Scalable and low-cost doping of graphene could improve technologies in a wide range of fields such as microelectronics, optoelectronics, and energy storage. While achieving strong p-doping is relatively straightforward, non-electrostatic approaches to n-dope graphene, such as chemical doping, have yielded electron densities of 9.5 × 1012 e/cm2 or below. Furthermore, chemical doping is susceptible to degradation and can adversely affect intrinsic graphene’s properties. Here we demonstrate strong (1.33 × 1013 e/cm2), robust, and spontaneous graphene n-doping on a soda-lime-glass substrate via surface-transfer doping from Na without any external chemical, high-temperature, or vacuum processes. Remarkably, the n-doping reaches 2.11 × 1013 e/cm2 when graphene is transferred onto a p-type copper indium gallium diselenide (CIGS) semiconductor that itself has been deposited onto soda-lime-glass, via surface-transfer doping from Na atoms that diffuse to the CIGS surface. Using this effect, we demonstrate an n-graphene/p-semiconductor Schottky junction with ideality factor of 1.21 and strong photo-response. The ability to achieve strong and persistent graphene n-doping on low-cost, industry-standard materials paves the way toward an entirely new class of graphene-based devices such as photodetectors, photovoltaics, sensors, batteries, and supercapacitors.
The benefit of using of chemical-vapor-deposited (CVD) graphene as a passive transparent electrode1,2 is well recognized, but its potential to be paired with a semiconductor and play an active role as part of an electronic junction remains a very active field of research3,4,5,6,7. To enable more control in fabricating active graphene-semiconductor junctions, pristine CVD graphene must be doped p-type or n-type, since unlike epitaxial graphene8, it is not doped upon growth. Electrostatic4,5,6 and chemical doping7 have resulted in Schottky diodes between p-doped graphene and n-type silicon. However, unlike p-doping, which occurs even naturally for graphene exposed to atmospheric water molecules9, persistent graphene n-doping with high electron density that is resistant to degradation has been more difficult to achieve. To this end, nitrogen based precursors during growth10 as well as amines11,12 and transition/alkali metals13,14,15,16,17 after growth have been explored. Although these approaches have shown promise in highly controlled experimental settings, all existing persistent n-doping techniques10,11,12,13,14,15,16,17 fail to achieve the strength (more than 9.5 × 1012 e/cm2 (ref. 11)), robustness, and scalability ultimately required for most applications1,2. Previous reports have shown that adsorbed alkali-metal atoms cause strong n-doping in graphene, but challenges remain, such as the reactivity of alkali metals and the lack of a scalable process15. We demonstrate that an alkali metal (Na) embedded in inert, industrial-grade (~8% Na2O), low-cost soda-lime glass (SLG) overcomes these challenges and strongly n-dopes graphene (1.33 × 1013 e/cm2, see Fig. S1 in the Supplementary Information for comparison to the n-doping strength achieved in refs 10, 11, 12, 13, 14, 15) via surface-transfer doping from Na, upon transfer of CVD-grown graphene onto the SLG. Initial tests show that the doping strength does not degrade when the devices are left in air for several weeks, which is already superior to previously demonstrated methods. The persistence of the doping achieved with this technique (that is, the resistance to degradation) is due to the effectively inexhaustible reservoir of Na in the SLG, in contrast to chemical doping where the doping strength degrades due to the reactivity or evaporation of the finite amount of externally introduced dopants10,11,12.
A field-effect transistor (FET) with multi-layer graphene (GR) transferred onto SLG (8% Na2O) was characterized to obtain a plot of conductance (G) (maximum normalized to one) vs. gate-voltage (VG) (Fig. 1A). The minimum G value (i.e., Dirac point) is seen at −67 V, indicating n-doping of 1.33 × 1013 e/cm−2 and a Fermi energy shift (ΔEF) of +426 meV. Photoelectron spectroscopy and secondary ion mass spectrometry (SIMS) of Na in the SLG (supplementary Figs 4 and 5) indicate a Na surface density (ρNa) of ρNa = 1.15 ± 0.05 × 1014 cm−2 at the surface adjacent to graphene; similar densities of alkali metals on graphene are known to induce strong n-doping via electron transfer from the metal atoms to graphene16,17. Density functional theory (DFT) calculations (Supplementary section 10) that assume a Na monolayer on graphene (with ρNa = 7.6 × 1014 cm−2–close to the measured surface-density of Na on SLG), show n-doping with ΔEF = + 474 meV (Fig. 1B), in close agreement with the experimental measurements (ΔEF = + 426 meV). The measured charge-transfer rate of 0.11e per-Na-atom is also in agreement with literature values of 0.1e–0.2e13,17. As a control experiment, the transconductance of a graphene FET on a low-Na (<1% Na2O) borosilicate-glass (BSG) substrate shows a Dirac point at VG ~0 V (inset Fig. 1A), indicating no doping and attributable to the lower ρNa (~2.30 ± 0.3 × 1013 cm−2, Fig. S5) of BSG compared to SLG. These measurements confirm that the strong graphene n-doping on SLG is caused by charge transfer from the high density of Na near the surface.
Next, to test if graphene/p-type semiconductor/SLG substrates result in n-doping of graphene via Na diffusion through the semiconductor, and the corresponding formation of a p-n junction, we deposited p-type CIGS onto the Mo-side of a Na-rich SLG substrate coated with 330 nm of Mo, and then transferred graphene onto the CIGS surface. CIGS/Mo/SLG was chosen because it is a standard substrate used in the solar industry, and so our measurements will help determine the feasibility and versatility of this doping method in real-world applications. SLG substrates are commonly used because Na in CIGS is known to improve solar cell performance18,19. During co-evaporation of CIGS on to Mo/SLG above 550 °C (evaporated Mo layer on SLG serves as a contact), Na diffuses from the SLG into the CIGS along the grain-boundaries seeking oxygen for an octahedral co-ordination20, ultimately forming Na2CO3, NaSeO3, or NaOH at the CIGS/air surface18,21. Figure 1C indicates that the Na concentration in CIGS increases rapidly near the CIGS/air surface, reaching a value of ρNa = 4.18 × 1013 cm−2 at the surface. In contrast, the CIGS/air surface ρNa in CIGS/Mo/BSG is nearly two orders of magnitude lower (ρNa = 6.16 × 1011 cm−2).
The HR-TEM in Fig. 1D shows that the graphene on top of the CIGS/Mo/SLG substrate is multi-layer graphene with 5-layers and an interplanar spacing of 340 pm, in agreement with previous reports for pristine graphene (335 pm)22. Raman spectroscopy (Fig. 1E) shows the primary CIGS peak23 at 177 cm−1, along with the graphene G peak at 1585 cm−1 and the 2D peak24 at 2665 cm−1; the graphene D peak24 at 1350 cm−1 is negligible, indicating minimal damage during transfer to the rough CIGS surface (Fig. S2). Energy dispersive spectroscopy (EDS) (Fig. 1F) reveals that Na is distributed uniformly (top-panel) in-plane along the GR/CIGS interface, making electronic interactions between the Na and graphene extremely likely (Fig. 1G). We note that by using a configuration in which the Na host (not necessarily SLG) is in direct contact with graphene (Na-host/graphene/semiconductor), this approach can be used to form n-graphene/p-semiconductor junctions for a wide range of p-type semiconductors.
The doping effects and junction properties of graphene on CIGS/Mo/SLG (and on CIGS/Mo/BSG) are investigated using the four-terminal device in Fig. 2A. Figure 2B shows an SEM top-view and the inset shows a TEM cross-section. Figure 2C shows the conductance (normalized) vs.VG and the ΔEF of each device (schematic on right). For GR/CIGS/Mo/SLG (red-curve), the conductance minimum VG (Dirac point) exceeds the measurement limit and is estimated via extrapolation to be VG = −106 V (Fig. S8), confirming strong n-doping (2.11 × 1013 e/cm−2) with ΔEF = +536 meV, surpassing the ΔEF for graphene on neat SLG (green-curve). This strong n-doping results from the high Na density that diffuses through CIGS and concentrates at the CIGS/air surface (ρNa = 4.18 × 1013 cm−2, Fig. S7). This conclusion is supported by the fact that graphene on CIGS/Mo/BSG (yellow-curve) with CIGS/air surface ρNa = 6.16 × 1011 cm−2 (Fig. S7) is not doped, similar to GR/BSG (cyan-curve). Furthermore, ΔEF = + 536 meV of GR/CIGS/Mo/SLG agrees with the potential-shift (ΔΦ) (+698 meV) due to the Na-ion dipole interaction on graphene, as calculated using Helmholtz equation (see Supplementary Information, Section 6)25. Comparatively, the calculated shift for GR/CIGS/Mo/BSG with ρNa = 6.16 × 1011 cm−2 is ΔΦ ~10 meV, explaining the lack of n-doping. Interestingly, the electron transfer rate from Na to graphene in GR/CIGS/Mo/SLG (0.50e per-Na-atom), is higher than in GR/SLG (0.11e per-Na-atom), which we attribute to ionization-rate differences of the Na species on the CIGS and SLG surfaces.
Figure 2D is the current-voltage (I–V) curve between graphene-Mo contacts in the dark (dashed), and 11.14 mW cm−2 white light (solid), with (red) and without (blue) the Al2O3 gate-dielectric (Fig. 2A). These measurements show non-linear diode-behavior with a photocurrent response, with much higher performance when the Al2O3 top layer is present. Relative to the measurements without the Al2O3 top-layer, the reverse saturation current density (J0) with Al2O3 is reduced by 104 to 0.36 nA/cm2 (Fig. S10), the photocurrent is enhanced by a factor of 650 at −10 mV, and the ideality factor becomes as low as 1.29. Figure 2C shows that a control GR/SiO2/p-Si FET without the Al2O3 dielectric (dashed blue curve) has a Dirac point beyond VG = +100 V, indicating strong p-doping; a GR/SiO2/p-Si FET with the Al2O3 dielectric (Fig. 2C, solid blue curve) shows much less p-doping, with a Dirac point near VG ~ 20 V. These measurements demonstrate that the Al2O3 dielectric shields the graphene from p-dopants in ambient air, resulting in an enhanced Schottky barrier (Φb) and built-in field.
Figure 2E shows I–V curves of GR/CIGS/Mo/SLG at different VG, where J0 is reduced as VG is increased from −100 V to 50 V. Plotting ln(J0) vs. (|VG + ΔVF|)1/2 , we obtain Φb = 0.29 eV (Supplementary Information, Section 8). The photocurrent at zero-bias increases as graphene is n-doped further by increasingly positive VG (Fig. 2F), which we attribute to the concomitant increase in the built-in field. Moreover, under 1000 W m−2 illumination at VG = 0, the photocurrent is 13.6 mA/cm2, yielding a power conversion efficiency of ~1%; this represents the first demonstration of n-graphene/p-CIGS photovoltaic behavior. The lowest ideality factor obtained was 1.21 (Fig. S11), indicating negligible recombination in the space-charge region26.
The behavior of J0 vs. temperature (T) is modeled assuming Landauer transport5 in the GR/CIGS/Mo/SLG (Fig. 3A) giving Φb = 0.13 eV. Assuming ideal Schottky-diode behavior, ln(J0/T2) vs. 1/T (inset to Fig. 3A) yields Φb = 0.11 eV, while ln(J0) vs. (|VG + ΔVF|)1/2 (Fig. S13) yields Φb = 0.29 eV at zero gate bias, with a constant Richardson coefficient of 1.18 × 10−6 mAcm−2K−2. As is discussed below, this range for Φb (0.11 eV–0.29 eV) is lower than expected, which we believe is due to surface defects and surface sodium doping of CIGS that lowers the surface ionization potential of CIGS relative to the bulk.
The barrier height (Φb) is equal to the ionization potential of the CIGS semiconductor (IPCIGS) minus the work function of graphene (ΦG), and represents the barrier that a hole in the valence band of CIGS must overcome to reach the graphene interface and recombine with an electron there. The activation energy (Ea), on the other hand, represents the characteristic energy that governs the rate of minority carrier (electron) excitation into the conduction band of the p-type semiconductor CIGS. In an intrinsic semiconductor, Ea is equal to half the bandgap, and for a doped p-type semiconductor like CIGS, its value should be close to the bandgap energy, since in this case the Fermi level is close to the valence band.
While fitting the J0 vs. T data to the Schottky barrier model allows us to determine Φb, fitting this same data to the modified-Arrhenius/activation-energy model (Eqs (S11 and S12) and Fig. 3B) allows us to determine a value for Ea, which will indicate whether the recombination is predominantly bulk or interfacial. The ideality factor n is expected to become temperature dependent in the presence of tunneling. The measured I–V data is used to determine n as a function of temperature and this is directly incorporated into Eq. (S11), which allows us to separate the effects of Ea and n on the reverse saturation current density J0. Figure 3B shows a modified Arrhenius-plot of nln(J0) vs. 1/T (where n is the ideality factor), yielding an activation energy (Ea) of 0.96 eV, which indicates dominant interfacial recombination since it is less than the CIGS bandgap of 1.15 eV (Ref. 26). We have demonstrated that this interfacial recombination can be reduced using a very thin (4 nm) TiO2 blocking layer between graphene and CIGS, thereby improving Voc from 0.23 V to 0.49 V (Fig. S14). The space-charge width (Wd) of the diode is measured to be 190 nm using C-V measurements (Fig. 3C). The approximate band structure of the Schottky diode is given in Fig. 3D. The difference between the CIGS ionization-potential (IPCIGS = 5.65 eV (ref. 27)), and graphene work function 4.69 eV (ref. 28) modified by the image-potential correction (0.15 eV), gives a theoretical ΦbT = 0.81 eV. Due to defects29 and Na surface density30, IPCIGS is ~0.5 eV lower, yielding ΦbT = 0.31 eV, which is much closer to the measured range of Φb = 0.11 eV–0.29 eV. It is worth noting that even though the best-fit range of Φb (0.11 eV–0.29 eV) is much less than the best-fit value of Ea (0.96 eV), both models yield good fits to the same J0vs. T data due to the inclusion of the temperature-dependent n in the activation-energy model.
In conclusion, we have demonstrated strong (1.33 × 1013 e/cm−2, corresponding to a Fermi energy shift of +426 meV.), robust, and spontaneous n-doping of graphene on the surface of a low-cost industrial-grade soda-lime-glass substrate via surface-transfer doping from the Na. By leveraging the Na diffusion through a p-type CIGS semiconductor deposited onto the soda-lime glass, we applied this method to the formation of a graphene(n)/semiconductor(p) Schottky diode with even stronger graphene n-doping (2.11 × 1013 e/cm−2, corresponding to a Fermi energy shift of +536 meV) than was achieved on bare glass. This method of n-doping does not require any high-temperature annealing steps, and should be compatible with a wide range of semiconductor/substrate systems. The junction properties, such as Schottky barrier height and interfacial recombination rate, can be controlled by tuning the doping strength via the thickness of a few-nm dielectric layer such as TiO2 or Al2O3. Advantages of this technique include the lack of external chemicals whose doping strength decays over time, the ability to achieve strong and persistent n-doping of graphene that is placed on top of a p-doped semiconductor, the ability to n-dope graphene on a wide range of p-doped semiconductors via the use of a Na host that is in direct contact with the graphene layer, and the ability to control the strength of the doping via the use of a spacer layer (e.g., TiO2) between the Na host and the graphene layer. Disadvantages include the possible restriction to p-doped semiconductors that are not too strongly affected by the Na diffusion from the Na host to the graphene layer, in the case where the semiconductor lies between the Na host and the graphene layer.
Strong, robust, and tunable graphene doping opens the door for the practical realization of many envisioned applications of graphene such as touch screens and organic light-emitting diodes1, where the reduction of sheet resistance is crucial to future success, and a broad array of other applications where strong and tunable n-doping is important, such as microelectronics, photodetectors, photovoltaics, electrochemical energy storage, and sensors2.
CIGS deposition on Mo/SLG
Given in Supplementary Information, Section 2.
Supplementary Fig. S3 shows a schematic of the graphene/CIGS device fabrication process. In order to make our GR/CIGS devices, 450 nm of SiO2 is first deposited on top of the CIGS/Mo/SLG (BSG) substrates via plasma-enhanced chemical vapor deposition (PECVD) at 160 °C at 1.6 nm/s rate. Next, 1 × 1 μm2–500 × 500 μm2 regions were patterned on the PECVD SiO2 either using optical lithography (or ebeam lithography) techniques depending on the feature size. E-beam was performed using the E-beam lithography JEOL JBX-6300FS system on E-beam resist positive resist ZEP520A (spun at 2000 rpm for 40 sec annealed at 180 °C for 3 minutes) by exposing with a dose of 400 μC/cm2 at 100 keV and developed with hexylacetate for 90 sec. In optical lithography, the tool MA6 Mask aligner was used with positive optical resist S1811spun at 4000 rpm for 45 sec annealed at 110 °C for 1 minute, and developed with MIF 312 3:2 with DI water for 1 minute. These patterned regions were then etched via Reactive Ion Etching (RIE) (Oxford Plasmalab 100 ICP etcher) using a mixture of (CHF3 and Ar) at 15 nm/min, until the CIGS was exposed. Commercially obtained CVD graphene on Cu foil (Graphene Platform) was then transferred from the Cu substrates to the SiO2/CIGS/Mo glass substrates. The graphene transfer was done by coating the graphene side of the graphene/Cu foils with PMMA (10% w/w in chlorobenzene spun at 3000 rpm for 1 min sec and annealed at 140 °C per 1 min), oxygen plasma etching (March Plasma Etcher, 20 W, 100 mT for 20 sec) the opposite side, and etching the Cu using ammonium persulfate (0.1 M) solution overnight. As the Cu is etched away, the graphene/PMMA film floats on the etchant and it is washed in de-ionized water (>18 MΩ resistivity using a Millipore DI system) and it then transferred, graphene-side down, onto the pattered CIGS/Mo/SLG or other control substrates such as neat SLG or BSG substrate. Afterwards, graphene transferred substrates are annealed at 100 °C for 30 minutes in a vacuum oven to remove water, and are subsequently annealed at 200 °C for 15 minutes to soften the PMMA and promote conformal adhesion onto substrates. It is found that the 200 °C annealing step is extremely critical in getting highly uniform, wrinkle- and damage-free graphene films on the rough surfaces of CIGS and SiO2 substrates. Afterwards, the PMMA is removed from the graphene by immersing in acetone overnight and the substrate is further annealed in a Rapid Thermal Annealer at 375 °C in Ar (96%): H2(4%) forming gas for 15 minutes for complete PMMA removal. Next, the graphene is etched following optical (ebeam) lithographic patterning using oxygen plasma etch. (March plasma, 100 W and 100 mT for 1 minutes or Oxford Plasma Lab DRIE at 20 °C for 20 seconds in O2) using a negative tone resist mask (E-beam lithography uses ma-N 2403, spun at 2000 rpm for 30 sec exposed at 200 μC/cm2 dose for 100 keV for electron beam and developed using ma-D 532 negative tone developer for 1 minute, Optical lithography uses maN-1410 negative resist spun at 3000 rpm for 30 seconds exposed and developed in ma-D 533 for 1 minute). After etching the graphene, source-drain electrical contacts (Au (30 nm)/Cr (5 nm)) are deposited using ebeam evaporation after optical (ebeam) lithography patterning. Next, a 200 nm top gate-dielectric layer (Al2O3) is blanket deposited on GR/CIGS/Mo/SLG(BSG) or GR/SLG(BSG) substrates via Atomic Layer Deposition at 1 Ǻ/cycle using (Tri Methyl Aluminum) TMA/Water precursor at 250 °C. On top of the Al2O3, a semi-transparent top-gate (10 nm of Au) is deposited via ebeam evaporation following optical (ebeam) lithography patterning. Next, the source and drain electrodes are exposed through the dielectric layer by RIE etching of Al2O3 using BCl3 by Oxford Plasmalab 100 ICP etcher, on a mask pattern using optical (ebeam) lithography.
Given in Supplementary Information, Section 3.
How to cite this article: Dissanayake, D. M. N. M. et al. Spontaneous and strong multi-layer graphene n-doping on soda-lime glass and its application in graphene-semiconductor junctions. Sci. Rep. 6, 21070; doi: 10.1038/srep21070 (2016).
Novoselov, K. S. et al. A roadmap for graphene. Nature . 490, 192–200 (2012).
Bonaccorso, F. et al. Graphene, related two-dimensional crystals, and hybrid systems for energy conversion and storage. Science . 347, 6217 (2015).
Tongay, S. et al. Rectification at Graphene-Semiconductor Interfaces: Zero-Gap Semiconductor-Based Diodes. Phys. Rev. X 011002, (2012).
Yang, H. et al. Graphene Barristor, a Triode Device with a Gate-Controlled Schottky Barrier. Science 336, 1140 (2012).
Sinha, D. & Lee, J. U. Ideal Graphene/Silicon Schottky Junction Diodes. Nano Lett. 14, 4660–4664 (2014).
Li, X. et al. Graphene-On-Silicon Schottky Junction Solar Cells. Adv. Mater . 22, 2743–2748 (2010).
Miao, X. et al. High Efficiency Graphene Solar Cells by Chemical Doping. Nano lett. 12, 2745–2750 (2012).
Zhou, S. Y. et al. Substrate-induced bandgap opening in epitaxial graphene. Nature Mater . 6, 770–775 (2007).
Schedin, F. et al. Detection of individual gas molecules adsorbed on graphene. N. Mater . 6, 652–655 (2007).
Wang, H., Maiyalagan, T. & Wang, X. Review on Recent Progress in Nitrogen-Doped Graphene: Synthesis, Characterization, and Its Potential Applications. ACS Catalysis 2, 781–784(2012).
Kim, Y., Yoo, J. M., Jeon, H. R. & Hong, B. H. Efficient n-doping of graphene films by APPE (aminophenyl propargyl ether): a substituent effect. Phys. Chem. Chem. Phys. 15, 18353–18356 (2013).
Dong, X. et al. Doping Single-Layer Graphene with Aromatic Molecules. Small. 5, 1422–1426 (2009).
Caragiu, M. & Finberg, S. Alkali metal adsorption on graphite: a review. J. Cond. Mater. Phys . 17, R995–R1024 (2005).
Uchoa, B., Lin, C. Y. & Castro Neto, A. H. Tailoring graphene with metals on top. Phys. Rev. Lett. 77, 035420 (2008).
Sung, S. J. et al. Band gap engineering for graphene by using Na+ ions. Appl. Phys. Lett. 105, 081605 (2014).
Breitholtz, M., Kihlgren, T., Lindgren, S.-Å. & Walldén, L. Condensation of Na metal on graphite studied by photoemission. Phys. Rev. B. 67, 235416 (2003).
Johnson, M., Stanberg, M. & Huges, H. Electronic-Structure of Alkali-metal Overlayers On Graphite Surface Science. Surface Science . 178, 290–299 (1999).
Granath, K., Bodegard, M. & Stolt, L. The effect of NaF on Cu(In, Ga)Se2 thin film solar cells. Sol. Eng. Mater. Sol. Cells . 60, 279–293 (2000).
Wei, S., Zhang, S. & Zunger, A. Effects of Na on the electrical and structural properties of CuInSe2 . J. of Appl. Phys . 85, 7214–7218 (1999).
Kronik, L., Cahen, D. & Schock, H. W. Effects of sodium on polycrystalline Cu(In,Ga)Se2 and its solar cell performance. Adv. Mater . 10, 31–36 (1998).
Niles, D. et al. Na impurity chemistry in photovoltaic CIGS thin films: Investigation with x-ray photoelectron spectroscopy. J. Vac. Sci. Technol. A. 15, 3044–3049 (1997).
Spanu, L., Sorella, S. & Galli, G. Nature and Strength of Interlayer Binding in Graphite. Phys. Rev. Lett. 103, 196401 (2009).
Witte, W., R. & Raman, M. P. Investigations of Cu(In,Ga)Se2 thin films with various copper contents. Thin Solid Films 517, 867–869 (2008).
Ferrari, A. C. et al. Raman Spectrum of Graphene and Graphene Layers. Phys. Rev. Lett. 97, 187 401 (2006).
Kohn, W. & Lau, K. H. Adatom Dipole Moments on Metals and Their Interactions. Solid State Commun. 18, 553–555 (1976).
Nadenau, V., Rau, U., Jasenek, A. & Schock, H. W. Electronic properties of CuGaSe2-based heterojunction solar cells. Part I. Transport analysis. J. Appl. Phys. 87, 584–593 (2000).
Siebentritt, S. & Rau, U . Wide-Gap Chalcopyrites (Springer Series in Materials Science). 86 (2006).
Yu, Y. et al. Tuning the Graphene Work Function by Electric Field Effect. Nano Lett. 9, 3430–3434 (2009).
Hinuma, Y., Oba, F., Kumagai, Y. & Tanaka, I. Ionization potentials of (112) and (112) facet surfaces of SuInSe2 and CuGaSe2 . Phys. Rev. B. 86, 245433 (2012).
Heske, C., Fink, R., Umbach, E., Riedl, W. & Karg, F. Na induced effects on the electronic structure and composition of Cu(In,Ga)Se2 thin film surfaces. Appl. Phys. Lett. 68, 3431–3433 (1996).
We thank Marcus Bär, Regan Wilks, and Fernando Camino for helpful discussions. We also thank Jesse Claypoole for SIMS and XPS measurements. This work was partially supported by the U.S. Department of Energy, Sustainable Energy Technologies Department under Contract No. DE-SC0012704, and Brookhaven National Laboratory’s Laboratory Directed Research and Development (LDRD) Program. Research carried out in part at the Center for Functional Nanomaterials, Brookhaven National Laboratory, which is supported by the U.S. Department of Energy, Office of Basic Energy Sciences, under Contract No. DE-SC0012704.
The authors declare no competing financial interests.
About this article
Cite this article
Dissanayake, D., Ashraf, A., Dwyer, D. et al. Spontaneous and strong multi-layer graphene n-doping on soda-lime glass and its application in graphene-semiconductor junctions. Sci Rep 6, 21070 (2016). https://doi.org/10.1038/srep21070
The Journal of Physical Chemistry C (2020)
Buckling of Multilayer Graphene Sheets Subjected to Axial Compression Based on a Continuum Mechanics Model
Journal of Applied Mechanics (2018)
Excitation Wavelength Dependence of Combined Surface- and Graphene-Enhanced Raman Scattering Experienced by Free-Base Phthalocyanine Localized on Single-Layer Graphene-Covered Ag Nanoparticle Arrays
The Journal of Physical Chemistry C (2018)
The Impact of Graphene on the Fabrication of Thin Film Solar Cells: Current Status and Future Prospects
A plate model for multilayer graphene sheets and its finite element implementation via corotational formulation
Computer Methods in Applied Mechanics and Engineering (2017)