Charge transport measurements form an essential tool in condensed matter physics. The usual approach is to contact a sample by two or four probes, measure the resistance and derive the resistivity, assuming homogeneity within the sample. A more thorough understanding, however, requires knowledge of local resistivity variations. Spatially resolved information is particularly important when studying novel materials like topological insulators, where the current is localized at the edges, or quasi-two-dimensional (2D) systems, where small-scale variations can determine global properties. Here, we demonstrate a new method to determine spatially-resolved voltage maps of current-carrying samples. This technique is based on low-energy electron microscopy (LEEM) and is therefore quick and non-invasive. It makes use of resonance-induced contrast, which strongly depends on the local potential. We demonstrate our method using single to triple layer graphene. However, it is straightforwardly extendable to other quasi-2D systems, most prominently to the upcoming class of layered van der Waals materials.
The past years have seen a tremendous increase in available quasi-2D materials, extending from graphene1 to van der Waals heterostructures2 and topological insulators3,4,5. Not only have remarkable physical phenomena such as Dirac-Weyl physics6,7 and Klein tunneling8 been observed, these materials also offer great opportunities for applications in electronic devices1,3. To maximize their potential, precise knowledge of the local electron transport properties is essential. In topological insulators for instance, the conductance is completely governed by edge states, while the bulk remains insulating5. In graphene, on the other hand, charge transport can be dominated by electron and hole puddles created by the intimate contact to a substrate9. Furthermore, small-scale variations like step edges, grain boundaries and atomic defects can strongly affect global properties. To elucidate such local conductance properties, several groups have performed ground-breaking experiments using scanning probe techniques such as Kelvin probe microscopy10, (four-probe) scanning tunneling microscopy11 and scanning squid microscopy12. The scanning nature of these techniques, however, inherently leads to long acquisition times and a limited field of view. Here, we introduce a novel tool, coined low-energy electron potentiometry (LEEP), which allows for rapid imaging of potential landscapes, with both high resolution and a field of view of up to 10 μm. From the known performance of the microscope13, we estimate <5 nm spatial resolution and ~10 meV energy resolution to be achievable with LEEP. The technique does not require a local, possibly invasive probe. Moreover, the entire field of view is imaged at once, reducing the acquisition time for a potential map below one minute. Hence, potentiometry studies of dynamic processes come within reach. Interestingly, LEEP experiments can be combined with Low-Energy Electron Microscopy (LEEM)14 and Photo Electron Emission Microscopy and Spectroscopy (PEEM) measurements on the same sample in the same microscope. This combination forms an extremely powerful set of complementary tools, LEEM allowing one to determine the structure and morphology of 2D materials, PEEM giving access to the electronic band structure and LEEP providing insight in charge transport on the nanoscale.
The basic idea behind LEEP is to determine the local potential at each position on a sample from LEEM images, i.e., from the intensity of specularly reflected low-energy electrons (0–100 eV) that are projected onto a pixelated detector14,15,16,17. The landing energy of the electrons at the surface can be tuned by varying the overall sample potential VE (Fig. 1a,b). Importantly, for each material the electron reflection probability depends strongly on the electron landing energy or, equivalently, on the electron wavelength λ as given by the de Broglie relation. In fact, a measurement of the signal intensity I versus VE, yielding a so-called IV-curve I(VE), is considered a fingerprint of a specific surface structure18,19. In a conductance experiment, an in-plane bias voltage Vbias is applied over a sample. This causes the local electron landing energy (wavelength) to become position-dependent, as depicted in Fig. 1c. Consequently, for each point on the sample, the local IV-curve is shifted in energy20. By quantifying this shift, one can determine a full surface potential map. This is the essence of the potentiometry method introduced here.
In principle, any clean material has its characteristic IV-curve and can thus be studied by potentiometry. Still, LEEP is expected to work best if the intensity exhibits a strong and well-defined energy dependence. The layered structure of van der Waals heterostructures, for example, has interesting consequences for LEEM IV-curves. The properties of these stacks of 2D systems like hexagonal boron nitride, graphene or transition metal dichalcogenides, held together by van der Waals forces, are tunable by choosing a specific stacking2. In these materials, there typically exist unoccupied states, localized between adjacent layers18. The electronic coupling between these interlayer states causes a splitting of their energy levels, resulting in n non-degenerate states for materials with n + 1 layers. When the electron landing energy in a LEEM experiment is equal to the energy of one of these states, resonant coupling between the electron wave and the interlayer state suppresses electron reflection. This yields minima in the IV-curve, with the number of such minima corresponding to the number of interlayer states n. For graphene on silicon carbide (SiC), for example, the number of minima corresponds to the number of conducting graphene layers, because the bottommost carbon layer is a buffer layer that is insulating, but does contribute to the formation of interlayer states21. Thus, LEEM IV-curves form a powerful tool to characterize novel van der Waals systems. Moreover they can be used as a basis for potentiometry.
To explore such ‘resonant’ IV-curves, we use multilayer graphene as a model system for van der Waals materials. Particularly, we choose graphene grown on SiC, because it is clean and homogeneous over large areas and has a well-defined step direction22. Electrical contact to a graphene device, patterned perpendicular to the SiC steps, is made via lithographically defined gold electrodes. Subsequently, remaining resist is thoroughly removed (see Supplementary Methods: Sample Preparation). Figure 2a,b, show LEEM images of the same area of the graphene device (circle in inset of Fig. 2c) acquired at two different electron landing energies with no in-plane bias applied. While the same features can be distinguished in both images, the contrast differs considerably. This can be understood by looking at the IV-curves presented in Fig. 2c. These curves, taken at three different spots of the sample, exhibit 1, 2 and 3 minima respectively, which, as discussed above, corresponds to monolayer, bilayer and triple layer of electronically well-defined graphene. This allows us to tune the contrast of LEEM images by changing the electron landing energy. For VE = 2.7 V (Fig. 2a), the bilayer IV-curve exhibits a maximum (appears bright), as the triple layer curve shows a minimum (appears dark), while the energy used in Fig. 2b (VE = 3.5 V) causes contrast inversion. We have taken IV-curves at every point of this field of view by recording LEEM images while sweeping VE (see Supplementary Video 1). From the number of minima in these IV-curves, we deduced the local graphene thickness experimentally, resulting in the spatial map in Fig. 2d. It shows enhanced graphene growth around the SiC step edges visible in Fig. 2a,b (indicated by black lines in d). The ability to accurately distinguish step edges as well as local thickness variations of layered materials is one of the exciting features of LEEM/LEEP.
We next use the rich structure of the graphene IV-curves to precisely measure local potential values. In such a LEEP experiment, we apply an in-plane bias voltage Vbias = −3 V over the sample as sketched in Fig. 1c. Next, we acquire LEEM images while sweeping VE (see Supplementary Video 2). Figure 3a shows a snapshot taken at VE = 5.4 V. The differences between the unbiased case (Fig. 2a,b) and the biased case (Fig. 3a) are immediately visible. While, for example, bilayer areas show the same intensity for the entire field of view in the unbiased situation, they appear darker on the left than on the right in the biased case. The latter is a direct result of the landing energy being larger at the left side than at the right side of the image, which causes an energy shift ΔV of the local IV-curves and thus a difference in the local image intensity. To quantify this effect, we have measured an IV-curve for every pixel in the image. Figure 3b shows three of these IV-curves, taken within the bilayer areas indicated in Fig. 3a. They all have a similar shape, featuring two minima, but are shifted in energy with respect to each other as well as to a reference IV-curve taken for the unbiased case. This shift ΔV is a direct measure for the local potential V(x, y). Note that the distinct shape of the IV-curves due to the resonant coupling to interlayer graphene states allows us to deduce this shift particularly precisely and thus enhances the resolution of the LEEP technique. Similar minima are expected for many layered quasi-2D crystals. In fact, most materials show clear structure in LEEM-IV19. The method to compute the shift using features in the IV-curve can therefore easily be extended to other quasi-2D systems. In particular, utilizing such features yields better results than taking the steep drop of the mirror mode transition as a measure for the local electrostatic potential (see Supplementary Note).
Results and Discussion
A complete potential map of the sample can now be produced by comparing the IV-curve at every pixel with a reference IV-curve taken at zero bias (Technical details of the algorithm used can be found in the Supplementary Methods: Shift Determination). Figure 4a presents a map of the local potential V(x, y), derived using the LEEP technique. The grainy structure of the image is mainly caused by residues of the resist used and is considered noise in the following. As expected for an Ohmic material like graphene, a voltage drop from left to right is apparent.
A potential profile along the indicated line (see Fig. 4b) show several remarkable features. First, the potential gradient and hence the resistivity within the triple layer is considerably lower than within the single layer. This is consistent with previous experimental reports and can be related to both the increased thickness and the protection of the bottom layers from doping from the ambient23. Second, we find no additional voltage drop at the macroscopic (5–10 nm high22) step edges of the SiC substrate below the triple layer graphene. Whereas these step edges are clearly resolved in LEEM images (cf. Fig. 3a) as thin dark lines within the triple layer area, they are barely visible in the potential map and the potential gradient in Fig. 4a,b. This indicates that no significant scattering occurs at these substrate steps that are covered with graphene in a carpet-like manner24. Remarkably, we do find a voltage drop of ~0.1 V at points where the graphene layer thickness changes. The latter is in agreement with scanning probe studies that relate this effect to a wave function mismatch between graphene of different layer number11,25,26.
One key factor in our experiment is LEEM’s ability to discriminate steps in the SiC substrate from a change in graphene layer number. This distinction is particularly challenging for other techniques, as graphene layer changes can coincide with SiC steps and are mainly found in the vicinity of macroscopic SiC step edges, where graphene growth is faster22. Consequently, standard conductivity experiments attributed the additional resistivity found to these macroscopic steps rather than to the graphene-induced steps27,28. Using LEEP, we find direct evidence that this conclusion is incorrect, demonstrating the added value of this local technique.
To quantify the energy resolution of LEEP and as a consistency check, we acquired potential maps for different external bias voltages Vbias. A linear relation between bias voltage and local potential is expected according to Ohm’s law. Figure 4c shows the measured local potential for the spot indicated in Fig. 4a as a function of Vbias. Deviations from the apparent linear trend yield an estimate for the uncertainty in the absolute value of the local potential of ~50 mV. Interestingly, a higher resolution can be obtained for the relative potential for a single bias voltage. We estimate errors in relative potential of 25 mV or 7 mV for monolayer or triple layer areas, respectively, from the noise in the linescan in Fig. 4b. This error is mainly caused by residues of the organic resist used during sample fabrication. These residues also limit the lateral resolution of our technique. If this issue could be overcome, we expect a resolution of LEEP of <5 nm given the resolution limit of the microscope of 1.4 nm29. Consequently, LEEP provides a complementary tool to existing scanning tunneling potentiometry (STP) set-ups that allow for sub-nanometer spatial resolution and microvolt potential resolution26,30. STP, however, relies on a charged, rigid probe in the vicinity of the sample that can influence the electron paths31,32 and local potentials33,34,35 and therefore, can create artifacts. Moreover, the scanning nature of STP leads to long acquisition times of multiple days per potential map30, thus posing high demands on sample and tip stability. With LEEP, in contrast, measuring a potential map takes less than a minute. The sample is almost not disturbed by the measurement as the LEEP image is formed with a probing beam current density of 5 pA/μm2. In addition, LEEP offers a wide field of view of up to 10 μm with the option to zoom in, thus making it the ideal tool for typical device dimensions.
In summary, we present a new method to analyze the laterally resolved conductivity of 2D systems. The LEEP technique introduced is based on the absorption of low-energy electrons resonant with unoccupied states in layered materials. It is fast and does not rely on an invasive, local probe. We demonstrate our technique by analyzing the conductance properties of few-layer graphene. We find an additional resistance contribution at points where the graphene layer thickness changes, while macroscopic steps in the SiC substrate do not perturb the current. We anticipate that LEEP is easily extended to other quasi-2D systems like van der Waals heterostructures and topological insulators. Moreover, given the recent developments in LEEM acquisition speed36, potentiometry of dynamic processes comes within range.
How to cite this article: Kautz, J. et al. Low-Energy Electron Potentiometry: Contactless Imaging of Charge Transport on the Nanoscale. Sci. Rep. 5, 13604; doi: 10.1038/srep13604 (2015).
Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat. Mater. 6, 183–191 (2007).
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Moore, J. Topological insulators: The next generation. Nat. Phys . 5, 378–380 (2009).
Qi, X.-L. & Zhang, S.-C. Topological insulators and superconductors. Rev. Mod. Phys. 83, 1057–1110 (2011).
Yang, F. et al. Spatial and Energy Distribution of Topological Edge States in Single Bi(111) Bilayer. Phys. Rev. Lett. 109, 016801 (2012).
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Zhang, Y., Tan, Y.-W., Stormer, H. L. & Kim, P. Experimental observation of the quantum Hall effect and Berry’s phase in graphene. Nature 438, 201–204 (2005).
Stander, N., Huard, B. & Goldhaber-Gordon, D. Evidence for Klein Tunneling in Graphene p-n Junctions. Phys. Rev. Lett. 102, 26807 (2009).
Martin, J. et al. Observation of electron–hole puddles in graphene using a scanning single-electron transistor. Nat. Phys . 4, 144–148 (2007).
Panchal, V., Pearce, R., Yakimova, R., Tzalenchuk, A. & Kazakova, O. Standardization of surface potential measurements of graphene domains. Sci. Rep . 3, 2597 (2013).
Ji, S.-H. et al. Atomic-scale transport in epitaxial graphene. Nat. Mater. 11, 114–119 (2012).
Nowack, K. C. et al. Imaging currents in HgTe quantum wells in the quantum spin Hall regime. Nat. Mater. 12, 787–791 (2013).
Schramm, S. M. et al. Low-energy electron microscopy and spectroscopy with ESCHER: Status and prospects. IBM J. Res. Dev. 55, 1:1–1:7 (2011).
Telieps, W. & Bauer, E. An analytical reflection and emission UHV surface electron microscope. Ultramicroscopy 17, 57–65 (1985).
Tromp, R. M. et al. A new aberration-corrected, energy-filtered LEEM/PEEM instrument. I. Principles and design. Ultramicroscopy 110, 852–861 (2010).
Tromp, R. M., Hannon, J. B., Wan, W., Berghaus, A. & Schaff, O. A new aberration-corrected, energy-filtered LEEM/PEEM instrument II. Operation and results. Ultramicroscopy 127, 25–39 (2013).
Bauer, E. Surface Microscopy with Low Energy Electrons . (Springer New York, 2014). 10.1007/978-1-4939-0935-3
Srivastava, N. et al. Low-energy electron reflectivity of graphene on copper and other substrates. Phys. Rev. B 87, 245414 (2013).
Flege, J. I. & Krasovskii, E. E. Intensity-voltage low-energy electron microscopy for functional materials characterization. Phys. Status Solidi - Rapid Res. Lett . 8, 463–477 (2014).
Anderson, M., Nakakura, C. Y., Saiz, K. F. & Kellogg, G. L. Imaging Oxide-Covered Doped Silicon Structures Using Low-Energy Electron Microscopy. MRS Proc. 1026, 1026–C15–03 (2007).
Hibino, H. et al. Microscopic thickness determination of thin graphite films formed on SiC from quantized oscillation in reflectivity of low-energy electrons. Phys. Rev. B 77, 075413 (2008).
Emtsev, K. V. et al. Towards wafer-size graphene layers by atmospheric pressure graphitization of silicon carbide. Nat. Mater. 8, 203–207 (2009).
Güneş, F. et al. Layer-by-layer doping of few-layer graphene film. ACS Nano 4, 4595–4600 (2010).
Lauffer, P., Emtsev, K. V, Graupner, R., Seyller, T. & Ley, L. Atomic and electronic structure of few-layer graphene on SiC(0001) studied with scanning tunneling microscopy and spectroscopy. Phys. Rev. B 77, 155426 (2008).
Clark, K. W. et al. Spatially Resolved Mapping of Electrical Conductivity across Individual Domain (Grain) Boundaries in Graphene. ACS Nano 7, 7956–7966 (2013).
Willke, P., Druga, T., Ulbrich, R. G., Schneider, M. A. & Wenderoth, M. Spatial extent of a Landauer residual-resistivity dipole in graphene quantified by scanning tunnelling potentiometry. Nat. Commun. 6, 6399 (2015).
Jouault, B. et al. Probing the electrical anisotropy of multilayer graphene on the Si face of 6H-SiC. Phys. Rev. B 82, 085438 (2010).
Weingart, S. et al. Low-temperature ballistic transport in nanoscale epitaxial graphene cross junctions. Appl. Phys. Lett. 95, 262101 (2009).
Schramm, S. M. PhD dissertation (Leiden University): Imaging with Aberration-Corrected Low Energy Electron Microscopy. (2013).
Druga, T., Wenderoth, M., Homoth, J., Schneider, M. A. & Ulbrich, R. G. A versatile high resolution scanning tunneling potentiometry implementation. Rev. Sci. Instrum . 81, 083704 (2010).
Aidala, K. E. et al. Imaging magnetic focusing of coherent electron waves. Nat. Phys . 3, 464–468 (2007).
Kozikov, A. A. et al. Interference of electrons in backscattering through a quantum point contact. New J. Phys. 15, 013056 (2013).
McEllistrem, M., Haase, G., Chen, D. & Hamers, R. J. Electrostatic sample-tip interactions in the scanning tunneling microscope. Phys. Rev. Lett. 70, 2471–2474 (1993).
Nagaoka, K., Comstock, M. J., Hammack, A. & Crommie, M. F. Observation of spatially inhomogeneous electronic structure of Si(100) using scanning tunneling spectroscopy. Phys. Rev. B 71, 121304 (2005).
Feenstra, R. M., Dong, Y., Semtsiv, M. P. & Masselink, W. T. Influence of tip-induced band bending on tunnelling spectra of semiconductor surfaces. Nanotechnology 18, 044015 (2007).
Van Gastel, R. et al. Medipix 2 detector applied to low energy electron microscopy. Ultramicroscopy 110, 33–35 (2009).
We are grateful to Raymond Koehler, Leendert Prevo, Marcel Hesselberth and Daan Boltje for technical assistance and to Maria Mytiliniou, Alexander van der Torren, Daniël Geelen, Aniket Thete, Jan van Ruitenbeek and Jan Aarts for useful discussions. This work was supported by the Netherlands Organization for Scientific Research (NWO) via an NWO-Groot grant (“ESCHER”) and a VIDI grant (#680-47-502, SJvdM), by the FOM foundation via the “Physics in 1D” program and by the Sonderforschungsbereich 953 “Synthetic carbon allotropes”, funded by Deutsche Forschungsgemeinschaft.
The authors declare no competing financial interests.
About this article
Cite this article
Kautz, J., Jobst, J., Sorger, C. et al. Low-Energy Electron Potentiometry: Contactless Imaging of Charge Transport on the Nanoscale. Sci Rep 5, 13604 (2015). https://doi.org/10.1038/srep13604
Spatial inhomogeneity and temporal dynamics of a 2D electron gas in interaction with a 2D adatom gas
Scientific Reports (2017)
Nature Communications (2017)
Quantifying electronic band interactions in van der Waals materials using angle-resolved reflected-electron spectroscopy
Nature Communications (2016)