Fibrillar collagens are the dominant proteins in mammalian tissue extracellular matrix. Although often viewed as static, solid proteins, extracellular matrix collagens were shown some 30 years ago to exhibit significant dynamical fluctuations1 and more recent studies have shown that model collagen-like peptides, at least, undergo structural changes upon binding proteins2,3,4, strongly suggesting that if replicated in native collagens, collagen molecular flexibility is of biological, as well as mechanical, importance. However, the corresponding molecular features that underlie the flexibility of collagens is not understood.

At a molecular level, collagens are triple-helical proteins with a repetitive Gly-Xaa-Yaa primary structure in each of the three constituent chains. Glycine is frequently followed by proline and hydroxyproline in the Xaa and Yaa positions, respectively. A key point here is that hydroxyproline (O or Hyp), an ascorbic acid–dependent post-translational modification of proline, is absolutely necessary for maintaining the stability of native collagens and severe pathologies arise when the post-translational modification of proline to hydroxyproline is disrupted, manifest for instance by scurvy in ascorbic acid deficiency.

GPO sequences constitute around 10% of all Gly-Xaa-Yaa triplets in native collagens5. Synthetic peptides containing sufficient (GPO)n and (GPP)n can self-assemble in water to give a collagen-like triple helix. These structures have helix parameters close to 7/2 helical symmetry (20.0 Å axial repeat, synonymous with 75)6,7,8,9, while fibre X-ray diffraction of native tendon collagen has indicated a looser 10/3 helical symmetry (28.6 Å axial repeat, synonymous with 107) in collagen proteins in vivo10. The difference in helical parameters between imino-rich model peptides and native collagens is generally ascribed to the native collagens having significant amino-rich segments, presumably adopting looser helical structures, in addition to imino-rich parts.

The backbone geometry of the imino residues and hence the molecular helical geometry, is strongly coupled to the prolyl ring conformation, which gives the intriguing possibility that the molecular helical geometry can be in large part be dictated by the steric and electronic factors that determine the ring conformation. Hence, the conformation of prolyl rings in (GPO)n and (GPP)n is a well-studied feature of triple helical peptides, with the expectation that general principles in these model systems will be replicated in native collagen triple helices. In general, imino acids in the Yaa position (denoted henceforth as PY and OY for proline and hydroxyproline respectively), tend to take the exo conformation (proline Cγ puckered towards the opposite side of the pyrrolidine ring to the exocyclic C–CO bond, also known as “up”), whilst proline in the Xaa position (PX) adopts an endo conformation (“down”)6,7,11. Experiments11,12 and calculations13 show clearly that the exo conformation of prolyl rings in the Yaa position stabilises the collagen triple helix, hence the fact Yaa prolines in native collagenous tissues are predominantly modified to exo-preferring hydroxyproline (exo-preferring through a combination of a gauche effect and an n → π* interaction)14,15,16.

The gain in thermodynamic stability from having prolyl rings in the exo conformation at the Yaa position in collagen-like peptides can be readily understood in structural terms—the exo conformation gives a backbone structure at the Yaa position that closely aligns with an ideal collagen 7/2 triple helical structure. Exo Yaa residues thus preorganise the peptide chain closer to the structure required in the 7/2 triple helix and thus triple helix formation comes at a lower entropic cost than for chains where the Yaa position conformation is not preorganised12. A similar situation exists for the endo conformation of proline residues in the Xaa position—rings in the endo conformation have a backbone geometry that closely aligns with the ideal 7/2 triple helical geometry, just as exo conformations in the Yaa position do. Model collagen peptides incorporating non-native proline derivatives in the Xaa positions that strongly favour endo conformations lead to very significantly enhanced stability of the collagen triple helix, as demonstrated by the much higher melting temperatures of such peptides, i.e. the temperature at which the three chains of the triple helix dissociate in aqueous solution, compared to a (GPP)n peptide of the same length17,18,19. This then brings us to the intriguing point: although GPP-based model collagen peptides show that PX rings in GPP triplets strongly favour endo conformations (as assessed by XRD analyses), the PX rings in GPO-based model collagen peptides, i.e. in native-like sequences, do not in fact have a strong preference for the endo conformation. So whilst the PX rings in triple helices containing only GPP sequences have almost exclusively endo conformations (e.g. PDB 3AH9 by Okuyama et al.), in (GPO)9, for instance, the PX rings occupy endo and exo conformations nearly equally. For example, of all the PX rings that were determined in the PDB structure 3B0S20, 29 endo and 24 exo ring conformations were observed. The clear question here is why do PX rings in GPO sequences apparently not favour a geometry that fits with the expected collagen 7/2 triple helix backbone structure and which would confer further thermodynamic stability? Thermodynamic stability is a feature which one might intuitively expect to be advantageous for a structural protein, especially one with a long half-life as the majority of collagens have in mammals. This is potentially a very important question—the difference in the prolyl backbone ϕ dihedral angle between endo and exo conformations is typically ≈15° and can be as much as 45°21. In other words, deviation of the PX rings from the endo conformation in GPO sequences potentially represents a very significant distortion from the ideal 7/2 triple helical structure, the very structure that the incorporation of hydroxyproline into the triplet was evolved to maintain. This apparent paradox strongly suggests that there are biological requirements for the collagen molecular structure that is beyond simply thermodynamic and structural stability. The further question then is, what is the biological relevance of the conformational promiscuity of PX rings in GPO triplets?

NMR spectroscopy has shown that a dynamic equilibrium exists between endo and exo states of prolyl rings in collagen, model collagen peptides and other related proteins1,22,23 which in turn will affect the average collagen molecular geometry observed on timescales slower than the ring flipping process. In (solid) native collagen, the molecular motions of the proline Cγ atom samples angular displacements of 20°–30° and hydroxyproline Cγ 10°–18°, on timescales of 10 μs to sub-nanoseconds, dynamic processes most likely corresponding to proline ring flipping1. These timescales are likely to be significantly faster than protein binding processes and so the average collagen molecular geometry presented to proteins will depend on the relative populations of the endo and exo states of the proline and hydroxyproline rings.

Here we show that when hydroxyproline is in the Yaa position of a collagen triple helix, Xaa proline rings have a frustrated geometry and flip rapidly between near-equally populated endo and exo conformations. This confers considerable flexibility on the peptide triple helix as a whole whilst maintaining the overall structure within clear boundaries. In contrast, Xaa prolines adjacent to Yaa unmodified prolines are more likely to be found “anchored” in the relatively deep potential energy minimum of the endo conformation, giving a less flexible structure.

Our approach is to determine Xaa proline ring endo:exo conformational populations experimentally using 13C NMR chemical shift measurements, combined with a potential energy landscape analysis24 to understand details of the ring-flipping dynamics at biologically-relevant temperatures. Our conclusion is that the rapid Xaa proline ring flipping, inherent in GPO triplets, results in an overall molecular geometry that flexes between 7/2 and tighter helical structures at biologically-relevant temperatures. This result implies that hydroxylation of Yaa prolines in collagens is not only essential for triple helix stability—it confers well-defined molecular flexibility at neighbouring Xaa prolines, which may have considerable biological significance and which may be critical in explaining pathologies associated with lack of Yaa proline hydroxylation.


Our primary aim is to understand the effect of hydroxylation of Yaa position prolines on the conformation and structure of the preceding Xaa-position proline, i.e. we want to compare and understand the relative ring conformer populations for PX in GPP versus GPO triplets. Whilst the distribution of proline ring conformations found from XRD structural analysis of model collagen peptides can be expected to broadly reflect the conformational propensity of proline rings, limits in resolution mean that XRD structural models cannot be expected to reproduce accurate ring conformation populations. Moreover, XRD data is often collected at 100 K, at which the ring conformation populations are likely to be very different from those at biologically-relevant temperatures.

Our protocol for experimentally determining the endo:exo populations of proline ring conformations uses the fact that 13C NMR shifts are sensitive to the ring conformation of imino residues. The rapid rate of ring flipping at all temperatures of biological interest means that the 13C chemical shifts observed are the equilibrium population–weighted average of those for the respective endo and exo conformations. Thus, proline ring 13C isotropic shifts are a direct measure of endo:exo populations at any temperature of interest. Proline Cγ 13C chemical shifts in particular are accurate sensors of proline ring conformation25, being sensitive to the dihedral angles describing the local bond geometry around this carbon. In type II poly-L-proline, a chemical shift difference of 1.5 ppm is observed between the (half chair) endo and exo conformations26, the endo conformation giving a Cγ 13C chemical shift of 23.8 ppm and exo, 25.5 ppm. In the collagen model peptides of this study, we expect Cγ chemical shifts approximately in this range, the precise value being determined by the endo:exo ratio for the imino residue ring being observed in the NMR spectrum, i.e. we will measure chemical shift values of nendo·δendo+nexo·δexo where nendo and nexo are the fractions of rings in the endo and exo conformational states respectively and δendo and δexo are the isotropic 13C shifts of the pure endo and exo conformations.

Two model peptides were synthesised, (GPO)11 and (GPO)5GPP(GPO)5, in which specific residues of the central triplet in each case, i.e. GPO and GPP respectively, were U-13C,15N-labelled in each chain of the homotrimeric triple helices (Table 1). Placing a GPP triplet in an otherwise GPO oligomer allows us to compare the local structure of GPO and GPP triplets within otherwise near identical molecules. Additionally, we synthesised (GPP)11 with the central triplet PY U-13C labelled for structural comparison with the (GPO)5GPP(GPO)5 GPP triplet, as there have been XRD structural analyses of pure (GPP)n peptides, but not GPP substituted into (GPO)n oligomers. The isotope labelling enables us to resolve NMR signals from specific residues in the central Gly-Xaa-Yaa triplet in each case, thus avoiding overlap of signals from all proline sites and so maximizing the sensitivity of 13C chemical shifts to proline ring conformation25,26,27. The nomenclature assigned to these variously labelled peptides is summarised in Table 1; GPO-GX, for example, refers to (GPO)11, i.e. dominant NMR signals are from a GPO triplet, with U-13C,15N-labeled Gly and PX. We use lyophilised samples so that the NMR spectra contain signals from a representative collection of possible structures for each peptide, rather than a single structure and thus probe a range of accessible prolyl ring conformations.

Table 1 Proline 13C chemical shifts showing the variation between Xaa and Yaa positions, preferred pucker and for endo and exo proline rings in poly(Pro)26.

13C NMR spectra of the peptides are, as expected, dominated by signals from the labelled residues (Fig. 1) and thus 13C chemical shift assignment for the model peptides is trivial, although line widths and low spectral dispersion preclude sub-assignment of signals from specific atoms to leading, middle and trailing peptide strands of the triple helices. In comparing 13C and 15N chemical shifts between these peptides, we are mindful of the fact that Pro/Hyp exert a particularly strong effect on the N, CO, Cα and Cβ chemical shifts of the i − 1 (preceding) residue in a peptide chain, which is the so-called “proline effect”28,29 That this effect does not extend to the Cγ and Cδ chemical shifts is evidenced from substantial literature chemical shift data29.

Figure 1
figure 1

13C CP-MAS ssNMR spectra of triple-helical peptides used in this study to model GPO and GPP triplets in the collagen triple helix.

Proline Ring Conformation and Chemical Shift Trends

Based on XRD results7,30,the 13C ,15N-labeled PY in both GPP11-Y and GPP-YG are expected to favour exo conformations. Thus we assign the chemical shifts for PY in these two peptides as being representative of a population that is biased towards a pure exo conformational state. The similarity of conformation for the labelled proline in these two peptides is clear from the very similar 13C chemical shifts throughout the PY residues.

Proline Cγ 13C chemical shifts for endo conformations are expected to be lower than those for exo cf. poly-L-proline (Table 1). That this is indeed the case is confirmed by comparing the Cγ 13C chemical shifts for exo-favouring PY in the GPP triplets of GPP11-Y and GPP-YG (both 25.7 ppm) with those for PX in the GPP triplet of GPP-GX—expected to strongly favour endo. The PXCγ for the GPP triplets in fact give two 13C signals, chemical shifts 24.4 and 25.0 ppm, both significantly lower frequency than for the largely exo conformation PY rings, as expected by analogy with poly-L-proline.

That there are two signals for the GPP PXCγ in GPP-GX over a wide range of temperature (Figure 2) implies there are two distinct endo:exo population distributions for the GPP triplet PX residue in this molecule. That two Cγ 13C signals only occur for the peptides in which a GPP triplet is substituted within an otherwise GPO oligomer suggests that the source of the two signals in this case is the GPP PX residue having two different possible environments created by the neighbouring chains in the triple-helix structure. Figure 3(a) shows that this is indeed the case. The chains of the triple helix are normally shifted by one residue with respect to each neighbouring chain as shown in this figure, the so-called register of the three peptide chains. This means that in any cross section of the triple helix, the three residues in the cross section will consist of a glycine, an Xaa (here PX) residue and a Yaa residue. For the cross sections containing the 13C-labelled GPP PX residues (i.e. one PX ring in each chain), the Yaa residue will be proline in two cross sections and hydroxyproline in one cross section. Thus, there are two different cross sections possible for the three GPP triplets in the molecule and so we expect two Cγ signals for the GPP PX residues, one associated with the G(13C-P)P cross sections and one associated with the G(13C-P)O cross sections. The signal at 25.0 ppm coincides closely in frequency with that for the PX Cγ signal for the (GPO)11 molecule (25.3 ppm in the latter), a molecule which consists entirely of GPO cross sections and thus we can confidently assign the 25.0 ppm signal for the (GPO)5GPP(GPO)5 PX Cγ to be from PX Cγ in GPO cross sections and hence the signal at 24.4 ppm, we assign to the PX Cγ in GPP cross sections. If all the molecules of the sample are in perfect register, then we would expect an intensity ratio of 2:1 for these two signals. However, chain misregisters (Fig. 3(b)), i.e. chain registers with the three peptide chains offset by two or more residues are highly likely. Key here is that (GPO)n triple helices are significantly less stable than (GPO)n triple helices, as evidenced by the much lower melting temperatures for (GPO)n triple helices. When the three chains are in perfect register, the molecule contains a clear section of GPP helix—presumably a less stable section than the sections containing only GPO triplets—which is dispersed by the chains misregistering. Thus, we can expect an equilibrium of chain registers in the sample. In any misregistered molecule, the three 13C-labelled PX rings are all in GPO cross sections and all three PXCγ sites would thus be expected to give signals at 25.0 ppm. We observed that the two GPP PX Cγ signals have approximately equal intensities at 242 K (see Fig. 1) which suggests that some of the (GPO)5GPP(GPO)5 molecules are in some form of misregister at this temperature.

Figure 2
figure 2

Cβ and Cγ signals from variable-temperature 13C CP-MAS ssNMR spectra for GPP-GX at 242–342 K.

Dashed lines are aligned with signal position at the lowest temperature, highlighting the existence of two Cγ signals over a wide temperature range. Signal maxima are tabulated in Supplementary Information, Tables S2–S4. NMR spectra for all signals at all temperatures are shown in Figure S1–S2.

Figure 3
figure 3

Schematic diagram of the chain register for triple-helical GPP-GX.

The 13C-labeled proline is highlighted in red and grey lines indicate inter-chain hydrogen bonds. (a) Normal register with a one residue stagger between chains in the triple helix. (b) One possible misalignment of the chains with a stagger of two residues, causing misregister. Rectangles indicate the two possible helix cross sections: GPP (black dots) or GPO (red dots).

The PXCγ chemical shift associated with the GPP cross section, 24.4 ppm, is close to that expected for a pure endo population of conformations and so implies that the PX rings in this cross section at least strongly favour the endo conformation, in line with conclusions from XRD analyses of GPP oligomers. In turn, the higher PXCγ chemical shift of 25.0 ppm for the PX in GPO cross sections implies a PX ring conformation with rather more equal endo and exo conformations in this case. The shift towards a larger exo population is even more pronounced for the PX ring in the GPO sequence (which necessarily also has a GPO cross section) in (GPO)11, where the Cγ chemical shift is 25.3 ppm, i.e. intermediate between the chemical shifts expected for endo and exo conformations.

The key question then is: why does hydroxylation at the Yaa position within a GXY triplet or a helix cross section appear to affect the PX ring conformational population distribution so markedly? Specifically, why does PX in a GPO triplet appear to have a much less strong preference for either endo or exo conformations than PX in GPP triplets in GPP cross sections? It is known that the proline (and presumably hydroxyproline) ϕ backbone dihedral angle is coupled to the ring conformation in peptides in general. This implies that when Yaa positions are occupied by strongly exo-favouring hydroxyproline, the time-averaged backbone ϕ dihedral angle for the Xaa residue is different from that when Yaa is occupied by less strongly exo-favouring, unmodified proline. Since the 7/2 helical geometry is most closely matched by PX in an endo conformation, the further implication is that the more equal endo:exo populations for PX in GPO triplets confers a PX backbone geometry that deviates significantly from the ideal for a 7/2 triple helix. The next question is then what is the helical geometry at the PX site in this case? Answering these questions will give us insight into the possible biological relevance of the conformational promiscuity of the PX ring conformation in GPO sequences.

We can answer these questions by modelling the potential energy landscape available to the proline rings in these triple helical molecules. Specifically, we can quantify changes in the landscape introduced by hydroxylating Y-position prolines in a collagen triple helix and so understand why PX in a GPO triplet behaves so differently from a GPP triplet in terms of its conformational preference.

Analysis of the Potential Energy Landscape

There have been many excellent studies modelling the factors that affect the stability of the collagen triple helix and collagen model peptides11 and modelling the dynamics between proline and hydroxyproline ring conformational states31,32,33,34,35. These have largely focused on single or small numbers of residues within a peptide. In our work, we need access to equilibrium ring conformation populations so that we can compare with experimental data and so we need to model the potential energy landscape in molecules in which there are many PX rings in similar environments. We therefore modelled the potential energy landscape for imino residue ring flips for the entire molecule in (POG)12 and (PPG)12, so that we can compare the PX ring conformation populations between GPP triplets in purely GPP cross sections and GPO triplets in purely GPO cross sections.

The results of these calculations are summarised in Fig. 4, which shows the potential energy change as each proline ring in the ground state conformation of (POG)12 and (PPG)12 is independently flipped to the opposite conformational state.

Figure 4
figure 4

Modelling the potential energy change resulting from a single flip of each proline or hydroxyproline ring in (POG)12 and (PPG)12.

Top panel: Yaa rings; bottom panel: Xaa rings. The potential energy changes for the terminal rings are not shown. All points were plotted relative to their respective ground state potential energy which is taken to be energy zero.

As expected, PY in (PPG)12 and OY in (POG)12 adopt predominantly exo states, with the preference stronger for hydroxyproline, for reasons which are already well-established11. PX, for the most part, adopts endo conformations in the ground state of both peptides. The key finding here is that the potential energy change for PX ring flip in (POG)12 is about half of that for PX in (PPG)12. The presence of the OH group on hydroxyprolines in the Yaa position is the only difference between these two molecules and so it must account for the reduced potential energy difference between the ring conformations in the Xaa position, in addition to the known increased potential energy difference between exo and endo conformations in the Yaa position for hydroxyproline compared with proline and the resulting higher energy barriers for the hydroxyproline ring flips in the Yaa position, i.e. slower ring flips for hydroxyproline. Also of note is that, for all rings, the potential energy differences between endo and exo conformations are small compared to the thermal energy (kT) for temperatures above around 200 K. This is in agreement with the NMR studies1,22,23,36, which have shown that proline rings in collagen-like peptides are not in a single conformational state, but are flipping rapidly between endo and exo states. Further analysis (see Supplementary Information, Section S3) shows that there is little coupling between rings and so the difference in potential energy between different ways of flipping two rings of a given type, i.e. two PX or one PX and one PY/OY etc. is largely independent of where the rings are in the peptide.

We can calculate the relative populations of the endo:exo conformations as a function of temperature (Fig. 5) using information from the potential energy landscape (harmonic superposition approximation)24. For (POG)12 at room temperature, there is a broad distribution of both PX and OY ring conformation populations, centred at 60:40 endo:exo for PX and 5:95 endo:exo for OY, which is consistent with our NMR observations and with X-ray diffraction (XRD) structures for analogous crystalline POG oligomers20. The behaviour for (PPG)12 is very different from (POG)12. For PY, the distribution is centred at 22:78 endo:exo, a significantly less strong preference for exo than PY has in (POG)12, which is consistent with expectations from theoretical analysis31,32,33,34,35 and XRD. For PX in (PPG)12, the relative population of ring conformations is very tightly centred on 72:28 endo:exo—only two PX rings close to the ends of the molecule have endo:exo ratios significantly different from this. Again, this is consistent with the distribution of endo:exo conformations for (PPG)10 found from XRD structures7,30 and our measured Cγ 13C NMR chemical shifts. Indeed, we can use these calculated ring conformational distributions with our experimental 13C chemical shift data to calculate the expected 13C chemical shifts for PX pure endo and exo states (for GPP and GPO triplets) as 23.7 ppm and 26.3 ppm respectively.

Figure 5
figure 5

Top: Calculated distributions of ring conformations as a function of temperature for (PPG)12 (left) and (POG)12 (right).

Bottom: Histograms showing the distributions of ring conformation populations at 297 K. Note the difference in vertical scaling.

These results suggest that stabilization of the Yaa exo state in GPO triplets and the corresponding strong preference for this conformation at the Yaa position, leaves the neighbouring PX ring in a metastable state, with the PX ring moving rapidly over nearly the entire conformational range. Thus hydroxylation of the Yaa-position proline not only stabilises the collagen triple helical structure, it confers considerable flexibility at the Xaa-position proline.

The next question is: does this flexibility of the PX residue have any significant effect on the backbone structure of these collagen model peptides? In general, endo—exo proline ring flips in proteins can change the proline ring dihedral angle by around 10° or more. Table 2 details the calculated changes in the peptide backbone torsion angles (ϕ and ψ) that arise when changing the proline ring conformation for Xaa and Yaa prolines and shows that there are differences of around 11° or more in PX backbone ϕ dihedral angle between endo and exo ring conformations.

Table 2 Changes in backbone dihedral angles upon flipping from ground state to the opposite puckered state, given as averages and standard deviations across each proline class.

Another pertinent question at this point is: how do these local structural changes arising from ring flipping affect the time-averaged overall molecular geometry at biologically-relevant temperatures? The geometric structures that correspond to minima in the potential energy landscape may be encountered by the molecule at any temperature. We computed two such structures with different imino residue ring conformations. The first, the ground state (lowest potential energy) geometric structure for (POG)12 has PX endo (very largely) and OY exo. In the second structure 40% of the PX rings were selected at random and flipped to the exo state, representing one possible configuration of the PX exo rings expected around room temperature.

Figure 6 shows Ramachandran plots for all glycine, proline and hydroxyproline residues in these structural models. Whilst the ground state structure dihedral angles cluster around those for the ideal 7/2 helix (ideal 7/2 helical twist is 54°), those for the excited state structure relevant at room temperature correspond to a tighter helical structure, with a helical twist around 59.4°. Interestingly, the PX rings in this excited state structure have backbone dihedral angles fairly evenly distributed about those for an ideal 10/3 helix, rather than 7/2. At temperatures of biological interest, the molecular structure is of course highly dynamic, sampling a wide range of endo:exo ratios and with different rings at any one time adopting endo and exo conformations and so the Ramachandran plot will be similarly varying with time, but nevertheless, this analysis serves to show how much structural distortion away from ideal 7/2 symmetry can be present at biologically-relevant temperatures, perhaps towards time-averaged PX molecular geometries that are more consistent with those expected for a 10/3 helix than 7/2.

Figure 6
figure 6

Ramachandran plots of the backbone dihedral angles for idealised 7/2 (imino-rich) and 10/3 (amino-rich) triple helices38 and our calculated structures of (POG)12 with 0% and 40% exo pucker.


Proline and hydroxyproline rings in both model collagen peptides and native collagens are known to flip between endo and exo conformations on the nanosecond timescale in the solid state. The proline ring conformation is known to be coupled to the peptide backbone ϕ dihedral angle21, so that flips between different proline ring conformations can be expected to lead to fluctuating proline dihedral angles. The very rapid timescale of the ring flipping means that for the vast majority of biological interactions, only the time-averaged structure is important, which in turn is simply determined by the relative time-averaged populations of the various conformational states visited by the imino rings, which in this work were directly measured by ssNMR.

By studying model collagen peptides containing GPP and GPO triplets, we have shown that proline has a frustrated structure in the Xaa position of a Gly-Xaa-Yaa triplet in a model collagen peptide when followed by hydroxyproline in the Yaa position and facing hydroxyproline in a neighbouring chain, i.e. for these proline rings, there is no strongly preferred potential energy minimum for any ring conformation. The “fixing” of OY in the exo conformation with its concomitant backbone dihedral angles, along with those in neighbouring chains, seems to be the factor that confers this metastable structural state on the preceding PX. The result is significant structural flexibility at PX, with the proline ϕ dihedral angle fluctuating through around 10° as the proline ring moves between endo and exo conformational states according to our calculations. Such flexibility may have biological relevance; XRD studies of proteins binding to collagen-like peptides suggest that the binding produces local “kinks” in the backbone of the peptide chain bound to the protein2,3,4 and local changes in the PX endo:exo ratio towards exo appear to accompany this effect. The broad range of endo:exo ratios for PX rings in GPO triplets predicted to exist at any given temperature implies that PX rings in GPO triplets dynamically sample both high and low endo:exo ratios, perhaps facilitating protein binding or fine-tuning the recognition segment to a particular binding affinity. It is interesting that the dominant equilibrium PX endo:exo ratio at biologically-relevant temperatures is close to 50:50. In pure statistical terms, this represents the most disordered state possible for the ring conformation and thus a natural “sink” for the triple helical-structure to return to, for example, when binding proteins dissociate.

Materials and Methods

Peptide Synthesis and Purification

Peptides were synthesised (0.1 mmol scale) as C-terminal amides on a TentaGel R RAM resin (loading of 0.19 mmol/g, Rapp Polymere) following the standard Fmoc-based solid-phase peptide synthesis strategy on a microwave-assisted automated peptide synthesiser (LibertyTM, CEM) and purified by reverse phase HPLC as detailed in Supplementary Information, Section S1.

Pure peptides were characterised by matrix-assisted laser desorption and ionization-time of flight (MALDI-TOF) mass spectrometry, then lyophilised.

Solid-state NMR

All ssNMR spectra were recorded on a 9.4 Tesla Bruker Avance I NMR spectrometer, operating at frequencies of 400 MHz (1H) and 100 MHz (13C). Magic angle spinning (MAS) frequency was 10 kHz for all experiments.

Labelled peptides were packed into kevlar inserts (Bruker) which in turn fit into standard zirconia 4 mm rotors (Bruker).

13C and 15N cross polarization (13C CP) experiments: The standard CP sequence in the Bruker pulse program library was used with 1H 90° pulse length 2.5 μs, contact time 2.5 ms; during the contact pulse a ramped pulse was applied on 1H with average spin lock field of 70 kHz. During acquisition, SPINAL64 decoupling at field strength 100 kHz was applied on 1H. Chemical shifts were referenced to external glycine (α polymorph), using the methylene signal at 43.1 ppm relative to TMS (13C).

Variable temperature experiment: using a Bruker Variable Temperature Unit, the temperature of the sample was varied from 242 K to 342 K in steps of 5 K. At each temperature, the sample was allowed to equilibrate for up to 10 minutes before a standard 13C CP-MAS spectrum was recorded.

Calculating the Potential Energy Landscape for Puckered States

The GMIN, OPTIM and PATHSAMPLE energy landscape exploration software employing the AMBER9 force field with implicit solvent (igb = 2) and standard amino acid parameters (ff99SB) was used. The non-standard hydroxyproline parameters were derived from ab initio quantum calculations37. The initial co-ordinates and topology for (POG)12 were generated from PDB 1V7H9 and modified to give (PPG)12. Full details can be found in Section S2, Supplementary Information.

Differential Scanning Calorimetry (DSC)

DSC was performed using a Mettler Toledo DSC 822 on the solid, as-prepared peptides with 80 cm3/min N2 and a heating rate of 5 °C/min from 20 °C to 70 °C while the power required to maintain this rate was monitored.

Additional Information

How to cite this article: Chow, W. Y. et al. Hydroxyproline Ring Pucker Causes Frustration of Helix Parameters in the Collagen Triple Helix. Sci. Rep. 5, 12556; doi: 10.1038/srep12556 (2015).