Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

# Synthesis of Large Area Graphene for High Performance in Flexible Optoelectronic Devices

## Abstract

This work demonstrates an attractive low-cost route to obtain large area and high-quality graphene films by using the ultra-smooth copper foils which are typically used as the negative electrodes in lithium-ion batteries. We first compared the electronic transport properties of our new graphene film with the one synthesized by using commonly used standard copper foils in chemical vapor deposition (CVD). We observed a stark improvement in the electrical performance of the transistors realized on our graphene films. To study the optical properties on large area, we transferred CVD based graphene to transparent flexible substrates using hot lamination method and performed large area optical scanning. We demonstrate the promise of our high quality graphene films for large areas with ~400 cm2 flexible optical modulators. We obtained a profound light modulation over a broad spectrum by using the fabricated large area transparent graphene supercapacitors and we compared the performance of our devices with the one based on graphene from standard copper. We propose that the copper foils used in the lithium-ion batteries could be used to obtain high-quality graphene at much lower-cost, with the improved performance of electrical transport and optical properties in the devices made from them.

## Introduction

Carbon based nanomaterials have provided a new perspective in electronics owing to their very high charge carrier mobility and nanoscale dimensions. In particular, the carbon nanotubes1 and graphene2 have been shown to have promising performances suitable for high frequency electronics, which will be needed in emerging applications such as smart cities and mobile health. It is essential to have high quality material for high-performance and scaling up of electronics on large areas. In this regard, the wafer scale synthesis of aligned arrays of single-walled carbon nanotubes on quartz3 and sapphire crystals4 are worth noting. As a two-dimensional crystal of carbon atoms, graphene is a basic building block of many carbon allotropes such as zero dimensional fullerene, one dimensional carbon nanotube and three dimensional graphite5. Since first observation of strong ambipolar electric field effect in the graphitic films6 by Andre Geim and Kostya Novoselov, there has been a tremendous effort from scientists to explore and enhance the electronic properties of graphene. These include ground-breaking discoveries such as experimental observation of the half integer quantum hall effect7,8, constant minimum conductivity in vicinity of charge carriers9, ballistic transport at room temperature5 and Klein paradox10. Graphene is also a viable material for optoelectronics because of its broad optical response and gate-tunable optical properties11. One can control the absorption of graphene via electrostatic doping12. The current focus of graphene research is to obtain high quality graphene over large areas to realize electronic and optic applications with advanced mechanical functionalities such as flexible transparent electrodes13 or large area touch sensor devices14.

Graphene layers can be isolated chemically from bulk graphite with intercalation of atoms or molecules through the graphite15, yielding the separation of graphene layers. However, partial separation of the bulk graphite results in a dispersion that contains variety of graphene fragments and graphitic films16. To overcome this non-uniformity of the resulting graphene layers, chemical reduction of graphene oxide17 and chemically functionalized graphene18 were introduced. As a common drawback, these materials suffer from low conductivity, therefore, it is challenging to achieve large area graphene from them with state of the art transport properties. A promising scalable route is the chemical vapour deposition (CVD) of graphene on copper (Cu) foils19. Cu is preferred in CVD of graphene because of low solubility limit of carbon in Cu, which makes graphene growth procedure self-limited19. This property of Cu provides a straightforward method to synthesize single layer graphene. The large area synthesis of graphene by using Cu in CVD has been investigated since 200920,21 and many breakthrough improvements on the quality of graphene films have been reported since then13,19,22.

The surface quality of the Cu foils and the transfer process greatly influence the performance and reliability of graphene based devices. Previous works have showed that the morphology of the Cu surface is one of the key parameters to have better quality graphene films23. To achieve the continuous and high quality graphene film over large area; impurities, defects, grain boundaries and other surface features that can serve as a nucleation seed should be carefully engineered23. To that end, variety of techniques to smoothen the Cu surfaces have been reported. For example, Luo et al.24 used standard electro-polishing technique to smoothen the Cu surfaces. Their Raman investigation implied better quality graphene with higher surface coverage compared to the unpolished Cu samples24. Similar electrochemical polishing technique was used in the work by Yan. et al.25. Together with the high pressure annealing, they produced hexagonal single crystal graphene domains nearly 2 mm in size25. Alternatively, melted Cu surfaces were also used to form single crystal hexagonal graphene flakes in previous works26,27. It has been known that the quality of the Cu surface directly effects the charge carrier transport properties of the resulting graphene layer28. Orofeo et al.28 demonstrated the hole mobility of the graphene grown on the hetero-epitaxial Cu film is nearly 10 times greater than that of the graphene grown on the standard Cu foil by chemical vapor deposition. Above technologies including Cu polishing and deposition techniques add extra cost and time consuming chemical process steps which are not effective in the case of large area synthesis of graphene.

In this paper, we demonstrate that the commercially available ultra-smooth Cu foils (which are generally used in Lithium-ion batteries) can help to open new avenues for large area device applications with the improved quality of the graphene films. We studied the synthesis of graphene on commercially available smooth Cu foils and we provided a detailed comparison between the graphene synthesized on ultra-smooth Cu foils and the one synthesized on the standard Cu foils in terms of structural, electrical and optical properties. We observed a stark improvement in the electrical performance of the transistors realized on our graphene films. Then, to demonstrate the advantage of high quality graphene films from ultra-smooth Cu foils, we fabricated 400 cm2 flexible graphene electrodes and enlarged 160 times the previously reported (2.5 cm2) supercapacitor structure29. To show the promises of our graphene films in electro-optic devices, we tested and compared the effects of graphene quality in large area supercapacitors. We anticipate that usage of commercially available ultra-smooth Cu foils for large area graphene growth would lead to higher performance devices especially for optical and electronic applications where low device variations are desired.

## Results

We start with the demonstration of the high quality single layer graphene synthesis on commercially available ultra-smooth Cu foils. In order to compare the surface quality, we used relatively rough Alfa Aesar Cu foil which is commonly used for CVD of graphene (Fig. 1(a–c)) and commercially available ultra-smooth surface Cu foils (Mitsui mining and smelting co., LTD, B1-SBS) (Fig. 1(d–f)) in the same CVD chamber. Deep trenches on the surface of rough copper foils are clearly seen in both optical microscope (Fig. 1(a)) and scanning electron microscope images. (Fig. 1(b,c)). On the other hand, commercially available smooth copper foils show uniform surface properties (Fig. 1(d–f)). We investigated the surface topography of the ultra-smooth Cu foils via scanning electron microscopy (SEM) and atomic force microscopy (AFM). The root mean square (RMS) surface roughness of the ultra-smooth Cu is around 100 nm before annealing which is two times lower than the value reported for the Cu foils commonly used in graphene growth30.

By sending the methane gas into the chamber with different intervals, we obtain both the graphene flakes (Fig. 2(a,b)) and full coverage graphene film (Fig. 2(c)) on the ultra-smooth Cu foils. Figure 2(a) shows the SEM image of Cu surface partially covered by graphene flakes. The average size of the flakes are ~1100 μm2 in the form of a snow-flake (Fig. 2(b)). Also we observed that the flake size and shape are directly related to the ratio of flow rate and partial pressure of hydrogen to methane gases, as reported in previous work31.

As a next step, the partial pressure and flow of the gases were set to have full coverage single layer graphene on both the ultra-smooth Cu foils and rough copper foils. We followed the similar growth conditions as in ref. 22. According to our observations, the formation of continuous graphene layer is initiated with single crystal graphene flakes. Increasing the growth time, under the same methane flow rate and partial pressure, results in the formation of continuous graphene layer. Moreover, the synthesized graphene flakes and continuous graphene layers includes ripples (Fig. 2(c)) because of the physical instability of perfectly flat graphene layer32,33,34,35.

To investigate the effect of the surface roughness on the quality of the graphene layer, both the ultra-smooth Cu and the rough Cu foils were placed in the same growth chamber so as to expose them to the same growth conditions. Once the graphene layers were formed on the both the smooth and the rough Cu surfaces, we transferred them to 100-nm-thick SiO2 coated Si wafers for structural characterization and transistor applications. (Supplementary Fig. S1)

From now on, we will denote the graphene synthesized on commercially available ultra-smooth Cu foils as “smooth-Cu-graphene” and the graphene synthesized on standard rough copper foils as “rough-Cu-graphene”. To present a structural comparison, we performed Raman mapping for both the smooth-Cu-graphene and rough-Cu-graphene. Figure 3(a) shows the optical microscope image of rough-Cu-graphene transferred on SiO2/Si. Rough-Cu-graphene includes longitudinal cracks along the graphene layer. These cracks are the graphene-free areas and resulted from the deep trenches of the rough Cu surface. Graphene synthesized on these trenches are not compatible to transfer techniques since they are formed in different height with respect to overall surface and when transferred to solid substrates these areas remain without graphene. Figure 3(b) shows the Raman mapping of the rough-Cu-graphene. Longitudinal cracks on the surface appears as low intensity black areas. Figure 3(c) shows the comparison of Raman spectrum taken from the different parts of rough-Cu-graphene including both the cracks and the full coverage graphene. Due to lacking of graphene in the cracked areas, Raman fingerprints of graphene such as G band and 2D band can hardly be detected in these areas and the Raman intensity is relatively low when compared to full coverage graphene areas. Figure 3(d) shows the optical microscope image of the smooth-Cu-graphene. After transferring to dielectric surfaces we didn’t observe any cracks on the smooth-Cu-graphene. We performed the Raman mapping in same conditions for smooth-Cu-graphene (Fig. 3(e)) and we obtain a stable Raman signal throughout the whole scanning area (25 μm x 25 μm) due to high surface coverage of the smooth-Cu-graphene. Figure 3(f) shows the Raman signal taken from the smooth-Cu-graphene surface. The Raman fingerprints of the single layer graphene, namely the peaks of G band and 2D band are clearly seen in the spectrum. We observed the G peak at 1587 nm with the full width at half maximum (FWHM) of ~23. The FWHM of 2D peak at 2658 cm−1 is ~40 and G/2D ratio is ~1.4.

To compare the electronic properties, we fabricated the graphene field effect transistors based on smooth and rough-Cu-graphene. Schematic drawing of the fabricated back-gated transistors are given in Fig. 4(a). Optical microscope images of the devices using smooth and rough-Cu-graphene are given in Fig. 4(b,c) respectively. The graphene-free spots can also cause variations in charge carrier transport and optical properties. This means the sensors in an array (e.g. active matrix display) or electronic devices in a circuit over large area graphene are likely to have non-uniform response. The transfer characteristics of the fabricated graphene transistors using rough and smooth-Cu-graphene are given in Fig. 4(d) and (e) respectively. We recorded the drain current as a function of gate voltage for six different devices at constant drain voltage. The variation of on-current (Fig. 4(d)) is significantly larger for the FETs using rough-Cu-graphene due to the non-uniform graphene formed on rough Cu foils. The calculated field effect mobility of the devices (Fig. 4(f)) scales with the channel length (See Supplementary Fig. S2 for device statistics). As it seems from the scattered plot, for longer channel lengths where the graphene uniformity starts to play critical role on the transport through the channel, field effect mobility values of the devices using smooth-Cu-graphene are enhanced compared to rough-Cu-graphene. This electrical transport measurements over large graphene areas simply shows the effects of usage of smooth Cu foils in CVD synthesis.

After the electrical measurements, to examine the optical properties of smooth-Cu-graphene we performed a large area optical scan. Figure 5(a) shows the schematic illustration for the experimental setup. We used 635 nm diode laser as a light source and with the help of motorized stage we recorded the transmittance on 5 cm x 5 cm graphene area. Figure 5(b) shows the large area graphene (~400 cm2) on flexible, 125 μm thick PVC substrate. After the CVD synthesis on ultra-smooth Cu foils, we transferred the graphene to the flexible PVC substrates by using hot lamination method. During the Cu etching, we protected the Cu foils at the edges of the sample to use them as contact electrodes for resistivity measurements and application of bias voltage. The measured total resistance of graphene is superposition of contact resistance and the sheet resistance terms (). By using transfer length method (TLM) we extracted the sheet resistance of smooth-Cu-graphene as ~2.68 kΩ and contact resistance value as ~0.4 kΩ (Supplementary Fig. S3). Figure 5(c) shows the transmittance measurement of the smooth-Cu-graphene on glass substrates by using conventional spectrometer. Theoretically, free-standing single layer graphene absorbs 2.3% of the incident light. We observed the transmittance of smooth-Cu-graphene on glass substrate is changing from 96% to 97.5% going from UV to near-infrared wavelengths. This is due to the substrate effect during transmittance measurement throughout the broad wavelength range. To check the optical uniformity in large area graphene holding PVC substrate we used the experimental setup given in Fig. 5(a) and mapped the transmittance behaviour in x and y directions. Figure 5(d) shows the transmittance mapping of graphene-free PVC substrate at 635 nm. Due to the scattering on the PVC surface, we observe a small deviation (0.5%) from a fully transparent state. Then we scanned the transmittance of smooth-Cu-graphene transferred on PVC. Figure 5(e) shows the transmittance mapping of smooth-Cu-graphene on PVC. We recorded the absorption of graphene which is stable throughout the scan area and around 1.6%. The difference between the theoretical value (2.3%) for free standing graphene and our result is likely due to the effect of PVC substrate to the measurement. Since the graphene layer is lying on the PVC surface, we also observed the same small deviation resulting from the scattering on the PVC surface in the large area optical scan for graphene. Figure 5(f) shows the histogram for the transmittance mapping of graphene-free PVC and smooth-Cu-graphene on PVC. The transmittance difference due to small optical absorption of graphene and the deviations regarding the PVC surface can be easily seen.

Previously we showed that the supercapacitor device structure can provide an efficient electrostatic doping of graphene which cannot be achieved by graphene based transistors using solid insulating dielectric layers29. To test and compare the effects of rough and smooth-Cu-graphene in large area electro-optic devices, we fabricated 20 cm × 20 cm graphene supercapacitors by using large area flexible graphene electrodes. Figure 6(a) shows the photograph of large area graphene based flexible supercapacitor. We formed the supercapacitor structure by putting the top and bottom graphene holding flexible PVC electrodes together and filling the gap with ionic liquid electrolyte (1-Butyl-3-methylimidazolium hexafluorophosphate). The inset shows the previously reported rigid device having ~2.5 cm2 graphene area. Before forming the supercapacitor structure, ionic liquid electrolyte was soaked into optical cleaning tissue to prevent the electrical shortage between top and bottom graphene electrodes which is due to the sagging of the large area flexible substrate. Figure 6(b,c) show the transmittance modulation of smooth and rough-Cu-graphene based supercapacitors which are operating as voltage controlled optical modulators. To avoid the scattering and absorption effects of PVC we used the unbiased device as reference, then recorded the transmittance changings with the applied bias voltage. Increasing the bias voltage causes the ions inside the electrolyte to form a double layer in the graphene electrolyte interface and the created electric field effectively dopes the graphene due to the extremely small separation between the graphene and the ion accumulation layer. Electrostatic doping of charge carriers in graphene shifts the Fermi level and this causes the inter-band transitions to be blocked by Pauli blocking. For Pauli blocking to take place, one should shift the Fermi level (EF) above the half of the incoming photon energy. This blocks the inter-band transitions and makes the graphene more transparent by blocking optical absorption mechanism of the material. By blocking the inter-band transitions, we achieved the light modulation over a broad range of wavelengths with the large area graphene supercapacitors. We achieve more efficient transmittance modulation in the case of smooth-Cu-graphene based supercapacitors due to the lower sheet resistance and high coverage of the smooth-Cu-graphene film. Figure 6(d) shows the transmittance versus voltage plot for both rough and smooth-Cu-graphene based supercapacitors at 700 nm. Transmittance modulation at single wavelength gives clear picture about the efficiency of using smooth-Cu-graphene in large area optoelectronic devices. Maximum modulation obtained from rough-Cu- graphene based supercapacitor is 1.16% at 4.4 V while the smooth-Cu-graphene based supercapacitor provides 2.35%. The transmittance spectra shown in Fig. 6(b,c) is a spectral distribution of the change of the transmission and it has a step-like behavior with transition centre at 2EF. Therefore we were able to extract the Fermi energy values corresponding to each curve. Figure 6(e) shows the Fermi energy level shift of the rough and smooth-Cu-graphene with respect to applied bias voltage. According to our observation, maximum Fermi level shift obtained by using rough-Cu-graphene is 0.89 eV while for the smooth-Cu-graphene it is 1.13 eV at 4.4 V. The small Fermi level difference between the rough-Cu-graphene and smooth-Cu-graphene (max. 6 meV) at lower voltages is due to the unintentional doping of graphene during the Cu etching and transfer processes.

Here the limiting factor for the bias voltage is the electrochemical window of the electrolyte used in the supercapacitor structure. Since our devices use mutual gating between top and bottom graphene electrodes, they are limited with the two times of the electrochemical window of the electrolyte (1-Butyl-3-methylimidazolium hexafluorophosphate) which is around 4.5 V. In mutual gating; the Dirac points of the top and bottom graphene shifts with respect to each other leading to two different dips in the capacitance modulation. Figure 6(f) shows the capacitance and resistance modulation of the graphene supercapacitor with respect to the applied bias voltage. As the voltage is increased to both polarizations, we observed a dramatic capacitance and resistance change due to the electrostatic doping of the top and bottom graphene layers. Detailed explanation of the physics behind this observations can be found in our previous work29.

As a result, we obtained a more efficient transmittance modulation up to two times (at 700 nm) by using smooth-Cu-graphene in supercapacitors operating as optical modulators. We also observed 27% more efficient Fermi level shift compared to rough-Cu-foils (at 4.4 V). By using electrolytes with broader electrochemical windows, the enhancement in transmittance and Fermi energy shift by using smooth-Cu-graphene can be further demonstrated in optoelectronic devices.

## Discussion

In summary, we demonstrated that using the commercially available ultra-smooth Cu foils (e.g. the one typically used in lithium-ion batteries) in CVD synthesis holds great promise for high performance in large area graphene based devices. Recent industrial progress of large scale production of smooth Cu foils, for application such as lithium-ion batteries, can also provide opportunities to improve the quality of graphene grown by CVD. After a detailed structural comparison between the rough and smooth-Cu-graphene, we studied the performance improvements in the transistors based on smooth-Cu-graphene by comparing them to transistors based on rough-Cu-graphene. To demonstrate the promises of the smooth-Cu-graphene on large area, we fabricated flexible graphene electrodes and mapped the transmittance by optical scan. These electrodes enabled us to fabricate graphene-based flexible supercapacitors operating as voltage controlled optical modulators. By enlarging the previously demonstrated supercapacitor structure, we examined the effects of usage of rough and smooth-Cu-graphene in the large area electro-optic devices. As against previous works relating the Cu surface morphology to resulting graphene quality, our method does not require chemical treatment or deposition of Cu foils. The effectiveness of our approach is two-fold:

1. 1

The lower price of commercially available ultra-smooth Cu foils (1 $per m2) that we used in this study makes the costs affordable for large scale production of graphene. Cu surface modification techniques also add to the overall cost to the graphene growth with the standard Cu foils which itself costs around 115$ per m2.

2. 2

Since there is a growing interest in realizing the electronics over large area and flexible substrates such as soft plastics and even paper36,37 synthesis of graphene in large areas with a high quality plays a crucial role in the applications. So far the flexible electronics landscape has been occupied by the low-mobility organic semiconductors37,38. But, recently major advances have also been reported through silicon39,40, metal oxides devices41 and graphene based flexible optoelectronics42 and sensing43. Our work will significantly advance these recent progresses.

We believe that large scale and low cost synthesis of high quality graphene films and the compatibility of our method to the roll-to-roll fabrication would open an avenue through the realization of graphene based flexible optoelectronic systems such as cell phones with roll-up displays, e-paper, radio-frequency identification (RFID) tags, as well as medical patches that can be attached to the skin to deliver drugs or monitor vital signs and tactile or electronic skin for robotics and prosthetics36,37,44,45.

## Methods

### CVD Synthesis of Graphene

For single layer graphene, at 1035 °C methane was sent into growth chamber in company with hydrogen (Partial pressures of CH4 and H2 gases are 285 mTorr and 40 mTorr and corresponding rate of flows are 25 sccm and 4 sccm respectively). We annealed the Cu substrates for half an hour at 1035 °C before the growth. Hydrogen flow was kept constant during the heating, annealing, growth and cooling. After 10 minutes of growth, samples were left for fast cooling to room temperature. The growth took place in a 8 inch diameter quartz chamber. We used both the commercially available 20 μm thick smooth Cu foils (Mitsui mining and smelting co., LTD, B1-SBS) and the standard 25 μm Alfa Aesar Cu foil (item #13382) as growth substrates in the same CVD chamber.

### Transfer of Graphene

For the transfer of graphene layers to the rigid substrates we used photoresist (PR) drop casting method. We drop casted thick droplets of S1813 photoresist on graphene holding Cu surfaces and waited overnight at 70 °C to gently harden the PR. Then hardened PR on graphene holding Cu was put into the dense FeCl3 solution for fast etching of Cu foils. When the Cu foil was completely etched away, graphene holding PR was put into DI water surface for 30 minutes to remove the FeCl3 residues. After air drying, we placed the graphene holding hardened PR on the target substrate and applied 110 °C for 1 minute to reflow the PR. During reflow, PR liquefies and releases the graphene layers on target substrate. Removing PR with acetone yields large area graphene on quartz and SiO2/Si substrates.

We also used lamination technique to transfer large area graphene on PVC. At 100 °C PVC becomes active and exhibits conformal sticking to the graphene holding side of ultra-smooth Cu foils when laminated through the hot rollers. Etching the Cu foils in FeCl3 solution yields the graphene on flexible PVC substrates.

### Raman spectroscopy

WITec Alpha 300 M Raman microscope system with 50x microscope objectives was used for Raman mapping. The excitation wavelength was 532 nm.

### Fabrication of transistors and electrical characterization

In order to fabricate the graphene based FETs, first conventional UV-photolithographic techniques were used to shape the source and drain electrodes on graphene. Then, thermal evaporation technique was used for metallization of the electrodes. The source and drain electrodes are 50 nm gold on 5 nm titanium adhesive layer. After lift-off step, we isolated the graphene layer by using reactive ion etching so that the graphene layers is aligned between the source and drain electrodes to define the channels. Transfer and output characteristics of the graphene based transistors were performed with HP4142B semiconductor parameter analyser. We recorded the drain current as a function of gate voltage at constant drain voltage. We repeat the measurements for devices having various channel lengths.

### Optical transmittance measurements

The transmittance measurements were performed by using Bruker Vertex 70 V FTIR spectrometer integrated with silicon photodetector working in visible and near-IR. We worked in the wavelength range between 400 nm to 1100 nm. We biased the graphene based transistors using Keithley 2400 source measure unit during the transmittance measurements. The leakage current is also recorded during the measurement.

How to cite this article: Polat, E. O. et al. Synthesis of Large Area Graphene for High Performance in Flexible Optoelectronic Devices. Sci. Rep. 5, 16744; doi: 10.1038/srep16744 (2015).

## References

1. Kocabas, C. et al. Radio frequency analog electronics based on carbon nanotube transistors. P Natl Acad Sci USA 105, 1405–1409, doi: 10.1073/pnas.0709734105 (2008).

2. Lin, Y. M. et al. 100-GHz Transistors from Wafer-Scale Epitaxial Graphene. Science 327, 662–662, doi: 10.1126/science.1184289 (2010).

3. Kocabas, C., Shim, M. & Rogers, J. A. Spatially selective guided growth of high-coverage arrays and random networks of single-walled carbon nanotubes and their integration into electronic devices. J Am Chem Soc 128, 4540–4541, doi: 10.1021/Ja0603150 (2006).

4. Ishigami, N. et al. Crystal plane dependent growth of aligned single-walled carbon nanotubes on sapphire. J Am Chem Soc 130, 9918–9924, doi: 10.1021/Ja8024752 (2008).

5. Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat Mater 6, 183–191, doi: 10.1038/Nmat1849 (2007).

6. Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669, doi: 10.1126/science.1102896 (2004).

7. Zhang, Y. B., Tan, Y. W., Stormer, H. L. & Kim, P. Experimental observation of the quantum Hall effect and Berry’s phase in graphene. Nature 438, 201–204, doi: 10.1038/Nature04235 (2005).

8. Du, X., Skachko, I., Duerr, F., Luican, A. & Andrei, E. Y. Fractional quantum Hall effect and insulating phase of Dirac electrons in graphene. Nature 462, 192–195, doi: 10.1038/Nature08522 (2009).

9. Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200, doi: 10.1038/Nature04233 (2005).

10. Katsnelson, M. I., Novoselov, K. S. & Geim, A. K. Chiral tunnelling and the Klein paradox in graphene. Nat Phys 2, 620–625, doi: 10.1038/Nphys384 (2006).

11. Blake, P. et al. Making graphene visible. Appl Phys Lett 91, Artn 063124, doi: 10.1063/1.2768624 (2007).

12. Wang, F. et al. Gate-variable optical transitions in graphene. Science 320, 206–209, doi: 10.1126/science.1152793 (2008).

13. Bae, S. et al. Roll-to-roll production of 30-inch graphene films for transparent electrodes. Nat Nanotechnol 5, 574–578, doi: 10.1038/Nnano.2010.132 (2010).

14. Novoselov, K. S. et al. A roadmap for graphene. Nature 490, 192–200, doi: 10.1038/nature11458 (2012).

15. Dresselhaus, M. S. & Dresselhaus, G. Intercalation compounds of graphite. Adv Phys 51, 1–186, doi: 10.1080/00018730110113644 (2002).

16. Hernandez, Y. et al. High-yield production of graphene by liquid-phase exfoliation of graphite. Nat Nanotechnol 3, 563–568, doi: 10.1038/nnano.2008.215 (2008).

17. Stankovich, S. et al. Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide. Carbon 45, 1558–1565, doi: 10.1016/j.carbon.2007.02.034 (2007).

18. Niyogi, S. et al. Solution properties of graphite and graphene. J Am Chem Soc 128, 7720–7721, doi: 10.1021/Ja060680r (2006).

19. Li, X. S. et al. Large-Area Synthesis of High-Quality and Uniform Graphene Films on Copper Foils. Science 324, 1312–1314, doi: 10.1126/science.1171245 (2009).

20. Kim, K. S. et al. Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 457, 706–710, doi: 10.1038/Nature07719 (2009).

21. Reina, A. et al. Large Area, Few-Layer Graphene Films on Arbitrary Substrates by Chemical Vapor Deposition. Nano Lett 9, 30–35, doi: 10.1021/Nl801827v (2009).

22. Li, X. S. et al. Graphene Films with Large Domain Size by a Two-Step Chemical Vapor Deposition Process. Nano Lett 10, 4328–4334, doi: 10.1021/Nl101629g (2010).

23. Han, G. H. et al. Influence of Copper Morphology in Forming Nucleation Seeds for Graphene Growth. Nano Lett 11, 4144–4148, doi: 10.1021/Nl201980p (2011).

24. Luo, Z. T. et al. Effect of Substrate Roughness and Feedstock Concentration on Growth of Wafer-Scale Graphene at Atmospheric Pressure. Chem Mater 23, 1441–1447, doi: 10.1021/Cm1028854 (2011).

25. Yan, Z. et al. Towards the Synthesis of Wafer-Scale Single-Crystal Graphene on Copper Foils. Acs Nano. doi: 10.1021/nn303352k (2012).

26. Geng, D. C. et al. Uniform hexagonal graphene flakes and films grown on liquid copper surface. P Natl Acad Sci USA 109, 7992–7996, doi: 10.1073/pnas.1200339109 (2012).

27. Wu, Y. M. A. et al. Large Single Crystals of Graphene on Melted Copper Using Chemical Vapor Deposition. Acs Nano 6, 5010–5017, doi: 10.1021/Nn3016629 (2012).

28. Orofeo, C. M. et al. Influence of Cu metal on the domain structure and carrier mobility in single-layer graphene. Carbon 50, 2189–2196, doi: 10.1016/j.carbon.2012.01.030 (2012).

29. Polat, E. O. & Kocabas, C. Broadband Optical Modulators Based on Graphene Supercapacitors. Nano Lett 13, 5851–5857, doi: 10.1021/Nl402616t (2013).

30. Zhang, B. et al. Low-Temperature Chemical Vapor Deposition Growth of Graphene from Toluene on Electropolished Copper Foils. Acs Nano 6, 2471–2476, doi: 10.1021/Nn204827h (2012).

31. Vlassiouk, I. et al. Role of Hydrogen in Chemical Vapor Deposition Growth of Large Single-Crystal Graphene. Acs Nano 5, 6069–6076, doi: 10.1021/Nn201978y (2011).

32. Fasolino, A., Los, J. H. & Katsnelson, M. I. Intrinsic ripples in graphene. Nat Mater 6, 858–861, doi: 10.1038/Nmat2011 (2007).

33. Meyer, J. C. et al. The structure of suspended graphene sheets. Nature 446, 60–63, doi: 10.1038/Nature05545 (2007).

34. Thompson-Flagg, R. C., Moura, M. J. B. & Marder, M. Rippling of graphene. Epl-Europhys Lett 85, Artn 46002, doi: 10.1209/0295-5075/85/46002 (2009).

35. Wang, Z. & Devel, M. Periodic ripples in suspended graphene. Phys Rev B 83, Artn 125422, doi: 10.1103/Physrevb.83.125422 (2011).

36. Nathan, A. et al. Flexible Electronics: The Next Ubiquitous Platform. Proceedings of the IEEE 100, 1486–1517, doi: 10.1109/jproc.2012.2190168 (2012).

37. Khan, S., Lorenzelli, L. & Dahiya, R. Technologies for Printing Sensors and Electronics over Large Flexible Substrates: A Review. IEEE Sensors Journal XX, 1–22, doi: 10.1109/JSEN.2014.2375203 (2014).

38. Sirringhaus, H. 25th Anniversary Article: Organic Field-Effect Transistors: The Path Beyond Amorphous Silicon. Advanced Materials. doi: 10.1002/adma.201304346 (2014).

39. Dahiya, R. S. & Gennaro, S. Bendable Ultra-Thin Chips on Flexible Foils. Ieee Sens J 13, 4030–4037, doi: 10.1109/Jsen.2013.2269028 (2013).

40. Dahiya, R. S., Adami, A., Collini, C. & Lorenzelli, L. Fabrication of Single Crystal Silicon Mirco-/Nanostructures and Transferring them to Flexible Substrates. Microelectronic Engineering 98, 502–507, doi: 10.1016/j.mee.2012.07.084 (2012).

41. Kim, Y. H. et al. Flexible metal-oxide devices made by room-temperature photochemical activation of sol-gel films. Nature 489, 128–U191, doi: 10.1038/Nature11434 (2012).

42. Polat, E. O., Balci, O. & Kocabas, C. Graphene based flexible electrochromic devices. Sci Rep-Uk 4, Artn 6484, doi: 10.1038/srep06484 (2014).

43. Wang, Y. et al. Super-Elastic Graphene Ripples for Flexible Strain Sensors. Acs Nano 5, 3645–3650, doi: 10.1021/Nn103523t (2011).

44. Kim, D.-H. et al. Epidermal Electronics. Science 333, 838–843, doi: 10.1126/science.1206157 (2011).

45. Dahiya, R. S., Mittendorfer, P., Valle, M., Cheng, G. & Lumelsky, V. Directions Towards Effective Utilization of Tactile Skin—A Review. IEEE Sensors Journal 13, 4121–4138, doi: 10.1109/JSEN.2013.2279056 (2013).

## Acknowledgements

The research leading to these results partly received funding from European Commission under grant agreements PITN–GA–2012–317488-CONTEST, Engineering and Physical Sciences Council (EPSRC) Fellowship for Growth – Printable Tactile Skin (EP/M002527/1) and Scientific and Technological Research Council of Turkey (TUBİTAK) Grants 112T686 and 113T278. N.K. and O. B. acknowledges the TUBİTAK-BİDEB for the scholarship program 2215 and 2211.

## Author information

Authors

### Contributions

C.K. proposed the idea. E.O.P. and C.K. planned the experiment. E.O.P., O.B. and N.K. synthesized and transferred graphene layers. E.O.P., O.B. and N.K. and H.B.U performed the electronic and optical characterizations. E.O.P., C.K. and R.D. analysed the data and wrote the manuscript.

## Ethics declarations

### Competing interests

The authors declare no competing financial interests.

## Rights and permissions

Reprints and Permissions

Polat, E., Balci, O., Kakenov, N. et al. Synthesis of Large Area Graphene for High Performance in Flexible Optoelectronic Devices. Sci Rep 5, 16744 (2015). https://doi.org/10.1038/srep16744

• Accepted:

• Published:

• ### High-performance printed electronics based on inorganic semiconducting nano to chip scale structures

• Abhishek Singh Dahiya
• Dhayalan Shakthivel
• Ravinder Dahiya

Nano Convergence (2020)

• ### Adlayer-free large-area single-crystal CVD graphene growth on copper

• Chaitanya Arya
• K. Kanishka H. De Silva
• Masamichi Yoshimura

Journal of Materials Science: Materials in Electronics (2020)

• ### Transmission Properties of FeCl3-Intercalated Graphene and WS2 Thin Films for Terahertz Time-Domain Spectroscopy Applications

• Maria O. Zhukova
• Benjamin T. Hogan
• Anton N. Tcypkin

Nanoscale Research Letters (2019)

• ### Gate-tunable graphene-based Hall sensors on flexible substrates with increased sensitivity

• Burkay Uzlu
• Zhenxing Wang
• Daniel Neumaier

Scientific Reports (2019)

• ### Enhanced adsorption of methylene blue on chemically modified graphene nanoplatelets thanks to favorable interactions

• Rabita Mohd Firdaus
• Noor Izzati Md Rosli
• Abdul Rahman Mohamed

Journal of Nanoparticle Research (2019)