Abstract
The unusual physical properties and formation conditions attributed to h-, i-, m- and n-nanodiamond polymorphs has resulted in their receiving much attention in the materials and planetary science literature. Their identification is based on diffraction features that are absent in ordinary cubic (c-) diamond (space group: Fd-3m). We show, using ultra-high-resolution transmission electron microscope (HRTEM) images of natural and synthetic nanodiamonds, that the diffraction features attributed to the reported polymorphs are consistent with c-diamond containing abundant defects. Combinations of {113} reflection and <011> rotation twins produce HRTEM images and d-spacings that match those attributed to h-, i- and m-diamond. The diagnostic features of n-diamond in TEM images can arise from thickness effects of c-diamonds. Our data and interpretations strongly suggest that the reported nanodiamond polymorphs are in fact twinned c-diamond. We also report a new type of twin (<11> rotational), which can give rise to grains with dodecagonal symmetry. Our results show that twins are widespread in diamond nanocrystals. A high density of twins could strongly influence their applications.
Similar content being viewed by others
Introduction
Interest in diamond nanocrystals stems from applications that range from materials to medical sciences1,2,3,4,5. These nanocrystals possess high hardness and wear resistance, are chemically inert and are promising for drug delivery. Wide band gap, optical transparency and unusually high thermal conductivity make them attractive materials for preparing semiconductors4 and electron-field emitters2. Fluorescent nanodiamonds have been used as non-toxic alternatives to semiconductor quantum dots for biomedical imaging5. Biocompatibility and resistivity enable use of nanodiamonds for coatings on medical implants6. The broad spectrum of possible functional chemical groups, biocompatibility, small sizes and homogeneous size distributions offer extensive possibilities for using them in nanofabrication, bioconjugation and drug delivery3,7.
Literature reports indicate that many diamond nanocrystals are structurally inhomogeneous, consisting of ordinary cubic (c-) diamond (space group: Fd-3m), plus several poorly characterized sp3-bonded forms, variously called polymorphs, allotropes, or polytypes8,9,10,11,12,13,14,15,16,17,18. For uniformity, we call these polymorphs. They are of interest to materials scientists because they are thought to possess exceptional physical properties. For example, h-diamond (aka lonsdaleite), whose existence as a distinct material was recently questioned19, has received attention because it is thought to possess superior compressive strength, hardness and rigidity, compared to c-diamond20,21. The i-diamond polymorph has been proposed to be a super-dense form, with a calculated density of 4.1 g/cm3, which is 15% greater than that of c-diamond22. m-diamond was attributed to a material that could possess extreme hardness23. Wen et al.24 suggested that, in distinction to c-diamond, n-diamond absorbs electromagnetic radiation and thus could eliminate electromagnetic interference caused by wireless communication tools.
Nanodiamonds of extraterrestrial origin are abundant in some meteorites25,26,27 and have been reported from impact-related horizons in sedimentary rocks such as the K/Pg boundary28. Meteoritic nanodiamonds also have the potential to provide insights into early Solar System formation conditions26. Of particular interest are reports of a world-wide nanodiamond-rich layer associated with the onset of the Younger Dryas (YD) cooling episode at ~12,800 before present29,30,31,32,33. These nanodiamonds are postulated to have formed from terrestrial carbon during an extraterrestrial impact, producing c-, h-, i- and n-diamonds33. According to this scenario, the catastrophic event had serious consequences on the climate and brought about the extinctions of most Pleistocene megafauna including Mammoths29,30,31,32,33. However, questions have been raised about the temporal association of nanodiamonds with the YD34,35, the occurrence of diamond polymorphs in these sediments34,36,37,38 and even evidence for impact signatures during the YD39. Although controversial, YD reports commonly use the presence of nanodiamond polymorphs as the impact signature.
The proposed polymorphs could be attractive for a range of applications and as proxies of major terrestrial impacts, but they have not been synthesized in pure form and have only been reported as mixtures of different carbonaceous phases such as graphite and amorphous carbon. As such, the structures and characteristics of the reported polymorphs are either controversial or not diagnostic (Table 1). In particular, the existence of h-diamond was recently questioned19 and several structural and chemical models were proposed for i-, m- and n-diamond, including substitution of carbon by hydrogen9,13,40 and incompletely described diamond forms41. Recently, Li et al.42 suggested a structure model for n-diamond consisting of layers of h-diamond and C3 isosceles triangle rings. In any case, there is no consensus on the structure or synthesis conditions of the polymorphs.
Transmission electron microscopy (TEM) is uniquely suited for the structural and chemical investigation of individual nanosized particles. Diamond polymorphs have been reported from high-resolution transmission electron microscope (HRTEM) images and selected-area electron diffraction patterns based on features absent from c-diamond. However, these features are not unique for the presumed polymorphs (Supplementary Note 1, Supplementary Figs 1-2). We show that natural and synthetic c-nanodiamonds commonly consist of sub-nanometer twin domains, which give rise to the characteristic features attributed to the proposed diamond polymorphs.
Results
Nano-sized twins in c-diamond
In order to investigate the diamond-polymorph issue, we selected several synthetic and natural samples for study. The synthetic samples were produced through chemical vapor deposition (CVD) and the natural ones were obtained from primitive (Murchison and Orgueil) and impact-shocked (Gujba) meteorites42. Samples of similar origins reportedly contain various diamond polymorphs9,10,11,12,13,16,25,27.
HRTEM images of these nanodiamonds reveal fringes with 0.206-, 0.126- and 0.108-nm spacings, corresponding to c-diamond {111}, {202} and {113} planes, respectively (Figs 1 and 2). All investigated grains show one or more of these sets of fringes and the C K-edge EELS spectral shapes from these crystals are consistent with c-diamond (Supplementary Fig. 2a). Twinning is characteristic of the nanocrystals (Figs 1, 2, 3, 4, 5), which commonly display both reflection and rotation twins. The most abundant types are the {111} reflection twins (Fig. 1a,b), also called ∑3 twins, which are consistent with previous studies25,44,45. These twins can give rise to the common <011> rotation twins25,45, in which the domains are rotated ∼71º with respect to each other around <011> (Fig. 1b). We report a new type of rotation twins (<11> twins) (Fig. 2), which divide the grains into sub-nanometer domains, similar to the <011> rotation twins. The symmetry of these domains matches that of c-diamond. However, as a result of rotational twinning, the HRTEM images exhibit new non-crystallographic symmetry elements. For example, the grains in Figs 1b and 2a have pentagonal and dodecagonal symmetries. Pentagonal and decagonal symmetries are common in gold nanoparticles46,47 and five-fold twins occur in nanodiamonds25,45,48. The nanodiamond grain with dodecagonal symmetry (Fig. 2), in which the domains are rotated 30° to each other, is a new example of non-crystallographic symmetry in nanoparticles.
Grains exhibiting hexagonal- and square-fringe patterns having 0.206-nm spacings corresponding to c-diamond {111} planes (Figs 3, 4, 5) are prominent in each sample. The fast Fourier transforms (FFTs) calculated from these patterns show c-diamond diffraction spots that are related through two types of twins. The diffraction spots calculated from the hexagonal-fringe pattern (Fig. 3d) can be interpreted as arising from {113} reflection twins. This type of twin is especially abundant in the shock-formed Canyon Diablo diamond and in synthetic samples prepared under conditions in which lonsdaleite was reported19. The FFTs calculated from the square-fringe pattern exhibit rows of perpendicular diffraction spots with 0.206-nm spacings corresponding to c-diamond {111} planes and additional diffraction spots with the same spacings (Figs 4, 5a). This diffraction-spot arrangement is consistent with <011> rotation twins, in which the twin domains are rotated 90° with respect to each other around <011>. In order to clarify details of this twin type, we modeled its structure (Fig. 4b) and generated amplitude images from the {111} diamond diffraction spots (Fig. 5b,c). The intensity maxima of these images occur where the selected sets of fringes occur. They show the {111} lattice fringes occur in different regions and do not overlap completely (Fig. 5b,c), as is characteristic of twin domains. Thus, although the hexagonal and square-fringe patterns exhibit symmetries not expected for c-diamond, twinned c-diamond provides an explanation.
Explanation for the diffraction features of the polymorphs
The twinned nanodiamonds described above display HRTEM images and spacings that match those used to recognize the reported diamond polymorphs. For example, nanosized grains of h-diamond have been identified from HRTEM images with hexagonal and square fringe-patterns25,27,29,30,31,32,33 showing 0.21-nm spacings. However, simulations of HRTEM images at different experimental conditions suggest the observed patterns are incompatible with this interpretation (Supplementary Fig. 3). The reported hexagonal and square-fringe patterns match those of Figs 3, 4, 5, i.e., they are consistent with the {113} twins and <011> rotation twins mentioned above. As such, the structural features attributed to h-diamond can be explained by twinned c-diamond. The case for i-diamond is more problematic as there is no consensus regarding its structure and reports of its unit-cell dimension range between 0.250 and 0.428 nm, with primitive or i-centered symmetry (Table 1). Assuming the most commonly reported9,18,22 unit-cell parameter of 0.428 nm and i-centering with an a glide22, the HRTEM image of i-diamond matches the square fringe-pattern having 0.21-nm spacings. However, our analysis shows this pattern is consistent with <011> rotation twins of c-diamond. The proposed m-diamond, which was recently reported from HRTEM images and corresponding FFTs based on a 0.63-nm d-spacing23, can be explained by {111} c-diamond twins (Supplementary Fig. 4). These twins in thick crystals (electron is scattered more than 1) can give rise to the spacings and diffraction spots attributed to m-diamond. Therefore, the diffraction patterns and HRTEM images used to identify h-, i- and m-diamond are compatible with twinned c-diamond.
The issue of n-diamond is ambiguous because its diagnostic d-spacings are not unique (Supplementary Fig. 1). For example, it is commonly identified using the 0.178-nm spacing (assigned as the 200 diffraction spots) from HRTEM images and their corresponding FFTs10,11,12,13,17,30,31,32,33. However, diffraction from dynamically scattered electrons for c-diamond yields the same spacing. Images show the intensity of the 200 diffraction spot, which violates the crystallographic selection rules for Fd-3m symmetry, arises with increasing sample thickness even in nanosized crystals (Supplementary Fig. 5). Identification from SAED ring patterns is similarly nondiagnostic because they are from areas large enough (>20-nm wide) to include grains of other nanomaterials. For example, graphite, whose d-spacings closely match those of n-diamond, is a common byproduct of synthesis and also occurs in natural samples together with c-diamond nanocrystals.
Conclusions
The literature contains numerous reports of diamond polymorphs, including h-, i-, m- and n- diamond8,9,10,11,12,13,14,15,16,17,18,23,25,27,28,29,30,31,32,33,35,49. However our ultra-high-resolution TEM data show that nanodiamonds are intimately twinned and these defects give rise to the image and diffraction features used to identify h-, i-, m- and n- diamond. This interpretation calls for reevaluation of previous reports and leads to a rethinking of materials and planetary science implications based on these polymorphs. For example, the reported exceptional material properties10,18,19,20,23 attributed to these polymorphs need to be reexamined. Furthermore, since nanosized diamond polymorphs reported in28,29,30,31,32,33 are not necessarily a marker for cosmic impact and therefore inappropriate for inferring the YD impact origin, the question of that origin is worth reconsidering as also proposed in34,36,37,38,39.
Twinning is common in c-diamond nanocrystals, produces grains with intricate patterns of structure fringes in HRTEM images and results in nanometer to sub-nanometer domains. Of the samples we studied, the twin domains are largest (>5 nm wide) in the Gujba meteorite, in which the crystals are also large (>10 nm wide) and which were reported to form as a result of shock metamorphism43. In contrast, the small twin domains (<1 nm wide) of Murchison and Orgueil are comparable in size to those of the CVD-produced diamond. Our findings imply that defective structure is favored for 1- to 5-nm diamond crystals, many of which contain abundant twin boundaries. These boundaries affect the mechanical, electronic and optical properties of c-nanodiamonds and promote the implantation of foreign elements (dopants), which are used to prepare semiconductors, electron-field emitters and quantum dots2,4,5.
Methods
Materials and Methods
Small droplets (ca. 2 ml) of Gujba, Murchison and Orgueil nanodiamond residues in suspension with water were dried on Cu grids coated with lacy-C. We also prepared TEM samples from (1) synthetic material provided by Andriy Sherehiy and Mahendra Sunkara (University of Louisville), grown in a chamber that was inadvertently contaminated with Cu; and (2) CVD-produced nanodiamonds provided by Robert Nemanich (Arizona State University). TEM data were acquired from electron-transparent areas of the residues protruding into the holes of the carbon-support film. HRTEM and bright-field STEM images were acquired with a JEOL 4000EX TEM (400 keV, 0.17-nm point resolution) and a JEOL ARM200F aberration-corrected scanning TEM (200 keV, 0.08-nm point resolution), respectively.
FFTs obtained from the HRTEM images were calculated using Gatan Digital Micrograph (DM) 3.5 software. The amplitude images of Fig. 5 were generated following the method described in50,51, using routines written for DM software and applying 0.2 nm−1 Lorentzian masks for the {−111} set of diamond diffraction spots. We performed this analysis on the Gujba sample, where the domains were sufficiently large (>5 nm wide). We set the upper and lower contrast limits to the same values for both images.
Additional Information
How to cite this article: Németh, P. et al. Twinning of cubic diamond explains reported nanodiamond polymorphs. Sci. Rep. 5, 18381; doi: 10.1038/srep18381 (2015).
References
Krueger, A. Beyond the shine: recent progress in applications of nanodiamond. J. Mater. Chem. 21(34), 12571–12578 (2011).
Zhirnov, V. V. et al. Electron emission properties of detonation nanodiamonds. Phys. Solid State 46(4), 657–661 (2004).
Mochalin, V. N., Shenderova, O., Ho, D. & Gogotsi, Y. The properties and applications of nanodiamonds. Nat. Nanotechnol. 7(1), 11–23 (2012).
Collins, A. T. The optical and electronic-properties of semiconducting diamond. Philos. Trans. A Math Phys. Eng. Sci. 342(1664), 233–244 (1993).
Mochalin, V. N. & Gogotsi, Y. Wet chemistry route to hydrophobic blue fluorescent nanodiamond. J. Am. Chem. Soc. 131, 4594–4595 (2009).
Mitura, S., Mitura, K., Niedzielski, P., Louda, P. & Danilenko, V. Nanocrystalline diamond, its synthesis, properties and applications. JAMME 16, 9–16 (2006).
Schrand, A. M., Hens, S. A. C. & Shenderova, O. A. Nanodiamond particles: properties and perspectives for bioapplications. Crit. Rev. Solid State Mater. Sci. 34, 18–74 (2009).
Bhargava, S., Bist, H. D., Sahli, S., Aslam, M. & Tripathi, H. B. Diamond polytypes in the chemical-vapor-deposited diamond films. Appl. Phys. Lett. 67(12), 1706–1708 (1995).
Cowley, J. M., Mani, R. C., Sunkara, M. K., O’Keefe, M. & Bonneau, C. Structures of carbon nanocrystals. Chem. Mater. 16, 4905–4911 (2004).
Wen, B., Zhao, J. J. & Li, T. J. Synthesis and crystal structure of n-diamond. Int. Mat. Rev. 52, 131–151 (2007).
Bucknum, M. J. & Castro, E. A. On the n-diamond and i-carbon nanocrystalline forms. J. Math. Chem. 50, 1034–1038 (2012).
Peng, J. L., Orwa, J. O., Jiang, B., Prawer, S. & Bursill, L. A. Nano-crystals of c-diamond, n-diamond and i-carbon grown in carbon-ion implanted fused quartz. Int. J. Mod. Phys. B 15, 3107–3123 (2001).
Konyashin, I. et al. A new hard allotropic form of carbon: Dream or reality? Int. J. Refract. Metals. Hard. Mater. 24, 17–23 (2006).
Santiago, P., Camacho-Bragado, G. A., Martin-Almazo, M., Murgich, M. & José-Yacaman, J. Diamond polytypes in Mexican crude oil. Energy Fuels 18, 390–395 (2004).
Yang, Z. Q. et al. TEM and Raman characterization of diamond micro- and nanostructures in carbon spherules from upper soils. Diam. Relat. Mater. 17, 937–943 (2008).
Liu, P., Cui, H. & Yang, G. W. Synthesis of body-centered cubic carbon nanocrystals. Cryst. Growth Des. 8, 581–586 (2008).
Kumar, A. et al. Formation of nanodiamonds at near-ambient conditions via microplasma dissociation of ethanol vapour. Nat. Commun. doi: 10.1038/ncomms3618 (2013).
Matyushenko, N. N., Strelnitskii, V. E. & Gusev, V. A. A dense new version of crystalline carbon C-8. Sov. Phys. Cryst. 26, 274–277 (1981).
Németh, P. et al. Lonsdaleite is faulted and twinned cubic diamond and does not exist as a discrete material. Nat. Commun. 5, 5447 doi: 10.1038/ncomms6447 (2014).
Pan, Z., Sun, H., Zhang, Y. & Chen, C. Harder than diamond: Superior indentation strength of wurtzite BN and lonsdaleite. Phys. Rev. Lett. 102, 055503 (1–4) (2009).
Quingkun, L., Yi, S., Zhiyuan, L. & Yu, Z. Lonsdaleite – a material stronger and stiffer than diamond. Scripta Mater. 65, 229–232 (2011).
Johnston, R. L. & Hoffmann, R. Superdense carbon, C-8 - Supercubane or analog of gamma -Si. J. Am. Chem. Soc. 111(3), 810–819 (1989).
Huang, Q. et al. Nanotwinned diamond with unprecedented hardness and stability. Nature 510, 250–253 (2014).
Wen, B., Zhao, J. J. & Li, T. J. Synthesis and crystal structure of n-diamond. Int. Mater. Rev. 52, 131–151 (2007).
Daulton, T. L., Eisenhour, D. D., Bernatowicz, T. J., Lewis, R. S. & Buseck, P. R. Genesis of presolar diamonds: comparative high-resolution transmission electron microscopy study of meteoritic and terrestrial nano-diamonds. Geochim. Cosmochim. Acta 60, 4853–4872 (1996).
Huss, G. R. Meteoritic nanodiamonds: Messengers from the stars. Elements 1(2), 97–100 (2005).
Garvie, L. A. J. Surface electronic structure of meteoritic nanodiamonds. Meteorit. Planet. Sci. 41(5), 667–672 (2006).
Hough, R. M., Gilmour, I., Pillinger, C. T., Langenhorst, F. & Montanari, A. Diamonds from the iridium-rich K-T boundary layer at Arroyo el Mimbral, Tamaulipas, Mexico. Geology 25(11), 1019–1022 (1997).
Kennett, D. J. et al. Nanodiamonds in the Younger Dryas boundary sediment layer. Science 323(5910), 94–94 (2009a).
Kennett, D. J. et al. Shock-synthesized hexagonal diamonds in Younger Dryas boundary sediments. Proc. Natl. Acad. Sci. USA 106(31), 12623–12628 (2009b).
Kurbatov, A. V. et al. Discovery of a nanodiamond-rich layer in the Greenland ice sheet. J. Glaciol. 56(199), 747–757 (2010).
Israde-Alcantara, I. et al. Evidence from central Mexico supporting the Younger Dryas extraterrestrial impact hypothesis. Proc. Natl. Acad. Sci. USA 109(13), E738–E747 (2012).
Kinzie, C. R. et al. Nanodiamond-Rich Layer across Three Continents Consistent with Major Cosmic Impact at 12,800 Cal BP. J. Geol. 122(5), 475–505 (2014).
van Hoesel, A. et al. Nanodiamonds and wildfire evidence in the Usselo horizon postdate the Allerød-Younger Dryas boundary. Proc. Natl. Acad. Sci. USA 109(20), 7648–7653 (2012).
Bement, L. C. et al. Quantifying the distribution in the pre-Younger Dryas to recent age deposits along Bull Creek, Oklahoma Panhandle, USA. Proc. Natl. Acad. Sci. USA 111(5), 1726–1731 (2014).
Daulton, T. L., Pinter, N. & Scott, A. C. No evidence of nanodiamonds in Younger-Dryas sediments to support an impact event. Proc. Natl. Acad. Sci. USA 107(37), 16043–16047 (2010).
Tian, H., Schryvers, D. & Claeys, P. Nanodiamonds do not provide unique evidence for a Younger Dryas impact. Proc. Natl. Acad. Sci. USA 108(1), 40–44 (2011).
Daulton, T. L. Suspect cubic diamond “impact” proxy and a suspect lonsdaleite identification. Proc. Natl. Acad. Sci. USA 109(34), 2242 (2012).
Pinter, N. et al. The Younger Dryas impact hypothesis: A requiem. Earth Sci. Rev. 106(3–4), 247–264 (2011).
Wen, B., Melnik, R., Yao, S. & Li, T. Hydrogen doped cubic diamond and the crystal structure of n-diamond. Chem. Phys. Lett. 516, 230–232 (2011).
Hu, M. et al. Exotic cubic carbon allotropes. J. Phys. Chem. C 116, 24 233–24 238 (2012).
Li, D. et al. Ab initio structure determination of n-diamond. Sci. Rep. 5, 13447 doi: 10.1038/srep13447 (2015).
Weisberg, M. K. & Kimura, M. Petrology and Raman spectroscopy of high pressure phases in the Gujba CB chondrite and the shock history of the CB parent body. Meteorit. Planet. Sci. 45(5), 873–884 (2010).
Buseck, P. R. & Barry, J. C. Twinned diamonds in the Orgueil carbonaceous chondrite. Meteoritics 23, 261–262 (1998).
Butler, J. E. & Oleynik, I. A mechanism for crystal twinning in the growth of diamond by chemical vapour deposition. Phil. Trans. R. Soc. A. 366, 295–311 (2008).
Sánchez-Iglesias, A. et al. Synthesis and optical properties of gold nanodecahedra with size control. Adv. Mater. 18, 2529–2534 (2006).
Johnson, C. L. et al. Effects of elastic anisotropy on strain distributions in decahedral gold nanoparticles. Nat. Mater. 7, 120–124 (2007).
Shechtman, D. Twin quintuplet surfaces in CVD diamond. J. Mater. Sci. 41, 7720–7724 (2006).
Hirai, H. & Kondo, K. I. Modified phases of diamond formed under shock compression and rapid quenching. Science 253(5021), 772–774 (1991).
Hÿtch, M. J. & Potez, L. Geometric phase analysis of high-resolution electron microscopy images of antiphase domains: example Cu3Au. Philos. Mag. A 76, 1119–1138 (1997).
Hÿtch, M. J., Snoeck, E. & Kilaas, R. Quantitative measurement of displacement and strain fields from HREM micrographs. Ultramicroscopy 74, 131–146 (1998).
Bundy, F. P. & Casper, J. S. (1967) Hexagonal diamond - A new form of carbon. J. Chem. Phys. 46, 3437 3446
Hirai, H. & Kondo, K. I. (1991) Possible structural models of n-diamond: A modified form of diamond. Appl. Phys. Lett. 61, 414 416.
Vora, H. & Moravec, T. J. (1981) Structural investigation of thin films of diamond-like carbon. Appl. Phys. Lett. 52, 6151 6157.
Acknowledgements
We thank Gary Huss for the Murchison and Orgueil nanodiamond residues and Andriy Sherehiy, Mahendra Sunkara and Robert Nemanich for the synthetic material. We acknowledge use of the facilities in the John M. Cowley Center for High Resolution Electron Microscopy at Arizona State University and thank John Mardinly and Toshihiro Aoki for helping obtain the STEM images, István Dódony for helpful discussions and Csilla Molnár for helping prepare the structure models of the 30° and 90° twins. P.N. acknowledges support from the János Bolyai Research Scholarship. L.A.J.G. and P.R.B. were supported by NASA Origins of Solar Systems grant NNX11AK58G.
Author information
Authors and Affiliations
Contributions
P.N., L.A.J.G. and P.R.B. conceived the project and P.N. took the lead on data analysis and manuscript writing. All authors contributed to interpreting the data and writing of the paper.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Németh, P., Garvie, L. & Buseck, P. Twinning of cubic diamond explains reported nanodiamond polymorphs. Sci Rep 5, 18381 (2016). https://doi.org/10.1038/srep18381
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep18381
This article is cited by
-
Complex nanostructures in diamond
Nature Materials (2020)
-
Quantifying hexagonal stacking in diamond
Scientific Reports (2019)
-
An Affordable Wet Chemical Route to Grow Conducting Hybrid Graphite-Diamond Nanowires: Demonstration by A Single Nanowire Device
Scientific Reports (2017)
-
Structural and morphological peculiarities of hybrid Au/nanodiamond engineered nanostructures
Scientific Reports (2016)