## Abstract

We present results from first-principles calculations on silane (SiH_{4}) under pressure. We find that a three dimensional *P*-3 structure becomes the most stable phase above 241 GPa. A prominent structural feature, which separates the *P*-3 structure from previously observed/predicted SiH_{4} structures, is that a fraction of hydrogen leaves the Si-H bonding environment and forms segregated H_{2} units. The H_{2} units are sparsely populated in the system and intercalated with a polymeric Si-H framework. Calculations of enthalpy of formation suggest that the *P*-3 structure is against the decomposition into Si-H binaries and/or the elemental crystals. Structural stability of the *P*-3 structure is attributed to the electron-deficient multicenter Si-H-Si interactions when neighboring silicon atoms are linked together through a common hydrogen atom. Within the multicenter bonds, electrons are delocalized and this leads to a metallic state, possibly also a superconducting state, for SiH_{4}. An interesting outcome of the present study is that the enthalpy sum of SiH_{4} (*P*-3 structure) and Si (fcc structure) appears to be lower than the enthalpy of disilane (Si_{2}H_{6}) between 200 and 300 GPa (for all previously predicted crystalline forms of Si_{2}H_{6}), which calls for a revisit of the stability of Si_{2}H_{6} under high pressure.

## Introduction

The pursuit of metallic hydrogen and its high-temperature superconductivity is of great interest to the condensed-matter community^{1,2}. Producing metallic hydrogen in bulk, however, requires a significant static pressure that exceeds the limit of current experimental capacities. Alternative approaches may be possible, as suggested by Ashcroft^{3}, that some simple hydrides, with the average valence density comparable to pure hydrogen, could become metallic at significantly reduced pressures. Similar to pure hydrogen, the metallic states of these hydrides should also have large band overlapping, high Debye temperature and strong electron-phononcoupling (EPC) that can all lead to phonon-mediated superconductivity. According to the Goldhammer-Herzfeld criterion, Group-IV hydrides, such as methane (CH_{4}) and silane (SiH_{4}), are potential candidates for this behavior^{3}.

At ambient temperature, SiH_{4} solidifies at around 1.7 GPa into a four-fold molecular crystal. Upon increasing the pressure, one expects higher coordinatedstructures of SiH_{4} to become stable, by virtue of multicenter bonding. Previously, several high-pressure structures of SiH_{4} have been predicted by different groups, with the metallization pressure estimated from as low as 20 GPa to above 220 GPa^{4,5,6,7,8}. Some of the predicted phases have been suggested to be superconducting, as well, with the estimate of *T*_{c} ~ 16 K to 260 K. Experimental determinations of high-pressure structures of SiH_{4} have been carried out using various techniques. Degtyareva*et al.* observed from powder x-ray diffraction patterns that SiH_{4} remains four-fold to around 25 GPa and likely transforms to a new phase at higher pressures^{9}. Chen *et al.* observed that SiH_{4} sample turns opaque above 27 GPa, which, in combination with measured Raman and IR reflectivity, led to the suggestion that SiH_{4} metallizes near 60 GPa^{10}. Eremets *et al.* later reported the metallization of SiH_{4} to occur between 50 and 65 GPa based on electrical resistance measurement and also found this phase to be superconducting(maximum *T*_{c} ~ 17.5 K)^{11}. The crystal structure of the metallic phase (*P*6_{3}), however, was unusual: its volume shrinks nearly 60% from its precursor the *P*2_{1}/*c* structure at the phase transition. According to Degtyareva *et al.*, this implies that the observed metallization actually arisesfrom contaminations in the system rather than from the SiH_{4} sample^{12}. This was supported by the x-ray diffractionstudy of Hanfland *et al.*^{13} in which SiH4 was found to undergo pressure-inducedamorphization at pressures above 60 GPa recrystallizing at 90 GPainto an insulating*I*4_{1}/astructure original proposed from *ab initio* calculations by Pickard and Needs^{14,15}. At about the same time, Strobel *et al.* reported a comprehensive experimental study which confirmed Hanfland *et al.*’s observations^{16}. Strobel *et al.* observed that SiH_{4} darkens above ~50 GPa and attributed it to a partial loss of crystallinity. Above 100 GPa, SiH_{4} recrystallizes intothe *I*4_{1}/*a* (or *I*-42*d*) structure and remainsin this structure to at least 150 GPa.

In addition to pure silane, the mixtures of silane and molecular hydrogen have also been investigated. In mixtures, hydrogen molecules are perturbed by SiH_{4}. Such intermolecular interactions can destabilize the covalent bonds in H_{2}, showing promise of obtaining a metallic state at moderate pressures. Almost concurrently, Strobel *et al.*^{17} and Wang *et al.*^{18} reported the synthesis of novel SiH_{4}–H_{2}complexes under high-pressure conditions. Using power X-ray diffraction, Strobel *et al.* observedthe formation of a stoichiometric SiH_{4}(H_{2})_{2} crystal near 7 GPaand identified its structure as a cubic *F*-43*m* structure. Using Raman spectroscopy, Wang *et al.* studied the behavior of SiH_{4}–H_{2} fluids and established a binary eutectic point at 72 mol% H_{2} and 6.1 GPa. Above the eutectic point the fluid crystallizes in a solid solution. The SiH_{4}–H_{2} phase diagrams revealed in both studies are very similar. Detailed electronic structures and chemical bonding of the SiH_{4}–H_{2} mixtures have been subsequently examined through the use of first-principles methods^{19,20,21,22,23}.

While recent studies revealed a great deal of information on the behavior of SiH_{4} under pressure, the jury is still out on the initial proposal. As the research progresses, the reported metallization of SiH_{4} near 55 GPa is now facing challenges. Theory suggests that SiH_{4} reaches a metallic state at a much greater pressure (220 GPa), through a phase transition to a *Pbcn* structure^{8}. Motivated by the significant interests in this subject, in the present study we employ theoretical structural searches and property predictions to investigate SiH_{4} in the post-*I*4_{1}/*a* region. We systematically searched for stable structures of SiH_{4} at pressures above 200 GPa, using a heuristic algorithm based on particle swarm optimization (calypso method)^{24,25}. We predict a new structure of SiH_{4} above 241 GPa. This structure (*P*-3) is computed to be metallic and perhaps also superconducting as inferred from the electron-phonon coupling. Our prediction helps to address the phase diagram of SiH_{4} at high pressure; while its significance goes beyond. Disilane (Si_{2}H_{6}) is the next member in silicon hydride series (Si_{n}H_{2n+2}), which was suggested in theory to become stable under pressure, stable with respect to decompositions into other binaries and/or the elemental crystals^{26}. Using similar argument as for SiH_{4}, solid Si_{2}H_{6} was predicted to be metallic and superconducting. With the addition of the *P*-3 structure in the SiH_{4} phase diagram, however, according to our convex hull calculations all previously predicted Si_{2}H_{6} structures appear to be thermodynamically unstable with respect to the decomposition of Si and SiH_{4} to at least 300 GPa. This therefore suggests a revisit of previous studies on solid Si_{2}H_{6} and a reconsidering of its very stability at high pressure.

## Methods

Our structure prediction is based on a global minimum search of the enthalpy surfaces obtained by *ab initio* calculations at a constant pressure, through CALYPSO (crystal structure analysis by particle swarm optimization) methodology and its same-name code^{24,25}. For silane, disilane, silylene and lilicane, structure predictions with upto 6 formula units (f.u.) in the simulation cell were performed at 200 and 300 GPa, respectively, however, for the complex Si_{5}H_{18}, simulation cells containing only 1 f.u. were considered. The *ab initio* calculations were performed using density functional theory^{27} within the Perdew-Burke-Ernzerhof (PBE) parameterization^{28} of the generalized gradient approximation (GGA) as implemented in the Vienna *ab initio* simulation package (VASP) code^{29}. The all-electron projector-augmented wave (PAW) method^{30} was adopted with 3*s*^{2}3*p*^{2} and 1*s*^{1} as valence electrons for Si and H atoms, respectively. Planewave energy cutoffs of 500 eV and 700 eV and uniform Monkhorst-Pack (MP) meshes^{31} for Brillouin zone (BZ) sampling with resolutions of 2π × 0.06 Å^{−1} and 2π × 0.03 Å^{−1} were employed in the structure predictions and subsequent calculations (e.g. of thermodynamic stability), respectively. The errors in the enthalpy differences of the structures studied in the structure predictions and the subsequent calculations were found to be in the order of 1 meV/atom and less than 1 meV/atom, respectively. The contribution of the electronic entropy to the enthalpy differences aroused by the MP method is less than 0.1 meV/atom and negligible. The phonon density of states was calculated in harmonic approximation by the finite displacement method^{32} as implemented in the PHONOPY program^{33} and the vibrational free energy was estimated therefrom^{34}. The underlying force constants were calculated in 2 × 2 × 1 supercells with 4 × 4 × 5 MP meshes for BZ sampling for the *P*-3 and *Pbcn* structures and a 4 × 4 × 4 MP mesh for the *I*4_{1}/*a* structure. Electron-phonon coupling (EPC) calculations were carried out by using density functional perturbation theory^{35} as implemented in the QUANTUM ESPRESSO package^{36} with a kinetic energy cutoff of 80 Ry. A 16 × 16 × 12 *q*-mesh in the first BZ was used with Gaussians of width of 0.05 Ry in the EPC calculations.

## Results and Discussion

In Fig. 1, the calculated enthalpies (*H* = *E* + *pV*) of the candidate structures of SiH_{4} are compared between 200 to 300 GPa. In this pressure range, our structural searches successfully predicted a new structure with the *P*-3 space group, as well as revealed the previously observed/suggested structures, *i.e.*, structures with *P*2_{1}/*c*, *Fdd*2, *I*4_{1}/*a*, *C*2/*c* and *Pbcn*space groups^{8,9,14}. The experimentally identified *I*4_{1}/*a* structure^{11,14,16} is calculated to be the most stable phase at the low-pressure end. The *I*4_{1}/*a* to *Pbcn* structural transformation is calculated to occur at about 225 GPa, in a good agreement with previous study^{8}. Near 241 GPa, the newly predicted *P*-3 structure becomes the most stable phase of SiH_{4}. Enthalpy of the *P*-3 structure is constantly lower than that of the *C*2/*c* structure^{14}, by more than 0.08 eV per formula unit. As well, we predict a metastable *C*2/*m* structure that also appears to be more stable than the *C*2/*c* structure. The optimized structural parameters of the *P*-3 and *C*2/*m* structures are listed in Table 1. To account for the temperature effects, we estimated the vibrational free energies (at 300 K) for the *I*4_{1}/*a*, *Pbcn* and *P*-3 structures at four different pressures, using a harmonic method^{34} (Table 2). As shown in the inset of Fig. 1, the inclusion of the vibrational free energies does not alter the phase transition sequence, but shift down the two transition points in pressure (see explanation later). It is worth noting that the small proton mass may induce significant quantum nuclear effects, which can deviate the system from a harmonic description and therefore, shift the two transition pressures further. A rigorous study of this should turn to explicit calculation of the free energy with anharmonic contributions from both the thermal and the quantum nuclear effects includedx^{37}. This could be achieved by performing *ab initio* path-integral molecular dynamics simulations^{38}, however, which is beyond the computational load we can afford nowadays. Here, we just speculate that the temperature effects will further stabilize the *P*-3 structure with respect to the other two structures. Moreover, the appearance of a molecular bonding environment in the *P*-3 structure (as will be discussed below) suggests that the van der Waals (vdW) interaction may play an important role in the phase transitions. To evaluate this effect, the enthalpies of *I*4_{1}/*a*, *Pbcn* and *P*-3 structureshave been recalculated usingoptB88-vdW functional^{39,40,41,42}. The results indicate that the vdW interaction does not change the phase transition sequence, but increase the transition pressures of *I*4_{1}/*a* → *Pbcn* and *Pbcn* → *P*-3 from 225 and 241GPa to 242 and 285 GPa, respectively.

The *P*-3 structure is shown in Fig. 2(a,b) in two different views. Its unit cell contains 5 SiH_{4} formula units. The extended structure can be described as a polymeric Si-H framework intercalated by quasi-hexagonal layers of H_{2} units. Isolated H_{2} units in Group-IV hydrides are not entirely new – previous studies^{43,44,45,46,47,48} suggested them to exist in solid germane (GeH_{4}), stannane (SnH_{4}) and plumbane (PbH_{4}). In SiH_{4}, the H_{2} units are sparsely populated with negligible intermolecular interactions. This is in contrast to heavier Group-IV hydrides in which the H_{2} units are strongly correlated with a tendency for H_{2} – H_{2} pairing. To analyze the bonding environment, we employed the electron localization function (ELF)^{49} as a measure of relative electron localization with respect to a uniform electron gas. The ELF value represents a probability (0 to 1), with large values identifying places in the structure where electrons of opposite spins present, e.g., in cores, bonds, or lone pairs. As Fig. 2(c) shows, the intramolecular regions in the H_{2} units have a very large ELF value (close to 1) resulted from a high degree of electron paring. In fact, the ELF map of the H_{2} units is consistent to that of a gas-phase H_{2} molecule, suggesting that these H_{2} units are inact. This conclusion is resonating with the exceptionally short H-H distance in the H_{2} units, *i.e.*, 0.75 Å (calculated at 300 GPa), not so different from that of a H_{2} molecule.

In the Si-H framework, each silicon atom is coordinated to 12 nearest neighbor hydrogen atoms, which are then bridged to other silicon atoms. Overall, a third of the bridging hydrogen atoms are shared by 4 silicon atoms and the rest are shared by 3, yielding a Si_{5}H_{18} stoichiometry. Such Si-H geometry goes far beyond the ubiquitous four-fold coordination of Group-IV elements and on the face of it, one sees the enigma of silicon atoms forming more bonds (12) than the number that seems to be sufficient for their available valence electrons (4). This ‘forbidden’ increment of crystal coordination, however, is a commonplace in materials under high pressure and can be explained by the schemes of electron-deficient multicenter bonding^{50}. A quantum Atoms in Molecules (AIM) analysis^{51} (Table 3) reveals that the bridging hydrogen receive ~0.7 e^{−} per atom from neighboring silicon (which is also seen in Fig. 2(c)). In contrast, the H_{2} units almost have no charge transfer from/to the Si-H framework. At this point, silicon atoms have much reduced *s*/*p* mixing in its delocalized multicenter bonding, compared with that in molecular SiH_{4} (which favors definite coordination geometry, as we know). A similar electron-deficient scenario is also encountered in the other two candidate structures, *I*4_{1}/*a* and *Pbcn*, but the difference is that in these two structures the bridging hydrogen atoms are shared by only 2 silicon atoms^{8,14}. Each silicon atom is coordinated to 8 hydrogen atoms; pairs of which bridge to four neighboring silicon atoms, forming two three-center-two-electron (3c-2e) bonds. This bonding arrangement is a prototypical electron-deficient geometry that is commonly known for the diborane molecule (B_{2}H_{6})^{52}.

Two interesting observations arise from a comparison of the *P*-3 structure to the *I*4_{1}/*a* and *Pbcn*structures. At first, the *P*-3 structure has higher coordination geometry which corresponds to a smaller volume. For example, at 250 GPa, the calculated volume for the *I*4_{1}/*a, Pbcn*and *P-*3 structuresgradually decreases in a sequence of 13.59 Å^{3}/f.u., 13.43 Å^{3}/f.u. and 13.17 Å^{3}/f.u., respectively. Evidently, the *P*-3 structure would have the smallest *p*V work, which provides energetic advantages. Secondly, in the *P*-3 structure the bridging hydrogen atoms are constrained by more silicon atoms. This yields reduced frequencies for the Si…H…Si bending modes in the mid-frequency range (20–70 THz, at 150 GPa), which is the main reason why the vibrational free energy of the *P*-3 structure is constantly lower than the other two structures (Table 2). In the translational region, *i.e*., below 20 THz, the vibrational free energy is mainly resulted from Si lattice modes, so it is very similar for all three structures. The *P*-3 structure also has high-frequency H-H vibron modes above 100 THz. These modes however do not have notable contributions to the vibrational free energy due to their low density of states. At 150 GPa, for example, the H-H vibrons only contribute 0.04 eV/f.u. to the vibrational free energy of the *P*-3 structure.

An important issue is worthy of investigation at this point. The appearance of the H_{2} units in the *P*-3 structure, as well as the short H-H contact, seems to indicate a trend of segregation toward the Si_{5}H_{18} + H_{2} limit. As crystalline SiH_{4} is known to decompose between 50 ~ 100 GPa^{16}, it is not unreasonable to speculate it to decompose again at higher pressures. To this end, we examined the phase stability of the *P*-3 structure with respect to the decompositions into other possible Si-H binaries and H_{2}. Four stoichiometries were used for the binaries, namely, Si_{5}H_{18}, Si_{2}H_{6} (disilane), SiH_{2} (silylene) and SiH (silicane). To find the most stable structure of these stoichiometries, we performed additional structure searches at 200 and 300 GPa. The lowest-enthalpy structure that arises from the search was employed as the candidate for each stoichiometry. In Fig. 3, the calculated enthalpy of formation (△*H*_{f}, with respect to elemental crystal of H_{2} and Si) is shown for all four stoichiometries. Here a negative △*H*_{f} means that the binary phase is more stable than the elemental crystals, while the convex hull of the △*H*_{f} values (solid lines) connects the stable phases; in this case they are H_{2}, Si and SiH_{4}. Clearly, SiH_{4} (*P*-3 structure) is the most stable Si-H stoichiometry at 200 and 300 GPa. The △*H*_{f} of the *P*-3 structure relative to Si_{5}H_{18} and H_{2} (*Cmca*12^{53}) structure is negative which confirms its stabilities.

It is perhaps not surprising that Si_{5}H_{18}, SiH_{2} and SiH crystals are predicted to be less stable than SiH_{4}, since these species are either reactive intermediates or not known to exist experimentally. A significant finding is that the Si_{2}H_{6} crystal appears to be unstable as well, with respect to the decomposition of Si + SiH_{4} crystal. To our best knowledge, Si_{2}H_{6} is the only known higher silanes that can readily be prepared in laboratory, usually by the reaction of silicon chloride (Si_{2}Cl_{6}) with lithium aluminum hydride (LiAlH_{4}). Due to the weaker Si-Si bond (226 kJ mol^{−1}), Si_{2}H_{6} decomposes slowly even at room temperature^{54}. On the other hand, previous theoretical studiessuggest that the stability of Si_{2}H_{6} can be enhanced by applying pressure^{26,55}. A series of crystalline Si_{2}H_{6} polymorphs, with the space group *Cmcm*, *C*2/*c* and *Pm*-3*m*, have been predicted to be thermodynamically stable and superconducting at pressures above 190 GPa. On the contrary, new calculations using the *P*-3 structure as the most stable structure of SiH_{4} show that these Si_{2}H_{6} polymorphs would all have positive △*H*_{f}with respect to the crystal of SiH_{4} + Si between 200 and 300 GPa (Table 4). This outcome therefore suggests a revisit on the stability of crystal Si_{2}H_{6} at high pressures. It should be noted here that the choices of the Si-H binaries as the decomposition products are based upon the known Si-H stoichiometries observed at ambient pressure. It is possible that other Si-H binaries, in additional to what have been considered here, can be stabilized at high pressure.

It is worth noting that another recent theoretical study^{56} reports an interesting result on the disproportionation of GeH_{4} at high pressure. In this study, zero-point energies were estimated using the harmonic approximation, which is very similar to the approach adopted in the present study. Under this consideration, a new stoichiometry for the Ge-H binaries, namely GeH_{3}, is predicted to become energetically stable with respect to the decomposition of elemental crystals of Ge and H_{2} near 175 GPa. The GeH_{4}, on the hand, was suggested to be unstable with respect to the decomposition of GeH_{3} and H_{2}. These results are distinctly different for that of the present study in which the SiH_{4} is suggested to be the most stable stoichiometry for the Si-H binaries at high pressures. Experimentally, SiH_{4} is the most stable binary in its hydride series (Si_{n}H_{2n+2}) at ambient pressure^{54}. At high pressure, SiH_{4} decomposes near 50 GPa but recrystallizes above 100 GPa and remains stable to at least 192 GPa, the highest pressure attempted in the experiments^{11,16}. The *P*-3 structure is predicted to become stable near 177 GPa (with harmonic zero-point corrections), which is well within the experimental stability range for SiH_{4}. The study of GeH_{3} on the other hand indicates that there are maybe new stoichiometries for this group, perhaps unprecedented at ambient pressures, may become stable at high pressures and this awaits to be discovered in future experiments.

Figure 4(a,b) show the calculated electronic band structure and projected density of states (DOS) for the *P*-3 structure at 300 GPa. It is of considerable interest that this structure is predicted to be metallic. The DOS reveals a pseudogap developed below the Fermi energy (*E*_{F}). Similar pseudogaps were also found in calculations on high-pressure GeH_{4} and SnH_{4} but not on PbH_{4}^{44,45,46,47,48}. This suggests that the electronic structure of the *P*-3 structure is not free-electron-like. Since in this case the Fermi level lies in the pseudogap, the DOS at the *E*_{F} in the *P*-3 structure is substantially lower than the value in a free electron gas (, where *n* is the density of electrons), which limits the possibility of achieving high superconductivity. It perhaps merits mention that the DOS characteristics of the *P*-3 structure is similar to that of the AlH_{3} at high pressure^{57}. Since Al has one less electron than Si, the Fermi level of AlH_{3} lies in the lower reach of the pseudogap which also results in a low DOS value and ultimately non-superconducting behaviors^{58}. In Fig. 4b, hydrogen atoms (mostly bridging ones) contribute to the DOS throughout the entire energy range. This indicates that the hydrogen and silicon electronic states are strongly mixed in the Si-H framework. If the states near the *E*_{F} can be effectively coupled with the phonon modes, especially the high-frequency ones from hydrogen vibrons, a credible superconductivity can be expected^{3}. However, the H_{2} units in the *P-*3 structure are populated sparsely in the lattice so their DOS and phonon DOS are both very low (Figs 4b,d), compared with their counterparts in SnH_{4}, GeH_{4} and PbH_{4}. We therefore do not anticipate exceptional electron-phonon coupling in the *P*-3 structure at this point.

Figure 4(c,d) show the calculated phonon dispersion relations and phonon DOS for the *P*-3 structure at 300 GPa. The absence of imaginary frequency modes suggests that this structure is mechanically stable. An outstanding feature of the ‘H_{2}’ intercalation in the structure is that the vibrational modes are divided into subsets in frequency. The H_{2} pairs occupy primarily two subsets; one induced by roton modes around 25 THz and the other induced vibron modes around 118 THz. In these two subsets, the contribution from the Si-H framework is minor, consistent with the fact that the H_{2} pairs are inactive. The Si lattice modes dominate the low-frequency subset below 20 THz, while the bridging hydrogen atoms are in the intermediate subset between 30 and 70 THz.

A brief discussion on the possibility of phonon-mediated superconductivity in the *P*-3 structure is of interest. The methodology was based on an extension of the BCS model in which the attractive, electron-phonon interaction for each phonon mode is treated explicitly. The strength of this interaction is characterized by the electron-phonon coupling parameterλ incorporating the contributions from all participating phonon modes. In Fig. 5, we present the Eliashberg phonon spectral function α^{2}*F*(ω) and the integrated λ (ω) () as a function of frequency ω at 300 GPa. The overall integrated λ is 0.63, which is a moderate value for hydrogen-rich materials and comparable to the zero-pressure value for MgB_{2}^{59,60,61}. The Si lattice modes contribute about 0.23 to the total λ. While the low frequencies of the lattice modes were considered as a disadvantage of attaining superconductivity, their reasonably strong EPC compensates it. The intermediate-frequency H modes contribute 0.36 while the high-frequency vibron modes only contribute 0.04. The logarithmic average of the phonon frequency ω_{log} is obtained as 1320 K. The electron-screened repulsive interaction is represented by the Coulomb pseudopotential μ^{*}. For typical phonon-mediated superconductors, the values of μ^{*} between 0.1–0.13 are generally considered as reasonable^{3}. The superconducting critical temperature *T*_{c} is estimated from the McMillan formula^{62} along with the Allen-Dynes correction ()^{63}, using an empirical value of μ* = 0.12. The estimated *T*_{c} of *P-*3 structure turns out to be 32 K at 300 GPa. A slightly improved estimate of the *T*_{c} of 35.1 K is made by directly solving the Eliashberg equations^{2} with the calculated α^{2}*F*(ω), using the methodology previously implemented by us^{64}. We note that these two estimates of *T*_{c} are both based on isotropic gap equations and an empirical value of μ*, which may not be adequate depending on the mechanism of the electron-phonon coupling in SiH_{4}. A more accurate estimate of the *T*_{c} may be made using a fully anisotropic treatment of the gap equations, which encourages future study in this direction. Moreover, it should be pointed out that the quantum nuclear effects may deviate the system from a harmonic description and alter the estimated *T*_{c}. As manifested by a study of AlH_{3}, anharmonicity of atomic motions can cause renormalization of the vibrational modes and suppress the superconductivity^{58}, On the other hand, however, anharmonic vibrations were found to enhance the electron–phonon matrix elements, as in the case of disordered materials^{65}.

## Conclusions

We present a theoretical study of high-pressure phase transitions and the metallization of crystalline silane (SiH_{4}). A new polymorph of SiH_{4} (space group: *P*-3) was predicted from structure searches using a heuristic algorithm based on particle swarm optimization (calypso methodology). This new phase becomes thermodynamically stable at pressures above 241 GPa, replacing the previous suggested *C*2/*c* structure in the phase diagram. The *P*-3 structure is calculated to be metallic and also superconducting with an estimated *T*_{c} of 32 K at 300 GPa. A unique structure feature of the *P*-3 structure is the presence of H_{2} units that are intercalated with the Si-H framework. Electron-deficient multicenter bonding along the Si…H…Si connections results in the delocalization of valence electrons and accounts for the increment of crystal coordination in the Si-H framework. Calculations of enthalpy of formation suggest that the *P*-3 structure is stable with respective to the decomposition to other Si-H binaries and/or the elemental crystals.

## Additional Information

**How to cite this article**: Cui, W. *et al.* Hydrogen segregation and its roles in structural stability and metallization: silane under pressure. *Sci. Rep.* **5**, 13039; doi: 10.1038/srep13039 (2015).

## References

Mao, H. & Hemley, R. Ultrahigh-pressure transitions in solid hydrogen. Rev. Mod. Phys. 66, 671–692 (1994).

McMahon, J. M., Morales, M. A., Pierleoni, C. & Ceperley, D. M. The properties of hydrogen and helium under extreme conditions. Rev. Mod. Phys. 84, 1607–1653 (2012).

Ashcroft, N. Hydrogen Dominant Metallic Alloys: High Temperature Superconductors? Phys. Rev. Lett. 92, 187002 (2004).

Feng, J. et al. Structures and Potential Superconductivity in SiH4 at High Pressure: En Route to ‘Metallic Hydrogen’. Phys. Rev. Lett. 96, 017006 (2006).

Yao, Y., Tse, J. S., Ma, Y. & Tanaka, K. Superconductivity in high-pressure SiH4 . Europhys. Lett. 78, 37003 (2007).

Chen, X. et al. Superconducting Behavior in Compressed Solid SiH4 with a Layered Structure. Phys. Rev. Lett. 101, 077002 (2008).

Kim, D. Y. et al. Crystal structure of the pressure-induced metallic phase of SiH4 from ab initio theory. Proc. Natl. Acad. Sci. USA 105, 16454–16459 (2008).

Martinez-Canales, M. et al. Novel Structures and Superconductivity of Silane under Pressure. Phys. Rev. Lett. 102, 087005 (2009).

Degtyareva, O. et al. Crystal structure of SiH4 at high pressure. Phys. Rev. B 76, 064123 (2007).

Chen, X. et al. Pressure-induced metallization of silane. Proc. Natl. Acad. Sci. USA 105, 20–23 (2008).

Eremets, M. I., Trojan, I. A., Medvedev, S. A., Tse, J. S. & Yao, Y. Superconductivity in hydrogen dominant materials: silane. Science 319, 1506–1509 (2008).

Degtyareva, O., Proctor, J. E., Guillaume, C. L., Gregoryanz, E. & Hanfland, M. Formation of transition metal hydrides at high pressures. Solid State Commun. 149, 1583–1586 (2009).

Hanfland, M., Proctor, J. E., Guillaume, C. L., Degtyareva, O. & Gregoryanz, E. High-Pressure Synthesis, Amorphization and Decomposition of Silane. Phys. Rev. Lett. 106, 095503 (2011).

Pickard, C. & Needs, R. High-Pressure Phases of Silane. Phys. Rev. Lett. 97, 045504 (2006).

Pickard, C. J. & Needs, R. J. Structures at high pressure from random searching. Phys. status solidi 246, 536–540 (2009).

Strobel, T. A. et al. High-pressure study of silane to 150 GPa. Phys. Rev. B 83, 144102 (2011).

Strobel, T. a., Somayazulu, M. & Hemley, R. J. Novel pressure-induced interactions in silane-hydrogen. Phys. Rev. Lett. 103, 2–5 (2009).

Wang, S., Mao, H., Chen, X.-J. & Mao, W. L. High pressure chemistry in the H2-SiH4 system. Proc. Natl. Acad. Sci. USA 106, 14763–14767 (2009).

Chen, X.-Q., Wang, S., Mao, W. L. & Fu, C. L. Pressure-induced behavior of the hydrogen-dominant compound SiH4 (H2)2 from first-principles calculations. Phys. Rev. B 82, 104115 (2010).

Li, Y. et al. Superconductivity at approximately 100 K in dense SiH4(H2)2 predicted by first principles. Proc. Natl. Acad. Sci. USA 107, 15708–15711 (2010).

Michel, K., Liu, Y. & Ozolins, V. Atomic structure and SiH4 -H2 interactions of SiH4 (H2)2 from first principles. Phys. Rev. B 82, 174103 (2010).

Yao, Y. & Klug, D. D. Silane plus molecular hydrogen as a possible pathway to metallic hydrogen. Proc. Natl. Acad. Sci. USA 107, 20893–20898 (2010).

Yim, W. L., Tse, J. S. & Iitaka, T. Pressure-induced intermolecular interactions in crystalline silane-hydrogen. Phys. Rev. Lett. 105, 1–4 (2010).

Wang, Y., Lv, J., Zhu, L. & Ma, Y. Crystal structure prediction via particle-swarm optimization. Phys. Rev. B 82, 094116 (2010).

Wang, Y., Lv, J., Zhu, L. & Ma, Y. CALYPSO: A method for crystal structure prediction. Comput. Phys. Commun. 183, 2063–2070 (2012).

Flores-Livas, J. A. et al. High-Pressure Structures of Disilane and Their Superconducting Properties. Phys. Rev. Lett. 108, 117004 (2012).

Kohn, W. & Sham, L. Self-consistent equations including exchange and correlation effects. Phys. Rev. 140, A1133 (1965).

Perdew, J., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).

Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).

Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758 (1999).

J., M. H. & D., P. J. Special points for Brillonin-zone integrations. Phys. Rev. B 13, 5188 (1976).

Parlinski, K., Li, Z. & Kawazoe, Y. First-Principles Determination of the Soft Mode in Cubic ZrO2 . Phys. Rev. Lett. 78, 4063–4066 (1997).

Togo, A., Oba, F. & Tanaka, I. First-principles calculations of the ferroelastic transition between rutile-type and CaCl2-type SiO2 at high pressures. Phys. Rev. B 78, 134106 (2008).

Pavone, P., Baroni, S. & de Gironcoli, S. α↔β phase transition in tin: A theoretical study based on density-functional perturbation theory. Phys. Rev. B 57, 10421–10423 (1998).

Baroni, S., de Gironcoli, S. & Dal Corso, A. Phonons and related crystal properties from density-functional perturbation theory. Rev. Mod. Phys. 73, 515–562 (2001).

Giannozzi, P. et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys. Condens. Matter 21, 395502 (2009).

Chen, J., Ren, X., Li, X.-Z., Alfè, D. & Wang, E. On the room-temperature phase diagram of high pressure hydrogen: An ab initio molecular dynamics perspective and a diffusion Monte Carlo study. J. Chem. Phys. 141, 24501 (2014).

Li, X.-Z. et al. Classical and quantum ordering of protons in cold solid hydrogen under megabar pressures. J. Phys. Condens. Matter 25, 85402 (2013).

Dion, M., Rydberg, H., Schröder, E., Langreth, D. C. & Lundqvist, B. I. Van der Waals Density Functional for General Geometries. Phys. Rev. Lett. 92, 246401 (2004).

Klimeš, J., Bowler, D. R. & Michaelides, A. Van der Waals density functionals applied to solids. Phys. Rev. B 83, 195131 (2011).

Román-Pérez, G. & Soler, J. M. Efficient Implementation of a van der Waals Density Functional: Application to Double-Wall Carbon Nanotubes. Phys. Rev. Lett. 103, 096102 (2009).

Klimeš, J., Bowler, D. R. & Michaelides, A. Chemical accuracy for the van der Waals density functional. J. Phys. Condens. Matter 22, 022201 (2010).

Martinez-Canales, M., Bergara, A., Feng, J. & Grochala, W. Pressure induced metallization of Germane. J. Phys. Chem. Solids 67, 2095–2099 (2006).

Gao, G. et al. Superconducting High Pressure Phase of Germane. Phys. Rev. Lett. 101, 107002 (2008).

Tse, J., Yao, Y. & Tanaka, K. Novel Superconductivity in Metallic SnH4 under High Pressure. Phys. Rev. Lett. 98, 117004 (2007).

Gao, G. et al. High-pressure crystal structures and superconductivity of Stannane (SnH4). Proc. Natl. Acad. Sci. USA 107, 1317–1320 (2010).

Gonzalez-Morelos, P., Hoffmann, R. & Ashcroft, N. W. Segregation into layers: a general problem for structural instability under pressure, exemplified by SnH4 . Chemphyschem 11, 3105–3112 (2010).

Zaleski-Ejgierd, P., Hoffmann, R. & Ashcroft, N. W. High Pressure Stabilization and Emergent Forms of PbH4 . Phys. Rev. Lett. 107, 037002 (2011).

Becke, A. D. & Edgecombe, K. E. A simple measure of electron localization in atomic and molecular systems. J. Chem. Phys. 92, 5397 (1990).

Grochala, W., Hoffmann, R., Feng, J. & Ashcroft, N. W. The chemical imagination at work in very tight places. Angew. Chem. Int. Ed. Engl. 46, 3620–3642 (2007).

Bader, R. F. W. Atoms in Molecules: A Quantum Thory Vol. 22 (Clarendon Press, Oxford, UK, 1990).

Yao, Y. & Hoffmann, R. BH3 under pressure: leaving the molecular diborane motif. J. Am. Chem. Soc. 133, 21002–21009 (2011).

Pickard, C. J., Martinez-Canales, M. & Needs, R. J. Density functional theory study of phase IV of solid hydrogen. Phys. Rev. B 85, 214114 (2012).

Chambers, C. & Holliday, A. K. Modern inorganic chemistry: Group IV 175–176 (Butterworth, London, UK, 1975).

Jin, X. et al. Superconducting high-pressure phases of disilane. Proc. Natl. Acad. Sci. USA 107, 9969–9973 (2010).

Abe, K. & Ashcroft, N. W. Quantum disproportionation: The high hydrides at elevated pressures. Phys. Rev. B 88, 174110 (2013).

Goncharenko, I. et al. Pressure-Induced Hydrogen-Dominant Metallic State in Aluminum Hydride. Phys. Rev. Lett. 100, 045504 (2008).

Rousseau, B. & Bergara, A. Giant anharmonicity suppresses superconductivity in AlH3 under pressure. Phys. Rev. B 82, 104504 (2010).

Bohnen, K.-P., Heid, R. & Renker, B. Phonon Dispersion and Electron-Phonon Coupling in MgB2 and AlB2 . Phys. Rev. Lett. 86, 5771–5774 (2001).

Choi, H., Roundy, D., Sun, H., Cohen, M. & Louie, S. First-principles calculation of the superconducting transition in MgB2 within the anisotropic Eliashberg formalism. Phys. Rev. B 66, 020513 (2002).

Singh, P. From E2g to Other Modes: Effects of Pressure on Electron-Phonon Interaction in MgB2 . Phys. Rev. Lett. 97, 247002 (2006).

McMillan, W. Transition temperature of strong-coupled superconductors. Phys. Rev. 167, 331 (1968).

Allen, P. B. & Dynes, R. C. Superconductivity at very strong coupling. J. Phys. C Solid State Phys. 8, L158–L163 (1975).

Yao, Y., Tse, J., Tanaka, K., Marsiglio, F. & Ma, Y. Superconductivity in lithium under high pressure investigated with density functional and Eliashberg theory. Phys. Rev. B 79, 054524 (2009).

Garland, J., Bennemann, K. & Mueller, F. Effect of Lattice Disorder on the Superconducting Transition Temperature. Phys. Rev. Lett. 21, 1315–1319 (1968).

## Acknowledgements

The authors appreciatively acknowledge the financial support by Natural Science Foundation of China under Grants No. 11474128, 11274136, 11025418 and 91022029, China 973 Program under Grant No. 2011CB808200 and the 2013 Program for New Century Excellent Talents in University. T.I. was supported by MEXT of Japan (Grant Nos. 20103001–20103005) and RIKEN iTHES project. A part of calculations were performed in the computing facilities at RIKEN Integrated Cluster of Clusters system (Japan) and the High Performance Computing Center of Jilin University. The work at the University of Saskatchewan was supported by Natural Sciences and Engineering ResearchCouncil of Canada (NSERC).

## Author information

### Authors and Affiliations

### Contributions

W.C., J.S. and H.L. performed the calculation. W.C., H.L., Y.Y., H.W., T.I. and Y.M. analyzed the data. Y.Y., W.C. and H.W. wrote the manuscript. H.W. and Y.M. supervised the work.

## Ethics declarations

### Competing interests

The authors declare no competing financial interests.

## Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

## About this article

### Cite this article

Cui, W., Shi, J., Liu, H. *et al.* Hydrogen segregation and its roles in structural stability and metallization: silane under pressure.
*Sci Rep* **5**, 13039 (2015). https://doi.org/10.1038/srep13039

Received:

Accepted:

Published:

DOI: https://doi.org/10.1038/srep13039

## Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.