Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Reversible superconductor-insulator transition in LiTi2O4 induced by Li-ion electrochemical reaction


Transition metal oxides display various electronic and magnetic phases such as high-temperature superconductivity. Controlling such exotic properties by applying an external field is one of the biggest continuous challenges in condensed matter physics. Here, we demonstrate clear superconductor-insulator transition of LiTi2O4 films induced by Li-ion electrochemical reaction. A compact electrochemical cell of pseudo-Li-ion battery structure is formed with a superconducting LiTi2O4 film as an anode. Li content in the film is controlled by applying a constant redox voltage. An insulating state is achieved by Li-ion intercalation to the superconducting film by applying reduction potential. In contrast, the superconducting state is reproduced by applying oxidation potential to the Li-ion intercalated film. Moreover, superconducting transition temperature is also recovered after a number of cycles of Li-ion electrochemical reactions. This complete reversible transition originates in difference in potentials required for deintercalation of initially contained and electrochemically intercalated Li+ ions.


Development of rechargeable Li-ion batteries with high cell-potential and capacity has become increasingly important for sustainable society1. Electrochemical reactions with Li+ ions involve intercalation to the anode and cathode materials, corresponding to charge and discharge of the batteries. Such a Li-ion intercalation is also utilized for modulation of materials properties; creation of a new superconductor that cannot be synthesized by conventional solid-state reactions. Various superconductors have been synthesized by the electrochemical Li-ion intercalation, e.g. LixMNCl (M = Zr and Hf), LixSr2CuO2 X2 (X = Cl, Br and I), LixASr2Nb3O10 (A = Rb and Cs) and related nonstoichiometric compounds2,3,4,5. The most electropositive Li+ ions enable to dope a large number of electrons in parent materials although a range of the doping is limited to space available for intercalation of excess Li+ ions. The degree of nonstoichiometry is also important for battery operation to keep high capacity without degradation of the electrode materials.

Amongst a variety of materials, LiTi2O4 (LTO) is a unique candidate for our experiment with the use of a Li-ion battery structure because LTO exhibits superconductivity with a critical temperature as high as 13.7 K6,7,8,9,10,11,12,13,14,15. LTO has a spinel-type structure with a lattice constant of a = 8.40 Å6. Li+ ions are located at the centre of oxygen tetrahedrons and Ti3+ and Ti4+ ions are of oxygen octahedrons6,7,8,9,10. The edge-shared TiO6 octahedrons form a conduction path of electrons and the LiO4 tetrahedrons play a role of charge reservoir to accommodate Ti sites with the carriers. The occupancy of Li+ ions at the tetrahedral sites is one-fourth for the ideal chemical formula. The excess Li+ ions can be introduced into empty space either at tetrahedral and octahedral sites. This situation is regarded as over-doping. Meanwhile, the excess Li+ ions also replace the Ti ions resulting in hole doping in addition to interruption of the edge-shared TiO6 network. Therefore, the electronic property of LTO dramatically changes depending on content and location of Li+ ions. In particular, superconductivity disappears and then metallic phase eventually undergoes to a transition to insulator with either increasing or decreasing Li content from the ideal chemical formula8,9,10. These facts suggest that superconductivity can be modulated by Li-ion electrochemical reactions.

Hamada et al. reported Li-ion electrochemical reaction to bulk LTO11. Li content x of bulk Li1+xTi2O4 was controlled in a range of –0.3 ≤ x ≤ 1 and found that superconducting transition temperature (TC) of LTO varied in a range from ~12 to 13.3 K. Superconductor-insulator transition (SIT) was not observed due to phase separation, which would be caused by inhomogeneous electrochemical reaction of bulk LTO with larger volume and smaller surface area.

In this article, we demonstrate clear SIT of LTO films induced by Li-ion electrochemical reaction. A compact electrochemical cell of pseudo-Li-ion battery structure was formed with a superconducting LTO film as an anode16. By applying a constant voltage exceeding reduction potential, Li content in the LTO film increased and the sample showed insulating behaviour. In contrast, by applying a constant voltage over oxidation potential, electrochemical deintercalation of Li+ ions occurred to regain superconductivity. In addition, TC was found to be almost identical even after a number of repeats for Li-ion intercalation/deintercalation reactions. The fact that after the repeated experiments the crystal structure of LTO film remained intact manifested itself in the complete and reversible SIT.


Li-ion electrochemical reaction

Our setup as illustrated in Fig. 1, Li-ion electrolyte sandwiched by LiCoO2/Al foil (cathode) and LTO film (anode), can be regarded as pseudo-Li-ion battery structure. Four-probe resistivity measurements and three-terminal Li-ion electrochemical reactions were performed by using a sourcemetre and a potentiostat, respectively. When a potential lower than the Ti3+/Ti4+ redox potential is applied, Li+ ions are intercalated into the LTO film, being analogous to charging battery. To balance the positive charge of the Li+ ions, electrons are injected into the film, resulting in the reduction of the Ti valence. Thus, application of negative potential to the anode corresponds to effective electron doping owing to the most electropositive ionicity of Li. In contrast, application of positive potential results in Li-ion deintercalation (removal of Li+ ions from the over-doped film), which corresponds to hole doping and thus discharging battery.

Figure 1
figure 1

Schematic illustration of the pseudo-Li-ion battery structure.

The anode and cathode materials are LiTi2O4 film and LiCoO2/Al, respectively. The Li-ion electrochemical reactions and resistivity measurements are independently performed by using electric circuits, drawn by at the side and bottom of the cell, respectively.

We first studied aforementioned Li-ion electrochemical reactions by cyclic voltammetry. Figure 2 shows typical cyclic voltammogram of LTO|LiClO4:propylene carbonate (PC)| LiCoO2/Al system taken at a rate of 5 mV/s. Rotationally symmetric curves with equal peak integral were clearly observed. The cathodic peak at −1.8 V (vs. Ag/AgClO4) was attributed to the reduction of Ti4+ to Ti3+, whereas subsequent oxidation of Ti3+ to Ti4+ represented the anodic peak at −1.5 V. We also measured cyclic voltammogram in a wide potential range from −4 to +1.5 V (vs. Ag/AgClO4). Decomposition of LTO films occurred at around +0.3 V and deposition of Li metal at the surface of the films occurred below −3 V (see Supplementary Note 1 online). From these characteristic cyclic voltammograms, the applied potentials in the chronoamperometric Li-ion intercalation (deintercalation) were set at −2.0 (−0.5) V to guarantee reversible Li-ion electrochemical reactions and stable battery operation.

Figure 2
figure 2

Li-ion electrochemical reaction of LiTi2O4 films.

Cyclic voltammogram of LiTi2O4|LiClO4:PC|LiCoO2/Al system at a rate of 5 mV/s.

Structural characterization

The chemical and structural stability of the LTO anode was also confirmed by x-ray diffraction (XRD). Figure 3(a,b) show the symmetric and asymmetric XRD patterns around LTO (111) and (400) reflections for the samples before and after Li-ion electrochemical reactions, respectively. We noted that the data shown in Fig. 3(a,b) were taken from the film with which the temperature dependence of resistivity shown in Fig. 4(a) was measured. The (111) reflection of the as-grown LTO film was detected at 2θ = 18.25°, corresponding to d111 = 4.86 Å. The film after the reaction exhibited this reflection at the exactly same angle. In addition, the asymmetric (400) reflections of LTO film were also detected 2θ = 43.1°, corresponding to d400 = 2.10 Å, regardless of Li-ion electrochemical reactions. The calculated lattice constant of the LTO films (a = 8.40 Å) agreed with that of bulk7,9. We also performed wide-range out-of-plane XRD measurements for both samples to find possible segregation of secondary phase (see Supplementary Note 2 online). Such a trace was not detected, indicating that the crystal structure remained intact during Li-ion electrochemical reactions17,18. We also investigated surface morphology of the LTO films before and after Li-ion electrochemical reactions by using atomic force microscopy (AFM) (see Supplementary Note 3 online). Both samples indicated flat surface with a root mean square roughness of less than 0.5 nm, but not a sign of corrosion such as dissolution, segregation and deposition. These data suggest that all of the following results have been established in the LTO film of original quality that remains intact during reversible Li-ion intercalation/deintercalation.

Figure 3
figure 3

Structural characterization of LiTi2O4 films.

XRD patterns for the LiTi2O4 films before (red) and after (blue) Li-ion electrochemical reactions. (a) XRD pattern around the symmetric (111) MgAl2O4 reflection. (b) XRD pattern around the asymmetric (400) MgAl2O4 reflection.

Figure 4
figure 4

Reversible superconductor-to-insulator transition of LiTi2O4 films induced by Li-ion electrochemical reactions.

(a) The black, red and blue markers indicate temperature-dependent resistivity for initial, intercalated (1st) and deintercalated (1st) LiTi2O4 films, respectively. The inset shows the magnified curves near TC (normalized by the values at 15 K). Note that the initial and the deintercalated curves are overlapped to each other. (b) Passage of TC against the number of repeats of Li-ion electrochemical reactions. The initial data is set at 0. For convenience, TC of 0 K for all the Li-ion intercalated films represents the fact that resistivity did not fall to zero above 2 K.

Superconductor-insulator transition

Electrochemical modulation of superconducting properties was investigated by measuring temperature dependence of resistivity. The initial LTO film (immersed in electrolyte) showed metallic conductivity with room-temperature resistivity of ~1 × 10−3 Ω cm and a superconducting transition at TC = 11.1 K [Fig. 4(a)]. We noted that lower TC of our LTO film than that of bulk was caused by slight nonstoichiometry of LTO films. It was difficult to make Li content exactly unity because of high vapour pressure of Li. (see ref. 15 for details) In contrast, the Li-ion intercalated film showed insulating behaviour with resistivity higher than the initial value by an order of magnitude. Moreover, the resistivity increased with decreasing temperature and eventually became a constant at temperatures from 80 to 2 K. The absence of the superconducting state indicates occurrence of SIT. We continued measurements after Li-ion deintercalation to find that resistivity curve was in excellent agreement with the initial one, including TC [see inset of Fig. 4(a)]. These results indicate that the superconducting state was completely regained after a cycle of electrochemical reaction.

Excellent reversibility in SIT was further seen in TC as a function of number of the Li-ion electrochemical reactions [Fig. 4(b)]. TC was nearly constant even after three cycles (deviation in TC was less than 0.3 K). Further measurement was only hampered by slow evaporation of Li-ion electrolyte. Except for this drawback, our setup including the use of thin film with large surface area is ideal for electrochemical modulation of the electronic state in LTO.


Now, we would like to discuss possible mechanism of SIT in the LTO film. Taking strong dependence of TC on Li content for bulk LTO into account, nearly constant TC in repeated experiments suggests that the Li contents in the initial and Li-ion deintercalated films are almost identical to each other, which implies that Li+ ions contained in the as-grown film were immobile and did not contribute electrochemical reactions. In fact, when the Li-ion deintercalation was first applied to another LTO film, its superconducting state remained although TC slightly changed (see Supplementary Note 4 online). The following Li-ion intercalation/deintercalation reactions (i.e. stepwise introduction/removal of excess Li+ ions) did not influence further change in TC. These results indicate that the chronoamperometric Li-ion intercalation (−2.0 V) and deintercalation (−0.5 V) induce simple transfer of a part of excess Li+ ions between the LTO film and Li-ion electrolyte.

This scenario does not necessarily interpret that the Li+ ions cannot be removed from an initial film by any Li-ion electrochemical reactions. When chronopotentiometric Li-ion deintercalation was applied to the initial LTO film, the oxidation current was clearly observed. (see Supplementary Note 5 online). Meanwhile, potential was found to be about −0.2 V (vs. Ag/AgClO4), which was higher than that applied in the chronoamperometric Li-ion deintercalation. The potential of −0.5 V (vs. Ag/AgClO4) was just too low to deintercalate the initially contained Li ions. Therefore, only the electrochemically intercalated Li+ ions could be deintercalated in the chronoamperometric Li-ion deintercalation, resulting in demonstration of complete reversible SIT of LTO film. Finally, we would like to emphasize that chronopotentiometric Li-ion electrochemical reactions are advantageous to subtle tuning of Li content in the films with monitoring redox currents. Using this method, the superconducting states with intermediate TC were achieved (see Supplementary Note 6 online).

In summary, we have demonstrated SIT of LTO films induced by Li-ion electrochemical reactions. Li-ion intercalation to the LTO film can control the electronic phase from superconductor to insulator. The intercalated Li+ ions can be completely removed by applying oxidation potential, resulting in reproduction of the superconducting state. In addition, TC is also recovered after a number of cycles of Li-ion electrochemical reactions. This complete reversible SIT originates in difference in potentials required for deintercalation of initially contained and electrochemically intercalated Li+ ions. Our study will pave a way to control electronic phase of thin layers electrochemically and in-situ and thus to reveal a complete electronic phase diagram in temperature and phase space.


Thin-Film Preparation

LTO films with thickness of approximately 50 nm were grown on (111) MgAl2O4 substrates by using pulsed-laser deposition technique in an ultrahigh-vacuum chamber. KrF excimer laser pulses (10 Hz, 0.7 J/cm2) were focused on a Li-excess ceramic tablet (LiTiOx). The Li-excess target was necessary for growing the high-quality LTO films because of significant loss of Li species during the ablation13,15. Substrate temperature was set 750 °C and Ar gas (6 N purity) was continuously fed into the camber with keeping the pressure of 0.1 mTorr during the growth. After the growth, the LTO films were cooled to room temperature under an Ar atmosphere.

Electrochemical Reactions and Resistivity Measurements

Li-ion electrochemical reactions were performed with using the standard three-electrode setup. The working, counter and reference electrodes consisted of LTO films, LiCoO2 coated Al foil and Ag wire, respectively. Liquid electrolyte was prepared by mixing lithium ion salt of LiClO4 (>99%) and organic solvent of PC (>98%) (weight ratio of LiClO4 to PC = 1:20) in a glovebox, followed by heating at ~50 °C to remove moisture. Cyclic voltammetry was performed with using a potentiostat (model 2323, ALS Co., Ltd). The Li-ion electrochemical reactions and successive temperature-dependent resistivity measurements were performed in-situ by using a four-probe method using physical properties measurement system (Quantum design, PPMS). This setup prevented the sample and Li-ion electrolyte from degradation caused by exposure to air. For four-probe resistivity measurements, Al wire (25 μm diametre) was directly welded to the surface of LTO films.

One cycle of the experiment was started from electrochemical Li-ion intercalation (deintercalation) to the LTO film performed at room temperature by applying a potential of −2.0 V (−0.5 V) with respect to the Ag/AgClO4 quasi-reference electrode. While keeping constant potential, the cell was cooled to 140 K at a rate of 10 K/min, with applying the continuous constant potential in order to prevent self-discharge. At 140 K, motion of the Li+ ions was completely frozen in a solidified medium, so that we stopped applying external potential and run resistivity measurements. After temperature reached 2 K, the cell was warmed to room temperature at a rate of 10 K/min.

Structural Characterizations

Before and after Li-ion electrochemical reactions, crystal structures and surface morphology of the LTO films were inspected by a Cu Kα1 XRD apparatus and AFM, respectively. Here, the Li-ion electrochemical reaction corresponds to applying a reduction potential of –2.0 V (vs. Ag/AgClO4) to the LTO film. Then, the film was washed with deionized water in an ultrasonic cleaner and dried by blowing N2 gas.

Additional Information

How to cite this article: Yoshimatsu, K. et al. Reversible superconductor-insulator transition in LiTi2O4 induced by Li-ion electrochemical reaction. Sci. Rep. 5, 16325; doi: 10.1038/srep16325 (2015).


  • Tarascon, J. –M. & Armand, M. Issues and challenges facing rechargeable lithium batteries. Nature 414, 359 (2001).

    CAS  ADS  Article  Google Scholar 

  • Kato, M. et al. Synthesis of oxide superconductors by soft-chemical techniques. Mater. Sci. Eng. B 148, 53 (2008).

    CAS  Article  Google Scholar 

  • Kato, M., Kajita, T., Hanakago, R. & Koike, Y. Search for new superconductor s by the Li-intercalation into layered perovskites. Physica C, 445–448, 26 (2006).

    ADS  Article  Google Scholar 

  • Yamanaka, S., Kawaji, H., Hotehama, K. & Ohashi, M. A new layer-structured nitride superconductor lithium-intercalated β-zirconium nitride chloride. Adv. Mater. 8, 771 (1996).

    CAS  Article  Google Scholar 

  • Yamanaka, S., Hotehama, K. & Kawaji, H. Superconductivity at 25.5 K in electron-doped layered hafnium nitride. Nature 392, 580 (1998).

    CAS  ADS  Article  Google Scholar 

  • Johnston, D. C., Prakash, H., Zachariasen, W. H. & Viswanathan, R. High temperature superconductivity in the Li-Ti-O ternary system. Mat. Res. Bull. 8, 777 (1973).

    CAS  Article  Google Scholar 

  • Johnston, D. C., Superconducting and normal state properties of Li1+xTi2-xO4 spinel compounds. I. Preparation, crystallography, superconducting properties, electrical resistivity, dielectric behaviour and magnetic susceptibility. J. Low Temp. Phys. 25, 145 (1976).

    CAS  ADS  Article  Google Scholar 

  • McCallum, R. W., Johnston, D. C., Luengo, C. A. & Maple, M. B. Superconducting and normal state properties of Li1+xTi2-xO4 spinel compounds. II. Low-temperature heat capacity. J. Low Temp. Phys. 25, 177 (1976).

    CAS  ADS  Article  Google Scholar 

  • Chen, C., Spears, M., Wondre, F. & Ryan, J. Crystal growth and superconductivity of LiTi2O4 and Li1+1/3Ti2−1/3O4 . J. Cryst. Growth 250, 139 (2003).

    CAS  ADS  Article  Google Scholar 

  • Moshopoulou, E., Bordet, P., Sulpice, A. & Capponi, J. J. Evolution of structure and superconductivity of Li1−xTi2O4 single crystals without Ti cation disorder. Physica C 235–240, 747 (1994).

  • Hamada, S., Kato, M., Noji, T. & Koike, Y. Superconductivity and electrochemistry of the spinel Li1+xTi2O4 . Physica C 470, S766 (2010).

    CAS  ADS  Article  Google Scholar 

  • Chopdekar, R. V., Wong, F. J., Takamura, Y., Arenholz, E. & Suzuki, Y. Growth and characterization of superconductivity spinel oxide LiTi2O4 thin films. Physica C 469, 1885 (2009).

    CAS  ADS  Article  Google Scholar 

  • Kumatani, A. et al. Growth processes of lithium titanate thin films deposited by using pulsed laser deposition. Appl. Phys. Lett. 101, 123103 (2012).

    ADS  Article  Google Scholar 

  • Inukai, T., Murakami, T. & Inamura, T. Preparation of superconducting LiTi2O4 thin films. Thin Solid Films 94, 47 (1982).

    CAS  ADS  Article  Google Scholar 

  • Oshima, T., Yokoyama, K., Niwa, M. & Ohtomo, A. Pulsed-laser deposition of superconducting LiTi2O4 ultrathin films. J. Cryst. Growth 424, 77 (2015).

    Article  Google Scholar 

  • Ferg, E., Gummow, R. J., Kock, A. & de, Thackeray, M. M. Spinel anodes for lithium-ion batteries. J. Electrochem. Soc. 141, L147 (1994).

    CAS  Article  Google Scholar 

  • Ohzuku, T., Ueda, A. & Yamamoto, N. Zero-strain insertion material of Li[Li1/3Ti5/3]O4 for rechargeable lithium cells. J. Electrochem. Soc. 142, 1431 (1995).

    CAS  Article  Google Scholar 

  • Kuhn, A., Baehtz, C. & G. –Alvarado, F. Structural evolution of ramsdellite-type LixTi2O4 upon electrochemical lithium insertion-deinsertion (0 ≤ x ≤ 2). J. Power Sources 174, 421 (2007).

    CAS  ADS  Article  Google Scholar 

Download references


The authors greatly thank Prof. K. Ueno for discussion. The authors also thank Prof. T. Takao, Dr. M. Oishi and Mr. M. Nagaoka for experimental assistance on preparation of electrolyte. This work was partly supported by MEXT Elements Strategy Initiative to Form Core Research Centre and a Grant-in-Aid for Scientific Research (No. 15H03881) from the Japan Society for the Promotion of Science Foundation.

Author information




M.N. and H.M. performed the experiment. K.Y. and M.N. analysed experimental data. All authors discussed the results and wrote the manuscript. A.O. supervised the project.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Electronic supplementary material

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Yoshimatsu, K., Niwa, M., Mashiko, H. et al. Reversible superconductor-insulator transition in LiTi2O4 induced by Li-ion electrochemical reaction. Sci Rep 5, 16325 (2015).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing