The low-dimensional transition metal oxides (TMOs) have a rich diversity of remarkable properties1,2,3, such as room-temperature ferroelectricity4, strong ferroelectric ferromagnetism5 and superconducting at the interface6, as well as strong polarization enhancement7. More importantly, their properties can be readily tuned by external fields8 so that the device functionalities are designed, just as in modern microelectronics based on conventional semiconductor interfaces9,10,11. The low-dimensional TMO structures based on perovskite ABO3(111) (A and B are cations) surfaces are particularly interesting. Along this direction, the crystal is stacked with alternative AO3 and B atomic layers. The so-called double perovskite A2BB’O6 in which the B/B’ cations are long-range ordered can be prepared as the [111] superlattice of AO3/B/AO3/B112,13,14,15,16,17,18. Such an artificial material cannot be synthesized in the bulk form with the B/B’ cation doping. The dopant spatial distribution in bulk is dictated by thermodynamics and falls in randomness at the atomic scale in normal cases due to the close energies of different ordering configurations12. By growing the LaFeO3/LaCrO3(111) superlattice, the ordered double perovskite La2FeCrO6 film15,19,20 was successfully obtained and showed unique magnetic ordering, in contrast to the solid solution of LaFeO3 and LaCrO3 where the long-range ordering of Fe/Cr distribution is missing.

The six-fold symmetry possessed by perovskite ABO3(111) also provides the opportunity to achieve novel quantum states. It was predicted that the double-layered ABO3(111) might be promising candidate of new topological insulators (TIs)21,22,23,24. Comparing with conventional TIs whose electric properties are dominated by s and p orbitals, TMO-based topological materials would be more flexible to control since d electrons with strong correlation contribute significantly to their electronic properties. The honeycomb lattice formed by the two trigonal sublattices on the top two layers of the perovskite (111) surface could reduce the symmetry of crystal field and introduce additional level splitting of d orbitals. Xiao et al. found that LaAuO3(111) has a large topological nontrivial band gap and could realize quantum spin Hall effect at room temperature23.

Strontium titanate, SrTiO3 is a typical perovskite oxide with very high dielectric performance. Its (111) surface matches the lattices of many novel quantum materials with hexagonal in-plane structure. Therefore SrTiO3(111) with an atomically well-defined surface not only serves as an epitaxial growth template, but also can be used as the insulating layer for the modulation of carriers density by gate electric field. Chen et al. reported the control of charge density of Bi2Se3 on SrTiO3(111) in the range of 2 × 1013/cm2 by applying the back gate voltage of 150 V25. Apparently the SrTiO3(111) thin film as a dielectric buffer layer on a metallic substrate would have effectively reduced the gate voltage required for carriers modulation thus making the structure convenient for device applications. However, due to the surface polarity of the ionic crystal26, it is essentially challenging to realize the high-quality layer-by-layer growth of SrTiO3(111) films. In the current work, we achieve the growth of high-quality homoepitaxial SrTiO3(111) films on Nb-doped metallic substrates by molecular beam epitaxy (MBE) method. Reconstructions are formed on the substrate surface and maintained all through the growth to compensate the surface polarity, enabling the layer-by-layer growth with atomically well-defined film surface. And with the monitor of reflective high-energy electron diffraction (RHEED) on the microstructure corresponding to different reconstruction phases of the growing surface, the deposition rates of metal sources are precisely controlled to realize the cation stoichiometry. The films show high dielectric performance. At 6 K, a 50 nm-thick film allows the carriers density modulation in the order of 2 × 1013/cm2 with the gate voltage less than 0.2 V. We present an ideal platform for the design and growth of low-dimensional quantum structures with easy and reliable tunability of the carriers.


The experiments were carried out in oxide MBE system equipped with a scanning tunneling microscope (STM). The base pressure was better than 1 × 10−10 mbar. The Nb-doped (0.7 wt.%) SrTiO3 (111) substrate was heated by passing a direct current and the temperature was measured with an infrared pyrometer. The monophased (4 × 4) reconstructed surface was prepared by Ar+sputtering (1 kV / 10 μA) for 12 minutes followed by annealing in oxygen with the pressure of 3 × 10−6 mbar at 1000 °C for 1 hour. Then the (6 × 6) reconstruction was formed by depositing 1.1 monolayer [ML, 1 ML = 3.8 × 1014 atom/cm2, corresponding to the cation density on the bulk truncated SrTiO3(111) surface] Ti atoms on (4 × 4) at 1000 °C with oxygen pressure of 3 × 10−6 mbar27. High purity (99.999%) Sr and Ti were evaporated by a low-temperature and a high-temperature effusion cells, respectively. The depositing rates of the sources were calibrated on SrTiO3(110) surface according to the reconstruction evolution behavior upon the surface metal cation concentration28. By setting the temperature of Sr and Ti sources at 420 °C and 1450 °C, respectively, the same flux rates of 0.4 ML/min from both sources were obtained. SrTiO3(111) film was grown by co-evaporating Sr and Ti under an oxygen pressure of 3 × 10−6 mbar with the substrate temperature of 1000 °C, followed by in situ annealing at 400 °C with oxygen pressure of 5 × 10−3 mbar for 3 hours. The cross-sectional microstructure of the film was characterized by high-resolution transmission electron microscopy (HRTEM) (FEI Tecnai G2 F20). The dielectric performance of the film was measured by a microampere meter (Agilent B2901A) that provides the gate voltage and a lock-in amplifier (SR830) that obtains the capacitive reactance in the measurement circuit with the test signal of 20.14 Hz/1 mV at 6 K.

Results and Discussions

Although the deposition rates of Sr and Ti sources have been calibrated on SrTiO3(110) surface29, further precise tuning is necessary for the MBE growth of SrTiO3(111) films due to the possibly different adhesion coefficients of metals. It has been reported that the SrTiO3(111) surface shows a series of reconstructions that evolve upon the cation concentration, e.g., a monophased (4 × 4) can be changed into (6 × 6) by depositing ~1.1 ML Ti on the surface and the transformation is totally reversible by depositing the same amount of Sr on (6 × 6)27. More importantly, the change between different microstructures corresponding to those reconstruction phases can be monitored by RHEED even at high temperature in real-time during the metal evaporation. This allows us to precisely synchronize the deposition rate of Sr and Ti during the MBE growth of the SrTiO3(111) films to optimize the cation stoichiometry. In the current work, we prepare a monophased SrTiO3(111)-(6 × 6) substrate surface and basically keep it unchanged all through the film homoepitaxial growth by adjusting the temperatures of Sr and Ti sources with RHEED patterns as the feedback control signal.

Figure 1 (a) shows the STM image of the (6 × 6)-reconstructed substrate surface. The corresponding sharp RHEED patterns of the surface also indicate the high quality of the long-range ordered surface. The SrTiO3(111) film is deposited with the substrate temperature at 1000 °C and oxygen pressure at 3 × 10−6 mbar. And the temperatures of Sr and Ti sources are initially set at 420 °C and 1450 °C, respectively. The intensity increase of RHEED (01) diffraction spot can be sensitively observed [see the bottom panel of Fig. 1 (b)]. And after 15-minutes growth, “ 4 × “ fractional spots appear in RHEED indicating that the Sr rate is higher than Ti. Knowing this relationship between the RHEED intensity (IR) and the Sr concentration relative to that on the monophased (6 × 6) surface (ΔSr), we immediately (after 86-seconds growth) recover ΔSr to 0 by closing the shutter of Sr source and evaporating Ti only (for 9 seconds) until IR drops back to the value as on the initial substrate surface. It can be estimated that during the 86-seconds growth, Sr deposits more than Ti by ~0.06 ML. Then both shutters of Sr and Ti sources are closed and the temperature of Sr source is reduced to 419 °C. Coevaporating Sr and Ti again, IR still increases with time although the slope is lowered. The above procedures are repeated until IR keeps constant for a long time [e.g., 4 minutes as shown in Fig. 1 (b)]. With the temperatures set at 417.5 °C and 1450 °C for Sr and Ti sources, respectively, they provide precisely the same evaporation rates.

Figure 1
figure 1

(a) The STM image (+2.5 V/50 pA) of the (6 × 6)-reconstructed SrTiO3(111) substrate surface. The right inset shows the zoom-in features and the left inset shows RHEED patterns of the corresponding surface. (b) Procedures of adjusting the source temperature for the optimization of film cation stoichiometry. The change of ΔSr is schematically shown while the corresponding intensity of RHEED (01) spot IR is presented in the bottom panel.

Growing for 340 minutes, a 30-nm thick SrTiO3(111) film is obtained. Figure 2 (a) shows the STM image of the as-grown surface. Although the (6 × 6) periodicity is still visible, the surface is covered by some disordered adsorbates. And the fractional RHEED patterns become fuzzy comparing to the initial monophased (6 × 6) substrate surface. We find that the quality of film surface can be completely recovered by depositing 0.12 ML Ti, exposing the well-ordered (6 × 6) lattice with negligible amount of disordered adsorbates [Fig. 2 (b)]. Considering Sr and Ti in equivalent amount induce the change of surface microstructure in the reverse way27, it is indicated that ΔSr increases to 0.12 ML after 340-minute growth. Therefore the deviation from the cation stoichiometry is less than 0.1% in the film. Actually, if we extend the calibration time as illustrated in Fig. 1 (b), the precision of cation stoichiometry could be further improved since the change of IR will accumulate to be sensitive for detection.

Figure 2
figure 2

(a) The STM image (+2.3 V/50 pA) of the as-grown surface of the 30 nm film. (b) The STM image (+2.2 V/50 pA) of the film surface after depositing 0.12 ML Ti onto the surface shown in (a). The right insets show the zoom-in features and the left insets show RHEED patterns of the corresponding surfaces, respectively.

Figure 3 (a) shows the large-scale STM image of the 30-nm film surface. The statistics over several images indicate the average terrace width of ~150 nm, significantly broadened relative to the substrate (<100 nm). And the surface topography shows the step height of single-unit-cell (0.23 nm). These are the signature of the high-quality layer-by-layer growth of the SrTiO3(111) film, although the oscillation of RHEED intensity during film growth, typically associating the layer-by-layer growth, is not observed. The case is similar to the layer-by-layer growth of SrTiO3(110) film when the RHEED incident angle was in a certain range making it to be sensitive to the surface microstructure rather than the atomic layer roughness30. The cross-sectional HRTEM also confirms the nice crystallinity of the (111) film with indistinguishable interface of the homoepitaxial structure, as shown in Fig. 3 (b). We cap the film in situ with a layer of amorphous Si to mark the surface position in HRTEM. And the interface position can be estimated by counting the atomic layers from the surface since the growth thickness is known.

Figure 3
figure 3

(a) The wide-range STM image (+2.3 V/50 pA) of the 30 nm SrTiO3(111) film surface. The height profile along the red line (the left panel) is shown in the right panel. (b) The cross-sectional HRTEM image of a 6-nm-thick film.

Keeping the growing surface reconstructed is the key to obtain the high-quality SrTiO3(111) film. Firstly, the microstructure evolves upon the amount of Sr/Ti deposited on the surface, allowing the sensitive monitoring by RHEED. Secondly, the surface polarity is effectively compensated by the reconstruction, facilitating the layer-by-layer film growth to obtain the atomically well-defined surface. Therefore the substrate temperature should be relatively high (1000 °C in the current work) to provide enough energy to deposited metal atoms diffusing on the surface to form the long-range ordered reconstruction promptly during the film growth. The reconstruction does not have to be limited to the (6 × 6) phase, as long as it is in the reversible range27. Tuning the substrate preparation parameters, i.e., the sputtering dosage or the initial Sr/Ti deposition amount, different reconstructions can be obtained for the homoepitaxial growth. Once the relationship between RHEED intensity and surface Sr/Ti concentration is established, the feedback signal will be obtained to optimize the cation stoichiometry precisely.

The SrTiO3(111) thin film with atomically well-defined surface can be used not only as a epitaxial template of many novel quantum materials, but also as an ideal insulating layer of gate structure for the tuning of carries density. We fabricate the back gate structure by evaporating 3-nm-Cr / 30-nm-Au electrodes with the size of 200 μm in diameter on the film, while the conducting Nb-doped substrate with high carrier density serves as the other electrode, as schematically shown in Fig. 4 (a). On the Nb-doped SrTiO3 substrate, a Au/Cr/SrTiO3/Nb-SrTiO3/Cr/Au capacitor is formed to characterize the dielectric performance of the SrTiO3 film. For the 30-nm thick film at 6 K, the leakage current density (J) keeps extremely low (<1 μA/cm2) until the electric field (E) reaches 14 kV/cm (the breakdown field, corresponding applied voltage is 45 mV) and above the breakdown field J increases exponentially, as plotted in Fig. 4 (b). The capacitance-voltage (C-V) measurement indicates the capacitance of 8.4 nF at 0 V, which decreases to 7.8 nF at 25 mV. The relative dielectric constant ε is calculated as 910 at 0 V with a slight decay when a bias applied. Importantly the modulation amplitude of carriers density at the electrode with a gate voltage VGn(VG)] can be determined by , where S is the area of the electrode and e is the unit charge. Figure 4 (d) shows the dependence of Δn on VG - Δn is ~4.5 × 1012/cm2 with the gate voltage as low as 25 mV. It has been reported that dopants in SrTiO3 might be redistributed due to high-temperature annealing31. To exclude the substrate effect on the measurement of dielectric performance of the homoepitaxial film, we anneal the Nb-doped substrate in oxygen with the pressure of 3 × 10−6 mbar at 1000 °C for 6 hours followed by annealing in oxygen with the pressure of 5 × 10−3 mbar at 400 °C for 3 hours (the same annealing as for the substrate for film growth). As shown in the inset of Fig. 4 (b), a purely resistive behavior with a high conductivity at 6 K was detected, distinct from the dielectric film. It is evident that the substrate has negligible influence on the quantitative determination of the charge modulation range of the homoepitaxial film.

Figure 4
figure 4

(a) The schematic drawing of the Au/Cr/SrTiO3/Nb-SrTiO3 capacitor structure. (b) The leakage current density at different electric field, (c) the capacitance at different bias and (d) the charge density modulation range with different gate voltage measured at 6 K, respectively.

In order to improve Δn of SrTiO3(111) thin film on Nb-doped substrate, we reduce the amount of residual oxygen vacancies (VOs) in the film by annealing at 400 °C in a tube furnace with oxygen flow at ~1 bar for 16 hours. As shown in Fig. 4 (b), the insulating performance of the 30-nm film (with a low oxygen vacancy density, LV) is effectively improved, resulting in the increase of breakdown field to 26 kV/cm. And Δn can be tuned in the range of 1.7 × 1013/cm2 by VG lower than 120 mV [Fig. 4 (d)]. It should be noted that, due to the exposure of film surface to air and the following contaminations at high temperature, the ex situ annealing leads to the formation of an amorphous layer on the film, which seriously destroys the atomically well-defined surface as characterized by STM. Additionally the amorphous layer has a lower dielectric constant than SrTiO3 and introduces a small serial capacitor to the measured back gate structure. As the consequence, both of the total capacitance and dielectric constant are deteriorated in an uncontrolled way.

Alternatively, Δn can be enhanced by increasing the film thickness. In a thick insulating layer, defects of holes are difficult to line up to form the conducting channels. Therefore the breakdown field of a 50 nm thick film is significantly increased to 33 kV/cm [Fig. 4 (b)]. The relative dielectric constant also increases to 1000 (at 0 V), comparable with the reported values of SrTiO3(001) films with the thickness of several hundreds of nanometers32,33,34. At VG = 170 mV, the maximal Δn reaches 1.9 × 1013/cm2. The estimation of the dieletric performance of even thicker films can be made by a first-order appoximation. For example, the breakdown field of the 100-nm film could be expected as ~95 kV/cm, with ε of about 1300 and the maximal Δn of 6 × 1013/cm2 (VG = 950 mV). In such a way, the atomically well-defined surface of SrTiO3(111) film is maintained, facilitating the following epitaxial growth of other quantum materials.


We grow high-quality homoepitaxial SrTiO3(111) thin film on Nb-doped substrate by MBE. The growing surface is kept reconstructed to compensate the surface polarity and thus guarantee the layer-by-layer growth mode. And determined by the surface cation concentration, the formation of different reconstruction phases can be monitored by RHEED, providing the sensitive feedback signal for the optimization of chemical stoichiometry in real-time during film growth. Besides the atomically well-defined surface microstructure, the films show high dielectric performance that allow the modulation of carriers density in the range of 2 × 1013/cm2 with the back gate voltage lower than 0.2 V. The film provides an ideal platform for the epitaxial growth of novel quantum materials as well as the control of electronic properties in their device structures.

Additional Information