Abstract
We show a simple and effective way to improve the vortex irreversibility line up to very high magnetic fields (60T) by increasing the density of second phase BaZrO3 nanoparticles. (Y0.77,Gd0.23)Ba2Cu3Oy films were grown on metal substrates with different concentration of BaZrO3 nanoparticles by the metal organic deposition method. We find that upon increase of the BaZrO3 concentration, the nanoparticle size remains constant but the twin-boundary density increases. Up to the highest nanoparticle concentration (n ~ 1.3 × 1022/m3), the irreversibility field (Hirr) continues to increase with no sign of saturation up to 60 T, although the vortices vastly outnumber pinning centers. We find extremely high Hirr, namely Hirr = 30 T (H||45°) and 24 T (H||c) at 65 K and 58 T (H||45°) and 45 T (H||c) at 50K. The difference in pinning landscape shifts the vortex solid-liquid transition upwards, increasing the vortex region useful for power applications, while keeping the upper critical field, critical temperature and electronic mass anisotropy unchanged.
Similar content being viewed by others
Introduction
Although the critical temperature (Tc) and upper critical field (Hc2) of high temperature superconductors are extremely high, superconductors only become technically useful at a much lower field-temperature boundary, called the melting, or irreversibility, line. This is due to the appearance of the vortex liquid phase, one of the unique characteristics of these superconductors. In this liquid phase, superconductors have finite resistivity behaving much like a normal metal, thus the need to move the melting line to higher fields/temperatures. Defects can move the melting line, with random point-like defects1 pushing it down and correlated defects moving this line up. The positive effect of correlated disorder is restricted to an angular range near the defects’ orientation and usually only up to a characteristic field related to the density of the defects (the matching field, typically a few tesla)2,3,4,5. Pushing up this upper limit is both technologically and scientifically important; given the interest in high magnetic field magnets. This requires finding ways to immobilize vortex densities much higher than the highest defect density that can be introduced without compromising the material integrity.
Recently, a third kind of disorder (neither correlated nor point-like) has been demonstrated to be effective at improving both Jc and Hirr at a very wide range of field orientations6,7,8,9,10,11,12,13,14. A deeper and more quantitative understanding of the effect of nanoparticles in a mixed pinning landscape (as they often work together with correlated defects) is necessary for assessing the potential of Cu-based superconducting wires for applications at high fields15.
In particular, it is important to establish the behavior of Hirr when the vortex density is much higher than that of the defects. Most REBa2Cu3Oy (REBCO) films (RE = rare earth) with self-assembled nanorods4,5 and YBCO crystals with columnar defects2,3 show improved Hirr and a “kink” in the vortex liquid-glass transition for H||c. This occurs when vortices stop populating columnar defects and start filling interstitial positions, at a density related to that of the defects at the so-called matching field (μ0Hϕ). These findings lead to the validation of the simple argument that once the pinning centers have been outnumbered by vortices, their effect on increasing Hirr decreases or may even be washed out. However, this idea overlooks the fact that vortices are interacting elastic objects, which form a lattice with different degrees of order depending on the underlying pinning landscape. The understanding of the physical system adds a layer of complexity when pinning centers of different dimensions (point defects, lines, planes or nanoparticles) are taken into account.
In this paper, we show that the combination of planar twin boundaries (TBs) and a higher density of three dimensional (3D) nanoparticles (NPs) increases Hirr at up to 60 T. In the case of TBs there is a clear signature of the matching field at very low fields (0.5 T) but nevertheless, their presence continues to increase Hirr up to 60 T. The effect of the NPs is also seen up to 60 T with the additional benefit of their being effective in the entire angular range. We find no signs of saturation in the improvement of Hirr up to 3 wt% BaZrO3 (BZO) added to REBCO wire up to the highest field measured (60 T) and obtain record high values.
Results
The results shown are distributed as follows. We start by explaining the growth methods and show superconducting and microstructural studies. We find that the use of (Y,Gd)BCO is beneficial (as compared to YBCO) and that the addition of BZO NPs does not degrade the general properties and increases twin boundary density. Then we focus on transport measurements in DC and pulsed fields as a function of temperature and field orientation. For the upper critical field, (Hc2), the addition of NPs produces no significant changes. For Hirr, the scenario is complex and depends on the field magnitude and orientation. For H||c, at low fields, twin boundaries dominate the irreversibility line with a matching field observed and a peak as function of field orientation. As the field increases the effects of TBs are less prominent as nanoparticles compete in the vortex localization. At high fields, NPs and TBs cooperate to enhance the Hirr. At intermediate angles (e.g. H||45°) nanoparticles produce the greatest increase in Hirr, showing no saturation up to the highest fields measured. Furthermore, at high fields we obtain a constant improvement of 25% with respect to YBCO films. For H|| ab, the changes due to NPs addition are small as compared to other orientations.
Uniformly dispersed BaZrO3 nanoparticles in (Y0.77Gd0.23)Ba2Cu3Oy wires
The samples used in this study were 0.5 μ thick films of standard YBCO, (Y0.77Gd0.23)Ba2Cu3Oy ((Y,Gd)BCO) and BZO-doped (Y,Gd)BCO ((Y,Gd)BCO+BZO) derived from the metal organic deposition (MOD) process, grown on metal substrates. The content of BZO in the films was 1–3 wt%. The film microstructure was studied by several techniques (see Methods). The planar view transmission electron microscopy (TEM) images of standard YBCO, (Y,Gd)BCO with 1wt% BZO (+1BZO) and 3wt% BZO (+3BZO) wires are shown in Fig. 1a–c, respectively. For clarity, the corresponding bottom panels in those figures show schematics of the main defects. All films have a low density (∼0.1 × 1021/m3) of large RE2Cu2O5 (225) precipitates (shown as open circles in the bottom panels) formed during REBCO crystallization from the precursors containing BaF2, RE2Cu2O5 and CuO. In both +1BZO and +3BZO wires, BZO NPs (modal size ∼23 nm) are randomly distributed and uniformly dispersed. The average density of these nanoparticles was determined to be n = 2.9 × 1021/m3 for +1BZO, n = 7.1 × 1021/m3 for +2BZO (not shown) and n = 13 × 1021/m3 for +3BZO wires, respectively. Note that the greater than linear dependence of n on BZO% derives from the slight decrease in size of the NPs with increasing BZO density. In addition to the uniformly randomly distributed 3D defects (BZO NPs), all samples, including the standard YBCO, contain high densities of two types of planar (2D) defects, namely c-axis correlated TBs (Fig. 1a–d) and stacking faults (SFs) parallel to the ab plane (Fig. 1e). In some previous studies of MOD REBCO with nanoparticles, it was observed that the SFs cut into the TBs, resulting in discontinuous short length TBs14. In contrast, although our +3BZO wire has a high density of SFs as shown in Fig. 1e, the TBs remain connected from the bottom to the surface (Fig. 1d), indicating that the TBs in the BZO NP-doped wire are c-axis correlated pinning centers.
Table 1 shows a summary of the crystallographic and superconducting properties for the YBCO, (Y,Gd)BCO, +1BZO, +2BZO and +3BZO films. No decrease in Tc, or increase of δω or δϕ is observed for the films with BZO inclusions. The only difference found is positive, being that films with Y,Gd have higher Tc and self-field Jc(Jcs.f.) than the YBCO film, consistent with good crystallinity (unchanged δω, δϕ). The Jcs.f. values of the +3BZO film at 65 and 77 K are 12.5 and 4.0 MA cm−2, respectively. These Jcs.f. values are almost as high as those of nanocomposite MOD-YBCO thin films on a single crystal substrate6. The fact that we maintained (or even improved) Jcs.f. and Tc after adding defects is significant given that in some cases, for films grown by pulsed laser deposition (PLD), Tc and Jcs.f decreased with increasing BZO content due to poor crystallinity, local strain and oxygen deficiency near second phases16. The difference in Tc and Jcs.f behavior with BZO% between MOD and PLD processes comes from differences in the formation mechanisms of the BZO/REBCO matrix17.
Irreversibility line at low and intermediate DC magnetic fields
To investigate the influence of the density of BZO NPs on the superconducting properties of the glassy phase, we measured the irreversibility temperature Tirr (H,θ). Figure 2a–c show Tirr (θ) at 0.5, 4 and 15 T for standard YBCO, (Y,Gd)BCO and (Y,Gd)BCO+BZO wires, where θ is the angle between the magnetic field and the c axis.
For the YBCO and (Y,Gd)BCO wires, at low magnetic fields we observe two maxima in Tirr, centered at H||c (θ = 0°) and H||ab (θ = 90°). The peak at H||c comes from c-axis correlated defects. The maximum at H||ab originates from the electronic-mass anisotropy and the SFs. At intermediate fields (see Fig. 2b), the c-axis peak of Tirr in both YBCO and (Y,Gd)BCO becomes very weak, but is evident again at higher fields (see Fig. 2c). We note that the Tirr(θ)/Tc for the YBCO and (Y,Gd)BCO wires are almost identical as shown in inset of Fig. 2, which validates the use of YBCO for the comparison that we are making.
All wires with BZO NPs show an enhanced Tirr(θ) as compared to that of the YBCO and (Y,Gd)BCO wires and the magnitude of the Tirr(θ) enhancement increases with increasing BZO NP content at all magnetic fields (0.5, 4 and 15 T) and at all angles. The Tirr anisotropy, Tirr(||ab)/Tirr(||c), is also smaller for the +BZO samples and decreases monotonically with BZO NP content. At low fields, the +3BZO wire exhibits nearly isotropic properties with a small (in height) c-axis peak. At 15 T, Tirr (θ) shows a small c-axis peak indicating a contribution from correlated pinning. This is consistent with Jc(θ) data10 at high fields where a c-axis peak is also found. In both cases (Jc and Tirr) the c-axis peak height is less pronounced in samples with BZO additions, partially because of the general increase in Jc and Tirr produced by the nanoparticles.
The results in Fig. 2 can be interpreted as follows. At low fields, below the matching field of the TBs (μ0Hϕ,TB) given by μ0Hϕ,TB = (ϕ0/dTB2), where ϕ0 and dTB are the flux quantum and TB spacing respectively, most vortices get localized by the TBs (Fig. 3a). At intermediate H, above μ0Hϕ,TB, the density of vortices is high enough that the TBs become “saturated”, the extra vortices sit outside them and become localized by the randomly distributed NPs which are strong pinning centers (Figs 2b and 3b). At even higher fields, once all the NPs are saturated, no elastic energy is lost by achieving pinning at the TBs, allowing for the localization effect of the TBs to be observed through the caging effect (Fig. 3c), similar to what happens for the standard YBCO sample (Fig. 2c).
To better determine the effects of the c-axis correlated defects, we measured μ0Hirr(T) at low fields for different θ (see Fig. 4). The c-axis irreversibility lines of the wires with and without BZO NPs exhibit a pronounced kink indicating a crossover field (see Hcr arrows). For fields smaller than μ0Hcr, Hirr shows a rapid increase with decreasing T; above μ0Hcr the irreversibility line is closer to a linear temperature dependence. For the +3BZO wire, μ0Hcr is 0.55 T, which is 1.6 times higher than that of YBCO (μ0Hcr = 0.34 T). From TEM images, we observe that this correlates with the higher TB density found in +3BZO as compared to YBCO wires. Indeed, we obtain μ0Hϕ,TB = 2.3T and 1.0T, for +3BZO and YBCO, respectively. This cross-over is remarkably similar to that observed in YBCO bulk with nanoscale TBs18,19 and columnar defects20. For TBs and columnar defects, the cross over field is usually not observed precisely at the matching field but around 1/3-1/2 of Hϕ. This also correlates very well with our observation of the crossover fields with Hcr/Hϕ,TB ∼ 1/3 for samples with and without BZO NPs, namely 0.34 and 0.24 for YBCO and +3BZO, respectively. To further corroborate that the observed crossover field arises from correlated defects and is not an artifact, we confirmed that no kink is found in Hirr-T at H||45° (see Fig. 4). Therefore, we can conclude that the array of TBs is the main source of correlated pinning at H||c in our MOD REBCO wires. Note that the TBs continue to contribute at μ0H ≫ μ0Hcr as seen in the peak of Tirr(θ) around H||c in Fig. 2c and the inset of Fig. 5d.
Irreversibility lines and upper critical fields in pulsed fields
To obtain the temperature and angular dependence of μ0Hc2 and μ0Hirr for the YBCO and (Y,Gd)BCO + BZO wires at even higher fields, we measured ρ(T) and ρ(H) at various θ values by using pulsed fields up to 60 T (see insert Fig. 5b). See Methods for further details.
Figure 5a shows μ0Hc2(T) at H||c, H||45° and H||ab. The results demonstrate that μ0Hc2(T) is remarkably similar for all samples in spite of their very different pinning landscapes. The inset of Fig. 5a shows the electronic-mass anisotropy (γ) vs. T obtained from the Hc2 measurements for the YBCO and (Y,Gd)BCO+BZO wires (see ref. 9 for details). The average values for γ are 5.1, 4.6 and 4.7 for the YBCO, +1BZO and +3BZO wires, respectively. Although γ is slightly smaller for the wires with BZO, all values are very close to 5. Further confirmation of the obtained value of γ, comes from the angular-dependent Hc2 shown in Fig. 5b. The angular dependence of Hc2 can be fit very well using Hε(θ) = H(cos2(θ)+γ-2sin2(θ)) (see ref. 21) with γ = 4.7, in agreement with the experimental result shown in the inset of Fig. 5a. This is also in accordance with our previous work, where we reported that the μ0Hc2(θ) dependence follows a single curve consistent with γ ~ 5 even with different additions and growth methods22. From the μ0Hc2 data, we conclude that μ0Hc2 is not greatly affected by the pinning landscape. It is worth noting that the value of γ ~ 5 is indeed smaller than the values found for YBCO single crystals23,24, as previously noted25. The lack of sensitivity in Hc2 upon increase of disorder can be found in the small coherence length of REBCO (also the reason for high Hc2). The small coherence length places REBCO in the clean limit, thus making its superconducting properties less sensitive to disorder.
On the other hand, the changes in pinning landscape do influence Hirr, as a clear enhancement is found for all +BZO wires compared with YBCO wire (see Fig. 5c,d). Figure 5c displays the μ0Hirr-T at various angles for the YBCO and (Y,Gd)BCO+BZO wires. For H||c and H||45°, wires with BZO NPs show a higher μ0Hirr(T) than that of standard YBCO. Furthermore, we observe that μ0Hirr(T) continues to increases with higher densities of BZO NPs. For H||ab, +BZO samples show a much smaller increase in μ0Hirr(T).
The changes can be better understood by analyzing the Hirr(θ) as shown in Fig. 5d. Consistent with Fig. 5c, the addition of BZO NPs produces a small increase near H||ab and a much bigger enhancement for H||c and intermediate orientations. The resulting angular dependence of Hirr for the +3BZO wire cannot be described using the electronic-mass anisotropy scaling model, unlike Hc2(θ) or YBCO’s Hirr(θ), which do follow ε(θ) for most of its angular dependence (see Fig. 5b,d). More information on the effect of the nanoparticles on Hirr can be observed in the inset to Fig. 5d. In this inset we plot the difference of μ0Hirr(θ)–ε(θ)μ0Hirr for the YBCO and +3BZO sample. For YBCO we observe that, except for the peaks around H||c and H||ab due to correlated disorder (TBs and SFs, respectively), over most of the angular range Hirr(θ) can be very well described by the electronic-mass anisotropy, γ = 5 indicating that most of the angular dependence of Hirr can be explained by pinning arising from weak random point defects such as oxygen vacancies (with diameter in the angstrom scale ≪ 2ξ(T)). For +3BZO we find very similar behavior near the ab-plane, where it shows a peak almost identical to that of the YBCO wire indicating similar ab-plane correlated pinning like SFs (consistent with Hirr(T) in Fig. 5c). However, a much broader maximum is found for |θ| < 80°. This is the consequence of the higher density of TBs coupled with the presence of strong random pinning from BZO NPs as shown in the TEM of Fig. 1b,c and the schematics of Fig. 3. The NPs are responsible for the increases in the wider angular range and the TBs are more effective near the c axis. The broad dome-shape like increase in μ0Hirr(θ)–ε(θ)μ0Hirr due to the NPs resembles the increases found in Jc in samples with nanosized inclusions, both in YBCO and Fe-based superconductors10,26,27,28,29. The reason for this dome shape (or inverse anisotropy) is found in the fact that while NPs are randomly dispersed, they are not point defects, thus do not follow the electronic mass anisotropy scaling as point defects do21. Recently Mishev et al. proposed a model to explain this effect based on the relative size of the vortex core compared to the inclusion size29.
The leveling off observed in Hirr(θ) due to nanoparticles translates into an smaller ratio of Hirr(||ab)/Hirr(||c), with values of 2.9 for +3BZO as compared to 5.0 for YBCO. The decrease in the Hirr ratio (also found in Jc) has been analyzed using an ‘effective anisotropy” (γeff) both for of Jc(θ) and Hirr(θ)6,7,30,31. We attempted to scale the Hirr(θ) data of our BZO NPs doped wires using γeff. Using intermediate angles we obtain γeff ~ 2, but the scaling is not successful, as the data do not collapse onto a single curve as shown in the literature6,7,30,31. It is worth mentioning that although in principle the samples in references 6,7,14 are also MOD with NPs, there are some differences in the microstructure with the wires in this study. Specifically, with the addition of BZO our samples have a higher density of twin boundaries, but the opposite is found in ref. 14.
As shown in Fig. 5c, overall the +3BZO wire shows an extremely high μ0Hirr at 65 K, at 30 T (H||45°) and 24 T (H||c) and at 50 K, 58 T (H||45°) and 45 T (H||c), values which to our knowledge are the highest reported for practical HTS wires31 as well as for thin films on single-crystal substrates32. Recently, very high μ0Hirr = 14.8 and 15.8 T at 77 K (H||c) were observed in a heavily BZO nanorod-doped (Y,Gd)BCO wire grown by metal organic chemical vapor deposition33,34 and BaHfO3 doped PLD GdBCO wire35; these methods could also translate to great improvements of Hirr at high fields. This indicates that a high density of NPs/columns is beneficial not only for MOD prepared materials but is a general trend for REBCO wires.
Discussion
In order to pinpoint H-T regions where the BZO additions are more effective, in Fig. 6 we plot the Hirr enhancement Δμ0Hirr = μ0Hirr,BZO−μ0Hirr,Y for different concentrations of BZO NPs. This also set the bases to determine possible H-T saturation regions and if so, the dependence with magnetic field orientation. The improvement, Δμ0Hirr, is bigger for higher BZO NP densities. We also find that ΔHirr shows similar temperature dependences for samples with +1BZO, +2BZO (not shown) and +3BZO for all orientations measured. At H||45°, Δμ0Hirr curves have a greater increase with respect to H||c for both concentrations, consistently with Fig. 5c, showing no signs of saturation up to the highest magnetic field measured.
The lack of saturation is also apparent in the inset of Fig. 6, which shows the ratio μ0Hirr,BZO/μ0Hirr,Y for the H||45° orientation for two different concentrations of BZO NPs, 1% and 3%. The enhancement factor is largest at low fields and initially decays with H, but then becomes constant up the highest accessible fields. In particular, Hirr for +3BZO is about 25% higher than for YBCO up to ~45 T.
Also observed in Fig. 6 is a steeper growth in Hirr at T > 80 K for both +1BZO and +3BZO wires. This temperature corresponds to μ0H ∼ 5 T, where the inter-vortex distance is af ∼ 22 nm, which is close to the average BZO NP spacing (dBZO ∼ 30 nm) observed in TEM images. This suggests that NPs are most effective in increasing μ0Hirr (at H||45°) when the intervortex spacing is similar the distance between NPs. This behavior is analogous to the Jc enhancement we observed as function of field for different NP densities in ref. 36.
The fact that improvements are smaller for H||c compared to H||45°, is partly due to the fact that Hirr is already higher due to the presence of correlated defects (insert Fig. 5d). After an initial increase of Hirr, Δμ0Hirr flattens around 75 K and appears to increase again for T < 60 K. The initial increase can be related to the higher density of NPs and/or of TBs, with the latter being 2.3 times more numerous in samples with BZO than in standard YBCO. However, the increase at lower temperatures is most likely related solely to the presence of nanoparticles, given the similarity of the behavior found at H||45°.
The lack of saturation in the increase of Hirr is remarkable. For +3BZO at H||45° we have achieved a 25% enhancement up to the highest fields measured, with no sign of decrease. This corresponds to an absolute increase over 9 T for μ0Hirr ~ 50 T, implying an increase of ~4–6 K in operational temperature (depending on the orientation). This enhancement is particularly significant knowing that at μ0H ∼ 60 T the inter-vortex spacing is at least 7 times smaller than the average distance between nanoparticles. These findings indicate that further improvement of Hirr in practical REBCO wires is still possible, thus pushing the technically relevant region up to even higher magnetic fields.
In summary, we find that up to the highest BZO NPs density we tested, Hirr can be increased further, with no indication of saturation up to 60 T. This allows us to report extremely high μ0Hirr, the highest values reported so far for REBCO films and wires. Our results suggest that higher densities of NPs will increase Hirr even more and that the high-field limit is far from being reached in nanoengineered REBCO wires. These results are further proof that REBCO wire is an enabling technology for several high field applications.
Methods
HTS wires based on epitaxial REBCO nanocomposite films of standard YBCO and (Y,Gd)BCO + BZO were grown from metal organic solutions including Y-, Gd- and Ba-trifluoroacetates and Cu-naphthenate with the cation ratio of 0.77 : 0.23 : 1.5 : 3 on ion-beam-assist deposited metal templates37. We added Zr-naphthenate into the (Y, Gd)BCO solutions; the content of BZO was 1–3wt% and the concentration of starting solution was 1.2 mol/L. The total thickness of the superconductive layer for all samples was 0.5 μm, which was confirmed by cross sectional transmission electron microscopy (TEM). The details of the calcinations and conversion steps have been published elsewhere17.
Films were patterned using photolithography and ion milling into bridges of ∼50 μm width. The crystalline quality was examined by x-ray diffraction (XRD). The resistivity measurements, ρ vs. H, were realized in pulsed fields up to 60 T at the Pulsed Field Facility of the National High Magnetic Field Laboratory at Los Alamos National Laboratory. The four-probe technique was applied in AC mode with a low current corresponding to 400 A/cm2 and a frequency of 100 kHz. Pulsed field measurements were performed at fixed orientations (θ) and the angular orientation was changed using a mechanical rotator. Additional ρ vs. T measurements were performed in a Quantum Design PPMS with a superconducting magnet (DC magnetic field) generating fields μ0H up to 15 T. For the transport measurements the current was always perpendicular to H. Criteria of 0.9ρn and 0.01ρn, where ρn is the normal state resistivity, were used to define Hc2 and Hirr, respectively. Both planar and cross sectional TEM images were taken to evaluate the microstructure of the film.
The microstructures and elemental concentration mappings of the films were analyzed by transmission electron microscopy (TEM) and energy-dispersive x-ray spectroscopy (EDS), respectively.
Additional Information
How to cite this article: Miura, M. et al. Upward shift of the vortex solid phase in high-temperature-superconducting wires through high density nanoparticle addition. Sci. Rep. 6, 20436; doi: 10.1038/srep20436 (2016).
References
Petrean, A. M., Paulius, L. M., Kwok, W. K., Fendrich, J. A. & Crabtree, G. W. Experimental evidence for the vortex glass phase in untwinned, proton irradiated YBa2Cu3O7−δ . Phys. Rev. Lett. 84, 5852 (2000).
Krusin-Elbaum, L., Civale, L., Thompson, J. R. & Field, C. Accommodation of vortices to columnar defects: evidence for large entropic reduction of vortex localization. Phys. Rev. B 53, 11744 (1996).
Olsson, R. J. et al. Bose glass transition in columnar-defected untwinned YBa2Cu3O7−δ . Phys. Rev. B 65, 104520 (2002).
Horii, S. et al. Vortex Bose glass in ErBa2Cu3Oy films with size-controlled nanorods. Appl. Phys. Lett. 93, 152506 (2008).
Ozaki, T. et al. Flux pinning properties and microstructure of SmBa2Cu3Oy thin films with systematically controlled BaZrO3 nanorods. J. Appl. Phys. 108, 093905 (2010).
Gutiérrez, J. et al. Strong isotropic flux pinning in solution-derived YBa2Cu3O7-x nanocomposite superconductor films. Nat. Mat. 6, 367 (2007).
Puig, T. et al. Vortex pinning in chemical solution nanostructured YBCO films. Supercond. Sci. Technol. 21, 34008 (2008).
Maiorov, B. et al. Synergetic combination of different types of defect to optimize pinning landscape using BaZrO3-doped YBa2Cu3O7 . Nat. Mat. 8, 398 (2009).
Miura, M. et al. Vortex liquid-glass transition up to 60 T in nanoengineered coated conductors grown by metal organic deposition. Appl. Phys. Lett. 96, 072506 (2010).
Miura, M. et al. Mixed pinning landscape in nanoparticle-introduced YGdBa2Cu3Oy films grown by metal organic deposition. Phys. Rev. B 83, 184519 (2011).
Palau, A., Bartolomé, E., Llordés, A., Puig, T. & Obradors, X. Isotropic and anisotropic pinning in TFA-grown YBa2Cu3O7−x films with BaZrO3 nanoparticles. Supercond. Sci. Technol. 24, 125010 (2011).
Llordés, A. et al. Nanoscale strain-induced pair suppression as a vortex-pinning mechanism in high-temperature superconductors. Nat. Mat. 11, 329 (2012).
Horide, T. et al. Jc improvement by double artificial pinning centers of BaSnO3 nanorods and Y2O3 nanoparticles in YBa2Cu3O7 coated conductors. Supercond. Sci. Technol. 26, 075019 (2013).
Rouco, V. et al. Role of twin boundaries on vortex pinning of CSD YBCO nanocomposites. Supercond. Sci. Technol. 27, 125009 (2014).
Sorbom, B. N. et al. ARC: A compact, high-field, fusion nuclear science facility and demonstration power plant with demountable magnets. Fusion Engineering and Design 100, 378–405 (2015).
Wee, S. H., Zuev, Y. L., Cantoni, C. & Goyal, A. Engineering nanocolumnar defect configurations for optimized vortex pinning in high temperature superconducting nanocomposite wires. Sci. Rep. 3, 2310 (2013).
Miura, M., Yoshizumi, M., Izumi, T. & Shiohara, Y., Formation mechanism of BaZrO3 nanoparticles in Y1−xSmxBa2Cu3Oy-coated conductors derived from trifluoroacetate metal–organic deposition. Supercond. Sci. Technol. 23, 014013 (2010).
Maiorov, B. & Osquiguil, E. Vortex solid state in YBa2Cu3O7−δ twinned crystals. Phys. Rev. B 64, 052511 (2001).
Shlyk, L. et al. Engineering periodic arrays of nanoscale twin boundaries in bulk YBa2Cu3O7−δ with RuO2 additions. Appl. Phys. Lett. 88, 062509 (2006).
Civale, L. & Krusin-Elbaum, L. Comment on “Upper Limit of the Bose-Glass Transition in YBa2Cu3O7 at High Density of Columnar Defects” Phys. Rev. Lett. 78, 1829 (1997).
Blatter, G., Feigel’man, M. V., Geshkenbein, V. B., Larkin, A. I. & Vinokur, V. M. Vortices in high-temperature superconductors. Rev. Mod. Phys. 66, 1125 (1994).
Holesinger, T., Maiorov, B. & Civale, L. Strategic materials development for enhanced coated conductor performance. Presented at 2010 Annual Peer Review for Advanced Cable and Conductors, Alexandria VA, USA, June 29-July 1, 2010, Available at: http://www.htspeerreview.com/pdfs/presentations/day%203/strategic-research/10_SR_StrategicMaterialsDevelopment_for_CoatedConductorPerformance.pdf (Accessed: 4 December 2015).
Maiorov, B., G. Nieva, G. & Osquiguil, E. First-order phase transition of the vortex lattice in twinned YBa2Cu3O7 single crystals in tilted magnetic fields, Phys. Rev. B 61, 12427–12432 (2000).
Kwok,W. K. et al. Vortex lattice melting in untwinned and twinned single crystals of YBa2Cu3O7−δ, Phys. Rev. Lett. 69, 3370 (1992).
Civale, L. et al. Angular-dependent vortex pinning mechanisms in YBa2Cu3O7 coated conductors and thin films, Appl. Phys. Lett. 84, 2121 (2004).
Maiorov, B. et al. Vortex pinning landscape in YBa2Cu3O7 films grown by hybrid liquid phase epitaxy. Supercond. Sci. Technol. 20, S223 (2007).
Koshelev, A. E. & Kolton, A. B. Theory and simulations on strong pinning of vortex lines by nanoparticles. Phys. Rev. B 84, 104528 (2011).
van der Beek, C. J., Konczykowski, M. & Prozorov, R. Anisotropy of strong pinning in multi-band superconductors. Supercond. Sci. Technol. 25 084010 (2012).
Mishev, V. et al. Interaction of vortices in anisotropic superconductors with isotropic defects. Supercond. Sci. Technol. 28, 102001(2015).
Chen, Z. et al. Three-dimensional vortex pinning by nano-precipitates in a Sm-doped YBa2Cu3O7−x coated conductor. Supercond. Sci. Technol. 20, S205 (2007).
Tarantini, C. et al. Anisotropy of the irreversibility field for Zr-doped (Y,Gd)Ba2Cu3O7−x thin films up to 45 T. Phys. Rev. B 84, 224514 (2011).
Rosenzweig, St. et al. Irreversibility field up to 42 T of GdBa2Cu3O7-δ thin films grown by PLD and its dependence on deposition parameters. Supercond. Sci. Technol. 23, 105017 (2010).
Selvamanickam, V. et al. High critical currents in heavily doped (Gd,Y)Ba2Cu3Ox superconductor tapes. Appl. Phys. Lett. 106, 032601 (2015).
Xu, A. et al. Strongly enhanced vortex pinning from 4 to 77 K in magnetic fields up to 31 T in 15 mol.% Zr-added (Gd,Y)-Ba-Cu-O superconducting tapes. APL Mater. 2, 046111 (2014).
Awaji, S. et al. High-performance irreversibility field and flux pinning force density in BaHfO3-doped GdBa2Cu3Oy tape prepared by pulsed laser deposition. Appl. Phys. Express 8, 023101 (2015).
Miura, M. et al. Strongly enhanced flux pinning in one-step deposition of BaFe2(As0.66P0.33)2 superconductor films with uniformly dispersed BaZrO3 nanoparticles. Nat. Commun. 4, 2499 (2013).
Yamada, Y. et al. Development of Long Length IBAD-MgO and PLD Coated Conductors. IEEE Trans. Appl. Supercond. 19 3236 (2009).
Acknowledgements
Work by B.M. and L.C. was supported by the U.S. DOE, Office of Science, BES, Materials Sciences and Engineering Division. Work by M.M. at LANL was supported by the LANL LDRD program and at Seikei Univ. by JSPS KAKENHI (26709076). Work by F.F.B. was supported by NSF Cooperative Agreement No. DMR-1157490 and the State of Florida. A part of the work at ISTEC-SRL was supported by METI and NEDO as a Collaborative Research. M.M. would like to thank Jeffrey O. Willis for helpful discussions and a critical reading of the manuscript.
Author information
Authors and Affiliations
Contributions
M.M. grew the films, carried out the experimental design, performed the superconducting property measurements and prepared the manuscript. B.M. carried out superconducting property measurements, data analysis, provided advice and consultation on flux pinning and assisted in preparing the manuscript and coordinated the research. F.F.B. carried out superconducting properties measurement. T.K. carried out microstructural studies. M.S. carried out superconducting property measurements. Y.T. carried out photolithography preparations. T.I. provided advice and consultation on film preparation. L.C. contributed to discussion and manuscript preparation. All authors discussed the results and implications and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Miura, M., Maiorov, B., Balakirev, F. et al. Upward shift of the vortex solid phase in high-temperature-superconducting wires through high density nanoparticle addition. Sci Rep 6, 20436 (2016). https://doi.org/10.1038/srep20436
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep20436
This article is cited by
-
Impact of high growth rates on the microstructure and vortex pinning of high-temperature superconducting coated conductors
Nature Reviews Physics (2023)
-
Features of Magnetization and Vortex System of Magnesium Diboride
Journal of Superconductivity and Novel Magnetism (2023)
-
Thermodynamic approach for enhancing superconducting critical current performance
NPG Asia Materials (2022)
-
Accelerated vortex dynamics across the magnetic 3D-to-2D crossover in disordered superconductors
npj Quantum Materials (2018)
-
Tuning nanoparticle size for enhanced functionality in perovskite thin films deposited by metal organic deposition
NPG Asia Materials (2017)