu-Al-Fe-Mn shape memory alloys have great potentials as new temperature-sensitive functional materials.
Similar content being viewed by others
Introduction
Metallic materials when heated are often accompanied with the changes of microstructure, shape or performance, which can be considered as functional materials for various practical applications. Typically, shape memory alloy (SMA) is a kind of temperature-sensitive metallic functional materials, possessing shape memory effect (SME) and superelasticity (SE) characteristics, such as Ni-Ti and Cu-Al-Mn alloys1,2,3,4,5. The SME and SE behaviors depend on the reversible martensitic transformation, having some differences between them. The SME phenomenon is that the deformation strain in the martensite sample could be recovered through reverse transformation via heating. The SE property is associated with the stress-induced martensitic transformation in the austenite sample and the corresponding immediate reverse transformation upon unloading. Typically, a large stress-plateau upon loading could be observed for above two situations, owing to the reorientation of martensite variants and/or de-twinning for SME1,6,7, or the stress-induced martensitic transformation process for SE1,6,8,9, respectively. Furthermore, the shape recovery process and the actuation speed reported in the existing SMAs usually takes place over a temperature range7,10,11,12,13, showing relatively low temperature-sensitivity.
The transformation temperatures of the existing SMAs that are used in practice are generally not higher than 100 °C, which cannot satisfy the requirements of high temperature applications10. To date, several types of high-temperature shape memory alloys (HTSMAs) for high temperature applications have been explored, such as Ni-Ti-Pd/Hf/Zr14,15,16,17, Ni-Mn-Ga-based7,11,18, Ni3Ta12, Zr-Cu-based13. Although the polycrystalline Ni-Ti-Pd14,15 and single crystal Ni-Mn-Ga7 alloys exhibit about 5.4% and 6.1% of high temperature shape recovery strains, the high-costs for the precious metal of Pd and for the production of single crystal of Ni-Mn-Ga have hindered their practical applications. Since the raw materials of Cu-Al-based SMAs are much cheaper, they have also attracted much attentions as high-temperature actuation purposes, such as Cu-Al-Nb19,20, Cu-Al-Ag21, Cu-Al-Fe22, Cu-Al-Ta23, Cu-Al-Co and Cu-Al-Zr24 alloys. However, the major drawbacks of these materials are their poor recovery strain and poor thermal stability, which are not desirable when being used at high temperature. These situations motivate us to further explore potential low-cost SMAs that can stably operate at high temperature. Here we present a novel Cu-12.2Al-4.3Fe-6.6Mn (mass%) SMA. It has a giant and stable full shape recovery strain of about 9% when cycling through high temperature (above 100 °C). It is further discovered that the shape recovery process can complete instantly accompanied with the jumping of the sample. Such extraordinary property has never been reported in other types of SMAs.
Results
Microstructure and martensitic transformation
Figure 1 shows the microstructure of Cu-12.2Al-4.3Fe-6.6Mn alloy (see the Methods). This sample consists of dominate parent (Fig. 1a) and a small amount of needle-like martensite (Figure S1a). The transmission electron micrograph (TEM) and the selected area diffraction pattern (SADP) of the parent shown in Fig. 1b,c. The parent is confirmed to be an ordered L21 structure, which is similar to those observed in Cu-Al-Mn SMAs4,5,25. The martensite has a 2H () structure based on the TEM image and SADP in Figure S1b, c. Additionally, in Fig. 1b, several fine precipitation particles are observed as indicated by a red circle. These particles are further identified to be two typed precipitates of A2 and ordered D03 structures25,26,27 (see the Figures S2 and S3 for the details). The martensitic transformation temperatures of the sample were determined by DSC test as shown in Fig. 2. The temperatures Ms, Mp and Mf, As, Ap and Af are −74.1 °C, −74.5 °C and −77.3 °C, −56.4 °C, −53.4 °C and −49.2 °C, respectively. The transformation thermal hysteresis Th (Th = Af − Ms) is only 24.9 °C.
Stress-strain behaviors
Figure 3a shows the compressive stress-strain curves of Cu-12.2Al-4.3Fe-6.6Mn alloy with a pre-strain of 12% during the 1st (black) and the 50th (red) thermomechanical cycles. Figure 3b exhibits the microstructure of the deformed sample after compressed to a pre-strain of about 12% and unloading. It is noted that the sample almost consists of martensite at the same time. The martensite has 2H () structure by electron diffraction (Figure S4a, b). Here, a novel stress-strain behavior is found in Cu-12.2Al-4.3Fe-6.6Mn alloy. The usual SE property associates with the stress-induced martensitic transformation1,6,8,9, though the transformation temperatures are significantly below testing temperature. Meanwhile, the reverse transformation immediately occurs during unloading process, along with the shape recovery. Interestingly, we find although the studied sample possesses predominant L21 parent before deformation, the stress-induced strain (namely the large stress-plateau during loading in Fig. 3a) does not recover during unloading accordingly. The stress-induced 2H martensite from L21 parent could be retained after unloading. Such martensite could be called the “stabilized stress-induced martensite”.
With the decrease of the transformation temperature by changing the alloy compositions, other Cu-Al-Fe-Mn alloys exhibit clearly different stress-strain behaviors. Figure S5 shows the reversible martensitic transformation temperatures of Cu-12.9Al-3.8Fe-5.6Mn alloy, which are lower than those of Cu-12.2Al-4.3Fe-6.6Mn alloy in Fig. 2. Two samples were prepared and different compressive pre-strains of 10% and 12% were performed with two cycles, and the results are provided in Fig. 4. When a 10% of compressive pre-strain is performed during two cycles, full shape recovery strain (εRS) of 10% is obtained after the removal of load in Fig. 4a. Increasing the compressive pre-strain to 12% in Fig. 4b, the sample still shows full shape recovery strain (εRS) of 12% during the first test indicated by the black line. However, during the second cycle, the “stabilized stress-induced martensite” process occurs, in which the residual strain is also about 9% indicated by the red line. With further decreasing the transformation temperature, the normal SE behavior is observed in Cu-13.5Al-2.9Fe-6.8Mn alloy (The martensitic transformation temperatures of Cu-13.5Al-2.9Fe-6.8Mn alloy are much lower than above two alloys, in which there are no transformation peaks cannot be detected by DSC test between −150 °C and 20 °C). Figure 5 is the compressive stress-strain curves of Cu-13.5Al-2.9Fe-6.8Mn alloy with five cycles. The same compressive pre-strain of 12% was performed before each cycle in the same sample. Here, the stress-induced strain during loading immediately recovers after the removal of load. Compared to other two studied alloys, the difference is that the “stabilized stress-induced martensite” process does not take place, whereas it suggests an excellent shape recovery strain (εRS) of about 12%.
Shape recovery characteristics
The shape recovery characteristics of Cu-12.2Al-4.3Fe-6.6Mn sample were investigated through thermomechanical cycles. The same compressive pre-strain (εpre) of 12% was performed before each cycle (Fig. 3a). Then the deformed sample was heated to introduce reverse transformation and the dimensional change was recorded by a thermal mechanical analyser (TMA). Figure 6a shows the shape recovery curve of the sample during the 1st thermal cycle. It is observed that the initial shape recovery starts within stage A-B (around 103–137 °C). However, the remaining residual strain recovers completely and instantly at 137 °C (stage B-C-D). At this stage, the sample jumps strongly during shape recovery, see the Video S1. Subsequently, fifty thermomechanical cycles were performed between room temperature and 700 °C in air. As shown in Fig. 6b, nearly perfect shape recovery strain of about 9% and shape recovery rate of about 100% are obtained each time, indicating excellent thermomechanical stability. The shape recovery behavior of the deformed specimen of Cu-12.9Al-3.8Fe-5.6Mn in Fig. 4b is similar to that of Cu-12.2Al-4.3Fe-6.6Mn alloy, see the Video S2. In Videos S1 and S2, the deformed sample is heated on a heating platform exposed to the air; the temperature at which the “jumping” of the samples occurs at 152 °C and 55 °C for Cu-12.2Al-4.3Fe-6.6Mn and Cu-12.9Al-3.8Fe-5.6Mn alloys, respectively. Such shape recovery properties have never been reported in other types of SMAs, in which the deformation strain of the present alloy can recover instantly and completely, showing extreme “temperature-sensitivity”.
Discussion
The novel stress-strain characteristics of the present quaternary Cu-Al-Fe-Mn SMAs are clearly different from the usual SE property. In this study, we think that the movement of the habit plane causing reverse transformation is probably inhibited by very fine precipitates, and/or the dislocations formed during deformation. Figure S6 shows the transmission electron microscopy-energy dispersive spectrometer (TEM-EDS) mapping analysis of the compressed Cu-12.2Al-4.3Fe-6.6Mn specimen and heated up to 140 °C. It is clearly seen that those Fe-rich particles exhibit the grain size of 10–30 nm in spherical shape (similar to those in Figure S2) and 100–200 nm in cuboidal shape respectively. Furthermore, the microstructure of the specimen is observed using TEM tests. Figure 7 shows the bright-field image (a) and weak-beam dark-field image (b) of the parent phase, the bright-field image in parent and martensite phases (c). From Fig. 7 it is found that a band of dislocation is observed close by those precipitates with the size of about 100 nm. Thus although the testing temperature is far above their Af temperatures in Fig. 3, the introduced dislocations probably stabilize the martensite after the removal of the load. As we known, the decrease of Fe content should reduce the volume fraction of the Fe-rich precipitates in the BCC phase separation26. So the amounts of Fe-rich precipitates decrease. This should result in the decrease of the martensitic transformation temperatures because that more Fe and Mn are retained in the parent4,5. As a result, the resistance to the movement of habit plane during reverse transformation reduces, and it results in a “normal” SE property of the alloys in Figs 4a and 5. Furthermore, with the increases of deformation level and mechanical cycling times, the more dislocations should be formed, thus the resistance to the movement of habit plane increases accordingly. It may also induce the phenomenon of the “stabilized stress-induced martensite” in Fig. 4b.
In our view, the shape recovery behaviors of Cu-12.2Al-4.3Fe-6.6Mn and Cu-12.9Al-3.8Fe-5.6Mn alloys are also different from the conventional SME. The above studied two alloys exhibit extreme “temperature-sensitivity”, in which the deformation strain after unloading can recover instantly and completely accompanied with the jumping of the sample. We consider the mechanism of jumping behavior based on the TEM images as follows. The precipitates play as obstacles for movement of habit plane during reverse transformation. The stress-induced martensite during loading is stabilized by the precipitates and the introduced dislocations. Therefore, the barrier for the habit plane movement becomes higher. The reverse transformation starts by building up the driving force from the inevitable trend of reverse martensitic transformation during heating. When a critical temperature is reached, the driving force is large enough to overcome the resistance of the pinners. In this situation, the suppressed reverse martensitic transformation can proceed instantly and completely with a full shape recovery. At the same time, the phenomenon of the “jumping” of the samples happens.
Conclusions
In summary, the presently developed low-cost Cu-12.2Al-4.3Fe-6.6Mn and Cu-12.9Al-3.8Fe-5.6Mn SMAs possess unique stress-strain and shape recovery characteristics. The large recovery strain of about 9% is originated from the reverse transformation of the stabilized stress-induced 2H martensite triggered through heating. The shape recovery process is extremely temperature-sensitive upon heating and can complete instantly when a critical temperature is reached. Our findings suggest that the present alloys can be considered to be used as new metallic functional materials, such as high sensitivity detector or sensor. Especially, Cu-12.2Al-4.3Fe-6.6Mn alloy exhibits a recovery temperature higher than 100 °C and excellent thermomechanical stability, which also offers great promise for high temperature applications.
Methods
Three samples with the chemical compositions of Cu-12.2Al-4.3Fe-6.6Mn, Cu-13.5Al-2.9Fe-6.8Mn and Cu-12.9Al-3.8Fe-5.6Mn (mass%) alloys were prepared by arc melting under an argon atmosphere using a non-consumable tungsten electrode. The ingots were cut into small bulks and sealed into vacuum quartz ampoules, and annealed at 900 °C for 24 h followed by quenching into ice-water. The chemical composition analysis was determined by electron probe microanalysis (EPMA) and transmission electron microscopy-energy dispersive spectrometer (TEM-EDS). The microstructure was observed by optical microscopy (OM) and transmission electron micrographs (TEM). The crystal structure was identified by TEM and the selected area diffraction pattern (SADP). The martensitic transformation temperatures were determined by differential scanning calorimetry (DSC) at a heating and cooling rate of 10 °C min−1.
Cylindrical specimens (3 mm diameter, 5 mm height) were cut from the quenched bulks. The shape recovery properties were performed by compressive tests. The thermomechanical stability of Cu-12.2Al-4.3Fe-6.6Mn alloy was measured by thermomechanical cycles. Before each cycle, the same sample was compressed to a pre-strain of 12% at room temperature and unloading, then followed by heating to about 700 °C for 2 min and cooling back to room temperature for one cycle. The shape recovery during the 1st cycle was measured by thermal mechanical analysis (TMA) under an argon atmosphere at a heating and cooling rate of 10 °C min−1. The subsequent cycles for the same sample were taken up in air until to fifty times. The height of the sample was measured before loading (h0), after unloading (h1) and after recovery (h2). The shape recovery strain and rate were calculated as: (h2 − h1)/h0 × 100% and (h2 − h1)/(h0 − h1) × 100%, respectively.
Additional Information
How to cite this article: Yang, S. et al. A jumping shape memory alloy under heat. Sci. Rep. 6, 21754; doi: 10.1038/srep21754 (2016).
References
Otsuka, K. & Wayman, C. M. Eds. Shape memory materials (Cambridge Univ. Press, Cambridge, 1998).
Dasgupta, R. A look into Cu-based shape memory alloys: Present scenario and future prospects. J. Mater. Res. 29, 1681–1698 (2014).
Omori, T. et al. Abnormal grain growth induced by cyclic heat treatment. Science 341, 1500–1502 (2013).
Kainuma, R., Takahashi, S. & Ishida, K. Thermoelastic martensite and shape memory effect in ductile Cu-Al-Mn alloys. Metall. Mater. Trans. 27A, 2187–2195 (1996).
Sutou, Y., Kainuma, R. & Ishida, K. Effect of alloying elements on the shape memory properties of ductile Cu-Al-Mn alloys. Mater. Sci. Eng. A. A273–275, 375–379 (1999).
Kainuma, R. et al. Magnetic-field-induced shape recovery by reverse phase transformation. Nature 439, 957–959 (2006).
Ma, Y. Q. et al. Study of Ni50+x Mn25Ga25−x (x = 2–11) as high-temperature shape memory alloys. Acta Mater. 55, 1533–1541 (2007).
Tanaka, Y. et al. Ferrous polycrystalline shape-memory alloy showing huge superelasticity. Science 327, 1488–1490 (2010).
Otsuka, K., Wayman, C. M., Nakai, K., Sakamota, H. & Shimizu K. Superelasticity effects and stress-induced martensitic transformations in Cu-Al-Ni alloys. Acta Metall. 24, 207–226 (1976).
Ma, J., Karaman, I. & Noebe, R. D. High temperature shape memory alloys. Inter. Mater. Rev. 55, 257–315 (2010).
Yang, S. Y., Liu. Y., Wang, C. P., Shi, Z. & Liu, X. J. The mechanism clarification of Ni-Mn-Fe-Ga alloys with excellent and stable functional properties. J. Alloys Compd. 560, 84–91 (2013).
Firstov, G. S., Koval, Yu. N., Van Humbeeck, J. & Ochin, P. Martensitic transformation and shape memory effect in Ni3Ta: A novel high-temperature shape memory alloy. Mater. Sci. Eng. A 481–482, 590–593 (2008).
Firstov, G. S., Van Humbeeck, J. & Koval, Yu. N. Comparison of high temperature shape memory behavior for ZrCu-based, Ti-Ni-Zr and Ti-Ni-Hf alloys. Scr. Mater. 50, 243–248 (2004).
Golberg, D. et al. High-temperature shape memory effect in Ti50Pd50-x Ni x (x = 10, 15, 20) alloys. Mater. Lett. 22, 241–248 (1995).
Golberg, D., Xu, Y., Murakami, Y., Morito, S. & Otsuka, K. Improvement of a Ti50Pd30Ni20 high temperature shape memory alloy by thermomechanical treatments. Scr. Metall. Mater. 30, 1349–1354 (1994).
Hsieh, S. & Wu, S. A study on ternary Ti-rich TiNiZr shape memory alloys. Mater. Charact. 41, 151–162 (1998).
Meng, X. L., Zheng, Y. F., Wang, Z. & Zhao, L. C. Shape memory properties of the Ti36Ni49Hf15 high temperature shape memory alloy. Mater. Lett. 45, 128–132 (2000).
Yang, S. Y., Liu, Y., Wang, C. P. & Liu, X. J. Martensite stabilization and thermal cycling stability of two-phase NiMnGa-based high-temperature shape memory alloys. Acta Mater. 60, 4255–4267 (2012).
Lelatko, J. & Morawiec, H. High temperature Cu-Al-Nb-based shape memory alloys. J. de Phys. IV. 11, 487–492 (2001).
Lelatko, J., Morawiec, N., Koval, Yu. N. & Kolomyttsev, V. I. Structure and properties of high-temperature alloys with the effect of shape memory in the system Cu-Al-Nb. Met. Sci. Heat Treat. 41, 351–353 (1999).
Guilemany, J. M., Fernández, J., Franch, R., Benedetti, A. V. & Adorno, A. T. A new Cu-based SMA with extremely high martensitic transformation temperatures. J. de Phys. IV. 05, 361–365 (1995).
Yang, S. Y., Su, Y., Wang, C. P. & Liu, X. J. Microstructure and properties of Cu-Al-Fe high-temperature shape memory alloys. Mater. Sci. Eng. B 185, 67–73 (2014).
Wang, C. P., Su, Y., Yang, S. Y., Shi, Z. & Liu, X. J. A new type of Cu-Al-Ta shape memory alloy with high martensitic transformation temperature. Smart Mater. Struct. 23, 025018-1-7 (2014).
Xu, H. B. Cu-based high-temperature shape-memory alloys and their thermal stability. Mater. Sci. Forum 394–395, 375–382 (2002).
Kainuma, R., Satoh, N., Liu, X. J., Ohnuma, I. & Ishida, K. Phase equilibria and Heusler phase stability in the Cu-rich portion of the Cu-Al-Mn system. J. Alloys Compd. 266, 191–200 (1998).
Wang, C. P., Liu, X. J., Ohnuma, I., Kainuma, R. & Ishida, K. Thermodynamic database of phase diagrams in Cu-Fe base ternary system. J. Phase Equilib. Diff. 25, 320–328 (2004).
Umino, R. et al. Experimental determination and thermodynamic calculation of phase equilibria in the Fe-Mn-Al system. J. Phase Equilib. Diff. 27, 54–62 (2006).
Acknowledgements
We acknowledge the financial supports from National Natural Science Foundation of China, grant numbers 51201145, 51471138 and 51571168, the Ministry of Science and Technology of China, grant number 2014DFA53040, the National Key Basic Research Program of China, grant number 2012CB825700.
Author information
Authors and Affiliations
Contributions
S.Y.Y. and X.J.L. initiated and supervised this work. S.Y.Y. and C.P.W. designed the alloy compositions. S.Y.Y. prepared the specimens in this study and preformed the research on shape memory properties. T.O., M.N. and R.K. identified the microstructure and crystal structure of the specimens. J.J.R. carried out the DSC experiments. S.Y.Y., Y.L., T.O., R.K. and K.I. contributed to the date interpretation and the revision of the manuscript. All authors discussed the results and approved the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Yang, S., Omori, T., Wang, C. et al. A jumping shape memory alloy under heat. Sci Rep 6, 21754 (2016). https://doi.org/10.1038/srep21754
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep21754
This article is cited by
-
Transformation Behavior of a Shape Memory Ni50.7Ti49.3 (at.%) Alloy during Partial Thermal Cycling
Journal of Materials Engineering and Performance (2023)
-
Exploding and weeping ceramics
Nature (2021)
-
Vision based supervised restricted Boltzmann machine helps to actuate novel shape memory alloy accurately
Scientific Reports (2021)
-
Microstructure, martensitic transformation and shape memory effect of polycrystalline Cu-Al-Mn-Fe alloys
Science China Technological Sciences (2021)
-
Microstructure characterization, stress–strain behavior, superelasticity and shape memory effect of Cu–Al–Mn–Cr shape memory alloys
Journal of Materials Science (2017)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.